20210324676
Insulated glazing units, spacers for insulated glazing units, and methods of making insulated glazing units are provided herein.
Conventional architectural window glass is highly thermally emissive. Solar energy easily passes through such glass. In order to reduce the passage of solar energy, low emissivity coatings are applied onto the glass. Low emissivity coatings act as thermal barriers that decrease the emission of radiant infrared (IR) energy, particularly thermal infrared energy. The lower the emissivity, the better the coating is in blocking the emission of thermal IR energy.
Heat transfer of an insulating glazing unit (IGU) may be controlled by a variety of factors, including the design of the spacer frame between panels (lites, panes, etc.) in an IGU and the structure and composition of the panels. Numerous IGU and IGU spacer structures are described, such as those of U.S. Pat. Nos. 3,981,111, 5,377,473, 5,705,010, 6,823,644, 8,586,193, 8,789,343, 9,127,502, 9,546,513, and 9,617,781, exhibiting great variation in heat transfer resistance, complexity, and complexity of manufacturing.
Heat transfer in IGUs may be measured in a number of ways. The overall heat transfer coefficient (U factor) is a measure of heat loss through the window. The lower the U factor, the lower the heat transfer through the window, i.e. the higher the insulating level of the window. The U factor is specific to a particular IGU. Resistance or Res-value (e.g., hr·° F.·in/BTU) is a measurement of edge resistance or heat loss through a unit length of an edge portion of an IGU, e.g., determined by the spacer composition and structure, and is independent of the overall size of the IGU.
Edge assemblies and IGUs often require multiple manufacturing steps and human intervention. As such, an IGU and a spacer or spacer frame for an IGU that has superior heat transfer profile, e.g., Res-value, and which can be simply manufactured with minimal human intervention is most desirable.
In one aspect of the invention, an insulating glazing unit is provided. The insulating glazing unit comprises: a first panel and a second panel, the first panel having a first major surface (surface 1) and an opposite second major surface (surface 2) and marginal edges, the second panel having a first major surface (surface 3) and an opposite second major surface (surface 4) and marginal edges; a metal spacer formed from a single metal sheet, having an internal side and an opposite external side, affixed with adhesive to marginal portions of surface 2 of the first panel and surface 3 of the second panel and supporting the first and second panel in a spaced-apart configuration, with the internal side of the spacer, surface 2 of the first panel, and surface 3 of the second panel defining a sealed compartment, the spacer comprising: a first wall on a first lateral side of the spacer adjacent to surface 2 of the first panel, having a major planar portion and comprising a first lip extending from an inward side of the first wall toward surface 3 of the second panel; a second wall on a second lateral side of the spacer opposite the first wall and adjacent to surface 3 of the second panel, having a major planar portion and comprising a second lip extending from an inward side of the second wall toward surface 2 of the first panel, wherein the first and second lips define a gap opening into the compartment, and a central portion extending from a marginal side of the first wall opposite the first lip to a marginal side of the second wall opposite the second lip, comprising two or more longitudinal ridges with a first lateral valley portion between and connecting the first wall and an adjacent ridge and defining a first lateral valley on the internal side of the spacer, a second lateral valley portion between and connecting the second wall and an adjacent ridge and defining a second lateral valley on the internal side of the spacer, and one or more central valley portions between and connecting longitudinal ridges and defining one or more central valleys on the internal side of the spacer, each ridge comprising a plurality of walls comprising parallel portions parallel to each other, with peak portions connecting adjacent walls; and desiccant disposed in a central valley.
In another aspect, a spacer for an insulated glazing unit is provided. The spacer comprises a single metal sheet formed into a structure comprising: an elongate corrugated portion comprising two or more longitudinal ridges; a first elongate lateral wall, having a major planar portion and extending from a first major edge of the corrugated portion; a second lateral elongate wall, having a major planar portion and extending from a second major edge of the corrugated portion in the same direction as the first elongate wall; a first lip extending from the first elongate lateral wall opposite the corrugated portion and extending towards the second elongate lateral wall; and a second lip extending from the second elongate lateral wall opposite the corrugated portion and extending towards the first elongate lateral wall and defining a gap between the first lip and the second lip; the corrugated portion comprising two or more longitudinal ridges, with a first lateral valley portion between and connecting the first elongate lateral wall and an adjacent ridge and defining a first lateral valley, a second lateral valley portion between and connecting the second elongate lateral wall and an adjacent ridge and defining a second lateral valley, and one or more central valley portions between and connecting adjacent longitudinal ridges and defining one or more central valleys, each ridge comprising a plurality of walls, with peak portions connecting adjacent walls.
In another aspect, a spacer is provided for use in an insulated glazing unit. The spacer is formed from a single sheet of stainless steel or tin-plated steel, and comprises lateral walls connected by a central portion comprising from two to four longitudinal ridges, wherein the width of the spacer is no more than 35% the linear width of the metal folded to form the spacer, and wherein, when assembled in an insulating glazing unit, has a Res-value ((in-hr-° F.)/BTU) of at least 190, 195, 200, 205, 210, or 215, optionally, as defined by the inverse of the flow of the (BTU/hr·° F.·in.) that occurs from the interface of the glass and adhesive layer at the inside side of the unit to the interface of the glass and adhesive layer of the outside of the unit per unit increment of temperature (1° F.), per unit length of edge assembly perimeter (inch), and wherein the glass/adhesive interfaces are assumed to be isothermal. Also provided is an insulated glazing unit comprising a first panel and a second panel, the first panel having a first major surface (surface 1) and an opposite second major surface (surface 2) and marginal edges, the second panel having a first major surface (surface 3) and an opposite second major surface (surface 4) and marginal edges; and the spacer, having an internal side and an opposite external side, affixed with adhesive to marginal portions of surface 2 of the first panel and surface 3 of the second panel and supporting the first and second panel in a spaced-apart configuration, with the internal side of the spacer, surface 2 of the first panel, and surface 3 of the second panel defining a sealed compartment.
