The present disclosure relates to a technique of magnetically separating ferromagnetic particles from a powdery and/or granular material containing ferromagnetic particles. The present disclosure particularly relates to a magnetic separator and a magnetic separation method suitable for, for example, separating iron from slag which is a by-product of a steelmaking process, and an iron source manufacturing method.
In a steelmaking process, slag (steelmaking slag) is produced as a by-product in hot metal pretreatment or converter decarburization. Slag is a product of a reaction between a calcium-based additive, which is added to remove impurities or unwanted elements in hot metal or molten steel, and the impurities or unwanted elements. The slag contains a large amount of iron, in addition to the removed impurities and unwanted elements.
To recycle iron in such slag, separation and recovery of iron are performed. Iron is typically separated and recovered according to the following process. First, the slag is put through a sieve, to remove large lumps (several hundred mm in diameter) contained in the slag. Small lumps that have passed through the sieve have iron and slag sticking together, and therefore are subjected to rough crushing using a hammer crusher, a rod mill, or the like to several 10 μm to several 10 mm in size, thus facilitating liberation (i.e. separation of slag and iron). After this, iron is separated using a magnetic separator. As the magnetic separator, suspended electromagnet type, magnetic drum separator type, magnetic pulley type, or the like is typically used.
In some cases, the slag is heated and then cooled for an appropriate time before being crushed, in order to liberate iron. Depending on the cooling time, it is possible to separate only the stuck slag without crushing the iron lumps, or pulverize the slag to about several 10 μm. With either method, liberation is promoted as the slag is more pulverized.
In general, liberation needs to be promoted in order to improve the iron recovery rate. Accordingly, mechanical crushing is repeatedly performed to reduce the particle size of the slag, or heat treatment is performed to reduce the particle size.
This magnetic separator has the following structure: In the conveyor end portion 102, the magnetic force of the magnets 104 inside the guide roll 103 acts on the powdery and/or granular material a on the conveyor belt 101. As a result, the non-magnetic particles not attracted to the magnets 104 fall first, and are collected in a non-magnetically attracted matter recovery portion 105. Meanwhile, the ferromagnetic particles attracted to the magnets 104 pass over a partition plate 106 provided below the guide roll 103, fall at a position where the magnetic force weakens, and are collected in a magnetically attracted matter recovery portion 107.
However, in the case where the powdery and/or granular material a is supplied in a large amount to the conventional magnetic separator illustrated in
Such a problem needs to be typically dealt with by, for example, reducing the supply amount of the powdery and/or granular material a using a vibrating feeder 108 or the like to reduce the thickness of the powdery and/or granular material layer on the conveyor belt 101 to a thickness corresponding to about one to two particles, as illustrated in
JP 2006-142136 A (PTL 1) proposes a method of separating foreign matter without excessively crushing slag by performing a plurality of specific processes. This is, however, a complex separation procedure, and requires high processing cost. Although a wet process is usually applied to avoid flocculation as described in JP H10-130041 A (PTL 2), enormous liquid waste disposal cost is required.
It could be helpful to provide a magnetic separator and a magnetic separation method that can, even in the case where a powdery and/or granular material containing ferromagnetic particles is processed in a large amount or the layer of the supplied powdery and/or granular material is thick, efficiently separate the ferromagnetic particles from the powdery and/or granular material by magnetic separation at low cost without requiring complex processes or liquid waste disposal.
It could also be helpful to solve the following problem specific to the magnetic separator of belt conveyor type illustrated in
In the concentric structure illustrated in
First, the discoveries concerning magnetic separation that led to conceiving the structure of a magnetic separator according to the present disclosure are described below.
In the case of separating, from a powdery and/or granular material in which ferromagnetic particles and non-magnetic particles are mixed, the ferromagnetic particles using moving magnets, the movement of each particle is observed as follows. First, the ferromagnetic particles are attracted to and move toward the magnets. With a change in magnetic field strength associated with the movement of the magnets, the attractive force acting on the ferromagnetic particles changes. When the magnetic field is strong, the ferromagnetic particles tend to gather together by the attractive force. When the magnetic field is weak, the ferromagnetic particles tend to disperse.
Such a change in attractive force has an effect similar to vibration on the powdery and/or granular material. As the strength of the magnetic field changes repeatedly, the state in which the ferromagnetic particles sandwich and embrace the non-magnetic particles is resolved. This facilitates the separation between the ferromagnetic particles and the non-magnetic particles. Moreover, due to a change in the direction of the magnetic field, a rotational force also acts on the ferromagnetic particles, so that the ferromagnetic particles move toward the magnets while rotating between the non-magnetic particles. By these two effects, a large number of ferromagnetic particles gradually gather near the magnets, whereas the non-magnetic particles move farther from the magnets. By using the changes in the magnitude and direction of the magnetic field in this way, the ferromagnetic particles and the non-magnetic particles can be separated from each other.
(A) to (D) in
This phenomenon inevitably occurs as long as at least one of the powdery and/or granular material a and the magnets is moving. In other words, the same phenomenon occurs in the case where only the powdery and/or granular material a is moving while the magnets are stationary.
