Magnesium alloy

Information

  • Patent Grant
  • 11685975
  • Patent Number
    11,685,975
  • Date Filed
    Wednesday, December 30, 2020
    3 years ago
  • Date Issued
    Tuesday, June 27, 2023
    10 months ago
Abstract
A magnesium alloy containing, in % by mass, 0.95 to 2.00% of Zn, 0.05% or more and less than 0.30% of Zr, 0.05 to 0.20% of Mn, and the balance consisting of Mg and unavoidable impurities, wherein the magnesium alloy has a particle size distribution with an average crystal particle size from 1.0 to 3.0 μm and a standard deviation of 0.7 or smaller.
Description
FIELD OF THE INVENTION

The present invention relates to a magnesium alloy. Specifically, the present invention relates to a magnesium alloy which can be used in applications such as a medical magnesium alloy and has an excellent deformation property.


BACKGROUND OF THE INVENTION

Conventionally, various types of metal devices for medical purposes have been developed, including stents, staplers, and artificial joints. Such metal devices are embedded in a living tissue and remain within a body unless they are removed by surgery. Depending on their purposes, however, it is desired that the metal devices maintain their strength in the body for a certain period of time from the initial phase of implantation and are dissolved and absorbed in the body after repairing of the living tissue. As magnesium is a highly safe metal having low toxicity to the living tissue and is quickly dissolved and absorbed by the body fluid, magnesium and magnesium alloys are being developed for various applications as biodegradable metal materials for medical purposes.


For example, WO 2007/108450 A1 describes a biodegradable magnesium material for medical use which contains magnesium oxides or magnesium hydroxides formed by anodization on crystallized magnesium or a crystallized magnesium alloy. The document also describes that where the magnesium material contains an accessary component other than magnesium, the accessary component is unevenly distributed to crystal grain boundaries at a concentration 1.2 times higher than an average concentration in crystal grains.


Where a magnesium alloy is used as a biodegradable medical material, it is necessary that the alloy maintains its strength until tissue of an affected site is repaired. In the case where the magnesium alloy is in electric contact with a more noble metal, it is preferred to avoid phase separation of a matrix phase in order to avoid rapid galvanic corrosion of the magnesium alloy in contact with the body fluid. In addition, where a magnesium alloy is used as a material for a medical device such as a stent which undergoes deformation, the alloy preferably has suitable deformability (extensibility) and does not contain coarse precipitates (compounds) which may be trigger of a fracture of the alloy after the deformation.


The alloy preferably has uniform crystal particle size in terms of biodegradability, and the particle size can preferably be controlled to fine size so as to enable fine processing of the alloy to a stent or the like.


An object of the present invention is to provide a magnesium alloy having a fine and uniform crystal distribution and excellent deformability.


SUMMARY OF THE INVENTION

A magnesium alloy of the present invention contains, in % by mass,


0.95 to 2.00% of Zn,


0.05% or more and less than 0.30% of Zr,


0.05 to 0.20% of Mn, and


the balance consisting of Mg and unavoidable impurities, wherein


the magnesium alloy has a particle size distribution with an average crystal particle size from 1.0 to 3.0 μm and a standard deviation of 0.7 or smaller.


The magnesium alloy having the above features is composed of substantially single-phase solid solution or has a microstructure in which nanometer-sized fine Zr-bearing precipitates are dispersed in the single-phase alloy. The magnesium alloy has excellent deformability (ductility, elongation ability) because of its fine and uniform particle size and has excellent mechanical properties such as tensile strength and proof strength because of the absence of coarse precipitates at which a fracture starts.


Where the unavoidable impurities of the magnesium alloy include Fe, Ni, Co, and/or Cu, a content of each of Fe, Ni, Co, and Cu being preferably lower than 10 ppm. The magnesium alloy may preferably be free of Co as an unavoidable impurity.


In the magnesium alloy, a total content of the unavoidable impurities may preferably be 30 ppm or lower, and the magnesium alloy preferably does not contain rare-earth elements and aluminum.


The magnesium alloy may have a fracture elongation from 15 to 50% in a value measured in accordance with JIS Z2241. The magnesium alloy may preferably have a fracture elongation exceeding 30%.


The magnesium alloy may have a tensile strength from 250 to 300 MPa and a proof strength from 145 to 220 MPa in values measured in accordance with JIS Z2241.


