Magnetic recording medium

Abstract

A magnetic recording medium is disclosed, which comprises a nonmagnetic support having thereon a magnetic layer containing at least ferromagnetic metal particles, wherein said ferromagnetic metal particles have a coercive force of from 1,700 to 3,000 Oe, an average long axis length of from 30 to 80 nm, an average acicular ratio of from 2.0 to 5.0, and a crystallinity of from 30 to 100%.

Description

FIELD OF THE INVENTION

The present invention relates to a magnetic recording medium, e.g., a magnetic tape. More particularly, this invention relates to a coating type magnetic recording medium which has a magnetic layer formed by coating on a nonmagnetic support a magnetic coating composition containing ferromagnetic metal particles and a binder as major components, and which is excellent in output, C/N, and overwriting characteristics in a short-wavelength region.

BACKGROUND OF THE INVENTION

The technique of magnetic recording has excellent advantages over other recording systems, for example, that a recording medium can be repeatedly used, that signal conversion into electronic signals is so easy that a magnetic-recording apparatus can be combined with peripheral devices to construct a system, and that signals can be easily revised. Due to such advantages, the magnetic recording has been widely utilized in various fields including video, audio, and computer applications.

With respect to recording media, a further improvement in recording density, reliability and durability has been always desired so as to cope with desires for size reduction in appliances, improvement in the quality of reproduced signals, elongation of recording time, and an increase of recording capacity.

For example, magnetic recording media for use in audio and video applications have come to be required to have suitability for the recording/reproduction of signals having an even shorter wavelength than in conventional systems and to be excellent in reliability and durability even at an increased head/medium relative speed, in order to cope with practical use of the digital recording system attaining improved sound and image quality and with the development of a video recording system for high-definition television.

Also, in computer applications, it is desired to develop a large-capacity digital recording medium for storing an increasing quantity of data therein.

For the attainment of a higher recording density in coating type magnetic recording media, various methods have been investigated and proposed, for example, from the standpoint of obtaining a magnetic layer having improved magnetic characteristics by replacing conventional magnetic iron oxide particles with magnetic particles of iron or an alloy mainly comprising iron or by using magnetic particles with improved magnetic characteristics, e.g., finer magnetic particles, and improving the filling property and orientation property of these magnetic particles, and from the standpoints of improving the dispersibility of ferromagnetic particles and enhancing the surface properties of a magnetic layer.

For example, a technique of using ferromagnetic metal particles or a hexagonal ferrite as ferromagnetic particles in order to enhance magnetic characteristics is disclosed in, e.g., JP-A-58-122623 (the term "JP-A" as used herein means an "unexamined published Japanese patent application"), JP-A-6174137, JP-B-62-49656 (the term "JP-B" as used herein means an "examined Japanese patent publication"), JP-B-60-50323, and U.S. Pat. Nos. 4,629,653, 4,666,770, and 4,543,198.

JP-A-1-18961 discloses ferromagnetic metal particles having a long axis length of 0.05 to 0.2 .mu.m, an acicular ratio of 4 to 8, a specific surface area of 30 to 55 m.sup.2 /g, a coercive force (Hc) of 1,300 Oe or more, and a saturation magnetization (.sigma..sub.s) of 120 emu/g or more. This technique is to provide fine metal particles having a small specific surface area.

JP-A-60-11300 and JP-A-60-21307 disclose a process for producing fine acicular crystals of .alpha.-iron oxyhydroxide which are suitable for use in producing ferromagnetic particles, in particular, ferromagnetic metal particles. The latter reference discloses that ferromagnetic metal particles having an Hc of 1,450 to 1,600 Oe and a .sigma.s of 142 to 155 emu/g are produced from goethite having a long axis length of 0.12 to 0.25 .mu.m and an acicular ratio of 6 to 8.

JP-A-6-340426 and JP-A-7-109122 disclose monodisperse spindle-shaped hematite particles obtained from hematite nuclei, iron hydroxide, and specific ions and extremely fine ferromagnetic particles obtained by reducing the hematite particles.

It has also been proposed to use various surfactants (as disclosed in, e.g., JP-A-52-156606, JP-A-53-15803, JP-A-53-116114) and various reactive coupling agents (as disclosed in, e.g., JP-A-49-59608, JP-A-56-58135, JP-B-62-28489) for enhancing the dispersibility of ferromagnetic particles.

JP-A-1-239819 discloses magnetic particles obtained by successively adhering a boron compound and an aluminum compound or an aluminum compound and a silicon compound to the surface of magnetic iron oxide particles. This prior art technique is to improve magnetic characteristics and dispersibility.

JP-A-7-22224 discloses ferromagnetic metal particles in which the content of Group 1a elements of the Periodic Table is 0.05% by weight or less and which may contain aluminum and a rare earth element in amounts of 0.1 to 30% and from 0.1 to 10%, respectively, in terms of the amount of the atoms thereof based on the total amount of all metallic elements and may have a content of residual Group 2a elements of the Periodic Table of 0.1% by weight or less. This technique is to provide a high-density magnetic recording medium having good storage stability and excellent magnetic characteristics.

Furthermore, a technique of treating the surface of a magnetic layer after coating and drying for improving the surface properties of the magnetic layer has been proposed (as disclosed in, e.g., JP-B-60-44725).

Strenuous efforts are being made to use signals having shorter wavelengths in order to attain higher recording densities in magnetic recording media. In a magnetic recording medium in which the length of a region used for recording a signal has become a size comparable with that of the magnetic particle used, recording is virtually impossible because a distinct magnetization transition state cannot be created. Consequently, it is necessary to develop a magnetic particle having a particle size sufficiently smaller than the shortest wavelength to be used, and investigations have long been direct to particle size reduction in magnetic particles.

With respect to metal particles for magnetic recording, an acicular particle shape is employed to impart shape anisotropy to thereby obtain a desired coercive force. It is well-known to persons skilled in the art that for attaining higher-density recording, ferromagnetic metal particles should be finely divided into finer particles so as to obtain a medium having diminished surface roughness. However, the metal particles for use in magnetic recording tend to have a lower acicular ratio with decreasing particle size and, as a result, come to be incapable of having a desired coercive force. A DVC system in which video signals are recorded as digital signals was proposed recently, for which a high-performance ME tape and a high-performance MP tape are used. Since the MP tape for use in DVC has a coercive force of 2,000 Oe or higher, it is necessary to employ fine ferromagnetic metal particles having a high coercive force and an excellent particle size distribution. Moreover, since DVC is a recording system in which signals are recorded over signals which have been recorded, the ferromagnetic metal particles for use therein are required to have satisfactory overwriting characteristics.

The applicant previously proposed ferromagnetic metal particles suitable for use in a DVC system and a magnetic recording medium containing the ferromagnetic metal particles (JP-A-7-326035), for the purpose of providing a magnetic recording medium having a magnetic layer regulated so as to have a coercive force of 2,000 to 3,000 Oe, a thickness of 0.05 to 0.3 .mu.m, and a surface roughness of 1 to 3 nm and to have a specific content of components undergoing reversal of magnetization.

SUMMARY OF THE INVENTION

The present invention is connected with the prior art technique described just above, and provides a means for further improving the uniformity in performance and quality of the prior art magnetic recording medium.

The present invention has been achieved in view of problems of the prior art techniques described above.

An object of the present invention is to provide a magnetic recording medium which has satisfactory short-wavelength output and SIN and excellent overwriting characteristics and is applicable to a high-density digital recording system.

The object of the present invention is accomplished with (1) a magnetic recording medium comprising a nonmagnetic support having thereon a magnetic layer containing at least ferromagnetic metal particles, wherein said ferromagnetic metal particles have a coercive force (Hc) of from 1,700 to 3,000 Oe, an average long axis length of from 30 to 80 nm, an average acicular ratio (long axis/short axis) of from 2.0 to 5.0, and a crystallinity of from 30 to 100%. Also object is preferably accomplished with (2) a magnetic recording medium of the kind described in (1) above which has a nonmagnetic layer mainly comprising inorganic nonmagnetic particles and a binder between the nonmagnetic support and the magnetic layer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a view illustrating a ferromagnetic metal particle for use in the present invention.

FIG. 2 is a view illustrating a conventional ferromagnetic metal particle.

Description of the Symbols!

1 ferromagnetic metal particle 2 crystallite

DETAILED DESCRIPTION OF THE INVENTION

In the present invention, the average long axis length of ferromagnetic metal particles means the average lengths of the long axes of the individual particles, while the average short axis length thereof means the average lengths of the short axis of the individual particles. The average acicular ratio thereof means the value obtained by dividing average long axis length by the average short axis length.

The crystallinity of ferromagnetic metal particles in the present invention means the proportion of particles each consisting of one crystallite to all of from 200 to 300 grains, which are examined with a high-resolution electron microscope. The crystallites mean the individual metal crystals of which the ferromagnetic metal particles are composed. The individual ferromagnetic metal particles, which each is defined by the metal particle contour, need not consist of one crystal and may be composed of two or more crystallites. In a photograph taken with a high-resolution transmission electron microscope, the particle defined by a largest particle contour is a ferromagnetic metal particle. Upon closer examination of the photograph, lattice images are obtained. The units which give the lattice images are crystallites. The acicular ratio of a crystallite means the value obtained by dividing the long axis length of the crystallite by the short axis length thereof.

According to the present invention, by regulating ferromagnetic metal particles so as to have an average long axis length of from 30 to 80 nm and an average acicular ratio of from 2.0 to 5.0 and simultaneously regulating the ferromagnetic metal particles so as to have a crystallinity of from 30 to 100%, the coercive force (H.sub.c) and the .sigma..sub.s of the ferromagnetic metal particles can be regulated to from 1,700 to 3,000 Oe and from 125 to 165, respectively. As a result, a magnetic recording medium having satisfactory short-wavelength output and S/N and excellent overwriting characteristics can be provided.