In the case where magnets of the same magnetic pole are arranged side by side and moving, the ferromagnetic particles move due to a change in the magnitude of the magnetic field, but no force deriving from a change in the direction of the magnetic field acts on the ferromagnetic particles, and so the movement of the ferromagnetic particles is smaller. This causes lower separation efficiency.
Although (A) to (D) in
We discovered that efficient magnetic separation of ferromagnetic particles is achieved by applying this mechanism to the magnetic separator of belt conveyor type in the following manner: Magnets are arranged inside the guide roll on the conveyor end portion side so that magnetic poles adjacent in the circumferential direction of the guide roll in the part facing the powdery and/or granular material are different and magnetic poles adjacent in the axial direction of the guide roll in the part facing the powdery and/or granular material are the same, and the powdery and/or granular material moves in the magnetic field formed by these magnets. We also discovered that this effect is further enhanced by rotating the magnets in the circumferential direction so that the magnitude and direction of the magnetic field acting on the ferromagnetic particles change fast.
We further conducted close study on the problem of the adhesion of ferromagnetic particles that enter between the guide roll and the belt. We consequently found out that ferromagnetic particles a1 causing such a problem mainly fly from the feeder 108 and the conveyor belt 101, and reach the roll circular arc portion of the guide roll 103 not in contact with the conveyor belt 101 from the space on the widthwise end side of the conveyor belt 101, as illustrated in
The present disclosure is based on these discoveries.
One aspect of the present disclosure provides a magnetic separator comprising: at least one pair of guide rolls; and a conveyor belt that extends between the pair of guide rolls, and conveys a powdery and/or granular material containing ferromagnetic particles, wherein one guide roll of the pair of guide rolls is a hollow roll, and includes, in a hollow part thereof, a magnet roll including a plurality of magnets that are arranged along an inner peripheral surface of the guide roll in lines at intervals so that different magnetic poles alternate in a circumferential direction, and the magnetic separator further comprises a shield wall that covers a circular arc region of an outer peripheral surface of the guide roll except a circular arc region around which the conveyor belt is wound, to block magnetic lines of force from the plurality of magnets.
The magnetic separator may further comprises an other conveyor belt that is located below the conveyor belt, and conveys the powdery and/or granular material containing the ferromagnetic particles, wherein a part of the conveyor belt corresponding to the magnet roll is located near a powdery and/or granular material conveyance downstream side of the other conveyor belt.
The magnetic separator may further comprise at least one conduit that passes through the shield wall from a back surface thereof to a side facing the guide roll, and supplies air to a clearance between the shield wall and the guide roll.
The magnet roll may be rotatable independently of the guide roll.
A magnetic field change frequency F defined by the following expression (1) and indicating the number of changes of magnetic poles acting on the powdery and/or granular material from the plurality of magnets may be 30 Hz or more:
F=(x·P)/60 (1)
where x is the number of rotations of the magnet roll expressed in rpm, and P is the number of magnetic poles of the magnet roll, a pair of a north pole and a south pole arranged side by side in the circumferential direction on a surface of the magnet roll facing the powdery and/or granular material being counted as one magnetic pole in the number of magnetic poles.
Magnetic poles of magnets adjacent in an axial direction of the magnet roll from among the plurality of magnets may be the same.
Alternatively, magnetic poles of magnets adjacent in an axial direction of the magnet roll from among the plurality of magnets may be different.
A rotational direction of the one guide roll and a rotational direction of the magnet roll may be the same.
Alternatively, a rotational direction of the one guide roll and a rotational direction of the magnet roll may be opposite.
A rotational direction of the conveyor belt and a rotational direction of the other conveyor belt may be the same.
Alternatively, a rotational direction of the conveyor belt and a rotational direction of the other conveyor belt may be opposite.
The conveyor belt and the one guide roll may be made of a non-metallic material.
Any of the pair of guide rolls may be a non-drive roll.
Another aspect of the disclosure provides a magnetic separation method of separating, from a powdery and/or granular material containing ferromagnetic particles, the ferromagnetic particles using the magnetic separator as described above, the magnetic separation method comprising supplying the powdery and/or granular material onto the conveyor belt, with a thickness that is greater than a diameter of a smallest particle contained in the powdery and/or granular material.
Yet another aspect of the disclosure provides an iron source manufacturing method of manufacturing an iron source from a by-product of a steelmaking process, using the magnetic separator or the magnetic separation method as described above.
It is thus possible to, even in the case where a powdery and/or granular material containing ferromagnetic particles is processed in a large amount or the layer of the supplied powdery and/or granular material is thick, efficiently separate the ferromagnetic particles from the powdery and/or granular material containing the ferromagnetic particles by magnetic separation in one separation process at low cost, without requiring complex processes or liquid waste disposal.
It is also possible to prevent the adhesion of ferromagnetic particles that enter between the guide roll and the conveyor belt, by providing the shield that covers the peripheral surface of the guide roll not in contact with the conveyor belt with a thickness that is beyond the reach of the magnetic force.
