Patent Application
20160125986
According to the known art, magnetic steel sheets having a layer that improves the electrical insulation are used, for example, in electric drives for the design of stators. The materials used are regulated by the standard EN 10106 (1995). The materials named in this standard give a wide-ranging product range in order that the demands of different applications can be satisfied. The usable materials range from low-alloyed steel, with outstanding magnetic permeability, good thermal conductivity and good stamping properties, to higher-alloyed steels having very low remagnetization losses even at higher frequencies. As alloying constituents, the alloys in the standard contain copper (<=0.02%), manganese (<=1.2%), silicon (0.1-4.4%), aluminum (0.1-4.4%), the sum formed from the silicon content and twice the aluminum content being <5%, phosphorus (<=0.15%), tin (<=0.2%) and antimony (<=0.2%). Iron forms the basis of the alloy.
Coatings which improve the insulation between the individual steel sheet layers and the processability have been developed for improving the properties of the magnetic steel sheets. The specific properties of the material used have to take into consideration influencing variables, such as corrosion protection, electrical insulation, influence on the stamping properties, heat resistance or weldability. Coatings for magnetic steel sheets can be gathered from the standard EN 10342 (2005).
The magnetic steel sheets available in the aforementioned standards, and the coatings thereof, cannot withstand all fields of use, however, as has been shown. Particularly when the magnetic steel sheets are exposed to highly corrosive media, e.g. sour gas (high hydrogen sulfide content), these magnetic steel sheets are at great risk of corrosion.
Various embodiments described herein relate to a magnetic steel sheet having a layer which improves the electrical insulation.
Various embodiments described herein relate to a magnetic steel sheet which is also suitable for use under highly corrosive conditions.
The layer includes a metal oxide containing mainly titanium oxide or tantalum oxide, and the magnetic steel sheet has a diffusion zone, into which the metal of the metal oxide has diffused into the material of the magnetic steel sheet and which adjoins the layer. Since the oxide layer adjoins a diffusion layer, the adhesion of the oxide layer is greatly improved. The use of the metals titanium or tantalum has the effect that the oxide layer which forms spontaneously on the surface of the magnetic steel sheet is highly resistant to corrosive media. Use under extreme corrosive conditions, e.g. sour gas, thereby also becomes possible. By way of example, it is possible to operate motor pumps which are used for conveying natural gas in a subsea environment. This gives rise to a new application for the magnetic steel sheets, these permitting the use of the electric machines under favorable conditions for maintenance.
If the oxide layers which form spontaneously under atmospheric oxygen are not adequate to provide effective corrosion protection, the oxide layer can also be produced by an electrochemical treatment of the surface.
The diffusion zone, which adjoins the oxide layer, has two advantages. Firstly, the diffusion zone improves the adhesion of the oxide layer, since the transition between the oxide layer and the matrix material of the magnetic steel sheet, a steel alloy, is continuous, and this reduces the formation of stresses. In addition, it is possible that, in the event of damage to the oxide layer, the titanium or tantalum material present in the diffusion layer can be used for passivation of the damaged site. To this end, the metal in question diffuses to the surface, where renewed passivation takes place. The corrosion protection is thereby retained.
According to various embodiments described herein, the layer has a thickness of at least 5 and at most 10 μm. These are layer thicknesses of the oxide layer which allow for effective corrosion protection and require little manufacturing outlay and little use of material in their production owing to the small thickness.
According to various embodiments described herein, the diffusion zone has a titanium or tantalum content of more than 50% by weight within a distance of 2 μm from the interface with the layer. These are alloying contents which still allow for the diffusion-induced transportation of titanium or tantalum to damaged sites. In this case, it is also possible for titanium or tantalum contents of up to 100% to arise directly beneath the oxide layer. The titanium or tantalum content in the matrix of the magnetic steel sheet (alloyed steel) reduces with an increasing distance from the surface of the magnetic steel sheet, and therefore the effect which improves the adhesion of the oxide layer can be utilized.
Various embodiments described herein relate to a method for treating a magnetic steel sheet, in which the magnetic steel sheet is coated with a layer which improves the electrical insulation. Various embodiments described herein relate to a method which makes it possible to treat magnetic steel sheets and which produces products which ensure adequate corrosion protection even under highly corrosive influences.