In the present invention, the average long axis length of the ferromagnetic metal particles is from 30 to 80 nm, preferably from 30 to 70 nm, more preferably from 35 to 60 nm, in order to reduce the surface roughness of the magnetic recording medium. The average acicular ratio of the ferromagnetic metal particles is from 2.0 to 5.0, preferably from 2.5 to 5.0. The crystallinity is from 30 to 100%, preferably from 35 to 100%, more preferably from 40 to 100%.

Ferromagnetic metal particles having an average long axis length of smaller than 30 nm are undesirable since not only the desired coercive force cannot be obtained, but also such ferromagnetic metal particles are dispersed with difficulty in the preparation of a magnetic coating composition and are less effectively oriented in magnetic field orientation. In addition, due to the influence of the oxide film formed for stabilization, it is difficult to ensure a high saturation magnetization necessary for high-density recording. Ferromagnetic metal particles having an average long axis length exceeding 80 nm are undesirable since H.sub.c cannot be effectively heightened because a crystallinity of from 30 to 100% is obtained with difficulty and the reversal of magnetization does not occur by the simultaneous rotation mechanism.

A crystallinity of lower than 30% are undesirable from the standpoint of overwriting characteristics because not only such ferromagnetic metal particles cannot have a high H.sub.c, but also the H.sub.c distribution thereof is deteriorated considerably �in particular, r3000/H.sub.c (i.e., (proportion of components undergoing reversal of magnetization at an H.sub.c of 3,000 Oe or higher)/H.sub.c) increases!. Although the crystallinity of ferromagnetic metal particles should be from 30 to 100%, it is preferably 40% to 100%. Ideal ferromagnetic metal particles have a sufficiently low coefficient of variation of average long axis length �(standard deviation of long axis length)/(average long axis length)! and an average acicular ratio of, in particular, from 3 to 5 and have a crystallinity of 100%, because such ferromagnetic metal particles have a high H.sub.c and a narrow H.sub.c distribution. When raw materials having the same composition were reduced under various conditions to impart various crystallinity, ferromagnetic metal particles having higher crystallinity tended to have lower contents of high-coercive-force components.

The ferromagnetic metal particles used in the present invention have a saturation magnetization of generally from 125 to 165 emu/g, preferably from 135 to 165 emu/g. A technique effective in obtaining ferromagnetic metal particles having a heightened saturation magnetization is to conduct, just after reduction, a treatment with any of compounds described in JP-A-61-52327 and JP-A-7-94310 and coupling agents having various substituents, followed by gradual oxidation. The coercive force of the ferromagnetic metal particles is from 1,700 to 3,000 Oe, preferably from 1,800 to 2,600 Oe. The present inventor presumes that by regulating ferromagnetic metal particles so as to have a crystallinity of from 30 to 100%, the mode of reversal of magnetization becomes close to the simultaneous rotation mode as stated above and the ferromagnetic metal particles obtained can be fine particles having a high coercive force as in the present invention.

The magnetic layer of the present invention has a coercive force (H.sub.c) of usually from 1,800 to 3,000 Oe, preferably from 1,900 to 2,800 Oe, more preferably from 2,200 to 2,800 Oe, and a B.sub.m (maximum flux density) of usually from 3,500 to 5,500 gauss (G), preferably from 3,900 to 5,500 G. If H.sub.c or B.sub.m is lower than the above lower limit, sufficiently high short-wavelength output cannot be obtained. If H.sub.c or B.sub.m is higher than the above upper limit, high output cannot be ensured because the head used for recording is saturated.

According to the present invention, both a high H.sub.c and an improved H.sub.c distribution can be imparted even to ferromagnetic metal particles to which it has been difficult to impart a high coercive force and a reduced content of high-coercive-force components, by directing attention to the crystallites which constitute the ferromagnetic metal particles and controlling the crystallinity. It is thought that in conventional processes, attainment of a high H.sub.c and improvement of H.sub.c distribution are insufficient because the starting material used has an insufficiently regulated shape and because the resulting ferromagnetic metal particles are not regulated in the number and shape of the crystallites constituting each ferromagnetic metal particle.

In the present invention, any desired method may be used for regulating the ferromagnetic metal particles without particular limitations. However, a preferred method is as follows.

A starting material having uniformity in particle size is subjected to a sintering prevention treatment and then reduced, while regulating the number of metal (e.g., Fe) nuclei formed from a metal oxide (e.g., FeO or Fe.sub.3 O.sub.4) and further regulating the crystallinity. Examples of the starting material include monodisperse goethite and monodisperse hematite.

The starting material desirably has an average long axis length of from 40 to 120 nm and an acicular ratio of from 3 to 10. If a starting material having an average long axis length of smaller than 40 nm is used, H.sub.c and .sigma..sub.s cannot be regulated to values within the respective desired ranges. If a starting material having an average long axis length of larger than 120 nm is used, it is difficult to heighten the crystallinity, so that H.sub.c cannot be heightened. If a starting material having an acicular ratio of higher than 10 is used, it is difficult to heighten the crystallinity. If the acicular ratio thereof is lower than 3, the ferromagnetic metal particles yielded therefrom have a reduced coercive force and are unusable for a high-density recording medium.

Means for regulating the ferromagnetic metal particles for use in the present invention are not particularly limited. Examples thereof include the following methods (1) and (2).

(1) A specific elemental composition mainly for the inner part of the ferromagnetic metal particles is specified.

In particular, in the case of ferromagnetic metal particles mainly comprising Fe, specific minor elements which interact with Fe are used. Preferred examples of the minor elements include Ca, Co, Ni, and Cr. These minor elements are preferably added during the preparation of goethite or hematite and/or after the preparation thereof by means of a surface treatment.

(2) In the technique of producing ferromagnetic metal particles by the reduction of an oxide of a ferromagnetic metal element, conditions for pretreatments performed prior to the reduction, e.g., conditions for the dehydration or annealing of goethite, are selected and conditions for the reduction, e.g., temperature, reducing gas, and reduction time, are selected.

For example, conditions for each step of the treatment of goethite-containing minor elements and obtained according to (1) above are as follows.

Dehydration may be conducted with a rotary type electric furnace in a nitrogen atmosphere at generally 250.degree. to 400.degree. C., preferably 300.degree. to 400.degree. C., for generally 0.5 to 2 hours, preferably 0.5 to 1 hour. Annealing may be conducted with a stationary reducing furnace in a nitrogen atmosphere at generally 500.degree. to 800.degree. C., preferably 550.degree. to 700.degree. C., for generally 1 to 5 hours, preferably 2 to 3 hours. Between the dehydration and the annealing, a step of washing the resulting hematite with water to remove soluble alkali metals may be conducted.

Reduction may be conducted with a stationary reducing furnace in such a manner that the iron oxide is first reduced in a hydrogen atmosphere at generally 350.degree. to 500.degree. C., preferably 425.degree. to 480.degree. C., for generally 0.25 to 1 hour, preferably 0.25 to 0.5 hours, and then heated in a nitrogen atmosphere at generally 450.degree. to 650.degree. C., preferably 500.degree. to 600.degree. C., for generally 0.5 to 3 hours, preferably 1 to 2 hours, and further then reduced in a pure hydrogen atmosphere at that temperature for 3 to 5 hours.

The completion of the reduction is determined by measuring the moisture content of the discharged gas with a dew-point hygrometer.

For producing the ferromagnetic metal particles described above, known methods may be used such as the methods described in JP-A-7-109122 and JP-A-6-340426.

Although the ferromagnetic metal particles are not particularly limited in the ferromagnetic metal elements thereof, preferably, they comprise Fe, Ni, or Co as their main component (at least 75%). An especially preferred element is Co, because it serves to enhance as and can form a dense and thin oxide film. The content of Co atoms is preferably from 5 to 45 atomic %, more preferably from 10 to 40 atomic %, based on the amount of Fe atoms. It is preferred that part of the necessary amount of Co be incorporated into a starting material by doping and the remainder be adhered to the surface of the doped starting material, before the Co is converted to an alloy through reduction.

The ferromagnetic metal particles for use in the present invention preferably contain up to 20 wt. % atoms of elements besides atoms of the given metals. Examples of the optional elements include Al, Si, S, Ti, V, Cr, Cu, Y, Mo, Rh, Pd, Ag, Sn, Sb, Te, Ba, Sr, W, Au, Pb, Bi, La, Ce, Pr, Nd, P, Mn, Zn, Sr, B, and Ca. These elements not only contribute to regulation of the shape of the starting material, but also are effective in preventing sintering, accelerating reduction, and regulating the shape and surface roughness of the ferromagnetic metal particles produced through reduction.

The final reduction for completely reducing monodisperse goethite or monodisperse hematite into the metal is conducted with pure hydrogen. It is useful for heightening the crystallinity to conduct annealing in the course of the reduction at the stage of .alpha.-Fe.sub.2 O.sub.3. For the reduction of .alpha.-Fe.sub.2 O.sub.3 to Fe.sub.3 O.sub.4 and FeO, various reducing gases may be used in stead of pure hydrogen. Since the presence of water during reduction influences the occurrence of sintering, it is necessary for heightening the crystallinity that the water resulting from reduction should be rapidly removed from the system after the formation of metal nuclei from a metal oxide or during the subsequent formation of crystallites, or that the reduction should be regulated so as to yield a reduced amount of water. This regulation of water amount can be accomplished by controlling the partial pressure or amount of a reducing gas.

An oxide film is formed on the surface of the ferromagnetic metal particles may contain a small amount of a hydroxide or oxide. If the gas used for the gradual oxidation contains carbon dioxide, the carbon dioxide is adsorbed onto basic sites present on the surface of the ferromagnetic metal particles. The ferromagnetic metal particles which have undergone the gradual oxidation may contain such adsorbed carbon dioxide.

