Magnetic field sensor having a flux guide to increase the effective capture area

Information

  • Patent Grant
  • 6344742
  • Patent Number
    6,344,742
  • Date Filed
    Friday, November 6, 1998
    25 years ago
  • Date Issued
    Tuesday, February 5, 2002
    22 years ago
Abstract
A magnetic field sensor has a SQUID, which is made of thin film of oxide superconductor deposited on a substrate, and a magnetic flux guide that has a higher permeability than vacuum to increase the effective capture area. The flux guide is positioned and aligned over a hole that is surrounded with superconducting current loop formed in a washer thereof. The SQUID also has a pair of Josephson junction formed on the washer and a pair of opposite terminals for connecting the washer to an outer circuit. In the SQUID, a variation in magnetic flux passing through the hole is detected in a form of variation in output voltage.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




The present invention relates to a magnetometer or a device for detecting or measuring a weak magnetic field (hereinafter, a magnetic field sensor) improved in the effective capture area, in particular a magnetic field sensor having SQUID made of oxide superconductor.




2. Description of the Related Art




SQUID (Superconducting Quantum Interference Device) is a high sensitive magnetic field sensor consisting of a superconducting loop having one or two Josephson junctions. A typical SQUID pattern formed in a thin film of oxide superconductor deposited on a substrate consists of a washer which forms a superconducting current loop surrounding a hole, a pair of Josephson junctions formed in the washer, and a pair of opposite terminals for connecting the washer to an outer circuit. In the SQUID, a variation in magnetic flux of a magnetic field passing through the hole is detected or measured as a variation in output voltage.




In order to enhance the sensitivity or resolution of SQUID type magnetic field sensor, it is necessary to increase the effective capture area (A


eff


) of the SQUID through which the magnetic flux passes.




Applied Physics Letters 59(1), July 1991, p123 discloses a SQUID coupled with a flux transformer to increase the sensitivity. This known magnetic flux sensor requires additional manufacturing step to prepare multi-turns of a pickup coil for the flux transformer in a thin film of oxide superconductor, so that the productivity is not high. Another demerit of this sensor resides in that flux transformer made of superconductor must be cooled down to a temperature lower than the critical temperature when it is used.




Japanese Journal of Applied Physics. Vol. 32 (1993), page L662 proposes to use a flux capture plate plate made of superconductor. Use of the flux capture plate plate is, however, limited due to such a fact that it is difficult to prepare in practice a large area thin film of oxide superconductor and hence its size is limited.




An object of the present invention is to solve the problems of known magnetic field sensors and to provide a magnetic field sensor having a simple structure but increased in the effective capture area.




SUMMARY OF THE INVENTION




The present invention provides a magnetic field sensor having a SQUID, characterized in that a flux guide made of a material that has a higher permeability than vacuum is arranged in such a manner that a flux passing through said flux guide is coupled with said SQUID.




The flux guide has preferably a height that is three times longer than a diameter of an end surface which is faced closely to the SQUID and has preferably a form of a truncated corn or polygon. The magnetic field guide can be a hollow body or has a through-hole passing from one end surface to another end surface.




The term “couple” includes two cases that the flux guide is coupled directly or indirectly with the SQUID.




In the direct coupling, the flux guide is placed preferably in coaxial with a hole and over a washer of the SQUID. In the indirectly coupling, the flux guide is placed on a pickup coil which is connected to the SQUID, so that the magnetic flux is guided to the pickup coil by the flux guide. Or, the flux guide is placed on a flux transformer which is connected to an input coil with which the SQUID is coupled, so that the magnetic flux is guided to the flux transformer by the flux guide and is sensed by the SQUID through the input coil.




The flux guide has preferably a pair of end surfaces each having a different surface area and a tapered side surface connecting the end surfaces, and one of the end surfaces is arranged in such a manner that the flux is guided to the SQUID and to the pickup coil by the flux guide. A ratio of diameter of an end surface which is opposite to an end surface which is faced closely to the SQUID to the latter end surface is more than 3 times but is less than 15 times.




The magnetic flux guide can be made of Permalloy.




The SQUID, coils, flux transformer and flux capture plate can be made of thin film(s) of oxide superconductor.




