This invention relates generally to the field of low permeability containers, such as those used in vehicle fuel tanks, and in particular is directed to improved low permeability containers with low permeability fittings.
Plastic storage containers provide a number of advantages over those made of other materials, such as reduced weight, reduced costs for both materials and construction, and greater flexibility in shape. Along with these advantages, the ability of certain plastic containers to stretch or flex makes them useful in automotive applications, as they are less likely to leak in an accident. Mono-layer polyethylene fuel tanks, while benefiting from the aforementioned advantages, suffer from a comparatively high permeability to gasoline with respect to containers formed of other materials, and cannot meet U.S. Environmental Protection Agency (EPA) and state evaporative emissions standards. For example, both the EPA and the California Air Resources Board (CARB) are requiring progressively tighter evaporative emissions standards. Along with Zero Emission Vehicle (ZEV) and Low Emission Vehicle (LEV) standards, on-board refueling vapor recovery standards must be met. By reducing evaporative emissions from fuel tank systems, vehicle manufacturers can earn partial credit towards meeting ZEV standards.
Therefore several approaches have been taken to improve the permeability characteristics of plastic fuel containers. One solution to this problem has been a fuel tank formed of a multi-layer wall material that is composed of layers of polyethylene and an ethylene-vinyl alcohol co-polymer (EVOH). The ethylene-vinyl alcohol co-polymer exhibits good gasoline vapor barrier properties.
Polyethylene-EVOH thermoplastic structures can be formed into a variety of container shapes using twin-sheet thermo-forming and blow molding techniques. Polyethylene-EVOH container walls typically have 5 to 7 layers. The basic 5 layers include polyethylene inner and outer layers and one EVOH layer with an adhesive layer on each side. An optional sixth layer is typically a “regrind” layer made up of a mixture of polyethylene, ethylene vinyl alcohol (EVOH), and adhesive ground up from multi-layer materials left over from other manufacturing processes. An optional seventh layer may be a conductive layer or a material contact layer. For example, a multi-layer wall material having excellent gasoline vapor barrier properties is illustrated in FIG. 1. An outer layer 1 formed of polyethylene, overlays a regrind layer 2. Adhesive layer 3 binds regrind layer 2 to a central barrier layer 4 formed of EVOH, which in turn is bound by adhesive layer 5 to inner layer 6 of polyethylene.
Containers constructed using such multi-layer materials have low permeability to hydrocarbon or other vapors contained therein. Other technologies, such as platelet additives in the polyethylene, can also be used to create a lower permeation wall structure. However, the low permeation characteristics of the resulting containers are compromised when fittings are connected to the containers. This can be more clearly illustrated by reference to a typical fuel tank.
A Typical Fuel Tank
With reference to
With reference to
Fitting Attachment Techniques
Prior art techniques for attaching a fitting to a plastic container include molding an opening into the product during the molding operation. This can be accomplished by forming the opening on the parting line of the mold by inserting a pin between the mold halves and material layers contained therein during the molding process. The opening in the container is dictated by the size and shape of the pin. This technique leads to a discontinuity in the barrier layer at the seam where the mold halves come together. The outer finish of the opening is typically not acceptable for the sealing of an attachment, and requires a post-machining process to create a smooth surface. Such a machining process also enlarges the gaps in the barrier material at the seam, further increasing permeation of the assembly. Since the opening in the container is determined by the size of the pin, if there is not enough container material, the diameter of the hole formed can be irregular. Further, in order to insert a fitting into the opening, the diameter of the inserted portion cannot be greater than the diameter of the opening. Thus, this method is limited since the opening for the fitting can only be on the parting line of the container, permeation is increased at the seam where the material comes together, and fitting portions to be inserted into the opening can only be as large as the opening.
In instances where the diameter of the portion of a fitting to be installed inside a container is greater than the diameter of an opening formed at the mold parting line, it is necessary to bore a hole into the molded container. The fitting can then be welded onto the surface of the container. This method suffers from the need to interrupt the barrier layer at the attachment-container interface. Further, the fitting attached to the container may have a permeation that is higher than the container barrier material. Even an over-molded welded-on fitting has a relatively large permeation path through the weld.
Further information on low permeability tanks and methods for forming same can be found in numerous patents, articles and books, such as but not limited to U.S. Pat. No. 6,189,716 to Lawrukovich et al., U.S. Pat. No. 6,033,749 to Hata et al., U.S. Pat. No. 5,766,713 to Ravi Shankar et al., U.S. Pat. No. 5,691,016 to Hobbs, U.S. Pat. No. 5,443,874 to Tachi et al., and U.S. Pat. No. 5,230,935 to Delimoy et al., all of which are incorporated by reference as if reproduced in full herein.
There remains a need for low permeation fittings for use with low permeation containers, and for low permeation containers that meet the demands for flexibility in component placement and low cost without sacrificing strength and fuel economy benefits. There is also a need for simple methods for forming such containers.
In one embodiment, the present invention provides a low permeability fitting for a low permeability container. The fitting has a hollow inner component and a hollow outer component between which can be sandwiched a low permeability material that forms the wall of a low permeability container.