In the accompanying drawings:
A magnetic separator and a magnetic separation method according to the present disclosure separate, from a powdery and/or granular material containing ferromagnetic particles, the ferromagnetic particles by a magnetic force.
A magnetic separator according to the present disclosure includes: at least one pair of guide rolls; and a conveyor belt that extends between the pair of guide rolls, and conveys a powdery and/or granular material containing ferromagnetic particles, wherein one guide roll of the pair of guide rolls is a hollow roll, and includes, in its hollow part, a magnet roll including a plurality of magnets that are arranged along the inner peripheral surface of the guide roll in lines at intervals so that different magnetic poles alternate in the circumferential direction, and the magnetic separator further includes a shield wall that covers a circular arc region of the outer peripheral surface of the guide roll except a circular arc region around which the conveyor belt is wound, to block magnetic lines of force from the magnets. The magnet roll forms a uniform magnetic field, and so a uniform force acts on the ferromagnetic particles, with it being possible to enhance the ferromagnetic particle separation efficiency. Moreover, the shield wall can prevent the adhesion of ferromagnetic particles that enter between the guide roll and the conveyor belt.
A magnetic separation method according to the present disclosure separates, from a powdery and/or granular material containing ferromagnetic particles, the ferromagnetic particles by a magnetic force using the magnetic separator having the above-mentioned structure.
In the magnetic separator and the magnetic separation method according to the present disclosure, the magnetic field change frequency F (Hz) defined by the following expression (1) and indicating changes in the magnitude of the magnetic field acting on the powdery and/or granular material from the magnet roll is set to 30 Hz or more:
F=(x·P)/60 (1)
where x is the number of rotations (rpm) of the magnet roll, and P is the number of magnetic poles of the magnet roll (a pair of a north pole and a south pole arranged side by side in the circumferential direction on the surface of the magnet roll facing the powdery and/or granular material being counted as one magnetic pole in the number of magnetic poles).
The magnetic field change frequency F is preferably 50 Hz or more and 160 Hz or less, and more preferably 50 Hz or more and 100 Hz or less.
For example, in the case where a north pole (a), a south pole (b), and a north pole (c) are arranged side by side in the circumferential direction, the pair of the north pole (a) and the south pole (b) is counted as one magnetic pole, and the pair of the south pole (b) and the north pole (c) is counted as one magnetic pole.
Setting the magnetic field change frequency F (Hz) to 30 Hz or more enables the magnitude and direction of the magnetic field acting on the powdery and/or granular material to change fast, with it being possible to accurately separate the ferromagnetic particles contained in the powdery and/or granular material.
Embodiments of the present disclosure are described in detail below.
As illustrated in
In
The magnet roll 20 is a roll that rotates by means such as a motor. The rotational direction of the magnet roll 20 may be the same as or opposite to the rotational direction of the guide roll 2, but is preferably opposite to the rotational direction of the guide roll 2. The magnet roll 20 is preferably rotated faster than the guide roll 2.
The rotational direction of the magnet roll 20 may be any of (i) the direction opposite to the direction of movement of the conveyor belt 1 (the rotational direction of the guide roll 2) and (ii) the same direction as the direction of movement of the conveyor belt 1 (the rotational direction of the guide roll 2). The ferromagnetic particles are subjected to a carrying force of moving them in the direction opposite to the rotational direction of the magnet roll 20 by the action of the magnetic field of the rotating magnet roll 20. In the case of (i), the carrying force on the ferromagnetic particles by the magnetic field and the frictional force between the conveyor belt 1 and the ferromagnetic particles are in the same direction. In the case of (ii), the carrying force and the frictional force are in opposite directions. In this case, the ferromagnetic particles are carried in the direction of movement of the conveyor belt 1 because the frictional force is greater.
Comparison between (i) and (ii) reveals the following. In the case of (ii), the carrying force on the ferromagnetic particles by the magnetic field and the frictional force between the conveyor belt 1 and the ferromagnetic particles are in opposite directions. Hence, while the ferromagnetic particles may sometimes stay on the conveyor belt 1, the ferromagnetic particles can be separated more efficiently. In the case of (i), the ferromagnetic particle separation efficiency is slightly lower than that of (ii), but there is the advantage of smoothly carrying the ferromagnetic particles without the ferromagnetic particles staying on the conveyor belt 1.
In
The size of each magnet 4 is not limited, and may be any size that allows a predetermined number of magnets 4 to be provided. The magnets 4 of the magnet roll 20 may be covered with a cover.
The array of the magnets 4 in the roll axial direction is preferably within the width of the conveyor belt 1, as illustrated in
The magnetic separator further includes a shield wall 5 that covers the circular arc region of the outer peripheral surface of the guide roll 2 except the circular arc region around which the conveyor belt 1 is wound, and extends across the full width of the guide roll 2 in the axial direction of the guide roll 2. It is important that the shield wall 5 has a function of blocking magnetic lines of force from the magnets 4 of the magnet roll 20. In the example illustrated in
Regarding the thickness of the shield wall 5, i.e. the distance that is beyond the influence of the magnetic lines of force, the back surface 5a is preferably at a distance of 30 mm or more and more preferably at a distance of 50 mm or more from the guide roll surface, to sufficiently reduce the influence of the magnetic lines of force and block the magnetic lines of force. No upper limit on the thickness of the shield wall 5 is placed, yet the thickness of the shield wall 5 is preferably 200 mm or less because a thickness of more than 200 mm imposes equipment constraints.