In a further aspect, a method of preparing an insulating glazing unit is provided. The method comprises affixing a spacer as described in the previous paragraphs between a first glazing panel and a second glazing panel with the spacer affixed with a adhesive to marginal portions of a major surface of the first panel and the second panel, holding the first and second panels in a spaced-apart configuration, thereby defining a compartment.
In yet another aspect, a method of preparing a spacer for an insulated glazing unit is provided. The method comprises roll-forming a metal sheet into an elongate unit comprising: an elongate corrugated portion comprising two or more longitudinal ridges; a first elongate lateral wall, having a major planar portion and extending from a first major edge of the corrugated portion; a second lateral elongate wall, having a major planar portion and extending from a second major edge of the corrugated portion in the same direction as the first elongate wall; a first lip extending from the first elongate lateral wall opposite the corrugated portion and extending towards the second elongate lateral wall; and a second lip extending from the second elongate lateral wall opposite the corrugated portion and extending towards the first elongate lateral wall and defining a gap between the first lip and the second lip; the corrugated portion comprising two or more longitudinal ridges, with a first lateral valley portion between and connecting the first elongate lateral wall and an adjacent ridge and defining a first lateral valley, a second lateral valley portion between and connecting the second elongate lateral wall and an adjacent ridge and defining a second lateral valley, and one or more central valley portions between and connecting adjacent longitudinal ridges and defining one or more central valleys, each ridge comprising a plurality of walls, with peak portions connecting adjacent walls.
The present invention is also directed to the following clauses.
Clause 1: An insulating glazing unit comprising:
a first panel and a second panel, the first panel having a first major surface (surface 1) and an opposite second major surface (surface 2) and marginal edges, the second panel having a first major surface (surface 3) and an opposite second major surface (surface 4) and marginal edges; a metal spacer formed from a single metal sheet, having an internal side and an opposite external side, affixed with adhesive to marginal portions of surface 2 of the first panel and surface 3 of the second panel and supporting the first and second panel in a spaced-apart configuration, with the internal side of the spacer, surface 2 of the first panel, and surface 3 of the second panel defining a sealed compartment, wherein the metal spacer comprises:
a first wall on a first lateral side of the metal spacer adjacent to surface 2 of the first panel, having a major planar portion and comprising a first lip extending from an inward side of the first wall toward surface 3 of the second panel;
a second wall on a second lateral side of the spacer opposite the first wall and adjacent to surface 3 of the second panel, having a major planar portion and comprising a second lip extending from an inward side of the second wall toward surface 2 of the first panel, wherein the first and second lips define a gap opening into the compartment, and
a central portion extending from a marginal side of the first wall opposite the first lip to a marginal side of the second wall opposite the second lip, comprising two or more longitudinal ridges with a first lateral valley portion between and connecting the first wall and an adjacent ridge and defining a first lateral valley on the internal side of the spacer, a second lateral valley portion between and connecting the second wall and an adjacent ridge and defining a second lateral valley on the internal side of the spacer, and one or more central valley portions between and connecting longitudinal ridges and defining one or more central valleys on the internal side of the spacer, each ridge comprising a plurality of walls comprising parallel portions parallel to each other, with peak portions connecting adjacent walls; and desiccant disposed in a central valley.
Clause 2: The insulating glazing unit of clause 1, wherein the first and second lateral valleys are free of desiccant.
Clause 3: The insulating glazing unit of clause 1 or 2, wherein the first wall is substantially parallel to the first panel and the second wall is parallel to or substantially parallel to the second panel.
Clause 4: The insulating glazing unit of any one of clauses 1-3, wherein the height of the ridges ranges from 50% to 80% of the height of the spacer.
Clause 5: The insulating glazing unit of any one of clauses 1-4, wherein the planar portions of the walls of the ridges are parallel to the planar portion of the first wall, the second wall, or both the first and second walls.
Clause 6: The insulating glazing unit of any one of clauses 1-5, wherein one or more of the peak portions and/or one or more of the valley portions comprises a flat portion perpendicular to, or substantially perpendicular to the walls of the ridges.
Clause 7: The insulating glazing unit of any one of clauses 1-6, further comprising a lateral fold extending from the first wall to the first lateral valley and/or from the second wall to the second lateral valley at an angle of less than 90° from a plane of the planar portion of the first and/or second wall.
Clause 8: The insulating glazing unit of clause 7, wherein the angle of the lateral fold or folds ranges from 5° to 85°, from 30° to 60°, e.g., 30°, 40°, 45°, 50°, or 60°, from a plane of the planar portion of first and/or second wall.
Clause 9: The insulating glazing unit of any one of clauses 1-8, wherein the adhesive between surface 2 of the first panel and the first wall adjacent to the first panel covers at least a portion of the external side of the first lateral valley portion, and the adhesive between surface 3 of the second panel and the second wall adjacent to the second panel covers at least a portion of the external side of the second lateral valley portion, and wherein a remainder of the external side of the spacer is in contact with a gas or an insulating material.
Clause 10: The insulating glazing unit of any one of clauses 1-9, wherein the first panel and the second panel are transparent.
Clause 11: The insulating glazing unit of any one of clauses 1-10, wherein one or both of the first panel and the second panel comprise low-emissivity glass.
