Low temperature sealing composition

BACKGROUND OF THE INVENTION
This invention relates to a low temperature sealing composition, and more particularly, to a low temperature sealing glass composition suitable for hermetically sealing ceramic packages for integrated circuits (ICs) and quartz resonators, and sealing display panels such as vacuum fluorescent displays (VFDs).
A sealing material for hermetically sealing packages for an IC or quartz resonators, and display panels are required to be sealable at a low temperature so as not to deteriorate the enclosed devices due to thermal effects. In addition, it is also necessary that the thermal coefficient of expansion (hereinafter, abbreviated to TCE) of the material is compatible with that of the ceramics or a display panel glass to be used. In particular, the IC packages should be sealed with the material that is high in mechanical strength besides meeting the aforementioned requirements. The material for sealing the IC package is also required to have superior insulating properties to avoid undesirable leak of signal currents. Further, the material for the IC package should have the least possible content of .alpha.-particle emitting impurities because the soft error often occurs when an IC chip such as DRAM and CCD is exposed to the .alpha.-particle.
Various sealing materials have been proposed that meet the above mentioned requirements. One of such materials is a PbO-B.sub.2 O.sub.3 glass of a low melting temperature. It has also been proposed to use the low melting temperature glass as an admixture with refractory fillers. For example, Japanese Patent Unexamined Publication 229738/1990 discloses a sealing material comprising PbO-B.sub.2 O.sub.3 glass powder, lead titanate ceramic powder and low expansion ceramic powder.
It is known about the PbO-B.sub.2 O.sub.3 glass that lowering content of B.sub.2 O.sub.3 generally lowers the glass transformation point resulting in a lower sealing temperature. However, sufficient content of B.sub.2 O.sub.3 is necessary to make the glass stable, which limites glass composition and makes it impossible to obtain sealing materials usable below 400.degree. C. The sealing temperature of 400.degree. C. or lower is thus difficult to be achieved. This means that the sealing material of the type described is not suitable for sealing packages for heat sensitive devices such as a highly integrated IC, or quartz resonators.
Several sealing materials have also been proposed which are sealable at the temperature of 400.degree. C. or lower. For example, Japanese Patent Publication No. 8060/1988 discloses a sealing material consisting of PbO-B.sub.2 O.sub.3 glass powder with Tl.sub.2 O contained therein. In addition, U.S. Pat. No. 4,743,302 discloses another sealing material comprising PbO-V.sub.2 O.sub.5 -TeO.sub.2 glass powder. However, both of these materials are unfavorable because of the following reasons. The sealing material disclosed in the Japanese Patent Publication No. 8060/1988 includes a highly toxic component, i.e., thallium carbonate in the raw material for the glass. Such a toxic material should be handled using special protective instrument. The sealing material disclosed in U.S. Pat. No. 4,743,302 is more likely to be crystallized and thus requires application of a large load to the package to be sealed.
SUMMARY OF THE INVENTION
Accordingly, a primary object of the present invention is to provide a low temperature sealing composition which meets the requirements for sealing material of IC packages or display panels and which is sealable at the temperature of 400.degree. C. or lower without application of load during sealing operation.
Another object of the present invention is to provide a low temperature sealing composition without use of highly toxic components.
A low temperature sealing composition according to the present invention is glass powder which essentially consists of 45.0 to 85.0 wt. % of PbO, 1.0 to 11.0 wt. % of B.sub.2 O.sub.3, 1.0 to 45.0 wt. % of Bi.sub.2 O.sub.3, 0.2 to 10.0 wt. % of Fe.sub.2 O.sub.3, 0 to 15.0 wt. % of ZnO, 0 to 5.0 wt. % of CuO, 0 to 5.0 wt. % of V.sub.2 O.sub.5, 0 to 3.0 wt. % of SnO.sub.2, 0 to 5.0 wt. % of SiO.sub.2 plus Al.sub.2 O.sub.3, 0 to 7.0 wt. % of BaO, 0 to 5.0 wt. % of TiO.sub.2, 0 to 5.0 wt. % of ZrO.sub.2 and 0 to 6.0 wt. % of F.sub.2.