An embodiment of a low permeation container forming method in accordance with the present invention includes incorporation of a low permeation fitting, such as that described above, into a container wall. One end of the outer component of the fitting is bonded to the container wall during formation of the container so that it is integral therewith. When the outer component is bonded to the container wall during formation of the container, the container end of a passageway in the outer component is blocked by container wall material. Thereafter, the inner component of the fitting is inserted into the outer component, thereby forcing the parent wall material up into the outer component. This results in a tight seal between the inner component and the outer component, with the container wall acting as a seal. As the container wall portion contained within the fitting is continuous with the container wall forming the rest of the container, the fitting continues the low permeation characteristics of the container wall outward from the main container.
In an embodiment, a new fuel tank inlet or fill spud fitting is disclosed, and in another embodiment, a fuel tank sender attachment fitting is disclosed.
It is to be understood that both the preceding summary and the detailed description that follows are intended merely to be exemplary and to explain further the invention claimed. The invention may be better understood by reference to the following detailed description read in conjunction with the accompanying drawings.
An embodiment of the present invention may be better understood with reference to
Projections 26 on the outer end of outer component 20 are designed to provide a grip for a hose fitting that can be placed thereover. Alternatively, the component may have a smooth-walled exterior, or the exterior may have threads or other type of connector device thereon.
Referring again to
Low Permeation Fill Spud
Using
With reference to
With reference to
Exemplary Fitting Component Materials
For an automobile gas tank fill spud, the fitting outer component, such at that shown in
High density polyethylene is widely available from numerous commercial sources, such as Exxon, Mobil, Solvay, Phillips, BASF, FINA, etc. Acetal materials are widely available from numerous commercial sources, such as DuPont, Ticona, etc.
An Examplary Low Permeation Fuel Tank
In an embodiment, a fitting such as that illustrated in
The matching outer component has a height of about 34.5 mm, an inner diameter of 34 mm, and an outer wall diameter of about 42 mm. The outer wall has an integral connecting flange with a diameter of about 54 mm and a thickness of about 5.5 mm, and a barb on its outer end with a maximum diameter of about 44.5 mm.
The container is thermoformed from a multi-layer material, such as that illustrated in
Parent Material
The depth of the fitting into which the container wall is to be extended by the inner component dictates the amount of the parent material required, as does the gap between the inner and outer fitting part. Generally, for automotive fuel tanks, a parent material thickness for use in a twin sheet thermoforming process will range from about 1 mm to about 7 mm, preferably 3 mm to 6 mm for an embodiment, and preferably will be about 4.5 mm for another embodiment. These dimensions will vary depending upon the demands of the fitting.
An exemplary multi-layer thermoplastic container forming material may have an outer layer and inner layer of fuel tank grade HDPE that can be obtained from commercial sources such as Exxon, Mobil, Solvay, Phillips, BASF, FINA, Equistar, and Baysell. The adhesive layers may be formed of linear low-density polyethylene with maleic anhydride, such as that commercial available from Mitsui and Equistar. Ethylene vinyl alcohol for the barrier layer is commercially available from Evalca and Soarus. Other suppliers may have or develop adequate substitute materials. The container wall forming materials can be extruded as a multi-layer sheet that is cut to desired width and length for forming a container.
Method for Forming a Low Permeation Container
An exemplary container forming process in accordance with the present invention may proceed as follows. The external or outer component of a fitting, such as that illustrated in
Preferably, while the thermoplastic wall material is still at a sufficient temperature to have the requisite flow characteristics, an inner component, such as that illustrated in
Once the inner component is inserted into the outer component to the desired degree, the wall material blocking the passageway through the center of the inner component and outer component can be cut. The passageway can be opened either in-mold, or as a post molding trimming operation. Alternatively, a cutting element can be provided that automatically cuts the excess wall container from the fitting upon insertion of the inner component into the outer component to the desired depth. In some instances, the internal component can be used for internal attachment or alignment. Since the external diameter of the fitting can be the external diameter of the outer component, and the outer component can be preformed, the need for post-machining in many instances may be eliminated.
In a conventional twin sheet thermoforming process, sheets of multilayer thermoplastic material are loaded into thermoformers at loading station(s), and the loaded sheets then transferred into an oven for heating.
In an embodiment of a twin sheet forming process of the present invention, the outer component of a fitting, such as that illustrated in
Internal air pressure may be used to assist in forming and cooling the container. Once the container is cooled, it is removed from the mold pieces, excess flash is removed, and any secondary finishing operations are performed.
In a blow molding process, the outer fitting component would be placed into a mold when the mold is open and prior to insertion of a parison of molten plastic. The parison is preferably a hollow tube formed of a multi-layer material structure such as that described in FIG. 1. The fitting inner component is placed on an inserting mechanism that extends inside the parison from the top or the bottom. As the mold closes on the parison, the open ends of the parison are pinched shut. During “pre-blow” low pressure compressed air is introduced inside the parison to begin inflating it against the outer walls of the container. This can be done as the mold is being closed and before the ends of the parison are sealed, or the sealed parison can be pierced by an inflation needle in the mold. Once the mold is closed, high pressure air is introduced via one or more inflation needles to inflate and cool the container. The fitting inner component can be inserted into the fitting outer component either during the pre-blow, or soon after the high pressure air is utilized. The fitting inner component must be present inside of the parison when it is inserted into the mold for blow molding. Once the container is cooled, it is removed from the mold, excess flash removed, and the container is finished.