An additional flux capture plate can be arranged between the SQUID and the flux guide.




The magnetic field sensor can have a shield plate made of a material having a higher permeability than vacuum. The shield plate is arranged around the flux guide and in parallel with the SQUID.




An essence of the magnetic field sensor according to the present invention resides in that the flux guide made of a material having a higher permeability than vacuum is combined with SQUID directly or indirectly.




The magnetic flux guide used in the magnetic field sensor according to the present invention can be produced very easily because the flux guide has a simple shape, but has improved sensitivity due to its magnetic property or high permeability. Still more, since the flux guide is not made of superconductor, there is no special limitation in its dimensions and any flux guide having desired properties can be obtained.




The magnetic flux guide of the magnetic field sensor according to the present invention has preferably such a height that is three times longer more than a diameter of an end surface which is faced closely to the SQUID, when a shape of the magnetic flux guide is considered as a cylinder.




The magnetic flux guide has preferably such a shape that a ratio of diameter of a larger end surface to a smaller end surface that is faced closely to the SQUID is more than 3 times. By this arrangement, the magnetic flux can be captured much effectively comparing to a SQUID having the same effective capture area. The advantage of enlargement in effective capture area can not be expected when the ratio becomes more than 15 times. Therefore, the ratio is limited preferably within a range between 3 times and 15 times.




The flux guide is preferably made of Permalloy that is a material having high permeability and available on market. “Material having high permeability” means material whose permeability is higher than that of vacuum.




DESCRIPTION OF THE PREFERRED EMBODIMENTS




Now, several embodiments of magnetic field sensor according to the present invention will be described with referring to attached drawings. The scope of the invention, however, is not limited by these embodiments.











BRIEF DESCRIPTION OF THE DRAWINGS





FIGS. 1A and 1B

illustrate a magnetic field sensor according to the present invention;

FIG. 1A

is a plan view and

FIG. 1B

is a side view.





FIG. 2A

schematically illustrates the flux field according to prior art.





FIG. 2B

schematically illustrates the flux field when a magnetic flux guide is used according to the present invention.





FIGS. 3A and 3B

illustrate another embodiment of the present invention;

FIG. 3A

is a plan view and

FIG. 3B

is a side view.





FIG. 4

illustrates another embodiment according to the present invention that incorporates a flux transformer.





FIGS. 5A-5C

illustrate various configurations of the magnetic flux guide according to the present invention;

FIG. 5A

is a perspective view of a truncated cone configuration,

FIG. 5B

is a perspective view of a truncated trapezoid configuration, and

FIG. 5C

is a side view of

FIGS. 5A and 5B

, illustrating how the magnetic flux guide is positioned.





FIG. 6

schematically illustrates the function of the magnetic flux guide of

FIGS. 5A-5C

.





FIGS. 7A and 7B

illustrate the magnetic field sensor of

FIG. 4

with a SQUID;

FIG. 7A

is a side view and

FIG. 7B

is an end view.





FIGS. 8A and 8B

illustrate another magnetic field sensor according to the present invention, with a capture plate.





FIG. 9

is a plan view of a prior art SQUID made of oxide superconductor.





FIGS. 10A and 10B

illustrate another embodiment of a magnetic flux guide;

FIG. 10A

is a perspective view and

FIG. 10B

is a cross-sectional view.





FIG. 11

illustrates how the magnetic flux guide of

FIGS. 10A and 10B

changes the flux field.





FIGS. 12A and 12B

illustrates another embodiment of a magnetic flux guide, which is similar to the embodiment of

FIGS. 10A and 10B

, but with a shield plate;

FIG. 12A

is a perspective view and

FIG. 12B

is a cross-sectional view.





FIG. 13

illustrates the function of the flux guide of FIGS.


12


A and


12


B.











DETAILED DESCRIPTION




Firstly, a structure of the conventional SQUID (Superconducting Quantum Interference Device) is recalled with reference to

FIG. 9

which shows a typical SQUID made of a t film of oxide superconductor. This SQUID is prepared in a thin film of oxide superconductor deposited on a substrate. A pattern of SQUID consists of a washer


13


that forms a superconducting current loop surrounding a hole


12


, a pair of Josephson junctions


11


formed on the washer


13


, and a pair of opposite terminals


14


for connecting the washer


13


to an outer circuit. In the SQUID, a variation in magnetic flux passing through the hole


12


is detectable in a form of variation in output voltage.





