Patent Application
20060240192
The present invention relates to repairs on surfaces of magnesium components, and more particularly to the build up of coatings on surfaces of magnesium components.
Magnesium has the advantage of being light weight and readily castable to complex forms. Thus, it would seemingly be a desirable material to use for aerospace applications. However, magnesium suffers from the disadvantage of being prone to corrosion. Corrosion of magnesium may produce corrosion pits, which can be deep and difficult to repair. Further, upon exposure to air above room temperature and at relatively low but elevated temperatures, magnesium may burn. For at least these reasons the use of magnesium in aerospace applications has been limited.
Various means have been proposed to address the above-noted disadvantages. For example, it has been proposed to cover magnesium components with coatings and/or paints as a way to improve corrosion protection for magnesium. However, coatings and paints can, in some instances, be relatively easily scratched. Moreover, a magnesium substrate with a coating may set up an electrical cell if the coating does get scratched, which can subsequently lead to rapid corrosion of the magnesium exposed by the scratch.
Magnesium is also susceptible to erosion and wear. Both these processes remove material that must be replaced during a repair. Otherwise the part may need to be scrapped. Thermal spray techniques employing other metals and materials have been used with other metals as a method to replace eroded material. However, thermal spraying is not well suited for use with magnesium. The temperatures involved to melt and bond the deposited metal in thermal spraying techniques can result in burning of the magnesium.
Aluminum has a low melting point and might thereof be considered a material that could be thermally sprayed to repair magnesium. However, there are problems in thermal spraying aluminum because it is prone to oxidation forming a tenacious oxide film. Even if it was possible to easily thermally spray aluminum, the phase diagram shows that it forms an intermetallic with magnesium at temperatures of approximately 450° C. and has significant solid solubility in magnesium. Thus, heretofore aluminum has not been considered a likely candidate for use in repairing magnesium.
Hence there is an ongoing need to provide protection for magnesium substrates against both corrosion and erosion. It is desired that these protective methods be stable and durable so as to avoid scratching. There is also a need to be able to repair corrosion pits and build up material lost to wear and erosion in magnesium parts. It is further desired to develop methods to apply these magnesium repair techniques on surfaces of cast magnesium parts used in aerospace applications such as those found in helicopter components. The present invention addresses one or more of these needs.
The present invention provides an apparatus and methods for use in repair of magnesium components. In one embodiment, and by way of example only, there is provided a method of applying a coating on a surface of a magnesium component that includes the steps of: accelerating a coating powder to a velocity of between about 500 to about 1200 meters/second, wherein the coating powder comprises a material selected from the group consisting of aluminum, aluminum alloys, titanium, titanium alloys, and hard particle dispersed composites and combinations thereof; directing the coating powder through a convergent-divergent nozzle onto the surface of the magnesium component; and forming a coating on the surface of the magnesium component so as to substantially cover the surface of the magnesium component. The step of forming a coating may include forming the coating with a thickness of between approximately 0.1 to approximately 1.0 mm. The method may also include the step of heating the coating powder to a temperature of between about 250° F. to about 750° F. The coating powder in the method may have a particle size (diameter) of between about 5 to about 50 microns. The method may also include the step of providing coating powder at a powder feed rate of about 0.01 to about 20 grams/second-cm2. The method may also include the step of preparing the surface of the magnesium component by an operation comprising a method selected from the group consisting of grinding, degreasing, and grit blasting. The method may also include the step of heat treating the coating and magnesium substrate. The method may also include the step of depositing the powder composition on the component surface in more than one layer through a series of more than one deposition steps.
