Manufacture of homopolymers and copolymers of .alpha.-monoolefins

Description

The present invention relates to a process for the manufacture of homopolymers and copolymers of .alpha.-monoolefins of 2 to 6 carbon atoms by polymerizing the monomer or monomers at from 30.degree. to 200.degree. C and pressures of from 0.1 to 200 bars, using a Ziegler catalyst system comprising
(1) A TITANIUM-CONTAINING CATALYST COMPONENT AND
(2) A METAL COMPOUND OF THE GENERAL FORMULA
Me A.sub.m-n X.sub.n
where Me is aluminum, magnesium or zinc, preferably aluminum, A is a hydrocarbon radical of 1 to 12 carbon atoms, in particular alkyl of 1 to 12 carbon atoms, and preferably alkyl of 2 to 8 carbon atoms, X is chlorine, bromine, iodine or hydrogen, preferably chlorine or hydrogen, m is the valency of the metal M and n is a number from 0 to m-1, preferably from 0 to 1, with the proviso that the atomic ratio of titanium from catalyst component (1) to metal (Me) from catalyst component (2) is from 1:0.1 to 1:500, preferably from 1:0.2 to 1:200.
Processes of this type have proved valuable in industrial operation, but still leave scope for a number of minor or major improvements. Thus, for example, the titanium-containing catalyst component (1) to be employed is in many cases unsatisfactory. This is true also of those titanium-containing catalyst components manufactured by starting from a finely divided carrier. It is known that these supported catalysts are in general to be preferred, in industrial operation, to other titanium-containing catalyst components, since they permit smooth operation and give good results. However, this advantage is offset by the disadvantage that the conventional supported catalysts of the type in question here present some hazards in handling and/or are expensive to manufacture, and cause a relatively high degree of pollution of the environment.
It is an object of the present invention to provide titanium-containing catalyst components (1) which are manufactured starting from a finely divided carrier but do not suffer from the above disadvantages, or do so to a substantially lesser degree, and furthermore prove advantageous in operation and in the result of the process, for example which are able to give a polymer which has particularly advantageous morphological properties.
We have found that this object is achieved by means of a titanium-containing catalyst component (1) which is obtained by bringing a particular finely divided silicon oxide carrier into contact with a particular solution formed from a particular alcohol, a titanium trihalide and a magnesium compound, and isolating a solid phase from the resulting dispersion by evaporation.
Accordingly, the present invention relates to a process for the manufacture of homopolymers and copolymers of .alpha.-monoolefins of 2 to 6 carbon atoms by polymerizing the monomer or monomers at from 30.degree. to 200.degree. C and pressures of from 0.1 to 200 bars by means of a Ziegler catalyst system comprising
(1) a titanium-containing catalyst component and
(2) a metal compound of the general formula
Me A.sub.m-n X.sub.n
where Me is aluminum, magnesium or zinc, preferably aluminum, A is a hydrocarbon radical of 1 to 12 carbon atoms, in particular alkyl of 1 to 12 carbon atoms, and preferably alkyl of 2 to 8 carbon atoms, X is chlorine, bromine, iodine or hydrogen, preferably chlorine or hydrogen, m is the valency of the metal M and n is a number from 0 to m-1, preferably from 0 to 1, with the proviso that the atomic ratio of titanium from catalyst component (1) to metal (Me) from catalyst component (2) is from 1:0.1 to 1:500, preferably from 1:0.2 to 1:200. In this process, the titanium-containing catalyst component (1) employed is the solid-phase product (IV) obtained by bringing into contact
(1.1) a finely divided, porous, inorganic oxidic material (I) which has a particle diameter of from 1 to 1,000 .mu.m, preferably from 1 to 400 .mu.m, a pore volume of from 0.3 to 3, preferably from 1 to 2.5, cm.sup.3 /g and a surface area of from 100 to 1,000, preferably from 200 to 400 m.sup.2 /g, and which has the formula SiO.sub.2 . aAl.sub.2 O.sub.3, where a is a number from 0 to 2, especially from 0 to 0.5, and
