Low viscosity polymer polyols a process for their production as well as the manufacture of polyurethane from materials

BACKGROUND OF THE INVENTION
Polymer polyols within the scope of the invention are products which can be obtained by the polymerization of ethylenically unsaturated compounds in the presence of polyether polyols (so-called "base polyols"), a macromer, and an enol ether of a specified formula. These can be used, for example, for the manufacture of polyurethane flexible foam materials. The principally used ethylenically unsaturated compounds are the monomers styrene and acrylonitrile, which are, for example, radically polymerized in polyether polyols as base polyols.
The production of such polymer polyols is, for example, described in the U.S. Pat. Nos. 3,383,351, 3,304,273, and Reissue 33,291, or in German Auslegeschrifien 1,152,536 and 1,152,537.
The polymer polyols in the ideal case are relatively low viscosity, finely dispersed, non-sedimenting dispersions of the polymerizate (preferably of an acrylonitrile/styrene-graft-copolymer)in the essentially unchanged polyether polyol. Characteristic identifiers for quality and applicability of the polymer polyols are viscosity, storage stability (sedimentation resistance) and small particle size. These characteristics are primarily influenced by the type and quantity ratio of the base materials. The solids content (monomer portion in the preparation) and the monomer ratio (for example, the styrene/acrylonitrile ratio) have an especially large influence on the quality of the final product.
The most important goals during the production of polymer polyols are achieving a high solids content (at least 40%) at the highest possible styrene percentage, and the lowest possible viscosity, with excellent product stability at the same time.
In order to achieve product stability, i.e the elimination of the formation of undesired, agglomerated polymer particles which precipitate from the continuous phase of the base polyol, these polymer particles must be stabilized during the polymer polyol production. This stabilization is effected on one hand through the building-in of a part of the molecules of the base polyether into the in-situ formed polymer. The effectiveness of stabilization is thereby favored on the other hand through a high molecular weight of the base polyethers, and through a high acrylonitrile portion in the monomer mixture. A nigh acrylonitrile content increases the color of the polymeric polyols, and correspondingly, the discoloration tendency of the flexible foam manufactured from them, and accordingly is undesirable. Another problem is that the viscosity of the polymer polyols is increased through the use of base polyols with higher molecular weights.
One possibility to obtain low viscosity polymer polyols with higher solids contents essentially independent from the molecular weight of the base polyol and from the acrylonitrile portion in the monomer mixture, is through the use of chain transfer agents. Some of the chain transfer agents commonly used in this polymerization technology include compounds such as, for example the usual mercaptans, halogenated alkanes, or alcohols.
Also known, is the use of enol ethers as chain transfer agents as described in EP-A 008,444, through which the production of polymer polyols having a relatively low viscosity at a relatively high solids content and styrene portion are made possible.
Another possibility for the stabilization of polymer polyols is the use of compounds that are compatible with the polyol phase, which contain ethylenically unsaturated, polymerizable groups. These so-called macromers copolymerize with the vinyl monomers such that the developing polymer particles become sterically stabilized by the polyether side chains, and are in this way protected against agglomeration and sedimentation.
The production of polymer polyols using macromers is disclosed in, for example, U.S. Pat. Nos. 3,652,639, 3,823,201, 4,460,715, 4,390,645, 5,093,412, and 4,342,840. The ethylenically unsaturated double bonds are introduced into the polyether polyols through reaction with cyclic, unsaturated carbonic acid anhydrides, such as maleic acid anhydride, and subsequent reaction with ethylene or propylene oxide; through esterification with acrylic or methacrylic acid (or derivatives thereof); through reaction with allylglycidyl ether; through reaction with an unsaturated isocyanate such as, for example, isocyanatoalkyl acrylate and isocyanatomethacrylate, 1-(1-isocyanato-1-methylethyl)-3-(1-methylethenyl)-benzene or NCO-functional adducts from a polyisocyanate and hydroxyethyl acrylate or hydroxypropyl acrylate.
Also, the combination of macromers with chain transfer agents such as mercaptans or alcohols, is described in German Auslegeschriff 2,500,274 E:P-A 0,190,769, as well as in EP-A 0,091,036.
Although the mentioned processes lead to polymer polyols which can basically be used as the polyol component for the manufacture of polyurethane flexible foams, further improvements are desirable. Also, the viscosities of higher solids content polymer polyols, especially those containing a higher styrene portion in the monomer mixture are still very high as can be seen from the literature, and often smaller agglomerized polymer particles can be observed in the residue, i.e. a finely dispersed product is not yet achieved.
Surprisingly, it was found that agglomerate-free polymer polyols with high solids content and low viscosities can be prepared when the polymer polyol is produced in the presence of a macromer of the type described above, and an enol ether of a specific formula as chain transfer agents.