In addition, a low temperature sealing glass composition according to the present invention comprises 45% to 80% by volume of glass powder and 20% to 55% by volume of refractory filler powder. The glass powder essentially consists of 45.0 to 85.0 wt. % of PbO, 1.0 to 11.0 wt. % of B.sub.2 O.sub.3, 1.0 to 45.0 wt. % of Bi.sub.2 O.sub.3, 0.2 to 10.0 wt. % of Fe.sub.2 O.sub.3, 0 to 15.0 wt. % of ZnO, 0 to 5.0 wt. % of CuO, 0 to 5.0 wt. % of V.sub.2 O.sub.5, 0 to 3.0 wt. % of SnO.sub.2, 0 to 5.0 wt. % of SiO.sub.2 plus Al.sub.2 O.sub.3, 0 to 7.0 wt. % of BaO, 0 to 5.0 wt. % of TiO.sub.2, 0 to 5.0 wt. % of ZrO.sub.2 and 0 to 6.0 wt. % of F.sub.2.
DESCRIPTION OF THE INVENTION
The present inventors have found that, as a result of tremendous studies and considerations, Fe.sub.2 O.sub.3 is considerably effective for stabilizing PbO-B.sub.2 O.sub.3 glass, in particular to PbO-B.sub.2 O.sub.3 glass with Bi.sub.2 O.sub.3 contained therein, and that the above mentioned objects can be achieved with the reduced content of B.sub.2 O.sub.3 by means of adding Fe.sub.2 O.sub.3 to the glass composition.
Briefly, the low temperature sealing composition according to the present invention is obtained by means of substituting Fe.sub.2 O.sub.3 for a part of B.sub.2 O.sub.3 of the PbO-B.sub.2 O.sub.3 glass, thereby reducing the content of B.sub.2 O.sub.3.
In the low temperature sealing composition according to the present invention, the ingredients of the glass powder are limited as set forth above because of the following reasons.
The content of PbO ranges from 45.0 to 85.0 wt. %, and preferably, from 50.0 to 83.0 wt. %. PbO content of lower than 45 wt. % increases the viscosity of the glass, impeding sufficient flow of the glass at a temperature of 400.degree. C. or lower. On the other hand, PbO content of higher than 85 wt. % causes crystallization upon sealing, which hinders flowing of the glass.
The content of B.sub.2 O.sub.3 ranges from 1.0 to 11.0 wt. %, and preferably, from 2.0 to 10.0 wt. %. B.sub.2 O.sub.3 content of lower than 1.0 wt. % makes the glass unstable to cause crystallization upon sealing. Such crystallization behavior also hinders flowing of the glass. B.sub.2 O.sub.3 content of higher than 11.0 wt. % increases the viscosity of the glass, impeding the glass from sufficient flow at a temperature of 400.degree. C. or lower.
Bi.sub.2 O.sub.3 has the effect of stabilizing the glass without increasing the viscosity and the content thereof is between 1.0 and 45.0 wt. %, and preferably, between 1.2 and 35.0 wt. %. The above mentioned effect cannot be achieved by Bi.sub.2 O.sub.3 of less than 1.0 wt. %. Bi.sub.2 O.sub.3 of more than 45 wt. % is responsible for the increased viscosity of the glass, inhibiting sufficient flow of the glass at a temperature of 400.degree. C. or lower.
Fe.sub.2 O.sub.3 has the significant effect for stabilizing the glass and the content thereof is within the range of 0.2 to 10.0 wt. %, and preferably, 0.2 to 9.0 wt. %. Fe.sub.2 O.sub.3 of less than 0.2 wt. % produces no effect of glass stabilization, so the glass significantly crystallizes upon heating. On the other hand, Fe.sub.2 O.sub.3 of more than 10.0 wt. % is responsible for the increased viscosity of the glass, inhibiting sufficient flow of the glass at a temperature of 400.degree. C. or lower.
The content of ZnO ranges from 0 to 15.0 wt. %, and preferably, from 0 to 13.0 wt. %. While ZnO contributes to stabilizing the glass as well as improving water-resistance thereof, ZnO of more than 15.0 wt. % causes crystallization of the glass to inhibit sufficient flow of it.
The content of CuO ranges from 0 to 5.0 wt. %, and preferably, 0 to 4.0 wt. %. While CuO is known to be the component capable of stabilizing the glass without increasing the viscosity, CuO content of higher than 5.0 wt. % results in precipitation of crystals upon sealing.