(1.2) a solution (II) obtained by bringing together
(IIa) 100 parts by weight of an alcohol of the general formula
Z--OH
where Z is a saturated hydrocarbon radical of 1 to 8 carbon atoms, especially a saturated hydrocarbon radical of 1 to 6 carbon atoms, and preferably alkyl of 1 to 4 carbon atoms,
(IIb) from 0.01 to 6, preferably from 0.04 to 3.5, parts by weight (calculated as titanium) of a titanium trihalide, where the halogen may be chlorine and/or bromine, preferably a titanium trichloride, and
(IIc) from 0.01 to 4, preferably from 0.04 to 2.5, parts by weight (calculated as magnesium) of a magnesium compound which is soluble in the alcohol (IIa), especially of a compound which contains halogen and/or carbon, and preferably a compound which contains chlorine and carbon, to form a dispersion (III), with the proviso that the weight ratio of inorganic oxidic material I to titanium in the titanium trihalide (IIb) is from 1:0.01 to 1:0.2, preferably from 1:0.03 to 1:0.15, and the weight ratio of inorganic oxidic material I to magnesium in the magnesium compound (IIc) is from 1:0.01 to 1:0.25, preferably from 1:0.03 to 1:0.15, and the dispersion (III) is evaporated at below 200.degree. C, preferably below 160.degree. C, and above the melting point of the alcohol (IIa) used, until it reaches a dry consistency, i.e. until the solid-phase product (IV) is formed.
In relation to comparable conventional processes, the process according to the invention is distinguished by the fact that, for example, it provides technical and economic improvements. Thus, manufacture of the catalyst is substantially simplified because it can be carried out in one stage, i.e. by a one-vessel process; since, furthermore, it is not necessary to use an excess of the titanium compound, in contrast to conventional processes, there is also a significant improvement in respect of economy and reduced pollution of the environment.
Furthermore, a substantial advantage achievable by polymerizing olefins by means of the new catalysts is that the latter can be obtained in forms which have a relatively high productivity (expressed as amount by weight of polymer per unit weight of titanium) and a relatively low halogen content. The inherently undesirable catalyst constituents in the polymer (titanium and halogen) are then present in such low amounts that they no longer interfere and that their removal -- which would require a separate process step -- is unnecessary. The polymers obtainable by the process of the invention furthermore exhibit other advantageous properties; for example, their morphology conforms to an important range of requirements, namely that the content of pulverulent polymer particles is very low, thereby greatly reducing the hazard of dust explosions, and the shape of the particles is such that not only can the material be stirred easily (an important aspect when manufacturing the polymer), but it also has a high tap density and good free-flowing characteristics, both being advantageous from the point of view of handling the polymers.
The following points of detail of the process of the invention may be noted:
The polymerization process as such can -- taking into account the characteristic features thereof -- be carried out in virtually all the relevant conventional technological embodiments, i.e. as a batchwise, cyclic or continuous process, which processes may be, for example, a suspension polymerization, solution polymerization or dry-phase polymerization. The said technological embodiments, i.e. the technological variants of the Ziegler polymerization of olefins -- are well known from the literature and from practical experience, so that further details are superfluous. The only point still worth noting is that the new titanium-containing catalyst component (1) can -- like corresponding conventional catalyst components -- be brought together with the catalyst component (2) either outside or inside the polymerization vessel, in the latter case, for example, by spatially separate introduction of the components, which may be handled in the form of a suspension (catalyst component (1)) or of a solution (catalyst component (2)). It is also possible, for example, to employ the catalyst component (1) or the combined catalyst components (1) and (2) in the form of particles provided with a wax coating; this method is at times of advantage in dry-phase polymerization processes.