Through the use of a combination of macromers with the special chain transfer agents of the enol ether type as demonstrated by the working examples herein, stable, finely dispersed polymer polyols are produced which have lower viscosities at a specific solids content and styrene portion, or contain a higher styrene content and/or solids content at a specific viscosity than previous products produced using other known combinations of chain transfer agents and macromers.
DESCRIPTION OF THE INVENTION
The subject of the invention is a process for the production of stable, agglomerate-free, low viscosity graft copolymer dispersions comprising the radical polymerization of at least one ethylenically unsaturated monomer in the presence of a base polyol, a macromer, and an enol ether of the general formula:
A.dbd.CH--O--R,
wherein:
R represents an aliphatic hydrocarbon radical having 1 to 18 carbon atoms, a cycloaliphatic hydrocarbon radical having 5 to 10 carbon atoms (or a substituted or unsubstituted benzyl radical);
A represents a divalent radical of the formula: ##STR2## wherein R' represents hydrogen or an aliphatic hydrocarbon radical having 1 to 8 carbon atoms.
This process is optionally carried out in the presence of an organic solvent.
According to the invention it is preferred that:
a) the ethylenically unsaturated monomer is present in a quantity of between 25 to 65% by weight, based on the total quantity of monomers and polyol (polyol is the mixture of base polyol and macromer.
b) the ethylenically unsaturated monomers comprise a mixture of styrene and acrylonitrile.
c) the mixtures of styrene and acrylonitrile suitable as the ethylenically unsaturated monomers are present in a weight ratio of between 20:80 and 100:0, and most preferably of between 50:50 and 80:20.
d) polyalkylene oxides containing at least two to six hydroxyl groups and having an OH-number between 20 and 100, and preferably between 30 and 70, are preferred as the base polyol.
e) the macromers preferably have a molecular weight between 3,000 and 15,000, preferably between 4,500 and 12,000 (g/mol), and a functionality between 2 and 6.
f) the macromers preferably have a statistical average of 0.1 to 1.5, preferably 0.3 to 1, mole of double bonds per mole polyol.
g) the macromers are preferably present in a quantity between 2 to 20%, most preferably 3 to 10% by weight, based on the total weight of polyol (polyol is the mixture of base polyol and macromer).
h) (cyclohex-3-enyliden methoxymethyl)-benzene is the preferred enol ether.
i) the enol ether is present in a quantity between 0.1 to 5% weight, based on the total weight of the monomer mixture.
and
j) preferred organic solvents are toluene and ethylbenzene.
The present invention also relates to the stable, agglomerate-free, low viscosity graft copolymer dispersions, obtainable based on the above process, and the manufacture of polyurethane foam materials based on the isocyanate-polyaddition process wherein the polyol component comprises the graft copolymer dispersion obtainable from the above process.
Suitable polyols for the so-called "base polyols" include, for example, those polyols having at least two hydroxyl groups, and preferably polyether polyols including, for example, the known addition products of cyclic ethers such as ethylene oxide, propylene oxide, styrene oxide, butylene oxide on starter compounds such as, for example, polyhydroxy compounds such as alkylene glycols, glycerin, trimethylol propane, pentaerythritol, sorbitol, amines such as, for example, ethylene diamine and toluene diamine. The polyether polyols which are suitable as "base polyols" preferably have functionalities between 2 and 6, and an OH number between 20 and 100. The polyether chains are preferably built up from propylene oxide and ethylene oxide units. Also, polyester polyols having functionalities of preferably from 2 to 6 and an OH number between 20 and 100 are considered suitable as "base polyols".
The polymer polyols are obtained through radical polymerization of at least one monomer containing ethylenically unsaturated end-groups or a mixture of monomers containing ethylenically unsaturated end-groups in the base polyols, which are preferably the polyether polyols as specified hereinabove. Some examples of suitable monomers containing ethylenically unsaturated end-groups include monomers such as butadiene, styrene, .alpha.-methylstyrene, methylstyrene, ethylstyrene, acrylonitrile, methacrylonitrile, methylmethacrylate, and acrylic acid ester. Styrene and acrylonitrile are the preferred monomers. The quantity of ethylenically unsaturated monomers to be used in the process according to the present invention is between 25 and 65% by weight, based on the total weight of monomers and polyol. The weight ratio of styrene to acrylonitrile monomers is preferably from 20:80 to 100:0, most preferably from 50:50 to 80:20.
The initiation of the radical polymerization is performed in the usual manner, with the usual radical-forming initiators. Initiators of this type include, for example, organic peroxides such as benzoyl peroxide, tertbutyloctoate, dodecanoyl peroxide; and azo compounds such as azoisobutyronitrile or 2,2'-azobis(2-methylbutyronitrile).
