Embodiments described herein relate generally to a magnetoresistive element and a method of manufacturing the same.
In recent years, a semiconductor memory utilizing a resistance variable element as a memory element, such as a PRAM (phase-change random access memory) or an MRAM (magnetic random access memory), has been attracting attention and being developed. The MRAM is a device which performs a memory operation by storing “1” or “0” information in a memory cell by using a magnetoresistive effect, and has features of nonvolatility, high-speed operation, high integration and high reliability.
One of magnetoresistive effect elements is a magnetic tunnel junction (MTJ) element including a three-layer multilayer structure of a storage layer having a variable magnetization direction, an insulation film as a tunnel barrier, and a reference layer which maintains a predetermined magnetization direction.
The resistance of the MTJ element varies depending on the magnetization directions of the storage layer and the reference layer, it takes a minimum value when the magnetization directions are parallel, and takes a maximum value when the magnetization directions are antiparallel, and information is stored by associating the parallel state and antiparallel state with binary information “0” and binary information “1”, respectively.
The writing of information into the MTJ element involves a magnetic-field write scheme in which only the magnetization direction in the storage layer is reversed by a current magnetic field that is generated when a current flowing is flowed through a write line, and a write (spin injection write) scheme using spin angular momentum movement in which the magnetization direction in the storage layer is reversed by passing a spin polarization current through the MTJ element itself.
In the former scheme, when the element size is reduced, the coercivity of a magnetic body constituting the storage layer increases and the write current tends to increase, and thus it is difficult to achieve both the miniaturization and low electric current.
On the other hand, in the latter scheme (spin injection write scheme), spin polarized electron to be injected into the MTJ element decreases with the decrease of the volume of the magnetic layer constituting the storage layer, so that it is expected that both the miniaturization and low electric current may be easily achieved.
Embodiments will be hereinafter described with reference to the accompanying drawings. In the following drawings, portions corresponding to already-shown drawings will be denoted by the same signs (including a sign having a different subscript), and their detailed explanations will be omitted.
In general, according to one embodiment, a magnetoresistive element is disclosed. The magnetoresistive element includes a lower electrode; a stacked body provided on the lower electrode and including a first magnetic layer, a tunnel barrier layer and a second magnetic layer. The first magnetic layer includes a first region and a second region provided outside the first region to surround the first region. The second region includes an element included in the first region and other element being different from the element. A hard mask layer is provided on the stacked body. A cap layer is provided on the hard mask layer. The magnetoresistive element further includes an upper electrode penetrating the cap layer and contacting the hard mask.
According to an embodiment, a method for manufacturing a magnetoresistive element is disclosed. A stacked body is formed on a substrate. The stacked body includes a first magnetic layer, a tunnel barrier layer and a second magnetic layer. A hard mask layer is formed on the stacked body. A cap layer is formed on the hard mask layer. The cap layer is processed. The stacked body and the hard mask are etched using the processed cap layer as a mask. Ions are implanted into a portion of the stacked body that is outside of the cap layer using the cap layer as a mask.
[
A lower electrode 101, a storage layer 102, a tunnel barrier layer 103, a reference layer 104, a hard mask 105 having conductivity and a cap layer 106 having insulating properties are successively formed on a substrate 100.
The substrate 100 comprises a silicon substrate (semiconductor substrate), a selection transistor formed on a surface of the silicon substrate and configured to select an MTJ element, an interlayer insulating film, etc. The storage layer 102 comprises, for example, CoFeB. The tunnel barrier layer 103 comprises, for example, magnesium oxide (MgO). The reference layer 102 comprises, for example, an alloy of Pt (precious metal) and Ni or Co (magnetic material). The hard mask 105 comprises, for example, W, Ta or Ru. The cap layer 106 comprises, for example, silicon nitride.
[
The cap layer 106 is processed into a predetermined shape by etching the cap layer 106 using a resist pattern which is formed on the cap layer 106 and not shown as a mask.
[
The resist pattern and the cap layer 106 are used as a mask, and the hard mask 105 and the reference layer 104 are etched by RIE process. The RIE process is performed under the condition that it stops on the tunnel barrier layer 103. The resist pattern disappears during the RIE process, and then the cap layer 106 functions as a mask of the etching.
Damage is caused on the storage layer 102 outside the cap layer 106 by the RIE process. The damage caused on the storage layer 102 may deteriorate magnetic anisotropy, spin injection efficiency and an MR ratio. Therefore, the damage may degrade the properties of the MTJ element.
