Machinable positive image model material for shape deposition manufacturing

Abstract

A manufacturing method comprising the steps of forming at first solidified wax layer of a desired shape, depositing onto the first solidified wax layer at least one layer of a liquid resin formulation, solidifying the layer of liquid resin formulation, depositing a second wax layer on to the combination of the first solidified wax layer and the layer of solidified resin formulation, solidifying the second wax layer, and separating the solidified resin formulation from first and second wax layers. Preferably, the resin formulation comprises at least one monofunctional water soluble vinyl or acrylic monomer in combination with a low molecular weight aliphatic polymer having acrylic or methacrylic acid functionality. The solidified wax and resin formulation layers can be machined as may be desired to form mold of a given shape comprising wax layers when the layer of formulation is separated from the wax layers.

Description

FIELD OF THE INVENTION

[0002] This invention relates to shape deposition manufacturing of products having a complex configuration from using a liquid resin formulation that may be deposited in layers, polymerized (preferably photopolymerized) and precision machined.

BACKGROUND OF THE INVENTION

[0003] Shape Deposition Manufacturing (SDM) technology comprises fabrication of parts or products by the sequential deposition, solidification, and precision Computer Numeric Controlled (CNC) machining of wax layers which are deposited upon one another until a desired product mold results. See e.g., U.S. Pat. Nos. 5,207,371; 5,286,573; 5,301,415 and 5,301,863. A liquid resin (i.e., polyurethane, epoxy, or ceramic gelcasting slurry) is subsequently cast into the wax mold and cured to produce a desired polymer or green ceramic part or product having a complex shape.

[0004] Unfortunately, many parts or products have complex geometries (i.e., internal chambers or overhang features) that make it difficult to accurately fabricate wax molds in successive layers without causing slumpage and remelting of previously deposited and CNC machined wax layer features. In particular, the highly fluid nature of the molten wax coupled by its slow solidification rate often causes a newly deposited layer of wax to slump considerably prior to its solidification on an adjacent or previously deposited layer. This can detract from product dimensional accuracy of the wax mold and thus the product will have imperfections. The problem of casting or molding complex parts or products using a layer by layer wax technique to form the complex mold has perplexed those of skill in the art.

SUMMARY OF THE INVENTION

[0005] Briefly, in accordance with the present invention, one is able to prepare accurate parts or products by depositing and photocuring liquid resin layers within each solidified and machined wax layer prior to the deposition of a subsequent wax layer. In other words, parts are fabricated by the deposition, solidification, and machining of successive wax and cured resin layers until the final mold encapsulating a resin formulated part results. The wax and resin layer solidification is accomplished by cooling and UV photopolymerization (e.g., photocuring) respectively. By following the described steps, a completed wax mold results with an internal core or cavity filled with a photocured resin product. The photocured resin product has the dimensions of the final desired molded part or product. Thus, the resin core may be washed from the mold by immersion in a neutral or weakly alkaline aqueous solution (preferably a solution having a pH of greater than about 8).

[0006] The resin which is preferred for use in the process is composed of at least one monofunctional water soluble vinyl or acrylic monomer (e.g., N-Vinyl pyrrolidone or N,N′-Dimethylacrylamide) combined with a low molecular weight aliphatic polymer having acrylic acid (AA) or methacrylic acid (MA) functionality. A major advantage of the cured resin of the present invention is that it has dimensional stability even after exposure to high ambient humidity, yet readily dissolves in aqueous solutions. This provides an attractive means for fabricating fugitive parts or products, support materials, or soluble cores for wax molds constructed using Shape Deposition Manufacturing technology.

[0007] An object of the present invention is to provide formulations that have the ability to photocure as very thick layers, e.g. a 3 millimeter resin layer, as opposed to thin wax layers (e.g., 100 micronmeter wax layers typically encountered in accordance with conventional Shape Deposition Manufacturing technology) over a 2 minute period in a single pass using ultraviolet (UV) radiation.

[0008] Another object of the present invention is to provide techniques and formulations that enable casting or molding parts and products that have smooth surfaces and with minimal chipping.

[0009] A further objection of the present invention is to provide techniques and formulations that provide the ability to fabricate positive image structures.

[0010] Another object of the present invention is to provide techniques and formulations that have the ability to fill fine crevices and machine features in a wax mold as it is being manufactured.

[0011] A further object of the present invention is to provide techniques and formulations that result in higher strength molds than conventional Shape Deposition Manufacturing technology.

