Patent Application
20160282275
The present disclosure is directed to photonic structures. In particular, the present disclosure is directed to photonic structures that have patterned surface properties that allows preferential interaction with certain fluids.
Three dimensional (3D) photonic crystals (PCs), materials with a 3D-periodic variation in refractive index, have been the subject of extensive scientific interest since their inception over two decades ago. Even when there is not sufficient index-contrast to allow a complete 3D photonic bandgap, 3D PCs display exceptionally bright reflected colors arising from photonic stop gaps in particular crystal directions. Structural colors from PC structures are exhibited in a wide range of biological organisms, and often display dynamic tunability. Infiltration and inversion of porous 3D photonic crystals with materials that are capable of dynamic actuation has produced a broad class of PCs with structural colors that can be dynamically manipulated by various forces, such as mechanical force, temperature, electrostatic/electrochemical forces, and the like. However, the surface properties of these porous structures were more or less uniform throughout the photonic crystal.
In certain embodiments, a product that includes a porous three-dimensional photonic structure having a first region and a second region is described. In certain embodiments, the first region comprises a first surface property on at least some of the interior surfaces of the porous three-dimensional photonic structure; and the first surface property allows a first indicator material to infiltrate at least some of the pores of said first region.
In certain embodiments, the indicator material is a fluid.
In certain embodiments, the first region without the first indicator material has a substantially similar visible appearance to the visible appearance of the second region.
In certain embodiments, the first region includes the first indicator material filled in at least some of the pores of the first region, and the first region has a different reflectance spectrum than the reflectance spectrum of the second region.
In certain embodiments, the first surface property includes wettability, hydrophobicity, hydrophilicity, lyophobicity, or lyophilicity.
In certain embodiments, the second region includes a second surface property on at least some of the interior surface of the porous three-dimensional photonic structure.
In certain embodiments, the second regions comprises a second material which fills the pores of the porous three-dimensional photonic structure.
In certain embodiments, the product further includes a third region which has a third surface property on at least some of the interior surface of the porous three-dimensional photonic structure.
In certain embodiments, the first region comprises a first functional group present on substantially all of the interior surfaces of the first region to provide the first surface property.
In certain embodiments, the first functional group includes reactive groups, protecting groups, hydrophilic groups, hydrophobic groups, lyophilic groups, lyophobic groups, nanoparticles or mixtures thereof.
In certain embodiments, the photonic structure is an inverse opal structure, a mesoporous silica, a short range order structure exhibiting structural color, a quasicrystal, or mixtures thereof.
In certain embodiments, the first region and the second region are patterned to provide an encrypted message that is readily visible after the first indicator material occupies at least some of the pores of said first region.
In certain embodiments, the first region is capable of wicking up the first indicator material.
In certain embodiments, the first region and the second region are located apart from each other in a lateral dimension of the photonic crystal.
In certain embodiments, the first region and the second region are located apart from each other in a vertical dimension of the photonic crystal.
In certain embodiments, the pore sizes are selected to provide a predetermined energy barrier for the first indicator material to infiltrate at least some of the pores of said first region.
In certain embodiments, the photonic crystal further includes one or more additives within the photonic crystal to enhance optical response of the photonic crystal.
In certain embodiments, the first indicator material includes a mixture of different fluids.
In certain embodiments, different devices, such as a sensor, encryption device, and the like can be fabricated.
In certain embodiments, a method including the following steps is described: providing a porous three-dimensional photonic structure; and patterning a first region of said porous three-dimensional photonic structure with a first surface property on at least some of the interior surfaces of the porous three-dimensional photonic structure; where the first surface property allows a first indicator material to occupy at least some of the pores of said first region.
In certain embodiments, the method further includes providing a mask in or over at least a second region of said porous three-dimensional photonic structure.
In certain embodiments, the first region includes a first functional group present on substantially all of the interior surfaces of the first region to provide the first surface property.
In certain embodiments, the first functional group includes reactive groups, protecting groups, hydrophilic groups, hydrophobic groups, lyophilic groups, lyophobic groups, nanoparticles or mixtures thereof.
In certain embodiments, the method further includes: providing said first region of said porous three-dimensional photonic structure with a second surface property by providing a reagent that reacts with said first functional group.
In certain embodiments, the first surface property includes wettability, hydrophobicity, hydrophilicity, lyophobicity, or lyophilicity.
In certain embodiments, the method further includes: providing said first indicator material that selectively fills at least some of the pores of said first region.
In certain embodiments, the first indicator material wicks into at least some of the pores of the first region.
In certain embodiments, the first region is patterned to provide an encrypted message that is not visible until the first indicator material occupies at least some of the pores of the first region.
In certain embodiments, the method further includes: patterning a second region of said porous three-dimensional photonic structure with a second surface property on at least some of the interior surfaces of the porous three-dimensional photonic structure.
In certain embodiments, the photonic structure is an inverse opal structure, a mesoporous silica, a short range order structure exhibiting structural color, a quasicrystal, or mixtures thereof.
A photonic structure having patterned surface properties that allows preferential interaction with certain selected fluids and reagents are described. Such a material can be used to embed desired information through selective wetting of the photonic structure.
In certain embodiments, 3D porous photonic structures patterned with regions of different functional groups that have differential wetting of liquids properties, and a method for producing such a structure by selective addition or removal of functional groups is described. The liquid wetting can cause a visible color change due to a change in effective index contrast.
Generally, a three-dimensional structure having a periodic pattern of higher index refractive material and a lower refractive index material, such as air, can be utilized as a photonic structure. The photonic structure can be tuned to have a size scale and refractive index contrast so that structural colors arise near the visible wavelengths. Generally, to obtain structural colors nears the visible wavelengths, photonic structures having nanometer to micron-scale feature sizes are desired.
As used herein, photonic structures can include structures having long range order (e.g., single crystal photonic crystals, single crystal mesoporous structures, etc.), structures having medium range order (e.g., photonic crystals having many small crystalline domains, mesoporous structures having many small crystalline domains, quasicrystals, etc.) and even short range order (e.g., glasses that have a fixed pore sizes, etc.). In certain embodiments, the photonic structure can provide a structural color. In some other embodiments, the photonic structures can provide change in appearance due to interference effects. Generally, photonic structures are meant to encompass structures that can provide optical effects in the visible wavelengths.