It should be noted that the etching may be performed not only in RIE process but in IBE process.
[
In the present embodiment, ions 107 are implanted into the storage layer 102 using the cap layer 106 as a mask to reduce an influence of the damage of the storage layer 102. In the figure, 102a denotes a storage layer of a portion into which the ions 107 are implanted (second region). The storage layer 102a includes, for example, CoFeB (magnetic material) and the ions 107 (element). The storage layer 102 (first region) under the cap layer 106 does not include the ions 107 (element).
The ions 107 are implanted also into the tunnel barrier layer 103 and the cap layer 106 on the storage layer 102a. The ions 107 may be implanted also into the lower electrode 101.
The thickness of the cap layer 106 is selected in such a manner that the ions 107 are not to be implanted into the hard mask 105 when the ions are implanted into the tunnel barrier layer 103 and the storage layer 102a. For example, the thickness of the cap layer 106 is greater than the sum of the thickness of the tunnel barrier layer 103 and the thickness of the storage layer 102a. Thus, a problem that the ions 107 are implanted into the hard mask 105 and resistance of the hard mask 105 increases does not occur.
The reason why the influence of the damage of the storage layer 102 is reduced is that the storage layer 102a is demagnetized by ion implantation of the ions 107. By the implantation of the ions 107, the storage layer 102a is not only electrically deactivated, but it may be magnetically deactivated.
An element used as the ions 107 is, for example, at least one of As, Ge, Ga, Sb, In, N, Ar, He, F, Cl, Br, I, O, Si, B, C, Zr, Tb and Ti. Among them, especially, As and Ge are effective in reducing the influence of the damage of the storage layer 102, since they have a large atomic radiuses. As and Ge may reduce a dose amount of the ion implantation.
[
An insulating layer is formed on an entire surface to cover the stacked body of the reference layer 104, the hard mask 105 and the cap layer 106, thereafter, a sidewall 108 comprising the insulating layer is formed on the side wall of the stacked body of the reference layer 104, the hard mask 105 and the cap layer 106 by etching the entire surface of the insulating layer
[
The tunnel barrier layer 103, the storage layer 102a and the lower electrode 101 are processed by etching using the sidewall 108 as a mask.
An insulating layer 109 is formed on an entire surface to cover the cap layer 106 and the sidewall 108, thereafter, an opening reaching the hard mask 105 is formed in the insulating layer 109 and the cap layer 106, and the upper electrode 110 is formed in this opening.
Since the ions 107 are not implanted into the hard mask 105 in the step of
A process for forming the upper electrode 110 includes, for example, depositing conducting layer to be processed into the upper electrode 110 to fill in the opening, and then planarizing surfaces of the conducting layer and the insulating layer 109 by chemical mechanical polishing (CMP). As a result, the upper electrode 110 penetrating the cap layer 106 and contacting the hard mask 105 is obtained.
The MRAM according to the present embodiment can be obtained in accordance with the manufacturing method according to the first embodiment, and has an advantage similar to that of the first embodiment. In
A step of
In the present embodiment, the thickness of the hard mask 105 (D1) is set to be greater than the sum (D2) of the thickness of the tunnel barrier layer 103 and the thickness of the storage layer 102 (D1>D2).
Thus, if ions 107 are implanted into the tunnel barrier layer 103 and the storage layer 102 under the condition that the ions 107 are not implanted into a lower electrode 101, a reference layer 104 is not damaged by the ions 107, since the ions 107 implanted into the hard mask 105 do not reach the reference layer 104.
Thereafter, the MRAM having a structure in which the upper electrode 110 shown in
The manufacturing method according to the above-described embodiments may be applied also to the MTJ element including a shift cancelling layer on the reference layer 104. Although MTJ elements having various types of structures are present, the manufacturing methods according to the embodiments may be applied generally to a method of manufacturing an MTJ element including implanting an element into a magnetic layer to reduce the influence of the damage of the magnetic layer caused by the RIE process.
While certain embodiments have been described, these embodiments have been presented by way of example only, and are not intended to limit the scope of the inventions. Indeed, the novel methods and systems described herein may be embodied in a variety of other forms; furthermore, various omissions, substitutions and changes in the form of the methods and systems described herein may be made without departing from the spirit of the inventions. The accompanying claims and their equivalents are intended to cover such forms or modifications as would fall within the scope and spirit of the inventions.