Clause 12: The insulating glazing unit of any one of clauses 1-11, wherein the spacer has a Res-value ((in-hr-° F.)/BTU) of at least 190, 195, 200, 205, 210, or 215, optionally, as defined by the inverse of the flow of the (BTU/hr·° F.·in.) that occurs from the interface of the glass and adhesive layer at the inside side of the unit to the interface of the glass and adhesive layer of the outside of the unit per unit increment of temperature (1° F.), per unit length of edge assembly perimeter (inch), and wherein the glass/adhesive interfaces are assumed to be isothermal.
Clause 13: The insulating glass unit of any one of clauses 1-12, wherein the spacer comprises stainless steel or tin-plated steel.
Clause 14: The insulating glazing unit of any one of clauses 1-13, wherein the width of the spacer is no more than 35% the linear width of the metal folded to form the spacer.
Clause 15: The insulating glazing unit of any one of clauses 1-14, wherein the spacer comprises three longitudinal ridges.
Clause 16: The insulating glazing unit of any one of clauses 1-15, wherein the spacer forms a contiguous frame surrounding, and forming an airtight seal about the compartment.
Clause 17: The insulating glazing unit of clause 16, wherein the compartment is filled with an inert gas, such as argon.
Clause 18: The insulating glazing unit of any one of clauses 1-17, wherein the adhesive further extends between the first and second panels below the valley portions and into a space formed between the adjacent walls and the connecting peak portions of the ridges.
Clause 19: The insulating glazing unit of any one of clauses 1-17, wherein a barrier member extends across the valley portions of the spacer and adhesive further extends between the first and second panels below the valley portions and barrier member such that adhesive does not enter into a space formed between the adjacent walls and the connecting peak portions of the ridges.
Clause 20: The insulating glazing unit of any one of clauses 1-19, wherein the adhesive comprises a polyisobutylene portion and a silicone portion.
Clause 21: A spacer for an insulated glazing unit, comprising a single metal sheet formed into a structure comprising:
an elongate corrugated portion comprising two or more longitudinal ridges;
a first elongate lateral wall, having a major planar portion and extending from a first major edge of the corrugated portion;
a second lateral elongate wall, having a major planar portion and extending from a second major edge of the corrugated portion in the same direction as the first elongate wall;
a first lip extending from the first elongate lateral wall opposite the corrugated portion and extending towards the second elongate lateral wall; and
a second lip extending from the second elongate lateral wall opposite the corrugated portion and extending towards the first elongate lateral wall and defining a gap between the first lip and the second lip;
the corrugated portion comprising two or more longitudinal ridges, with a first lateral valley portion between and connecting the first elongate lateral wall and an adjacent ridge and defining a first lateral valley, a second lateral valley portion between and connecting the second elongate lateral wall and an adjacent ridge and defining a second lateral valley, and one or more central valley portions between and connecting adjacent longitudinal ridges and defining one or more central valleys, each ridge comprising a plurality of walls, with peak portions connecting adjacent walls.
Clause 22: The spacer of clause 21, wherein a major planar portion of the first elongate lateral wall is parallel to a major planar portion of the second elongate lateral wall.
Clause 23: The spacer of clause 21 or 22, wherein the longitudinal ridges extend from 50% to 80% of the height of the spacer.
Clause 24: The spacer of any one of clauses 21-23, wherein the plurality of walls of the ridges are substantially parallel to the first elongate lateral wall and/or the second elongate lateral wall.
Clause 25: The spacer of any one of clauses 21-24, wherein one or more of the peaks and/or one or more of the valleys comprises a flat portion substantially perpendicular to the walls of the ridges.
Clause 26: The spacer of any one of clauses 21-25, further comprising a lateral fold extending from the first wall to the first lateral valley and/or from the second wall to the second lateral valley at an angle of less than 90° from the plane of major planar portions of the first and/or second elongate lateral wall.
Clause 27: The spacer of clause 26, wherein the angle of the lateral fold or folds ranges from 5° to 85°, from 30° to 60°, e.g., 30°, 40°, 45°, 50°, or 60°, from the plane of major planar portions of the first and/or second elongate lateral wall.
Clause 28: The spacer of any one of clauses 21-27, wherein, when assembled in an insulating glazing unit, has a Res-value ((in-hr-° F.)/BTU) of at least 190, 195, 200, 205, 210, or 215, optionally, as defined by the inverse of the flow of the (BTU/hr·° F.·in.) that occurs from the interface of the glass and adhesive layer at the inside side of the unit to the interface of the glass and adhesive layer of the outside of the unit per unit increment of temperature (1° F.), per unit length of edge assembly perimeter (inch), and wherein the glass/adhesive interfaces are assumed to be isothermal.
Clause 29: The spacer of any one of clauses 21-28, comprising stainless steel or tin-plated steel.
Clause 30: The spacer of any one of clauses 21-29, wherein the spacer comprises three longitudinal ridges.
Clause 31: The spacer of any one of clauses 21-30, comprising desiccant disposed in a central valley, wherein the first and second lateral valleys are free of desiccant.
Clause 32: The spacer of any one of clauses 21-31, wherein the width of the spacer is no more than 35% the linear width of the metal folded to form the spacer.
Clause 33: The spacer of any one of clauses 21-32, wherein the adhesive further extends between the first and second panels below the valley portions and into a space formed between the adjacent walls and the connecting peak portions of the ridges.
Clause 34: The spacer of any one of clauses 21-32, wherein a barrier member extends across the valley portions of the spacer and adhesive further extends between the first and second panels below the valley portions and barrier member such that adhesive does not enter into a space formed between the adjacent walls and the connecting peak portions of the ridges.