Particularly, when porous photonic structures are involved (e.g., pores having sizes on the order of about tens to hundreds of nanometers, pores in the mesoscale size ranges, etc.), it was conventionally thought that selective or patterned functionalization of the photonic structures would be difficult or nearly impossible as diffusion of etchants or reagents through the pores were likely to occur, washing out spatial contrast in surface properties. Nevertheless, contrary to conventional wisdom, the present disclosure provides photonic structures having patterned surface properties and methods for making such structures.
As shown in
Any suitable 3D, porous photonic structure material can be utilized. In certain embodiments, a porous three-dimensional photonic structure can be utilized, where the photonic structure has at least one higher refractive index material phase and a plurality of pores as the lower refractive index material phase that are interconnected with each other. In certain embodiments, the high refractive index material phase can also contain a plurality of pores that are smaller than the pores forming the low refractive index material. In certain embodiments, pores can have aperiodic arrangement, exhibiting incoherent scattering that can be tuned by selective liquid infiltration. In certain embodiments, a plurality of different high refractive index materials can be utilized to form the higher refractive index material phase. In certain embodiments, a plurality of different high, medium, and low refractive index material phases may be present.
Suitable exemplary porous three-dimensional photonic structures include SiO2 based inverse opals structures. As a non-limiting example, large-area single-crystal inverse opal photonic crystals can be prepared by evaporation-induced coassembly of a monodisperse colloidal suspension of particles (e.g., poly (methyl methacrylate) (PMMA) nanospheres (d˜280 nm)) with a silica sol-gel solution (e.g., prepared from the acid-catalyzed hydrolysis of tetraethyl orthosilicate (TEOS)) onto a substrate. Thereafter, the colloidal template particles can be removed (e.g., by calcination for 8 h at 500° C.). The resulting porous inverse-opal photonic crystals generally have a face-centered-cubic geometry. Such a technique is described in PCT/US09/55044, which is incorporated by reference herein in its entirety.
Alternative techniques exist to make any desired three-dimensional photonic structure, as would be readily apparent to one of ordinary skill in the art. Other techniques include sequential formation of a colloidal template followed by infiltration, polymerization induced by interference patterns produced by laser, direct laser writing (e.g. by two-photon polymerization), glancing-angle deposition, stacking of 2D photonic structures by micromanipulation, etc. Selection of how and what photonic structure to form will be dependent on the ease of fabrication, desired photonic or stop bandgap, desired degree of long range order, and the like. For example, if a long range order is desired, co-assembly technique described above may be favored over the sequential formation of a colloidal template followed by infiltration because unlike post-infiltrated colloidal inverse opals, photonic structures formed via the above-mentioned co-assembly technique can provide a near single-orientation structure with the (110) direction pointed in the growth direction.
In certain embodiments, suitable three-dimensional photonic structure materials can selectively be provided with desired surface properties. Desired surface properties include wettability, hydrophobicity, hydrophilicity, lyophilicity, lyophobicity, and the like.
Desired surface properties can be provided in any number of techniques, including functionalization by formation self-assembled organic monolayers (SAMs) on the surfaces of the porous structure, functionalization by etching away materials on the surface of the porous structure, deprotection or protection of moieties present on the surface of the porous structure, reaction of molecules carrying desired functional groups with reactive groups on the surface of the porous structure, attachment of nanoparticles, and the like. Generally, “functional group” is meant to encompass any specific surface property, and “functionalized photonic structure” is meant to encompass a porous structure having desired surface properties, whether through additional pendant groups or through reaction or etching away of existing moieties on the surface of the pores, or through surface adsorption.
For example, inverse opal SiO2 can be selectively surface-functionalized when exposed to alkylchlorosilanes in solution or in the vapor phase, a class of compounds which are widely commercially available. The chlorosilane moiety can react with an exposed polar surface group of the inverse opal SiO2 walls, replacing it with the organic group attached to the chlorosilane. In certain embodiments, the native surface groups of the photonic materials can also be used with or without modification as an end-functionality.
Returning to
In certain embodiments, the functional groups may be chosen based on particular affinity to certain materials, such as specific solvents, vapors, chemical reagents, biological reagents, metals, nanoparticles, and the like.
In certain embodiments, the functional groups can be chosen based on particular repulsion to certain materials, such as specific solvents, vapors, chemical reagents, biological reagents, metals, nanoparticles, and the like.
In certain embodiments, the functional groups can be chosen based on reactivity of the functional groups (with the fluid itself or something suspended in the fluid). In certain embodiments, the functional groups may be non-reactive while in other embodiments, the functional groups may be reactive.
In certain embodiments, desired functional groups can be provided through a number of different techniques. Suitable techniques include cleaving off certain protecting groups using etchants, reactants, radiation, plasma and the like, and/or exposing desired functional groups.
Other suitable techniques involve reaction of reactive functional groups with other introduced functional moieties to provide new desired functional groups. In certain embodiments, the reactive functional groups can be obtained after cleaving off certain protecting groups, as described above, from the surfaces of the porous three-dimensional photonic structures, and via subsequent exposure of these newly-formed functional groups of the porous three-dimensional photonic structures to reactive groups, and the like.
Other techniques involve formation of a self-assembled monolayer on the surface of the porous three-dimensional photonic structure through covalent, ionic, or van der Waals interactions with the surface, possibly following the “cleaving” step above. Other functionalities can also be added through grafting of additional compounds/molecules to a self-assembled monolayer, or adsorbing or growing materials on top of a self-assembled monolayer. New surface functionality can also be achieved by adsorption of mixed layers of two or more species.