The following points should be noted with regard to the new titanium-containing catalyst component (1):
It is manufactured by bringing a finely divided inorganic oxidic material (I) of the type defined above and a particular solution (II), defined above, into contact with one another, resulting in the formation of a dispersion (III) which is then evaporated until the product has a dry consistency.
Specifically, the procedure which may be followed is to combine the inorganic oxidic material (I), undiluted or dispersed in an alcohol (advantageously an alcohol as defined under (IIa), the dispersion having a solids content of not less than 5 percent by weight) with the solution (II). It is advantageous to keep the batch, after combining the constituents, at from 10.degree. to 160.degree. C, especially from 20.degree. to 120.degree. C, for from 5 to 120 minutes, especially from 20 to 90 minutes, and only then to evaporate the dispersion (III) which has been formed.
The solution (II) can itself be prepared by conventional methods and to this extent exhibits no special features. An advantageous technique has proved to be the preparation of the solution (II) by combining a solution containing the alcohol (IIa) and the titanium trihalide (IIb) with a solution containing the alcohol (IIa) and the magnesium compound (IIc).
The final measure in manufacturing the titanium-containing catalyst component (1) is to evaporate the dispersion (III) to a dry consistency, the resulting solid-phase product (IV) being the new catalyst component (1) according to the invention.
Specifically, the procedure adopted can be one of the conventional methods of evaporating dispersions under gentle conditions, providing the temperatures specified above are observed. This means that it is generally advantageous -- and in the case of relatively high alcohols (IIa) at times essential -- to carry out the evaporation under reduced pressure, the value of which depends on the case in question. As a rule of thumb, the temperature/pressure combination should be selected so that the evaporation process is complete after from about 1 to 10 hours. It is also advantageous to carry out the evaporation under conditions which ensure that the material undergoing treatment remains homogeneous throughout; for example, rotary evaporators have proved suitable for this purpose. Any residual alcohol, for example alcohol bonded by complex formation, is generally not detrimental to the solid-phase product (IV).
The new titanium-containing catalyst components (1) i.e. the solid-phase products (IV) can be employed, within the scope of the process defined at the outset, for the manufacture of the polymers referred to, by the conventional methods employing titanium-containing compounds in the Ziegler polymerization of olefins. To this extent, the process according to the invention thus exhibits no special features and reference may be made to the methods of using such catalysts which are well-known from the literature and from practical experience. It merely remains to record that the process is exceptionally suitable for the manufacture of homopolymers of ethylene, and that where copolymers of ethylene with higher .alpha.-monoolefins, or homopolymers of higher .alpha.-monoolefins are manufactured, such .alpha.-monoolefins are, above all, propene, 1-butene, 4-methyl-1-pentene and 1-hexene. The molecular weights of the polymers may be regulated in the relevant conventional manner, especially by means of hydrogen as the regulator.
As regards the composition of the new titanium-containing catalyst components (1), the following details should also be noted:
(1.1) The inorganic oxidic material (I) to be employed is in general an aluminosilicate or, in particular, a silicon dioxide; it is important that the material should have the requisite properties and should be very dry (no further weight loss after 6 hours at 160.degree. C under 2 mm Hg). Particularly suitable inorganic oxidic materials are those in accordance with stage (1) of the process described in German Laid-Open Application DOS 24 11 735, especially if hydrogels obtained by the process described in German Laid-Open Application DOS 21 03 243 are used as starting materials.