Preferably, the magnesium alloy does not contain precipitates each having a particle size of 500 nm or larger. More preferably, the magnesium alloy does not contain precipitates each having a particle size of 100 nm or larger.


A medical device of the present invention comprises a metal member containing the above-described magnesium alloy according to the present invention. Since the medical device is made of an alloy having an excellent deformation property, the medical device can stably maintain the shape of the metal member deformed within a body, and the biodegradability of the metal member can be suitably controlled.


The present invention encompasses any combination of at least two features disclosed in the claims and/or the specification and/or the drawings. In particular, any combination of two or more of the appended claims should be equally construed as included within the scope of the present invention.





BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be more clearly understood from the following description of preferred embodiments thereof, when taken in conjunction with the accompanying drawings. However, the embodiments and the drawings are given only for the purpose of illustration and explanation, and are not to be taken as limiting the scope of the present invention in any way whatsoever, which scope is to be determined by the appended claims. In the figures,



FIG. 1 shows an SEM (scanning electron microscope) image of a microstructure of a magnesium alloy according to Example 1 of the present invention;



FIG. 2 shows an SEM image of a microstructure of a magnesium alloy according to Example 2 of the present invention;



FIG. 3 shows a graph of a particle size distribution of a magnesium alloy according to Example 1 of the present invention; and



FIG. 4 shows a graph of a particle size distribution of a magnesium alloy according to Example 2 of the present invention.





DESCRIPTION OF THE EMBODIMENTS

Hereinafter, an embodiment of the present invention will be described.


Magnesium Alloy


A magnesium alloy of the present invention contains, in % by mass, 0.95 to 2.00% of Zn, 0.05% or more and less than 0.30% of Zr, 0.05 to 0.20% of Mn, and the balance consisting of Mg and unavoidable impurities, wherein the magnesium alloy has a particle size distribution with an average crystal particle size from 1.0 to 3.0 μm and a standard deviation of 0.7 or smaller.


The present invention has revealed that plastic working of the magnesium alloy is improved by controlling a composition of the alloy to the above ranges and that properties of the magnesium alloy such as fracture elongation are improved by achieving fine and uniform particle size of the alloy.


The magnesium alloy having the above features can avoid formation of coarse precipitates which may be triggers (starting points) of fractures and thereby reduce the possibility of breakage during and after deformation. It should be noted that although Zr, which is added in order to reduce the crystal particle size of the alloy, may form precipitates, the precipitates are typically dispersed at a nanometer scale (in a size smaller than 100 nm) in the matrix phase and thus has a negligible impact on deformation and corrosion of the alloy. For example, FIG. 1 shows an SEM image of an alloy of Example 1, and FIG. 2 shows an SEM image of an alloy of Example 2, as described later. In the figures, the areas having dark contrast show the magnesium alloy (brightness differs among crystal grains), and the white bars at the bottom show a scale of 1 μm. In both of FIG. 1 and FIG. 2, only a few precipitates having particle sizes smaller than 100 nm are observed in some crystal grains of the magnesium alloy, and there are virtually no precipitates in the crystal grain boundaries.


Zinc (Zn): in % by mass, 0.95% or more and 2.00% or less


Zn is added in order to enhance the strength and elongation ability of the alloy by forming a solid solution with Mg. Where the content of Zn is less than 0.95%, a desired effect cannot be obtained. An amount of Zn exceeding 2.00% is not preferred because such an amount may exceed a solid solubility limit of Zn in Mg so that Zn-rich precipitates are formed, resulting in reduced corrosion resistance. For this reason, Zn content is regulated to 0.95% or more and 2.00% or less. The content of Zn may be less than 2.00%.


Zirconium (Zr): in % by mass, 0.05% or more and less than 0.30%


Zr hardly forms a solid solution with Mg and forms fine precipitates, providing an effect of preventing formation of coarse crystal particles of the alloy. Addition of Zr at an amount less than 0.05% cannot provide a sufficient effect. Addition of Zr at an amount equal to or exceeding 0.30% leads to formation of a large amount of precipitates, with a reduced effect of particle size reduction. In addition, corrosion and breakage would start occurring at portions where the precipitates are segregated. For this reason, content of Zr is regulated to 0.05% or more and less than 0.30%. The content of Zr may be 0.10% or more and less than 0.30%.


