Magnesium-based energy storage systems and methods having improved electrolytes

Abstract

Electrolytes for Mg-based energy storage devices can be formed from non-nucleophilic Mg2+ sources to provide outstanding electrochemical performance and improved electrophilic susceptibility compared to electrolytes employing nucleophilic sources. The instant electrolytes are characterized by high oxidation stability (up to 3.4 V vs Mg), improved electrophile compatibility and electrochemical reversibility (up to 100% coulombic efficiency). Synthesis of the Mg2+ electrolytes utilizes inexpensive and safe magnesium dihalides as non-nucleophilic Mg2+ sources in combination with Lewis acids, MRaX3-a (for 3≧a≧1). Furthermore, addition of free-halide-anion donors can improve the coulombic efficiency of Mg electrolytes from nucleophilic or non-nucleophilic Mg2+ sources.

Description

BACKGROUND

Battery systems with low cost, high energy density, safe operation and long cycling life time have been sought after as viable technologies for storing sustainable energy and have also been greatly desired to meet increasing demands of powering portable devices and electric vehicles (EVs). In this regard, advanced rechargeable batteries can help to reduce the use of fossil fuels and the emission of CO₂. Recently, Mg batteries have attracted increasing attention as a promising high energy density battery technology and alternative to lithium-based batteries for grid scale energy storage, portable devices, and transportation applications.

Magnesium as an anode material inherently possesses a number of benefits. It is relatively safe to use without jeopardous dendrite formation. It is earth abundant, relatively low in cost, and has a high volumetric capacity (3832 AWL) due to the divalent nature of the Mg^2+/0 redox couple. However, the lack of practical, high-performance Mg²⁺ electrolytes has been a primary technical hurdle to the development of practical Mg²⁺ batteries. Unlike Li⁺ salts, simple Mg²⁺ salts (e.g. MgCl₂, Mg(ClO₄)₂, MgTFSI₂, MgSO₄ etc.) in organic solvents are not electrochemically active for Mg⁺ plating and stripping because of the formation of passivation films on electrode surfaces.

The current methods for preparing Mg²⁺ electrolytes involve the use of nucleophilic sources and/or Grignard reagents (or analogues like RMgCl and MgR₂). However, these nucleophilic sources and Grignard reagents are difficult because they are highly reactive and because employing them for synthesis of Mg²⁺ electrolytes is complex and can result in low yields. Furthermore, their presence can limit oxidation stability of the Mg²⁺ electrolyte. Further still, the highly reactive chemicals can have limited compatibility with electrophiles such as high capacity cathodes (e.g., sulfur cathodes) and related electrolyte additives.

As an example of these disadvantages associated with the presence of these nucleophilic species, poor oxidation stability and undesired nucleophilicity of the resulting electrolytes is due to incomplete reactions and/or byproduct formation (i.e. MgR₂ generated from RMgCl. Electrolytes using RMgCl or MgR₂ are precluded from being included in high energy density Mg batteries with sulfur cathode (i.e., electrophilic) materials because of the formation of disulfide species.

Mg(BH₄)₂ and Mg(BPh₄)₂ have also been considered as active Mg²⁺ electrolytes. However, low oxidation stability or insufficient coulombic efficiency of these mono-component electrolytes limits their practical application. Accordingly, a need exists for improved electrolytes for Mg-based energy systems and methods for synthesizing such electrolytes.

SUMMARY

This document describes conductive electrolytes for Mg-based energy storage systems as well as methods for synthetizing the electrolytes from relatively inexpensive, non-nucleophilic Mg²⁺ sources. The electrolytes described herein exhibit outstanding electrochemical performance and improved electrophilic susceptibility compared to electrolytes employing nucleophilic RMgCl or MgR₂. They are characterized by high oxidation stability (up to 3.4 V vs Mg), improved electrophile compatibility and electrochemical reversibility (up to 100% coulombic efficiency). Synthesis of the Mg²⁺ electrolytes utilizes inexpensive and safe magnesium dihalides as non-nucleophilic Mg²⁺ sources in combination with Lewis acids. The Lewis acids comprise supporting ligands that can significantly enhance the solubility of the MgCl₂. Also described are electrolytes that further comprise free-halide-anion donors, which can improve the coulombic efficiency.

In one embodiment, a Mg-based energy storage system having an anode comprising Mg metal is characterized by an electrochemical window greater than 2.8V vs. Mg and by an electrolyte solution comprising an organic solvent and an active Mg²⁺ dimer monocation concentration greater than or equal to 0.2 M, wherein at least a portion of the active Mg²⁺ dimer monocation concentration is a reaction product of a magnesium dihalide and a Lewis acid. The reaction can, for example, be a transmetalation reaction. The magnesium dihalide is represented as MgX₂ (wherein X represents a halogen element) and comprises a Mg²⁺ source and a Lewis base donor (i.e., X). The Lewis acid has a formula MR_aX_3-a (3≧a≧1), wherein M represents a metal center, R is an organic ligand, and X is the halogen element. In preferred embodiments, the molar ratio between the magnesium dihalide and the Lewis acid is approximately 2:1. In most instances, the Mg-based energy storage systems described herein can exhibit a Coulombic efficiency greater than 99%.

Examples of X can include, but are not limited to, Cl, Br, F, I, and combinations thereof. In preferred embodiments, the magnesium dihalide comprises MgCl₂ or MgBr₂.

Examples of M can include, but are not limited to B, Al, Ga, In, Fe, and combinations thereof. The organic ligands, R, can include, but are not limited to organic moieties such as alkyl, aryl, alkoxide, aryloxide, thiolate and amide, and combinations thereof. In some embodiments, the Lewis acid can include, but is not limited to, MX₂R, MXR₂, MR₃, and any combination thereof. In view of the above, some instances of the Lewis acid can include, but are not limited to, AlCl₂Et, AlCl₂Ph, AlF₂Et, AlF₂Ph, GaCl₂Et, GaCl₂Ph, BBr₂Et, and BBr₂Ph. Preferably, the halogen element of the Lewis acid is the same as the halogen element of the magnesium dihalide.

In preferred embodiments, the organic solvent is an ether solvent. Examples of ether solventes can include, but are not limited to, dimethyl ether (DME), diglyme, triglyme, tetraglyme and tetrahydrofuran (THF).

The supporting ligand of the Lewis acid contributes to unexpected results. The supporting ligand can significantly increase the solubility of the Mg²⁺ active species. For example, Lewis acids having the formula MR_aX_3-a (3≧a≧1) result in much higher concentrations of the active Mg²⁺ dimer monocations compared to Lewis acids having the formula MX₃. Accordingly, embodiments of the present invention, which employ MR_aX_3-a (3≧a≧1), exhibit much higher performance, coulombic efficiency and current densities compared to systems and methods utilizing conventional electrolyte compositions. In one embodiment, the active Mg²⁺ dimer monocation concentration is greater than or equal to 0.4 M. In another embodiment, the concentration is greater than or equal to 0.7 M.