The length of the shield wall 5 along the axial direction of the guide roll 2 is preferably the full width of the guide roll 2 as mentioned above, but the shield wall 5 functions sufficiently if the edge of the shield wall 5 is in the the region RT depicted in
A magnetic separation method using this device is described below, together with the functions and actions of the magnetic separator illustrated in
When performing magnetic separation using this magnetic separator, the feed speed of the conveyor belt 1 is set to a speed required for the process. The rotational speed of the magnet roll 20 is determined so that the change of the magnetic field is sufficiently fast with respect to the belt feed speed. In particular, the rotational speed of the magnet roll 20 is preferably set so as to satisfy the condition in the foregoing expression (1).
In the state where the conveyor belt is rotating, the powdery and/or granular material a containing the ferromagnetic particles is supplied, with a sufficient thickness, from the supply device 100 onto the moving conveyor belt 1, and conveyed to the guide roll 2 side of the conveyor belt 1.
The powdery and/or granular material a conveyed by the conveyor belt 1 is exposed to the magnetic field of the magnet roll 20, upon reaching the region where the conveyor belt 1 is in contact with the guide roll 2.
In the magnetic separator illustrated in
In particular, with the structure in the embodiment illustrated in
By rotating the magnet roll 20 in the magnet roll structure illustrated in
In Embodiment 1, the magnetic field is desirably changed as fast as possible (fast changes in the strength and direction of the magnetic field). As mentioned above, the magnetic field change frequency F (Hz) of the magnet roll 20 defined by the following expression (1) is preferably 30 Hz or more:
F=(x·P)/60 (1)
where x is the number of rotations (rpm) of the magnet roll, and P is the number of magnetic poles of the magnet roll (a pair of a north pole and a south pole arranged side by side in the circumferential direction on the surface of the magnet roll facing the powdery and/or granular material being counted as one magnetic pole in the number of magnetic poles).
The magnetic field change frequency is more preferably 50 Hz or more and 160 Hz or less.
For example, in the case where a north pole (a), a south pole (b), and a north pole (c) are arranged side by side in the circumferential direction, the pair of the north pole (a) and the south pole (b) is counted as one magnetic pole, and the pair of the south pole (b) and the north pole (c) is counted as one magnetic pole. Suppose magnets (e.g. neodymium magnets) of 12 poles (a pair of a north pole and a south pole being counted as one magnetic pole) are arranged in the circumferential direction. Then, a magnetic field change frequency of 30 Hz is realized if the rotational speed of the magnet roll 20 is 150 rpm. Suppose magnets of 24 poles (a pair of a north pole and a south pole being counted as one magnetic pole) are arranged in the circumferential direction. Then, a magnetic field change frequency of 30 Hz is realized if the rotational speed of the magnet roll 20 is 75 rpm.
The upper limit of the magnetic field change frequency is about 160 Hz, given that the number of rotations of the magnet roll 20 has a mechanical upper limit and the effect of the magnetic field change may be saturated even when the frequency is increased.
The magnetic separator according to Embodiment 1 can magnetically separate the ferromagnetic particles from the powdery and/or granular material a efficiently, as described above. Accordingly, in the magnetic separation of the powdery and/or granular material a using the device, the powdery and/or granular material a is desirably supplied from the supply device 100 onto the conveyor belt 1 with a layer thickness that is greater than the diameter of the smallest particle contained in the powdery and/or granular material a and for which the magnetic force acts sufficiently, as illustrated in
The powdery and/or granular material subjected to magnetic separation is not limited. Examples of the powdery and/or granular material include slag such as steelmaking slag, and tailing ores. The magnetic separator is particularly suitable for the magnetic separation of slag.
In iron recovery from slag, steelmaking slag is first atomized. If the atomization is insufficient, the iron recovery rate is low. Since there are various ironmaking or steelmaking processes in which steelmaking slag is produced, various slags are produced. The slag particle size after the atomization is determined depending on the slag. The slag often needs to be atomized to about several 10 μm to 1 mm, depending on the form of iron contained. A typical atomization method is grinding. After grinding the slag using a jaw crusher or a hammer crusher as rough grinding, the slag is further ground for pulverization using a ball mill, a rod mill, a jet mill, a pin mill, an impact mill, or the like. Another method is to heat the slag to about 1000° C. to 1300° C. and then gradually cool the slag.
The atomized slag is then subjected to magnetic separation by the magnetic separator according to the present disclosure. According to the present disclosure, iron can be efficiently separated and recovered from the slag.