Manganese (Mn): in % by mass, 0.05% or more and 0.20% or less


Mn allows the alloy to have extremely fine particle size and have improved corrosion resistance. Where an amount of Mn is less than 0.05%, a desired effect cannot be obtained. An amount of Mn exceeding 0.20% is not preferred because plastic workability of the alloy tends to decrease. For this reason, Mn content is regulated to 0.05% or more and 0.20% or less. A preferable content of Mn may be 0.10% or more and 0.20% or less.


Unavoidable Impurities


Preferably, the content of unavoidable impurities is also controlled in the magnesium alloy for medical use. Since Fe, Ni, Co, and Cu promote corrosion of the magnesium alloy, the content of each of these unavoidable impurities is preferably lower than 10 ppm, further preferably 5 ppm or lower, and preferably substantially absent. The total content of the unavoidable impurities is preferably 30 ppm or less, and further preferably 10 ppm or less. Preferably, the magnesium alloy is substantially free from rare-earth elements and aluminum. Where an amount of an impurity element in the alloy is less than 1 ppm, it is regarded that the alloy is substantially free from the impurity element. The amount of impurity may be determined, for example, by ICP optical emission spectrometry.


Production of Magnesium Alloy


In accordance with an ordinal production method of a magnesium alloy, the magnesium alloy may be produced by throwing ground metals or alloys of Mg, Zn, Zr, Mn into a crucible, melting the ground metals and/or alloys in the crucible at a temperature from 650 to 800° C., and casting the molten alloy. Where necessary, the cast alloy may be subjected to solution heat treatment. The ground metals do not contain rare-earth elements (and aluminum). It is possible to suppress the amounts of Fe, Ni, Co, and Cu in the impurities by the use of high purity ground metals. Fe, Ni, and Co in the impurities may be removed by de-ironing treatment to the molten alloy. In addition, or alternatively, it is possible to use ground metals produced by distillation refining.


Metal Microstructure and Mechanical Properties


By the above-described controls of composition and production process, the magnesium alloy can have a fine and uniform structure as seen in a particle size distribution with an average crystal particle size from 1.0 to 3.0 μm (for example, from 1.0 to 2.0 μm) and a standard deviation of 0.7 or smaller (for example, from 0.5 to 0.7). The standard deviation is preferably 0.65 or smaller. Fine precipitates containing Zr may each have a particle size smaller than 500 nm (preferably smaller than 100 nm). A matrix phase excluding the Zr precipitates may preferably be an single-phase solid solution of Mg—Zn—Mn ternary alloy.


The alloy has the following mechanical properties: a tensile strength from 230 to 380 MPa (for example, from 250 to 300 MPa), a proof strength from 145 to 220 MPa, and a fracture elongation from 15 to 50% (for example, from 25 to 40%) in accordance with JIS Z2241. The alloy preferably has a tensile strength exceeding 280 MPa. The alloy preferably has a fracture elongation exceeding 30%.


Medical Device


The magnesium alloy of the present invention has excellent properties as a metal for medical purposes because the alloy has excellent elongation ability and the components of the alloy is controlled to be non-toxic components with non-toxic concentrations for living tissue. The magnesium alloy of the present invention may be suitably used as a metal member constituting a medical device, such as stents, staplers, screws, plates, and coils. For example, the magnesium alloy may be processed to a pipe-shaped member by hot extrusion. The thus-obtained pipe-shaped member may be processed to have a tubular tubular shape by cold-drawing and be further laser-processed to form a stent.


Example

Preparation of Magnesium Alloy


High purity ground metals of Mg, Zn, Mn, and Zr were prepared as initial materials. Each of the metals was weighed so as to have a component concentration as described in Table 1 and was thrown into a crucible. Then, at 730° C. the metals were molten with stirring, and a thus-obtained melt was cast to form ingots. Thus-obtained magnesium alloys of Example 1 and Example 2 contained the main components at formulation ratios which fall within the present invention. The initial materials used did not contain rare earth elements or aluminum even as unavoidable impurities. In this regard, 99.99% pure magnesium ground metal having a low concentration of impurity Cu was used. De-ironing treatment was carried out in the furnace in order to remove iron and nickel from the melt. Concentrations of impurities in the thus-obtained samples were determined using an ICP optical emission spectrometer (AGILENT 720 ICP-OES manufactured by AGILENT). Table 1 shows the compositions of Example 1 and Example 2. The concentrations of Fe, Ni, and Cu were all lower than 8 ppm (Ni and Cu were lower than 3 ppm). Al and the rare-earth elements were not detected, and Co was also below a detection limit. The total content of the unavoidable impurities was 11 ppm.