In a further embodiment, and still by way of example, there is provided a method for providing corrosion and erosion protection to a surface of a magnesium component comprising the steps of: providing a magnesium component with a surface; inspecting the magnesium component for suitability for high velocity cold spraying; preparing the surface of the magnesium component by an operation comprising a method selected from the group consisting of: machining, degreasing, and grit blasting; and applying a coating onto the surface of the magnesium component by high velocity cold spraying so as to substantially cover the surface of the magnesium component with the coating, thereby providing corrosion and erosion protection to the surface of the magnesium component. The step of applying a coating onto the surface of the magnesium component may include applying a first powder material onto the surface of the magnesium component so as to form a first coating layer, checking material build-up of the first coating layer, and applying a second powder material onto the first coating layer so as to form a second coating layer. The first powder material may be different from the second powder material. The step of applying a coating onto the surface of the magnesium component may include applying a first powder material onto a first surface area of the magnesium component and applying a second powder material onto a second surface area of the magnesium component. The first powder material may be different from the second powder material. The method may also include the step of heat treating the coated component, and heat treating the coated component may comprise heating the coated component at approximately 600° F. to approximately 725° F. for approximately 0.5 to approximately 2 hours, cooling the coated component, and then heating the coated component to approximately 250° F. to approximately 425° F. for approximately 4 to approximately 16 hours. The method may also include inspecting the component by x-ray inspection or FPI inspection.
In a further embodiment, still by way of example, there is provided a coated component comprising: a magnesium substrate having a surface; and a coating deposited on the surface of the magnesium substrate wherein the coating comprises a material selected from the group consisting of aluminum, aluminum alloys, titanium, titanium alloys, iron, iron alloys, copper, copper alloys, nickel, nickel alloys, and composites; and wherein the coating substantially covers the surface of the magnesium substrate. The coating and the magnesium substrate may be part of a helicopter gear box covering or a helicopter generator housing. The coating may have a first layer comprising a first material and a second layer comprising a second material. The surface of the magnesium substrate may have a first surface area and a second surface area, and in such case the coating may have a first coating comprising a first material deposited on the first surface area and a second coating comprising a second material deposited on the second surface area.
Other independent features and advantages of the method to provide magnesium repair and build up will become apparent from the following detailed description, taken in conjunction with the accompanying drawings which illustrate, by way of example, the principles of the invention.
The following detailed description of the invention is merely exemplary in nature and is not intended to limit the invention or the application and uses of the invention. Furthermore, there is no intention to be bound by any theory presented in the preceding background of the invention or the following detailed description of the invention. Reference will now be made in detail to exemplary embodiments of the invention, examples of which are illustrated in the accompanying drawings. Wherever possible, the same reference numbers will be used throughout the drawings to refer to the same or like parts.
In a preferred method, a powder of a protective coating composition is deposited onto a surface of a magnesium substrate through a high velocity cold spraying process. The deposition forms a protective coating that protects the magnesium substrate from forces such as wear, erosion, and corrosion. Referring now to
The high velocity cold spray process may be referred to as a “cold gas” process because the particles are mixed and applied at a temperature that is far below the melting point of the particles. The kinetic energy of the particles on impact with the component surface 15, rather than particle temperature, causes the particles to plastically deform and bond with the component surface 15. Therefore, bonding to the component surface 15 takes place as a solid state process with insufficient thermal energy to transition the solid powders to molten droplets. Typically, prior to spraying the powder is heated to an average temperature of between approximately 250° F. to approximately 750° F. However, during and after spraying the average temperature rise of the powder and magnesium substrate is less than 100° C.
A variety of different systems and implementations can be used to perform the high velocity cold spraying process. For example, U.S. Pat. No. 5,302,414, entitled “Gas Dynamic Spraying Method for Applying a Coating” and incorporated herein by reference, describes an apparatus designed to accelerate materials having a particle size diameter of between about 5 to about 50 microns, and to mix the particles with a process gas to provide the particles with a density of mass flow between about 0.01 and about 20 g/s-cm2. In other embodiments, a more focused range of mass flow may be about 0.1 to about 1 g/s-cm2. Supersonic velocity is imparted to the gas flow, with the jet formed at high density and low temperature using a predetermined profile. The resulting gas and powder mixture is introduced into the supersonic jet to impart sufficient acceleration to ensure a particle velocity ranging between about 500 and about 1200 m/s. In this method, the particles are applied and deposited in the solid state, i.e., at a temperature that is considerably lower than the melting point of the powder material and of the substrate. The resulting coating is formed by the impact and kinetic energy of the particles which gets converted to high-speed plastic deformation, causing the particles to bond to the surface. The system typically uses gas pressures of between 5 and 20 atm. As non limiting examples, the gases can comprise air, nitrogen, helium and mixtures thereof. Again, this system is but one example of the type of system that can be adapted to cold spray powder materials to the target surface.