The polyols suited for the preparation of macromers used for the process of the present invention include, for example, the known polyols, preferably polyether polyols, such as the known addition products of cyclic ethers such as ethylene oxide, propylene oxide, styrene oxide. butylene oxide, etc. with starter compounds such as, for example, polyhydroxy compounds including alkylene glycols, glycerin, trimethylol propane, penterythritol, sorbitol, and amines such as, for example, ethylene diamine and tolylene diamine. The polyether polyols used in the preparation of the macromers have functionalities between 2 and 6, and a molecular weight between 3,000 and 15,000 g/mol, preferably 4,500 to 12,000. The polyether chains are preferably built from propylene oxide and ethylene oxide units.
The ethylenically unsaturated groups can be introduced into the polyol material to form the macromer as described in the processes known in the literature. The macromer formation is preferably via the reaction of the base polyol with maleic acid anhydride, and the subsequent alkoxylation with ethylene or propylene oxide; the reaction of the base polyol with acrylic acid or the methyl or ethyl ester of acrylic acid; and the reaction with an unsaturated isocyanate such as, for example, 1-(1-isocyanato-1-methylethyl)-3-(1-methylethenyl)-benzene or an NCO-functional adduct produced from a polyisocyanate and a hydroxyethyl acrylate or hydroxypropyl acrylate. For the production of the latter type of macromer, suitable polyisocyanates include, for example, hexamethylene diisocyanate, isophorone diisocyanate, diphenylmethane diisocyanate and most preferably toluene diisocyanate.
The produced macromers contain on as a statistical average normally from 0.1 to 1.5, and preferably 0.3 to 1 moles of double bonds per mole of polyol.
The enol ether to be used in accordance with the invention is known in the literature. The production of suitable enol ethers is described in, for example, the U.S. Pat. No. 3,639,485, the disclosure of which is herein incorporated by reference, and in German patents 1,668,091 and 1,768,396. Suitable representatives of compounds of this class are specified in, for example, U.S. Pat. No. 4,230,823, the disclosure of which is herein incorporated by reference. A particularly preferred enol ether is (cyclohex-3-enyliden methoxymethyl)-benzene, which is commercially available from Bayer AG under the name Vulkazon AFD.
The enol ether is normally present in a quantity between 0.1 and 5% by weight, based on the total weight of the monomer or mixture of monomers used.
It is also within the scope of the present invention that organic solvents are present in the process according to the invention. Suitable organic solvents include hydrocarbons such as, for example, toluene, ethylbenzene, isopropylbenzene, xylols, ketones, such as acetone or methylethyl ketone, and alcohols such as methanol, ethanol, isopropanol or butanol. Preferred solvents are toluene and ethylbenzene.
The process can be operated either on a discontinuous basis or on a continuous basis. It is within the scope of the invention, for example, to meter-in a mixture which contains the ethylenically unsaturated monomers, the enol ether, the initiator, and a portion of the polyol and optionally any solvent into a mixer, which contains the preheated polyether and the macromer. It is also within the scope of the invention to meter in a portion of the macromer, together with the ethylenically unsaturated monomers, the enol ether, a portion of the polyether, and, optionally, the solvent. Another possibility is to add the enol ether to the polyether or to a major portion of the polyether and the macromer in the reactor, and to meter in the remaining components.
In addition, a mixture of all the reaction components can be continuously metered into a reactor, and the product can likewise be taken from an overflow.
The temperature at which the polymerization is carried out is normally 80.degree. to 140.degree. C., preferably 90.degree. to 130.degree. C.
Following the completion of the polymerization reaction, the product is usually purified by separating readily volatile parts such as residual monomers, solvents, etc. by vacuum distillation.
The polymer polyols produced in accordance with the inventive process are particularly suitable for polyurethane plastic materials based on the isocyanate polyaddition process. These polymer polyols are free of agglomerates, are stable, and have low viscosities.
The manufacture of polyurethane plastic materials, preferably, flexible polyurethane foams comprise the reaction of a) organic polyisocyanates with b) the polymeric polyols produced according to the invention, and in the presence of c) optionally, other high molecular weight and/or low molecular weight compounds containing hydrogen atoms reactive with isocyanate groups, d) catalysts, e) water and/or low-boiling hydrocarbons as blowing agents and f) aids and/or additives
In the manufacture of polyurethane plastic materials, the following components are suitable for use as base components.
Suitable polyisocyanates include, for example, the aliphatic, cycloaliphatic, araliphatic, aromatic and heterocyclic polyisocyanates such as those described by, for example, W. Siefken in Justus Liebigs Annalen der Chemie, 362, pages 75 to 136. These polyisocyanates include those compounds of the general formula:
Q(NCO).sub.n,
wherein
n represents a number of from 2 to 5, preferably 2 to 3;
and
Q represents an aliphatic hydrocarbon radical having 2 to 18, preferably 6 to 10 carbon atoms; a cycloaliphatic hydrocarbon radical having 4 to 15, preferably 5 to 10 carbon atoms; an aromatic hydrocarbon radical having 6 to 15, preferably 6 to 13 carbon atoms.