In step 130, selected areas of the photonic structure can be masked. A suitable mask can include any material (e.g., rubbery) that can provide a good seal to the surface of the photonic structure with or without the application of pressure. Moreover, the suitable mask should also be easily removed from the photonic structure surface. Exemplary masking materials form good contact with the photonic structure surface so that the underlying regions are fully shielded during the exposure process. In some instances, the mask can be clamped or secured to the surface using external forces to ensure full and sealing contact with the photonic crystal. In addition, they are of sufficient material integrity that do not flow or change shape upon exposure to etching medium, which can result in the undesired infiltration of the porous network of the photonic structure. Suitable masks include, for example, polydimethylsiloxane, polyurethane, and the like.
In some embodiments, step 130 can also be carried out using a mask deposited from fluid (e.g. spin-on polymers, photoresist, etc.) when the surface chemistry of the photonic structure is first adjusted so as to resist infiltration of the liquid/solvent. Alternatively, to allow for nanoscale feature patterning the photonic structure could be infiltrated first with a selectively etchable material (e.g. photoresist). After the material is selectively patterned and removed in certain areas, the surfaces chemistry of the newly-exposed photonic structure can be modified according to step 120. Subsequently, the remaining material (e.g. photoresist) could also be removed.
Thereafter, steps 120 and 130 can be repeated as many times as desired.
Many different embodiments can be envisioned. For example, step 120 can involve a multi-step process where the desired functional groups are provided through multiple etching, reaction, dissolution, and the like.
In certain embodiments, the photonic structure may already be provided with suitable functional groups and step 130 may be carried out before 120.
In certain embodiments, one or more regions of the photonic structure can be selectively provided with reactive functional groups (e.g., hydroxyl, amine, aldehyde, carboxylic acid, sulfonic acid, thiol, nitrile, isothiosulfate, enzyme, antibodies, DNA, RNA, and the like). For example, by masking one or more desired regions of the photonic structure (i.e., carrying out step 130) and exposing the unmasked portions to reagents or etchants (e.g., oxygen plasma, radiation, reactive ions, reactive chemical species, and the like), reactive functional groups can be formed.
Thereafter, in certain embodiments, subsequent reactions can be carried out with the reactive functional groups to provide additional, functional groups. For example, vapors or solutions of certain reactants (e.g., different alkylchlorosilane, organosilane, organothiol, DNA, antibodies, and the like) can be introduced, allowing the reactants to be grafted onto the reactive functional groups.
In certain embodiments, the reactive functional groups that remain after etching/exposure to reactive groups can themselves be used without further reactions in desired applications. Furthermore, the native surface chemistry of the photonic crystal material can be used with or without modification as a functionality in the final product.
In certain embodiments, different regions can be provided with identical functional groups. However, depending upon the density or amount of functional groups present on the porous surface, different fluids may be attracted to the respective regions having different density or amount of the functional groups. For example, a first region having 100% coverage of hydrophobic functional group may entirely repel alcohol mixed with water whereas a second having 10% coverage of hydrophobic functional group may attract the same alcohol mixed with water.
In certain embodiments, the functional groups can provide a desired level of “contrast” between the type of materials the functional groups are attracted to or repulsed by. “Contrast,” as used herein, refers to the degree of differentiation the respective regions with desired surface properties can make with respect to similar fluids. In certain embodiments, regions having a high contrast may be able to differentiate between two liquids that contain mixtures of very chemically similar fluids, such as alcohols containing differing amounts of water. An exemplary photonic crystal having regions of high contrast may be able to differentiate between a first mixture containing 95% ethanol and 5% water from a second mixture containing 90% ethanol and 10% water. In other embodiments, regions having a low contrast may be able to differentiate between two liquids that contain mixtures of very chemically different fluids, such as organic solvents and alcohols.
In certain embodiments, the differing regions can be patterned with different degrees of lateral resolution. For example, if small microscopic patterns are desired, the various regions can be provided with a high resolution where the boundary between the regions having different surface properties can be sharp. In some other embodiments, where a gradual shift is desired, the differing regions can be patterned so that the boundary between the regions gradually changes in the lateral direction.
In certain embodiments, the order in which the different functional groups are added can be optimized to produce different global surface properties in the channels of photonic structure. For example, it is observed that differences in wetting properties and contrast between areas of different functionality are achieved depending on whether the functional groups are added starting with the largest surface groups and ending with the smallest groups or in the reverse order. For example, if molecules having long and bulky functional groups are first added, there may be sufficient space in between the attached functional groups to allow further addition of molecules having smaller functional groups. In contrast, if molecules having short and compact functional groups are first added, the molecules may be too compactly added onto the surface and not allow further addition of molecules having larger functional groups. As another example, if small molecules are first added and contain large number of defect sites that allow addition of molecules having large functional groups, insertion of those larger functional groups may have a significant impact on the overall properties as the later added larger functional groups may mask the functional groups of the earlier added smaller molecules.
In certain embodiments, the functional groups can also be selectively modified or even completely removed, exposing the native surface chemistry (e.g. SiOH for silica) through longtime exposure to reactants or etchants (e.g., O2-plasma, piranha cleaning solution, radiation, reactive ions, etc.), allowing the photonic structure to be recycled and provided with new patterns of different functional groups. Additionally, incomplete removal of a functional group, with or without subsequent application of step 120 to graft a new functionality to what remains, can be used to create new surface functionalities.
In certain embodiments, the functional groups may be completely removed, by for example, flood exposure of the structure to an etching agent. Thereafter, steps 120 and 130 can be repeated as described the above with arbitrarily different masks and functional groups, making the photonic structures fully re-writable.
As noted above, it was conventionally thought that selective or patterned functionalization of inner surfaces of porous three-dimensional photonic structures would be difficult or nearly impossible when utilizing air as the low refractive material as diffusion of etchants or reagents through the pores were likely to occur. Nevertheless, contrary to conventional wisdom, by carefully controlling the etching and/or deposition conditions as described herein, the present disclosure provides photonic structures having patterned surface functional groups and methods for making such structures.
Without wishing to be bound by theory, reagents and or conditions (e.g., chemicals, plasma power, UV power, etc.) can be selected so that the vertical diffusion (e.g., along the z-axis direction in
In certain embodiments, lateral and vertical diffusion for the particular porous three-dimensional photonic structure is controlled so that the functional groups are distributed uniformly on substantially all of the interior surfaces of desired regions of the photonic structures.
