Manufacture of light-stable polyurethane integral foams

The present invention relates to a process for the manufacture of light-stable polyurethane integral skin foams, especially soft integral foams, by reacting an aliphatic and/or cycloaliphatic polyisocyanate, either of which may or may not contain urethane and/or biuret groups, with a polyol in the presence of a blowing agent and of a synergistic catalyst combination comprising an alkali metal hydroxide, alkali metal alcoholate, alkali metal phenolate, alkali metal salt of a weak acid and/or hexahydrotriazine derivative and an organic tin, zinc and/or iron(II) compound, in the presence or absence of assistants and adjuvants.
Polyurethane foams have long been known. A review of the manufacture and properties of polyurethane foams is given, for example, in Kunststoff-Handbuch, volume VII, "Polyurethane" by R. Vieweg and A. Hochtlen, Verlag Carl Hanser, Munich 1966, or in the monograph by J. H. Saunders and K. C. Frisch "High Polymers", volume XVI, Polyurethanes, parts 1 and 2, Interscience Publishers 1962 and 1964.
Polyurethane foams manufactured from aromatic polyisocyanates and polyols are usually not light-stable, ie. they yellow when exposed to light. The reason for the yellowing is the formation of quinonoid structures from aromatic polymer units. It has therefore been proposed to reduce the light-sensitivity of the polyurethane foams by adding stabilizers, as a rule compounds which have a reducing action. It is true that such stabilizers can delay the yellowing, but they cannot suppress it completely. Since, for many applications, a yellowing or color change of the polyurethane foams is undesirable soft integral skin foams employed, for example, as cushioning, seats, headrests, dashboards and fenders in the automotive industry, must be either laminated with polymer films, or be surface-coated. The same remarks apply to thermoset resin foams, which are used for sports goods, window frames and as a wood substitute.
In the case of polyurethane elastomers and coatings the difficulties are circumvented by using aliphatic and/or cycloaliphatic polyisocyanates, in place of aromatic polyisocyanates, for the manufacture of the polyurethane. However, these methods have hitherto been unsuccessful in the manufacture of polyurethane foams, since the reactivity of aliphatic polyisocyanates is substantially less than that of the aromatic polyisocyanates.
According to the disclosures of German Laid-Open Application DOS No. 2,710,901 and U.S. Pat. No. 4,025,466, polyurethane foams or integral foams are manufactured using polyisocyanates whereof the NCO groups are not directly bonded to an aromatic radical, and catalyst combinations based on amines having a ##STR1## structure and alkaline earth metal salts of carboxylic acids having a dissociation constant K.sub.a <10.sup.-1, alcoholates and phenolates and organic lead compounds, and compounds having primary or secondary amino groups.
A disadvantage of the processes described is that the polyurethane foams thus obtained have a low heat distortion point and in some cases have inadequate mechanical properties.
It is an object of the present invention to manufacture light-fast polyurethane integral skin foams, especially soft integral foams, in such a way that the reaction conditions, and the mechanical properties of the polyurethane integral foams obtained, correspond to those when using aromatic polyisocyanates.
We have found that this object is achieved by a process for the manufacture of light-stable polyurethane integral skin foams by reacting a mixture of organic polyisocyanates, polyols, catalysts and blowing agents, with or without assistants and adjuvants, wherein the organic polyisocyanates used are aliphatic and/or cycloaliphatic polyisocyanates, of which both categories may or may not contain urethane and/or biuret groups, and the catalysts used are synergistic catalyst combinations consisting of
(A) one or more compounds from the group comprising the alkali metal hydroxides, alkali metal alcoholates, alkali metal phenolates, alkali metal salts of weak acids and/or hexahydrotriazine derivatives and
(B) one or more compounds from the group comprising organic tin, zinc and/or iron(II) compounds.
Surprisingly, we have found that by the specific selection, according to the invention, of a strongly basic polyisocyanurate catalyst and an organo-metallic polyurethane catalyst from the plurality of conventional and commercially available polyisocyanurate and polyurethane catalysts, a synergistic catalyst combination is obtained, which can adequately catalyze the reaction of polyols with aliphatic or cycloaliphatic polyisocyanates. It is particularly advantageous that the preferentially used polyisocyanates containing urethane groups and/or biuret groups are non-toxic and that the ratio in which the polyol and polyisocyanate compounds are mixed can be varied within wide limits without causing collapse of the polyurethane integral skin foams obtained.