Such polyisocyanate are specified in, for example, German 2,832,253, pages 10 to 11.
Normally, the technically easily accessible polyisocyanates are particularly preferred including compounds such as, for example, the 2,4- and 2,6-toluene diisocyanate, as well as any mixtures of these isomers ("TDI"), diphenylmethane diisocyanate ("MDI") and polyphenylpolymethylene polyisocyanate, such as those produced based on the aniline-formaldehyde-condensation and following phosgenation. It is also possible to use polyisocyanates commonly referred to as the "modified polyisocyanates". These may contain carbodiimide groups, urethane groups, allophanate groups, isocyanurate groups, carbamide groups and/or biuret groups. These also include those modified polyisocyanates that are derived from 2,4- and/or 2,6-toluene diisocyanate or 4,4'- and/or 2,4'-diphenylmethane diisocyanate.
The polymer polyols produced by the process of the present invention are suitable active hydrogen atom containing materials to be used in the production of polyurethane plastic materials.
In addition to the polymer polyols, it is also possible to optionally include organic compounds having at least 2 hydrogen atoms reactive with isocyanates as base components with molecular weights between 40 and 10,000 g/mol, preferably polyether polyols. These include the known addition products of cyclic ethers such as ethylene oxide, propylene oxide, styrene oxide, butylene oxide, etc. with suitable starter compounds such as, for example, polyhydroxy compounds such as alkylene glycols, glycerin, trimethylol propane, pentaerythritol, sorbitol, amines such as ethylene diamine or tolylene diamine, as well as the starter compounds themselves.
Suitable catalysts for the manufacture of polyurethane plastic materials include, for example, the known catalysts commonly used in polyurethane chemistry may be used.
It is also possible to include water and/or low-boiling hydrocarbons as blowing agents including, for example, low-boiling alkanes such as pentane, cycloalkanes, such as cyclopentane, furthermore, alkenes as well as gases like carbon dioxide that are brought into the reaction mixture under pressure. Other known additives and auxiliary agents may also be included in this reaction mixture to produce polyurethane plastic materials. These additives and auxiliary agents include, for example, surface active additives such as emulsifiers and foam stabilizers, reaction inhibitors, cell regulators of known type such as paraffin, fatty alcohols, or dimethyl polysiloxane, as well as pigments or dyestuffs, and flame retardants of known type, stabilizers against aging and environmental factors, softeners and fungistatically and bacteriostatically acting substances.
Suitable examples of optional additives and auxiliary agents such as surface active additives and foam stabilizers, reaction inhibitors, stabilizers, flame retardant substances, softeners, dyestuffs, as well as fungistatically and bacteriostatically effective substances and details about the method of application and effectiveness of these additives are discussed in detail in the Kunststoff-Handbuch, Volume VII, by G. Oertel, Carl Hanser Publishers, Munich, 1993, for example, on pages 104 to 127.
The manufacture of flexible polyurethane foam materials is done through known methods such as described in the Kunststoff Handbuch, Volume VII, by G. Oertel, Carl Hanser Publisher, Munich, 1993, on pages 139 to 263.

The invention is further illustrated but is not intended to be limited by the following examples in which all parts and percentages are by weight unless otherwise specified.
EXAMPLES
The following compounds are used in the process of the present invention.
Polyol A:
A glycerin/propylene glycol started (weight ratio 90:10) polyether, produced by the addition of PO (30%), PO/EO (40/10%) and PO (20%), and having an OH number of 56 mg KOH/g.
Polyol B:
A trimethylol propane started polyether produced by addition of PO (82.3%) and EO (17.7%), having a molecular weight of 6,000.
Polyol C:
A trimethylol propane started polyether produced by addition of PO (82.5%) and EO (17.5%), having a molecular weight of 4,800.
Polymer polyol A:
VP.PU 80WB40, commercially available from Bayer AG., solids content approx. 40%, styrene portion approx. 60%.
Macromer A:
The reaction product from one mole polyol C with 0.75 mole maleic acid anhydride, and followed by the addition of 0.9 mole ethylene oxide. The product has a double bond content of 49 meq/kg.
Macromer B:
The reaction product from one mole polyol C with 1.2 mole acrylic acid, produced through azeotropic esterification in the presence of 0.1% by weight p-toluene sulfonic acid (based on the weight of polyol C) and toluene as a solvent. The product has a double bond content of 100 meq/kg.