In some instances, a free-halide-anion donor comprising X⁻, but not Mg, can contribute free anions of X⁻ to the electrolyte solution. Rather than Mg, the free-halide-anion donor can be an organic salt having X⁻ or an inorganic salt having X. Examples of organic salts having X⁻ can include, but are not limited to tetraalklylammonium halides, bis(triphenylphosphine)iminium halides, imidazolium halides, and combinations thereof. Examples of inorganic salts having X⁻ but not Mg can include, but are not limited to, Li halides, Na halides, K halides, and combinations thereof. Preferably, the halogen element of the free-halide-anion donor is the same as the halogen element of the magnesium dihalide and the Lewis acid.

Another embodiment encompasses a Mg-based energy storage system having an anode comprising Mg metal and is characterized by an electrochemical window greater than 2.8V vs. Mg and by an electrolyte solution comprising an organic solvent and reaction products of a magnesium dihalide and a Lewis acid. The magnesium dihalide has a formula MgCl₂ or MgBr₂. The Lewis acid has a metal center (M) comprising Al or Ga and a supporting ligand comprising Cl⁻ or Br⁻, respectively. The electrolyte solution further comprises a salt contributing free anions of Cl⁻ or Br⁻, respectively, to the electrolyte solution. The salt does not comprise Mg.

Another embodiment encompasses a Mg-based energy storage system having an anode comprising Mg metal and is characterized by an electrolyte solution comprising an organic solvent and reaction products of Mg compound and a Lewis acid. The Mg compound comprises Mg and a halogen element (X). The Lewis acid has a metal center (M) and a supporting ligand comprising a halide (X), an organic ligand (R), or both. The electrolyte solution further has a free-halide-anion donor comprising X, but not Mg, wherein the free-halide anion donor contributes free anions of X⁻ to the electrolyte solution. In preferred embodiments, the Mg-based energy storage system has a coulombic efficiency greater than 99%.

In some instances, the free-halide-anion donor can be an organic salt having X⁻ or an inorganic salt having X. Examples of organic salts having X⁻ can include, but are not limited to tetraalklylammonium halides, bis(triphenylphosphine)iminium halides, imidazolium halides, and combinations thereof. Examples of inorganic salts having X⁻ but not Mg can include, but are not limited to, Li halides, Na halides, K halides, and combinations thereof.

Yet another embodiment encompasses a method for improving Coulombic efficiency of Mg-based energy storage systems having an anode comprising Mg metal. The method comprises providing an electrolyte solution that comprises an organic solvent and reaction products of a Mg compound and a Lewis acid. The Mg compound has Mg and a halogen element (X). The Lewis acid has a metal center (M) and a supporting ligand comprising a halide (X⁻), and organic ligand (R), or both. The method further comprises providing a free-halide-anion donor having X, but not Mg. The free-halide-anion donor contributes free anions of X⁻ to the electrolyte solution. In preferred embodiments, the step of providing a free-halide-anion donor comprises providing an amount of the free-halide-anion donor sufficient to yield a Coulombic efficiency greater than 99%.

Examples of the metal center (M) of the Lewis acid can include, but are not limited to B, Al, Ga, In, Fe, and combinations thereof. Examples of X in the Mg compound and the Lewis acid can include, but are not limited to, Br, Cl, F, I, and combinations thereof. In a preferred embodiment, at least some of the Lewis acid comprises MR_aX_3-a (3≧a≧1).

In one instance, the Mg compound comprises MgX₂ and the Mg-based energy storage system has an electrochemical window greater than 2.8 V vs. Mg.

The purpose of the foregoing summary is to enable the United States Patent and Trademark Office and the public generally, especially the scientists, engineers, and practitioners in the art who are not familiar with patent or legal terms or phraseology, to determine quickly from a cursory inspection the nature and essence of the technical disclosure of the application. The summary is neither intended to define the invention of the application, which is measured by the claims, nor is it intended to be limiting as to the scope of the invention in any way.

Various advantages and novel features of the present invention are described herein and will become further readily apparent to those skilled in this art from the following detailed description. In the preceding and following descriptions, the various embodiments, including the preferred embodiments, have been shown and described. Included herein is a description of the best mode contemplated for carrying out the invention. As will be realized, the invention is capable of modification in various respects without departing from the invention. Accordingly, the drawings and description of the preferred embodiments set forth hereafter are to be regarded as illustrative in nature, and not as restrictive.

DESCRIPTION OF DRAWINGS

Embodiments of the invention are described below with reference to the following accompanying drawings.

FIG. 1 contains nuclear magnetic resonance spectra obtained from a MgCl₂—AlCl₃ electrolyte.

FIGS. 2A and 2B include illustrations depicting a comparison of the molecular structures of [(μ-Cl)₃Mg₂(THF)₆]AlCl₄ and [(μ-Cl)₃Mg₂(THF)₆]AlPh₃Cl, respectively.

FIG. 3 is a cyclic voltammogram of a cell having an MgCl₂—AlCl₃ electrolyte.

FIGS. 4A and 4B are cyclic voltammograms of cells having an MgCl₂—AlPh₃Cl electrolyte and an MgCl₂—AlEtCl₂ electrolyte, respectively, according to embodiments of the present invention.

FIG. 5A-5D includes, according to embodiments of the present invention, (A) Overlap of continuously repeated 250 cycles of CV of the MgCl₂—AlEtCl₃ electrolyte (0.7 M based on [(μ-Cl)₃Mg₂(THF)₆]AlEtCl₃ in THF) recorded on Pt electrode. Inset shows coulombic efficiency vs. CV cycles; (B) Plots of charge over time of the representative Mg²⁺ plating and stripping cycles; (C) an energy dispersive X-ray spectrum recorded for a Pt plate electrode after electrochemical Mg²⁺ deposition using the MgCl₂—AlEtCl₃ electrolyte; and (D) scanning electron microscope micrographs of the deposited Mg on a Pt plate at 100 μm and 10 μm (inset) resolutions.

FIG. 6 Galvanostatic charging and discharging profiles (cell voltage-capacity plots) after 1, 30, 60, and 90 cycles of a coin-cell prototype of a Mg rechargeable battery comprising an MgCl₂—AlEtCl₂ electrolyte, Mg anode, and Mo₆S₈ cathode, according to embodiments of the present invention. The inset shows the charging and discharging capacities over 100 cycles.