In Embodiment 1 illustrated in
In the case where the magnets 4 are arranged so that the magnetic poles are different in the axial direction of the magnet roll 20 as illustrated in
Members around the rotating magnet roll are affected by the eddy current effect due to the changing magnetic field, and metal members, even when they are non-magnetic, are heated by the eddy current. Therefore, the conveyor belt 1, the guide roll 2, and the shield wall 5 in this embodiment are preferably made of a non-metallic material such as resin or ceramic.
Instead of the shield wall 5 having a thick wall structure in Embodiment 1 illustrated in
As illustrated in
Embodiment 3 may also be applied to Embodiment 2 illustrated in
A device according to Embodiment 5 illustrated in
In the first belt conveyor A, reference sign 8 is a conveyor belt different from the conveyor belt 1 in the foregoing Embodiments 1 to 4, 81 is a guide roll on the conveyor start portion 82 side, and 83 is a guide roll on the conveyor end portion 84 side. The belt conveyor A is formed by extending the conveyor belt 8 between the guide rolls 81 and 83.
In the second belt conveyor B, reference sign 1 is a conveyor belt same as the conveyor belt 1 in the foregoing Embodiments 1 to 4, 2 is a guide roll on the conveyor start portion 11 side, and 3 is a guide roll on the conveyor end portion 12 side. The belt conveyor B is formed by extending the conveyor belt 1 between the guide rolls 2 and 3. In Embodiment 5, the guide roll 2 has a larger diameter than the guide roll 3, and the rotational axis of the guide roll 3 is located higher than the rotational axis of the guide roll 2, so that the upper surface of the conveyor belt 1 (the upper belt portion between the guide rolls 2 and 3) is substantially horizontal. Alternatively, the upper surface of the conveyor belt 1 may be tilted downward to the guide roll 3.
The supply device 100 that supplies the powdery and/or granular material a containing the ferromagnetic particles onto the conveyor belt 1 is located near the conveyor start portion 82 of the belt conveyor A.
The ferromagnetic particles attracted to and held by the belt conveyor B are, having been conveyed by the belt conveyor B, discharged from the conveyor end portion 12. A magnetically attracted matter recovery portion 70 is provided below the conveyor end portion 12 of the belt conveyor B. Meanwhile, the non-magnetic particles fall below the conveyor start portion 11 of the belt conveyor B, where a non-magnetically attracted matter recovery portion 71 is provided.
In Embodiment 5 illustrated in
Any of the guide rolls 2 and 3 of the belt conveyor B is driven by drive means such as a motor. Typically, the guide roll 3 is a drive roll, and the guide roll 2 is a non-drive roll.
In Embodiment 5, the magnet roll 20 including the plurality of magnets 4 is provided inside the guide roll 2, as mentioned above. The magnet roll 20 is rotatable independently of the guide roll 2.
The plurality of magnets 4 are arranged at predetermined intervals in the roll circumferential direction and axial direction of the magnet roll 20, as illustrated in
The number of magnets 4 arranged in the roll circumferential direction, the intervals between the magnets 4, and the like are not limited. When the number of magnets 4 is greater or the intervals between the magnets 4 are smaller, the magnitude and direction of the magnetic field change faster. In other words, fast magnetic field change can be achieved even if the rotational speed of the magnet roll 20 is low.
The strength of the magnetic field by the magnets 4 is not limited. Typically, the magnets 4 are preferably selected so that the strength is about 0.01 T to 0.5 T in the conveyor belt portion in contact with the guide roll 2, depending on the object. If the magnetic field is excessively weak, the effect by the magnet roll 20 is insufficient. If the magnetic field is excessively strong, an excessively strong attractive force acts on the ferromagnetic particles, which can hamper the separation of the ferromagnetic particles.
In the device according to Embodiment 5, by the plurality of magnets 4 arranged at predetermined intervals and the gap portion between adjacent magnets 4, the magnetic field changes as strong→weak→strong→weak→ . . . , and the effect on the ferromagnetic particles in the powdery and/or granular material layer alternates as gather→disperse→gather→disperse→ . . . . The width of the gap portion between magnets 4 adjacent in the roll circumferential direction is not limited, but a width of about 1 mm to 50 mm is appropriate in order to achieve the above-mentioned effect.
The magnetic field applied by the magnet roll 20 is desirably changed as fast as possible (fast changes in the strength and direction of the magnetic field). As mentioned above, the magnetic field change frequency F of the magnet roll 20 defined by the foregoing expression (1) is preferably 30 Hz or more.
A magnetic separation method using this device is described below, together with the functions and actions of the magnetic separator illustrated in
When performing magnetic separation using this magnetic separator, the feed speed of the conveyor belt 1 is set to a speed required for the process. The rotational speed of the magnet roll 20 is determined so that the change of the magnetic field is sufficiently fast with respect to the belt feed speed. In particular, the rotational speed of the magnet roll 20 is preferably set so as to satisfy the condition in the foregoing expression (1).
