Patent Application
20050200438
The present invention relates generally to magnetic nanoparticles and method of synthesising magnetic nanoparticles. More specifically, the invention relates to ferromagnetic nanoparticles made upon decomposition of organometallic precursors, used for example in high density information storage media, light emitting diodes, passive components such as transformers, on-chip signal isolation, inductors, and the like, to improve passive component performance in high frequency integrated circuit applications.
In high frequency integrated circuit applications, such as used in wireless portable electronic devices, there is a demand for miniaturisation, greater functionality, higher performance, and lower cost, which can be achieved through the integration of passive components such as inductors and transformers in integrated circuits. The lack of passive component integration on integrated circuits contributes to a passives-to-actives component ratio as high as 100:1 in typical electronic systems. However, current passive components, when integrated with active elements on integrated circuits consume large areas of silicon, making their integration often not economical. Therefore, methods are developed to reduce the space used up by passive components on integrated circuits.
One approach to reduce the area of an inductor in an integrated circuit is through the integration of magnetic materials, for example materials that have a permeability greater than one. The aim of this approach is to increase the inductance per unit area through taking advantage of the increased electro-magnetic energy storage capability of high-permeability materials. The associated size reduction of the inductor enables enhanced performance (higher Q-factor) through reduced series resistance and reduced parasitic capacitance. In transformers, the same materials properties enable an increased coupling coefficient, hence increasing the energy transfer in a transformer while also enabling smaller area through confining the electromagnetic field lines within the magnetic material, hence allowing increased device packing density. The traditional method for achieving such passive device improvements is using amorphous or crystalline solid thin film magnetic materials, such as for example as disclosed in EP0716433. However, at high frequency applications, for example high MHz or low GHz frequencies, methods such as this have performance limitations due to eddy current losses and loss-generating ferromagnetic resonance (FMR).
An attempt to overcome these associated deficiencies has been to spatially separate and electrically isolate magnetic nanoparticles, i.e. particles of nanometer size, such that the material is ferromagnetic at device operating temperatures, and preferably being composed of a single magnetic domain. Since eddy current losses can be suppressed and the FMR decay extended to higher frequencies, the magnetic nanoparticles allow an increase in inductance density per unit area in the MHz-GHz range. It is important, however, that the composite magnetic nanoparticle material has properties such as a magnetic permeability (μ), i.e. greater than 1 (one), and corresponding losses (μ″) such that the quotient of (permeability)/(loss) is, for example, greater than 5 in the MHz-GHz frequency range of interest.
Several methods have been attempted to produce nanoparticles with some of these qualities, and generally fall in three categories: physical methods, template methods and chemical methods.
Physical methods such as sputtering and epitaxy (See for instance Y. M. Kim et al, IEEE Trans. on Magn. vol. 37, no. 4, 2001, and M. Dumm et al, Journal of Applied Physics vol. 87, no. 9, 2000, respectively) produce thin layers. However, both methods produce high permeability films only up to approximately 500 MHz and generally cannot be thicker than 2-3 micrometers in order to minimise eddy current losses. However, such performance is not sufficient for an effective magnetic field confinement needed to enhance passive devices.
Template methods such as the one described by Cao, H., Xu, Z., Sang, H., Sheng, D., Tie, C. Adv. Mater. 2001, vol. 13, p. 121 grow, usually electrochemically, nanorods or nanowires within the channels of inorganic or track-etched organic matrices. The main drawback of this method comes from the destruction of the organic or inorganic matrix after the particle formation that yields by-products, which generally interfere with the nanoparticles. This results in a decrease of the saturation magnetization compared to that of bulk metal and may also prevent the formation of high density material.