Clause 35: A method of preparing an insulating glazing unit, comprising affixing a spacer according to any one of clauses 21-34 between a first glazing panel and a second glazing panel with the spacer affixed with a adhesive to marginal portions of a major surface of the first panel and the second panel, holding the first and second panels in a spaced-apart configuration, thereby defining a compartment.
Clause 36: The method of clause 35, wherein the compartment is air-tight.
Clause 37: The method of clause 36, wherein the compartment is filled with an inert gas or a mixture of air and an inert gas.
Clause 38: The method of clause 37, wherein the compartment is filled with at least 90% argon.
Clause 39: The method of any one of clauses 37-38, further comprising depositing a desiccant to one or more of the central valleys within the compartment, and leaving the lateral valleys of the compartment free of desiccant.
Clause 40: The method of any one of clauses 35-39, wherein the first panel and the second panel are transparent.
Clause 41: The method of any one of clauses 35-40, wherein one or both of the first panel and the second panel comprises low-emissivity glass.
Clause 42: The method of any one of clauses 35-41, further comprising nicking at least the first and second lips of the spacer and optionally a portion of the first and second wall adjacent to the lips, at a bending location on the spacer, and bending the spacer towards the nicks at the bending location.
Clause 43: The method of any one of clauses 35-42, comprising, in order, applying adhesive to the spacer, bending the spacer to align with marginal portions of the panels, and affixing the spacer between the first glazing panel and the second glazing panel.
Clause 44: The method of any one of clauses 35-43, wherein the adhesive comprises a polyisobutylene portion and a silicone portion.
Clause 45: A method of preparing a spacer for an insulated glazing unit, comprising roll-forming a metal sheet into an elongate unit comprising:
an elongate corrugated portion comprising two or more longitudinal ridges;
a first elongate lateral wall, having a major planar portion and extending from a first major edge of the corrugated portion;
a second lateral elongate wall, having a major planar portion and extending from a second major edge of the corrugated portion in the same direction as the first elongate wall;
a first lip extending from the first elongate lateral wall opposite the corrugated portion and extending towards the second elongate lateral wall; and
a second lip extending from the second elongate lateral wall opposite the corrugated portion and extending towards the first elongate lateral wall and defining a gap between the first lip and the second lip;
the corrugated portion comprising two or more longitudinal ridges, with a first lateral valley portion between and connecting the first elongate lateral wall and an adjacent ridge and defining a first lateral valley, a second lateral valley portion between and connecting the second elongate lateral wall and an adjacent ridge and defining a second lateral valley, and one or more central valley portions between and connecting adjacent longitudinal ridges and defining one or more central valleys, each ridge comprising a plurality of walls, with peak portions connecting adjacent walls.
Clause 46: The method of clause 45, further comprising forming corner clearances in the metal sheet or roll-formed spacer at corner locations in the metal sheet or spacer.
Clause 47: The method of clause 45 or 46, further comprising forming swaged ends in the metal sheet or roll-formed spacer.
Clause 48: The method of any one of clauses 45-47, further comprising cutting the spacer into a single frame length after roll-forming the spacer.
Clause 49: The method of any one of clauses 45-48, further comprising applying one or more adhesives to the exterior side of the longitudinal walls.
Clause 50: The method of any one of clauses 45-49, further comprising applying a desiccant matrix to a central valley of the interior side of the formed spacer with no desiccant matrix applied to corner locations of the spacer.
Clause 51: The method of clause 50, further comprising bending the spacer into a spacer frame using one or more internal dies.
Clause 52: The method of any one of clauses 45-51, wherein, when assembled in an insulating glazing unit, the spacer has a Res-value ((in-hr-° F.)/BTU) of at least 190, 195, 200, 205, 210, or 215, optionally, as defined by the inverse of the flow of the (BTU/hr·° F.·in.) that occurs from the interface of the glass and adhesive layer at the inside side of the unit to the interface of the glass and adhesive layer of the outside of the unit per unit increment of temperature (1° F.), per unit length of edge assembly perimeter (inch), and wherein the glass/adhesive interfaces are assumed to be isothermal.
Clause 53: The method of any one of clauses 45-52, performed as continuous, automated process in a single manufacturing line.
Clause 54: A spacer for use in an insulated glazing unit formed from a single sheet of stainless steel or tin-plated steel, comprising lateral walls connected by a central portion comprising from two to four longitudinal ridges, wherein the width of the spacer is no more than 35% the linear width of the metal folded to form the spacer, and wherein, when assembled in an insulating glazing unit, has a Res-value ((in-hr-° F.)/BTU) of at least 190, 195, 200, 205, 210, or 215, optionally, as defined by the inverse of the flow of the (BTU/hr·° F.·in.) that occurs from the interface of the glass and adhesive layer at the inside side of the unit to the interface of the glass and adhesive layer of the outside of the unit per unit increment of temperature (1° F.), per unit length of edge assembly perimeter (inch), and wherein the glass/adhesive interfaces are assumed to be isothermal.
Clause 55: An insulated glazing unit comprising a first panel and a second panel, the first panel having a first major surface (surface 1) and an opposite second major surface (surface 2) and marginal edges, the second panel having a first major surface (surface 3) and an opposite second major surface (surface 4) and marginal edges; and the spacer of clause 54, having an internal side and an opposite external side, affixed with adhesive to marginal portions of surface 2 of the first panel and surface 3 of the second panel and supporting the first and second panel in a spaced-apart configuration, with the internal side of the spacer, surface 2 of the first panel, and surface 3 of the second panel defining a sealed compartment.