In the state where the belt conveyors A and B are in operation, the powdery and/or granular material a containing the ferromagnetic particles is supplied, with a sufficient thickness, from the supply device 100 onto the moving conveyor belt 8 of the belt conveyor A, and conveyed to the conveyor end portion 84. The upper surface of the powdery and/or granular material a conveyed by the conveyor belt 8 comes into contact with the lower surface of the conveyor start portion 11 of the belt conveyor B near the conveyor end portion 84, and the powdery and/or granular material a enters between the conveyor end portion 84 of the belt conveyor A and the conveyor start portion 11 of the belt conveyor B. Here, the powdery and/or granular material a is subjected to the magnetic field of the magnet roll 2 of the belt conveyor B.
In the magnetic separator illustrated in
Since the magnet roll 20 rotates independently of the guide roll 2 as illustrated in
In the device according to Embodiment 5 illustrated in
Even the conventional device illustrated in
The magnetic separator according to Embodiment 5 can magnetically separate the ferromagnetic particles from the powdery and/or granular material a efficiently, as described above. Accordingly, in the magnetic separation of the powdery and/or granular material a using the device, the powdery and/or granular material a is desirably supplied from the supply device 6 onto the conveyor belt 1 of the belt conveyor A with such a layer thickness that is greater than the diameter of the smallest particle contained in the powdery and/or granular material a and for which the magnetic force acts sufficiently, as illustrated in
The device according to Embodiment 5 subjects the powdery and/or granular material a (powdery and/or granular material layer) conveyed by the belt conveyor A to the action of the magnetic field of the magnets 4 provided inside the guide roll 2 on the conveyor start portion 11 side of the belt conveyor B, and attracts the ferromagnetic particles in the powdery and/or granular material a and moves the ferromagnetic particles toward the lower surface of the belt conveyor B, thus separating the ferromagnetic particles. The interval between the conveyor end portion 84 of the belt conveyor A and the conveyor start portion 11 of the belt conveyor B may be any interval with which the magnetic force of the magnet roll 20 sufficiently acts on the ferromagnetic particles in the powdery and/or granular material a. Typically, the interval is preferably such an interval with which the upper surface of the layer of the powdery and/or granular material a conveyed by the conveyor belt 8 of the belt conveyor A comes into contact with the conveyor start portion 11 of the belt conveyor B, i.e. the powdery and/or granular material layer can enter between the conveyor end portion 84 of the belt conveyor A and the conveyor start portion 11 of the belt conveyor B.
Embodiment 6 which is a modification of Embodiment 5 is described below, with reference to
In Embodiment 6, the positional relationship between the belt conveyor A and the belt conveyor B is different from the example illustrated in
Such an arrangement equally ensures the separation of the ferromagnetic particles. The structures other than the positional relationship between the belt conveyors A and B are approximately the same as those in Embodiment 5 illustrated in
Embodiment 7 which is another modification of Embodiment 5 is described below, with reference to
In Embodiment 7, the guide roll 2 is a sleeve body that is hollow inside, and is rotatably supported. The magnet roll 20 including the plurality of magnets 4 arranged at predetermined intervals is provided inside the guide roll 2, in the circular arc portion of the inner peripheral surface of the guide roll in contact with the conveyor belt.
The guide roll 2 in Embodiment 7 differs from the guide roll 2 in Embodiment 5 in that the magnet roll 20 including the magnets 4 is stationary. In other words, the magnets 4 are non-rotating stationary magnets installed independently of the guide roll 2. The magnets 4 are arranged so that magnetic poles adjacent in the roll circumferential direction are different and magnetic poles adjacent in the roll width direction are the same, as illustrated in
In Embodiment 7, the range of the installation of the magnets 4 in the roll circumferential direction is at least about 1800 (half around the magnet roll 20) from the lower end position of the magnet roll 20 (the position facing the conveyor end portion 84 of the belt conveyor A) to the top position of the magnet roll 20, as illustrated in
In the magnetic separator according to Embodiment 7, the ferromagnetic particles in the powdery and/or granular material a are attracted by the stationary magnets 4, and the powdery and/or granular material a (or part of the material a) in a form that the ferromagnetic particles embrace the non-magnetic particles is carried by the conveyor belt 1 while adhering to (and held by) the lower surface of the belt conveyor B. With this device, too, although the effect is lower than that of the magnet roll 20 in
The magnetic separator according to Embodiment 7 has the following functional effects: (i) Since a basic system of subjecting the powdery and/or granular material a discharged from the first belt conveyor A to the action of the magnetic field of the magnets 4 in the second belt conveyor B from above to attract the ferromagnetic particles in the powdery and/or granular material a and move the ferromagnetic particles toward the belt conveyor B is employed, the embracement and enfoldment of the non-magnetic particles by the ferromagnetic particles can be reduced as compared with the conventional device; and (ii) The enfoldment and embracement of the non-magnetic particles by the ferromagnetic particles can be resolved by the magnetic field change by the magnets 4.