FIG. 7 depicts a possible reaction sequence to form [(μ-Cl)₃Mg₂(THF)₆]⁺ according to embodiments of the present invention.

FIG. 8A-8C depicts metathiesis reactions of (A) MgCl₂ according to embodiments of the present invention compared to those of (B) RMgCl and (C) MgR₂ with AlCl₃.

FIG. 9 includes cyclic voltammograms comparing the presence and absence of a free-halide-anion donor (Bu₄NCl) in a MgCl₂—AlCl₃ electrolyte according to embodiments of the present invention. Conditions: scan rate, 50 mV/s; working electrode, Pt; reference electrode, a Mg strip; counter electrode, glassy carbon; 22° C.; under 1.0 atm Ar.

FIGS. 10A and 10B are continuous cyclic voltammograms from a cell having a MgCl₂—AlCl₃ electrolyte comparing the (A) absence of a free-halide-anion donor (Bu₄NCl) over 10 cycles and the (B) presence of (Bu₄NCl) over 400 cycles according to embodiments of the present invention. Same conditions as data shown in FIG. 9.d

DETAILED DESCRIPTION

The following description includes the preferred best mode of one embodiment of the present invention. It will be clear from this description of the invention that the invention is not limited to these illustrated embodiments but that the invention also includes a variety of modifications and embodiments thereto. Therefore the present description should be seen as illustrative and not limiting. While the invention is susceptible of various modifications and alternative constructions, it should be understood, that there is no intention to limit the invention to the specific form disclosed, but, on the contrary, the invention is to cover all modifications, alternative constructions, and equivalents falling within the spirit and scope of the invention as defined in the claims.

The reaction products of a Lewis acid with magnesium compounds or magnesium dihalides, and/or the solvent can result in Mg²⁺ dimer monocations solvated by the solvent of the electrolyte solution. For instance, one THF-solvated Mg²⁺ dimer monocation, [(μ-Cl)₃Mg₂(THF)₆]⁺ (see FIG. 2A) has previously been identified in recrystallized products of electrochemically active Grignard reagents and electrolytes derived from Grignard reagents (or MgR₂) with Al-based Lewis acids in THF. Such Mg²⁺ dimer salts have been shown to be electrochemically active for Mg²⁺ cycling.

The dimer salt is believed to be a significant contributor to electrochemical activity. However, previously described systems typically contain very little of the solvated Mg²⁺ dimer monocations. The low yield is believed to be due to competing side reactions when using a nucleophilic Mg²⁺ source or Grignard reagent. In contrast, embodiments of the present invention contain significantly higher concentrations of the Mg²⁺ dimer monocations and, furthermore, are free of nucleophilic Mg²⁺ species. The increased concentration of the Mg²⁺ dimer monocations can be attributed to the presence of the MR_aX_3-a (3≧a≧1) Lewis acid and/or other features of embodiments of the present invention as described herein.

Regarding the structure and composition of [(μ-Cl)₃Mg₂(THF)₆]AlR_xCl_4-x (x=0-3, R=alkyl or aryl group), the dimer salts can be deconvoluted into three simple synthons: two equivalents of MgCl₂, six equivalents of THF solvent molecules and one equivalent of an Al Lewis acid, AlR_xCl_3-x (see equation 1).

According to aspects of the present invention, the straightforward retrosynthesis analysis suggested that the dimer salts could be prepared, for example, using two equivalents of a magnesium dihalide (e.g., MgCl₂) and one equivalent of a Lewis acid in an ether solvent (e.g., THF). For example, according to equation 1, two equivalents of MgCl₂ transfer one Cl⁻ to the Lewis acid and the resulting Mg₂Cl₃ core can complex with 6 THF molecules to form the target [(μ-Cl)₃Mg₂(THF)₆]⁺ cation. Accordingly, in some embodiments the molar ratio of the magnesium dihalide to the Lewis acid is approximately 2:1. The ratio may deviate slightly from 2:1 due to measurement limitations and/or impurities within the reagents. Regardless of the ratio, the approach described herein intrinsically circumvents the use of the nucleophilic Mg²⁺ starting materials, RMgCl or MgR₂. Instead, magnesium dihalides can be used. Furthermore, the absence of nucleophilic Mg²⁺ starting materials in the resulting electrolytes leads to improved electrochemical performance and electrophilic susceptibility. The use of the MR_aX_3-a (3≧a≧1) Lewis acid, results unexpectedly in significantly higher solubility and yield of the Mg²⁺ dimer cation than previously demonstrated using AlCl₃.

While a magnesium dihalide has been tested as a Mg²⁺ source for Mg²⁺ plating and stripping with AlCl₃, it was quickly dismissed due to the poor performance and very low solubility. The synthetic approach of the instant embodiments is referred to herein as “mono-chloride abstraction” and it can yield a series of the Mg²⁺ dimer electrolytes characteristic of exceptional oxidation stability (up to 3.4 V vs Mg), improved electrophilic susceptibility, high current density (up to 32.7 mA/cm²) and reversible Mg²⁺ ion plating and stripping (up to 100% Coulombic efficiency). Electrolytes described in some embodiments herein are experimentally established to be sulfur compatible and can be utilized in Mg—S batteries. Compared to previously reported formulations, the embodiments described herein are much more synthetically feasible and effective in terms of the cost of the starting materials, purification requirements, waste management, yield, and electrochemical performance of the produced electrolytes. In general, the approach can be widely applied to produce Mg²⁺ electrolytes with desired chemical and physical characters for Mg²⁺ batteries and Mg-plating applications.

Three different electrolyte systems (MgCl₂—AlCl₃, MgCl₂—AlPh₃, and MgCl₂—AlEtCl₂) in THF have been characterized and compared by multinuclear NMR (¹H, ²⁷Al{¹H} and ²⁵Mg{¹H}) spectroscopies and electrochemical analysis.

All synthesis reactions and manipulations were performed under Ar using a glovebox. Solvents were pre-purged with N₂ and were dried using an activated alumina column and stored under Ar. All reagents were used as received. MgCl₂, AlEtCl₂, AlPh₃, AlCl₃, MoS₂, CuS, and Mo were purchased from ALDRICH Chemical Company.