In the conventional processes for producing magnetic metal particles from goethite (.alpha.-FeOOH) or hematite (.alpha.-Fe.sub.2 O.sub.3) as a starting material, the particle contours attributable to the size and shape of the starting material are large. Specifically, the conventional ferromagnetic metal particles have an average long axis length of about 0.2 to 0.3 .mu.m. In those conventional processes, the particle contours contract simultaneously with reduction into the metal with elimination of oxygen to give polycrystalline sparse metal particles as shown in FIG. 2. In addition, the crystallites of each metal particle are not uniform in size and shape, and the number of crystallites per particle is from 4 to 10 or larger. In contrast, in the present invention, the size of the particle contours attributable to the size and shape of a starting material is reduced and the proportion of single-crystal particles in which, unlike the conventional polycrystalline state, each particle is constituted of one crystallite as shown in FIG. 1 is increased as much as possible in the ferromagnetic metal particles.

In the present invention, at least 30% of all ferromagnetic metal particles each is constituted of one crystallite, and the proportion of particles each having more than one crystallite is below 70%. It is generally desired that the proportion of particles each having two crystallites to all particles be 40 to 30%, that of particles each having three crystallites to all particles be 10 to 0%, and that of particles each having four or more crystallites be zero.

In the present invention, a photograph of ferromagnetic metal particles was taken with a high-resolution transmission electron microscope, and the acicular ratio of the crystallites was determined from the average long axis length of the ferromagnetic metal particles and from the lattice images of the ferromagnetic metal particles. About 200 particles were thus examined to determine the average long axis length of the ferromagnetic metal particles. The acicular ratio of the crystallites was determined by tracing the contour of each crystallite image in the high-resolution electron photomicrograph with an image analyzer to determine the long axis length and short axis length thereof and calculating the value of (long axis length)/(short axis length).

Furthermore, the fine ferromagnetic metal particles may be treated with, for example, a dispersant, a lubricant, a surfactant, or an antistatic agent described below, before the dispersion. These treatments are described in, for example, JP-B-44-14090, JP-B-45-18372, JP-B-47-22062, JP-B-47-22513, JP-B-46-28466, JP-B-46-38755, JP-B-47-4286, JP-B-47-12422, JP-B-47-17284, JP-B-47-18509, JP-B-47-18573, JP-B-39-10307, JP-B-48-39639, and U.S. Pat. Nos. 3,026,215, 3,031,341, 3,100,194, 3,242,005, and 3,389,014.

The water content of the ferromagnetic metal particles is preferably from 0.01 to 2% by weight, and is preferably optimized according to the kind of the binder, which will be described later.

The tap density of the ferromagnetic metal particles is preferably from 0.2 to 0.8 g/ml. Ferromagnetic metal particles having a tap density of higher than 0.8 g/ml are undesirable since such particles are not evenly oxidized in gradual oxidation, not only they are difficult to handle safely, but also the tape obtained using the same undergoes a decrease in magnetization with the lapse of time. Ferromagnetic metal particles having a tap density of lower than 0.2 g/ml tend to be poorly dispersed.

The binder resin for use in the magnetic layer in the magnetic medium of the present invention may be a conventionally known thermoplastic resin, thermosetting resin, or reactive resin, or a mixture thereof.

The thermoplastic resin may be one having a glass transition temperature of -100.degree. to 150.degree. C., a number-average molecular weight of 1,000 to 200,000, preferably 10,000 to 100,000, and a degree of polymerization of about 50 to 1,000.

Examples of the thermoplastic resin include polymers or copolymers containing a structural unit derived from vinyl chloride, vinyl acetate, vinyl alcohol, maleic acid, acrylic acid, acrylate, vinylidene chloride, acrylonitrile, methacrylic acid, methacrylate, styrene, butadiene, ethylene, vinyl butyral, vinyl acetal, or vinyl ether; polyurethane resins; and various rubber-type resins.

Examples of the thermosetting or reactive resin include phenolic resins, epoxy resins, thermosetting polyurethane resins, urea resins, melamine resins, alkyd resins, reactive acrylic resins, formaldehyde resins, silicone resins, epoxy-polyamide resins, mixtures of polyester resin and isocyanate prepolymer, mixtures of polyester polyol and polyisocyanate, and mixtures of polyurethane and polyisocyanate.

For obtaining further improved dispersibility of the ferromagnetic particles and durability of the magnetic layer, it is preferred to use, according to need, one or more of the above-enumerated binders which have incorporated therein through copolymerization or addition reaction, at least one polar group selected from --COOM, --SO.sub.3 M, --OSO.sub.3 M, --P.dbd.O(OM).sub.2, --O--P.dbd.O(OM).sub.2 (wherein M represents a hydrogen atom or an alkali metal salt group), --OH, --NR.sub.2, --N.sup.+ R.sub.3 (R represents a hydrocarbon group), an epoxy group, --SH, and --CN. The amount of the polar group(s) is generally from 10.sup.-1 to 10.sup.-8 mol/g, preferably from 10.sup.-2 to 10.sup.-6 mol/g.

The amount of the binder resin for use in the magnetic recording medium of the present invention is generally from 5 to 50% by weight, preferably from 10 to 30% by weight, based on the amount of the ferromagnetic metal particles. When the vinyl chloride resin, the polyurethane resin, and the polyurethane resin are preferably used in combination in an amount of 5 to 100% by weight, 2 to 50% by weight, and 2 to 100% by weight.

The filling degree of the ferromagnetic metal particles are calculated by the maximum saturation magnetization degree .sigma.s and Bm of the ferromagnetic metal particles used (Bm/4.pi..sigma.s). In the present invention, the amount thereof is preferably 1.7 g/ml or more, more preferably 1.9 g/ml or more, and most preferably 2.1 g/ml or more.

In using polyurethane in the present invention, the polyurethane preferably has a glass transition temperature of -50.degree. to 100.degree. C., an elongation at break of 100 to 2,000%, a stress at break of 0.05 to 10 kg/cm.sup.2, and a yield point of 0.05 to 10 kg/cm.sup.2.

Examples of the polyisocyanate for use in the present invention include isocyanates such as tolylene diisocyanate, 4,4'-diphenylmethane diisocyanate, hexamethylene diisocyanate, xylylene diisocyanate, naphthylene 1,5-diisocyanate, o-toluidine diisocyanate, isophorone diisocyanate, and triphenylmethane triisocyanate, products of the reactions of these isocyanates with polyalcohols, and polyisocyanates formed through condensation of isocyanates. These isocyanates are commercially available under the trade names of: Coronate L, Coronate HL, Coronate 2030, Coronate 2031, Millionate MR, and Millionate MTL (manufactured by Nippon Polyurethane Co., Ltd.); Takenate D-102, Takenate D-110N, Takenate D-200, and Takenate D-202 (manufactured by Takeda Chemical Industries, Ltd.); and Desmodule L, Desmodule Ill, Desmodule N, and Desmodule HL (manufactured by Sumitomo Bayer Co., Ltd.). For each of the layers, these polyisocyanates may be used alone, or used in combination of two or more thereof, taking advantage of a difference in curing reactivity.

The magnetic layer of the present invention may contain additives which have various functions, such as lubricants, abrasives, dispersants, antistatic agents, plasticizers, and antimolds, if necessary.

Examples of lubricants for use in the magnetic layer of the present invention include silicone oils such as dialkylpolysiloxanes (each alkyl has from 1 to 5 carbon atoms), dialkoxypolysiloxanes (each alkoxy has from 1 to 4 carbon atoms), monoalkylmonoalkoxypolysiloxanes (the alkyl and the alkoxy have from 1 to 5 and from 1 to 4 carbon atoms, respectively), phenylpolysiloxane, and fluoroalkylpolysiloxanes (the alkyl has from 1 to 5 carbon atoms); electrically conductive fine particles, e.g., graphite particles; inorganic powders, e.g., molybdenum disulfide and tungsten disulfide; fine particles of plastics, e.g., polyethylene, polypropylene, polyethylene-vinyl chloride copolymers, and polytetrafluoroethylene; .alpha.-olefin polymers; saturated fatty acids which are solid at ordinary temperature (having from 10 to 22 carbon atoms); unsaturated aliphatic hydrocarbons which are liquid at ordinary temperature (compounds having an n-olefin double bond bonded to a terminal carbon atom, and having about 20 carbon atoms); fatty acid esters formed from monobasic fatty acids having from 12 to 20 carbon atoms and monohydric alcohols having from 3 to 12 carbon atoms; and fluorocarbons.

Of the above-enumerated lubricants, the saturated fatty acids and the fatty acid esters are preferred, with a combination of both being preferred. Examples of alcohols usable as starting materials for the fatty acid esters include monohydric alcohols such as ethanol, butanol, phenol, benzyl alcohol, 2-methylbutyl alcohol, 2-hexyldecyl alcohol, propylene glycol monobutyl ether, ethylene glycol monobutyl ether, dipropylene glycol monobutyl ether, diethylene glycol monobutyl ether, and s-butyl alcohol; and polyhydric alcohols such as ethylene glycol, diethylene glycol, neopentyl glycol, glycerol, and sorbitan derivatives. Examples of fatty acids usable as starting materials for the fatty acid esters include aliphatic carboxylic acids such as acetic acid, propionic acid, octanoic acid, 2-ethylhexanoic acid, lauric acid, myristic acid, stearic acid, palmitic acid, behenic acid, arachic acid, oleic acid, linoleic acid, linolenic acid, elaidic acid, and palmitoleic acid, and mixtures of these acids.

Specific examples of the fatty acid esters include butyl stearate, s-butyl stearate, isopropyl stearate, butyl oleate, amyl stearate, 3-methylbutyl stearate, 2-ethylhexyl stearate, 2-hexyldecyl stearate, butyl palmitate, 2-ethylhexyl myristate, butyl stearate/butyl palmitate mixtures, butoxyethyl stearate, 2-butoxy-1-propyl stearate, dipropylene glycol monobutyl ether stearate, diethylene glycol dipalmitate, hexamethylenediol dimyristate, and glycerol oleate.

In order to diminish the hydrolysis of a fatty acid ester which often occurs during use of the magnetic recording medium in a high-humidity atmosphere, a technique is used in which branched/linear isomers, cis/trans isomers, other isomers, and branching sites are taken in account when selecting a fatty acid and an alcohol used as starting materials for the ester.