Fittings for use with the present invention include by way of non-limiting examples fill spuds, attachment mounts (e.g., flange mounts), check valves, fill limit valves, and roll over valves.
Flange Mount
With reference to
Outer component 100 includes a vertical wall 101, which forms a cylinder. A plurality of openings 103 are placed in wall 101 to permit molten thermoplastic material to flow therethrough during molding of the part to a thermoplastic material.
Inner component 112 is a ring with annular flange 113. Inner component 112 made be made of metal, but preferably is made of a plastic that will bond well to the wall of a container. The plastic may be a low permeability plastic coated with a thin layer of polyethylene to enhance bonding to a thermoplastic polyethylene wall material. In an embodiment, inner component 112 can be formed of metal, and have a plastic coating.
The fitting produces a large sealing surface 116, which in a preferred embodiment is sufficiently large that an attached device overlaps the barrier layer 106 and the entire opening 110 surrounded by the fitting inner component 112.
The fitting rings may optionally be formed of metal, for example mild steel with a coating for corrosion protection or perhaps stainless steel.
Containers constructed in accordance with the present invention have numerous advantages in addition to low permeability. For example, since plastic fuel containers can alter their shape due to temperature, the fuel or other chemicals stored therein, and/or under physical stresses, use of the fittings of the present invention reduce the likelihood of a fitting leaking at the junction of the fitting with the container wall. Further, unlike prior containers, the diameter of the internal components of a fitting can be much larger than the opening in the container. Further, the inner fitting component can be made of a material less susceptible to swell and deformation so that the opening inside of the container can be used for calibration purposes and to accurately direct placement of other components inside the container. The fittings of the present invention and methods for forming same into a container require less parent container material thickness to form a robust attachment due to the strength created by the sandwich structure.
Even containers that do not require low permeation characteristics will benefit from the advantages made possible by the present invention, such as improved structural integrity. For example, containers for storage of nonvolatile fluids may be constructed in accordance with the present invention by using a parent wall material that would be permeable to volatile fluid vapors. For example, polyethylene without a hydrocarbon barrier layer may be used.
The improved containers of the present invention are useful in all modes of self-propelled vehicles, such as but not limited cars, buses, marine and recreational vehicles, and trucks, and may also be useful in other applications, such as mobile or stationary storage containers for fuel and other volatile liquids.
While new low permeability fittings, low permeability containers, and methods of forming same have been disclosed as examples, there could be a wide range of changes without departing from the present invention. Thus, it is intended that the foregoing detailed description be regarded as illustrative rather than limiting and that it be understood that it is the following claims, including all equivalents, which are intended to define the scope of the invention.
This application claims priority of U.S. provisional patent application Ser. No. 60/250,278, filed Nov. 30, 2000.
Number | Name | Date | Kind |
---|---|---|---|
3115987 | Barnstead | Dec 1963 | A |
3426937 | Boschi et al. | Feb 1969 | A |
3606958 | Coffman | Sep 1971 | A |
3779420 | Knaus | Dec 1973 | A |
3811173 | Baumann | May 1974 | A |
3912107 | Baumann | Oct 1975 | A |
4513906 | Chang et al. | Apr 1985 | A |
4753368 | Lescaut | Jun 1988 | A |
4962862 | Farrington et al. | Oct 1990 | A |
5129544 | Jacobson et al. | Jul 1992 | A |
5230935 | Delimoy et al. | Jul 1993 | A |
5443874 | Tachi et al. | Aug 1995 | A |
5547096 | Kleyn | Aug 1996 | A |
5582729 | Shioda et al. | Dec 1996 | A |
5691016 | Hobbs | Nov 1997 | A |
5766713 | Ravishankar et al. | Jun 1998 | A |
6033749 | Hata et al. | Mar 2000 | A |
6044999 | Kido | Apr 2000 | A |
6179145 | Roth | Jan 2001 | B1 |
6189716 | Lawrukovich et al. | Feb 2001 | B1 |
20010025666 | Brown et al. | Oct 2001 | A1 |
20010029994 | Brown et al. | Oct 2001 | A1 |
Number | Date | Country |
---|---|---|
0 448 329 | Mar 1991 | EP |
0 930 190 | Jul 1999 | EP |
0 930 190 | Mar 2000 | EP |
1 031 725 | Aug 2000 | EP |
1 031 725 | May 2001 | EP |
1 108 598 | Jun 2001 | EP |
1 108 599 | Jun 2001 | EP |
WO 0142692 | Jun 2001 | WO |
Number | Date | Country | |
---|---|---|---|
20020063129 A1 | May 2002 | US |
Number | Date | Country | |
---|---|---|---|
60250278 | Nov 2000 | US |