Single crystal X-ray diffraction and NMR studies consistently established molecular structures of three electrolytes sharing a common Mg²+-dimer mono-cation, [(μ-Cl)₃Mg₂(THF)₆]⁺, along with an anion (AlCl₄⁻, AlPh₃Cl⁻ and AlEtCl₃⁻ respectively). Clean Mg²⁺ plating and viable battery performances were validated through the representative studies using an MgCl₂—AlEtCl₂ electrolyte. ¹H and ²⁷Al{¹H} NMR spectra were recorded on a Varian INOVA spectrometer (500 MHz for ¹H) at 22° C. ²⁵Mg {H} NMR spectra were recorded on a Varian-AGILENT spectrometer (900 MHz for ¹H) at 22° C. The ²⁷Al{¹H} NMR and ²⁵Mg {¹H} NMR spectra were proton decoupled and are referenced to external AlCl₃/H₂O and MgCl₂/H₂O respectively.

All electrochemical experiments were carried out under an atmosphere of Argon. Cyclic voltammetry experiments were performed with a CH Instruments model 660C potentiostat. The working electrodes (1.0 mm PEEK-encased glassy carbon, Cypress Systems EE040; 2.0 mm Pt working electrode, CH Instruments, CHI102) were polished using Al₂O₃(BAS CF-1050, dried at 150° C. under vacuum) suspended in methanol, and then rinsed with neat tetrahydrofuran. A glassy carbon rod was used as the counter electrode. A piece of Mg strip was freshly polished and used as the reference electrode.

The electrolyte conductivity was measured using WP CP650 conductivity meter Oakton Instruments): MgCl₂—AlCl₃(0.04 M), 0.26 mS/cm; MgCl₂—AlPh₃(0.43 M), 2.96 mS/cm; MgCl₂—AlEtCl₂(0.7 M), 6.99 mS/cm.

Prototype rechargeable Mg batteries in coin type cells (standard 2030 parts from NRC Canada) were assembled from a fresh polished Mg disk anode, a Mo₆S₈-carbon composite cathode, and a separator (glass fiber B) soaked in the electrolyte solution. Cell tests were performed on an Arbin Battery Tester BT-2000 (Arbin Instruments, College Station, Tex.) at room temperature. A Mo₆S₈-carbon composite electrode slurry was prepared by mixing 80 wt % active material (Mo₆S₈), 10 wt % super-C carbon powder and 10 wt % poly(vinylidene fluoride) (PVDF) in N-methyl-2-pyrrolidinone. The slurry was coated onto carbon paper substrate to prepare the cathode disks.

The MgCl₂—AlCl₃ electrolyte was prepared by adding AlCl₃ (0.400 g, 3.0 mmol in 50 mL THF) dropwise to a suspension of MgCl₂ (0.570 g, 6.0 mmol in 50 mLTHF) in a 200 mL round-bottom flask under Ar. The mixture was stirred for 6 h at 22° C. Reaction completion was confirmed by ²⁷Al{¹H} NMR spectroscopy. After filtration, THF was removed under vacuum to give a white powder. Yield was approximately quantitative. The white powder was used for spectroscopic analyses and electrochemical studies without further purification. Solubility of the electrolyte (0.04 M) was determined by slowly dissolving the electrolyte powder in 1.0 mL THF until a supersaturated solution was observed. Higher concentrations were not attainable, which is consistent with what is known in the art. Single crystals of [(μ-Cl)₃Mg₂(THF)₆]AlCl₄ for X-ray diffraction studies were grown by pentane vapor diffusion into a THF solution. ¹H NMR (THF-d₈): 3.62 (m, 24H, THF), 1.78 (m, 24H, THF). ²⁷Al{¹H} NMR (THF):102.4 ppm, assigned to AlCl₄⁻.^{21 25}Mg{¹H} NMR (THF): 6.4 ppm.

The MgCl₂—AlPh₃ electrolyte was prepared from AlPh₃ (0.258 g, 1.0 mmol in 1.0 mL dibutylether) and MgCl₂ (0.190 g, 2.0 mmol in 10 mL THF) similarly to the MgCl₂—AlCl₃ Electrolyte. Solubility of the electrolyte was determined to be 0.43 M, which is at least ten times greater than that when using AlCl₃ Single crystals of [(μ-Cl)₃Mg₂(THF)₆]AlPh₃Cl for X-ray diffraction studies were grown by pentane vapor diffusion into a THF solution. ¹H NMR (THF-d₈): 7.70 (m, 6H, Ph), 7.09 (m, 9H, Ph), 3.62 (m, 24H, THF), 1.78 (m, 24H, THF). ²⁷Al{¹H} NMR (THF): 136.0 ppm, assigned to AlPh₃Cl⁻.^{10 25}Mg {¹H} NMR (THF): 5.4 ppm.

The MgCl₂—AlEtCl₂ electrolyte was prepared from AlEtCl₂ (0.315 g, 5.0 mmol in 10 mL THF) and MgCl₂ (0.950 g, 10.0 mmol in 10 mL THF) using a procedure similar to that described for the MgCl₂—AlCl₃ electrolyte. Solubility of the electrolyte was determined to be 0.7 M. Single crystals of [(μ-Cl)₃Mg₂(THF)₆]AlEtCl₃ for X-ray diffraction studies were grown by pentane vapor diffusion into a THF solution. ¹H NMR (THF-d₈): 3.62 (m, 24H, THF), 1.78 (m, 24H, THF), 0.96 (m, 3H, —CH₃), −0.10 (m, 2H, —CH₂—). ²⁷Al{¹H} NMR (THF): 128.1 ppm, assigned to AlEtCl₃⁻.^{22 25}Mg{¹H} NMR (THF): 4.6 ppm.

One of the possible reaction mechanisms of MgCl₂ and the Al Lewis acids in THF is described to demonstrate the formation of the electrochemically active [(μ-Cl)₃Mg₂(THF)₆]⁺ dimer monocation in these electrolytes and their improved performance compared to traditional electrolytes using nucleophilic Mg²⁺ sources. This mechanism, which can be generalized for a magnesium dihalide and a Lewis acid according to embodiments of the present invention, has been tested according to DFT calculations. The anion possesses a low-lying HOMO frontier orbit and is more difficult to oxidize compared to other anions. Furthermore, the resulting dimer species is expected to have a high oxidation stability.

A mixture of MgCl₂ and AlCl₃ in a ratio of 2:1 was combined in THF and stirred for 6 h at room temperature. The ²⁷Al{¹H} NMR spectrum of the resulting solution shows one Al³⁺ resonance at 102.4 ppm²¹ (see FIG. 1), confirming the formation of the AlCl₄⁻ anion. The ²⁵Mg {¹H} NMR spectrum displays a singlet at 6.5 ppm, consistent with the formation of a new Mg²⁺ species (see FIG. 1) compared to MgCl₂ in THF (7.9 ppm).²² A single crystal X-ray diffraction analysis of the recrystallized product further confirmed the chemical nature of the reaction product.