These lubricants may be added in an amount of 0.2 to 20 parts by weight per 100 parts by weight of the binder.

Other usable lubricants include silicone oils, graphite, molybdenum disulfide, boron nitride, fluorinated graphite, fluorinated alcohols, polyolefins, polyglycols, alkyl phosphates, and tungsten disulfide.

Examples of abrasives for use in the magnetic layer of the present invention include generally employed abrasive materials such as .alpha.-alumina, .gamma.-alumina, fused alumina, corundum, artificial corundum, silicon carbide, chromium oxide (Cr.sub.2 O.sub.3), diamond, artificial diamond, garnet, emery (main components; corundum and magnetite), and .alpha.-Fe.sub.2 O.sub.3. These abrasive materials have a Mohs' hardness of 6 or more. Specific examples thereof include AKP-10, AKP-12, AKP-15, AKP-20, AKP-30, AKP-50, AKP-1520, AKP-1500, HIT-50, HIT60A, HIT70, HIT80, and HIT-100 (manufactured by Sumitomo Chemical Co., Ltd.); G5, G7, S-1, and Chromium Oxide K (manufactured by Nippon Chemical Industrial Co., Ltd.); UB40B (manufactured by Uemura Kogyo K.K.); WA8000 and WA10000 (manufactured by Fujimi Kenmazai Kogyo Co., Ltd.); and TF100, TF140, and TF180 (manufactured by Toda Kogyo Co., Ltd.). Effective are abrasives having an average particle diameter of generally 0.05 to 3 .mu.m, preferably from 0.05 to 1.0 .mu.m.

The total addition amount of these abrasives is generally from 1 to 20 parts by weight, preferably from 1 to 15 parts by weight, per 100 parts by weight of the magnetic particle. If the amount of abrasives is smaller than 1 part by weight, sufficient durability cannot be obtained. If the amount thereof is larger than 20 parts by weight, surface properties and filling degree are impaired. These abrasives may be dispersed into a binder, before being added to a magnetic coating composition.

Electrically conductive particles may be incorporated as an antistatic agent, besides the nonmagnetic particles described above, into the magnetic layer of the magnetic recording medium of the present invention. However, from the standpoint of forming an uppermost layer having a saturation flux density heightened to the highest level, it is preferred to incorporate most of the electrically conductive particles into a layer other than the uppermost layer to minimize the amount thereof incorporated in the uppermost layer. Carbon black is especially preferably incorporated as an antistatic agent from the standpoint of reducing the surface electrical resistance of the whole medium. Examples of the carbon black for use in the present invention include furnace black for rubbers, thermal black for rubbers, coloring black, conductive carbon blacks, and acetylene black. The carbon black preferably has a specific surface area of 5 to 500 m.sup.2 /g, a DBP absorption amount of 10 to 1,500 ml/100 g, a particle diameter of 5 to 300 m.mu., a pH of 2 to 10, a water content of 0.1 to 10%, and a tap density of 0.1 to 1 g/ml. Specific examples of the carbon black include BLACKPEARLS 2000, 1300, 1000, 900, 800, 700, and VULCAN XC-72 (manufactured by Cabot Co., Ltd.); #80, #60, #55, #50, and #35 (manufactured by Asahi Carbon Co., Ltd.); #3950B, #3250B, #2700, #2650, #2600, #2400B, #2300, #900, #1000, #95, #30, #40, #10B, MA230, MA220, and MA77 (manufactured by Mitsubishi Chemical Corp.); CONDUCTEX SC, RAVEN 150, 50, 40, and 15 (manufactured by Columbian Carbon Co.); and Ketjen Black EC, Ketjen Black ECDJ-500, and Ketjen Black ECDJ-600 (manufactured by Lion Akzo Co., Ltd.). These carbon blacks may be surface-treated with a dispersant or other agent, oxidized, or grafted with a resin before use. The carbon black whose surface has been partly graphitized may also be used. Furthermore, before being added to a magnetic coating composition, the carbon black may be dispersed into a binder. In using the carbon black in the magnetic layer, the amount thereof is preferably from 0.1 to 30% by weight based on the amount of the magnetic particle. In forming a nonmagnetic layer, the carbon black is preferably incorporated therein in an amount of 3 to 20% by weight based on the amount of the inorganic nonmagnetic particles.

In general, the carbon black functions as an antistatic agent, and further serves to reduce the coefficient of friction, to impart a light screen, and to improve film strength. These effects are produced to different degrees depending on the kind of carbon black used. Therefore, it is, of course, possible in the present invention to change the kind, amount, and combination of carbon blacks according to purposes on the basis of the above-described properties including particle size, oil absorption amount, electrical conductivity, and pH. With respect to carbon blacks usable in the present invention, reference may be made to, for example, Carbon Black Binran (Carbon Black Handbook), edited by Carbon Black Association.

In forming a nonmagnetic layer between the magnetic layer and the nonmagnetic support in the magnetic recording medium of the present invention, the nonmagnetic layer (hereinafter often referred to also as a "lower layer") is a layer consisting mainly of inorganic nonmagnetic particles dispersed in a binder resin. Various materials can be used as the inorganic nonmagnetic particles for the nonmagnetic layer. Examples thereof include .alpha.-alumina having an alpha-conversion of 90% or more, .beta.-alumina, .gamma.-alumina, silicon carbide, chromium oxide, cerium oxide, .alpha.-iron oxide, corundum, silicon nitride, titanium carbide, titanium oxide, silicon dioxide, boron nitride, zinc oxide, calcium carbonate, calcium sulfate, and barium sulfate. These may be used alone or in combination. These inorganic nonmagnetic particles preferably have a particle size of 0.01 to 2 .mu.m. If needed, inorganic nonmagnetic particles having different particle sizes may be used in combination, or a single inorganic nonmagnetic particles having a widened particle diameter distribution may be used so as to produce the same effect. The inorganic nonmagnetic particles to be used may have been surface-treated so as to enhance interaction with the binder resin used to thereby improve dispersibility. The surface treatment may be performed with either an inorganic substance, e.g., silica, alumina, or silica-alumina, or a coupling agent. The inorganic nonmagnetic particles preferably have a tap density of 0.3 to 2 g/ml, a water content of 0.1 to 5% by weight, a pH of 2 to 11, and a specific surface area of 5 to 100 m.sup.2 /g. The inorganic nonmagnetic particles may have any particle shape selected from the acicular, spherical, cubical, and tabular forms. Specific examples of the inorganic nonmagnetic particles for use in the present invention include AKP-20, AKP-30, AKP-50, and HIT-50 (manufactured by Sumitomo Chemical Co., Ltd.); G5, G7, and S-1 (manufactured by Nippon Chemical industrial Co., Ltd.); TF-100, TF-120, and TF-140 (manufactured by Toda Kogyo Co., Ltd.); TTO 55 Series and ET300W (manufactured by Ishihara Sangyo Kaisha, Ltd.); STT30 (manufactured by Titan Kogyo CO., LTD.); and acicular hematite particles used as an intermediate for a magnetic iron oxide or an intermediate for producing ferromagnetic metal particles by the iron oxide reduction method.

The layer constitution of the magnetic recording medium of the present invention is not particularly limited, as long as the medium basically comprises at least a nonmagnetic support and the above-described magnetic layer formed thereover or further has the nonmagnetic layer described above. A magnetic or nonmagnetic layer having another composition may be formed. For example, in the case of forming a ferromagnetic layer in place of the above-described nonmagnetic layer, various ferromagnetic particles can be used therefor, such as, e.g., a ferromagnetic iron oxide, a cobalt-modified ferromagnetic iron oxide, CrO.sub.2, a hexagonal ferrite, and other ferromagnetic metals. These ferromagnetic materials are dispersed in a resin to form the ferromagnetic layer. This ferromagnetic layer is also referred to as a lower layer.

Forming two or more coating layers on a nonmagnetic support is effective in producing a magnetic recording medium for high-density recording. A simultaneous coating technique is especially superior since an ultrathin magnetic layer can be formed. Specific examples of wet-on-wet coating as the simultaneous coating techniques include the following methods.

1. A lower layer is first applied with a coating apparatus commonly used for magnetic coating composition, e.g., a gravure coating, roll coating, blade coating, or extrusion coating apparatus, and an upper layer is then applied, while the lower layer is in a wet state, by means of a support-pressing extrusion coater such as those disclosed in JP-B-1-46186, JP-A-60-238179, and JP-A-2-265672.

2. An upper layer and a lower layer are applied almost simultaneously using a single coating head having therein two slits for passing coating compositions, such as those disclosed in JP-A-63-88080, JP-A-2-17971, and JP-A-2-265672.

3. An upper layer and a lower layer are applied almost simultaneously with an extrusion coater equipped with a back-up roll, such as that disclosed in JP-A-2-174965.

In wet-on-wet coating, it is preferred that the flow characteristics of the coating composition for magnetic-layer formation be akin as much as possible to those of the coating composition for nonmagnetic-layer formation, because the interface between the magnetic and nonmagnetic coating layers formed therefrom has no disturbance and, as a result, the magnetic layer obtained can have uniformity in thickness with diminished thickness fluctuations. Since the flow characteristics of a coating composition largely depend on the combination of the particles and the binder resin contained in the coating composition, special care should be taken in selecting nonmagnetic particles for use in the nonmagnetic layer.

The nonmagnetic support used in the magnetic recording medium of the present invention has a thickness of generally 1 to 100 .mu.m, and preferably 3 to 20 .mu.m (as a tape) or 40 to 80 .mu.m (as a flexible disk). The nonmagnetic layer has a thickness of generally 0.5 to 10 .mu.m, and preferably 0.5 to 3 .mu.m. When a magnetic layer is formed on a nonmagnetic layer, the thickness of the magnetic layer is generally 0.05 to 3.0 .mu.m, and preferably 0.05 to 1.0 .mu.m.

