1. Field of the Invention
The present invention relates to a magnetic recording medium and a manufacturing method thereof, and more particularly to a magnetic recording medium suitable for external storage devices of computers and a manufacturing method thereof. More specifically, the present invention relates to a magnetic recording medium which has a lubricating layer including a perfluoropolyether compound having a perfluorotrimethyleneoxy repeating unit in the main chain and a cyclic triphosphazene structure, and which makes it possible to reduce the head flying height, and also to a manufacturing method thereof. The present invention also relates to a method for reducing the head flying height and improving the electromagnetic conversion property of a magnetic recording medium by changing the mixing ratio of the perfluoropolyether compound in the lubricating layer.
2. Background of the Related Art
In order to improve durability and reliability of a magnetic recording medium (in particular, a magnetic disk) and also to reduce a friction force generated between the protective layer of the magnetic recording medium and the head, it is necessary to impart a lubricating property to the magnetic recording medium. For example, a lubricating property has been improved by forming a lubricating layer including a perfluoropolyether lubricant having a polar end group such as a hydroxyl group in a molecule on a diamond-like carbon (DLC) film that is typically used as a protective layer for magnetic recording media.
Further, Patent Document 1, WO 2007/043450, describes the feature of forming a lubricating layer by using a perfluoropolyether lubricant represented by Formula (V) and having a cyclic triphosphazene structure in a molecule with the objective of improving the adhesion to a magnetic recording medium and reducing decomposition ability. Further, Patent Document 2, WO 2006/009057, describes the feature of forming a lubricating layer by using a mixture of a compound with p=1 and a compound with p=2 in Formula (V). Patent Document 3, WO 2008/140121, describes the feature of forming a lubricating layer by using a perfluoropolyether lubricant having a cyclic triphosphazene structure with a different number of perfluoropolyether side chains.
A lubricating layer formed on a protective layer can be assumed to be constituted by two layers. The first layer is a layer bonded to the protective layer (referred to hereinbelow as “bonded lubricating layer”), and the other is a layer present on the bonded lubricating layer and not bonded to the protective layer (referred to hereinbelow as “free lubricating layer”). From the standpoint of improving the properties, it is preferred that the lubricating layer have a structure with a thin free lubricating layer and a thick bonded lubricating layer.
However, following recent trend to increase in density of magnetic recording media (magnetic disks), more stringent requirements have been placed on the lubricant properties. In order to meet such requirements, it is important to ensure compatibility of heads and magnetic disks, and a lubricant material is needed that will make it possible to bring the head close to the magnetic disk (to reduce the head flying height).
In addition, the number of cases in which the recently developed hard disk drives are used not only for personal computers that are used indoors, but also in outdoor environment such as portable devices and car navigation systems, has grown. When the hard disk drive is used in an outdoor environment, in particular, a high-temperature and high-humidity environment, such environment makes it difficult for a magnetic head slider to levitate. This problem is apparently attributable to cohesion of moisture contained in high-humidity air. Therefore, the problem of disposing a lubricant more accurately on the surface of a magnetic recording medium (magnetic disk) used in a hard disk drive is of major importance.
In order to solve this problem, it is important to reduce the height of the molecule and control the orientation of the lubricant on the protective film. Fomblin (trade name) Z-dol (Formula (III)) and Fomblin (trade name) Z-tetraol (Formula (IV)) lubricants, which are presently typically used for magnetic recording media, are perfluoropolyether compounds having a hydroxyl group at either end (in the formulas, p and q are integers equal to or greater than 0, but the case in which p=q=0 is excluded).
The specific feature of the compound represented by Formula (III) and/or Formula (IV) is that when a lubricating layer is formed by coating on a protective layer, C, F, and O contained in the molecular structure are arranged randomly. This specific feature is affected by the molecular structure (hydroxyl group present at each end) represented by Formula (III) or Formula (IV). Due to random arrangement, active oxygen atoms face the head side (front surface side), rather than the protective layer side. As a result, the adsorption of contaminating substances is enhanced and the adsorptivity on the head slider surface is increased. Such phenomena cause a variation in head flying property.