(1.2) The alcohols (IIa) employed may be, for example, methanol, ethanol, the propanols and the butanols. Examples of alcohols which have proved particularly suitable are methanol, ethanol, isopropanol and n-butanol.
The alcohols (IIa) may be employed in the form of individual compounds or of mixtures of two or more of these.
The titanium trihalide (IIb) employed may be a trihalide conventionally used in Ziegler catalyst system, e.g. a reaction product obtained by reducing a titanium tetrahalide by means of hydrogen, aluminum or aluminum-organic compounds.
Examples of particularly suitable compounds have proved to be trichlorides of the formula TiCl.sub.3, as obtained by reduction of titanium tetrachloride by means of hydrogen, and trichlorides of the formula TiCl.sub.3.1/3 AlCl.sub.3, such as are obtained by reduction of titanium tetrachloride by means of metallic aluminum.
The titanium trihalides may be employed in the form of individual compounds or of mixtures of two or more of these.
The magnesium compound (IIc) employed may advantageously be a compound from the following categories:
(A) Magnesium compounds of the general formula Mg(OR').sub.2, where R' is a hydrocarbon radical of 1 to 10 carbon atoms, especially alkyl of 1 to 6 carbon atoms.
Examples of particularly suitable compounds are magnesium methylate, ethylate, n-propylate, i-propylate, cyclohexylate and phenolate.
Magnesium ethylate and magnesium n-propylate are especially suitable.
(B) Complex alkoxides of magnesium with other metals, especially with lithium, boron, aluminum and titanium.
Examples of very suitable compounds are the complex alkoxides of the formulae Mg [Al(OC.sub.2 H.sub.5).sub.4 ].sub.2, Mg.sub.3 [Al(OC.sub. 2 H.sub.5).sub.6 ].sub.2, Li.sub.2 [Mg(OC.sub.3 H.sub.7).sub.4 ], Mg [Ti(OC.sub.3 H.sub.7).sub.6 ] and Mg [B(OC.sub.2 H.sub.5).sub.4 ].sub.2.
(C) Magnesium halides of the general formula MgZ.sub.2, where Z is chlorine, bromine or iodine, especially chlorine or bromine.
Examples of very suitable compounds are magnesium chloride and magnesium bromide.
(D) Complexes of the magnesium halides, mentioned under (C), with alcohols of 1 to 6 carbon atoms, especially with alkanols of 1 to 6 carbon atoms.
Amongst these, the complexes of the formulae MgCl.sub.2.6 C.sub.2 H.sub.5 OH and MgCl.sub.2 .4CH.sub.3 OH are particularly suitable.
(E) Magnesium halide compounds of the general formula MgZ(OR'), where Z is as defined under (C) and R' as defined under (A).
A particularly suitable compound amongst these has the formula MgCl(OC.sub. 2 H.sub.5).
(F) The carriers, containing chemically bonded magnesium, which characterize the subject of German Laid-Open Application DOS 21 63 851, especially manasseite (of the formula Mg.sub.6.Al.sub.2.(OH).sub. 16.CO.sub.3 .4H.sub.2 O), which has been brought to a chlorine content of from 50 to 75 percent by weight by chlorination with phosgene.
The magnesium compounds (IIc) may be employed in the form of individual compounds or of mixtures of two or more of these; they may of course also be compounds formed in situ when preparing the solution (II).
Magnesium compounds to be preferred within the scope of the present invention are those of categories A, C, D and especially F.
The relevant conventional compounds may be used as catalyst component (2); examples of suitable compounds are Al(C.sub.2 H.sub.5).sub.3, Al(C.sub.2 H.sub.5).sub.2 Cl, Al(C.sub.2 H.sub.5).sub.2 H, Al(i-C.sub.4 H.sub.9).sub.3, Al(n-C.sub.4 H.sub.9).sub.3, Al(C.sub.8 H.sub.17).sub.3 and isoprenyl-aluminum.
In conclusion, it should be noted that the titanium-containing catalyst components (1) of the invention, i.e. the products (IV), are sensitive to hydrolysis and to oxidation. To this extent, the relevant conventional precautionary measures for Ziegler catalysts (e.g. exclusion of moisture, and working under an inert gas atmosphere) should be taken when handling these substances.