Layers other than the magnetic and nonmagnetic layers described above can be formed according to purposes. For example, an undercoat layer may be formed between the nonmagnetic support and the lower layer in order to improve adhesion. This undercoat layer has a thickness of generally 0.01 to 2 .mu.m, and preferably 0.05 to 0.5 .mu.m. A back coat layer may be formed on the surface of the nonmagnetic support opposite to the magnetic layer. This back coat layer has a thickness of generally 0.1 to 2 .mu.m, and preferably 0.3 to 1.0 .mu.m. These undercoat and back coat layers may be known layers. In a disk-form magnetic recording medium, the above-described layers may be formed on one or both sides.

The nonmagnetic support for use in the present invention is not particularly limited, and ordinarily employed nonmagnetic supports may be used in the present invention. Examples of materials used for constituting nonmagnetic supports include films of various synthetic resins such as poly(ethylene terephthalate), polyethylene, polypropylene, polycarbonates, poly(ethylene naphthalate), polyamides, poly(amide-imide)s, polyimides, polysulfones, and polyethersulfones and metal foils such as aluminum foil and stainless-steel foil.

In order to attain the objects of the present invention, it is preferred to use a nonmagnetic support having a center line average surface roughness (Ra: cutoff value: 0.25 mm) of 0.03 .mu.m or less, more preferably 0.02 .mu.m or less, and particularly preferably 0.01 .mu.m or less. In addition that the nonmagnetic recording medium of the present invention has a small center line average surface roughness, the nonmagnetic support is preferably free from projections as large as 1 .mu.m or more. The state of the surface roughness of the support can be freely controlled by changing the size and amount of a filler which is incorporated into the support if needed. Examples of the filler include oxides or carbonates of Ca, Si, and Ti and fine organic powders such as acrylic powder. The nonmagnetic support for use in the present invention preferably has an F-5 value in the web running direction of 5 to 50 kg/mm.sup.2 and an F-5 value in the web width direction of 3 to 30 kg/mm.sup.2. Although the F-5 value in the web longitudinal direction is generally higher than that in the web width direction, this does not apply in the case where the width direction strength, in particular, should be enhanced.

The degrees of thermal shrinkage of the support in the web running direction and in the web width direction are preferably 3% or less, more preferably 1.5% or less, under conditions at 100.degree. C. for 30 minutes, and are preferably 1% or less, more preferably 0.5% or less, under conditions at 80.degree. C. for 30 minutes. The strength at break thereof is preferably from 5 to 100 kg/mm.sup.2, and the modules thereof is preferably from 100 to 2,000 kg/mm.sup.2.

Examples of organic solvents for use in the present invention include ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone, diisobutyl ketone, cyclohexanone, isophorone, and tetrahydrofuran; alcohols such as methanol, ethanol, propanol, butanol, isobutyl alcohol, isopropyl alcohol, and methylcyclohexanol; esters such as methyl acetate, butyl acetate, isobutyl acetate, isopropyl acetate, ethyl lactate, and glycol acetate; glycol ethers such as glycol dimethyl ethers, glycol monoethyl ethers, and dioxane; aromatic hydrocarbons such as benzene, toluene, xylene, cresol, and chlorobenzene; chlorinated hydrocarbons such as methylene chloride, ethylene chloride, carbon tetrachloride, chloroform, ethylene chlorohydrin, and dichlorobenzene; and other compounds such as N,N-dimethylformamide and hexane. These solvents may be used in arbitrary proportions. These organic solvents need not be 100% pure, and may contain impurities, such as isomers, unreacted raw materials, by-products, decomposition products, oxidation products, and water, besides the main components. The content of these impurities is preferably 30% or less, more preferably 10% or less. In the present invention, the organic solvents used in the magnetic layer and the nonmagnetic layer may be different in kind and amount, if needed. For example, it is possible to use a highly volatile solvent for forming a nonmagnetic layer having improved surface properties, to use a solvent with a high surface tension (e.g., cyclohexane or dioxane) for improving the stability of the coating for forming a nonmagnetic layer, or to use a solvent with a high solubility parameter for forming a magnetic layer for increasing filling degree. However, methods of using organic solvents are, of course, not limited to these examples.

The magnetic recording medium of the present invention is obtained by a process comprising kneading the above-described ferromagnetic metal particles and binder resin together with an organic solvent if necessary further with other optional additives, applying the resulting magnetic coating composition on a nonmagnetic support, and drying the coating composition. Prior to the drying step, orientation may be conducted if needed.

The process for preparing a magnetic coating composition to be used for producing the magnetic recording medium of the present invention comprises at least a kneading step and a dispersing step, and may further comprise a mixing step that may be conducted, if necessary, before and after the two steps. Each step may include two or more stages. Each of the materials for use in the present invention, including the ferromagnetic metal particles, binder, carbon black, abrasive material, antistatic agent, lubricant, and solvent, may be added in any step either at the beginning of or during the step. Furthermore, each ingredient may be added portion-wise in two or more steps. For example, a polyurethane may be added portion-wise in each of the kneading step, the dispersing step, and the mixing step for viscosity adjustment after the dispersion.

For kneading and dispersion for preparing a magnetic coating composition, any of various kneading machines may be used. Examples thereof include a two-roll mill, three-roll mill, ball mill, pebble mill, tron mill, sand grinder, Szegvari, attritor, high-speed impeller dispersing machine, high-speed stone mill, high-speed impact mill, disper, kneader, high-speed mixer, homogenizer, and ultrasonic dispersing machine.

Conventionally known manufacturing techniques can, of course, be used as part of the process to attain the object of the present invention. It is, however, preferred to use a kneading machine having high kneading power, such as a continuous kneader or pressure kneader, in the kneading step. In the case of using a continuous kneader or pressure kneader, the ferromagnetic metal particles are kneaded together with all or part (preferably at least 30%) of the binder, the binder amount being in the range of 15 to 500 parts by weight per 100 parts by weight of the ferromagnetic metal particles. Details of this kneading treatment are described in JP-A-1-106338 and JP-A-64-79274. The magnetic recording medium of the present invention can be efficiently produced by employing a technique of simultaneous multiple coating as disclosed in JP-A-62-212933.

The residual solvent content in the magnetic layer in the magnetic recording medium of the present invention is preferably 100 mg/m.sup.2 or less, more preferably 10 mg/m.sup.2 or less. It is preferred that the residual solvent content in the magnetic layer be lower than that in the nonmagnetic layer.

The void content in the lower layer and that in the upper layer are each preferably 30% by volume or less, and more preferably 10% by volume or less. The nonmagnetic layer preferably has a higher void content than the magnetic layer, but may have a lower void content as long as its void content is 5% by volume or more.

The magnetic recording medium of the present invention, which may have a lower layer and an upper layer, can be made to have a difference in physical property between the upper and lower layers according to purposes, as can be easily presumed. For example, the upper layer is made to have a heightened modulus to improve running durability and, at the same time, the lower layer is made to have a lower modulus than the magnetic layer to improve the head touching of the magnetic recording medium.

The magnetic coating layer thus formed on a support is subjected, if necessary, to an orientation treatment for orienting the ferromagnetic metal particles contained in the layer, and then dried. A surface-smoothing treatment may be performed if needed, and the resulting structure is cut into a desired shape. Thus, the magnetic recording medium of the present invention is produced. The above-described composition for upper-layer formation and the optional composition for lower-layer formation each is dispersed along with a solvent. The coating compositions thus obtained are applied to a nonmagnetic support, and orientation and drying are conducted to obtain a magnetic recording medium.

The magnetic layer preferably has a modulus at 0.5% elongation of 100 to 2,000 kg/mm.sup.2 in each of the machine and transverse directions and a strength at break of 1 to 30 kg/cm.sup.2. The magnetic recording medium preferably has a modulus of 100 to 1,500 kg/mm.sup.2 in each of the machine and transverse directions and a residual elongation of 0.5% or less. The degree of thermal shrinkage of the magnetic recording medium at any temperature of not higher than 100.degree. C. is preferably 1% or less, more preferably 0.5% or less, and most preferably 0.1% or less.

The magnetic recording medium of the present invention may be a tape for video, audio, or another use, or may be a floppy disk or magnetic disk for data recording. The recording medium of this invention is particularly effective when used as a digital recording medium in which the occurrence of signal dropouts should be avoided by all means. By employing a constitution in which the lower layer is a nonmagnetic layer and the uppermost layer has a thickness of 1 .mu.m or less, a large-capacity magnetic recording medium can be obtained which has high electro-magnetic characteristics and excellent overwriting characteristics and is suitable for high-density recording.

EXAMPLE

The present invention will be explained in detail by reference to the following Examples and Comparative Examples, but the invention should not be construed as being limited thereto. All percents, parts, ratios and the like are by weight unless otherwise indicated.

PRODUCTION EXAMPLE 1

Production Examples 1-1 to 1-4

(Production of Ferromagnetic Metal Particles)

To a mixture of 35 liters of 1.7 mol/l sodium carbonate and 15 liters of 2.0 mol/l sodium hydroxide placed in a 150-liter tank equipped with a stirrer was added 0.6 liters of 0.5 mol/l aqueous sodium phosphate solution. While nitrogen was continuously bubbled thereinto at a liquid temperature of 20.degree. C., 40 liters of an aqueous solution of ferrous sulfate and cobalt sulfate (Fe.sup.2+ concentration, 1.35 mol/l; Co concentration, 0.15 mol/l) having a temperature of 20.degree. C. which was prepared in another tank with nitrogen bubbling was added thereto. After the resulting mixture was stirred for 10 minutes, the temperature of the suspension was adjusted to 25.degree. C. to form a precipitate containing ferrous iron as the main component. Air was introduced in place of nitrogen to oxidize the precipitate to thereby yield nuclear goethite crystals. At the time when the Fe.sup.2 + concentration of the suspension reached 0.75 mol/l, the oxidation with air was stopped. Nitrogen was introduced in place of air, and the suspension was heated to 40.degree. C. and maintained at this temperature for 2 hours, following which 1.5 liters of 1.1 mol/l aqueous sodium aluminate solution was added. Thereafter, air was introduced in place of nitrogen to further conduct an oxidation reaction to thereby yield spindle-shaped particles of a solid solution of Al in goethite. The particles obtained were taken out by filtration and washed with water. Part of the particles were dried and photographed with a transmission electron microscope to determine the average particle diameter thereof. As a result, the particles were found to have an average long axis length of 0.10 .mu.m and an average acicular ratio of 7. Further, the specific surface area of the particles was measured after dehydration by 30-minute heating at 120.degree. C. in nitrogen, and was found to be 110 m.sup.2 /g.