V.sub.2 O.sub.5 contributes to reducing surface tension of the glass and improves flowability thereof. The content of V.sub.2 O.sub.5 is between 0 and 5.0 wt. %, and preferably, between 0 and 3.0 wt. %. V.sub.2 O.sub.5 of more than 5.0 wt. % causes the glass to be crystallized significantly and makes the glass difficult to flow.
SnO.sub.2 favorably affects on stabilization of the glass and is contained therein ranging from 0 to 3.0 wt. %, and preferably, from 0 to 2.0 wt. %. SnO.sub.2 of more than 3.0 wt. % also causes the glass to be crystallized significantly and makes the glass difficult to flow.
The content of SiO.sub.2 and Al.sub.2 O.sub.3 in total ranges from 0 to 5.0 wt. %, and preferably, from 0 to 3.0 wt. %. SiO.sub.2 and Al.sub.2 O.sub.3 can be effectively used to avoid crystallization of the glass. However, the total content thereof exceeding 5.0 wt. % increases viscosity of the glass, which makes the glass to flow only at a temperature higher than 400.degree. C.
The content of BaO ranges from 0 to 7.0 wt. %, and preferably, 0 to 5.0 wt. %. While BaO has the effect of preventing the glass from being crystallized, its content of higher than 7.0 wt. % results in the increased viscosity of the glass. The higher viscosity is responsible for insufficient flow thereof at a temperature of 400.degree. C. or lower.
TiO.sub.2 exhibits the effect of stabilizing the glass when being contained in the amount between 0 to 5.0 wt. %, and preferably, between 0 and 1.0 wt. %. With the higher content of TiO.sub.2 than 5.0 wt. %, the glass shows significant tendency to be crystallized and to hardly flow.
The content of ZrO.sub.2 ranges from 0 to 5.0 wt. %, and preferably, from 0 to 1.0 wt. %. While ZrO.sub.2 has the effect of preventing the glass from being crystallized, the higher content thereof than 5.0 wt. % results in the increased viscosity of the glass and makes the glass to hardly flow at a temperature of 400.degree. C. or lower.
The content of F.sub.2 is between 0 and 6.0 wt. %. F.sub.2 serves to lower the sealing temperature of the glass of a Bi.sub.2 O.sub.3 -rich composition. However, the content higher than 6.0 wt. % strongly influences the stabilization of the glass to lead the glass to crystallization upon sealing. As a result, the glass is reduced in flowability.
Other components may be contained in the glass addition to those described above and the possible examples of these other components are: 5% or less, by weight, of Ag.sub.2 O, SrO, P.sub.2 O.sub.5, Co.sub.2 O.sub.3 and TeO.sub.2 ; 3% or less, by weight, of Mo.sub.2 O.sub.3, Rb.sub.2 O, Cs.sub.2 O, Nb.sub.2 O.sub.5, Ta.sub.2 O.sub.3, CeO.sub.2, NiO, Cr.sub.2 O.sub.3 and Sb.sub.2 O.sub.3 ; and rare earth oxides such as La.sub.2 O.sub.3. However, it should be avoided to add any components using highly toxic element such as Tl.sub.2 O.
The glass having the above mentioned composition is amorphous and no crystal will be precipitated upon sealing. With this glass composition, superior flowability can be achieved accordingly. In addition, the glass transformation point is low, i.e., 300.degree. C. or lower and the viscosity is low as well. The TCE of this glass at 30.degree. to 250.degree. C. is equal to or higher than 115.times.10.sup.-7 /.degree.C. Thus, this glass can be used for sealing, at a low temperature, materials having the relatively high coefficient of thermal expansion compatible with that of glass. It is, however, necessary to adjust the TCE of the glass when the latter is used for sealing IC packages or display panels manufactured with materials having various TCE. For example, the TCE of the glass is required to be lowered for sealing alumina (having the TCE of 70.times.10.sup.-7 /.degree.C.), aluminum nitride (having the TCE of 45.times.10.sup.-7 /.degree.C.), or the display glass panel (having the TCE of 85.times.10.sup.-7 /.degree.C.).