The following may, for example, be used as starting components for the manufacture, according to the invention, of the light-stable rigid and soft polyurethane integral skin foams:
Organic polyisocyanates which may be used according to the invention have the formula R(NCO).sub.n, where R is a polyvalent aliphatic or cycloaliphatic radical or a mixed radical of this type, which radicals may or may not contain urethane and/or biuret groups, and n is an integer which corresponds to the valency of R and is at least 2, preferably 2 or 3. Specific examples are aliphatic diisocyanates, eg. ethylene diisocyanate, 1,2-propylene diisocyanate, 1,4-butylene diisocyanate, 2,2,4-trimethyl-1,6-hexamethylene diisocyanate and preferably 1,6-hexamethylene diisocyanate, cycloaliphatic diisocyanates, such as 1,2-cyclohexane diisocyanate, 1,3-cyclohexane diisocyanate, 1,4-cyclohexane diisocyanate, 1-methyl-2,4-cyclohexane diisocyanate, 1-methyl-2,6-cyclohexane diisocyanate and the corresponding 1-methylcyclohexane diisocyanate isomer mixtures, 4,4'-, 2,4'- and 2,2'-dicyclohexylmethane diisocyanate and the corresponding isomer mixtures and, preferably, 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate and polyisocyanates, such as polycyclohexyl-polymethylene polyisocyanates with from 2 to 6, preferably with 3, cyclohexylene radicals in the molecule.
Preferably, however, polyisocyanates containing urethane groups or, in particular, containing biuret groups, and mixtures of such compounds, prepared from aliphatic or cycloaliphatic polyisocyanates, are used. Polyisocyanates containing urethane groups may for example be obtained by reacting the above aliphatic or cycloaliphatic diisocyanates, preferably hexamethylene diisocyanate and isophorone diisocyanate, with alkanediols, which may or may not be substituted or modified, of 2 to 10, preferably 2 to 6, carbon atoms in the alkylene radical, eg. ethylene glycol, butane-1,4-diol, dipropylene glycol, hexane-1,6-diol and neopentylglycol, as well as neopentylglycol mono-hydroxypivalate or mixtures of these, in the molar ratio of about 2:1. The preparation of polyisocyanates containing biuret groups is described, for example, in U.S. Pat. Nos. 3,124,605 and 3,903,126, which are incorporated by reference. The polyisocyanates containing biuret groups have NCO contents of from 30 to 15, preferably from 25 to 20, % by weight and viscosities, at 20.degree. C., of from 6,000 to 500, preferably from 1,000 to 4,000, m.Pas.
Suitable polyols are preferably polyester-ols and especially polyether-ols. However, it is also possible to use other hydroxyl-containing polymers having molecular weights of from 500 to 8,000 and hydroxyl numbers of from 20 to 500, for example polycarbonates, especially those prepared by trans-esterifying diphenyl carbonate with hexane-1,6-diol, polyacetals, eg. polyoxymethylene, and polyester-amides.
Suitable polyester-ols may for example be prepared from dicarboxylic acids, preferably from aliphatic dicarboxylic acids of 2 to 12 carbon atoms in the alkylene radical, and polyhydric alcohols, preferably diols. Examples of suitable acids are aliphatic dicarboxylic acids, eg. glutaric acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, undecanedicarboxylic acid, dodecanedicarboxylic acid and, preferably, succinic acid and adipic acid, and aromatic dicarboxylic acids, such as phthalic acid and terephthalic acid. Examples of dihydric and polyhydric, especially dihydric, alcohols are ethylene glycol, diethylene glycol, 1,2- and 1,3-propylene glycol, dipropylene glycol, decane-1,10-diol, glycerol, trimethylolpropane, pentaerythritol and, preferably, butane-1,4-diol, hexane-1,6-diol and neopentylglycol. The polyester-ols have molecular weights of from 500 to 8,000, preferably from 1,000 to 4,000, and hydroxyl numbers of from 20 to 500, preferably from 50 to 200. The polyester-ols may be employed singly or in the form of mixtures.