A high velocity spraying system may be adapted for various materials. With respect to coatings on magnesium, it is preferred to use aluminum, titanium, or alloys thereof as the coating. Iron, nickel, copper, and alloys thereof may also be used to coat magnesium. Other materials that may be used as materials to produce a coating on aluminum include alloys of AlMg, alloys of AlSi, and mixtures of Al alloys with ceramic particles.
AlMg and AlSi alloys provide good corrosion resistance, provided impurity levels are controlled. These alloys also have sufficient strength and hardness to also provide erosion and wear resistance. Alloys of aluminum with inert ceramic particles can also provide good corrosion, erosion, and wear resistance. In general these alloys are not prone to form galvanic cells with the magnesium and so there is no need to cover the entire part. In addition, for duplex coatings these alloys should be used as a first base layer over which the other coatings are applied in order to reduce the possibility of setting up a galvanic cell.
Coatings with aluminum, titanium, their alloys, and composites containing hard particles of these metals provide a relatively hard coating that isolates the magnesium substrate. These coatings protect the magnesium material from degrading forces of wear, erosion, and corrosion. It is thus preferred that a coating substantially cover the substrate area where it is desired to provide protection. Voids and pin holes that expose the magnesium substrate are to be avoided. A coating with a thickness on the order of approximately 0.1 to 1.0 mm provides a significant degree of protection without significant weight increase to the component.
Material build up to repair corrosion and erosion pits in magnesium may still be significantly greater, even on the order of 10 to 20 mm in thickness. Such a thick deposition can be achieved according to the present invention partly because of the low average temperature rise. Such a thick repair is not feasible with thermal spray techniques.
Process parameters for the high velocity cold spray process can be varied depending on the repair material to be used. Examples of parameters that may be controlled include particle velocity, particle size, and particle preheat. With respect to the titanium and aluminum materials, titanium has a higher density than aluminum. At a given velocity, titanium will have a higher momentum than aluminum. However, in order to build-up coating deposits through high velocity cold spray process, a threshold critical velocity has to be exceeded; this is true for aluminum, titanium, and any other material. Although the higher density of titanium allows for a somewhat lowered critical velocity, other factors such as material strength and melting temperature also considerably affect the critical velocity. Hence, the estimated critical velocities for aluminum and titanium are somewhat similar, with a theoretical value of approximately 650 m/sec. A high velocity cold spray process would want to set a minimum velocity slightly above this number. Thus, to achieve good bonding with the magnesium substrate, it is possible to deposit titanium and aluminum powders when the particle velocities exceed 700 m/sec. Particle size also affects momentum. As particle size increases, it is generally necessary to increase the particle velocity.
The parameters of the high velocity cold spraying system are preferably balanced so as to achieve a good bonding between the particles and the substrate, yet without unduly damaging or gritting the substrate. The spraying process presents a potentially destructive force in the powder spray directed against the magnesium substrate. Additionally, the spraying process can produce a gritting effect on the substrate if the powder spray is directed against the magnesium substrate with particle velocities lower than the critical velocity. Cast magnesium structures as used in helicopter applications are relatively brittle. Application of inappropriate velocities can stress and crack the magnesium. Thus, to promote plastic deformation the process parameters of process gas and its temperature as well as inlet pressure, particle size, velocity, and particle temperature may be varied to form cold spray deposits. For aluminum, with helium as the process gas an exemplary range of parameters is about 5 to about 20 microns for the particle size range, particle velocities of about 500 m/sec to about 1200 m/sec. If the process gas is changed the parameters also necessarily change to meet the boundary conditions of cold spray deposit formation. For titanium deposition the parameters are similar, however, higher particle temperatures/higher velocities as compared to aluminum are advantageous to compensate for its inherent reduced plastic deformation behavior.
Referring now to
Referring now to
A suitable workpiece is first identified in step 100. Inspection of the workpiece confirms that the workpiece is a suitable candidate for repair according to embodiments of the present invention. The workpiece should not suffer from mechanical defects or other damage that would disqualify it from service, after receiving the coating treatment.