The TCE adaptable to seal IC packages or display panels can be obtained by means of adding of the refractory filler powder of an amount within the above mentioned range to the low temperature sealing glass composition. Suitable refractory filler powder may be: lead titanate based ceramic powder, willemite-based ceramic powder, cordierite ceramic powder, zircon-based ceramic powder, tin oxide based ceramic powder, .beta.-eucryptite ceramic powder, mullite ceramic powder or mixture-thereof. As other fillers than those exemplified above, silica glass, alumina, titanium oxide and niobium pentoxide are also applicable.
In the present invention, the mixing ratio of the glass powder and the filler powder is limited as set forth above because of the following reasons.
The composition with the glass component of less than 45 vol. % (i.e., with the refractory fillers of more than 55 vol. %) makes the mixture insufficient or poor in flowability, which makes the composition unsuitable as the sealing material used at a temperature of 400.degree. C. or lower. On the contrary, in the composition having the glass content of higher than 80 vol. % (i.e., the refractory filler content of lower than 20 vol. %), the TCE will be lowered only by an insufficient extent and is never compatible with materials of the IC packages and display panels.
Described hereinbelow is a method of manufacturing the low temperature sealing composition according to the present invention. Raw materials are blended and mixed to obtain a desired composition, thereafter, melted at 700.degree. to 1000.degree. C. for 1 or 2 hours, and then formed into a plate. The plate is then ground to powder in a ball-mill or the like. The powder is then classified according to predetermined particle sizes to obtain glass powder of a desired size. If desired, the glass powder obtained in this manner may be mixed with refractory filler powder at a specific ratio.
The foregoing features of the low temperature sealing composition according to the present invention will be more readily apparent in the context of a specifically delineated set of examples.

EXAMPLE 1
Table 1 shows effects of addition of Fe.sub.2 O.sub.3 to PbO-B.sub.2 O.sub.3 glass. A sample No. 1a is a typical PbO-B.sub.2 O.sub.3 glass while sample No. 1b is PbO-B.sub.2 O.sub.3 glass containing a reduced amount of B.sub.2 O.sub.3 by 3.7 wt. % less than that sample No. 1a. A sample No. 1c is a low temperature sealing composition according to the present invention, in which 1.5 wt. % of Fe.sub.2 O.sub.3 is added to the sample No. 1b.
TABLE 1__________________________________________________________________________(wt %) Sample No.Composition 1a 1b 1c__________________________________________________________________________PbO 77.3 77.3 (80.3) 77.3 (79.0)B.sub.2 O.sub.3 10.2 6.5 (6.8) 6.5 (6.7)Bi.sub.2 O.sub.3 7.7 7.7 (8.0) 7.7 (7.9)Fe.sub.2 O.sub.3 -- -- (--) 1.5 (1.5)ZnO 2.8 2.8 (2.9) 2.8 (2.9)SiO.sub.2 1.0 1.0 (1.0) 1.0 (1.0)Al.sub.2 O.sub.3 0.5 0.5 (0.5) 0.5 (0.5)BaO 0.5 0.5 (0.5) 0.5 (0.5)Sum 100 wt % 96.3 wt % (100 wt %) 97.8 wt % (100 wt %)Glass Transformation 310 261 272Point (.degree.C.)Flowability OK no good goodStability good no good good__________________________________________________________________________
The samples being set forth in Table 1 were prepared through the following procedures.
The raw materials were blended and mixed into batches to obtain the compositions indicated in Table 1. Each composition was melted in a platinum crucible at 900.degree. C. for 1 hours and then formed into a thin plate. The plate was ground to powder and passed through a 250-mesh stainless steel screen to obtain the samples having the average particle diameter of 4 .mu.m.
As apparent from Table 1, sample No. 1b with the lower content of B.sub.2 O.sub.3 has the glass transformation point of 261.degree. C., which is lower by 49.degree. C. than that of the sample No. 1a. However, sample 1b was poor or not good in flowability and stability. On the contrary, sample No. 1c with the addition of Fe.sub.2 O.sub.3 exhibited the lower glass transformation point of 272.degree. C. and good stability. The flowability of sample No. 1c was also good and much superior to that of sample No. 1a.