A diffusion zone is produced on the surface of the magnetic steel sheet, tantalum or titanium diffusing as metal into the surface. The tantalum or titanium metal at the surface is converted into the associated metal oxide, titanium oxide or tantalum oxide, a layer including the metal oxide being formed and a residual content of the metal of the metal oxide remaining in the diffusion zone. This produces the oxide layer described above, which has outstanding resistance to corrosion. The residual content of the metal of the metal oxide remains in the diffusion zone, as a result of which, the adhesion of the oxide layer is improved. In addition, the diffusion zone forms a deposit of the corresponding material, and in the event of damage to the oxide layer this is available for healing the damage by spontaneous passivation.
Before the formation of the layer, the diffusion zone has a titanium or tantalum content of more than 50% by weight within a distance of 5 μm from the interface with the layer. Before the formation of the layer, the diffusion zone has to have a larger region with a high titanium or tantalum concentration, since oxidation of the titanium or tantalum converts part of the previously formed diffusion layer into the oxide layer. In order for there to still be sufficient material available for repairing the oxide layer in the matrix of the magnetic steel sheet after this oxidation operation, the proportion of titanium or tantalum therefore has to be sufficiently high.
Various methods described herein can be carried out in such a way that the production of the diffusion zone on the surface of the magnetic steel sheet is carried out as a physical (PVD) process with a subsequent heat treatment. PVD processes are easy to handle. Both titanium and tantalum can be deposited on steel by using suitable target materials. Titanium is deposited in many ways by PVD processes, for example to produce tool coatings, this normally being effected in a reactive nitrogen atmosphere, in order to be able to produce titanium nitride. If an inert gas atmosphere is chosen instead, pure titanium is deposited. It is also possible for tantalum to be deposited readily on steel. A process of this type is described, for example, in EP 77 535 A1. Titanium can also be deposited, for example, by spraying or powder coating, as can be gathered, for example, from the Derwent Abstract with the Accession Number 1978-43006 A. The powder processes are also referred to as packing processes, where the diffusion layers arise as a result of the diffusion of the tantalum into the workpiece. Unlike in PVD processes, the diffusion layer thus forms immediately, whereas in PVD processes a heat treatment has to take place after the coating operation, this leading to diffusion of the tantalum or of the titanium into the matrix of the magnetic steel sheet. Parameters for diffusion treatments of this nature are generally known and can be gathered, for example, from the Derwent Abstract with the Accession Number 1984-104398. In addition to the aforementioned treatment methods, electrochemical coatings, for example in a salt bath, or else coating by means of chemical (CVD) are also conceivable in principle.
If a passivation layer which forms spontaneously on the titanium or the tantalum is not adequate for effective corrosion protection, but rather the passivation layer is to be produced electrochemically, a passivation layer which forms spontaneously beforehand may be removed. In this way, the electrochemically assisted formation of the passivation layer can be effected uninterrupted. The heat treatment then takes place in an oxygen-containing atmosphere, it also being possible for the oxygen to be enriched compared to atmospheric conditions in order to accelerate the oxidation operation.
These and other objects and advantages will become more apparent and more readily appreciated from the following description of the various embodiments, taken in conjunction with the accompanying drawings of which:
Reference will now be made in detail to the various embodiments, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to like elements throughout.
The various embodiments have been described in detail with particular reference and examples, but it will be understood that variations and modifications can be effected within the spirit and scope of the various embodiments covered by the claims which may include the phrase “at least one of A, B and C” as an alternative expression that means one or more of A, B and C may be used, contrary to the holding in Superguide v. DIRECTV, 69 USPQ2d 1865 (Fed. Cir. 2004).
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2013 208 617.2 | May 2013 | DE | national |
This application is based on and hereby claims priority to International Application No. PCT/EP2014/057879 filed on Apr. 17, 2014 and German Application No. 10 2013 208 617.2 filed on May 10, 2013; the contents of both are hereby incorporated by reference.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2014/057879 | 4/17/2014 | WO | 00 |