Patent Application
20150056505
1. Technical Field
The present subject matter is in the technical field of energy storage devices. More particularly, the present subject matter is in the technical field of rechargeable batteries employing an iron electrode.
2. Background of the Invention
Iron electrodes have been used in energy storage batteries and other devices for over one hundred years. In particular, iron electrodes are often combines with a nickel-based positive electrode in alkaline electrolyte to form a nickel-iron (Ni—Fe) battery. The Ni—Fe battery is a rechargeable battery having a nickel (III) oxy-hydroxide positive electrode in combination with an iron negative electrode with an alkaline electrolyte such as potassium hydroxide.
Traditionally, the iron electrode active material is produced by dissolving pure iron powder in sulfuric acid, followed by drying and roasting to produce iron oxide (Fe2O3). The material is washed and partially reduced in hydrogen and partially oxidized to give a mix of Fe and magnetite (Fe3O4). Additives such as FeS may be added to the active material mass. The negative electrode structure is typically that of a pocket plate construction wherein the active material is introduced into the current collector. The current collector is made up of steel strips or ribbons that are perforated and nickel plated and the strip is formed into a tube or pocket with one end left for introduction of the active material (D. Linden and T. Reddy, Editors, “Handbook of Batteries, Third Edition”, McGraw-Hill©2002).
The Ni—Fe batteries have been displaced by other battery technologies due to the high cost of manufacturing. While the technology of preparing iron electrodes is well known and the current preferred process for making theses electrodes is a pocket design, pocket design electrodes are also difficult to produce in high volumes and the energy and power utilization from this design is low. The industry would be well served by a low cost, high quality and high performance iron electrode design and manufacturing process.
Other forms of electrode production are known in the art, particularly electrodes of a pasted construction. This type of electrode typically incorporated a binder with the active material, which can then be coated onto a two or three dimensional current collector, dried, and compacted to from the finished electrode.
U.S. Pat. No. 3,853,624 describes a Ni—Fe battery incorporating iron electrodes employing a metal fiber structure which is loaded with sulfurized magnetic iron oxide by a wet pasting method. The plates are electrochemically formed outside the cell to electrochemically attach the iron active materials to the plaque structure. Such a process in unwieldy in high volume manufacturing and adds to produce cost.
U.S. Pat. No. 4,021,911 describes an iron electrode wherein the iron active mass is spread onto a grid and rolled and dried. The electrode is then treated with an epoxide resin solution to form a solid reinforcing film-like layer on the electrode surface. However, it can be expected that such a surface film would contribute to an insulating nature to the electrode surface, significantly increasing charge transfer resistance and lowering the cell's ability to sustain high charge and/or discharge rates.
Pasted electrodes using various binders have been proposed for alkaline electrodes most particularly for electrodes employing the hydrogen-absorbing alloys for NiMH batteries (for example U.S. Pat. No. 5,780,184). However, the desired properties for these electrodes differ significantly from those desired for a high capacity iron electrode. In the case of the MH electrode, high electrode density (low porosity) is required to maintain good electrical contact between the alloy particles and to facilitate solid-state hydrogen diffusion in the alloy. By contrast, high porosity is desirable for iron electrodes due to the low solubility of the iron oxide species. Hence, binder system developed for other types of alkaline electrodes have not been optimized for Fe—Ni batteries and hence have not found commercial application.
The industry, however, would be greatly served by a battery, e.g., a Ni—Fe or Mn—Fe battery, which shows improved performance. The uses would thereby be increased. A battery with an iron anode having improved efficiency, charge retention and cycle like would be greatly welcome.
The present invention provides one with a Mn—Fe having an iron anode having improved performance characteristics. The iron anode comprises a single layer of a conductive substrate coated on at least one side with a coating comprising an iron oxide material and a binder. The anode is prepared by coating the substrate with a coating mixture comprising iron active material and a binder. The battery cell can use a particular electrolyte and/or battery separator. The resulting characteristics of efficiency, charge retention and cycle life are much improved over such iron anode batteries in the prior art.
In one embodiment, the iron electrode is coated with a continuous process. The manufacturing benefits are lower cost, higher volume, continuous process, if desired, and a higher quality product and method for manufacturing compared to the standard pocket electrode design.
The invention comprises a Mn—Fe battery with an iron anode. The battery, in one embodiment comprises an iron electrode comprised of a single, coated conductive substrate, prepared by a simple coating process, which can be continuous. The substrate can be coated on one side, or on both sides. The combination of such an iron electrode with a manganese cathode provides one with a battery cell of enhanced power, capacity and efficiency.