TABLE 1









Component
Impurity



concentration (%)
concentration (ppm)
















Mg
Zn
Mn
Zr
Fe
Ni
Cu
Total



















Example 1
the balance
1.86
0.14
0.12
5
3
3
11


Example 2
the balance
0.95
0.11
0.24
8
3
1
11









Measurement of Mechanical Properties


Each alloy according to the examples was formed into a round bar material through hot extrusion. In accordance with JIS Z2241, a tensile strength, a proof strength, and a fracture elongation of the round bar material were determined. Table 2 shows the results.


Observation of Metal Microstructure


A cross section of an extruded material of the alloy was cleaned by Ar ion beam sputtering and was observed using a scanning electron microscope (JSM-7000F manufactured by JEOL). From the observation, an average particle size was determined using electron back scattering diffraction (EBSD) technique, and a standard deviation of a particle size distribution was calculated. Table 2 shows the results, and FIG. 3 and FIG. 4 show graphs of particle size distributions. As for each sample, observation of precipitates was carried out over an observation region of 2 mm×2 mm, and no precipitate having a particle size of 100 nm or larger was found.















TABLE 2







Tensile
Proof

Average




strength
strength
Elongation
crystal particle
Standard



(MPa)
(MPa)
(%)
size (μm)
deviation





















Example 1
288
213
38
1.97
0.62


Example 2
297
217
27
1.97
0.63









The present invention provides a magnesium alloy which has an excellent deformation property and can prevent corrosion due to potential difference because the magnesium alloy includes a matrix phase which forms a single-phase solid solution. Thus, it is possible to suitably control a decomposition rate of the magnesium alloy in living tissues. For this reason, the magnesium alloy is highly applicable, for example, as a metal member for a medical device, such as stents and staplers, which involves deformation during use and requires stable biodegradability.

Claims
  • 1. A magnesium alloy containing, in % by mass, 0.95 to 2.00% of Zn,0.05% or more and less than 0.30% of Zr,0.05 to 0.20% of Mn, andthe balance consisting of Mg and unavoidable impurities, wherein a total content of the unavoidable impurities is 30 ppm or less,a content of each of Fe, Ni, Co, and Cu as unavoidable impurities is less than 10 ppm,the magnesium alloy consists of a matrix phase consisting of single-phase solid solution and Zr-bearing precipitates dispersed in the matrix phase, wherein the particle size of the precipitates is smaller than 100 nm,the matrix phase of the magnesium alloy has a particle size distribution with an average crystal particle size from 1.0 to 3.0 μm and a standard deviation of 0.7 or smaller, andthe magnesium alloy has a fracture elongation of 38% or more and a tensile strength from 288 to 300 MPa in a value measured in accordance with JIS Z2241.
  • 2. The magnesium alloy as claimed in claim 1, wherein the magnesium alloy does not contain rare-earth elements and aluminum.
  • 3. The magnesium alloy as claimed in claim 1, wherein the fracture elongation of the magnesium alloy is 50% or less in a value measured in accordance with JIS Z2241.
  • 4. The magnesium alloy as claimed in claim 1, wherein the magnesium alloy has a proof strength from 145 to 220 MPa in values measured in accordance with JIS Z2241.
  • 5. A medical device comprising a metal member including the magnesium alloy as claimed in claim 1.
CROSS REFERENCE TO THE RELATED APPLICATION

This application is a continuation application, under 35 U.S.C. § 111(a), of international application No. PCT/JP2018/025869, filed on Jul. 9, 2018, the entire disclosures of which are herein incorporated by reference as a part of this application.