Therefore, in order to decrease the head flying height and improve the flying stability, a lubrication material is needed that has a chemical structure different from that represented by Formula (III) and/or Formula (IV). In this regard, Non-Patent Document 1, IEEE Transactions on Magnetics, “Lubricant Pickup of Ultra-Thin PFPE Lubricants with Different Backbone Structures”, Vol. 47, No. 7, July, 2011, pp. 1837-1841, reports that a lubricant pickup by the head is different when a lubricant is used that has the structure represented by Formula (I) which has a different main-chain repeating unit.
In the case of conventional lubricant containing the compound represented by Formula (III) and/or Formula (IV), the head flying property has been improved by optimizing the additive to be added and the mixing ratio thereof, the total film thickness of the lubricating layer, and the bonded ratio. However, the problem is that when such means as the decrease in the total film thickness and/or increase in the bonded ratio is used to improve the head flying property, other properties (durability and the like) of the magnetic recording medium (in particular, the lubricating layer) are degraded.
An objective of the present invention is to provide a magnetic recording medium that can realize high electromagnetic conversion property by reducing the head flying height, without degrading other properties, and also to provide a manufacturing method thereof.
A magnetic recording medium according to a first embodiment of the present invention, comprises: a nonmagnetic substrate and provided thereon, in the order recited; an underlayer; a magnetic layer; a protective layer comprised of carbon; and a lubricating layer comprised of a lubricant mixture comprising a lubricant represented by Formula (I) below
where m is an integer equal to or greater than 1, and R1 and R2 are divalent straight chains consisting of both —CH2CF2—or both —CH2CF2CF2—; and
a lubricant represented by Formula (II) below
where p and q are integers equal to or greater than 0, provided that p =q =0 is excluded. The lubricant represented by Formula (II) is described in Patent Documents 1 and 2.
A method of manufacturing a magnetic recording medium according to a second embodiment of the present invention comprises forming an underlayer on a non-magnetic substrate; laminating a magnetic layer on the underlayer; laminating a protective layer comprised of carbon on the magnetic layer; and forming a lubricating layer by laminating, on the protective layer, a lubricant mixture comprised of a lubricant represented by Formula (I) below
where m is an integer equal to or greater than 1, and R1 and R2 are divalent straight chains consisting of both —CH2 CF —or both —CH2 CF2CF2—; and
a lubricant represented by Formula (II) below
where p and q are integers equal to or greater than 0, provided that p=q=0 is excluded.
A method according to a third embodiment of the present invention is a method for reducing flying height of a head and improving an electromagnetic conversion property in a magnetic recording medium, comprising: providing the magnetic recording medium described above; and changing at least one of a usage amount of the lubricant represented by Formula (I) and a mixing ratio of the lubricant represented by Formula (I) and the lubricant represented by Formula (II).
In the magnetic recording medium in accordance with the present invention, a lubricating layer constituted by a mixture of a compound represented by Formula (I) that includes a —(CF2CF2CF2O)m— structure in the main chain and the compound represented by Formula (II) is provided instead of the lubricating layer including a generally used lubricant having a —(CF2CF2O)m(CF2O)n— structure in the main chain, thereby making it possible to reduce the head flying height and realize a magnetic recording medium surface with high durability. Further, it is found out that this effect is made more prominent by setting the usage amount of the lubricant represented by Formula (II) (see Patent Documents 1 and 2) equivalent to the film thickness ranging from 0 Å to 3 Å. By reducing the head flying height, it is possible to improve the electromagnetic conversion property of the magnetic recording medium.
The magnetic recording medium according to the first embodiment of the present invention includes a non-magnetic substrate, an underlayer, a magnetic layer, a protective layer including carbon, and a lubricating layer.