As used herein, spatial or directional terms, such as “left”, “right”, “inner”, “outer”, “above”, “below”, and the like, relate to the invention as it is shown in the drawing figures. However, it is to be understood that the invention can assume various alternative orientations and, accordingly, such terms are not to be considered as limiting. The drawings are not necessarily to scale. Further, as used herein, all numbers expressing dimensions, physical characteristics, processing parameters, quantities of ingredients, reaction conditions, and the like, used in the specification and claims are to be understood as being modified in all instances by the term “about”. Accordingly, unless indicated to the contrary, the numerical values set forth in the following specification and claims may vary depending upon the desired properties sought to be obtained by the present invention. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical value should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques. Moreover, all ranges disclosed herein are to be understood to encompass the beginning and ending range values and any and all subranges subsumed therein. For example, a stated range of “1 to 10” should be considered to include any and all subranges between (and inclusive of) the minimum value of 1 and the maximum value of 10; that is, all subranges beginning with a minimum value of 1 or more and ending with a maximum value of 10 or less, e.g., 1 to 3.3, 4.7 to 7.5, 5.5 to 10, and the like. “A” or “an” refers to one or more.
The articles described herein typically, but not exclusively, find use in architecture. The articles may be discussed with reference to their use in an insulating glass unit (IGU). In an IGU, a spacer described herein may be used to space apart two panels, such as panels used in architectural transparencies. As used herein, the term “architectural transparency” refers to any transparency located on a building, such as, but not limited to, windows and sky lights. However, it is to be understood that the articles described herein are not limited to use with such architectural transparencies but may be practiced with transparencies in any desired field, such as, but not limited to, laminated or non-laminated residential and/or commercial windows, insulating glass units, and/or transparencies for land, air, space, above water, and underwater vehicles. In one aspect or embodiment, the coated articles as described herein are transparencies for use in a vehicle, such as a window or a sunroof. Therefore, it is to be understood that the specifically disclosed exemplary aspects or embodiments are presented simply to explain the general concepts of the invention, and that the invention is not limited to these specific exemplary embodiments. Additionally, while a typical “transparency” can have sufficient visible light transmission such that materials can be viewed through the transparency, the “transparency” need not be transparent to visible light but may be translucent or opaque. That is, by “transparent” is meant having visible light transmission of greater than 0% up to 100%.
A non-limiting transparency 10 is illustrated in
As indicated above, in the broad practice of the invention, the panels 12, 18, 12′, 18′, 26′ of the transparency 10, 10′ can be of the same or different materials and may have the same or different dimensions. The panels 12, 18, 12′, 18′, 26′ may include any desired material having any desired characteristics. For example, one or more of the panels 12, 18, 12′, 18′, 26′ may be transparent or translucent to visible light. By “transparent” is meant having visible light transmission of greater than 0% up to 100%. Alternatively, one or more of the panels 12, 18, 12′, 18′, 26′, may be translucent. By “translucent” is meant allowing electromagnetic energy (e.g., visible light) to pass through but diffusing that energy such that objects on the side opposite the viewer are not clearly visible. Examples of suitable materials for the panels include, but are not limited to, plastic substrates (such as acrylic polymers, such as polyacrylates; polyalkylmethacrylates, such as polymethylmethacrylates, polyethylmethacrylates, polypropylmethacrylates, and the like; polyurethanes; polycarbonates; polyalkylterephthalates, such as polyethyleneterephthalate (PET), polypropyleneterephthalates, polybutyleneterephthalates, and the like; polysiloxane-containing polymers; or copolymers of any monomers for preparing these, or any mixtures thereof); ceramic substrates; glass substrates; or mixtures or combinations of any of the above. For example, one or more of the panels 12, 18, 12′, 18′, 26′ may include conventional soda-lime-silicate glass, borosilicate glass, or leaded glass. The glass may be clear glass. By “clear glass” is meant non-tinted or non-colored glass. Alternatively, the glass may be tinted or otherwise colored glass. The glass may be annealed or heat-treated glass. As used herein, the term “heat treated” means tempered or at least partially tempered. The glass may be of any type, such as conventional float glass, and may be of any composition having any optical properties, e.g., any value of visible transmission, ultraviolet transmission, infrared transmission, and/or total solar energy transmission. By “float glass” is meant glass formed by a conventional float process in which molten glass is deposited onto a molten metal bath and controllably cooled to form a float glass ribbon. Examples of float glass processes are disclosed in U.S. Pat. Nos. 4,466,562 and 4,671,155.
The panels 12, 18, 12′, 18′, 26′ may each comprise, for example, clear float glass or may be tinted or colored glass or one panel 12, 18, 12′, 18′, 26′ may be clear glass and the other panel(s) 12, 18, 12′, 18′, 26′, colored glass. Although not limiting, examples of glass suitable for the panels 12, 18, 12′, 18′, 26′ are described in U.S. Pat. Nos. 4,746,347; 4,792,536; 5,030,593; 5,030,594; 5,240,886; 5,385,872; and 5,393,593. The panels 12, 18, 12′, 18′, 26′ may be of any desired dimensions, e.g., length, width, shape, or thickness. In one exemplary automotive transparency, the first and second plies may each be 1 mm to 10 mm thick, such as 1 mm to 8 mm thick, such as 2 mm to 8 mm, such as 3 mm to 7 mm, such as 5 mm to 7 mm, such as 6 mm thick. Non-limiting examples of glass that may be used for the panels include clear glass, Starphire®, Solargreen®, Solextra®, GL-20®, GL-35™, Solarbronze®, Solargray® glass, Pacifica® glass, SolarBlue® glass, and Optiblue® glass.