As shown in FIG. 2, the molecular structure of the electrolyte consists of a Mg-dimer monocation, [(μ-Cl)₃Mg₂(THF)₆]⁺ and an AlCl₄⁻ anion, according to equation 2. The cation adopts a pseudo-D3h symmetry with three bridging Cl⁻ ligands between two Mg²⁺ and three terminal THF ligands on each Mg²⁺; each Mg has an octahedral geometry. Selected bonding distances (Å) and angles (°) for [(μ-Cl)₃Mg₂(THF)₆]AlEtCl₃: averaged Mg—O, 2.08; averaged Mg—Cl, 2.504; averaged Al—Cl, 2.101; averaged Mg1-Cl—Mg2, 77.81. Selected bonding distances and angles for [(μ-Cl)₃Mg₂(THF)₆]AlPh₃: averaged Mg—O, 2.084; averaged Mg—Cl, 2.523; Al—Cl, 2.2160 (9); averaged Al—C(Ph), 2.014; averaged Mg1-Cl—Mg2, 78.12. Similar structures are relevant for different halide species (e.g., F, Br, I, etc.), metal centers (e.g., B, Ga, In, Fe, etc.), and solvents (e.g., DME, diglyme, THF, etc.), though bonding distances and angles would vary.

$\begin{array}{cc}2{\mathrm{MgCl}}_2+{\mathrm{AlR}}_x{\mathrm{Cl}}_{3\text{-}x}\stackrel{\mathrm{THF},22°C.}{⟶}\left[{\left(\mu -\mathrm{Cl}\right)}_3{{\mathrm{Mg}}_2\left(THF\right)}_6\right]{\mathrm{AlR}}_x{\mathrm{Cl}}_{4-X}{\mathrm{AlR}}_x{\mathrm{Cl}}_{3\text{-}X}={\mathrm{AlCl}}_3,{\mathrm{AlPh}}_3,{\mathrm{AlEtCl}}_2{\mathrm{AlR}}_x{\mathrm{Cl}}_{4\text{-}X}={\mathrm{AlCl}}_4^{-},{\mathrm{AlEtCl}}_3^{-},{\mathrm{AlPh}}_3{\mathrm{Cl}}^{-}& \mathrm{eq}.\left(2\right)\end{array}$

The reaction product without further purification was examined for its activity as an electrolyte for Mg²⁺ plating and stripping. As shown in FIG. 3 (red trace), a cyclic voltammogram of a MgCl₂—AlCl₃ electrolyte (0.04 M based on [(μ-Cl)₃Mg₂(THF)₆]AlCl₄ in THF) recorded at 50 mV/s on a glassy carbon (GC) electrode displays the redox process for the Mg²⁺ plating and stripping with an onset potential at −0.29 V vs Mg. A cyclic voltammogram recorded on a Pt electrode shows almost identical electrochemical observations except decreased current density for Mg²⁺ cycling (FIG. 3, blue trace). The coulombic efficiencies on GC and Pt are calculated to be approximately 90% by comparing the amount of charges passed for the plating and stripping processes. The irreversible oxidation wave of the electrolyte, at which the oxidation current is <20 μA/cm², was observed at approximately 3.4 V vs Mg (see inset in FIG. 3). Compared to MgBu₂—AlCl₃ (oxidized at ca. 2.3 V vs Mg) electrolytes using the same Lewis acid (AlCl₃) but a nucleophilic Mg²⁺ source, the oxidation stability of the MgCl₂—AlCl₃ electrolyte is improved by 1.1 V. The difference is attributed to the absence of nucleophilic species in the MgCl₂—AlCl₃ electrolyte described herein and the oxidation stability of AlCl₄⁻. Identical CV results were observed for an electrolyte solution prepared from the crystallized product, indicating that the same electrochemically active species of the electrolyte solution exists whether obtained from the magnesium dihalide and Lewis acid constituents or the crystallized product. Changing the ratio of MgCl₂ and AlCl₃ (1:1 and 1:2) resulted in decreasing current density and increasing overpotential (>0.58 V) for Mg²⁺ cycling. The control studies suggest that changing the ratio of the Lewis base and Lewis acid might lead to formation of different electrochemically active species, which can result in different reaction mechanisms than that described above. Such mechanisms are encompassed by embodiments of the present invention.

A MgCl₂—AlPh₃ electrolyte solution and a MgCl₂—AlEtCl₂ electrolyte solution were prepared in a similar fashion as used for the MgCl₂—AlCl₃ electrolyte solution (equation 2). Both electrolyte solutions were characterized by ¹H, ²⁷Al{¹H} and ²⁵Mg{¹H} NMR spectroscopies. Single crystal X-ray diffraction study of the MgCl₂—AlPh₃Cl electrolyte confirmed its molecular identity comprising of the same Mg²⁺-dimer cation with AlPh₃Cl⁻ (see FIG. 2, right). Preliminary single crystal X-ray diffraction data of the MgCl₂—AlEtCl₂ electrolyte also confirmed the core structural connectivity (Mg2Cl₃O₆) of the Mg²⁺-dimer cation. Together with its NMR data, the molecular structure of the MgCl₂—AlEtCl₂ electrolyte is assigned as [(μ-Cl)₃Mg₂(THF)₆]AlEtCl₃.

The electrochemical activities of the MgCl₂—AlPh₃ and MgCl₂—AlEtCl₂ electrolytes for Mg²⁺ cycling were confirmed by cyclic voltammetry recorded on a GC (glassy carbon) electrode and a Pt electrode (see FIG. 4). Both electrolytes demonstrated approximately 100% coulombic efficiency for Mg²⁺ plating and striping. The onset potentials of both electrolytes occur at −0.29 V vs Mg, suggesting that the three electrolytes share the same active Mg²⁺ species, [(μ-Cl)₃Mg₂(THF)₆]⁺, for the Mg²⁺ cycling. The MgCl₂—AlPh₃ electrolyte and the MgCl₂—AlEtCl₂ electrolyte possess the irreversible oxidation at 3.1 and 2.9 V vs Mg respectively (see FIGS. 4A and 4B, inset). Compared to the MgCl₂—AlCl₃ electrolyte, the reduced anodic stability of both electrolytes is believed to be associated with their less oxidatively stable anions. It is noteworthy that the electrochemical oxidation stability of the MgCl₂—AlEtCl₂ electrolyte can be enhanced by 0.8 V and 0.4 V compared to the in situ MgBu₂—AlEtCl₂ electrolyte and the recrystallized MgBu₂—AlEtCl₂ electrolyte, which appear to contain the same active species, [(μ-Cl)₃Mg₂(THF)₆]AlEtCl₃. The poor oxidation stability of the MgBu₂—AlEtCl₂ electrolyte is ascribed to the presence of nucleophilic MgBu₂ even after recrystallization. In addition, the change of the anion also dramatically affects the solubility of both electrolytes in THF; almost 0.43 M for the MgCl₂—AlPh₃ electrolyte and approximately 0.7 M for the MgCl₂—AlEtCl₂ electrolyte, which is significantly higher than that of the MgCl₂—AlCl₃ electrolyte (0.04 M). Correspondingly, the current densities of both electrolytes at their saturated concentrations are much higher than that of the MgCl₂—AlCl₃ electrolyte: 28.2 mA/cm² for the MgCl₂—AlPh₃ electrolyte and 32.7 mA/cm² for the MgCl₂—AlEtCl₂ electrolyte. Consistently, the MgCl₂—AlPh₃ and MgCl₂—AlEtCl₂ electrolytes exhibit much higher conductivity than the MgCl₂—AlCl₃ electrolyte, 6.99 mS/cm at 0.7 M and 2.96 mS/cm at 0.43 M respectively, which are comparable to the electrolytes used in Li batteries.