[0012] Yet another object of the present invention is to provide techniques and formulations that enable manufacture of a completely soluble, organic molded product with no mineral filler.

[0013] Additional objects of the present invention include the provision of techniques and formulations for making molds that incorporate the use of sucrose, which reduces shrinkage and reduces exotherm (i.e., energy) on curing, resulting in less bubbling and smoother surfaces in the part and/or mold. Notably, the refractive index of sucrose is similar to the resin monomers of the present invention. Further, it has been discovered that sucrose has minimal effect upon UV transmission and resin curing.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] In the detailed description which follows, reference will be made to the drawing comprised of a single FIGURE which stepwise illustrates the method of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] In FIG. 1, each step of a preferred embodiment of the manufacturing method of the present invention is illustrated. In Step 1, a resin layer 11 is deposited onto a first mold or base layer 10, which is made of mold material 14. In a preferred embodiment, the mold material 14 is a wax. Prior to deposit of the resin layer 11, the mold layer 10 can be formed by depositing liquid wax into a layer border (not shown), and then solidifying the wax by cooling the wax. Mold layer can be machined if desired to any suitable shape. Prior to curing resin layer 11, the resin layer 11 can be maintained on top of first mold layer 10 in any suitable manner. For example, a layer border (not shown) can be used to maintain the resin layer 11 on top of first mold layer 10, and then removed after the resin layer 11 is cured. In a preferred embodiment, the resin layer 11 is hardened by photocuring. Preferably, photocuring is accomplished by subjecting the resin layer 11 to UV radiation. Further, in a preferred embodiment, the UV radiation causes the resin material to photopolymerize, thereby hardening the resin material. Other mold layers and resin layers can also be maintained after deposition and prior to hardening using layer borders (not shown). The solidified mold layers and the cured resin layers can be machined as may be desired. As shown in FIG. 1, after curing, the resin layer 11 can be machined to any desired shape in Step 1, in this case a polygon 13.

[0016] In Step 2, a second mold layer 20 is then deposited so that is surrounds the sides of polygon 13. Second mold layer 20 is made of wax mold material 14 just as the first mold or base layer 10. Second mold layer 20 is then hardened by cooling.

[0017] In Step 3, a third mold layer 30 is then deposited onto second mold layer 20 and polygon 13. Mold layer 30, which is also be made of wax mold material 14, can then be hardened by cooling and machined to define any desired space 32 in Step 3, in this case a mirror image of polygon 13.

[0018] In Step 4, a second resin layer 41 is deposited into the space 32 and is subsequently photocured.

[0019] In Step 5, a fourth mold layer 50 deposited onto the third mold layer 30 and the second resin layer 41. Fourth mold layer 50, which is also made of wax mold material 14, can be hardened by cooling and machined to define any desired shape 52 in Step 5. In this example, mold layer 50 is machined in a manner so that in combination with resin layer 41 and mold layer 30, space 52 is defined thereby.

[0020] In Step 6, a third resin layer 61 is deposited into space 52 and onto the second resin layer 41, mold layer 50 and mold layer 30, and after curing, third resin layer 61 is machined as desired. In this example, resin layer 61 defines a parallelogram 63. Parallelogram 63 and mold layer 30 define space 62.

[0021] In Step 7, a fifth mold layer 70 is deposited to the space 62 previously filled by third resin layer 61 prior to being removed away (by machining) in Step 6. Mold layer 70 is made of mold material 14 just as the prior mold layers 10, 20, 30, and 50, and hardened by cooling.

[0022] In Step 8, a sixth mold layer 80 is deposited onto fifth mold layer 70 and third resin layer 61, and after hardening by cooling, mold layer 80 is then machined as desired. Mold layer 80 is made of mold material 14 just as the prior mold layers.

[0023] In Step 9, the first resin layer 1, the second resin layer 41, and the third resin layer 61, which in combination define a mold cavity or product shape, can be dissolved using a suitable solvent. A suitable solvent may include, but is not limited to, water, aqueous alkaline and/or detergent solutions. Preferably, the solvent has a pH of greater than about 8. Mold layers 10, 20, 30, 50, 70 and 80 then define a space or mold cavity 92.

[0024] In Step 10, a suitable part material 100 is then deposited into the space 92 previously filled with the resin layers 11, 41, and 61. Part material 100 is then allowed to harden or cure.

