Claims
- 1. In a process for the selective ortho0alkylation of a phenolic compound preferentially to the para or meta alkylation by the vapor phase reaction of a feed mixture comprising an alkyl alcohol which is a branched or linear saturated alcohol having up to about 16 carbon atoms and a phenolic compound represented by the formula ##STR2## in which R is, independently, a monovalent substituent selected from the group consisting of hydrogen, alkyl having from 1 to 12 carbon atoms, phenyl, and alkyl-substituted phenyl in which the alkyl-substituent has from 1 to 12 carbon atoms, the improvement comprising conducting the reaction in the presence of a catalyst which is the calcined product derived by calcining a precursor comprising a source of magnesium and a source of manganese, said precursor formed by the steps comprising
- (i) providing an aqueous slurry of a magnesium-containing material selected from the group consisting of magnesium carbonate, basic magnesium carbonate and magnesium hydroxide,
- (ii) contacting the aqueous slurry with an aqueous solution of a soluble manganese compound under conditions which cause a precipitate of manganese hydroxide to form in the presence of the slurry,
- (iii) recovering the mixture of said magnesium-containing material and manganese hydroxide, which constitutes the precursor; and
- (iv) calcining the precursor recovered from step (iii) at an elevated temperature of at least 300.degree. C. in an environment selected from the group consisting of air, an inert gas and vacuum, to activate it for subsequent use in an ortho-alkylation process, said process being conducted at temperature of from about 300.degree. C. to about 550.degree. C.
- 2. A process according to claim 1, in which the catalyst precursor has been calcined by heating in air.
- 3. A process according to claim 1, in which the catalyst precursor has been calcined by heating in a vacuum.
- 4. A process according to claim 1, in which the phenolic compound is ortho-cresol.
- 5. A process according to claim 1, in which the alkyl alcohol is methanol.
- 6. A process according to claim 1, in which the magnesium-containing material is basic magnesium carbonate.
- 7. A process according to claim 1, in which the magnesium compound is magnesium carbonate or magnesium hydroxide.
- 8. A process according to claim 1, in which the catalyst precursor has been calcined at a temperature of at least 500.degree. C.
- 9. A process according to claim 8, in which the calcining temperature is between about 350.degree. and about 550.degree. C.
- 10. A process according to claim 1, in which the catalyst also includes a binder and/or shaping aid.
- 11. A process according to claim 10, in which the binder is a polyphenylene ether resin.
- 12. A process according to claim 11, in which the polyphenylene ether resin is poly(2,6-dimethyl-1,4-phenylene)ether.
- 13. A process according to claim 10, in which the shaping aid is particulate graphite.
- 14. A process according to claim 1, in which the catalyst precursor has been calcined by heating in an inert gas comprised of nitrogen.
- 15. A process according to claim 1, in which the catalyst precursor is calcined outside of the reactor.
- 16. A process according to claim 1, in which the catalyst precursor has been calcined in situ in the reactor prior to contacting said catalyst with an alkylation feed mixture.
- 17. A process according to claim 1, in which the reaction temperature is from about 300.degree. C. to about 500.degree. C.
- 18. A process according to claim 17, in which the reaction temperature is from about 300.degree. C. to about 400.degree. C.
- 19. A process according to claim 17, in which the reaction temperature is from about 400.degree. C. to about 500.degree. C.
Parent Case Info
This is a continuation of application Ser. No. 555,714 filed Nov. 28, 1983.
US Referenced Citations (10)
Foreign Referenced Citations (3)
Number |
Date |
Country |
1948607 |
Sep 1969 |
DEX |
2135602 |
Jan 1972 |
DEX |
0497235 |
May 1972 |
JPX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
555714 |
Nov 1983 |
|