The goethite obtained was dispersed into water to give a 2% slurry. An aqueous solution of cobalt sulfate and/or an aqueous solution of magnesium chloride was added to the slurry with stirring so as to result in the Co and/or Mg addition amount (amount of the atoms (%) based on the iron atom amount) shown in Table 1. This slurry was neutralized with ammonia water to deposit a cobalt compound and/or a magnesium compound on the surface of the particles. The slurry was filtered, and the particles taken out were dispersed into water to give a 2% slurry again. Aqueous sodium aluminate solution was added thereto (the Al atom (%) based on the iron atom amount is shown in Table 1), and the resulting mixture was stirred for 20 minutes. Thereafter, dilute sulfuric acid was added to neutralize the slurry. The particles were taken out by filtration, washed with water, and dispersed into water to give a 2% slurry. Aqueous yttrium nitrate solution was added (the Y atom (%) based on the iron atom amount is shown in Table 1), and the pH of the slurry was adjusted to 8.5 with ammonia water. The particles were taken out by filtration, washed with water, and dispersed into water to give a 5% slurry, which was then heated at 150.degree. C. for 1 hour. Thereafter, the particles were taken out by filtration and washed with water. The resulting cake was compacted with a compactor and then dried to obtain spindle-shaped goethite particles which had undergone a sintering prevention treatment.

The spindle-shaped goethite obtained was placed in a stationary reducing furnace, and heated in nitrogen at 350.degree. C. for 30 minutes for dehydration and then at 650.degree. C. for 2 hours to enhance the crystalline property of the hematite. The temperature was lowered to 400.degree. C., and a hydrogen/CO=20/80 mixed gas was introduced in place of nitrogen to conduct reduction for 1 hour. Thereafter, nitrogen was introduced in place of the mixed gas, and pure hydrogen was then introduced in place of nitrogen to conduct reduction for 5 hours. Nitrogen was introduced in place of pure hydrogen to cool the contents to room temperature, and an air/nitrogen mixture regulated to have an oxygen concentration of 0.2% was introduced to conduct gradual oxidation at 50.degree. C. or lower while monitoring the temperature of the metal powder. After heat generation ended, the oxygen concentration was adjusted to 1% to continue gradual oxidation for 10 hours. Thereafter, a vapor of distilled water was introduced together with air in such an amount as to result in a water amount of 1% based on the amount of the metal particle to humidify and stabilize the particle.

Magnetic characteristics of the thus-obtained ferromagnetic metal particles were determined with a vibrating sample magnetometer (manufactured by Toei Kogyo K.K., Japan) at an external magnetic field of 10 kOe. Each ferromagnetic metal particles obtained was photographed with a high-resolution transmission electron microscope to determine the average long axis length, average acicular ratio, and crystallinity of the ferromagnetic metal particles and the average acicular ratio of the crystallites. Further, the specific surface area (S.sub.BET) of each powder was measured with Quantasorb (manufactured by Quantachrome Inc.) after 30-minute dehydration at 250.degree. C. in nitrogen. The results obtained are shown in Table 1.

PRODUCTION EXAMPLE 2

Production Examples 2-1 to 2-3

Using the elements shown in Table 1, spindle-shaped goethite particles which had undergone a sintering prevention treatment were obtained through the same steps as in Production Example 1. The goethite particles were placed in a stationary reducing furnace, and dehydrated at 350.degree. C. for 60 minutes in nitrogen. The temperature was elevated to 450.degree. C., and pure hydrogen was introduced in place of nitrogen to conduct reduction for 6 hours. The subsequent treatments were carried out in the same manner as in Production Example 1. The ferromagnetic metal particles thus obtained were evaluated in the same manner as in Production Example 1. The results obtained are shown in Table 1.

PRODUCTION EXAMPLE 3

Production Examples 3-1 and 3-2

Goethite was produced in the same manner as in Production Example 1, except the following. After nuclear goethite crystals were formed at 25.degree. C. and at the time when the Fe.sup.2+ concentration of the suspension reached 0.75 mol/l, oxidation with air was stopped and nitrogen was introduced in place of air. Sodium aluminate was added, and the suspension was heated to 50.degree. C. to conduct oxidation with air. The goethite thus yielded had an average long axis length of 0.20 .mu.m, an average acicular ratio of 14, and a specific surface area of 130 m.sup.2 /g. Subsequently, the goethite was treated using the elements shown in Table 2 in the same manner as in Production Example 1, and then treated with the antisintering agents. This goethite was taken out by filtration, washed with water, compacted with a compactor, and then dried. Thereafter, the material obtained was reduced and subjected to gradual oxidation in the same manner as in Production Example 1. The ferromagnetic metal particles thus obtained were evaluated in the same manner as in Production Example 1. The results obtained are shown in Table 1.

TABLE 1__________________________________________________________________________ Ferromagnetic Metal Particle Element Antisinter- Average Average AverageProduction added ing Agent H.sub.c .sigma..sub.s S.sub.BET Long Axis Acicular Acicular RatioExample Mg Co Al Y (Oe) emu/g m.sup.2 /g Length Ratio Crystallinity of Crystallites__________________________________________________________________________1-1 0.5 0.0 8.0 6.0 1900 136.0 55.0 70 4.5 37 3.01-2 0.5 10 8.0 7.0 2120 140.5 53.5 68 4.0 45 2.81-3 1.0 20 5.0 8.0 2340 148.5 47.7 63 4.0 50 2.91-4 0.0 15 5.0 8.0 2210 143.4 53.7 64 4.3 42 2.72-1 0.5 0.0 8.0 6.0 1630 132.3 57.8 75 6.8 22 3.42-2 0.5 10 8.0 7.0 1800 135.5 56.3 73 6.5 26 3.22-3 1.0 20 5.0 8.0 2015 137.5 51.7 68 5.4 24 3.03-1 0.5 0.0 8.0 6.0 1750 134.3 57.0 125 7.7 20 3.63-2 1.0 20 8.0 7.0 1980 138.5 55.4 110 7.5 24 3.5__________________________________________________________________________

EXAMPLE 1

Production of Magnetic Recording Media

Examples 1-1 to 1-4 and Comparative Examples 1-1 to 1-5

The composition for magnetic-layer formation and the composition for nonmagnetic-layer formation both shown below were prepared in order to produce multilayered magnetic tapes respectively using the ferromagnetic metal particles obtained in Production Examples 1-1 to 1-5, 2-1 to 2-3, and 3-1 and 3-2. In the following formulations, all "parts" are by weight.

______________________________________(Composition for Magnetic-Layer Formation)Ferromagnetic metal particle 100 parts(shown in Table 2)Binder resinVinyl chloride copolymer 13 parts(--SO.sub.3 Na group content, 1 .times. 10.sup.-4 eq/g;degree of polymerization, 300)Polyester polyurethane resin 5 parts(neopentyl glycol/caprolactonepolyol/MDI =0.9/2.6/1 (by mol)--SO.sub.3 Na group content, 1 .times. 10.sup.-4 eq/g).alpha.-Alumina 5.0 parts(average particle diameter, 0.13 .mu.m)Carbon black 1.0 part(average particle diameter, 40 nm)Butyl stearate 1 partStearic acid 2 partsMethyl ethyl ketone/cyclohexanone 200 parts(1:1) mixed solvent(Composition for Nonmagnetic-Layer Formation)Acicular hematite 80 parts(BET specific surface area, 55 m.sup.2 /g;average long axis length, 0.12 .mu.m;acicular ratio, 8; pH, 8.8; aluminumtreatment: Al atom amount, 6.5 atom %based on Fe atoms)Carbon black 20 parts(average primary particle diameter, 17 nm;DBP absorption amount, 80 ml/100 g;BET specific surface area, 240 m.sup.2 /g;pH, 7.5)Binder resinVinyl chloride copolymer 12 parts(--SO.sub.3 Na group content, 1 .times. 10.sup.-4 eq/g;degree of polymerization, 300)Polyester polyurethane resin 5 parts(neopentyl glycol/caprolactonepolyol/MDI =0.9/2.6/1 (by mol);--SO.sub.3 Na group content, 1 .times. 10.sup.- 4 eq/g)Butyl stearate 1 partStearic acid 2.5 partsMethyl ethyl ketone/cyclohexanone 200 parts(1:1) mixed solvent______________________________________

With respect to each of the composition for magnetic-layer formation and the composition for nonmagnetic-layer formation, the ingredients were kneaded with a kneader and then dispersed with a sand grinder. To the resulting dispersions was added a polyisocyanate in an amount of 5 parts for the coating composition for nonmagnetic-layer formation and in an amount of 6 parts for the coating composition for magnetic-layer formation. To each dispersion was further added 20 parts of a methyl ethyl ketone/cyclo-hexanone (1:1) mixed solvent. These dispersions were filtered through a filter having an average opening diameter of 1 .mu.m to prepare a coating composition for nonmagnetic-layer formation and a coating composition for magnetic-layer formation.