Macromer C:
The reaction product of one mole polyol B with 1.2 mole acrylic acid, produced through azeotropic esterification in the presence of 0.1% by weight p-toluene sulfonic acid (based on the weight of polyol B) and toluene as a solvent. The product has a double bond content of 139 meq/kg.
Macromer D:
The reaction product from one mole polyol C with the reaction product of 0.75 mole hydroxypropylacrylate and 0.825 mol toluene diisocyanate. The product has a double bond content of 56 meq/kg.
Macromer E:
The reaction product from one mole polyol B with the reaction product of 0.75 mole hydroxypropylacrylate and 0.9 mole toluene diisocyanate. The product has a double bond content of 71 meq/kg.
Macromer F:
The reaction product from one mole polyol C with one mole 1-(1-isocyanato-1-methylethyl)-3-(1-methylethenyl)-benzene. The product has a double bond content of 228 meq/kg.
Macromer G:
The reaction product from one mole polyol B with
one mole 1-(1-isocyanato-1-methylethyl)-3-(1-methylethenyl)-benzene. The product has a double bond content of 211 meq/kg.
Enol ether A:
(Cyclohex-3-enylidenemethoxymethyl)-benzene (cis, trans-isomer mixture), commercially available under the name Vulkazon AFD from Bayer AG. ##STR3## Enol ether B:
(Cyclohex-3-enylidene)-cyclohexylether (cis, trans-isomer mixture), produced by the reaction of cyclohex-3-en-carbaldehyde with cyclohexanol in the presence of p-toluene sulfonic acid and quinoline (similar to the method described in EP 008,444, believed to correspond to U.S. Pat. No. 4,230,823). b.p.: 82.degree. C. at 0.15 mbar ##STR4## Enol ether C:
(Norbornen-3-enylidenemethoxymethyl)-benzene (cis,trans-isomer mixture) produced by the reaction of 5-norbornen-2-aldehyde with benzyl alcohol in the presence of p-toluene sulfonic acid and quinoline (similar to the method described in EP 008,444, believed to correspond to U.S. Pat. No. 4,230,823). b.p.:106.degree. C. at 0.1 mbar. (not according to the invention). ##STR5## Enol ether D:
Butylidene-benzylether (cis,trans-isomer mixture) produced by the reaction of 2-butyraldehyde with benzyl alcohol in the presence of p-toluene sulfonic acid and quinoline (similar to the method described in EP 008,444, believed to correspond to U.S. Pat. No. 4,230,823). b.p.: 73.degree. C. at 0.2 mbar. (not according to the invention). ##STR6## Enol ether E:
(Cyclohex-3-enylidene)-butylether (cis,trans-isomer mixture), produced through transformation of cyclohex-3-en-carbaldehyde with n-butanol in the presence of p-toluene sulfonic acid and quinoline (similar to the method described in EP 008,444, believed to correspond to U.S. Pat. No. 4,230,823)., b.p.: 68.degree. C. at 0.1 mbar. ##STR7## Guidelines for the Production of Polymer Polyols:
A mixture consisting of 375.3 g polyol, 250.2 g styrene, 166.8 g acrylonitrile 8.34 g enol ether (or other chain transfer agents), 5.21 g 2,2'-azobis(2-methylbutyronitrile) and 144 g toluene is uniformly metered over a period of two hours into a mixture of 225.2 g polyol and 25 g macromer under agitation at 125.degree. C. This is followed by post agitation for 30 minutes at 125.degree. C. Then, a solution of 0.92 g 2,2'-azobis(2-methylbutyronitrile) in 25.4 g toluene is quickly added, and agitation is continued for another hour at 125.degree. C. Subsequently, the toluene and other volatile components are distilled off at 125.degree. C. first with the aid of a water aspirator (15 mbar) for more than an hour, and then under reduced pressure for two hours (<2 mbar). The product is discharged through a sieve having a mesh size of 100 .mu.m after cooling to approx. 100.degree. C. Performance of the Residue Test:
Approx. 3 ml polymer polyol is placed in a 10 ml beaded rim glass whose inside walls are completely wetted with the polymer polyol. After standing for 24 hours at room temperature, the residue on the glass walls is evaluated by counting the number of particles of approx. 5 to 30 .mu.m diameter.
good: up to approx. 10 particles per cm.sup.2
medium: from approx. 10 to 30 particles per cm.sup.2
poor: from approx. 30 particles per cm.sup.2
EXAMPLES 1
Polymer polyols were produced from a system wherein polyol A was used as the base polyol, macromer A was used as the macromer, and different chain transfer agents were used according to the general production instructions above. The reaction was also carried out without chain transfer agents for comparison purposes.