In some embodiments, the Mg-based energy storage device is a high energy density Mg—S battery. Such embodiments are feasible because of the substantial absence of reactive W nucleophiles. The compatibility of magnesium dihalide and Lewis acid reactants with excess sulfur powder (5 times) was observed by ¹H and ²⁷Al{¹H} NMR spectroscopies over a course of 20 days. The electrolyte solution (0.015 g, 20 mM in 1.0 mL THF) was loaded into two J-Young NMR tubes under Ar. For ²⁷Al{¹H} NMR, the NMR tube was preloaded with a sealed capillary containing 40 mM Al(H₂O)₆Cl₃ as the internal reference of chemical shift and concentration. The first ¹H NMR and ²⁷Al{¹H} NMR spectra were recorded and then excess sulfur powder (0.026 g, 0.1 mmol, 5.0 equivalents) was added into the NMR tubes. The two NMR tubes containing the resulting mixture were followed by ¹H NMR and ²⁷Al{¹H} NMR spectroscopies respectively up to 20 days. According to ¹H NMR and ²⁷Al{¹H} NMR data, there was no degradation observed for the MgCl₂—AlCl₃ and MgCl₂—AlEtCl₂ electrolytes. ¹H NMR indicates slow degradation of the MgCl₂—AlPh₃ electrolyte, accompanied with a color change of colorlessness to yellow.

For MgCl₂—AlCl₃ and MgCl₂—AlEtCl₂ electrolytes, ¹H and ²⁷Al{¹H} NMR studies no degradation was detected. The sulfur inertness confirms the non-nucleophilic nature of these electrolytes, which is attributed to their non-nucleophilic anions and the absence of reactive R⁻ nucleophiles. For the MgCl₂—AlPh₃ electrolyte, slow degradation was indicated by the appearance of new proton resonances of phenyl groups from 7.2 to 7.65 ppm, accompanied with a color change from colorless to yellow. Although there are no R⁻ nucleophiles present in the MgCl₂—AlPh₃ electrolyte, the anion, AlPh₃Cl, still possesses a slight character of nucleophilicity. These results indicate the sulfur compatibility of the electrolytes is also dependent on the chemical nature of the anions.

The electrochemical stability of an MgCl₂—AlEtCl₂ electrolyte (0.7 M based on [(μ-Cl)₃Mg2(THF)₆]AlEtCl₃ in THF) was examined by continuous cyclic voltammetry. 150 cycles of continuously repeated CVs (scan rate, 50 mV/s; reference electrode, a Mg strip; counter electrode, glassy carbon; 22° C.; under 1.0 atm Ar) of the electrolyte recorded on a Pt electrode in 5 hr was completely overlapped (see FIG. 5A). In FIG. 5B, the plots of the charge (including both plating and stripping) over time were shown for cycles 1, 50, 100 and 150. The overlapped plots and equivalent charges of plating and stripping processes indicate the coulombic efficiency of Mg²⁺ cycling was approximately 100% from the first cycle to the 150th cycle (FIG. 5A, inset). The electrochemical observation confirms a reversible and clean electrochemical reaction of the electrolyte for Mg²⁺ cycling, a highly desired electrolyte property for assembling rechargeable Mg batteries.

Clean plating of Mg²⁺ on a Pt plate was confirmed by EDX (see FIG. 5C) after deposition using a MgCl₂—AlCl₃ electrolyte (0.15 M based on [(μ-Cl)₃Mg₂(THF)₆]AlEtCl₃ in THF). The morphology of the deposited Mg using the MgCl₂—AlEtCl₃ electrolyte was investigated by high resolution SEM. The SEM images exhibit dendrite free, smooth and uniform Mg deposition on the Pt plate (FIG. 5D). The size of the deposited Mg grains in rock shape ranges from ca. 2 to 5 μM (see inset in FIG. 5D).

A coin-cell prototype of rechargeable Mg batteries was fabricated from a Mg disk anode, a cathode disk consisting of the intercalating Mo₆S₈ (1.05 V vs Mg) cluster and carbon powder, and 0.3 M MgCl₂—AlEtCl₂ electrolyte. Chevrel phase Mo₆S₈ was synthesized using the molten salt synthesis method described by Aurbach et al (see E. Lancry, E. Levi, A. Mitelman, S. Malovany and D. Aurbach, J. Solid State Chem., 2006, 179, 1879-1882.). The cell test was performed at a rate of 0.1 C with the charging and discharging limits at 1.6 V and 0.6 V for 100 cycles. FIG. 6 displays the representative charging and discharging profiles in steady plateau shapes for the 1^st (blue trace), 30^th (green trace), 60^th (red trace) and 90^th (pink trace) cycles. The cell capacity was initially recorded at 104 mAh/g and retained at 95.1% (99 mAh/g) at the 100^th cycle (see FIG. 5, inset). The results indicate stable cell performance of the electrolyte.