Embodiment 8 which is a modification of the shield wall 50 is described below, with reference to
Moreover, an auxiliary device 9 may be provided in the inside space of the conveyor belt 1 between the pair of guide rolls 2 and 3, as illustrated in
Magnetic separation was performed on steelmaking slag using the magnetic separator according to Embodiment 1 illustrated in
After putting a ground product of the steelmaking slag through a 400 μm sieve, slag passed through the sieve was set as a powdery and/or granular material to be magnetically separated. The iron concentration of the powdery and/or granular material was 54 mass %. The supply layer thickness of the powdery and/or granular material onto the conveyor belt 1 was 7 mm. The outer diameter of the magnet roll 2 was 200 mm, the number of magnetic poles of the magnets 4 was 12 (a pair of a north pole and a south pole being counted as one magnetic pole), the feed speed of the conveyor belt 1 was 0.5 m/s, the rotational speed of the magnet roll 20 was 31.9 rpm, and the magnetic field strength in the conveyor belt portion in contact with the magnet roll 20 was 0.2 T. To investigate the effect of the rotational speed of the magnet roll 20, the rotational speed of the magnet roll 20 was set to 100 rpm (magnetic field change frequency F=20 Hz), 150 rpm (magnetic field change frequency F=30 Hz), 500 rpm (magnetic field change frequency F=100 Hz), 850 rpm (magnetic field change frequency F=170 Hz), and 1200 rpm (magnetic field change frequency F=240 Hz).
The shield wall 5 was made of resin, and was 100 mm in thickness. The magnetic force at the back surface 5a of the shield wall 5 was 100 gauss or less.
For comparison, the same powdery and/or granular material of the steelmaking slag was magnetically separated at a feed speed of 0.5 m/s, using a magnetic drum separator X (the magnetic field strength on the drum surface: 0.16 T) and a magnetic pulley Y (the magnetic field strength in the conveyor belt portion in contact with the guide roll: 0.2 T) which have been commonly used conventionally.
In each example, the iron concentration of the recovered magnetically attracted matter and the iron recovery rate from the slag were examined. Moreover, the adhesion amount of the iron powder to the guide roll was investigated. The adhesion amount of the iron powder was compared between the case where the shield wall 5 was installed and the case where the shield wall 5 was not installed.
In the case of using the magnetic drum separator X, the iron concentration of the recovered magnetically attracted matter was low because the non-ferrous component was also caught, and also the iron recovery rate was low because iron escaped to the non-magnetically attracted side. In the case of using the magnetic pulley Y, almost the whole powdery and/or granular material was caught, and so the recovery rate was high. However, the important iron concentration of the recovered magnetically attracted matter was almost the same as that of the powdery and/or granular material before the magnetic separation.
In Example according to the present disclosure, on the other hand, both the iron concentration of the recovered magnetically attracted matter and the iron recovery rate of the slag were high. Particularly when the magnetic field change frequency of the magnet roll 2 was 30 Hz or more, both the iron concentration of the recovered magnetically attracted matter and the iron recovery rate of the slag were higher.
The adhesion amount of the iron powder in the above-mentioned operation was compared between the case where the shield wall 5 was installed and the case where the shield wall 5 was not installed. As a result, while the adhesion amount was 100 g/h in the case where the shield wall 5 was not installed, the adhesion amount was reduced to 0.5 g/h or less in the case where the shield wall 5 was installed.
The same operation was performed with regard to the respective shield walls in Embodiments 2 to 4. As a result, while the adhesion amount was 100 g/h in the case where the shield wall 5 or the shield wall 50 (the distance from the magnet roll 2 to the back surface 5a of the shield wall 5: 100 mm) was not installed, the adhesion amount was reduced to 0.5 g/h or less in the case where the shield wall 5 was installed. Further, when the shield wall 5 or the shield wall 50 is supplied with air at 5 MPa, the adhesion amount of the iron powder was reduced to 0.3 g/h or less.
Magnetic separation was performed on steelmaking slag using the magnetic separator according to Embodiment 5 illustrated in
After putting a ground product of the steelmaking slag through a 400 μm sieve, slag passed through the sieve was set as a powdery and/or granular material to be magnetically separated. The iron concentration of the powdery and/or granular material was 54 mass %. The supply layer thickness of the powdery and/or granular material onto the conveyor belt 1 of the belt conveyor A was 7 mm. The outer diameter of the guide roll 3 of the belt conveyor B was 300 mm, the number of magnetic poles of the magnet roll 20 was 12 (a pair of a north pole and a south pole being counted as one magnetic pole), the feed speed of the conveyor belt of each of the belt conveyors A and B was 0.5 m/s, the rotational speed of the magnet roll 02 was 31.9 rpm, and the magnetic field strength in the conveyor belt portion in contact with the magnet roll 20 was 0.2 T. To investigate the effect of the rotational speed of the magnet roll 20 of the belt conveyor B, the rotational speed of the magnet roll 20 was set to 100 rpm (magnetic field change frequency F=20 Hz), 150 rpm (magnetic field change frequency F=30 Hz), 500 rpm (magnetic field change frequency F=100 Hz), 850 rpm (magnetic field change frequency F=170 Hz), and 1200 rpm (magnetic field change frequency F=240 Hz).
The shield wall 5 was made of resin, and was 100 mm in thickness. The magnetic force at the back surface 5a of the shield wall 5 was 100 gauss or less.