The solar control coating 30, 130 of the invention is deposited over at least a portion of at least one major surface of one of the panels 12, 18, 12′, 18′, 26′. In the example according to
Coatings may be deposited by any useful method, such as, but not limited to, conventional chemical vapor deposition (CVD) and/or physical vapor deposition (PVD) methods. Examples of CVD processes include spray pyrolysis. Examples of PVD processes include electron beam evaporation and vacuum sputtering (such as magnetron sputter vapor deposition (MSVD)). Other coating methods could also be used, such as, but not limited to, sol-gel deposition. In one non-limiting embodiment, the coating 30, 130 is deposited by MSVD. Examples of MSVD coating devices and methods will be well understood by one of ordinary skill in the art and are described, for example and without limitation, in U.S. Pat. Nos. 4,379,040; 4,861,669; 4,898,789; 4,898,790; 4,900,633; 4,920,006; 4,938,857; 5,328,768; and 5,492,750.
Peripheral area may comprise an area extending any suitable distance, such as, without limitation from 1″ to 24″, including any increment therebetween, such as 1″, 2″, 3″, 4″, 5″, 6″, 7″, 8″, 9″, 10″, 11″, or 12″, from an edge of the panel, and may depend on the dimensions of the IGU. The peripheral area may be peripheral to, that is, in a direction toward the edges of the IGU, the sight line of the IGU 100.
According to one aspect or embodiment, a spacer is provided for use in an IGU, such as described in connection with
A spacer, as described herein, for example in
In the context of the IGUs and spacers described herein, “parallel” means that a portion of a stated element, such as a wall of the spacer is parallel to the plane of the referenced element, such as a panel, within practical manufacturing tolerances, e.g., within ±1° of parallel. “Substantially parallel,” meaning that a portion of a stated element, such as a wall of the spacer is parallel to, or within ±1°, ±2°, ±3°, ±4°, or ±5° of the plane of the referenced planar element, such as a panel. Likewise, “perpendicular” means that a portion of a stated element, such as a wall of the spacer is perpendicular to the plane of the referenced planar element, such as a panel, within practical manufacturing tolerances, e.g., within ±1° of perpendicular (90°). “Substantially perpendicular” refers to a portion of a stated element, such as a wall of the spacer is perpendicular to, or within ±1°, ±2°, ±3°, ±4°, or ±5° of a plane perpendicular to a plane of the referenced planar element, such as a panel.
By “free of desiccant”, e.g., in the context of valleys formed by ridges on the internal side of the spacer, it is meant that the valleys, e.g., the lateral valleys, do not contain desiccant, or only contain small amounts of desiccant, for example as compared to the central valleys, for example as a result in inaccuracy of deposition or movement of the desiccant matrix during manufacture of an insulated glazing unit, within manufacturing tolerances.
The spacers may be prepared by any useful method. Because the spacers may be prepare from a single coil of metal stock, roll-forming may be preferred for preparing the spacer as depicted schematically in
An example of a spacer 624 is shown in
The spacer, such as a spacer as depicted in
The spacers described herein exhibit exceptional insulation, e.g., Res-values, when incorporated into an IGU.
In certain aspects, the thermal resistance (Res-value [(in-hr-° F.)/BTU]) of the spacer when incorporated into an IGU is at least 175, at least 190, at least 175, at least 190, at least 195, at least 200, at least 205, at least 210, or at least 215. U.S. Pat. Nos. 5,655,282, 5,675,944 and 6,115,989, among many others, describe IGUs, methods of making IGUs, and various applicable standards for assessing the insulating capacity of IGUs. IGUs may be used to reduce heat transfer between the outside and inside of a home or other structures. A measure of insulating value generally used is the “U-value”. The U-value is the measure of heat in British Thermal Unit (BTU) passing through the unit per hour (hr)-square foot (ft2)-degree Fahrenheit (° F.) (Formula 1):
The lower the U-value the better the thermal insulating value of the unit, e.g., higher resistance to heat flow resulting in less heat conducted through the unit. Another measure of insulating value is the “R-value” which is the inverse of the U-value. Still another measure is the resistance to heat flow (Res-value) which is stated in hr-° F. per BTU per inch of perimeter of the unit (Formula 2):
Modeling software, such as ANSYS finite element code (i.e. ANSYS; Finite Element Program {FEA}, Release 14, SAS IC. Inc. 2012), may be used to determine the Res-value (see, e.g., European Patent Application Publication Number 0 475 213 A1 and U.S. Pat. Nos. 5,531,047 and 5,655,282). The result of the ANSYS calculation is dependent on the geometry of the cross section of the edge assembly and the thermal conductivity of the constituents thereof. The geometry of any such cross section may be measured by studying the unit edge assembly.
In some aspects, the edge resistance of the edge assembly (hr·° F.·in/BTU) is defined by the inverse of the flow of the (BTU/hr·° F.·in.), calculated by ANSYS, that occurs from the interface of the glass and adhesive layer at the inside side of the unit to the interface of the glass and adhesive layer of the outside of the unit per unit increment of temperature (1° F.), per unit length of edge assembly perimeter (inch). The glass/adhesive interfaces are assumed to be isothermal to simplify the model.
As such, in certain examples, a spacer is provided, and an IGU is provided, where the spacer is formed from a single, folded metal sheet, such as a stainless steel or tin-plated steel sheet, where Wsp/Wsh×100% is 36% or less, at most 35%, e.g., 25% or less, 20% or less, or 15% or less, e.g., ranging from 15% to 35%, or from 21% to 30%, and having a Res-value of at least 175, at least 190, at least 175, at least 190, at least 195, at least 200, at least 205, at least 210, or at least 215 when the spacer is incorporated into an IGU.