US Referenced Citations (38)
Number Name Date Kind
5342576 Whitehead Aug 1994 A
6080177 Igaki et al. Jun 2000 A
7666351 Nishikawa et al. Feb 2010 B2
8569333 Mollison et al. Oct 2013 B2
9254350 Udipi et al. Feb 2016 B2
9474637 Zhao Oct 2016 B2
9510932 Kumta et al. Dec 2016 B2
9522720 Edick Dec 2016 B2
9593397 Imwinkelried et al. Mar 2017 B2
10052405 Koo et al. Aug 2018 B2
10196715 Imwinkelried et al. Feb 2019 B2
10350093 Yan et al. Jul 2019 B2
10478529 Imwinkelried et al. Nov 2019 B2
20020004060 Heublein et al. Jan 2002 A1
20050043788 Luo et al. Feb 2005 A1
20060130947 Oishi et al. Jun 2006 A1
20070135908 Zhao Jun 2007 A1
20070231185 Nishikawa et al. Oct 2007 A1
20090090479 Westengen Apr 2009 A1
20090116994 Luo May 2009 A1
20090131540 Hiromoto et al. May 2009 A1
20100145436 Weber et al. Jun 2010 A1
20100305684 Kim et al. Dec 2010 A1
20130004362 Soba et al. Jan 2013 A1
20130090741 Guo et al. Apr 2013 A1
20130209195 Kuwabara et al. Aug 2013 A1
20140200652 Bayer Jul 2014 A1
20140248288 Kumta et al. Sep 2014 A1
20140277396 Mendelson et al. Sep 2014 A1
20150196691 Covelli et al. Jul 2015 A1
20160022863 Decker Jan 2016 A1
20160022876 Imwinkelried et al. Jan 2016 A1
20160024629 Liang et al. Jan 2016 A1
20160129162 Pulugurtha et al. May 2016 A1
20190330718 Ueda et al. Oct 2019 A1
20190343666 Sasaki et al. Nov 2019 A1
20200139017 Meyer-Kobbe et al. May 2020 A1
20210001013 Sasaki et al. Jan 2021 A1
Foreign Referenced Citations (41)
Number Date Country
1809701 Jul 2006 CN
101257860 Sep 2008 CN
101468216 Jul 2009 CN
101629260 Jan 2010 CN
102387825 Mar 2012 CN
102548589 Jul 2012 CN
102719717 Oct 2012 CN
104046867 Sep 2014 CN
104498790 Apr 2015 CN
104630587 May 2015 CN
105143483 Dec 2015 CN
105256213 Jan 2016 CN
105256213 Jan 2016 CN
105586521 May 2016 CN
107385419 Nov 2017 CN
110191971 Aug 2019 CN
03482947 Apr 1992 EP
851871 Oct 1960 GB
35018704 Dec 1960 JP
09256099 Sep 1997 JP
2842943 Jan 1999 JP
2004183062 Jul 2004 JP
2005531391 Oct 2005 JP
2006087704 Apr 2006 JP
2009530039 Aug 2009 JP
2010013725 Jan 2010 JP
2010503486 Feb 2010 JP
2012082474 Apr 2012 JP
2013215332 Oct 2013 JP
5425364 Feb 2014 JP
2014534841 Dec 2014 JP
5701497 Apr 2015 JP
2017501756 Jan 2017 JP
2006003833 Jan 2006 WO
2007108450 Sep 2007 WO
2013052791 Apr 2013 WO
2014159328 Oct 2014 WO
2015147184 Oct 2015 WO
2018122418 Jul 2018 WO
2018131476 Jul 2018 WO
2018139647 Aug 2018 WO
Non-Patent Literature Citations (57)
Entry
CN-105256213-A: Espacenet English Machine Translation (Year: 2016).
International Search Report, and English Translation thereof, for International Application No. PCT/JP2018/025869, dated Aug. 21, 2018, (2 pages).
Notification of Reasons for Refusal, and English Translation thereof, for Japanese Application No. 2019-555699, dated Dec. 24, 2019, (6 pages).
Decision to Grant, and English Translation thereof, for Japanese Application No. 2019-555699, dated Mar. 10, 2020, (5 pages).
English Abstract for JP2004183062A.
English Abstract for WO2007108450A1.
English Abstract for WO2015147184A1.
English Abstract for WO2018131476A1.
First Chinese Office Action, and English MachineTranslation thereof, for Corresponding Chinese Application No. 201880086293.6, dated Feb. 26, 2021, (15 pages).
First Examination Report for corresponding Indian Patent Application No. 202017054524, dated Apr. 15, 2021, (6 pages).
First Canadian Office Action corresponding Canadian Patent Application No. 3,104,447, dated Apr. 26, 2021, (4 pages).
E-Space English Abstract for CN105143483A.
E-Space English Abstract for CN105256213A.
E-Space English Abstract for CN105586521A.
E-Space English Abstract for CN110191971A.
E-Space English Abstract for CN1809701A.
E-Space English Abstract for CN102719717A.
Yamamoto, “Biomedical Application of Magnesium Alloys,” Journal of Japan Institute of Light Metals, vol. 58, No. 11, pp. 570-576, 2008, (13 pages).