Referring to FIG. 7, illustrations depict potential reaction sequences between MgCl₂ and an Al Lewis acid, according to one embodiment. THF-solvated MgCl₂ in solid state was determined as octahedral trans-MgCl₂(THF)₄ while DFT calculations suggests several possible THF solvated MgCl₂ species in THF including trigonal planar MgCl₂(THF), tetrahedral MgCl₂(THF)₂, trigonal bipyramidal cis-MgCl₂(THF)₃, trans-MgCl₂(THF)₄ and cis-MgCl₂(THF)₄. As discussed below, cis-MgCl₂(THF)₃ would be mostly feasible to form the [(μ-Cl)₃Mg₂(THF)₆]⁺ dimer without involving THF dissociation or association. One equivalent of cis-MgCl₂(THF)₃ transfers one Cl⁻ to the Lewis acid, AlR_xCl_3-x (X=1-3), i.e. mono-Cl⁻ abstraction, to generate a tetra-coordinated cation, [MgCl(THF)₃]⁺. The resulting [MgCl(THF)₃]⁺ cation undergoes a dimerization reaction with the second equivalent of cis-MgCl₂(THF)₃ to form the dimer cation. It is possible that there are equilibriums between [(μ-Cl)₃Mg₂(THF)₆]⁺, trans-MgCl₂(THF)₄, [MgCl(THF)₅]⁺ and cis-MgCl₂(THF)₃. The different Mg resonances observed for three electrolytes could be ascribed to the different equilibrium distributions of these THF solvated Mg²⁺ species which can lead to different averaged chemical shifts through fast exchange.

RMgCl and MgR₂ involve both alkyl (or aryl) and Cl⁻ transmetalation reactions with Lewis acid to form a more complicated equilibrium mixture of different Mg²⁺ species and anion species. In the case of RMgCl, the optimal reaction stoichiometry to form the Mg²⁺ dimer is three equivalent of RMgCl and 1 equivalent of Lewis acid. For example, a proposed reaction between RMgCl and AlCl₃ is exhibited in FIG. 8B. The formation of the Mg²⁺ dimer is accompanied with the formation of one equivalent of MgR₂. MgR₂ is an undesired nucleophilic species. Also MgR₂ could further undergo further exchange reactions with the anion, AlRCl₃⁻, to form multiple R substituted anions. Similarly, MgR₂ can react with AlCl₃ in a complicating fashion (see FIG. 8C).

Embodiments of the present invention do not yield the many species characteristic of traditional electrolytes (see FIG. 8A). Furthermore, embodiments of the present invention have several synthetic advantages over the previous traditional methods using nucleophilic Mg²⁺ sources. Magnesium dihalides, like MgCl₂, as a Mg²⁺ source are much cheaper compared to RMgCl or MgR₂ and are non-nucleophilic. Handling magnesium dihalides is much easier than the reactive Mg²⁺ chemicals such as RMgCl or MgR₂. Because of the clean reaction nature, there is no need for recrystallization or other purification steps after reaction. Consequently, yields of the electrolytes are almost quantitative, representing an atom-economical synthesis. However, for electrolytes prepared from the nucleophilic Mg²⁺ sources or Grignard reagents, recrystallization must commonly be done to remove any nucleophilic Mg²⁺ species along with sacrificing product yield. However purification is not guaranteed to effectively remove all nucleophilic Mg²⁺ byproducts.

The electrolytes comprising magnesium dihalides and Lewis acids according to embodiments described herein, exhibit overall performance (synthetic feasibility, oxidation stability and nulceophilic susceptibility) superiority compared to traditional electrolytes. According to some embodiments, the characteristics and performance of the resulting electrolytes including oxidation stability, electrophilic susceptibility and conductivity can be modulated by the Lewis acid component (or the corresponding metal center anion). It can be expected, by selecting the Lewis acid component, which is widely commercially available or synthetically accessible, the oxidation stability, non-nucleophilicity and conductivity (i.e. electrolyte solubility) of the MgX₂-Lewis acid electrolytes can be further enhanced.

The electrochemical oxidation stability of X⁻ containing electrolytes can be strongly dependent on the current collector. For example, Cl⁻ containing electrolytes are typically not highly compatible with traditional current collectors (e.g., stainless steel and aluminum). In such instances, the current collector should be chosen to maximize compatibility with the electrolyte composition. Control experiments using stainless steel showed the oxidation of the MgCl₂—AlEtCl₂ electrolyte occurred at approximately 1.8 V, similar to the values of other Cl⁻ containing electrolytes reported by others.

Magnesium dihalide (MgX₂) can be used as a non-nucleophilic and inexpensive Mg²⁺ source in combining with the Lewis acids to yield high performance Mg²⁺ electrolytes with oxidation stability up to 2.8V or even 3.4 V, coulombic efficiency up to 100% and improved electrophilic stability. The electrolytes according to embodiments described herein are sulfur compatible and can be applied for assembling high energy density Mg—S batteries. The reaction between MgX₂ and the Lewis acid can form the electrochemically active [(μ-Cl)₃Mg₂(THF)₆]⁺ mono-cations in a manner that is more atomically efficient (free of undesired byproducts), more cost effective and operationally easier (cheap Mg²⁺ source, no precursor synthesis and no purification) in comparison to previously reported methods using nucleophilic RMgCl or MgR₂.

In some embodiments, one or more additional halide salts are added to the electrolyte. The additional halide salts can comprise a free-halide-anion donor comprising X⁻, but not Mg. The free-halide-anion donor can increase the coulombic efficiency while retaining value over continuous runs. Furthermore, the free-halide-anion donor can significantly increase current density and charges passed for Mg²⁺ cycling by enhancing ionic conductivity of electrolytes, even those containing nucleophilic Mg²⁺ sources or Grignard reagents.

The practical use of Mg-electrolytes in energy storage devices can be evaluated initially according one electrochemical parameter, coulombic efficiency for Mg²⁺ deposition and stripping. Coulombic efficiency as used herein, can refer to the ratio of the charge passed for Mg²⁺ deposition and reverse stripping of Mg⁰. The coulombic efficiency should be as close to 100% as possible for reliable battery performance in a practical device, meaning fully reversible for Mg²⁺ deposition and stripping. Otherwise, Mg-batteries will rapidly lose the cycling capability of charging and discharging. Very few reported Mg²⁺ electrolytes can meet this criterion. Many are subject to stripping fading during continuous Mg²⁺ cycling (gradually decreasing coulombic efficiency from approximately 90% to even lower values) because of kinetically slow or unclean electrochemical reactions on electrode surface. The lack of a sufficient halide concentration is believed to be one reason for low coulombic efficiency because the absence of halide ions can hamper formation of Mg⁺ intermediates during the Mg⁰ stripping. Accordingly, embodiments of the present invention encompass the addition of a free-halide-anion donor. The free-halide-anion donor can be added to electrolytes resulting from the reaction of a Mg compound and a Lewis acid. The Mg compound has Mg and a halogen element (X). The Lewis acid has a metal center (M) and a supporting ligand comprising a halide (X). Examples of such Mg electrolytes include those resulting from the magnesium dihalide and Lewis acid compositions described herein as well as those resulting from traditional Mg sources (e.g., nucleophilic sources and/or Grignard reagents).