Spacers are automatically formed as follows: Flat metal coil is fed from an uncoiler to a feeder press where corners, muntin bar locators, corner tabs, and gas fill holes are punched. After punching, the flat coil stock advances to a roll former where it is bent into the proprietary U-shape. At the roll former exit, individual IGU spacers are automatically cut to length, corner tabs are swaged, and advanced via a conveyor belt to the adhesive and desiccant matrix extruder.
Adhesive (usually a hot melt butyl or hot applied curable material) and desiccant matrix is applied by the extruder in a linear fashion to the un-bent spacer as it advances on a conveyor belt. A worker folds the spacer (with adhesive and desiccant matrix applied), inserts the preformed tab to form a rectangular shape and hangs it on the overhead conveyor. Two glass lites are washed in a horizontal washer and advance to the spacer topping station. A worker removes a spacer from the overhead conveyor and with assistance from a second worker places the spacer on the first glass lite. The two workers then place the second glass lite on top of the spacer. Low strength adhesion is established via the initial adhesive “tack” and the IGU advances to the heated oven/roll press. Final overall thickness, adhesive bond line width, and adhesion is achieved by high heat and pressure through the continuously moving oven/roll press. Workers inspect and offload the IGUs and place them on transport racks for cooling. After the IGUs reach room temperature, they are argon filled via lances in batches of 5 at a time by a worker. After argon filling is complete, screws are inserted in the fill holes and a hot melt butyl patch is applied by a worker. The IGUs are finished and ready for installation in the window sash.
Metal spacer material is roll formed and cut into standard lengths. This is often done at a dedicated plant outside of the IGU manufacturing facility. A section of formed spacer metal is cut to length by a worker. The spacer metal is bent to the desired rectangular shape (corners formed) by a worker. A worker drills holes in the spacer to enable desiccant bead filling. Desiccant beads “injected” into spacer by the same worker. Drilled holes are manually patched closed with foil tape or butyl adhesive by the same worker. Primary adhesive (polyisobutylene or PIB) is applied by a worker using a “cartwheel” motion with a PIB extruder. Spacer is placed on overhead conveyor. The first lite of glass exits the vertical glass washer and advances to the spacer topping station. Spacer is removed from overhead conveyor and positioned by a worker on the first glass lite. The glass and spacer advance to the argon filling press. The second glass exits the washer and advances to the argon filling press. The two glass lites are flooded with argon and pressed together. Low strength adhesion is achieved via the PIB, forming the IGU. The IGU advances to the secondary adhesive robot. Secondary adhesive (usually silicone or polysulfide—sometimes polyurethane, hot applied butyl, or a hot applied curable material) is applied to the back of the spacer. The finished IGU exits the robot sealer and is inspected then removed from the manufacturing line. The IGUs are finished and ready for installation in the window sash.
Metal spacer material is roll formed and cut into standard lengths (e.g., about 21′ long). This is often done at a dedicated plant outside of the IGU manufacturing facility. A section of formed spacer metal is cut to length by a worker. A lineal key is inserted in one end of the spacer by a worker. Desiccant beads are filled through the open end. The spacer metal is bent to the desired rectangular shape (corners formed). Primary adhesive (PIB) is applied by a worker using a “cartwheel” motion with a PIB extruder. Spacer is placed on overhead conveyor. The first lite of glass exits the vertical glass washer and advances to the spacer topping station. Spacer is removed from overhead conveyor and positioned by a worker on the first glass lite. The glass and spacer advance to the argon filling press. The second glass exits the washer and advances to the argon filling press. The two glass lites are flooded with argon and pressed together. Low strength adhesion is achieved via the PIB, forming the IGU. The IGU advances to the secondary adhesive robot. One part silicone secondary adhesive is applied to the back of the spacer. The finished IGU exits the robot sealer and is inspected then removed from the manufacturing line. The IGUs are finished and ready for installation in the window sash.
Spacers are automatically formed by the machine in the following order: Flat metal coil is fed from an uncoiler to a feeder press where muntin bar locators and corner clearances are punched. After punching, the flat coil stock advances to a roll former where it is bent into the proprietary shape. At the roll former exit, individual IGU spacers are automatically cut to length, the lineal key tab is swaged, and advanced via a conveyor belt to the adhesive and desiccant matrix extruder.
Adhesive (usually a hot melt butyl or hot applied curable material) and desiccant matrix is applied by the extruder in a linear fashion to the un-bent spacer as it advances on a conveyor belt. Desiccant matrix is not applied to the corner areas.
The spacer bender bends the spacer by use of interior and exterior forming dies, referred to herein as mandrel bending. The same machine inserts the swaged end of the spacer into the trailing end of the spacer. Spacer joining techniques may include: spot welding, positive locking/mating stamped sections, adhesive adhesives, and foil tapes. The finished spacer is collected by an automated overhead conveyor.
Two glass lites are washed in a horizontal washer and advance to the spacer topping station.
A worker removes a spacer from the overhead conveyor and with assistance from a second worker places the spacer on the first glass lite.
The two workers then place the second glass lite on top of the spacer. Low strength adhesion is established via the initial adhesive “tack” and the IGU advances to the heated oven/roll press.
Final overall thickness, adhesive bond line width, and adhesion is achieved by high heat and pressure through the continuously moving oven/roll press.
Workers inspect and offload the IGUs and place them on transport racks for cooling.
After the IGUs reach room temperature, they are argon filled via lances in batches of 5 at a time by a worker.
After argon filling is complete, screws are inserted in the fill holes and a hot melt butyl patch is applied by a worker. The IGUs are finished and ready for installation in the window sash.