These facts indicate that addition of Fe.sub.2 O.sub.3 with reduction of B203 in the PbO-B.sub.2 O.sub.3 glass insures the good and excellent flowability and stability of the glass, thereby to provide an excellent sealing composition sealable at a low temperature.
The glass transformation point of each sample was determined according to the differential thermal analysis (DTA) while the flowability was determined through the following procedures. Buttons were formed of sample glass powder, respectively. Each button had of 20 mm in outer diameter and 5 mm in thickness. The buttons were heated at 380.degree. C. for 10 minutes. One having resultant diameter larger than 23 mm was considered to be fine and that of between 20 and 23 mm was considered to be fair. In addition, one having the resultant diameter smaller than 20 mm was considered to be failure. The considerations of fine, fair and failure are indicated by "good," "OK," and "no good," respectively, in Table 1 as the evaluation results on the flowability and the stability for each sample. It should be understood that "good" is meant to be superior to "OK."
The stability was determined through the visual inspection of surfaces of the samples after being subjected to the flowability test. According to the results of the visual inspection, the sample where no crystal was found was considered to be fine ("good") while if any crystals were found in the sample, the sample was considered as failure ("no good").
EXAMPLE 2
Table 2 and Table 3 show various samples of the low temperature sealing composition according to the present invention.
TABLE 2______________________________________(wt %) A B C D E F______________________________________PbO 83.0 77.0 82.0 74.2 78.7 75.1B.sub.2 O.sub.3 9.2 8.2 4.8 2.8 7.9 7.9Bi.sub.2 O.sub.3 3.0 10.3 7.2 9.5 1.2 7.3Fe.sub.2 O.sub.3 3.8 0.5 1.5 8.5 3.7 2.1ZnO -- 3.0 4.0 4.0 6.2 2.7CuO -- -- -- -- 1.0 --V.sub.2 O.sub.5 -- -- -- -- -- 1.0SnO.sub.2 -- -- -- 0.5 -- --SiO.sub.2 1.0 1.0 0.5 -- 1.3 0.9Al.sub.2 O.sub.3 -- -- -- 0.5 -- --BaO -- -- -- -- -- --TiO.sub.2 -- -- -- -- -- --ZrO.sub.2 -- -- -- -- -- --F.sub.2 -- -- -- -- -- 3.0Glass Trans- 295 290 287 280 285 246formationPoint (.degree.C.)TCE 115 122 124 124 125 132(.times. 10.sup.-7 /.degree.C.)Flowability good good good good good good______________________________________
TABLE 3__________________________________________________________________________(wt %) G H I J K L M N O P Q__________________________________________________________________________PbO 81.3 67.2 80.3 52.0 61.5 78.0 69.8 51.4 65.5 53.6 66.5B.sub.2 O.sub.3 4.5 5.5 9.1 2.5 7.5 6.5 5.5 3.6 6.0 5.2 6.4Bi.sub.2 O.sub.3 7.2 11.0 5.1 33.2 20.5 8.5 15.0 34.0 20.0 31.8 15.8Fe.sub.2 O.sub.3 0.5 1.3 0.3 8.4 3.5 1.5 1.5 1.0 1.0 6.7 3.0ZnO 6.0 12.0 -- 3.6 3.0 4.5 2.7 5.0 4.0 -- 4.6CuO -- -- -- -- -- -- 0.5 1.5 -- 0.7 2.2V.sub.2 O.sub.5 -- -- -- -- -- -- 1.0 -- -- -- 0.5SnO.sub.2 -- -- -- -- -- -- -- -- -- -- --SiO.sub.2 0.5 1.0 -- 0.3 0.5 0.5 1.0 0.5 0.5 2.0 --Al.sub.2 O.sub.3 -- -- 0.5 -- -- -- -- -- -- -- 0.5BaO -- 2.0 4.2 -- -- -- -- -- -- -- --TiO.sub.2 -- -- 0.5 -- -- -- -- -- -- -- --ZrO.sub.2 -- -- -- -- 0.5 -- -- -- -- -- --F.sub.2 -- -- -- -- 3.0 0.5 3.0 3.0 3.0 -- 0.5Glass Transformation 280 273 289 270 248 278 244 249 247 264 254Point (.degree.C.)TCE (.times. 10.sup.-7 /.degree.C.) 124 122 115 129 136 123 131 133 133 132 138Flowability good good good good good good good good good good good__________________________________________________________________________
As apparent from Table 2 and Table 3, samples A through Q has the glass transformation point ranging from 244.degree. to 295.degree. C. and the TCE ranging from 115 to 138.times.10.sup.-7 /.degree.C. All samples exhibited excellent or good flowability.