Step 110 reflects that the workpiece may be subjected to a pre-processing treatment to prepare the piece for receiving a material deposition in further steps. In one embodiment a surface of the component/workpiece receives a pre-treatment machining and/or degreasing in order to remove materials that interfere with cold spraying such as corrosion, impurity buildups, and contamination on the face of the workpiece. In addition the piece may receive a grit blasting with an abrasive such as aluminum oxide. In a further embodiment the method includes the step of shot or grit blasting the surface of the substrate prior to coating to create a rough surface.
After these preparatory steps, deposition of coating material commences in step 120 through high velocity cold spraying. In high velocity cold spraying, particles at a temperature below their melting temperature are accelerated and directed to a target surface on the component. When the particles strike the target surface, the kinetic energy of the particles is converted into plastic deformation of the particle, causing the particle to form a strong bond with the target surface.
The deposition of a coating layer through high velocity cold spraying may occur over several deposition cycles. For example, after a first pass takes place 120, the coating thickness of the first layer is checked 130. If the build-up of material is below a minimum, a second pass occurs 120 on top of the first layer. The thickness of material deposited is then checked again 130. In this manner a series of material deposition steps 120, 130 are repeated, as necessary or desired. Thus a series of spraying passes can build up a desired thickness of newly deposited material. Likewise, a series of spraying passes may be implemented in order to cover a desired surface area with subsequent spraying passes depositing material adjacent to coatings from earlier spraying passes. A series of spraying passes also advantageously provides thorough coverage of the coating over a desired substrate area. Multiple passes further help to avoid pin holes or other voids that expose the magnesium substrate to the environment.
In one embodiment, the additional layers deposited over a first layer in a coating may be of a different metal or alloy than the first layer. In this manner coatings are developed so that different laminates or layers of material may have different compositions. In one embodiment, a first layer of aluminum, aluminum alloy, or aluminum composite is deposited, and a second layer of titanium or titanium alloy is deposited over the underlying aluminum layer. The composition of each laminate may be selected so as to provide desired physical and metallurgical characteristics for the coating. For example, an outer titanium layer provides a relatively high degree of toughness, an outer layer of nickel provides a relatively high degree of wear resistance, and a layer of aluminum provides advantageous corrosion and weight characteristics.
In addition to varying the composition of the laminates in a particular coating, a coating may also be tailored to suit the needs of particular areas on the overall component surface. Areas in need of wear resistance may include coatings with nickel; areas needing toughness may include coatings with titanium. Areas without a need for toughness or wear resistance may be coated with aluminum. Thus, a component may be coated with one kind of coating in one area and with a different coating in another area. Care, however, must be taken to avoid forming galvanic cells. Coating all surfaces of the part and the use of alloys such as AlMg or AlSi minimizes that risk.
Next, an optional heat treatment 140 may be performed on the coated component. The heat treatment, when performed above recrystallization temperature, can provide a degree of crystal growth, if desired. An exemplary heat treatment for aluminum deposited on a magnesium substrate includes 1) a homogenizing treatment in the range of about 600° F. to about 725° F. for about 0.5 hours to about 2 hours in duration, and 2) a precipitation/aging treatment in the range of about 250° F. to about 425° F. for about 4 to about 16 hours in duration. The lower time limits in this heat treatment example are generally preferred when the higher temperatures are employed in the homogenization and the precipitation heat treatments. However, when other materials, such as titanium, are sprayed, temperatures higher than those mentioned may be used while taking into consideration the characteristics of magnesium base alloy materials.
Finally, an FPI (Fluorescent Penetration Inspection) procedure, as well as an x-ray inspection 150 may follow on the refurbished component. At this time the component may be returned to service, or placed in service for the first time.
Referring now to
While the high velocity coating process may be used with many kinds of substrates, it finds particular application with respect to magnesium substrates. One preferred embodiment entails restoring surfaces of magnesium gear boxes, generator housings, and other components. Examples of such magnesium structures are found in helicopter components.
While the invention has been described with reference to a preferred embodiment, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt to a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments falling within the scope of the appended claims.