Maeda et al., “Fabrication and mechanical properties of biodegradable magnesium stent,” Journal of Japan Institute of Light Metals, vol. 66, No. 6, pp. 312-317, 2016, (6 pages).
Mao, L. et al., “Enhanced bioactivity of Mg-Nd-Zn-Zr alloy achieved with nanoscale MgF2 surface for vascular stent application,” ACS Appl Mater Interfaces, 2015, vol. 7, No. 9, pp. 5320-5330, abstract, p. 5320, right column, line 2 from the bottom to p. 5321, left column, line 2, section of “Materials and surface modification”, (11 Pages).
Liu et al., “Multifunctional MgF2/polydopamine coating on Mg alloy for vascular stent application,” Journal of Materials Science and Technology, vol. 31, ISSN: 1005-0302, pp. 733-743, 2015, (11 pages).
Kubota, “Properties of Magnesium Alloys & Their Technology”, Journal of the Surface Finishing Society of Japan, vol. 53, No. 3, pp. 8-11, 2002, with machine English translation, (7 pages).
Database Compendex (Online), “Microstructure and properties of Mg-3Zn-0.8Zr-xMn alloy”, Database accession No. E20151300692382, Engineering Information, Inc., New York, NY, US, vol. 36, No. 2, pp. 27-31, Feb. 25, 2015, (1 page).
Gui et al., “Mechanical and corrosion properties of Mg·Gd·Zn·Zr·Mn biodegradable alloy by hot extrusion”, Journal of Alloys and Compounds, Elsevier Sequoia, Lausanne, CH, vol. 685, pp. 222-230, May 24, 2016, (9 pages).
Extended European Search Report for European Application No. 18926369.2, dated May 18, 2021, (8 pages).
Second Chinese Office Action, and English Translation thereof, for Chinese Application No. 201880086293.6, dated Jul. 23, 2021, (10 pages).
Agarwal et al., “Biodegradable magnesium alloys for orthopaedic applications: A review on corrosion, biocompatibility and surface modifications”, Materials Science and Engineering, vol. 68, pp. 948-963, 2016, (27 pages).
E-Space English Abstract for CN101257860A.
E-Space English Abstract for CN101468216A.
E-Space English Abstract for CN101629260A.
E-Space English Abstract for CN102387825A.
E-Space English Abstract for CN102548589A.
E-Space English Abstract for CN104046867A.
E-Space English Abstract for CN104498790A.
E-Space English Abstract for CN104630587A.
E-Space English Abstract for CN107385419A.
E-Space English Abstract for JP2842943A.
E-Space English Abstract for JP5425364A.
E-Space English Abstract for JP5701497A.
E-Space English Abstract and machine translation for JP09256099A.
E-Space English Abstract and machine translation for JP2005-531391A.
E-Space English Abstract and machine translation for JP2006-087704A.
E-Space English Abstract and machine translation for JP2009-530039A.
E-Space English Abstract for JP2010-013725A.
E-Space English Abstract and machine translation for JP2010-503486A.
E-Space English Abstract JP2012-082474A.
E-Space English Abstract for JP2013-215332A.
E-Space English Abstract and machine translation for JP2014-534841A.
E-Space English Abstract and machine translation for JP2017-501756A.
E-Space English Abstract for WO2018122418A1.
E-Space English Abstract for WO2018139647A1.
Decision on Rejection, and English Translation thereof, for Chinese Application No. 201780082913.4, dated Aug. 31, 2021, (12 pages).
Indian Office Action for Indian Application No. 201917027629, dated Oct. 27, 2021, (6 pages).
“Microstructure and properties”, retrieved from ‘https://www.researchgate.net/publication/282288987_Microstructureand_properties_of_Mg-sZn-08Zr-xMn_alloy’on Nov. 23, 2021, (4 pages).
Notice of Allowance and Issue Fee Due, U.S. Appl. No. 16/506,298 dated Oct. 1, 2021, (12 pages).
Decision on Rejection, and English Translation thereof, for Chinese Application No. 201880086293.6, dated Nov. 19, 2021, (12 pages).
Chinese Office Action, and English Translation thereof, for Chinese Application No. 202210151600.2 dated Feb. 17, 2023, (13 pages).
Related Publications (1)
Number Date Country
20210115539 A1 Apr 2021 US
Continuations (1)
Number Date Country
Parent PCT/JP2018/025869 Jul 2018 US
Child 17138492 US