Chemical methods like chemical reduction or decomposition of a carbonyle precursor such as described by Sun, S. Murray, C. B. J. Appl. Phys. 1999, vol. 85, p. 4325 or by Alivisatos, P. Puntes, V. F. Krishnan, K. M. Appl. Phys. Lett. 2001, vol. 78, p. 2187 involve synthesis of nanoparticles in solutions. The chemical methods, and more specifically the method of Sun et al. results in the production of self-assembled monodisperse spherical cobalt particles from a carbonyl cobalt precursor for use in high-density recording. However, due to their small size, the particles remain superparamagnetic at room temperature, and hence will not generate the required magnetic field confinement as achieved by high permeability materials. Additional work has been disclosed by the same authors in Sun, S. Murray, C. B. Weller, D. Folks, L. Moser, A. Science 2000, vol. 287, p. 1989 generating iron-platinum (Fe/Pt) particles to enhance the magnetic anisotropy of the material. However, similarly to above, the small size of the particles in the material makes them superparamagnetic, hence not useful for magnetic field confinement. In Puntes, V. F. Krishnan, K. M. Alivisatos, A. P. Science 2001, vol. 291, p. 2115 cobalt nanorods are produced from a carbonyl cobalt precursor by using a mixture of oleic acid and trioctylphosphine oxide (TOPO). However this requires a high temperature process of, for example, approximately 300° C. Moreover, the nanorods obtained in this way are not thermodynamically stable and typically spontaneously rearrange into spherical nanoparticles within the first few seconds of the reaction. Iron and Nickel nanorods have also been recently reported through decomposition of, respectively Fe(CO)5 (Park, S.-J.; Kim, S.; Lee, S.; Khim, Z. G.; Char, K.; Hyeon, T. J. Am. Chem. Soc. 2000, vol. 122, p. 8581) and Ni(COD)2 (N. Cordente, C. Amiens, F. Senocq, M. Respaud, and B. Chaudret, Nano Letters 2001, 1(10), p. 565) in the presence of ligands such as TOPO and hexadecylamine (HDA). Both materials are not homogeneous (particles do not display the same shape). Furthermore, these particles are superparamagnetic at room temperature and hence unsuitable for magnetic field confinement.
Thus, there is a need for a magnetic material consisting of magnetic nanoparticles that are ferromagnetic at room temperature and/or operating temperatures up to for example approximately 105° C., and of homogeneous size, shape, and magnetic orientation. Furthermore, there is a need for a method of making such thermodynamically stable magnetic nanoparticles of adjustable aspect ratio encapsulated within a non-magnetic matrix, so that such final magnetic nanoparticle materials could be used in high frequency integrated circuit applications, such as used in wireless portable electronic devices, to enhance magnetic field confinement in a variety of passive and active devices.
In accordance with the invention there is provided a magnetic nanoparticle as claimed in claim 1, a magnetic nanomaterial as claimed in claim 12, and a method for synthesising magnetic nanoparticles as claimed in claim 14.
Embodiments of the invention will now be more fully described, by example, with reference to the drawings, of which:
In high frequency integrated circuit applications, such as used in wireless portable electronic devices, passive components such as inductors and transformers, as well as structures for signal isolation, can be improved through the integration with magnetic nanoparticle materials. One particular method in accordance with an embodiment of the invention is the use of composite materials comprising of a matrix material containing a certain volume fraction of magnetic nanoparticles that have a saturation magnetization (Ms) and an anisotropy (Hk) where all three (volume fraction, Ms, and Hk) are optimised such that the composite material has a permeability high enough and a ferromagnetic resonance at high enough frequencies such as to allow improved RF-passive devices (such as inductors, transformers, isolation) at high MHz and GHz frequencies. Saturation magnetization (Ms) can be optimised through varying the chemical composition of the nanoparticles. Anisotropy (Hk) can be optimised through the crystal structure, the shape of the nanoparticles and the composite material itself. In addition, in order to take maximum advantage of the electric-field confining property of composite magnetic nanoparticle materials it is required that the axis of anisotropy of the particles are all aligned with each other. The typical approach taken to meet this requirement is to first increase the overall anisotropy of the material, which can be achieved by modifying the shape of the particles. Instead of forming nanospheres one forms more desirable shapes such as elongated particles (ellipsoids, rods, wires or other regular, non-spherical particles). These particles must be large enough to be ferromagnetic at the maximum device operating temperature (e.g. 105° C.) but small enough that they consist preferably of a single magnetic domain (or only a few magnetic domains), i.e. their size has to be in the order of 2 to 30 nm in both, diameter and length. Then, the nanoparticles are self-assembled and are electrically isolated from each other through a ligand shell or other means of insulating layers, such as a native oxide shell, a silicon oxide coating or other insulating coatings. However, ideally the material that contains the nanoparticles should be highly resistive, act as an oxidation inhibitor for the nanoparticles, and be chemically stable for temperatures of at least up to, for example, approximately 150° C.