In some other embodiments, lateral and vertical diffusion for the particular porous three-dimensional photonic structure is controlled so that the functional groups are located on certain sides of the pores (e.g., bottom portion, etc.).
One non-limiting surface patterning technique is illustrated in
The entire structure is functionalized by exposure to vapors of a functional group (e.g., chlorosilane with an attached organic functional group, R). Particularly, the inner pore-surfaces of the photonic crystal (PC) (e.g., SiO2) can be functionalized by exposure to a molecule containing a desired functional group (e.g., an alkyl chlorosilane with a non-wetting organic group, SiCl3R) to obtain the structure shown in
Exposure to an etchant (e.g., oxygen plasma) through a removable mask (e.g., PDMS slabs sealed to the surface under pressure, such as a clamp, that can be readily peeled off after etching without damaging the structure) can selectively modify the surface only in the unprotected regions. For example, oxygen plasma can etch organic functional groups and add polar oxygen species (e.g., ROH, RCOOH, RCOH etc., referred to hereafter collectively as ROH for simplicity) to the surface. The resulting structure is shown in
Exposing the now patterned structure to vapors of a second functional group containing material (e.g., second alkyl chlorosilane, SiCl3R′) adds a new functional group to surface sites that are occupied by these reactive oxygen species and not already occupied by a non-reactive organic group (e.g. in areas protected by the mask in the previous step). As shown in
Further plasma-etching through another mask with a different pattern (see
This process represents an example of steps 120 and 130 which can be repeated n times to produce (n+1) different surface chemistries. Different chemistries are applied by adding new chlorosilanes or adjusting the etching or chlorosilane exposure conditions to produce mixed monolayers or monolayers containing grafted organic groups originating from different chlorosilanes.
An inverse opal structure can be recycled and re-written through flood exposure of the structure to oxygen plasma for long time, removing organic monolayers and restoring a polar functional group throughout the structure. The above procedure can then be repeated with arbitrarily different masks and functional groups.
In certain embodiments, additional materials that enhance the optical response (e.g., enhance color contrast) can be incorporated into the photonic crystal. For example, nanoparticles (e.g., gold nanoparticles, silver nanoparticles, carbon-black nanoparticles, quantum dots, dyes) can be incorporated into the non-porous regions of the photonic crystal during growth, which in turn may enhance the optical response of the photonic crystal (see
Incorporation of materials such as gold nanoparticles can allow for the tunability of color depending on the gold nanoparticle concentration. In addition, an optical structure that has an angle dependent structural color from the inverse opal structure as well as an angle-independent plasmonic color from the gold nanoparticles can be obtained.
In certain embodiments, after a photonic crystal containing gold nanoparticles is formed as described above, additional growth of the nanoparticles can be carried out to further enhance the optical response of the photonic crystal. For example, as shown in
In yet another embodiment, selective growth of the nanoparticles can be carried out to further enhance the optical response in only certain regions. For example, as shown in
In certain embodiments, as shown in
For example, the photonic crystals can be functionalized with varying amount of R1 and R2 by preparing a mixture containing the desired relative amounts of R1 and R2, exposing the photonic crystals to the mixture or to the vapors of the mixture. In certain embodiments, the photonic crystal can be exposed two vapors of a first liquid containing a predetermined amount of R1 groups and a second liquid containing a predetermined amount of R2 groups. Adjusting the relative concentration of molecules containing R1 and R2 groups in the respective liquids can alter the relative density of groups on the surface of the photonic crystal.
In certain embodiments, photonic crystals functionalized with more than one functional groups in an appropriate ratio of the functional groups can be utilized to determine the amount of liquid 1 relative to liquid 2 in a mixture of liquids 1 and 2. For example, if R1 groups have greater affinity for liquid 1 and R2 groups have greater affinity for liquid 2, photonic crystals functionalized with greater amount of R1 may allow a mixture containing 95% liquid 1 and 5% liquid 2 to infiltrate whereas a mixture containing 90% liquid 1 and 10% liquid 1 may not be able to infiltrate the photonic crystal.
In certain embodiments, a photonic crystal that has a varying amount of two or more functional groups across the lateral dimensions of the photonic crystal (e.g., certain patterned regions, etc.) may provide a combinatorial approach to identifying unknown solvents. For example, a photonic crystal may have along the x-direction regions that have been functionalized with increasing amounts of R2 groups and along the y-direction, regions that have been functionalized with increasing amounts of R3 groups to form an array of photonic crystal regions that have been functionalized with known and differing amounts of R1, R2, and R3 functional groups. Each of these areas may attract certain mixture of liquids.
In certain embodiments, in addition to controlling the surface chemistries of the pores of the photonic crystal to control the infiltration of liquids (and thus the colorimetric response to liquids), the size of the pores can be utilized as yet another parameter to further fine-tune the wetting selectivity of liquids into the photonic crystal.
When a liquid front propagates through the pores, there is a free-energy tradeoff between the favorable wetting of the solid surface and the unfavorable creation of liquid-air interface. Hence, for a liquid to propagate through the structure, it must overcome an activation barrier. Particularly, many photonic crystals contain a re-entrant geometry where a liquid traversing through the pores of the photonic crystal expands the most. In these regions, the activation barrier can be the highest, which can be calculated for many different photonic crystal structures.
Taking an inverse opal structure as an example (see
As shown, θc can be estimated by measuring the contact angle of the infiltrating liquid with a flat substrate. φ0 can be calculated for a number of different structures, including and not limited to inverse opal structures, body-centered cubic, simple cubic structures that can be formed by forming similar “neck” regions as shown in
In certain embodiments, a photonic crystal with uniform surface chemistry has the capacity to colorimetrically differentiate liquids based on differences in θc of less than 10°, or less than 5°, or less than 2°, or less than 1°. Taking ethanol-water mixture as an example, an inverse opal photonic crystal with uniform surface chemistry with the ability to differentiate liquids based on differences in θc less than 5° corresponds to the ability to differential just 5% changes in the relative amounts of ethanol and water (i.e., between 90% and 95% ethanol in water).
