Claims
- 1. A method for manufacturing a catalyst composition that is substantially free of crystalline aluminum phosphate comprising the steps of:
- (a) combining zeolite Beta with a matrix precursor comprising an acid-soluble source of aluminum to produce a mixture;
- (b) forming particles from the mixture;
- (c) calcining the formed particles;
- (d) modifying the calcined particles by treating the calcined particles with an aqueous solution of a phosphorus containing compound; and
- (e) recovering the catalyst composition by calcining the phosphorus modified particles.
- 2. The catalyst composition produced by the method of claim 1.
- 3. The method of claim 1, wherein the acid-soluble source of aluminum comprises pseudoboehmite alumina.
- 4. The method of claim 1, wherein the matrix precursor of step (a) further comprises at least one component selected from the group consisting of clay, a source of silica, a source of zirconia, and combinations thereof.
- 5. The method of claim 1, wherein the matrix precursor of step (a) further comprises a source of silica and clay.
- 6. The method according to claim 1, wherein the matrix precursor of step (a) consists of pseudoboehmite alumina, colloidal silica, and kaolin clay.
- 7. The method according to claim 1, wherein the phosphorus containing compound of step (d) is selected from the group consisting of ammonium monohydrogen phosphate, ammonium dihydrogen phosphate, triammonium phosphate, ammonium hypophosphate, ammonium orthophosphate, ammonium dihydrogen orthophosphate, ammonium monohydrogen orthophosphate, ammonium hypophosphite, ammonium dihydrogen orthophosphite, phosphoric acid, ammonium metaphosphate and mixtures thereof.
- 8. The method of claim 1, wherein the zeolite Beta comprises about 0.01 to about 50 weight percent of the catalyst composition.
- 9. The method of claim 1, wherein the zeolite Beta comprises about 0.1 to about 25 weight percent of the catalyst composition.
- 10. A method for manufacturing a catalyst composition that is substantially free of crystalline aluminum phosphate comprising the steps of:
- (a) combining zeolite Beta with a matrix precursor comprising pseudoboehmite alumina to produce a mixture;
- (b) forming particles from the mixture;
- (c) calcining the formed particles;
- (d) modifying the calcined particles by treating the calcined particles with an aqueous solution of a phosphorus containing compound; and
- (e) recovering the catalyst composition by calcining the phosphorus modified particles.
- 11. The catalyst composition produced by the method of claim 10.
- 12. The method of claim 10, wherein the matrix precursor consists of pseudoboehmite alumina.
- 13. The method of claim 10, wherein the matrix precursor of step (a) further comprises at least one component selected from the group consisting of clay, a source of silica, a source of zirconia, and combinations thereof.
- 14. The method of claim 10, wherein the matrix precursor of step (a) further comprises a source of silica and clay.
- 15. The method according to claim 10, wherein the matrix precursor of step (a) consists of pseudoboehmite alumina, colloidal silica and kaolin clay.
- 16. The method according to claim 10, wherein the phosphorus containing compound of step (d) is selected from the group consisting of ammonium monohydrogen phosphate, ammonium dihydrogen phosphate, triammoniumphosphate, ammonium hypophosphate, ammonium orthophosphate, ammonium dihydrogen orthophosphate, ammonium monohydrogen orthophosphate, ammonium hypophosphite, ammonium dihydrogen orthophosphite, phosphoric acid, ammonium metaphosphate and mixtures thereof.
- 17. The method of claim 10, wherein the zeolite Beta comprises about 0.01 to about 50 weight percent of the catalyst composition.
- 18. The method of claim 10, wherein the zeolite Beta comprises about 0.1 to about 25 weight percent of the catalyst composition.
CROSS-REFERENCE TO RELATED APPLICATIONS
This is a continuation of application Ser. No. 08/158,325, filed on Nov. 29, 1993 now U.S. Pat. No. 5,457,078.
US Referenced Citations (8)
Continuations (1)
|
Number |
Date |
Country |
Parent |
158325 |
Nov 1993 |
|