The results are summarized in the following table:
TABLE 1______________________________________ Chain Viscosity transfer (mPa .multidot. s/Example agent 25.degree. C.) Residue______________________________________1 -- 3990 good2 isopropanol 3670 [1] poor3 2-butanol 3710 good4 methylethylketone 3720 good5 tetrachloromethane 3740 good6 1-dodecylmercaptan 4990 medium7 enol ether A 3240 good8 enol ether B 3190 good______________________________________ [1] unfiltrable product
The polymer polyols produced from enol ethers A and B in accordance with the present invention gave the lowest viscosity in this series of experiments.
EXAMPLES 9-19
Polymer polymers were produced from a system wherein polyol A was used as the base polyol, macromer B was used as the macromer, and different chain transfer agents were used according to the general production instructions above. The reaction was also carried out without chain transfer agents for comparison purposes. The results are summarized in the following table:
TABLE 2______________________________________ Chain Viscosities transfer (mPa .multidot. s/Example agent 25.degree. C.) Residue______________________________________ 9 -- -- [2] --10 isopropanol 7450 [1] poor11 2-butanol 7970 [1] poor12 methylethylketone -- [3] --13 tetrachloromethane 4000 good14 1-dodecylmercaptan 29850 poor15 enol ether A 3550 good16 enol ether B 3450 good17 enol ether C -- [3] --18 enol ether D 4480 medium19 enol ether E 3480 good______________________________________ [1] unfiltrable product [2] The reaction had to be interrupted because the preparation was no longer stirrable due to high viscosity. [3] The reaction had to be interrupted because the product was lumpy and unstable.
The enol ethers A, B and E based on the invention gave finely dispersed, low viscosity products in this series, while the enol ethers C and D and the other chain transfer agents not based on the invention resulted in dispersions which were either unstable or coarse, and exhibited higher viscosities.
EXAMPLES 20-27
Polymer polyols were produced from a system wherein polyol A was used as a base polyol, macromer C was used as the macromer, and different chain transfer agents were used according to the general production instructions. The reaction was also carried out without chain transfer agents for comparison purposes. The results are summarized in the following table:
TABLE 3______________________________________ Chain Transfer ViscosityExample Agent (mPa .multidot. s/25.degree. C.) Residue______________________________________20 -- 4950 [1] poor21 isopropanol 4330 [1] poor22 2-butanol 4710 [1] poor23 methylethylketone 4630 poor24 tetrachloromethane 4100 medium25 1-dodecylmercaptan -- [2] --26 enol ether A 3550 good27 enol ether B 3300 good______________________________________ [1] unfiltrable product [2] The reaction had to be interrupted because the preparation could no longer be stirred due to high viscosity.
Enol ethers A and B when used in combination with macromer C in accordance with the present invention, also resulted in finely dispersed, low viscosity products. By comparison, the other chain transfer agents resulted in dispersions which were either unstable or coarse, and exhibited higher viscosities.
EXAMPLE 28-35
Polymer polyols were produced from a system wherein polyol A was used as the base polyol, macromer D as the macromer, and different chain transfer agents were used according to the general production instructions above. The reaction was also carried out without chain transfer agents for comparison purposes.
The results are summarized in the following table:
TABLE 4______________________________________ Chain transfer ViscosityExample agent (mPa .multidot. s/25.degree. C.) Residuee______________________________________28 -- 19000 [1] poor29 isopropanol -- [3] --30 2-butanol -- [2] --31 methylethylketone -- [2] --32 tetrachloromethane 5840 medium33 1-dodecylmercaptan 13200 poor34 enol ether A 3140 good35 enol ether B 3340 good______________________________________ [1] unfiltrable product [2] The reaction had to be interrupted because the preparation was no longer stirrable due to high viscosity [3] The reaction had to be interrupted because the product was lumpy and unstable.
When enol ethers A and B are used in combination with the macromer D, the advantage of the present invention becomes clearer. Stable, low viscosity products are only obtained when the specific enol ethers of the present invention are used.
EXAMPLES 36-43
Polymer polyols were produced from a system wherein polyol A was used as the base polyol, macromer E as the macromer, and different chain transfer agents were used according to the general production instructions above. The reaction was also carried out without chain transfer agents for comparison purposes.
The results are summarized in the following table:
TABLE 5______________________________________ Chain transfer ViscosityExample agent (mPa .multidot. s/25.degree. C.) Residue______________________________________36 -- 7110 [1] poor37 isopropanol 4800 [1] poor38 2-butanol 5180 poor39 methylethylketone 5100 poor40 tetrachloromethane 4850 medium41 1-dodecylmercaptan 5250 medium42 enol ether A 3550 good43 enol ether B 3260 good______________________________________ [1] unfiltrable product
Only the enol ethers A and B in accordance with the present invention resulted in finely dispersed, low viscosity products.
EXAMPLES 44-51
Polymer polyols were produced from a system wherein polyol A was used as the base polyol, macromer F as the macromer, and different chain transfer agents were used according to the general production instructions above. The reaction was also carried out without chain transfer agents for comparison purposes.