Various substrates with a smooth surface that are known in the related art can be used as the non-magnetic substrate. For example, a NiP-plated Al alloy (Al—Mg or the like), reinforced glass, and crystallized glass, which are used in the conventional magnetic recording media, can be used as the non-magnetic substrate.
In the present invention, the underlayer may be a soft magnetic layer for concentrating a magnetic flux generated by the head in the magnetic layer when perpendicular magnetic recording is performed, an intermediate layer for forming a magnetic layer having good magnetic properties by controlling the orientation of the magnetic layer, a seed layer for improving the orientation ability and adhesivity of the intermediate layer, or a laminated structure thereof.
A soft magnetic underlayer can be formed by using a crystalline material such as FeTaC and Sendust (FeSiAl) alloy, or an amorphous material including a Co alloy such as CoZrNb and CoTaZr.
The intermediate layer is used for controlling the crystal grain size and crystal orientation of the magnetic layer and preventing magnetic coupling between the soft magnetic underlayer (when such is present) and the magnetic layer. Therefore, it is preferred that the intermediate layer be nonmagnetic. The crystal structure of the intermediate layer is appropriately selected according to the material of the magnetic layer. For example, when the magnetic layer positioned directly thereabove is formed from a material based on Co and having a hexagonal closely packed (hcp) structure, the intermediate layer can be formed using a material having a hcp or a face-centered cubic (fcc) structure. Alternatively, the intermediate layer may have a non-crystalline structure. Examples of the preferred materials for forming the intermediate layer include Ru, Re, Rh, Pt, Pd, Ir, Ni, Co, and alloys thereof.
The seed layer is used with the object of ensuring adhesion between the intermediate layer and the non-magnetic substrate or soft magnetic underlayer (when such is present) and controlling the orientation of the intermediate layer. The seed layer can be formed using NiW, Ta, Cr, or an alloy including Ta and/or Cr. The seed layer may also have a layered structure constituted by a plurality of layers including the aforementioned material.
In the present invention, the magnetic layer can be formed using a crystalline magnetic material. The crystalline magnetic materials that can be used include ferromagnetic materials such as alloys including at least Co or Pt (for example, Co—Cr—Ta, Co—Cr—Pt). In this case, the axis of easy magnetization of the ferromagnetic material should be oriented in the direction in which magnetic recording is performed. In order to perform perpendicular magnetic recording, the axis of easy magnetization of the material of the magnetic layer (c-axis of the hcp structure) should be oriented in the direction perpendicular to the surface of the magnetic recording medium (that is, to the main plane of the non-magnetic substrate). Alternatively, the magnetic layer may have a structure in which magnetic crystal grains are separated by a non-magnetic body (the so-called granular structure). In this case, it is preferred that the magnetic crystal grains have a columnar shape with a diameter of several nanometers. It is preferred that the non-magnetic body have a subnanometer thickness. The materials for forming magnetic crystal grains include alloys based on magnetic elements such as Co, Fe, and Ni. It is preferred that materials for forming the magnetic crystal grains include materials obtained by adding a metal such as Cr, B, Ta, and W to a CoPt alloy. Meanwhile, the materials for forming the non-magnetic body include oxides or nitrides of Si, Cr, Co, Ti, or Ta.
In the present invention, the carbon materials for forming the protective layer include amorphous carbon and diamond-like carbon (DLC).
The underlayer, magnetic layer, and protective layer including carbon are formed using means typically used in the related art.
The lubricating layer of the magnetic recording medium in accordance with the present invention can be formed using a mixture of a lubricant represented by Formula (I)
(in the formula, m is an integer equal to or greater than 1), which includes a perfluorotrimethylene repeating unit (—CF2CF2CF2O—) in the main chain and has a hydroxyl group (—OH) at each end, and a lubricant represented by Formula (II)
(in the formula, p and q are integers equal to or greater than 0; the case in which p=q=0 is excluded). As an example of the lubricant represented by Formula (I) includes D4OH (manufactured by MORESCO), which is described in Non-Patent Document 1. As an example of the lubricant represented by Formula (II) includes ADOH (manufactured by MORESCO).