The substrate for the iron electrode is used as a current conducting and collecting material that houses the active material (iron) of the electrode. In the current pocket design, the substrate encompasses the active material and holds the material. Two layers of substrate are therefore required per electrode. In the present invention, a single layer of substrate is used. This single layer acts as a carrier with coated materials bonded to at least one side. In one embodiment, both sides of the substrate are coated. This substrate may be a thin conductive material such as a perforated metal foil or sheet, metal mesh or screen, woven metal, or expanded metal. The substrate can also be a three dimensional material such as a metal foam or felt. For example, metal plated perforated foil can be used.
The coating mix is a combination binder and active materials in aqueous or organic solution. The mix can also contain other additives such as pore formers. Pore formers are often used to insure sufficient H2 movement in the electrode. Without sufficient H2 diffusion, the capacity of the battery will be adversely affected. Conductive additives such as carbon or Ni powder can also be used in the coating mix. The binder is generally resistant to degradation due to aging, temperature, and caustic environment. The binder can compromise polymers, alcohols, rubbers, and other materials, such as advanced latex formulation that has been proven effective. A polyvinyl alcohol binder is used in one embodiment and provides excellent results.
The active material for the mix formulation is selected from iron species that are generally less oxidative. Such materials include metal Fe and iron oxide materials. The iron oxide material will convert to iron metal when a charge is applied. A suitable iron oxide material includes Fe3O4. In addition, any other additives are generally required to be of a less oxidative nature, such as sulfur, antimony, selenium, and tellurium.
The coating method can be a continuous process that applies the active material mixture to the substrate such as spraying, dip and wipe, extrusion, low pressure coating die, or surface transfer. A batch process can also be used, but a continuous process is advantageous regarding cost and processing. The coating mixture has to maintain a high consistency for weight and thickness and coating uniformity. This insures that finished electrodes will have similar loadings of active material to provide uniform capacity in the finished battery product.
The coating method is conducive to layering of various materials and providing layers of different properties such as porosities, densities and thicknesses. For example, the substrate can be coated with three layers. The first layer being of high density, second layer of medium density, and final layer of a lower density to create a density gradient. This gradient improves the flow of gases from the active material to the electrolyte, and provides better electrolyte contact and ionic diffusion with the active material throughout the structure of the electrode.
After coating, the iron electrode is dried to remove any residual liquid, i.e., aqueous or organic solvent. The drying methods will generally provide a continuous method for liquid removal from the coated active material which will enhance the adhesion and binding effects of the dry constituents without iron ignition. This drying method provides a uniform and stable active material coating with the substrate material. Two stages of drying can be used. For example, the first can be radiation for bulk drying, for cost and quality control, followed by convection drying to remove the remaining liquid. The radiation used can be any radiation, such as infrared, microwave or UV, and is very fast. In one embodiment, IR is used. However, the radiation creates a high temperature at the surface of the coated electrode. The high temperature is fine as long as sufficient water is still present to act as a heat sink. Therefore, the water is generally removed to about 10-20 wt % water. This can generally be determined using a control chart. Going below 10% water is dangerous, as the electrode becomes too dry and the high temperature can ignite the iron. Thus, using the convention drying to complete the removal of water/liquid is a preferred embodiment, once the amount of water remaining is in the 10-20 wt % range. In another embodiment, radiation can be used to complete the drying if the process is conducted in an inert atmosphere.
The compaction methods used can be accomplished by rolling mill, vertical pressing, and magnetic compaction of the active material to the desired thickness from 0.005 to 0.500 inches and porosities from 10% to 50%, for high quality and low cost continuous processing. In one embodiment, the porosity of the electrode is from 15-25 % porosity. These compaction methods can be used in conjunction with the layering method described above for providing material properties of density, thickness, porosity, and mechanical adhesion.
In addition, continuous in-line surface treatments can be applied continuously throughout any of the steps including coating, layering, and drying processes. The treatments can apply sulfur, polymer, metal spray, surface lament, etc. In one embodiment, a polymer post-coat is applied.