The two coating composition obtained were applied on a 7 .mu.m-thick poly(ethylene terephthalate) support by wet-on-wet simultaneous multi-layered coating as follows. The coating composition for nonmagnetic-layer formation was applied first at a dry thickness of 1.5 .mu.m, and the coating composition for magnetic-layer formation was applied immediately thereafter on the still wet nonmagnetic layer coating in such an amount as to obtain a 0.15 .mu.m-thick magnetic layer. While the two coating layers were still in a wet state, longitudinal orientation was performed by passing the coated support through an orientation apparatus. In this orientation, the coated support was passed by a rare earth magnet (surface flux density, 5,000 G) and then passed through a solenoid magnet (flux density, 5,000 G), and was dried within the solenoid to such a degree that the oriented state was maintained. The magnetic layer was further dried, before the coated support was wound up. Thereafter, calendering was conducted with a 7-roll calender comprising metal rolls at a roll temperature of 90.degree. C. to obtain a magnetic recording medium as a web. The web was slit into an 8-mm width. Thus, 8-mm video tape samples were produced. The samples were examined for magnetic characteristics with a vibrating sample magnetometer and for surface roughness. The samples were further examined with a drum tester for 1/2 Tb output, C/N, and overwriting characteristics. The results obtained are shown in Table 2. As a standard for the examination of electromagnetic characteristics, Super DC Tape (manufactured by Fuji Photo Film Co., Ltd.) was used.

Overwriting characteristics were examined using a drum tester by the following method. At a relative speed of a TSS head (head gap, 0.2 .mu.m; track width, 14 .mu.m; saturation flux density, 1.1 T) of 10.2 m/sec, signals of 1/90 Tb (.lambda.=22.5 .mu.m) were recorded at the optimum recording current determined from the input/output characteristics of signals of 1/2 Tb (.lambda.=0.5 .mu.m), and signals of 1/2 Tb were then written thereover. From the degree of erasion of the recorded 1/90 Tb signals, the overwriting characteristics were determined.

Magnetic characteristics were determined in the direction parallel to the orientation direction with a vibrating sample magnetometer (manufactured by Toei Kogyo K.K.) at an intensity of external magnetic field of 5 kOe. SQ means squareness ratio. The content of high-H.sub.c components was determined as follows. A magnetic recording medium sample was set on the vibrating sample magnetometer (manufactured by Toei Kogyo K.K.), in such a manner that the orientation direction for the sample was the same as the direction of magnetic field. A magnetic field of -10 kOe was applied to bring the sample into DC saturation, and the magnetic field was then returned to zero to measure the residual magnetization (-M.sub.rmax). A magnetic field of 3,000 Oe was applied in the opposite direction, and the magnetic field was then returned to zero to measure the residual magnetization M.sub.r. Thereafter, a magnetic field of 10 kOe was applied to bring the sample into DC saturation in that opposite direction, and the magnetic field was then returned to zero to measure the residual magnetization M.sub.rmax. The content of high-H.sub.c components was calculated from the thus-obtained residual magnetization values using the following equation.

High-H.sub.c component (%)=100.times.(M.sub.rmax -M.sub.r)/(M.sub.rmax -(-M.sub.rmax))

Although the magnetic field applied in that opposite direction can have any desired intensity, an intensity of 3,000 Oe was employed herein (r3000) from the standpoint of detection sensitivity. The high-H.sub.c components are components which undergo reversal of magnetization at that magnetic field intensity or higher. Since r3000 necessarily increases with increasing value of average H.sub.c, it is necessary to standardize r3000 with H.sub.c for comparison among samples. The results obtained are shown in Table 3 in terms of (r3000/H.sub.c).times.100.

Each sample was further examined with a torque magnetometer (Type TRT-2, manufactured by Toei Kogyo K.K.) at various magnetic field intensities to determine the magnetic torque curve for the film plane. From the results obtained, the rotational hysteresis loss integral was calculated and is shown to utilize the same as a measure of the mode of reversal of magnetization.

Surface roughness was measured by examining a sample area 250 .mu.m square with light-interference three-dimensional roughness meter "TOPO-3D," manufactured by WYKO Inc. (Ariz., U.S.A.). In calculation from the found values, corrections such as slope correction, sphere correction, and cylinder correction were conducted according to JIS-B601. The center-line average roughness R.sub.a was taken as the value of surface roughness.

TABLE 2__________________________________________________________________________ Production Magnetic Characteristics Example for Rotational Surface Overwriting Ferromagnetic H.sub.c B.sub.m r3000/H.sub.c Hysteresis Roughness Output C/N Character- Metal Particle (Oe) SQ (G) SFD (%) Loss Integral (nm) (dB) (dB) istics__________________________________________________________________________Example 1-1 1-1 2010 0.82 3730 0.45 0.48 1.12 2.5 2.6 3.5 1.5Example 1-2 1-2 2230 0.83 4120 0.44 0.45 1.05 2.6 3.5 4.8 2.8Example 1-3 1-3 2470 0.82 4450 0.42 0.40 0.99 2.6 4.8 4.6 4.5Example 1-4 1-4 2320 0.80 4360 0.42 0.46 1.10 2.7 4.2 5.3 4.1Comparative 2-1 1740 0.78 3400 0.56 0.63 1.26 3.2 0.0 -0.5 1.5Example 1-1Comparative 2-2 1930 0.77 3620 0.57 0.75 1.25 3.1 0.8 0.2 5.7Example 1-2Comparative 2-3 2120 0.76 3760 0.58 0.71 1.28 3.2 1.0 0.0 6.9Example 1-3Comparative 3-1 1880 0.83 3740 0.54 0.75 1.40 3.5 0.2 -1.0 3.2Example 1-4Comparative 3-2 2300 0.81 3950 0.61 0.72 1.36 3.3 0.9 0.7 8.5Example 1-5__________________________________________________________________________

PRODUCTION EXAMPLE 4

Formation of Nuclear Crystals

Into a 2-liter sealable glass container was introduced 500 ml of 2M aqueous FeCl.sub.3 solution. To the solution was added, with stirring, 500 ml of 5.94N aqueous NaOH solution over a period of 5 minutes. After completion of the addition, the mixture was stirred for further 20 minutes, and the container was then sealed tightly.

The container was placed in an oven preheated at 100.degree. C. and kept therein for 72 hours. Thereafter, the container was quenched with running water. The reaction mixture was separated into portions and centrifuged with a centrifugal separator at 15,000 rpm for 15 minutes. The resulting supernatant was discarded. Distilled water was added to the residue to redisperse the same. The dispersion was centrifuged again and the resulting supernatant was discarded. This water washing operation using a centrifugal separator was conducted three times. The resulting precipitate of hematite particles (average particle diameter, about 80 nm) which had undergone the water washing was dried. To 50 g of the dry particle was added 5 ml of distilled water. This mixture was treated with a mortar for 30 minutes to pulverize the particles. The pulverized particles were washed out of the mortar and put into a beaker using 500 ml of distilled water. The mixture was separated into 100 ml portions, which were respectively placed into 200-ml mayonnaise bottles containing steel beads and treated for 10 hours to disperse the particles. The resulting dispersions were collected, and the mayonnaise bottles were washed with distilled water to recover the remaining dispersions. Distilled water was added to the collected dispersion to a total volume of 1,200 ml, and this diluted dispersion was treated with ultrasonic for 30 minutes to further disperse the particles.

The ultrasonic-treated dispersion was separated into portions and centrifuged at 10,000 rpm for 30 minutes. The resulting supernatant, which contained ultrafine hematite particles (average particle diameter, about 70 .ANG.) dispersed therein, was taken out as a solution of nuclear crystals. This solution had an iron concentration of 2,000 ppm.

Crystallite Size Control of Spindle-shaped Monodisperse Hematite

Into a reactor equipped with a stirrer was introduced 180 ml of 1 mol/l ferric nitrate. The solution was cooled to 5.degree. C. Thereto was added, with stirring, 180 ml of 2.4 mol/l sodium hydroxide solution over a period of 5 minutes. After the addition, stirring was continued for further 5 minutes. Subsequently, 180 ml of the solution of nuclear crystals was added, and the contents were stirred for 10 minutes. To each of 60 ml portions taken from the resulting mixture were added 10 ml of 0.048 mol/l NaH.sub.2 PO.sub.4 as shape control ions and 10 ml of H.sub.2 O. The containers were sealed and kept for 72 hours in an oven preheated at 120.degree. C. Thereafter, the containers were quenched with running water. The reaction mixture was centrifuged with a centrifugal separator at 18,000 rpm for 15 minutes, and the resulting supernatant was discarded. Distilled water was added to the residue to redisperse the same. The dispersion was centrifuged again and the resulting supernatant was discarded. This water washing operation using a centrifugal separator was conducted three times. Subsequently, 1M ammonia water was added to the residue to redisperse the same. This dispersion was centrifuged and the resulting supernatant was discarded. Distilled water was added to the residue to redisperse the same. The dispersion was centrifuged again and the resulting supernatant was discarded. This water washing operation using a centrifugal separator was conducted three times. Part of the reaction product was taken out and dried. The dry particles were examined with a transmission electron microscope. As a result, it was found that the particles obtained were .alpha.-Fe.sub.2 O.sub.3 particles having an average long axis length of 70 nm and an acicular ratio (long axis/short axis) of 4.5 and having an excellent particle size distribution with a variation of long axis length �(standard deviation of long axis length)/(average long axis length)! of 7%.

The spindle-shaped monodisperse hematite obtained was dispersed into distilled water in such an amount as to result in a hematite concentration of 2%. Cobalt sulfate was added thereto in an amount of 10% in terms of Co atom amount based on the amount of the Fe atoms contained in the hematite. The mixture was sufficiently stirred. Ammonia water was added to this suspension with stirring while monitoring the pH of the suspension to adjust the pH to 8.0. Thus, a Co compound was deposited on the hematite surface. Thereafter, sodium aluminate was added to the suspension with stirring in an amount of 8% in terms of Al atom amount based on the amount of the Fe atoms contained in the hematite, and dilute sulfuric acid was then added to adjust the pH of the suspension to 6.5. Further, an yttrium nitrate solution was added to the suspension with stirring in an amount of 6% in terms of Y atom amount based on the amount of the Fe atoms contained in the hematite, and ammonia water was added to adjust the pH of the suspension to 7.5. The suspension was then filtered and washed with distilled water to remove impurities. The surface-treated spindle-shaped hematite obtained was compacted into cylindrical granules by passing the hematite through compaction plates having a diameter of 3 mm, and then dried.