Spacers are automatically formed by the machine in the following order: Flat metal coil is fed from an uncoiler to a feeder press where muntin bar locators and corner clearances are punched. After punching, the flat coil stock advances to a roll former where it is bent into the proprietary shape. At the roll former exit, individual IGU spacers are automatically cut to length, the lineal key tab is swaged, and advanced via a conveyor belt to the primary adhesive and desiccant matrix extruder.
Primary adhesive (e.g., polyisobutylene, PIB) and desiccant matrix is applied by the extruder in a linear fashion to the un-bent spacer as it advances on a conveyor belt. Desiccant matrix is not applied to the corner areas.
The spacer bender bends the spacer by use of interior and exterior forming dies. The action is described as mandrel bending. The same machine inserts the swaged end of the spacer into the trailing end of the spacer. Spacer joining techniques may include: spot welding, positive locking/mating stamped sections, adhesive adhesives, and/or foil tapes. The finished spacer is collected by an automated overhead conveyor.
The first lite of glass exits the vertical glass washer and advances to the spacer topping station
Spacer is removed from overhead conveyor and positioned by a worker on the first glass lite. The glass and spacer advance to the argon filling press.
The second glass exits the washer and advances to the argon filling press.
The two glass lites are flooded with argon and pressed together. Low strength adhesion is achieved via the PIB, forming the IGU. The IGU advances to the secondary adhesive robot.
Secondary adhesive (usually silicone or polysulfide—sometimes polyurethane, hot applied butyl, or a hot applied curable material) is applied to the back of the spacer.
The finished IGU exits the robot sealer and is inspected, then removed from the manufacturing line. The IGUs are finished and ready for installation in the window sash.
Spacers are automatically formed by the machine in the following order: Flat metal coil is fed from an uncoiler to a feeder press where muntin bar locators and corner clearances are punched. After punching, the flat coil stock advances to a roll former where it is bent into the proprietary shape. At the roll former exit, individual IGU spacers are automatically cut to length, the lineal key tab is swaged, and advanced to a barrier member applicator (example of such is a pressure sensitive tape), then advances via a conveyor belt to the primary adhesive and desiccant matrix extruder.
Primary adhesive (e.g., polyisobutylene, PIB) and desiccant matrix is applied by the extruder in a linear fashion to the un-bent spacer as it advances on a conveyor belt. Desiccant matrix is not applied to the corner areas.
The spacer bender bends the spacer by use of interior and exterior forming dies. The action is described as mandrel bending. The same machine inserts the swaged end of the spacer into the trailing end of the spacer. Spacer joining techniques may include: spot welding, positive locking/mating stamped sections, adhesive adhesives, and/or foil tapes. The finished spacer is collected by an automated overhead conveyor.
The first lite of glass exits the vertical glass washer and advances to the spacer topping station
Spacer is removed from overhead conveyor and positioned by a worker on the first glass lite. The glass and spacer advance to the argon filling press.
The second glass exits the washer and advances to the argon filling press.
The two glass lites are flooded with argon and pressed together. Low strength adhesion is achieved via the PIB, forming the IGU. The IGU advances to the secondary adhesive robot.
Secondary adhesive (usually silicone or polysulfide—sometimes polyurethane, hot applied butyl, or a hot applied curable material) is applied to the back of the spacer.
The finished IGU exits the robot sealer and is inspected, then removed from the manufacturing line. The IGUs are finished and ready for installation in the window sash.
Simulation results for fourteen spacers in a generic vinyl casement frame were obtained. One IGU with the same glass in each was built for a generic vinyl casement frame and evaluated with 14 different spacers. The data collected included U-factor (Center-of-Glass and Total Product), and also temperature of the glass in the sill sections. The glass option imported into each window was a 3 mm pane of Vitro Solarban®60 coated glass—½″ gap of 90% Argon/10% Air—3 mm pane of clear glass. The ½″ gap was modified if the spacer plus adhesive was not manufactured at exactly that dimension.
All software used was by Lawrence Berkley National Laboratory and is considered the industry standard: Window7 software used is version 7.4.14.0; Therm7 software used is version 7.4.4.0; International Glazing Data Base used is version 60. Table 1 includes Center-of-Glass U-factor, Total Window Product U-factor, and sill glass interior surface temperature at the glass sightline for experimental spacer 1, essentially shown in
Res values were modeled for a number of variations of the spacer described herein and were compared to values obtained from commercial comparative examples, as well as other spacer variations. Res-values, or edge resistance values ((in-hr-° F.)/BTU) were determined essentially as described in European Patent Application Publication Number 0 475 213 A1 and U.S. Pat. Nos. 5,531,047 and 5,655,282, among others. In short, the edge resistance of the edge assembly (hr·° F.·in/BTU) was defined by the inverse of the flow of the (BTU/hr·° F.·in.), calculated by ANSYS, that occurs from the interface of the glass and adhesive layer at the inside side of the unit to the interface of the glass and adhesive layer of the outside of the unit per unit increment of temperature (1° F.), per unit length of edge assembly perimeter (inch). The glass/adhesive interfaces are assumed to be isothermal to simplify the model.
In another example, for spacers having a width of 15/32″, the width of the metal in the central folded region, excluding lateral walls and lips, is 1.019″ for a single-seal spacer, and 0.897″ for a dual-seal spacer.
It will be readily appreciated by those skilled in the art that modifications may be made to the invention without departing from the concepts disclosed in the foregoing description. Accordingly, the particular embodiments described in detail herein are illustrative only and are not limiting to the scope of the invention, which is to be given the full breadth of the appended claims and any and all equivalents thereof.
This application claims the benefit of U.S. Provisional Application No. 63/010,169, filed Apr. 15, 2020, which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 63010169 | Apr 2020 | US |