Accordingly, a photonic crystal having a long range order with well-defined pore sizes and well-defined re-entrant geometry have a significant advantage over that of a structure that utilizes a random network of pores having different sizes. In a random network of pores, there is a high likelihood that an infiltrating liquid will find a nearby pore that has sufficiently large enough pore size to continue its path along the network of pores. In contrast, in a perfectly symmetric photonic crystal structure with exactly the identical pores throughout, the transition between a photonic crystal that is completely impervious to liquid infiltration (e.g., displaying iridescent color) and one that is completely infiltrated (e.g., transparent, showing the color of the underlying substrate) at equilibrium can occur over an infinitesimally narrow range of liquid contact angles (θc) because the free-energy landscape associated with fluid percolation through the pores will be the same at every identical unit cell.
Fabricated photonic crystals do display some degree of both short-range (<mm scale) and long-range (>mm scale) variations in the pore sizes. However, these variations can be taken into account to provide further control in the wetting behavior. For example, an inverse opal structure having an average neck angle of 20° can be fabricated with some variation in the neck angles.
In certain embodiments, vertical gradients of wettability can be generated, which in turn can provide added benefits of enhanced optical response. Vertical gradient of wettability can be formed by changing the number and/or type of functional groups along the vertical (i.e., thickness) direction of the photonic crystal film. As shown in
In certain embodiments, the vertical gradient described above can be provided to a photonic crystal that increases its thickness along the lateral dimension. For instance, assuming a photonic crystal that changes its thickness from only four layers to six layers along a lateral dimension (e.g., left to right). If the vertical gradient is provided so that the photonic crystal uniformly functionalized with R1 groups is treated to remove the R1 groups from only the top four layers of the photonic crystal followed by functionalization with R2 groups in only those removed regions, then the left portion of the photonic crystal will have its entire thickness functionalized with R2 whereas the right portion of the photonic crystal will have its first four layers functionalized with R2 groups with the bottom two layers functionalized with R1 groups. In practice, the right portion of the photonic crystal may gradually change from the top to bottom from a predominantly R1 functional group to a predominantly R1 functional group. Then, as shown in
As discussed above, if the infiltrating liquid provides a refractive index match with the photonic crystal, filling of the photonic crystal can lead to a transparent material. In that case, the region of the photonic crystal near the left edge in
Even if the infiltrating liquid does not provides a refractive index match with the photonic crystal, the different regions will exhibit different colors due to the differences arising from the filled and unfilled layers.
Accordingly, as schematically shown in
In certain embodiments, as shown in
This particular embodiment possesses two important advantages with respect to the colorimetric differentiation of liquids: i) the minimum colorimetrically discernable difference in wettability can be smaller for vertical gradients than for uniformly functionalized photonic crystals (for the same short-range variability in the neck-angle, φ0); and ii) a single vertical gradient can produce many distinct patterns in many different liquids. Vertical gradients allow enhancement of the colorimetric selectivity, not by decreasing the range of θc over-which partial infiltration patterns are observed, but by transforming partial infiltration patterns to a form that become easy to mutually distinguish visibly (i.e. have countable differences).
In certain embodiments, a large numbers of photonic crystal particles can be fabricated, followed by any of the functionalization discussed above. While the previous disclosure focused on forming large sheets of photonic crystals, it is within the scope of the present invention to form much smaller particles of photonic crystals, functionalizing the photonic particles, dispersing the functionalized photonic particles in a suitable fluid, and utilizing the mixture as a photonic crystal applicator liquid, such as a photonic crystal paint to be applied on any desired surfaces. Accordingly, whereas the discussion above focused on forming photonic crystals on a specific substrate shape, the photonic crystals can be applied in any arbitrary shape that is desired without being limited to the particular shape and geometry of the underlying substrate.
In certain embodiments, two or more paints containing photonic crystal particles that have been functionalized with different functional groups can be utilized. For example, a first paint can include photonic crystal particles that have hydrophobic functional groups whereas a second paint can include photonic crystal particles that have hydrophilic functional groups. The two different paints can be applied in any manner, such as on different lateral locations or on top of each other to mimic vertical gradient functionalization. Any number of different paints, each having different photonic crystal particles having predetermined functionalities that are different from each other can be envisioned.
Taking the example of applying a sign with road sign first with a first photonic crystal paint having hydrophilic functional groups followed by a second photonic crystal paint having hydrophobic functional groups painted with the words “CAUTION: WET,” the hydrophilic particles would become saturated with water when raining, and lose their color, while the hydrophobic particles would remain the original color. As a result, the sign would change to exhibit the words “CAUTION: WET” when it rains or the environment is heavily saturated with water.
In some embodiments, photonic crystal particles can be fabricated and dispersed in a paint. Thereafter, the photonic crystal particles can be applied to a surface and any of the surface functionalization techniques discussed above (e.g., lateral patterning, vertical gradient functionalization, etc.) can be carried out.
Numerous different methods for forming photonic crystal particles can be envisioned. For example, colloidal co-assembly can be applied to structured surfaces, such as parallel grooves and holes, to produce hierarchically-structured inverse opals.
In addition to a microstructure of regular bricks and hexagons, a microstructure which may be more practical and useful is an array of inverted pyramid cavities. Such surface structures are relatively easy to produce over large areas, and may allow for easier release of the particles from the mold. In certain embodiments, a large sheet of microstructured cavities for the colloidal co-assembly suspension to be cast into, such as shown in
The present disclosure provides methods for patterning many different surface functional groups in 3D porous structures. The technique can be used to create technology serving a vast array of purposes. Through a simple, repeatable process, fluids can be confined and manipulated in a structurally homogeneous material. Once selective infiltration of fluids is achieved, these fluids themselves can also be used as a carrying medium or mask for further functionalization reagents.