EXAMPLE 1
Manufacture of the titanium-containing catalyst component (1):
The starting material is a suspension of 20 parts by weight of silicon dioxide (SiO.sub.2, particle diameter 2-40 .mu.m, pore volume 1.6 cm.sup.3 /g, surface area 300 m.sup.2 /g) in 80 parts by weight of methanol.
This suspension is combined with a solution of 3.25 parts by weight of TiCl.sub.3.1/3 AlCl.sub.3 and 5 parts by weight of manasseite (Mg.sub.6.Al.sub.2.(OH).sub.16.CO.sub.3 .4H.sub.2 O), which has been brought to a chlorine content of 72 percent by weight by chlorination with phosgene, in 140 parts by weight of methanol. The resulting suspension is stirred for 15 minutes at 60.degree. C and the resulting solid-phase reaction product is then isolated by driving off the volatiles on a rotary evaporator which is taken to an operating pressure of 20 mm Hg and an operating temperature of 80.degree. C. Analysis of the resulting product, i.e. of the titanium-containing catalyst component (1), shows a titanium content of 2.1 percent by weight and a chlorine content of 13.4 percent by weight.
Polymerization:
0.32 part by weight of the titanium-containing catalyst component (1) is suspended in 20 parts by weight of heptane and 3.3 parts by weight of Al(C.sub.2 H.sub.5).sub.3 (2) are added (these amounts correspond to an atomic ratio of titanium from catalyst component (1) to metal (Me = aluminum) from catalyst component (2) of about 1:206).
The Ziegler catalyst system thus obtained is introduced into a stirred autoclave which is charged with 12 parts by weight (corresponding to about 50% of its capacity) of isobutane. The polymerization is then carried out, whilst stirring, for a period of 2 hours, with the following parameters, which are each regulated to maintain constant values: ethylene pressure = 15 bars, hydrogen pressure = 5 bars, temperature = 100.degree. C. The polymerization is then discontinued by letting down the autoclave.
Details of the product are to be found in the Table which follows.
EXAMPLE 2
Manufacture of the titanium-containing catalyst component (1):
The starting material is a suspension of 1,000 parts by weight of silicon dioxide (SiO.sub.2, particle diameter 40 - 150 .mu.m, pore volume 2.1 cm.sup.3 /g, surface area 330 m.sup.2 /g) in 3,000 parts by weight of methanol.
This suspension is combined with a solution of 163 parts by weight of TiCl.sub.3.1/3 AlCl.sub.3 and 250 parts by weight of mannasseite (Mg.sub.6.Al.sub.2.(OH).sub.16.CO.sub.3 .4H.sub.2 O), which has been brought to a chlorine content of 72 percent by weight by chlorination with phosgene, in 4,000 parts by weight of methanol. The resulting suspension is stirred for 60 minutes at 40.degree. C and the resulting solid-phase reaction product is then isolated by driving off the volatiles on a rotary evaporator which is taken to an operating pressure of 20 mm Hg and an operating temperature of 85.degree. C. Analysis of the resulting product, i.e. of the titanium-containing catalyst component (1), shows a titanium content of 2.21 percent by weight and a chlorine content of 13.1 percent by weight.
Polymerization:
0.38 part by weight of the titanium-containing catalyst component (1) is suspended in 20 parts by weight of heptane and 1.1 parts by weight of Al(C.sub.2 H.sub.5).sub.3 (2) are added (these amounts correspond to an atomic ratio of titanium from catalyst component (1) to metal (Me = aluminum) from catalyst component (2) of about 1:55).
The Ziegler catalyst system thus obtained is introduced into a stirred autoclave whch is charged with 5 liters (corresponding to about 50% of its capacity) of isobutane. The polymerization is then carried out, whilst stirring, for a period of 2 hours, with the following parameters, which are each regulated to maintain constant values: ethylene pressure = 15 bars, hydrogen pressure = 5 bars, temperature = 100.degree. C. The polymerization is then discontinued by letting down the autoclave.
Details of the product are to be found in the Table which follows.
EXAMPLE 3
The titanium-containing catalyst component (1) is manufactured as in Example 2.
Polymerization:
0.026 part by weight of the titanium-containing catalyst component (1) is suspended in 10 parts by weight of heptane and 0.3 part by weight of Al(i-C.sub.4 H.sub.9).sub.3 (2) is added (these amounts correspond to an atomic ratio of titanium from catalyst component (1) to metal (Me = aluminum) from catalyst component (2) of about 1:127).
The Ziegler catalyst system thus obtained is introduced into a stirred autoclave which is charged with 80 parts by weight (corresponding to about 20% of its capacity) of finely divided polyethylene. The polymerization is then carried out, whilst stirring, for a period of 2 hours, with the following parameters, which are each regulated to maintain constant values: ethylene pressure = 27.5 bars, hydrogen pressure = 5 bars, temperature = 100.degree. C. The polymerization is then discontinued by letting down the autoclave.