FIGS. 1A and 1B

illustrate showing the principle of a Magnetic field sensor according to the present invention. As is shown in

FIGS. 1A and 1B

, a magnetic field sensor according to the present invention consists mainly of a SQUID


10


formed on a substrate


15


and a flux guide


20


positioned on the SQUID


10


. The SQUID


10


itself is same as the conventional SQUID of FIG.


9


. The flux guide


20


is placed on a hole pattern


12


in such a manner that the SQUID


10


is positioned coaxially with the washer


13


.





FIGS. 2A and 2B

is an illustrative view explaining the function of the magnetic field sensor shown in FIG.


1


.

FIG. 2A

shows a case when only SQUID


10


that is formed on the substrate


15


detects the magnetic flux. In this case, the magnetic flux detected by the SQUID


10


is limited to those that pass inside the washer


13


of the SQUID


10


.

FIG. 2

(B) shows a case of the present invention in which the magnetic flux is attracted or absorbed by the flux guide


20


of high permeability so that SQUID


10


detects a larger area of the magnetic flux which is determined by a horizontal cross sectional area of the flux guide


20


. In other words, a larger area of the magnetic flux which is wider than effective capture area (A


eff


) of the SQUID


10


alone.





FIGS. 3A and 3B

illustrate another embodiment of a magnetic field sensor according to the present invention. The magnetic field sensor has a pickup coil


16


connected to a SQUID


10


as is shown in

FIG. 3A and a

flux guide


20


according to the present invention is placed on the pickup coil


16


.





FIG. 4

is an illustration showing a flux transformer that is used in another embodiment of a magnetic field sensor according to the present invention. The flux transformer


30


is a pattern formed in a thin film of oxide superconductor deposited on a substrate


33


as is shown in FIG.


4


and consists of a pickup coil


31


of a big rectangular and an input coil


32


having a plurality of windings. The windings of the input coil


32


are separated from crossunder by an insulator layer


34


inserted beneath the input coil


32


. A flux guide


20


according to the present invention is positioned at the center of the pickup coil


31


of the flux transformer


30


.





FIGS. 5A-5C

illustrate variations of the flux guide usable in the magnetic field sensor according to the present invention. As is shown in

FIG. 5A

, the flux guide


21


has a smaller base end, a larger top end and a tapered side surface connecting the end surfaces.





FIG. 6

is an illustration showing such a fact that the above-mentioned shape permits to converge the magnetic flux capture plated at the larger top end and to guide the resulting converged flux toward a SQUID so that the magnetic flux is introduced into the SQUID at high efficiency. Sensitivity of the magnetic field sensor can be adjusted by modifying the shape or configuration of the flux guide.




The flux guide has a horizontal cross section of a circle as is shown in FIG.


5


A and can have a horizontal cross section of a rectangular as is shown in

FIG. 5B

so as to accord to a hole pattern of SQUID. Of course, any horizontal cross section can be used in accordance with necessity and advantage of the present invention does not depend on the shape of horizontal cross section.





FIGS. 7A and 7B

illustrate how to combine the magnetic flux transformer


30


shown in

FIG. 4

with a SQUID. As is shown in

FIGS. 7A and 7B

, a substrate


15


having a SQUID


10


thereon is reversed up and down and is positioned in such a position that an input coil


32


of the magnetic flux transformer on which a magnetic flux guide


21


(


22


) is positioned is faced closely to the SQUID


10


. This arrangement permit to transfer a magnetic flux capture plated by the flux guide


21


(


22


) to the SQUID


10


at very high efficiency.





FIGS. 8A and 8B

show another embodiment of the present invention in which a capture plate


35


is used. The capture plate


35


can be prepared by a thin film of oxide superconductor deposited on a substrate.





