Claims
- 1. Magnesium-silicate bound zeolite granulates, comprising zeolite dispersed in a silicate binder, the binder having contained a cation which is essentially completely replaced by magnesium, wherein the zeolite does not contain magnesium exclusively as the cation, or is magnesium free.
- 2. The magnesium-silicate bound zeolite granulates of claim 1 further comprising the binder is sodium silicate wherein the sodium ions are essentially completely exchanged by magnesium.
- 3. The magnesium-silicate bound zeolite granulates of claim 1 further comprising wherein the zeolite has a portion of its cation exchanged by a different cation.
- 4. The magnesium-silicate bound zeolite granulates of claim 1 further comprising the zeolite having sodium at its cation.
- 5. The magnesium-silicate bound zeolite granulates of claim 1 further comprising the sodium cation of the zeolite having been partially replaced by a different cation.
- 6. The magnesium-silicate bound zeolite granulates of claim 3 further comprising the cation of the zeolite partially exchanged by a different cation capable of penetrating into the zeolite lattice.
- 7. The magnesium-silicate bound zeolite granulates of claim 3 further comprising the cation of the zeolite partially exchanged by a metal ion selected from the group of potassium, sodium, silver, calcium, barium and zinc.
- 8. The magnesium-silicate bound zeolite granulates of claim 1 which contain as the zeolite a magnesium-sodium zeolite A having the following adsorption data and a kinetic index for water of at least 0.8:
- ______________________________________ Temp. Adsorp- Spec. Weight Degrees tion Partial loadingMolecule Percent C. time min. Press. l/min g*______________________________________H.sub.2 O .gtoreq. 22 20 30 20 0.8NH.sub.3 .gtoreq. 10 20 30 620 0.85CH.sub.3 OH .gtoreq. 15 20 30 150 1.0CO.sub.2 .gtoreq. 8 20 30 150 1.0n-Hexane .gtoreq. 4 20 30 580 1.1(C.sub.6 H.sub.14)______________________________________ *(adsorbed gas is diluted with carrier air, indicated in liters gas mixture per minute and per gram zeolite).
- 9. The magnesium-silicate bound zeolite granulates of claim 1 which contain as the zeolite a potassium zeolite A having the following adsorption data and a kinetic index of at least 0.7:
- ______________________________________ Temp. Adsorp- Spec. Weight Degrees tion Partial loadingMolecule Percent C. time min. Press. l/min g*______________________________________H.sub.2 O .gtoreq. 21 20 30 20 0.8NH.sub.3 .gtoreq. 7 20 30 620 0.85CH.sub.3 --OH .gtoreq. 6 20 30 150 1.0CO.sub.2 .gtoreq. 2 20 30 150 1.0n-Hexane .gtoreq. 3 20 30 580 1.1______________________________________ *(adsorbed gas is diluted with carrier air, indicated in liters gas mixture per minute and per gram zeolite).
- 10. The magnesium silicate-bound zeolite granulates of claim 1 which contain as the zeolite a sodium zeolite A having the following adsorption data and a kinetic index for water of at least 0.8:
- ______________________________________ Temp. Adsorp- Spec. Weight Degrees tion Partial loadingMolecule Percent C. time min. Press. l/min g*______________________________________H.sub.2 O .gtoreq. 24 20 30 20 0.8NH.sub.3 .gtoreq. 10 20 30 620 0.85CH.sub.3 --OH .gtoreq. 15 20 30 150 1.0CO.sub.2 .gtoreq. 10 20 30 150 1.0n-Hexane .gtoreq. 4 20 30 580 1.1______________________________________ *(adsorbed gas is diluted with carrier air, indicated in liters gas mixture per minute and per gram zeolite).
- 11. The magnesium-silicate bound zeolite granulates of claim 1 which contain as the zeolite a calcium zeolite A having the following adsorption data and kinetic index for water of at least 0.8:
- ______________________________________ Temp. Adsorp- Spec. Weight Degrees tion Partial loadingMolecule Percent C. time min. Press. l/min g*______________________________________H.sub.2 O .gtoreq. 22 20 30 20 0.8NH.sub.3 .gtoreq. 10 20 30 620 0.85CH.sub.3 --OH .gtoreq. 15 20 30 150 1.0CO.sub.2 .gtoreq. 14 20 30 150 1.1n-Hexane .gtoreq. 12 20 30 580 1.1______________________________________ *(adsorbed gas is diluted with carrier air, indicated in liters gas mixture per minute and per gram zeolite).