Details of the product are to be found in the Table which follow.
EXAMPLE 4
Manufacture of the titanium-containing catalyst component (1):
The starting material is a suspension of 10 parts by weight of silicon dioxide (SiO.sub.2, particle diameter 2-40 .mu.m, pore volume 2.0 cm.sup.3 /g, surface area 320 m.sup.2 /g) in 120 parts by weight of ethanol.
This suspension is combined with a solution of 1.63 parts by weight of TiCl.sub.3.1/3 AlCl.sub.3 and 5 parts by weight of manasseite (Mg.sub.6.Al.sub.2.(OH).sub.16.CO.sub.3 .4H.sub.2 O), which has been brought to a chlorine content of 72 percent by weight by chlorination with phosgene, in 40 parts by weight of ethanol. The resulting suspension is stirred for 15 minutes at 60.degree. C and the resulting solid-phase reaction product is then isolated by driving off the volatiles on a rotary evaporator which is taken to an operating pressure of 20 mm Hg and an operating temperature of 80.degree. C. Analysis of the resulting product, i.e. of the titanium-containing catalyst component (1), shows a titanium content of 2.40 percent by weight and a chlorine content of 14.9 percent by weight.
Polymerization:
0.40 part by weight of the titanium-containing catalyst component (1) is suspended in 20 parts by weight of heptane and 1.70 parts by weight of Al(C.sub.2 H.sub.5).sub.3 (2) are added (these amounts correspond to an atomic ratio of titanium from catalyst component (1) to metal (Me = aluminum) from catalyst component (2) of about 1:75).
The Ziegler catalyst system thus obtained is introduced into a stirred autoclave which is charged with 5 liters (corresponding to about 50% of its capacity) of isobutane. The polymerization is then carried out, whilst stirring, for a period of 2 hours, with the following parameters, which are each regulated to maintain constant values: ethylene pressure = 15.5 bars, hydrogen pressure = 5 bars, temperature = 100.degree. C. The polymerization is then discontinued by letting down the autoclave.
Details of the product are to be found in the Table which follows.
EXAMPLE 5
Manufacture of the titanium-containing catalyst component (1):
The starting material is a suspension of 20 parts by weight of silicon dioxide (SiO.sub.2, particle diameter 2-40 .mu.m, pore volume 1.6 cm.sup.3 /g, surface area 300 m.sup.2 /g) in 150 parts by weight of n-butanol.
This suspension is combined with a solution of 3.25 parts by weight of TiCl.sub.3.1/3 AlCl.sub.3 and 5.0 parts by weight of manasseite (Mg.sub.6.Al.sub.2.(OH).sub.16.CO.sub.3 .4H.sub.2 O), which has been brought to a chlorine content of 71 percent by weight by chlorination with phosgene, in 400 parts by weight of n-butanol. The resulting suspension is stirred for 15 minutes at 80.degree. C and the resulting solid-phase reaction product is then isolated by driving off the volatiles on a rotary evaporator which is taken to an operating pressure of 20 mm Hg and an operating temperature of 80.degree. C. Analysis of the resulting product, i.e. of the titanium-containing catalyst component (1), shows a titanium content of 2.3 percent by weight and a chlorine content of 14.0 percent by weight.
Polymerization:
0.04 part by weight of the titanium-containing catalyst component (1) is suspended in 10 parts by weight of heptane and 0.3 part by weight of Al(i-C.sub.4 H.sub.9).sub.3 (2) is added (these amounts correspond to an atomic ratio of titanium from catalyst component (1) to metal (Me = aluminum) from catalyst component (2) of about 1:79).
The Ziegler catalyst system thus obtained is introduced into a stirred autoclave which is charged with 80 parts by weight (corresponding to about 20% of its capacity) of finely divided polyethylene. The polymerization is then carried out, whilst stirring, for a period of 2 hours, with the following parameters, which are each regulated to maintain constant values: ethylene pressure = 27.5 bars, hydrogen pressure = 5 bars, temperature = 100.degree. C. The polymerization is then discontinued by letting down the autoclave.
Details of the product are to be found in the Table which follows.
__________________________________________________________________________ Residual Grams of polyethylene amount ofYield of per chlorine polyethylene gram of Tap Melt index in the parts by catalyst gram of density FT* MI.sub.2.16 polymerExample weight component (1) titanium g/l sec g/10 min. ppm**__________________________________________________________________________1 2,800 8,750 467,000 430 7.0 2.2 152 2,800 7,630 347,000 340 8.5 5.5 173 320 12,300 537,000 370 8.0 1.7 114 2,100 5,250 219,000 370 6.8 3.8 285 225 5,625 245,000 440 6.7 1.8 25__________________________________________________________________________ *FT = flow test, carried out in accordance with ASTM D 1895-67, method A **calculated from the productivity and from the chlorine content of the catalyst