The lubricating layer of the magnetic recording medium in accordance with the present invention is desirably constituted only by the mixture of the lubricant represented by Formula (I) and the lubricant represented by Formula (II). In this case the added amount of the lubricant represented by Formula (II) is desirably set equivalent to a film thickness of 0.3 Å to 3 Å.
The lubricating layer of the magnetic recording medium in accordance with the present invention can be formed by a coating method using a solution including, as a solid component, a mixture of the lubricant represented by Formula (I) and the lubricant represented by Formula (II). The coating method can be a dipping method. Post-treatment such as UV treatment and tape varnish treatment may be implemented after the lubricating layer has been formed.
The magnetic recording medium in accordance with the present invention will be explained below in greater detail on the basis of examples therefor. However, the present invention is not limited to the below-described examples and can be variously changed without departing from the essence thereof.
A magnetic disk substrate with a diameter of 65 mm that was covered with a protective layer of diamond-like carbon with a thickness of 2.0 nm was fabricated by a plasma CVD method. A mixture of D4OH represented by Formula (I) and ADOH represented by Formula (II) was dissolved in a Vertrel XF (manufactured by Du Pont-Mitsui Fluorochemicals Co., Ltd.) solvent, and a lubricating layer coating liquid was produced. A magnetic disk substrate was immersed into the lubricating layer coating solution, pulled up at a rate of 1.5 mm/sec and then dried. The dry coating film was then UV treated using a UV lamp with an emission peak wavelength of 185 nm/254 nm and an output of 200 W and the lubricating layer was formed. In this case, the concentration of D4OH in the lubricating layer coating liquid containing only D4OH and the concentration of D4OH and ADOH in the lubricating layer coating liquid using the mixture were adjusted such that the total film thickness of the obtained lubricating layer was 7 Å to 10 Å and the film thickness of ADOH, which was an additive, was 0.3 Å to 3.0 Å. Further, the lubricating layer was formed such that the thickness of the bonded lubricant was about 6.00 Å and the bonded ratio was 75.0%.
The “total film thickness of the lubricating layer” in the present invention is the thickness of the lubricating layer at the time the lubricating layer is formed, and it is measured with a Fourier transform IR spectrophotometer (FT-IR). The “film thickness of the bonded lubricating layer” in the present invention is the thickness of the layer of the lubricant that is actually bonded to the carbon surface of the protective layer. More specifically, the “film thickness of the bonded lubricating layer” is the thickness of the lubricating layer after the obtained lubricating layer has been washed using Vertrel XF (manufactured by Du Pont-Mitsui Fluorochemicals Co., Ltd.), and it is measured with a Fourier transform IR spectrophotometer (FT-IR).
The degree of bonding of a lubricant with functional groups present on the carbon surface of a protective layer is typically represented by the ratio of the lubricating layer thickness after washing with a fluorine-containing solvent to the lubricating layer thickness prior to washing with the fluorine-containing solvent, and the percentage value thereof is called “bonded ratio”. In the present invention, the “bonded ratio” is determined by the following formula by using the film thickness prior to washing with the aforementioned Vertrel XF (manufactured by Du Pont-Mitsui Fluorochemicals Co., Ltd.) (that is, the total film thickness of the lubricating layer) to the film thickness after the washing (that is, the film thickness of the bonded lubricating layer).
Math. 1:
Bonded ratio (%)=[(Film thickness of lubricating layer after washing)/(Film thickness of lubricating layer prior to washing)]×100
A lubricating layer was formed by repeating the procedure of Example 1, except that the lubricating layer coating liquid was formed using a mixture of Fomblin (trade name) Z-tetraol (Formula (IV)) and ADOH. The concentrations of the Fomblin (trade name) Z-tetraol and ADOH in the coating liquid were adjusted such that the total film thickness of the obtained lubricating layer was 8.0 Å and the film thickness of ADOH, which was the additive, was 2.0 Å. Further, the lubricating layer was formed such that the thickness of the bonded lubricating layer was about 6.00 Å and the bonded ratio was 75.0%.