The results are summarized in the following table:
TABLE 6______________________________________ Chain transfer ViscosityExample agent (mPa .multidot. s/25.degree. C.) Residue______________________________________44 -- -- [2] --45 isopropanol -- [2] --46 2-butanol -- [2] --47 methylethylketone -- [2] --48 tetrachloromethane 6410 poor49 1-dodecylmercaptan 5870 poor50 enol ether A 4410 good51 enol ether B 4020 good______________________________________ [2] Reaction had to be interrupted because the preparation could no longe stirred due to high viscosity.
The advantage of the enol ethers A and B according to the invention becomes particularly clear when these are used in combination with macromer F. Only the enol ethers required by the present invention resulted in fine, low viscosity dispersions. Dispersions which were either unstable or coarse, and exhibited higher viscosities were obtained with the other chain transfer agents.
EXAMPLE 52-59
Polymer polyols were produced from a system wherein polyol A was used as the base polyol, macromer G was used as the macromer, and different chain transfer agents were used according to the general production instructions above. The reaction was also carried out without chain transfer agents for comparison purposes.
The results are summarized in the following table:
TABLE 7______________________________________ Chain transfer ViscosityExample agent (mPa .multidot. s/25.degree. C.) Residue______________________________________52 -- 9500 poor53 isopropanol 6800 [1] poor54 2-butanol 6330 poor55 methylethylketone 5950 poor56 tetrachloromethane 4940 medium57 1-dodecylmercaptan 3800 medium59 enol ether A 3480 good60 enol ether B 3780 good______________________________________ [1] unfiltrable product
Only enol ethers A and B which are according to the invention resulted in finely dispersed, low viscosity products.
EXAMPLES 60-91
These examples demonstrate the manufacture of flexible foam materials from the polymer polyols produced according to the invention as set forth hereinabove in Examples 8, 15, 27, 35, 42, 50 and 59. The following procedure was used.
A mixture comprising all of the components (except the catalyst and polyisocyanate) was intensely mixed. The catalyst 3 was added, and the mixture was briefly mixed. Then, the polyisocyanate was added while stirring. Subsequently, the reaction mixture was poured into an open mold, wherein it foams up to form a flexible foam.
In addition to the components described above, the following components were used to manufacture the flexible foams.
Catalyst 1
Desmorapid DEMEA, commercially available from Rhein Chemie, Rheinau
Catalyst 2
RC-PUR activator 108, commercially available from Rhein Chemie, Rheinau
Catalyst 3
Desmorapid SO, commercially available from Rhein Chemie, Rheinau
Stabilizer:
Stabilizer OS 22, commercially available from Bayer AG
Isocyanate:
Toluylene diisocyanate (Desmodur T 80, commercially available from Bayer AG)
The results of the foaming tests are summarized in the table below: (quantity in weight portions each).
The properties of the foams were determined using the following test methods:
______________________________________Raw Density DIN 53420Tensile Strength DIN 53571Breaking Elongation DIN 53571Compression Force DIN 53577______________________________________
TABLE 8__________________________________________________________________________Results of the foam recipes with 10% solids (Information in parts byweight; Isocyanate Index 108;raw density approx. 23 to 24 kg/m.sup.3) Example Example Example Example Example Example Example Example 60 61 62 63 64 65 66 67__________________________________________________________________________Polyol A 75 75 75 75 75 75 75 75Polymer Polyol A 25Example 8 25Example 15 25Example 27 25Example 35 25Example 42 25Example 50 25Example 59 25Water 4.5 4.5 4.5 4.5 4.5 4.5 4.5 4.5Stabilizer 1 1 1 1 1 1 1 1Catalyst 1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1Catalyst 2 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05Catalyst 3 0.13 0.15 0.15 0.15 0.15 0.15 0.15 0.15Foamability very very very very very very very very good good good good good good good goodOpen cells very very very very very very very very good good good good good good good goodRaw density (kg/m.sup.3) 23 24 24 23 24 24 24 24Tensile strength 121 126 126 145 137 123 146 128(kPa)Elongation at Break 131 103 117 128 123 97 125 101(%)Hardness 4.4 5.5 4.90 5.1 5.3 5.6 5.4 5.740% (kPa)Grip/Elasticity very very very very very very very good good good good good good good good__________________________________________________________________________