The iron electrode is used with a manganese cathode to make a battery. The cathode comprises a substrate and a cathode paste. The cathode paste comprises active manganese metal powder mixed with an aqueous or organic binder. The active manganese material generally comprises manganese dioxide. The paste is of a viscosity and texture to allow consistent coating in one or both sides of a substrate. As described above, the substrate holds active material, in this case the manganese metal paste, and acts as a current collector. In one embodiment, the substrate is made of conductive material such as steel, Ni or Cu, and maybe plated with iridium or Ni, i.e., a material that is non-active relative to MnO2. In one embodiment, the substrate comprises a porous conductive substrate such as, for example, perforated metal, metal foam, metal felt, expanded metal, or carbon foam. More specifically, the substrate comprises nickel foam. In one embodiment, the cathode paste is coated on and throughout the foam mesh.
In one embodiment, the cathode paste comprises about 70-90 weight %, electrolytic manganese dioxide; about 2-15 weight %, for example, about 7.5 weight %, graphite and/or carbon black; about 3-10 weight %, for example, about 5 weight %, hydrogen recombination catalysts include silver, silver oxides, and hydrogen absorbing alloys. The cathode paste may further comprise indium.
Exemplary polymeric binders for the cathode paste include carboxymethyl cellulose (CMC), polyacrylic acid, starch, starch derivatives, polyisobutylene, polytetrafluoroethylene, polyamide, polyethylene, and a metal stearate. The polymeric binder can include conductive graphite, for example, conductive graphite having an average particle size between 2 and 6 microns. In one embodiment, the cathode paste comprises CMC as the binder in an amount of about 2 wt % of the cathode paste.
The battery can be made as is conventional, with a standard electrolyte and battery separator. The electrolyte, for example, can be a potassium hydroxide based electrolyte. In one embodiment the electrolyte used is a sodium hydroxide based electrolyte, with the sodium hydroxide generally having a concentration of 5-7 N in the electrolyte. In one embodiment, the electrolyte comprises sodium hydroxide, lithium hydroxide and sodium sulfide. For example, the sodium hydroxide concentration in the electrolyte is about 6 N, the lithium hydroxide concentration in the electrolyte is about 1 N, and the sodium sulfide concentration in the electrolyte is about 2 wt %. In using this electrolyte with an iron anode battery, it has been discovered that the life, capacity and power of the battery is much improved. It is believed that the use of the sodium hydroxide based electrolyte reduces the iron solubility in the electrolyte, which extends the battery life. The entire cell is also more stable and effective at high temperatures. The lithium hydroxide increases charge acceptance of the positive, which increases capacity. The presence of the sodium sulfide has been discovered to be important for the effective deposit of sulfur on the iron anode. A battery with an iron anode seems to work better with sodium sulfide in the electrolyte, as the sulfide ends up in the iron anode as a performance enhancer after a few cycles. The sodium sulfide in essence is believed to increase the effective surface area of the iron, so one obtains more utilization of the iron. The capacity and power is therefore improved. Overall, it is believed that use of the present sodium hydroxide electrolyte improves the capacity; increases the power; reduces gassing; and, improves efficiency of a Mn—Fe cell.
The battery separator that can be used in the present battery, either alone without the sodium hydroxide based electrolyte, but preferably in combination with the electrolyte, is one that is iron-phobic. The separator can be etched for wettability, but this is merely optional when using the present battery separator. The battery separator is made of a polymer, with a generally smooth surface. The polymer can be any polymer which provides a non-polar surface, which is also generally very smooth. Examples of such polymers include polyolefins, such as polyethylene, and polytetrafluoroethylene (e.g., Teflon®). By using a separator which is more iron-phobic, the separator picks up iron at a slower rate. This results in a significant increase in the cycle life of the battery. Use of the separator is believed to improve the capacity; improve the power; and, the efficiency of a Mn—Fe cell. When the separator is used with the sodium hydroxide based electrolyte of the present invention, the life of a Mn—Fe battery is believed increased at least threefold.
The present batteries including the iron electrode can be used, for example, quite effectively in a cellphone, thereby requiring an electrode with only a single side coated. However, both sides are preferably coated allowing the battery to be used in many applications as is known in the art. For example, the battery cell can be utilized in a vehicle for starting an internal combustion engine. In a more portable format, besides a cellphone, the present battery can be used in power tools and portable electronic devices.
Turning to the figures of the drawing,
While the foregoing written description of the invention enables one of ordinary skill to make and use what is considered presently to be the best mode thereof, those of ordinary skill will understand and appreciate the existence of variations, combinations, and equivalents of the specific embodiment, method, and examples herein. The invention should therefore not be limited by the above described embodiment, method, and examples, but by all embodiments and methods within the scope and spirit of the invention.
This application claims priority to U.S. Provisional Application Ser. No. 61/867,854, filed Aug. 20, 2013, which application is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61867854 | Aug 2013 | US |