A 500 g portion of the surface-treated spindle-shaped monodisperse hematite was placed in a stationary reducing furnace, and annealed in nitrogen at 650.degree. C. for 1 hour. Thereafter, the temperature was lowered to 400.degree. C., and a hydrogen/CO.dbd.30/70 mixed gas was introduced in place of nitrogen to conduct reduction for 1 hour. Nitrogen was then introduced in place of the mixed gas. After the temperature was elevated to 450.degree. C., pure hydrogen was introduced in place of nitrogen to conduct reduction for 5 hours. Nitrogen was introduced in place of pure hydrogen to cool the contents to room temperature, and an air/nitrogen mixture regulated to have an oxygen concentration of 0.5% was introduced to conduct gradual oxidation at 50.degree. C. or lower while monitoring the temperature of the metal powder. After heat generation ended, the oxygen concentration was adjusted to 1% to continue gradual oxidation for 10 hours. Thereafter, a vapor of distilled water was introduced together with air in such an amount as to result in a water amount of 1% based on the amount of the metal particle to humidify and stabilize the particle.

PRODUCTION EXAMPLE 5

The hematite obtained in Production Example 4 was dispersed into distilled water in such an amount as to result in a hematite concentration of 2%. Sodium aluminate was added thereto with stirring in an amount of 8% in terms of Al atom amount based on the amount of the Fe atoms contained in the hematite, and dilute sulfuric acid was then added to adjust the pH of the suspension to 6.5. Further, a neodymium nitrate solution was added to the suspension with stirring in an amount of 5% in terms of Nd atom amount based on the amount of the Fe atoms contained in the hematite, and ammonia water was then added to adjust the pH of the suspension to 7.8. The suspension was filtered and washed with distilled water to remove impurities. The surface-treated spindle-shaped hematite obtained was compacted into cylindrical granules by passing the hematite through compaction plates having a diameter of 3 mm, and then dried.

The surface-treated hematite was treated under the same conditions as in Production Example 4 to obtain a ferromagnetic metal particle.

Magnetic characteristics of the ferromagnetic metal particles obtained in Production Examples 4 and 5 were determined with a vibrating sample magnetometer (manufactured by Toei Kogyo K.K.) at an external magnetic field of 10 kOe. Each ferromagnetic metal powder obtained was photographed with a high-resolution transmission electron microscope to determine the average long axis length, average acicular ratio, and crystallinity of the ferromagnetic metal particles and the average acicular ratio of the crystallites. Further, the specific surface area of each powder was measured with Quantasorb (manufactured by Quantachrome Inc.) after 30-minute dehydration at 250.degree. C. in nitrogen. The results obtained are shown in Table 3.

TABLE 3__________________________________________________________________________ Antisintering Agent Ferromagnetic Metal Particle Element Rare Average Average AverageProduction Added earth H.sub.c .sigma..sub.s S.sub.BET Long Axis Acicular Acicular RatioExample Co Al element (Oe) emu/g m.sup.2 /g Length Ratio Crystallinity of Crystallites__________________________________________________________________________4 5.0 8.0 Y 6.0 2050 145.8 48.5 42 3.3 75 3.05 0.0 8.0 Nd 5.0 1975 138.3 45.2 45 3.8 70 3.1__________________________________________________________________________

EXAMPLE 2

Tapes were produced under the following conditions using the ferromagnetic metal particles obtained in Production Examples 4 and 5, and examined for magnetic characteristics and electromagnetic characteristics.

______________________________________(Composition for Upper-Layer Formation)Ferromagnetic metal powder (Table 4) 100 partsBinder resinVinyl chloride copolymer 12 parts(--SO.sub.3 Na group content, 1 .times. 10.sup.-4 eq/g;degree of polymerization, 300)Polyester polyurethane resin 4 parts(neopentyl glycol/caprolactonepolyol/MDI =0.9/2.6/1 (by mol)--SO.sub.3 Na group content, 1 .times. 10.sup.-4 eq/g).alpha.-Alumina (average particle size, 0.1 .mu.m) 3.5 partsCarbon black 0.5 parts(average particle size, 80 nm)Butyl stearate 1 partStearic acid 2 partsMethyl ethyl ketone/cyclohexanone (1:1) 200 partsmixed solvent(Composition for Nonmagnetic-Layer Formation)Spherical titanium oxide 80 parts(average particle diameter, 0.025 .mu.m;treated with alumina;BET specific surface area, 60 m.sup.2 /g;pH, 7.5)Carbon black 20 parts(average primary particle diameter, 16 nm;DBP absorption amount, 80 ml/100 g;BET specific surface area, 250 m.sup.2 /g;pH, 8.0)Binder resinVinyl chloride-vinyl acetate-vinyl 10 partsalcohol copolymer(content of polar group --N.sup.+ (CH.sub.3).sub.3 Cl.sup.-,5 .times. 10.sup.-6 eq/g;monomer composition ratio, 86/13/1;degree of polymerization, 400)Polyester polyurethane resin 8 parts(backbone: 1,4-BD/phthalic acid/HMDI =2/2/1 (by mol);molecular weight, 10,200;hydroxyl group content, 0.23 .times. 10.sup.-3 eq/g;--SO.sub.3 Na group content, 1 .times. 10.sup.-4 eq/g)Butyl stearate 1 partStearic acid 2.5 partsMethyl ethyl ketone/cyclohexanone (1:1) 200 partsmixed solvent______________________________________

With respect to each of the composition for non-magnetic-layer formation and the composition for magnetic-layer formation, the ingredients were kneaded with a kneader and then dispersed with a sand grinder. To the resulting dispersions was added a polyisocyanate in an amount of 5 parts for the coating composition for nonmagnetic-layer formation and in an amount of 6 parts for the coating composition for magnetic-layer formation. To each dispersion was further added 20 parts of a methyl ethyl ketone/cyclo-hexanone (1:1) mixed solvent. These dispersions were filtered through a filter having an average opening diameter of 1 .mu.m to prepare a coating composition for nonmagnetic-layer formation and a coating composition for magnetic-layer formation.

The two coating compositions obtained were applied on a 7 .mu.m-thick poly(ethylene terephthalate) support by wet-on-wet simultaneous multi-layered coating as follows. The coating composition for nonmagnetic-layer formation was applied first at a dry thickness of 1.5 .mu.m, and the coating composition for magnetic-layer formation was applied immediately thereafter on the still wet nonmagnetic layer coating in such an amount as to obtain a 0.15 .mu.m-thick magnetic layer. While the two coating layers were still in a wet state, magnetic orientation of the ferromagnetic metal particles was performed with a rare earth magnet (surface flux density, 5,000 G) and a solenoid magnet (surface flux density, 5,000 G). The coating was then dried. Subsequently, calendering was conducted with a 7-roll calender comprising metal rolls at a roll temperature of 90.degree. C. to obtain a magnetic recording medium as a web. The web was slit into an 8-mm width. Thus, 8-mm video tape samples were produced. The samples were evaluated in the same manner as in Example 1, and the results obtained are shown in Table 4. As a standard for the examination of electromagnetic characteristics, Super DC Tape (manufactured by Fuji Photo Film Co., Ltd.) was used.

TABLE 4__________________________________________________________________________ Production Example for Ferro- Magnetic Characteristics magnetic Rotational Surface Overwriting Metal H.sub.c B.sub.m r3000/H.sub.c Hysteresis Roughness Output C/N Character- Particle (Oe) SQ (G) SFD (%) Loss integral (nm) (dB) (dB) istics__________________________________________________________________________Example 2-1 4 2230 0.83 4350 0.42 0.36 0.85 2.5 4.5 5.5 2.5Example 2-2 5 2170 0.84 4160 0.44 0.41 0.88 2.6 3.9 4.8 2.6__________________________________________________________________________

As is apparent from the results of Tables 2 and 4, in each of the Examples of the present invention, r3000/H.sub.c was low, and the tape has a satisfactory coercive force distribution. Further, the rotational hysteresis integral determined through a magnetic torque measurement is small, and the reversal of magnetization occurred by a mechanism closes to simultaneous rotation.

The ferromagnetic metal particles used in the Examples of the present invention, in which particles each had a crystallinity of 30% or higher, had nearly the same average long axis length and acicular ratio. In contrast, the ferromagnetic metal powders used in the Comparative Examples, in which particles each had a crystallinity of below the lower limit specified in the present invention, each had an average long axis length outside the range specified in the invention and had an increased coefficient of variation of long axis length. It is presumed that the increased coefficients of variation in the Comparative Examples resulted in the increased values of r3000/H.sub.c.

Even an extraordinarily fine ferromagnetic metal powder having an average long axis length of from 30 to 80 nm can be made to be a magnetic particle having a high coercive force and an excellent coercive force distribution by using a starting material having uniformity in particle size and by controlling the number of metal nuclei during the formation thereof to regulate the metal particles so as to have a crystallinity of from 30 to 100%. The magnetic recording medium containing this magnetic particle has a high output, a high C/N, and excellent overwriting characteristics.

While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Claims

1. A magnetic recording medium comprising a nonmagnetic support having thereon a magnetic layer containing at least ferromagnetic particles, wherein said ferromagnetic particles have a coercive force of from 1,700 to 3,000 Oe, an average long axis length of from 30 to 80 nm, an average acicular ratio of from 2.0 to less than 5.0, and a crystallinity of from 30 to 100%.

2. The magnetic recording medium as claimed in claim 1, wherein the ferromagnetic metal particles have a saturation magnetization .sigma..sub.s of from 125 to 165 emu/g.

3. The magnetic recording medium as claimed in claim 1, wherein the ferromagnetic metal particles comprise iron and Co and have a coercive force of from 1,700 to 2,800 Oe.

4. The magnetic recording medium as claimed in claim 1, which has a nonmagnetic layer mainly comprising inorganic nonmagnetic particles and a binder between the nonmagnetic support and the magnetic layer.