FIGS. 10A and 10B

illustrate another structure of the magnetic flux guide that can be used in the magnetic field sensor according to the present invention. As is shown in

FIG. 10A

, the magnetic flux guide


23


used in this embodiment has the same side view of a truncated cone as shown is

FIG. 5B

but is a hollow body having an open top end and an open bottom end as is shown in a cross section of FIG.


10


B.





FIG. 11

is a mimetic diagram illustrating how the magnetic fluxes pass or distribute when the hollow magnetic flux guide


23


of

FIGS. 10A and 10B

is placed in a magnetic field.

FIG. 11

reveals such a fact that the fluxes passing through the magnetic flux guide


23


is concentrated at a narrower end thereof and such displacement occurs along a surface of the flux guide


23


and that the flux guide functions to concentrate the magnetic flux. In other words, the effective capture area (A


eff


) of SQUID can be increased by arranging the flux guide in such a manner that its narrower end surface faces closely to the SQUID.




The hollow flux guide can be manufactured by any known technique such as molding in which the flux guide is obtained in a piece, machining in which a bore is drilled in a solid body, or deformation of a sheet metal. Material of the hollow flux guide may be the same as those above-mentioned.





FIGS. 12A and 12B

illustrate a magnetic flux guide assembly that can be made of basically same material as the magnetic flux guide shown in

FIGS. 10A and 10B

. The magnetic flux guide assembly shown in

FIGS. 12A and 12B

comprises the same flux guide


23


as shown in

FIGS. 10A and 10B

and a flat shield plate


24


. The flat shield plate


24


has a center hole as is shown in

FIG. 12B

into which a top end of the flux guide


23


is inserted. The flat shield plate


24


can be made of a material having high permeability.




The magnetic flux guide assembly is placed on a SQUID in such a manner that the flux guide


23


is arranged at the same position as the flux guide shown in

FIGS. 5A-5C

. In this assembly, the function of flux guide


23


is same as shown in

FIGS. 10A and 10B

but an additional advantage is obtained by the flat shield plate


24


.





FIG. 13

is a mimetic diagram illustrating how the magnetic fluxes pass or distribute when the flat shield plate


24


is placed in a magnetic field.

FIG. 13

reveals that the magnetic fluxes passing through the flat shield plate


24


is concentrated at opposite ends thereof and hence, when the flat shield plate


24


is used, surrounding magnetic fluxes that do not pass through the flux guide


23


can be separated from SQUID so that much precious detection of fluxes is assure. The flat shield plate


24


has another function to that the SQUID can be separated from magnetic fluxed which are in parallel with the SQUID.




Now, we will explain several examples of magnetic field sensors produced according to the present invention.




EXAMPLE 1




A thin film of Ho


1


Ba


2


Cu


3


O


7−x


(0≦x≦1) having a thickness of 2,000 Å was deposited on a substrate made of SrTiO


3


on which a step having a height of 1,500 Å was made. The thin film was then etched to have a pattern and dimensions shown in

FIG. 9

to produce a step-edge type SQUID having Josephson junctions. The Josephson junction has a width of 3 μm. The SQUID has an inductance of 80 pH.




The SQUID was immersed in liquid nitrogen to find the effective capture area (A


eff


) of 0.2 mm


2


.




Then, a cylindrical flux guide made of Permalloy and having a diameter of 2 mm and a height of 10 mm was placed on the SQUID and the effective capture area (A


eff


) was measured. The effective capture area (A


eff


) increased to 0.3 mm


2


.




EXAMPLE 2




Example 1 was repeated but the magnetic flux guide made of Permalloy and having a shape and dimensions shown in

FIG. 5A

was placed on the SQUID.




The effective capture area (A


eff


) increased to 0.6 mm


2


.




EXAMPLE 3




A SQUID having a pickup coil shown in

FIG. 3

was fabricated with the same material as Example 1. This SQUID has a hole having the same dimension as Example 1 and the pickup coil is rectangular each side being 5 mm. The same magnetic flux guide as Example 2 was placed on the SQUID equipped with the pickup coil and the effective capture area (A


eff


) was determined.




The effective capture area (A


eff


) increased from 0.2 mm


2


to 0.6 mm


2


.




