Claims
- 1. A process for preparing a thermoplastic resin having high heat resistance by emulsion polymerization of a monomer mixture consisting essentially of .alpha.-alkylstyrene compound of the formula: ##STR3## wherein R.sub.1 is C.sub.1 -C.sub.3 alkyl and R.sub.2 is hydrogen, C.sub.1 -C.sub.3 alkyl or halo(C.sub.1 -C.sub.3)alkyl and an unsaturated nitrile in a weight proportion of 65:35 to 80:20 in the presence of a radical initiator, characterized in that the whole amount of the .alpha.-alkylstyrene compound and 10 to 99% by weight of the unsaturated nitrile on the basis of its total amount are first subjected to polymerization and, after the polymerization, the remaining portion of the unsaturated nitrile is added to the reaction mixture and the resultant mixture is subjected to further polymerization until the polymerization is substantially completed.
- 2. The process according to claim 1, wherein the amount of the unsaturated nitrile to be used for the first polymerization is from 20 to 95% by weight on the basis of the total amount of the unsaturated nitrile.
- 3. The process according to claim 1, wherein the amount of the unsaturated nitrile to be used for the first polymerization is from 2.5 to 50% by weight on the basis of the whole amount of the .alpha.-alkylstyrene compound.
- 4. The process according to claim 3, wherein the amount of the unsaturated nitrile to be used for the first polymerization is from 10 to 40% by weight on the basis of the whole amount of the .alpha.-alkylstyrene compound.
- 5. The process according to claim 1, wherein the .alpha.-alkylstyrene compound is .alpha.-methylstyrene.
- 6. The process according to claim 1, wherein the unsaturated nitrile is acrylonitrile.
Priority Claims (3)
Number |
Date |
Country |
Kind |
53-151807 |
Dec 1978 |
JPX |
|
53-151808 |
Dec 1978 |
JPX |
|
79-4310[U] |
Dec 1979 |
KRX |
|
Parent Case Info
This is a continuation-in-part application of our copending application Ser. No. 100,763 filed on Dec. 6, 1979, now abandoned.
US Referenced Citations (4)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
100763 |
Dec 1979 |
|