[0025] As shown in FIG. 1, in Step 11a, mold layers 10, 20, 30, 50, 70 and 80 are removed from part material 100 using a suitable method, such as dissolving away the mold layers with a suitable solvent and/or detergent and/or vaporizing/pyrolyzing the wax mold layers using heat. In Step 12a, the part material 100 can be further machined to a desired shape 120.

[0026] Alternatively, as shown in FIG. 1, in Step 11b, mold layer 80 is machined away from part material 100 and part material 100 can be machined to a desired shape 120. In Step 12b, mold layers 10, 20, 30, 50 and 70 are removed from shape 120 using a suitable method, such as dissolving away the mold layers with a suitable solvent and/or detergent and/or burning off the mold layers using heat. Shape 120 is the same resulting shape in accordance with following the method shown in Steps 11b and 12b with the method shown in Steps 11a and 12a.

[0027] A wide variety of shapes that can be made in accordance with the present invention. In accordance with the present invention, much thicker layers can be used than in conventional manufacturing techniques, and the time to make a product with a given shape using the present invention is much shorter than attainable using conventional manufacturing techniques wherein only wax layers are used. For example, the present invention can cure a 3 millimeter thick resin layer over a two minute period in a single pass using UV radiation, whereas conventional techniques can only cure a 100 micronmeter wax layer in a single pass using UV radiation over the same period time. Because the resin acts as a support, thicker layers may be employed in the described process.

[0028] As previously noted, the preferred resin formulations of the present invention comprise at least one monofunctional water soluble vinyl or acrylic monomer (e.g., N-Vinyl pyrrolidone or N,N′-Dimethylacrylamide) combined with a low molecular weight aliphatic polymer having acrylic acid (AA) or methacrylic acid (MA) functionality. The AA or MA functionality may be either incorporated into the main chain backbone or as pendant groups. The AA or MA functionality can be any suitable polymer, for example, polyethylene co-acrylic acid, polystyrene co-acrylic acid, or polyalkylacrylate co-acrylic acid. The acid groups present in the AA or MA derived polymer have been shown to strongly hydrogen bond to the polar carbonyl groups present in the monofunctional water soluble monomers. These hydrogen bonds are sufficiently strong that they render the monofunctional monomer as well as its UV photocured polymer product to be insoluble in water. See E. M. Pearce, S. P. Ting, & T. K. Kwei, J. Polym. Sci. Polym. Letters Ed. 18 201 (1980); and K. R. Shah, Polymer 28 1212-6 (1987).

[0029] Addition of a weakly alkaline aqueous solution to the photocured resin neutralizes the acid groups and disrupts the interchain hydrogen bonded complexes which enable the polymers to become dissolved in water. Suitable bases which yield water sufficiently alkaline include dilute ammonium hydroxide and its carbonate salts, as well as alkali/alkaline earth hydroxides. Other suitable bases may be employed. Furthermore, this interchain association is sufficiently strong that the resulting polymer complex has a heat distortion temperature above that of either individual polymer. See E. M. Pearce, S. P. Ting, & T. K. Kwei, J. Polym. Sci. Polym. Letters Ed. 18 201 (1980). The enhanced interchain interaction arising from complexation may enhance the strength and toughness of the polymer materials as reflected by its facile CNC machinability and resistance to chipping.

[0030] Some U.S. patents describe compositions between linear water soluble polymers and polymers having carboxylic acid functionality, whereby the acid complex is touted as being water insoluble yet readily dissolved in alkaline solution. These materials are claimed to be useful as strippable coatings for floors, automobiles, and other protective coatings. Examples of alkali strippable coatings include: J. S. Shih, U.S. Pat. No. 4,927,667, (1990); G. W. Grogan, U.S. Pat. No. 5,604,282 (1997); R. D. Meiner, U.S. Pat. No. 4,046,726 (1977); R. Swindler, U.S. Pat. No. 5,719,221 (1998); R. G. Adams, U.S. Pat. No. 4,485,131 (1984). However, none of these patents teach or suggest the use of linear water soluble polymers and polymers having carboxylic acid functionality for use in shape deposition manufacturing as described herein.

[0031] Other components may be incorporated into the resin formulation of the present invention to enhance its properties. In particular, a sugar, such as a confectioner's powdered sugar, is added as a soluble filler. In addition, a surfactant is added to enhance the resin wetting upon the wax surface. A variety of commercial substituted acetophenone or benzophenone UV photoinitiators, as well as substituted amine or phosphine oxide synergists, can also be added to impart rapid photocuring properties to the resin.