EXAMPLE 4




A magnetic capture plate for fluxes is added to a SQUID that was then combined with the magnetic flux guide to prepare a magnetic field sensor. Namely, the capture plate having a shape and dimensions shown in

FIG. 8A

was placed over the same SQUID as Example 1 and then a magnetic flux guide made of the same material and having a shape and dimensions shown in

FIG. 5A

was placed on the capture plate to produce a magnetic field sensor having a cross sectional view of FIG.


8


B.




The effective capture area (A


eff


) determined by the same method as other Examples increased from 0.3 mm


2


to 0.9 mm


2


.




EXAMPLE 5




A magnetic flux transformer having an input coil consisting of ten (10) rectangular turns or windings and having a 10 mm square pickup coil was fabricated with the same material of SQUID in Example 1. An insulation layer


34


for the input coil was made of thin film of SrTiO


3


. The magnetic flux transformer was combined with the same SQUID as Example 1 to fabricate a magnetic field sensor. The effective capture area (A


eff


) of this sensor was 1.0 mm


2


.




Then, a magnetic flux guide having the same shape as

FIG. 5A

but having a base diameter of 9 mm was placed on the magnetic flux transformer to fabricate another magnetic field sensor. The effective capture area (A


eff


) of this sensor was 2.0 mm.




EXAMPLE 6




A member which functions by itself as a magnetic field sensor was prepared by using the same SQUID and magnetic flux transformer as Example 5 was fabricated. A magnetic flux guide having a reverse truncated conical shape having a base diameter of 9 mm which faces to the member, a top diameter of 27 mm and a height of 45 mm was placed on the member to fabricate a magnetic field sensor.




The effective capture area (A


eff


) of this magnetic field sensor was 4.0 mm


2


.




EXAMPLE 7




A member, which functions by itself as a magnetic field sensor, was prepared by using the same SQUID. A hollow magnetic flux guide having a reverse truncated conical shape having a base diameter of 10, a top diameter of 3 mm and a height of 10 mm was fabricated from a sheet having a thickness of 1 mm and was placed on the SQUID to prepare a magnetic field sensor.




The effective capture area (A


eff


) of this magnetic field sensor was 0.6 mm


2


.




EXAMPLE 8




The same SQUID and a magnetic flux guide as Example 7 were used.




A magnetic shield plate as is shown in

FIGS. 12A and 12B

was fabricated form a metal sheet having a thickness of 1 mm, a width of 30 mm and a length of 30 mm. The magnetic flux guide was placed on the SQUID and the magnetic shield plate was positioned in parallel with a surface of the, SQUID at a distance of 2 mm to prepare a magnetic field sensor.




The effective capture area (A


eff


) of this magnetic field sensor was 0.6 mm


2


. Magnetic noise was reduced one order comparing to Example 1 by using the magnetic shield plate.




In the examples, although Ho


1


Ba


2


Cu


3


O


7−1


was used to prepare SQUID and other parts, the material is not limited to this but the same advantages can be obtained when the magnetic flux is combined with SQUID made of other oxide superconductors such as Y


1


Ba


2


Cu


3


O


7−


or metal type superconductors are used.




As is described above, the magnetic field sensor according to the present invention has a simple structure but permits to increase the effective capture area at high efficiency.




The magnetic flux guide used in the magnetic field sensor according to the present invention can be produced from not expensive material and easily so that manufacturing cost of the magnetic field sensor can be reduced. The magnetic field sensor according to the present invention can be handled easily. In summary, the present invention increases application of the magnetic field sensors.