For comparison, the same powdery and/or granular material of the steelmaking slag was magnetically separated at a feed speed of 0.5 m/s, using a magnetic drum separator X (the magnetic field strength on the drum surface: 0.16 T) and a magnetic pulley Y (the magnetic field strength in the conveyor belt portion in contact with the guide roll: 0.2 T) which have been commonly used conventionally.
In each example, the iron concentration of the recovered magnetically attracted matter and the iron recovery rate from the slag were examined. Moreover, the adhesion amount of the iron powder to the magnet roll was investigated. The adhesion amount of the iron powder was compared between the case where the shield wall 5 was installed and the case where the shield wall 5 was not installed.
In the case of using the magnetic drum separator X, the iron concentration of the recovered magnetically attracted matter was low because the non-ferrous component was also caught, and also the iron recovery rate was low because iron escaped to the non-magnetically attracted side. In the case of using the magnetic pulley Y, almost the whole powdery and/or granular material was caught, and so the iron recovery rate was high. However, the important iron concentration of the recovered magnetically attracted matter was almost the same as that of the powdery and/or granular material before the magnetic separation.
In Example according to the present disclosure, on the other hand, both the iron concentration of the recovered magnetically attracted matter and the iron recovery rate of the slag were high. Particularly when the magnetic field change frequency of the magnet roll 2 was 30 Hz or more, both the iron concentration of the recovered magnetically attracted matter and the iron recovery rate of the slag were higher.
The adhesion amount of the iron powder in the above-mentioned operation was compared between the case where the shield wall 5 was installed and the case where the shield wall 5 was not installed. As a result, while the adhesion amount was 100 g/h in the case where the shield wall 5 was not installed, the adhesion amount was reduced to 0.5 g/h or less in the case where the shield wall 5 was installed.
Number | Date | Country | Kind |
---|---|---|---|
PCT/JP2015/005947 | Nov 2015 | WO | international |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/JP2016/085631 | 11/30/2016 | WO | 00 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2017/094803 | 6/8/2017 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
2272719 | Maynard | Feb 1942 | A |
2992733 | Buus | Jul 1961 | A |
3454913 | Israelson | Jul 1969 | A |
4318804 | Nakajima | Mar 1982 | A |
5101980 | Arvidson | Apr 1992 | A |
5207330 | Siesco, Jr. | May 1993 | A |
5494172 | Siesco, Jr. | Feb 1996 | A |
6338903 | Takigawa | Jan 2002 | B1 |
6540088 | Oder | Apr 2003 | B2 |
6634504 | Robinson | Oct 2003 | B2 |
9010538 | Smolkin | Apr 2015 | B2 |
9962710 | Suderman | May 2018 | B2 |
20130264248 | Smolkin et al. | Oct 2013 | A1 |
Number | Date | Country |
---|---|---|
102000629 | Apr 2011 | CN |
104736249 | Jun 2015 | CN |
2910309 | Aug 2015 | EP |
H10130041 | May 1998 | JP |
H10165838 | Jun 1998 | JP |
2001121028 | May 2001 | JP |
2002331257 | Nov 2002 | JP |
2006142136 | Jun 2006 | JP |
2013063423 | Apr 2013 | JP |
1020150058475 | May 2015 | KR |
2014061256 | Apr 2014 | WO |
Entry |
---|
English Translation of JP 2013063423 A; Pub Date: Apr. 2013; INV: Naoe Tekko (Year: 2013). |
English Translation of WO 2014061256 A1; Pub Date: Apr. 2014; INV: Ishida et al. (Year: 2014). |
Nov. 2, 2018, the Extended European Search Report issued by the European Patent Office in the corresponding European Patent Application No. 16870740.4. |
Jan Svoboda, Magnetic Techniques for the Treatment of Materials, 2004, pp. 70-72, Kluwer Academic Publishers. |
Jan. 17, 2017, International Search Report issued in the International Patent Application No. PCT/JP2016/085631. |
Jan. 9, 2018, Notification of Reasons for Refusal issued by the Japanese Patent Office in the corresponding Japanese Patent Application No. 2017-505683, with English language Concise Statement of Relevance. |
Apr. 28, 2019, Office Action issued by the State Intellectual Property Office in the corresponding Chinese Patent Application No. 201680069413.2 with English language search report. |
May 13, 2019, Office Action issued by the IP Australia in the corresponding Australian Patent Application No. 2016362141. |
Oct. 1, 2019, Office Action issued by the Korean Intellectual Property Office in the corresponding Korean Patent Application No. 10-2018-7014666 with English language concise statement of relevance. |
Feb. 28, 2020, Office Action issued by the Canadian Intellectual Property Office in the corresponding Canadian Patent Application No. 3,002,928. |
May 6, 2020, Office Action issued by the China National Intellectual Property Administration in the corresponding Chinese Patent Application No. 201680069413.2 with English language concise statement of relevance. |
Number | Date | Country | |
---|---|---|---|
20180353969 A1 | Dec 2018 | US |