The methods described herein will readily be apparent to one of ordinary skill in the art to be applicable to a wide variety of porous media, such as mesoporous ceramics and silica gels used in thin-layer chromatography, making it suitable to a host of different applications.
Numerous different applications are envisioned to arise from the present disclosure.
Encryption of Optical Messages:
One of the applications of this technology that may be possible is in a multilevel document and art authentication and message encryption. Secret messages can be encoded in the structure through its local surface functionality. As the surface functional groups considered here have no direct effect on the optical properties of the photonic structure, no message would be viewable until the photonic structure is immersed in a solvent. Depending on the number of different functional groups used, different solvents could reveal different messages, with only the intended recipient knowing the correct solvent in-which to read the message. Upon solvent evaporation, the encoded message disappears again returning to the original appearance of the colored region.
Accordingly, no message may be visible in air, while n messages may be visible from immersion in n-different solvents with a sample having n+1 different pore-functionalities. More messages can be encrypted with relatively few functional groups using controlled mixing of functionalities, either by grafting or spatial mixing, or using wicking from designated starting points through selectively connected domains to define multiple distinguishable messages in the same sample.
Colorimetric Indicator for Liquids Based on Wetting Properties:
A photonic structure strip, able to colorimetrically distinguish between liquids with different wetting properties (e.g, various alcohols, acetone, water and their mixtures), can be very effective as a field-test for the identification or authentication of liquids. This could be useful, for example the identification of small spills or unlabelled/abandoned containers that are frequently found in communal laboratory environments. The strip would give an instant optical indication of the type of organic liquid present (for example, differentiating ethanol or isopropanol from their lethal counterpart, methanol), as pH paper does for pH. As wettability is a generic property of liquids, this type of field test could be tailored to give colorimetric determination of the composition of liquids across a wide variety of classes (e.g. identifications of unlabeled/spilled laboratory solvents, in-situ identification of liquid explosives, diagnostics for bodily fluids such as blood or urine based on their wetting properties, etc.). This technology could also be useful for the authentication of liquid formulations again forgery, which could be applied in a variety of industries (e.g. liquid formulation pharmaceutical products, field test for the validation of the grade and quality of engine fuels, liquors, etc.).
Invisible Reconfigurable Microfluidic Channels:
As this material is able to confine liquids in areas of compatible surface functionality, multiple channels can be written on one chip purely through the definition of the surface chemistry. Propagation through the channels can occur without external pumping through capillary processes (i.e. wicking). As the channels are defined through surface functional groups only, they can easily be erased and rewritten in a different configuration.
Microfluidic/Chromatographic Channels with Fixed Configurations and Patterned, Reconfigurable Functionality:
Material precursors can be selectively infiltrated only into regions of compatible functionality. After curing or solidification, permanent channels (where the material precursor did not infiltrate) are defined in the microporous structure. These channels can be used for applications where a microporous medium integrated into microfluidic channels is desired (e.g. intra-microfluidic chromatography columns for chemical separation). This also can be a useful technique for defining channels containing a porous medium with well-defined periodicity.
Extension to Other Porous Inorganic Media:
This patterning technique can be applied to any interconnected porous medium (where all or some pores are plasma/fluid-accessible) that has compatibility with oxygen plasma or similar etching technique and the ability to absorptively interact or to react with functional monolayers. This could be extended beyond silica inverse opals to mesoporous materials (silica, titania etc.), inorganic xerogels and aerogels such as those used in thin layer chromatography etc., and may find further uses in those materials.
Extension to Other 3D Patterning Techniques:
The present patterning technique in a three-dimensionally porous structure could be varied for example by applying the self-assembled monolayers through liquid reactions. Monolayers may be able to be selectively added rather than removed, particularly in materials with smaller pores, owing to low diffusion through the porous network.
Time Dependent Color Change to Determine Volatility:
The evaporation of infiltrated liquid can produce a change in color, which can provide a simple method for determining the evaporation rate of a fluid.
Selective Wetting to Detect Particle (e.g., Protein) Adsorption:
If particles such as proteins, viruses, colloidal particles and the like adsorb onto the photonic crystal surface, this can effectively change the pore size, which can in turn change the type of fluids that can infiltrate the photonic crystal as well as the colorimetric response. Hence, the photonic crystals can be useful as a diagnostic tool to determine the presence of any known particles in an infiltrating liquid. Specificity can be added by functionalizing the surfaces with known functional groups that bind to a specific class of materials (e.g. anti-bodies, particle tags, etc.).
Enantioselective Colorimetric Indicator:
Chiral liquids can change its contact angles depending on the amount of S and R molecules that are present. Accordingly, the photonic crystal of the present disclosure can serve as a fast diagnostic to determine the relative amount of S and R molecules inside a fluid.
The applications listed here represent the tip of the iceberg of the new technologies that may be possible in areas such as authentication and security, encryption, fluid-manipulation and simple diagnostics.
To study the wetting interfaces present in the patterned photonic structures, channels of SiOH functional groups were patterned into a photonic crystal (PC) that was functionalized uniformly with (1H,1H,2H,2H-perfluorooctyl)silyl (13FS) groups. The pores of the 13FS-functionalized PC were found to be sufficiently nonwetting to resist infiltration of most solvents, including pre-cured PDMS (Sylgard 184). By selective infiltration of PDMS into the ROH-functionalized channels followed by thermal curing, detailed measurements of the resolution of the wetting-non-wetting interface was possible.
As shown, interfaces are well defined over a large scale and the transition between complete infiltration and non-infiltration can be as small as 10-20 periods (5-10 μm). In particular, the resolution was estimated by comparing the dimensions of the PDMS mask to the final infiltration interface using optical and scanning electron microscopy.
To demonstrate the encoding capabilities of the photonic structure with multiple functional groups, SiO2 inverse opals were patterned with combinations of ROH surfaces and those treated with four different alkylchlorosilanes with decreasing hydrophilicity: trimethylchlorosilane (TMS), (3,3,3-trifluoropropyl)trichlorosilane (3FS), (n-decyl)trichlorosilane (DEC), and 13FS.