[0032] Examples of useable resin compositions in accordance with the preferred embodiments of the present invention are listed in tabular form below (Tables I through V). All of these materials can be readily cured using UV light obtained from either natural or mercury vapor lamps. An example of a mercury vapor lamp is a 200 W, 200-400 nm lamp manufactured by UVEXS Inc., Sunnyvale, Calif.

[0033] In Examples I through V, the liquid ingredients were initially mixed together at room temperature followed by heating to 80-90° C., upon which the polyethylene-co-acrylic acid was then added. The polyethylene co-acrylic acid is a waxy solid and is added as prills to the heated monomers while stirring. The mixture was then stirred for about 5-10 minutes to uniformly disperse the polymer in the liquid. The suspension was subsequently cooled to room temperature prior to use. Example V includes the additional step of mixing sucrose last into the suspension at room temperature.

[0034] The benefits of the present invention using the resins described herein include:

[0035] (a) the ability to photocure very thick resin layers, e.g. a 3 millimeter layer, as opposed to 100 micronmeter wax layers over a 2 minute period in a single pass using UV radiation;

[0036] (b) the ability to machine the resin material easily and effectively for smooth surfaces with minimal chipping;

[0037] (c) the ability to fabricate positive image structures;

[0038] (d) due to the low viscosity of the resin material, the ability to fill fine crevices and machine features in the wax mold as it is being fabricated;

[0039] (e) higher strength molds; and

[0040] (f) no mineral filler—thereby providing a completely soluble, organic system.

[0041] The additional benefits of using a sugar as a filler, i.e. sucrose, in the present invention include:

[0042] (a) lower shrinkage on curing;

[0043] (b) lower exotherm on curing, and thus less bubbling;

[0044] (c) a refractive index match between sucrose and resin monomers;

[0045] (d) minimal effect upon UV transmission/resin curing; and

[0046] (e) sugar is typically a lower cost material than resin.

[0047] Sucrose refractive index=1.5376 (source: Handbook of Chemistry & Physics, 66th Edition (1985-86) CRC Press, Boca Raton, Fla.); N-vinylpyrrolidone refractive index=1.5120.

EXAMPLE 1

[0048]

		Concentration
Component	Function	(wt. %)
N-Vinyl Pyrrolidone	Monomer	74.0
Surfadone LP-300*	Surfactant	1.0
1-Dodecyl-2-Pyrrolidone
Polyethylene-co-acrylic acid**	Toughening agent/	6.0
	complexing agent
N,N′-dimethylacrylamide	Monomer	10.0
Ethyl-4-(dimethyl-amino)-benzoate	Photocure synergist	2.0
Irgacure 1700***	Photoinitiator	5.0
N-methyldiethanolamine	Photocure synergist	2.0
*Trademark of ISP, Inc., Wayne, NJ
**A-C 5120 Copolymer exhibiting 92 degrees C. melting point & 120 Acid Number, from Allied Signal Advanced Materials, Morristown, NJ
***mixture containing bis(2,6-Dimethoxybenzoyl)(2,4,4-trimethylpentyl)phosphine oxide & 2-Hydroxy-2-methyl-1-phenyl-1-propanone obtained from Ciba Specialty Chemicals Corp., White Plains, NY

EXAMPLE II

[0049]

		Concentra-
Component	Function	tion (wt. %)
N-Vinyl Pyrrolidone	Monomer	63.6
N,N′-dimethylacrylamide	Monomer	22.0
Ethyl-4-(dimethyl-amino)-benzoate	Photoinitiator synergist	3.0
N-methyldiethanolamine	Photoinitiator synergist	3.0
2,2-Dimethoxy-2-Phenyl	Photoinitiator	5.0
acetophenone
Polystyrene-coacrylic acid Joncryl	Toughening agent/	3.4
690*	complexing agent
*Copolymer exhibiting 16,500 MW, & 240 Acid Number (NV), from S.C. Johnson Polymer Sturtevant, WI

EXAMPLE III

[0050]