However, particularly suitable polyols are polyether-ols having molecular weights of from 500 to 8,000, preferably from 1,000 to 4,000, and hydroxyl numbers of from 20 to 500, preferably from 50 to 200. The polyether-ols are prepared by conventional processes from one or more alkylene oxides of 2 to 4 carbon atoms in the alkylene radical and a starter molecule which contains from 2 to 8, preferably 2 or 3, active hydrogen atoms. Examples of suitable alkylene oxides are tetrahydrofuran, 1,3-propylene oxide, 1,2- and 1,3-butylene oxide, styrene oxide and, preferably, ethylene oxide and 1,2-propylene oxide. The alkylene oxides may be used singly, in alternation or as mixtures. Examples of suitable starter molecules are water, dicarboxylic acids, eg. succinic acid, adipic acid, phthalic acid and terephthalic acid, N,N'-dialkyl-substituted diamines, where alkyl is of 1 to 4 carbon atoms, for example N,N'-dimethyl-ethylenediamine, N,N'-dimethyl-1,2- and -1,3-propylenediamine, N,N'-diethyl-1,4-butylenediamine and N,N'-dimethyl-1,6-hexamethylenediamine, as well as N-alkyl-dialkanolamines, where alkyl is of 1 to 4 carbon atoms, eg. N-methyldiethanolamine, N-ethyl-diethanolamine and N-butyl-diethanolamine, and preferably dihydric to octahydric, especially dihydric or trihydric, alcohols, eg. ethylene glycol, 1,2- and 1,3-propylene glycol, diethylene glycol, dipropylene glycol, 1,4-butylene glycol, 1,6-hexamethylene glycol, glycerol, trimethylolpropane, pentaerythritol, sorbitol and saccharose.
The polyether-ols may be used singly or in the form of mixtures.
Instead of the polyester-ols or polyether-ols, mixtures of polyester-ols and polyether-ols may also be employed, in which mixtures the weight ratio of polyester-ol to polyether-ol may be varied within wide limits, for example from 20:80 to 80:20, depending on the end use of the polyurethane integral foam to be manufactured.
It may at times be advantageous to employ chain extenders or crosslinking agents, in addition to the above polyols, when manufacturing the polyurethane integral skin foams. Suitable agents of this type are polyfunctional, especially difunctional and trifunctional, compounds with molecular weights of from 18 to 600, preferably from 60 to 300. For example, dialkanolamines and trialkanolamines, eg. diethanolamine and triethanolamine, and, preferably, aliphatic diols and triols of 2 to 6 carbon atoms, eg. ethylene glycol, 1,4-butylene glycol, 1,6-hexamethylene glycol, glycerol and trimethylolpropane, may be used.
An essential feature of the process according to the invention is the use of a synergistic catalyst combination consisting of
(A) one or more compounds from the group comprising the alkali metal hydroxides, alkali metal alcoholates, alkali metal phenolates, alkali metal salts of weak acids and hexahydrotriazine derivatives and
(B) one or more compounds from the group comprising the organic zinc compounds, iron(II) compounds and, preferably, tin compounds
for accelerating the reaction between the aliphatic and/or cycloaliphatic polyisocyanates and polyols, in the presence or absence of water and chain extenders and/or cross-linking agents. The above catalyst combinations essentially comprise a strongly basic polyisocyanurate catalyst and an organo-metallic polyurethane catalyst. Suitable strongly basic polyisocyanurate catalysts include alkali metal hydroxides, especially sodium hydroxide and potassium hydroxide, alkali metal alcoholates, preferably sodium alcoholates and especially potassium alcoholates of alcohols of preferably 1 to 6 carbon atoms, eg. methanol, ethanol, propanol, isopropanol, n-butanol, iso-butanol and hexanol, phenolates, eg. sodium phenolate and potassium phenolate, salts of weak organic and inorganic acids, eg. sodium formate, potassium formate, sodium acetate, potassium acetate, sodium octoate, potassium octoate, sodium carbonate and potassium carbonate, and, preferably, hexahydrotriazine derivatives.