In the stripping process for Mg²⁺ electrolytes, the free-halide-anion donor is believed to increase the free halide anion concentration, which can stabilize the Mg⁺ oxidation state by forming the halide-ligated intermediate to facilitate the Mg⁺ species undergoing complete oxidation to the Mg²⁺ oxidation state. The free-halide-anion donor comprises a halide (X), but not Mg. The halide in the free-halide-anion donor should correspond to the halide in the magnesium compound and the Lewis acid, as described elsewhere herein.

In one embodiment, the halide is chloride. A number of Cl salts (including tetraalkylammonium chloride, Bu₄NCl (TBACl), bis(triphenylphosphine)iminium chloride, PPNCl, and LiCl) have been tested as an additive component for electrolytes lacking 100% coulombic efficiency. For example, one MgCl₂—AlCl₃ electrolyte exhibited a 90% CE prior to addition of the free-halide-anion donor. Referring to FIG. 9, the addition of free Cl⁻ anions (0.02 M) can effectively increase the coulombic efficiency of the tested Mg²⁺ electrolytes to 100%. Furthermore, comparing to FIGS. 10A (no free Cl⁻ anion donor) and 10B (0.02 M free Cl⁻ anion donor) the performance is stable with the free Cl⁻ anion donor and can retain the full reversibility of Mg²⁺ cycling for many cycles (up to 400 cycles tested over 10 h).

Besides improving the coulombic efficiency, the free-halide-anion donor can significantly increase current densities and passed charges of the electrolytes up to 3 times by enhancing the electrolyte conductivity. Halide salts are ubiquitous and are typically very cheap chemicals. In general, the effect of the free-halide-anion donor can be achieved using other commercial halide salts including organic and inorganic halide salts. Accordingly, the addition of free-halide-anion donors can upgrade quasi-reversible Mg-electrolytes to fully reversible ones for practical Mg-batteries application without significant additional costs.

While a number of embodiments of the present invention have been shown and described, it will be apparent to those skilled in the art that many changes and modifications may be made without departing from the invention in its broader aspects. The appended claims, therefore, are intended to cover all such changes and modifications as they fall within the true spirit and scope of the invention.

Claims

1. A Mg-based energy storage system having an anode comprising Mg metal, the system characterized by an electrochemical window greater than 2.8 V vs. Mg and by an electrolyte solution comprising: (i) an organic solvent;(ii) an active Mg2+ dimer monocation concentration greater than or equal to 0.2 M, wherein the active Mg2+ dimer monocation comprises a Mg2X3 core complexed with six solvent molecules, and wherein at least a portion of the active Mg2+ dimer monocation concentration is a reaction product of a magnesium dihalide MgX2, wherein X represents a halogen elemental, anda Lewis acid MRaX3-a, wherein 3≧a≧1, M is a metal center, R is an organic ligand, and X is the halogen element; and(iii) an anion having a formula MRaX4-a−.

2. The Mg-based energy storage system of claim 1, wherein the Lewis acid is MRX2 or MR3.

3. The Mg-based energy storage system of claim 1, wherein the metal center of the Lewis acid comprises a metal selected from the group consisting of B, Al, Ga, In, Fe, and combinations thereof.

4. The Mg-based energy storage system of claim 1, wherein the organic ligand is selected from the group consisting of alkyl, aryl, alkoxide, aryloxide, thiolate, amide, and combinations thereof.

5. The Mg-based energy storage system of claim 1, wherein the active Mg2+ dimer monocation concentration is greater than or equal to 0.4 M.

6. The Mg-based energy storage system of claim 1, wherein the active Mg2+ dimer monocation concentration is greater than or equal to 0.7 M.

7. The Mg-based energy storage system of claim 1, wherein the molar ratio of the magnesium dihalide to the Lewis acid is approximately 2:1.

8. The Mg-based energy storage system of claim 1, wherein the Lewis acid comprises AlEtCl2, AlPhCl2, or both, and the electrolyte solution comprises AlEtCl3−, AlPhCl331 , or both.

9. The Mg-based energy storage system of claim 1, wherein the electrolyte comprises MgCl2.

10. The Mg-based energy storage system of claim 1, wherein the organic solvent is an ether solvent.

11. The Mg-based energy storage system of claim 1, further having a free-halide-anion donor comprising X−, but not Mg, wherein the free-halide-anion donor contributes free anions of X− to the electrolyte solution.

12. The Mg-based energy storage system of claim 11, wherein the free-halide-anion donor comprises an organic salt having X−.

13. The Mg-based energy storage system of claim 11, wherein the free-halide-anion donor comprises an inorganic salt having X−.

14. The Mg-based energy storage system of claim 1, having a coulombic efficiency greater than 99%.

15. The Mg-based energy storage system of claim 1, further comprising a second Lewis acid, MX3.

16. The Mg-based energy storage system of claim 1, wherein the magnesium dihalide is MgCl2, the solvent is tetrahydrofuran, and the Mg2+ dimer monocation is [(μ−Cl)3Mg2(THF)6]+.

17. A Mg-based energy storage system having an anode comprising Mg metal, the system characterized by an electrochemical window greater than 2.8 V vs. Mg and by an electrolyte solution comprising: (i) an organic ether solvent;(ii) an active Mg2+ dimer monocation concentration greater than or equal to 0.4 M, wherein at least a portion of the active Mg2+ dimer monocation concentration is a reaction product of MgCl2 with a Lewis acid comprising AlEtCl2, AlPhCl2, or both, and wherein the active Mg2+ dimer monocation comprises a Mg2Cl3 core complexed with six organic ether solvent molecules; and(iii) AlEtCl3−, AlPhCl3−, or both.

18. The Mg-based energy storage system of claim 17, wherein the molar ratio of the MgCl2 to the Lewis acid is approximately 2:1.

19. The Mg-based energy storage system of claim 17, wherein the electrolyte solution further comprises a salt contributing free anions of Cl− to the electrolyte solution, wherein the salt does not comprise Mg.

20. A method for improving performance of Mg-based energy storage systems having an anode comprising Mg metal and having an electrochemical window greater than 2.8 V vs. Mg, the method comprising the steps of: providing an electrolyte solution according to claim 1; andproviding a free-halide-anion donor having X, but not Mg, thereby contributing free anions of X− to the electrolyte solution.

21. The method of claim 20, wherein the metal center M comprises a metal selected from the group consisting of B, Al, Ga, In, Fe, and combinations thereof.

22. The method of claim 20, wherein the organic ligand R comprises ethyl, phenyl, or both.

23. The method of claim 20, wherein said providing a free-halide-anion donor comprises providing an amount of the free-halide-anion donor sufficient to yield a Coulombic efficiency greater than 99%.