		Concentration
Component	Function	(wt. %)
N-Vinyl Pyrrolidone	Monomer	76.0
Surfadone LP-300*	Surfactant	1.0
1-Dodecyl-2-Pyrrolidone
Polyethylene-co-acrylic acid**	Toughening Agent/	6.0
	complexing agent
N,N′-dimethylacrylamide	Monomer	12.0
Irgacure 1700***	Photoinitiator	5.0
*Trademark of ISP, Inc., Wayne, NJ
**A-C 5120 Copolymer exhibiting 92 degrees C. melting point & 120 Acid Number, from Allied Signal Advanced Materials, Morristown, NJ
***mixture containing bis(2,6-Dimethoxybenzoyl)(2,4,4-trimethylpentyl)phosphine oxide & 2-Hydroxy-2-methyl-1-phenyl-1-propanone obtained from Ciba Specialty Chemicals Corp., White Plains, NY

EXAMPLE IV

[0051]

		Concentration
Component	Function	(wt. %)
N-Vinyl Pyrrolidone	Monomer	68.1
N,N′-dimethylacrylamide	Monomer	20.0
Irgacure 1700	Photoinitiator	6.0
Carboset 526*	Toughening Agent/	6.9
Polyalkylacrylate-co-acrylic acid	complexing agent
*B F. Goodrich Chemical Corp. (Cleveland, OH)

EXAMPLE V

[0052]

			Concentration
Component	Function	Manufacturer	(wt. %)
Polyethylene-co-acrylic	Toughening	Allied Signal Specialty Materials,	1.50
acid**	Agent	Morristown, NJ
Surfadone LP-300*	Surfactant	International Specialty Products,	1.00
Surfactant		Wayne, NJ
N-Vinyl Pyrrolidone	Monomer	International Specialty Products,	48.50
Monomer		Wayne, NJ
-- A.C.S. Reagent Grade
(stabilized with NaOH)
N,N′-Dimethylacrylamide	Monomer	Aldrich Chemical Company,	3.75
Monomer		Milwaukee, WI
A.C.S. Reagent Grade
Confectioner's Powdered	Soluble	Safeway Corp.,	45.00
Sugar (Sucrose)	filler	Pleasanton, CA
Irgacure 1700	Photoinitiator	Ciba Specialty Chemicals,	0.25
Photoinitiator***		Tarrytown, N.Y.
*Trademark of ISP, Inc., Wayne, NJ
**A-C 5120 Copolymer exhibiting 92 degrees C. melting point & 120 Acid Number, from Allied Signal Advanced Materials, Morristown, NJ
***mixture containing bis(2,6-Dimethoxybenzoyl)(2,4,4-trimethylpentyl)phosphine oxide & 2-Hydroxy-2-methyl-1-phenyl-1-propanone obtained from Ciba Specialty Chemicals Corp., White Plains, NY

[0053] The preferred composition ranges of the present invention are as follows.

COMPOSITION RANGES               % by Weight
Water Soluble Monofunctional Monomers
N-Vinyl Pyrrolidone              50-80
N,N′-Dimethylacrylamide          0-50
Surfactant                       1-10
1-Dodecyl-2-Pyrrolidone (Surfadone LP-300)
Toughening/Complexing Agent
Polyethylene-co-acrylic acid     1-8
Polystyrene-co-acrylic acid      1-15
Polyalkylacrylate-co-acrylic acid 1-15
Photoinitiator
Irgacure 1700                    1-8
2,2-Dimethoxy-2-Phenyl acetophenone 1-8
Photocure Synergist
Ethyl-4-(dimethylamino)-benzoate 0-8
N-methyldiethanolamine           0-8
Soluble Filler                   0-55
Confectioner's Powdered Sugar - Sucrose

[0054] The present invention has been described in detail with particular reference to certain preferred embodiments thereof, and those of skill in the art will appreciate that variations and modifications are within the spirit and scope of the present invention as set forth in the following claims.

Claims

1. A liquid resin formulation comprising at least one monofunctional water soluble vinyl or acrylic monomer in combination with a low molecular weight aliphatic polymer having acrylic or methacrylic acid functionality.

2. The liquid resin of claim 1 wherein the liquid resin formulation is hardened by photocuring.

3. The liquid resin of claim 2 wherein the liquid resin formulation is hardened by photocuring using ultraviolet radiation.

4. The liquid resin formulation of claim 1 wherein the monofunctional water soluble vinyl or acrylic monomer is N-Vinyl pyrrolidone or N,N′-Dimethylacrylamide.

5. The liquid resin formulation of claim 1 further comprising a sugar.

6. The liquid resin formulation of claim 5 wherein the sugar comprises confectioner's powdered sugar.

7. The liquid resin formulation of claim 1 wherein the low molecular weight aliphatic polymer having acrylic or methacrylic acid functionality comprises polyethylene co-acrylic acid, polystyrene co-acrylic acid, or polyalkylacrylate co-acrylic acid.