When a solvent penetrates the pores of a PC, the refractive index-contrast is reduced and the optical path-length between periods increases, resulting in a redshifted and diminished reflection peak for a PC of finite thickness. Spectra of regions with the three different functional groups are shown in
The 13FS-functionalized opal shows little shift in all three solvents (
This indicates that while water does not enter either TMS of 13FS-functionalized areas, ethanol enters the TMS areas while not entering the 13FS area.
The same result as with ethanol was observed in hexane (and liquids with lower polarity) and un-cured PDMS resin.
With PDMS, selective liquid infiltration was also verified with SEM after curing.
To demonstrate the concept of document authentication and multilevel message encryption, the word “INK” was patterned with 13FS functional groups. Moreover, a letter “W-” having TMS functional groups was encrypted in front of the word “INK”.
The resulting structure shows no distinguishable pattern in air (see
When exposed to ethanol, the structure shows “INK” due to the contrast between 13FS-TMS/ROH regions as shown in
When exposed to water, “W-INK” appears due to the contrast between 13FS/TMS-ROH regions, as shown in
The more functional groups in the message, the more highly specific the solvent choice must be and also, the more different solvent-specific messages can be simultaneously coded into the same material.
Using this approach, a different text in the sample can be observed each time the wettability of the solvent passed the threshold for infiltration of each functional group.
As shown in
As shown in
As shown in
As shown in
For applications in authentication, one could mark the document/package/art with a small piece of the photonic crystal and require several specific, different patterns to appear in several different solvents (or mixtures) for validation of the package.
By employing the similar principle as that of Example 4, photonic crystals can also be used as a cheap, reusable pH-paper-like indicator for organic solvents. Here, we demonstrate that differences between different surface functionalities can be adjusted to match subtle differences between the wettabilities of otherwise similar liquids. Below we demonstrate a strip that visibly distinguishes between different alcohols, including methanol and ethanol.
While 3FS-areas can distinguish between water (no infiltration) and most organic solvents (infiltration), DEC-areas resist infiltration to water and acetone and total infiltration by isopropyl alcohol. The 13FS-stripe is not infiltrated by any of these solvents.
This type of functionalized PC-strip, along with pH paper for acids and bases, would be very effective in the identification of small spills or unlabelled/abandoned containers that are frequently found in a communal cleanroom environments, where alcohols and acetone are commonly used organic solvents. Laboratories commonly using a larger number of solvents would require a W-Ink indicator having more encoded functional groups. The samples shown in
Owing to its ability to allow the infiltration of solvents in a selective manner, a selectively functionalized photonic structure also has potentially interesting applications in microfluidics.
Fluidic channels containing a highly regular microporous network with modifiable chemical functional group can be defined in two different ways, denoted here as “visible channels” and “invisible channels”.
Fluid transport through the channels can occur through capillary forces (wicking) or through active pumping.
Visible channels were formed by patterning a homogeneous inverse opal sample with 13FS functional group in the channel regions and ROH functional group outside. Submerging the sample in un-cured PDMS resulted in infiltration of the ROH regions while the 13FS regions remain un-infiltrated (see
Although only one particular functionality is shown in this specific example, similar to the previous examples, channels with many different functionalities can be provided on the same chip allowing for selective transport of different solvents in specially designated channels.
Since 13FS functionality in the pores of PC allows for its resistance to infiltration of most solvents, it can be used to define the walls of “invisible” channels.
Hence, “invisible channels” are defined using chemical functionality for lateral confinement. 13FS-functional groups, resisting infiltration by most solvents, are used in the channel walls. While they lack the longevity and robustness against chemical contamination of the visible channels (i.e. it is more difficult to remove contaminants without removing the channel functionality), they have the advantage that they can be both chemically and configurationally repatterned, through the same erasing-rewriting procedure described above.
Gold nanoparticles were synthesized and added to the colloidal suspension and silica precursors prior to deposition, to create hierarchical inverse opal structures via a three-phase co-assembly method.
All glassware used in these preparations was thoroughly cleaned in aqua regia (3 parts HCl, 1 part HNO3), rinsed in triply distilled H2O, and oven-dried prior to use. The following stock solutions were prepared from triply distilled H2O: 1.0 mM HAuCl4 (Sigma Aldrich), 38.8 mM sodium citrate (Sigma Aldrich).
In a 250 mL round-bottom flask equipped with a condenser, 150 mL of 1 mM HAuCl4 was brought to a rolling boil with vigorous stirring (magnetic stir bar) in an oil bath. Rapid addition of 15 mL of 38.8 mM sodium citrate to the vortex of the solution resulted in a color change from pale yellow to burgundy. Boiling was continued for 10 min; the solution was removed from the oil bath, and stirring was continued for an additional 15 min. The solution was then allowed to reach room temperature prior to use.
The nanoparticle solution was then centrifuged, the solvent removed, and varying amounts of the remaining pellets were redispersed into a solution containing monodisperse colloidal suspension of particles (e.g., poly (methyl methacrylate) (PMMA) nanospheres (d˜450 nm)) with a silica sol-gel (e.g., prepared from the acid-catalyzed hydrolysis of tetraethyl orthosilicate (TEOS)) prior to evaporative deposition of inverse opal photonic crystals onto a substrate. Thereafter, the colloidal template particles can be removed (e.g., by calcination for 8 h at 500° C.). The resulting porous inverse-opal photonic crystals generally have a face-centered-cubic geometry. Such a technique is described in PCT/US09/55044, which is incorporated by reference herein in its entirety.
For the photonic crystals produced with the gold nanoparticles,
To demonstrate the selective growth of the nanoparticles to further enhance the optical response in only certain regions, a photonic crystal was patterned with a letter “M” by exposing the regions outside of the letter “M” using oxygen plasma. The inverse opal was previously treated with a hydrophobic silane (tridecafluoro-1,1,2,2-tetrahydrooctyl)-trichlorosilane (Gelest Inc.) by vapor exposure in a desiccator under vacuum overnight. Then, a gold nanoparticle growth solution was introduced which wets only the hydrophilic portions of the photonic crystal. As shown in
Mixed 13FS:DEC monolayers were prepared by exposing photonic crystals to vapors from a liquid-liquid mixture of 13FS- and DEC-trichlorosilanes. As shown in
Ethanol-water mixtures of varying concentration was prepared to produce a continuum of surface tensions (and values of θc). 13FS-functionalized photonic crystals display an unfilled state in all water-ethanol mixtures (including 100% EtOH) and DEC-functionalized photonic crystals display a filled state in EtOH concentrations larger than 85% (as enforced by quality control).