Claims
  • 1. A magnetic field sensor comprising:a SQUID having a washer with a hole, a superconducting current loop surrounding the hole, a pair of Josephson junction formed on the washer, and a pair of opposite terminals for connecting the washer to an outer circuit; and a flux guide that has a higher permeability than vacuum coupled with said SQUID to increase an effective capture area of flux passing through the hole, wherein said flux guide comprises a truncated cone with a through-hole extending from one end surface to an opposite end surface, wherein said flux guide further includes a shield plate made of a material having a higher permeability than vacuum, said shield plate being arranged around the opposite end surface of said truncated cone and parallel with said SQUID.
  • 2. The magnetic field sensor set forth in claim 1, wherein said truncated cone is coupled directly with the SQUID.
  • 3. The magnetic field sensor set forth in claim 2, wherein said truncated cone is positioned coaxially with said hole, over said washer of said SQUID.
  • 4. The magnetic field sensor set forth in claim 1, wherein said truncated cone is coupled indirectly with the SQUID.
  • 5. The magnetic field sensor set forth in claim 4, further including a magnetic flux transformer connected to said washer, wherein said truncated cone is placed on said magnetic flux transformer so that said truncated cone guides magnetic flux to said magnetic flux transformer.
  • 6. The magnetic field sensor set forth in claim 5, wherein said magnetic flux transformer has a pickup coil and an input coil connected to said pickup coil, wherein said truncated cone is placed on said pickup coil so that said truncated cone guides magnetic flux to said pickup coil.
  • 7. The magnetic field sensor set forth in claim 6, wherein the one end surface is arranged over said pickup coil to guide flux to said pickup coil.
  • 8. The magnetic field sensor set forth in claim 7, wherein a ratio of diameter of the opposite end surface and the one end surface positioned next to said pickup coil is more than 3 times but is less than 15 times.
  • 9. The magnetic field sensor set forth in claim 1, wherein said truncated cone is made of Permalloy.
  • 10. The magnetic field sensor set forth in claim 1, wherein said SQUID, said pickup and input coils of said magnetic flux transformer, and flux capture plate are made of thin film of oxide superconductor.
  • 11. A magnetic field sensor comprising:a SQUID having a washer with a hole, a superconducting current loop surrounding the hole, a pair of Josephson junction formed on the washer, and a pair of opposite terminals for connecting the washer to an outer circuit; and a flux guide that has a higher permeability than vacuum coupled with the SQUID to increase an effective capture area of flux passing through the hole, wherein the flux guide comprises a body having a through-hole passing from one end surface to an opposite end surface, and having a tapered side surface that connects the end surfaces, wherein the one and opposite end surfaces of the body have different surface areas and the one end surface is positioned facing the washer, and wherein the flux guide has a shield plate made of a material having a higher permeability than vacuum, the shield plate being arranged around the opposite end surface of the body and parallel with the SQUID.
  • 12. The magnetic field sensor set forth in claim 11, further including a magnetic flux transformer connected to the washer, wherein the body is placed on the magnetic flux transformer so that the body guides the magnetic flux to the magnetic transformer.
  • 13. The magnetic field sensor set forth in claim 12, wherein the magnetic flux transformer has a pickup coil and an input coil connected to said pickup coil, wherein the one end surface of the body is placed on said pickup coil so that the body guides magnetic flux to said pickup coil.
  • 14. The magnetic field sensor set forth in claim 13, wherein the body has a truncated cone configuration, with a ratio of diameter of the other end surface and the one end surface positioned next to said pickup coil is more than 3 times but is less than 15 times.
Priority Claims (3)
Number Date Country Kind
9-322432 Nov 1997 JP
10-163788 Jun 1998 JP
10-258350 Sep 1998 JP
US Referenced Citations (5)
Number Name Date Kind
4971947 Barnes et al. Nov 1990 A
4996621 Ruigrok et al. Feb 1991 A
5463518 Otomo et al. Oct 1995 A
5483161 Deeter et al. Jan 1996 A
5901453 Zhang et al. May 1999 A
Foreign Referenced Citations (2)
Number Date Country
0 315 258 May 1998 EP
9000742 Jan 1990 WO
Non-Patent Literature Citations (3)
Entry
Musikowski et al., “Welding unit for hollow section bolts—with magnetic flux shaping to produce field componensts radial to the bolt”, Derwent Information ltd., Acct. No. 1995-124084, pp. 1-2.*
Oh, B., et al., “Multilevel YBaCuO Flux Transformers With High Tc SQUIDs: A Prototype High Tc SQUID Magnetometer Working at 77 K,” Applied Physics Letters, 59(1), pp. 123-125 (Jul. 1991).
Tanaka, S., et al., “Properties of YBa2Cu3O7-y Large Washer SQUID,” Japanese Journal of Applied Physics, vol. 32, pp. L662-L664 (May 1993).