This application claims the benefit of U.S. Provisional Application No. 61/876,081, filed Sep. 10, 2013, the entire contents of which are incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
6165803 | Chen et al. | Dec 2000 | A |
6297983 | Bhattacharyya | Oct 2001 | B1 |
6365286 | Inomata et al. | Apr 2002 | B1 |
6391430 | Fullerton et al. | May 2002 | B1 |
6479353 | Bhattacharyya | Nov 2002 | B2 |
6483675 | Araki et al. | Nov 2002 | B1 |
6713830 | Nishimura et al. | Mar 2004 | B2 |
6829121 | Ikeda et al. | Dec 2004 | B2 |
6895658 | Shimazawa et al. | May 2005 | B2 |
6965138 | Nakajima et al. | Nov 2005 | B2 |
6987652 | Koganei | Jan 2006 | B2 |
7220601 | Hwang et al. | May 2007 | B2 |
7586781 | Saitoh et al. | Sep 2009 | B2 |
7619431 | De Wilde et al. | Nov 2009 | B2 |
7746603 | Gill et al. | Jun 2010 | B2 |
7768824 | Yoshikawa et al. | Aug 2010 | B2 |
7916430 | Kagami et al. | Mar 2011 | B2 |
7957184 | Yoshikawa et al. | Jun 2011 | B2 |
8119018 | Ikemoto et al. | Feb 2012 | B2 |
8130474 | Childress et al. | Mar 2012 | B2 |
8139405 | Yoshikawa et al. | Mar 2012 | B2 |
8154915 | Yoshikawa et al. | Apr 2012 | B2 |
8218355 | Kitagawa et al. | Jul 2012 | B2 |
8223533 | Ozeki et al. | Jul 2012 | B2 |
8268713 | Yamagishi et al. | Sep 2012 | B2 |
8270125 | Gill | Sep 2012 | B2 |
8339841 | Iwayama et al. | Dec 2012 | B2 |
8475672 | Iori et al. | Jul 2013 | B2 |
8710605 | Takahashi et al. | Apr 2014 | B2 |
8716034 | Ohsawa et al. | May 2014 | B2 |
8928055 | Saida et al. | Jan 2015 | B2 |
8963264 | Dimitrov et al. | Feb 2015 | B2 |
20010022742 | Bhattacharyya | Sep 2001 | A1 |
20010024347 | Shimazawa et al. | Sep 2001 | A1 |
20020070361 | Mack et al. | Jun 2002 | A1 |
20020146851 | Okazawa et al. | Oct 2002 | A1 |
20020167059 | Nishimura et al. | Nov 2002 | A1 |
20020182442 | Ikeda et al. | Dec 2002 | A1 |
20030067800 | Koganei | Apr 2003 | A1 |
20040080876 | Sugita et al. | Apr 2004 | A1 |
20040188732 | Fukuzumi | Sep 2004 | A1 |
20050020076 | Lee et al. | Jan 2005 | A1 |
20050048675 | Ikeda | Mar 2005 | A1 |
20050174876 | Katoh | Aug 2005 | A1 |
20050254289 | Nakajima et al. | Nov 2005 | A1 |
20050274997 | Gaidis et al. | Dec 2005 | A1 |
20060043317 | Ono et al. | Mar 2006 | A1 |
20060105570 | Hautala et al. | May 2006 | A1 |
20070164338 | Hwang et al. | Jul 2007 | A1 |
20080122005 | Horsky et al. | May 2008 | A1 |
20090080238 | Yoshikawa et al. | Mar 2009 | A1 |
20090191696 | Shao et al. | Jul 2009 | A1 |
20090243008 | Kitagawa et al. | Oct 2009 | A1 |
20090285013 | Saitoh et al. | Nov 2009 | A1 |
20100097846 | Sugiura et al. | Apr 2010 | A1 |
20100135068 | Ikarashi et al. | Jun 2010 | A1 |
20100183902 | Kim et al. | Jul 2010 | A1 |
20100230770 | Yoshikawa et al. | Sep 2010 | A1 |
20110037108 | Sugiura et al. | Feb 2011 | A1 |
20110059557 | Yamagishi et al. | Mar 2011 | A1 |
20110159316 | Wang et al. | Jun 2011 | A1 |
20110174770 | Hautala | Jul 2011 | A1 |
20110211389 | Yoshikawa et al. | Sep 2011 | A1 |
20110222335 | Yoshikawa et al. | Sep 2011 | A1 |
20110233697 | Kajiyama | Sep 2011 | A1 |
20120032288 | Tomioka | Feb 2012 | A1 |
20120056253 | Iwayama et al. | Mar 2012 | A1 |
20120074511 | Takahashi et al. | Mar 2012 | A1 |