A photonic crystal having a vertical gradient of surface functionality that changes from p-tolyl to 13FS as a function of thickness was prepared. As shown in
In other words, while the photonic crystal functionalized with a mixture of p-tolyl and 13FS sample can show the same pattern in 90% EtOH and n-decane (left column of FIG. 10), these liquids can show distinct patterns in a photonic crystal functionalized with a mixture of DEC and 13FS sample.
By building arrays of photonic crystals, each functionalized with different functional groups, it may be possible to extract even more specific information, by comparing the combinations of patterns produced by the array.
For example,
Using intrinsic contact angles measured from DEC-functionalized flat surfaces, the expected equilibrium filling states were derived from bond connectivities using a numerical percolation simulation. The model considered an fcc lattice of pores, 30 close-packed layers thick with a large lateral area (104 unit cells). Neck-angles were randomly assigned to each nearest-neighbor connection according to a normal distribution. Inputting θc and starting with a completely filled top layer, the simulation filled all pores with paths of inter-pore fluid-connectivity (i.e. where φ0>θc) connecting them to the top filled layer. The solid curves in
To verify the correlation between the neck angle and the wetting behavior, the neck angle distribution was characterized from SEM images sampled randomly across each film. The infiltration state from the presence or absence of iridescent color in 80%, 85% and 90% EtOH uniformly functionalized with DEC groups was also determined. These measurements are represented by the isolated points in
Short-range variability in the neck angles is what ultimately limits the selectivity of a photonic crystal's colorimetric response to liquids. Infiltration of a liquid through an photonic crystal with uniform surface chemistry and a random distribution of neck-angles will proceed as percolation through a regular fcc lattice with a bond-connectivity determined by θc. The final equilibrated infiltration state will be a statistical distribution of filled and empty pores over a range of θc determined by the local variance of φ0. To extract a colorimetric selectivity from this continuous distribution of partial filling states, what constitutes “easily visually distinct” color patterns can be determined, which is inherently subjective. In this example, it was chosen to define easily visually distinct patterns as those with countable differences (e.g. each region can only be assigned two possible states). Therefore it was assumed that a user can only designate a region with uniform surface chemistry as being “unfilled” (bright color) and “filled” (transparent, negligible contrast with the underlying substrate).
A maximum fraction of filled pores that defines the colorimetric “unfilled” state and a maximum fraction of unfilled pores that defines the “filled” state was chosen in this example. The colorimetric selectivity (minimum resolvable difference in θc) was defined by the range of θc over-which the filling fraction does not fit into either of these definitions. To extract this range, lower and upper bounds of connectivity were chosen to define the resolution limit of our colorimetric indicator. In estimating of the colorimetric selectivity, the bond percolation threshold that occurs at 12% connectivity for an fcc lattice was chosen as the upper-bound connectivity defining the “unfilled” state. For connectivity below the bond percolation threshold all paths of fluid flow have finite length. This means a sufficiently thick photonic crystal will have completely empty layers at equilibrium, thereby producing color that can be easily distinguished from the filled state.
The onset of the “filled” state was defined by a maximum tolerance of empty pores.
A photonic crystal was functionalized with the more lyophobic group (R1, 13FS). Following a short (<2 min) exposure of the structure to oxygen plasma, some removal of the R1 groups occurred, with the efficiency of removal decreasing with increasing depth. Subsequent addition of less lyophobic groups (R2, DEC) via exposure to SiCl3R2 vapors generated a mixed, graded surface chemistry with an increasing ratio of R2/R1 from the bottom to the top of the photonic crystal.
As a result, as illustrated in
The total thickness of the film varies from only two close-packed layers on the far left to a large number (>20 layers) on the far right, each visible “stripe” representing a region of fixed thickness, having one more layer than the stripe to the left of it. In thinner regions (N<˜10) these stripes are wide enough to be visible by eye (˜0.5-1 mm wide). In the thickest regions very close to the edges, the thickness increases on shorter length-scales and the stripes become harder to resolve. When this sample is immersed in liquid precursors to polydimethylsiloxane (PDMS, Sylgard 184, subsequently cured to allow visualization by SEM), the liquid completely penetrates the first 6 layers (n=6) and the photonic crystal becomes transparent (displaying the grey of the silicon substrate) in regions where N≦6. The SEM cross-sections in
The color displayed by a photonic crystal having N layers, the top n-of-which are filled (n<N), should match the color produced by an empty (N−n)-layer photonic crystal, since the filled regions become transparent, provided there is sufficient index-matching between the fluid and the silica.
In contrast,
Accordingly, if the filling liquid has a similar refractive index as the photonic crystal, adjacent curves in
In certain embodiments, in order to further enhance the visual perceptibility certain regions of the photonic crystal can be selectively oxidized to control the patterns that appear in the different analyte liquids.
In
This application is a continuation application of U.S. application Ser. No. 13/990,324, filed Oct. 2, 2013, which is a national stage application of PCT International Application No. PCT/US2011/061710, filed Nov. 21, 2011, which claims the benefit of the earlier filing date of U.S. Provisional Application No. 61/417,779, filed on Nov. 29, 2010, all of which are hereby incorporated by reference in their entireties.
This work was supported by the United States government under the following grants: Air Force Office of Scientific Research Award FA9550-09-1-0669-DOD35CAP and Department of Energy Award DE-AC05-06OR23100. The government agency has certain rights in this invention.
| Number | Date | Country | |
|---|---|---|---|
| 61417779 | Nov 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13990324 | Oct 2013 | US |
| Child | 15013263 | US |