The high yield synthesis, for example nearly 70% of the cobalt initially introduced in the solution is found in the nanorods, of this method results at step 20 in air-stable nanorods aligned along the same axis, e.g. c-axis, and of uniform diameter size, as shown in
The nanoparticles that result from this embodiment exhibit magnetic properties, such as for example: i) saturation magnetization similar to the magnetic characteristics and properties of bulk cobalt; ii) enhanced magnetic anisotropy and strongly enhanced coercive magnetic field (as compared to bulk cobalt and spherical nanoparticles) due to the shape anisotropy. Here the coercive field is mainly determined by the shape anisotropy. For example in spherical nanoparticles of 4.9 nm diameter, the magnetic anisotropy Hc=800 Gauss, but for the nanorods obtained with oleylamine and oleic acid as stabilizing agents, Hc=8900 Gauss; and iii) ferromagnetism at room temperature (or higher) while remaining single domain.
The decomposition of the organometallic precursor at step 18 may be achieved within, for example, 48 hours at 150° C. in anisole, and provides a high yield, for example, approximately 70% in organized nanomaterial that in this embodiment is composed of individual nanorods having dimensions of, for example, approximately 9 nm in diameter and of a length of 50-100 nm as shown in
In this embodiment, the nanoparticles are single crystalline and display the hcp structure of bulk cobalt, such that each particle is aligned along the c-axis of the hcp structure. The nanoparticles are spaced apart by a distance of, for example, 3 nm, which corresponds to the total width of the ligand shell between two neighbouring nanoparticles.
Thus, in this embodiment, the ferromagnetic nanoparticles, for example nanorods, synthesised contain a ligand shell, for example oleylamine and oleic acid, any combination of carboxylic-acid/amine or any amine or acid, or the like, which has multiple beneficial consequences. For example, the organic ligands serve some of the following purposes: i) induce the anisotropic growth of the nanoparticles with the main axis coinciding with the c_axis of the hcp crystallographic structure ii) protect the nanoparticles from air oxidation and other chemical reactions such as formation of surface hydroxides, and the like; iii) allow the dispersion of nanoparticles in organic solvents with no detrimental influence on the nanoparticle magnetic properties; iv) allow nanoparticles to self-align along each nanoparticle crystal anisotropy axis; and v) generate electrically isolated particles hence limiting eddy current losses and preventing domain formation across multiple particles which results in improved high-frequency behaviour; and vi) allow particle orientation in magnetic fields to optimise high-frequency device applications.
Of course, it will be appreciated that the method herein described may be used for other ferromagnetic elements such as for example iron, nickel, and the like, and related alloys such as for example FeCo, NiFeCo and the like, and the inclusion of metallic or non-metallic impurities that may be intentionally added with the particles such as, tantalum, boron, oxygen, nitrogen and the like, to modify the magnetic material properties in a predetermined configuration to best suit specific implementations, such as integrated passive component devices.
It will be appreciated that although the particular embodiments of the invention have been described above, various other modifications and improvements may be made by a person skilled in the art without departing from the scope of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 02290455.1 | Feb 2002 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP03/01165 | 2/6/2003 | WO | 4/27/2005 |