20120135543 | Shin et al. | May 2012 | A1 |
20120139019 | Iba | Jun 2012 | A1 |
20120244639 | Ohsawa et al. | Sep 2012 | A1 |
20120244640 | Ohsawa et al. | Sep 2012 | A1 |
20130017626 | Tomioka | Jan 2013 | A1 |
20130069186 | Toko et al. | Mar 2013 | A1 |
20130099338 | Nakayama et al. | Apr 2013 | A1 |
20130181305 | Nakayama et al. | Jul 2013 | A1 |
20140327096 | Guo | Nov 2014 | A1 |
20140356979 | Annunziata et al. | Dec 2014 | A1 |
20150069542 | Nagamine et al. | Mar 2015 | A1 |
Number | Date | Country |
---|---|---|
04241481 | Aug 1992 | JP |
09041138 | Feb 1997 | JP |
2000156531 | Jun 2000 | JP |
2001052316 | Feb 2001 | JP |
2001308292 | Nov 2001 | JP |
2002176211 | Jun 2002 | JP |
2002280640 | Sep 2002 | JP |
2002299726 | Oct 2002 | JP |
2002299727 | Oct 2002 | JP |
2002305290 | Oct 2002 | JP |
2003110162 | Apr 2003 | JP |
2003536199 | Dec 2003 | JP |
2004006589 | Jan 2004 | JP |
2004500483 | Jan 2004 | JP |
2005209951 | Aug 2005 | JP |
2006005342 | Jan 2006 | JP |
2006510196 | Mar 2006 | JP |
2006165031 | Jun 2006 | JP |
2007053315 | Mar 2007 | JP |
2007234897 | Sep 2007 | JP |
2007305610 | Nov 2007 | JP |
2008066612 | Mar 2008 | JP |
2008522429 | Jun 2008 | JP |
2008153527 | Jul 2008 | JP |
2008171882 | Jul 2008 | JP |
2008193103 | Aug 2008 | JP |
2008-282940 | Nov 2008 | JP |
2009054715 | Mar 2009 | JP |
2009081216 | Apr 2009 | JP |
2009239120 | Oct 2009 | JP |
2010003342 | Jan 2010 | JP |
2010113782 | May 2010 | JP |
2011040580 | Feb 2011 | JP |
2011054873 | Mar 2011 | JP |
2012-244051 | Dec 2012 | JP |
2013153232 | Aug 2013 | JP |
2005088745 | Sep 2005 | WO |
Entry |
---|
Related U.S. Appl. No. 13/226,868; First Named Inventor: Yuichi Ohsawa; Title: “Method of Manufacturing Magnetic Memory”; Filed: Sep. 7, 2011. |
Related U.S. Appl. No. 13/226,960; First Named Inventor: Yuichi Ohsawa; Title: “Method of Manufacturing Multilayer Film”; Filed: Sep. 7, 2011. |
Related U.S. Appl. No. 13/604,537; First Named Inventor: Masahiko Nakayama; Title: “Magnetic Memory Element and Magnetic Memory”; Filed: Sep. 5, 2012. |
Albert, et al., “Spin-polarized current switching of a Co thin film nanomagnet”, Applied Physics Letters, vol. 77, No. 23, Oct. 7, 2000, 3809-3811. |
Otani, et al., “Microfabrication of Magnetic Tunnel Junctions Using CH3OH Etching”, IEEE Transactions on Magnetics, vol. 43, No. 6, Jun. 6, 2007, 2776-2778. |
U.S. Appl. No. 13/231,894; First Named Inventor: Shigeki Takahashi; Title: “Magnetic Memory and Method of Manufacturing the Same”; Filed: Sep. 13, 2011. |
U.S. Appl. No. 14/202,802; First Named Inventor: Masahiko Nakayama; Title: “Magnetoresistive Element and Method of Manufacturing the Same”; Filed: Mar. 10, 2014. |
U.S. Appl. No. 14/203,249; First Named Inventor: Masahiko Nakayama; Title: “Magnetic Memory and Method of Manufacturing the Same”; Filed: Mar. 10, 2014. |
U.S. Appl. No. 14/200,742; First Named Inventor: Masaru Toko; Title: “Magnetoresistive Element and Method for Manufacturing the Same”; Filed: Mar. 7, 2014. |
Number | Date | Country | |
---|---|---|---|
20150069550 A1 | Mar 2015 | US |
Number | Date | Country | |
---|---|---|---|
61876081 | Sep 2013 | US |