The samples indicated in Table 2 and Table 3 were prepared in the same manner as in Example 1.
EXAMPLE 3
Table 4 through Table 8 show various samples (samples Nos. 1 to 31) of the low temperature sealing composition for IC packages prepared by mixing refractory filler powder with each of the sample glass powder in Table 2 and Table 3.
TABLE 4______________________________________ 1 2 3 4 5 6______________________________________Mixing Ratio (vol %)glass powder (A) (B) (C) (D) (E) (F)(Table 2) 75 60 60 60 60 60refractory fillerpowderlead titanate 5 5 -- -- -- 10basedceramic powderwillemite based -- 25 30 35 25 20ceramic powdercordierite -- -- -- -- 10 --ceramic powderzircon based -- 10 -- 5 -- --ceramic powdertin oxide based -- -- 10 -- -- 10ceramic powder.beta.-eucryptite 20 -- -- -- -- --ceramic powdermullite -- -- -- -- 5 --ceramic powderSealing Temperature 400 390 400 380 390 360(.degree.C.)Bending Strength 590 640 650 630 660 610(kg/cm.sup.2)Volume Resistivity 14.4 14.8 13.8 14.2 14.6 13.2(150.degree. C., log .OMEGA. .multidot. cm).alpha.-particle Emission 0.12 0.11 0.25 0.13 0.15 0.25Quantity (count/cm.sup. 2 .multidot. hr)TCE 60 69 73 68 69 68(.times. 10.sup.-7 /.degree.C.)______________________________________
TABLE 5______________________________________ 7 8 9 10 11 12______________________________________Mixing Ratio (vol %)glass powder (G) (H) (I) (J) (K) (L)(Table 3) 75 60 60 60 50 55refractory fillerpowderlead titanate 20 -- -- -- -- --basedceramic powderwillemite based -- 20 10 30 -- --ceramic powdercordierite 5 10 10 -- 35 30ceramic powderzircon based -- 10 20 -- 15 15ceramic powdertin oxide based -- -- -- 10 -- --ceramic powder.beta.-eucryptite -- -- -- -- -- --ceramic powdermullite -- -- -- -- -- --ceramic powderSealing Temperature 370 380 400 370 370 390(.degree.C.)Bending Strength 580 610 630 610 570 670(kg/cm.sup.2)Volume Resistivity 14.3 13.2 12.8 13.1 12.8 13.4(150.degree. C., log .OMEGA. .multidot. cm).alpha.-particle Emission 0.12 0.17 0.12 0.15 0.16 0.09Quantity (count/cm.sup.2 .multidot. hr)TCE 65 67 68 72 65 69(.times. 10.sup.-7 /.degree.C.)______________________________________
TABLE 6______________________________________ 13 14 15 16 17______________________________________Mixing Ratio (vol %)glass powder (M) (N) (O) (P) (Q)(Table 3) 60 60 60 53 55refractory fillerpowderlead titanate 5 -- 10 -- --basedceramic powderwillemite based 25 -- 20 40 --ceramic powdercordierite -- 30 -- -- 30ceramic powderzircon based 10 10 10 -- 15ceramic powdertin oxide based -- -- 7 --ceramic powder.beta.-eucryptite -- -- -- -- --ceramic powdermullite -- -- -- -- --ceramic powderSealing Temperature 360 360 360 380 380(.degree.C.)Bending Strength 620 650 620 600 620(kg/cm.sup.2)Volume Resistivity 14.5 15.2 14.6 15.0 13.3(150.degree. C., log .OMEGA. .multidot. cm).alpha.-particle Emission 0.20 0.22 0.10 0.15 0.25Quantity (count/cm.sup.2 .multidot. hr)TCE 64 64 67 67 67(.times. 10.sup.-7 /.degree.C.)______________________________________