A lubricating layer was formed by repeating the procedure of Example 1, except that ADOH was not used. The concentrations of the D4OH in the coating liquid were adjusted such that the total film thickness of the obtained lubricating layer was 9.0 Å. Further, the lubricating layer was formed such that the thickness of the bonded lubricating layer was about 6.00 Å and the bonded ratio was 75.0%.
Evaluation
1. Low Flying Height Property:
A flying height limit was measured using RQ7800 (manufactured by Hitachi) which is shown schematically in
The flying height limit value obtained for the sample of Comparative Example 2 that used D4OH including a —(CF2CF2CF2O)m— structure in the main chain and the sample of Example 1 using the mixture of D4OH and ADOH was lower than that obtained for the sample of Comparative Example 1 using Fomblin (trade name) Z-tetraol including a —(CF2CF2O)m(CF2O)n— structure in the main chain. The dependence of the flying height limit value on the added amount of ADOH, which was an additive, and the dependence of the flying height limit value on the total film thickness of the lubricating layer were not observed. However, as a result of using D4OH or the mixture of D4OH and ADOH, the flying height limit value was improved by about 2% to about 5%.
2. Low Flying Height Property:
As shown schematically in
The results in Table 2 and
3. Durability Characteristic:
Durability was evaluated by using a friction player (FPR-2100) manufactured by RHESCA and shown schematically in
The results in Table 3 and
The above-described results demonstrate that the lubricating layer in accordance with the present invention that is constituted by a mixture of D4OH having the structure represented by Formula (1) and ADOH having the structure represented by Formula (II) makes it possible to reduce the head flying height by comparison with that of the lubricating layer constituted by the generally used mixture of Fomblin (trade name) Z-tetraol and ADOH. Therefore, it is apparent that the lubricating layer in accordance with the present invention is extremely effective means for reducing a gap between a head and a magnetic recording medium and providing a magnetic recording medium having a better electromagnetic conversion property. Furthermore, it is determined that durability of the lubricating layer is greatly increased by the addition of ADOH by comparison with that in the case in which only D4OH is used. Thus, it is clear that by optimizing the added amount of ADOH it is possible to decrease the head flying height and increase durability of the lubricating layer.
Number | Date | Country | Kind |
---|---|---|---|
2012-015247 | Jan 2012 | JP | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/JP2012/007058 | 11/2/2012 | WO | 00 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2013/111223 | 8/1/2013 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
20080020171 | Wakabayashi et al. | Jan 2008 | A1 |
20090291325 | Xu et al. | Nov 2009 | A1 |
20100136371 | Shimizu et al. | Jun 2010 | A1 |
20100239887 | Kobayashi | Sep 2010 | A1 |
20110143165 | Kobayashi et al. | Jun 2011 | A1 |
20120021253 | Nakata et al. | Jan 2012 | A1 |
20130083422 | Ooeda et al. | Apr 2013 | A1 |
Number | Date | Country |
---|---|---|
1989228 | Jun 2007 | CN |
2009-270093 | Nov 2009 | JP |
2009-542805 | Dec 2009 | JP |
2010-108583 | May 2010 | JP |
2010168512 | Aug 2010 | JP |
2010-248463 | Nov 2010 | JP |
WO-2006009057 | Jan 2006 | WO |
WO-2007043450 | Apr 2007 | WO |
WO-2008140121 | Nov 2008 | WO |
WO-2009066784 | May 2009 | WO |
WO-2009122988 | Oct 2009 | WO |
WO-2010027096 | Mar 2010 | WO |
Entry |
---|
Tani, H. et al., “Lubricant Pickup of Ultra-Thin PFPE Lubricants With Different Backbone Structures”, IEEE Tranactions on Magnetics, vol. 47, No. 7, pp. 1837-1841, Jul. 2011. |
Number | Date | Country | |
---|---|---|---|
20140212692 A1 | Jul 2014 | US |