- 12. A process for the production of the magnesium-silicate bound zeolite granulates comprising mixing powdered zeolite A containing a cation with an alkali metal silicate binder solution until zeolite granulates with a grain size of at least 0.1 mm are obtained, treating the zeolite granulates thus obtained with an aqueous magnesium salt solution to thereby exchange the alkali metal of the said silicate binder with magnesium ions and permitting the exchanged alkali metal ions of the silicate binder to remain in the solution of magnesium salt whereby complete exchange of the cation in the zeolite is prevented, to thereby obtain magnesium-silicate bound zeolite granulates wherein the zeolite contains no magnesium or wherein only a portion of the cations of the zeolite are replaced by magnesium.
- 13. The process of claim 12 further comprising rolling the zeolite granulates after they are formed.
- 14. The process of claim 12 further comprising initially drying the zeolite granulate.
- 15. The process of claim 14 further comprising drying at a temperature of about 20 to 39 degrees C.
- 16. The process of claim 14 further comprising drying in air where the carbon dioxide content is less than 200 ppm.
- 17. The process of claim 12 further comprising a second drying step.
- 18. The process of claim 17 further comprising a second drying step at 40 to 120 degrees C.
- 19. The process of claim 17 further comprising a third drying step.
- 20. The process of claim 19 further comprising a third drying step at 121 to 200 degrees C.
- 21. The process of claim 12 further comprising activating the zeolite granulate by heating to a temperature of no more than 600 degrees C.
- 22. The process of claim 12 further comprising thereafter washing the magnesium salt treated zeolite granules.
- 23. The process of claim 12 further comprising treating the zeolite granulate with a second aqueous salt solution.
- 24. The process of claim 23 further comprising thereafter washing.
- 25. The process of claim 24 further comprising drying.
- 26. The process of claim 25 further comprising drying at 40 to 200 degrees C.
- 27. The process of claim 26 further comprising drying at 100 to 120 degrees C.
- 28. The process of claim 25 further comprising calcining.
- 29. The process of claim 28 further comprising calcining at 300 to 650 degrees C.
- 30. The process of claim 28 further comprising calcining at 300 to 600 degrees C.
- 31. The process of claim 30 further comprising calcining at 400 to 450 degrees C.
- 32. The process of claim 12 further comprising washing to zeolite granulates obtained after treatment with the aqueous magnesium salt solution, and then treating with an aqueous potassium salt solution, washing, and drying.
- 33. The process of claim 32 further comprising calcining at 300 to 550 degrees C.
- 34. The process of claim 33 further comprising calcining at 350 to 450 degrees C.
- 35. The process of claim 12 further comprising washing the zeolite granulates obtained after treated with the aqueous magnesium salt solution, and then treating with an aqueous sodium salt solution, washing and drying.
- 36. The process of claim 35 furthor comprising calcining at 300 to 600 degrees C.
- 37. The process of claim 36 further comprising calcining at 400 to 500 degrees C.
- 38. The process of claim 12 further comprising washing zeolite granulates obtained after treatment with the aqueous magnesium salt solution, and then treating with an aqueous calcium salt solution, washing and drying.
- 39. The process of claim 38 further comprising calcining at 300 to 650 degrees C.
- 40. The process of claim 39 further comprising calcining at 450 to 600 degrees C.
- 41. Magnesium-silicate bound zeolite granulates comprising zeolite dispersed in a silicate binder, the binder having contained a cation which is essentially completely replaced by magnesium and wherein the zeolite is magnesium free, said granulates having been produced by reacting silicate bound zeolite A with an aqueous magnesium salt.
- 42. Magnesium-salt bound zeolite granulates comprising zeolite dispersed in the silicate binder, the binder having contained a cation which is essentially completely replaced by magnesium, the zeolite being a metal alumino silicate, the metal of which is only partially replaced by magnesium, said granulates having been produced by reacting silicate bound zeolite A with an aqueous magnesium salt.
Priority Claims (1)
Number |
Date |
Country |
Kind |
3312877 |
Apr 1983 |
DEX |
|
REFERENCE TO RELATED APPLICATION
This is a continuation of our copending application Ser. No. 597,286 filed Apr. 6, 1984, now abandoned, which is relied on and incorporated by reference.
US Referenced Citations (8)
Continuations (1)
|
Number |
Date |
Country |
Parent |
597286 |
Apr 1984 |
|