TABLE 7______________________________________ 18 19 20 21 22 23 24______________________________________Mixing Ratio(vol %)glass powder (A) (C) (F) (G) (I) (K) (L)(Tables 2 & 3) 55 55 55 50 55 55 50refractory fillerpowderlead titanate 10 15 20 15 20 20 20basedceramic powderwillemite based 15 30 25 25 -- 15 20ceramic powdercordierite 20 -- -- 10 20 -- 10ceramic powderzircon based -- -- -- -- 5 10 --ceramic powdertin oxide based -- -- -- -- -- -- --ceramic powder.beta.-eucryptite -- -- -- -- -- -- --ceramic powdermullite -- -- -- -- -- -- --ceramic powderSealing 400 400 380 400 400 380 400Temperature(.degree.C.)Bending 680 640 650 670 660 610 650Strength(kg/cm.sup.2)Volume 13.8 14.8 13.8 13.6 13.6 12.9 13.7Resistivity(150.degree. C.,log .OMEGA. .multidot. cm).alpha.-particle Emission 0.12 0.11 0.13 0.13 0.11 0.12 0.19Quantity(count/cm.sup.2 .multidot. hr)TCE 51 55 55 52 55 55 49(.times. 10.sup.-7 /.degree.C.)______________________________________
TABLE 8______________________________________ 25 26 27 28 29 30 31______________________________________Mixing Ratio(vol %)glass powder (B) (D) (E) (G) (H) (I) (L)(Tables 2 & 3) 65 70 65 65 65 65 65refractory fillerpowderlead titanate 10 15 5 10 5 20 10basedceramic powderwillemite based -- -- -- 15 -- -- --ceramic powdercordierite -- -- 10 -- 20 -- --ceramic powderzircon based 25 -- -- 10 10 15 25ceramic powdertin oxide based -- -- 20 -- -- -- --ceramic powder.beta.-eucryptite -- -- -- -- -- -- --ceramic powdermullite -- 15 -- -- -- -- --ceramic powderSealing 390 380 380 380 370 380 380Temperature(.degree.C.)Volume 14.1 14.3 14.1 13.5 14.2 14.5 14.3Resistivity(150.degree. C.,log .OMEGA. .multidot. cm)TCE 74 78 73 76 74 73 74(.times. 10.sup.-7 /.degree.C.)______________________________________
As apparent from Table 4 through Table 7, samples Nos. 1 through 24 have satisfactory properties: the sealing temperature ranging from 360.degree. to 400.degree. C., the bending strength ranging from 570 to 680 kg/cm.sup.2, the volume resistivity ranging from 12.8 to 15.2 .OMEGA..cm and the amount of .alpha.-particle emission ranging from 0.09 to 0.25 count/cm.sup.2.hr. The TCE of the samples Nos. 1 through 17 was between 60 and 73.times.10.sup.-7 /.degree.C. and that of the samples Nos. 18 through 24 was between 49 and 55.times.10.sup.-7 /.degree.C. The TCE of these two groups are approximate to those of alumina (70.times.10.sup.-7 /.degree.C.) and aluminium nitride (45.times.10.sup.-7 /.degree.C.), respectively.
As apparent from Table 8, samples Nos. 25 to 31 have a desired sealing temperature ranging from 370.degree. to 380.degree. C. and a high volume resistivity ranging from 13.5 to 14.5 .OMEGA..cm. The TCE of these samples is in the range from 73 to 76.times.10.sup.-7 /.degree.C., which is approximate to that of the display glass panel (85.times.10.sup.-7 /.degree.C.).
These facts indicate that the low temperature sealing composition according to the present invention meets the requirements for the sealing material used to seal IC packages or display panels. In particular, the low temperature sealing composition according to the present invention is sealable at a temperature of 400.degree. C. or lower and the TCE thereof can be adjusted to be compatible with that of alumina, aluminium nitride or display glass panels.
The TCE was measured by a dilatometer. The sealing temperature was defined as the temperature at which a button of 20 mm in outer diameter and 5 mm in thick formed of each sample was heated and deformed to 21 mm or larger in diameter. The bending strength was measured according to the three-load method on each sample sintered and formed to square pillars of 10.times.10.times.50 mm. The volume resistivity was measured at 150.degree. C. using a megohm meter, and the .alpha.-particle emission was measured using a ZnS scintillation counter.