Claims

1. A process for the manufacture of a homopolymer or copolymer of one or more .alpha.-monoolefins of 2 to 6 carbon atoms by polymerizing the monomer or monomers at from 30 to 200.degree. C and from 0.1 to 200 bars by means of a Ziegler catalyst system comprising
(1) a titanium-containing catalyst component and
(2) a metal compound of the general formula
Me A.sub.m-n X.sub.n
where Me is aluminum, magnesium or zinc, A is a hydrocarbon radical of 1 to 12 carbon atoms, X is chlorine, bromine, iodine or hydrogen, m is the valency of the metal Me and n is a number from 0 to m-1, with the proviso that the atomic ratio of titanium from catalyst component (1) to metal (Me) from catalyst component (2) is from 1:0.1 to 1:500, wherein the titanium-containing catalyst component (1) employed is the solid-phase product (IV) obtained by bringing into contact
(1.1) a finely divided, porous, inorganic oxidic material (I) which has a particle diameter of from 1 to 1,000 .mu.m, a pore volume of from 0.3 to 3 cm.sup.3 /g, and a surface area of from 100 to 1,000 m.sup.2 /g, and which has the formula SiO.sub.2.aAl.sub.2 O.sub.3, where a is a number from 0 to 2, and
(1.2) a solution (II) obtained by bringing together
(IIa) 100 parts by weight of an alcohol of the general formula
Z--OH
where Z is a saturated hydrocarbon radical of 1 to 8 carbon atoms,
(IIb) from 0.01 to 6 parts by weight (calculated as titanium) of a titanium trihalide, where the halogen may be chlorine and/or bromine, and
(IIc) from 0.01 to 4 parts by weight (calculated as magnesium) of a magnesium compound which is soluble in the alcohol (IIa), to form a dispersion (III), with the proviso that the weight ratio of inorganic oxidic material (I) to titanium in the titanium trihalide (IIb) is from 1:0.01 to 1:0.2, and the weight ratio of inorganic oxidic material (I) to magnesium in the magnesium compound (IIc) is from 1:0.01 to 1:0.25, and the dispersion (III) is evaporated at below 200.degree. C, and above the melting point of the alcohol (IIa) used, the evaporation being substantially complete in about 1 to 10 hours, until it reaches a dry consistency, i.e. until the solid-phase product (IV) is formed, any residual alcohol being left in said solid-phase product (IV).
2. A process as set forth in claim 1, wherein the titanium trihalide is titanium trichloride.
3. A process as set forth in claim 1, wherein the titanium trihalide has the formula TiCl.sub.3.1/3 AlCl.sub.3.
4. A process as set forth in claim 1, wherein the magnesium compound contains halogen and/or carbon.
5. A process as set forth in claim 1, wherein the magnesium compound has the formula Mg(OR').sub.2 where R' is a hydrocarbon radical of 1 to 10 carbon atoms.
6. A process as set forth in claim 1, wherein the magnesium compound is a complex alkoxide of magnesium with lithium, boron, aluminum or titanium.
7. A process as set forth in claim 1, wherein the magnesium compound has the formula MgZ.sub.2 where Z is chlorine, bromine or iodine.
8. A process as set forth in claim 7, wherein the magnesium halide is complexed with alcohols of 1 to 6 carbon atoms.
9. A process as set forth in claim 1, wherein the magnesium compound has the formula MgZ(OR') where z is chlorine, bromine or iodine and R' is a hydrocarbon radical of 1 to 10 carbon atoms.
10. A process as set forth in claim 1, wherein the magnesium compound is a manasseite of the formula Mg.sub.6.Al.sub.2.(OH).sub.16.CO.sub. 3 .4H.sub.2 O which has been brought to a chlorine content of from 50 to 75 percent by weight.
11. A process as set forth in claim 1, wherein the dispersion III is evaporated at below 160.degree. C.
12. A process as set forth in claim 1, wherein the dispersion III is kept at from 10.degree. to 160.degree. C for from 5 to 120 minutes prior to evaporation.
13. A process as set forth in claim 1, wherein the evaporation is carried out at reduced pressure.
14. A process as set forth in claim 1, wherein the inorganic oxidic material (I) is very dry and exhibits no weight loss when heated for 6 hours at under 2 mm Hg and 160.degree. C.

Priority Claims (1)

Number	Date	Country	Kind
2603920	Feb 1976	DE

US Referenced Citations (3)

Number	Name	Date
3941760	Herbeck et al.	Mar 1976
3993588	Thukrol	Nov 1976
4021599	Kochhar et al.	May 1977

Foreign Referenced Citations (5)

Number	Date	Country
2352154	Jun 1974	DE
4718846	May 1972	JP
1264416	Feb 1972	GB
1352718	May 1974	GB
1381605	Jan 1975	GB

Manufacture of homopolymers and copolymers of .alpha.-monoolefins

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (3)

Foreign Referenced Citations (5)