TABLE 9__________________________________________________________________________Results of the foam recipes with 20% solids (Information in weight parts;Isocyanate Index 108;raw density approx. 23 to 24 kg/m.sup.3) Example Example Example Example Example Example Example Example 68 69 70 71 72 73 74 75__________________________________________________________________________Polyol A 50 50 50 50 50 50 50 50Polymer polyol A 50Example 8 50Example 15 50Example 27 50Example 35 50Example 42 50Example 50 50Example 59 50Water 4.5 4.5 4.5 4.5 4.5 4.5 4.5 4.5Stabilizer 1 1 1 1 1 1 1 1Catalyst 1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1Catalyst 2 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05Catalyst 3 0.13 0.13 0.13 0.13 0.13 0.13 0.13 0.13Foamability very very very very very very very very good good good good good good good goodOpen cells very very very very very very very very good good good good good good good goodRaw density (kg/m.sup.3) 23 23 23 23 23 24 23 23Tensile strength 147 121 148 144 148 144 137 141(kPa)Elongation at Break 126 95 97 86 100 102 103 108(%)Hardness 5.7 6.1 6.1 6.8 6 6.1 5.9 5.640% (kPa)Grip/elasticity very very very very very very very very good good good good good good good good__________________________________________________________________________
TABLE 10__________________________________________________________________________Results of the foam recipes with 10% solids (Information in weight parts,Isocyanate Index 108;raw density approx. 37 to 39 kg/m.sup.3) Example Example Example Example Example Example Example Example 76 77 78 79 80 81 82 83__________________________________________________________________________Polyol A 75 75 75 75 75 75 75 75Polymer polyol A 25Example 8 25Example 15 25Example 27 25Example 35 25Example 42 25Example 50 25Example 59 25Water 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5Stabilizer 0.7 0.7 0.7 0.7 0.7 0.7 0.7 0.7Catalyst 1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1Catalyst 2 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05Catalyst 3 0.13 0.12 0.12 0.12 0.12 0.12 0.12 0.12Foamability very very very very very very very very good good good good good good good goodOpen cells very very very very very very very very good good good good good good good goodRaw density (kg/m.sup.3) 37 38 38 38 38 39 38 38Tensile strength 156 142 104 160 149 147 157 46(kPa)Elongation at Break 155 142 114 156 141 138 145 148(%)Hardness 5.6 5.2 5 5.3 5.4 5.3 5.5 5.440% (kPa)Grip/elasticity very very very very very very very very good good good good good good good good__________________________________________________________________________
TABLE 11__________________________________________________________________________Results of the foam recipes with 20% solids (Information in weight parts;Isocyanate Index 108;raw density approx. 37 to 39 kg/m.sup.3) Example Example Example Example Example Example Example Example 84 85 86 87 88 89 90 91__________________________________________________________________________Polyol A 50 50 50 50 50 50 50 50Polymer polyol A 50Example 8 50Example 15 50Example 27 50Example 35 50Example 42 50Example 50 50Example 59 50Water 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5Stabilizer 0.7 0.7 0.7 0.7 0.7 0.7 0.7 0.7Catalyst 1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1Catalyst 2 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05Catalyst 3 0.13 0.12 0.12 0.12 0.12 0.12 0.12 0.12Foamability very very very very very very very very good good good good good good good goodOpen cells very very very very very very very very good good good good good good good goodRaw density (kg/m.sup.3) 36 38 38 37 38 39 37 39Tensile strength 182 159 187 195 181 162 166 173(kPa)Elongation at Break 148 109 131 146 131 108 121 110(%)Hardness 6.4 6.9 6.6 6.6 6.8 6.8 6.6 740% (kPa)Grip/elasticity very very very very very very very very good good good good good good good good__________________________________________________________________________
The foaming Examples 60 to 91 show that the finely dispersed, low viscosity polymer polyol dispersions produced according to the present invention resulted in foams with comparable characteristics to those foams produced from actual commercial products which have a higher viscosity. Foam recipes containing the dispersions produced according to the present invention can be more easily processed due to their lower viscosities at the same filler content. In addition, higher solids contents can be used with them under consideration of the same maximum processing viscosity, which delivers foams with appropriately higher rigidities.
Although the invention has been described in detail in the foregoing for the purpose of illustration, it is to be understood that such detail is solely for that purpose and that variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention except as it may be limited by the claims.

Number	Name	Date
RE33291	Ramlow et al.	Aug 1990
3304273	Stamberger	Feb 1967
3383351	Stamberger	May 1968
3652639	Pizzini et al.	Mar 1972
3823201	Pizzini et al.	Jul 1974
4230823	Alberts et al.	Oct 1980
4342840	Kozawa et al.	Aug 1982
4390645	Hoffman et al.	Jun 1983
4460715	Hoffman et al.	Jul 1984
4652589	Simroth et al.	Mar 1987
5093412	Mente et al.	Mar 1992

Number	Date	Country
1152536	Aug 1963	DEX
1152537	Aug 1963	DEX

Low viscosity polymer polyols a process for their production as well as the manufacture of polyurethane from materials

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (11)

Foreign Referenced Citations (2)