The refractory filler powder indicated in Table 4 through Table 8 were prepared through the following procedures.
Lead titanate based ceramic powder was prepared by blending raw material powder in the ratio of 65 wt. % of PbO, 30 wt. % of TiO.sub.2 and 5 wt. % of CaO. The blend was mixed and sintered at 1100.degree. C. for 5 hours and the resultant sintered body was then ground into powder with alumina balls. The powder was sieved using a 350-mesh stainless steel screen to obtain powder having the average particle diameter of 5 .mu.m.
Willemite based ceramic powder was prepared by blending raw materials in the ratio of 70 wt. % of ZnO, 25 wt. % of SiO.sub.2 and 5 wt. % of Al.sub.2 O.sub.3. The blend was mixed and sintered at 1440.degree. C. for 15 hours. The sintered body was then ground into powder and sieved using a 250-mesh stainless steel screen to obtain a desired ceramic powder.
Cordierite ceramic powder was prepared by blending powder of magnesium oxide, aluminium oxide and high purity quartz sand in the ratio of 2MgO.2Al.sub.2 O.sub.3.5SiO.sub.2. The blend was mixed and sintered at 1400.degree. C. for 10 hours. The sintered body was then ground into powder and sieved using a 250-mesh stainless steel screen to obtain the powder used.
Zircon based ceramic powder was prepared through the following processes. Natural zircon sand was subjected to soda decomposition and the resultant product was dissolved in hydrochloric acid, following which concentration and crystallization were repeated, whereby obtaining zirconium oxychloride with extremely low content of .alpha.-particle emitting substances, i.e., uranium (U) and thorium (Th). The zirconium oxychloride was neutralized with an alkali. The resultant product was then heated, whereby obtaining purified zirconium oxide (ZrO.sub.2). The purified zirconium oxide was mixed with high purity silica powder and ferric oxide to form a ratio of 66 wt. % ZrO.sub.2, 32 wt. % SiO.sub.2 and 2 wt. % Fe.sub.2 O.sub.3. The mixture was sintered at 1400.degree. C. for 16 hours. The resultant sintered body was ground into powder and sieved using a 250-mesh stainless steel screen to obtain the powder used.
Tin oxide based ceramic powder was prepared by blending raw powder in the ratio of 93 wt. % of SnO.sub.2, 2 wt. % of TiO.sub.2 and 5 wt. % of MnO. The blend was mixed and sintered at 1400.degree. C. for 16 hours. The sintered body was then ground into powder and sieved using a 250-mesh stainless steel screen to obtain the powder used.
Beta-eucryptite ceramic powder was obtained by mixing lithium carbonate, alumina and high purity quartz sand into the composition of Li.sub.2 O.Al.sub.2 O.sub.3.2SiO.sub.2. The mixture was sintered at 1250.degree. C. for 5 hours. The sintered body was then ground into powder and sieved using a 250-mesh stainless steel screen to obtain the powder used.
Mullite ceramic powder was prepared by blending aluminium oxide and high purity quartz sand into the composition of 3Al.sub.2 O.sub.3 .2SiO.sub.2. The blend was mixed and sintered at 1600.degree. C. for 10 hours. The sintered body was then ground into powder and sieved using a 250-mesh stainless steel screen to obtain the powder as used.
As mentioned above, the low temperature sealing composition according to the present invention fulfills various properties and features required for the sealing materials to seal IC packages or display panels. The present composition is particularly suitable as the sealing material for sealing ceramic or glass containers containing temperature sensitive devices because it is sealable at a temperature of 400.degree. C. or lower without load. In addition, the present sealing composition is readily produced from raw materials of the glass containing no highly toxic materials, which otherwise should be handled using special protective instrument.

Number	Name	Date
4310357	Matsuura et al.	Jan 1982
4365021	Pirooz	Dec 1982
4696909	Weaver	Sep 1987
4704370	Seki et al.	Nov 1987
4743302	Dumesail et al.	May 1988
5281561	Dumesnil et al.	Jan 1994

Number	Date	Country
8060	Feb 1988	JPX
229738	Sep 1990	JPX

Low temperature sealing composition

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (6)

Foreign Referenced Citations (2)