8. A manufacturing method comprising the steps of: (a) forming at first solidified wax layer of a desired shape; (b) depositing onto the first solidified wax layer at least one layer of a liquid resin formulation; (c) solidifying the layer of liquid resin formulation; (d) depositing a second wax layer on to the combination of the first solidified wax layer and the layer of solidified resin formulation; (e) solidifying the second wax layer; and (f) separating the solidified resin formulation from first and second wax layers.

9. The method of claim 8 further comprising the step of machining any of the solidified first wax layer, solidified layer of resin formulation, and second wax layer to make a mold of a desired shape comprising the wax layers when the solidified resin formulation is separated from the solidified wax layers.

10. The method of claim 8 wherein the resin formulation comprises at least one monofunctional water soluble vinyl or acrylic monomer in combination with a low molecular weight aliphatic polymer having acrylic or methacrylic acid functionality.

11. The method of claim 10 wherein the monofunctional water soluble vinyl or acrylic monomer is N-Vinyl pyrrolidone or N,N′-Dimethylacrylamide.

12. The method of claim 10 wherein the low molecular weight aliphatic polymer having acrylic or methacrylic acid functionality comprises polyethylene co-acrylic acid, polystyrene co-acrylic acid, or polyalkylacrylate co-acrylic acid.

13. The method of claim 8 wherein the step of separating the solidified resin formulation from the wax layers comprises dissolving the solidified resin formulation in a solvent.

14. The method of claim 8 wherein the step of separating the solidified resin formulation from the wax layer comprises immersing and dissolving the solidified resin formulation in the solvent.

15. The method of claim 13 wherein the solvent is an alkaline aqueous solution has a pH of greater than about 8.

16. The method of claim 14 wherein the solvent is an alkaline aqueous solution has a pH of greater than about 8.

17. A manufacturing method comprising the steps of: (a) forming at first solidified wax layer of a desired shape; (b) depositing onto the solidified first wax layer at least one layer of a liquid resin formulation; (c) solidifying the layer of liquid resin formulation; (d) depositing a second wax layer on to the combination of the solidified first wax layer and the layer of solidified resin formulation; (e) solidifying the second wax layer; (f) repeating any of the steps (a) through (e) to form successive solidified wax and resin formulation layers; and (g) separating the solidified resin formulation layers from the solidified wax layers.

18. The method of claim 17 further including the step of machining any of the solidified wax layers and layers of solidified resin formulation to make a mold of a desired shape comprising the wax layers when the layers of solidified resin formulation are separated from the solidified wax layers.

19. The method of claim 17 wherein the resin formulation comprises at least one monofunctional water soluble vinyl or acrylic monomer in combination with a low molecular weight aliphatic polymer having acrylic or methacrylic acid functionality.

20. The method of claim 17 wherein the step of separating the solidified resin formulation from the wax layers comprises dissolving the solidified resin formulation in a solvent.

21. The method of claim 8 wherein wax layer and liquid resin formulation solidification is accomplished by cooling and UV photopolymerization, respectively.

22. The method of claim 17 wherein wax and liquid resin formulation solidification is accomplished by cooling and UV photopolymerization, respectively.

23. The method of claim 13 wherein the solvent comprises dilute ammonium hydroxide and its carbonate salts, and alkali and alkaline earth hydroxides.

24. The method of claim 20 wherein the solvent comprises dilute ammonium hydroxide and its carbonate salts, and alkali and alkaline earth hydroxides.

25. The method of claim 8 wherein at least one sugar is added to the liquid resin formulation as a soluble filler prior to solidification of the resin formulation.

26. The method of claim 25 wherein the sugar comprises confectioner's powdered sugar.

27. The method of claim 8 wherein including the step of adding a surfactant to enhance the wetting of the liquid resin formulation upon the wax layer prior to solidification of the resin formulation.

28. The method of claim 8 further including the step of adding a photoinitiator to the liquid resin formulation to increase the solidifying of the liquid resin formulation.

29. The method of claim 17 wherein at least one sugar is added to the liquid resin formulation as a soluble filler prior to solidification of the resin formulation.

30. The method of claim 29 wherein the sugar comprises confectioner's powdered sugar.

31. The method of claim 17 further including the step of adding a surfactant to enhance the wetting of the liquid resin formulation upon the wax layer prior to solidification of the resin formulation.