Particularly suitable hexahydrotriazine derivatives are 1,3,5-tris-(N,N-dialkylaminoalkyl)-s-hexahydrotriazines, for example 1,3,5-tris-(N,N-dimethyl-2-aminoethyl)-s-hexahydrotriazine, 1,3,5-tris-(N,N-dimethyl-3-aminopropyl)-s-hexahydrotriazine, 1,3,5-tris-(N,N-diethyl-2-aminoethyl)-s-hexahydrotriazine, 1,3,5-(N,N-diethyl-3-aminopropyl)-s-hexahydrotriazine and 1,3,5-tris-(N,N-dipropyl-2-aminoethyl)-s-hexahydrotriazine. For the purposes of the present invention, the use of 1,3,5-tris-(N,N-dimethyl-3-aminopropyl)-s-hexahydrotriazine is preferred.
These hexahydrotriazine components and their preparation are known and are described, for example, by Nicholas et al., Journal of Cellular Plastics 1 (1) (1965), 85 and by Graymore, Journal of the Chemical Society (1931), 1493.
The amounts of alkali metal hydroxide, alkali metal alcoholate, alkali metal phenolate, alkali metal salt of a weak acid and hexahydrotriazine derivative to be employed are from 0.01 to 5, preferably from 0.1 to 3, parts by weight per 100 parts by weight of polyol.
The other component of the catalyst combination is a zinc compound, iron(II) compound or, preferably, tin compound. Specific examples are iron acetylacetonate, zinc 2-ethyl-hexoate, zinc naphthenate, dibutyl-tin versatate and dibutyl-tin diacetate and preferably tin dioctoate and especially dibutyl-tin dilaurate. The amount of organic zinc compound, iron(II) compound or tin compound employed is from 0.01 to 5 parts by weight, preferably from 0.1 to 3 parts by weight, per 100 parts by weight of polyol.
A catalyst combination of tris-(N,N-dimethylaminopropyl)-s-hexahydrotriazine and dibutyl-tin dilaurate has proved particularly suitable and is therefore used preferentially.
A suitable blowing agent is water, which reacts with the polyisocyanates and provides carbon dioxide. Preferably, from 0.1 to 2% by weight, especially from 0.01 to 1% by weight, of water, based on the weight of polyol, is used. Instead of water, other, physically acting, blowing agents, or mixtures of water and physically acting blowing agents can be used. Physically acting blowing agents are usually chemically inert, low-boiling hydrocarbons or halohydrocarbons. For example, hydrocarbons or halohydrocarbons with boiling points, at atmospheric pressure, of below 50.degree. C., preferably of from -50.degree. C. to 30.degree. C., are employed. Specific examples are halohydrocarbons, eg. monochlorodifluoromethane, dichloromonofluoromethane, dichlorodifluoromethane, trifluoromethane and mixtures of these, hydrocarbons, eg. propane and isobutane, and dimethyl ether. The amount of physically acting blowing agent which is required can readily be determined; it is a function of the desired foam density and is from about 2.5 to 20% by weight, preferably from 5 to 15% by weight, based on the weight of polyol. Suitable mixtures of water and hydrocarbons or halohydrocarbons in general comprise from 0.01 to 2% by weight, preferably from 0.1 to 1% by weight, of water and from 2.5 to 20% by weight, preferably from 5 to 10% by weight, of hydrocarbon or halohydrocarbon, the percentages being based on the weight of polyol.
Preferably, trichlorofluoromethane and methylene chloride, or a mixture of these blowing agents, in an amount of from 2.5 to 20 parts by weight per 100 parts by weight of polyol, are used to manufacture the integral skin foams. The content of water, where any is added, is usually less than 1 part by weight, preferably from 0.01 to 0.5 part by weight, per 100 parts by weight of polyol.
In addition, assistants and adjuvants, such as are conventionally used for the manufacture of polyurethane foams, may be incorporated into the foamable reaction mixtures. Examples include surfactants, flameproofing agents, pore regulators, antioxidants, anti-hydrolysis agents, colorants, fillers and other additives.
Suitable surfactants are, for example, compounds which serve to assist the homogenization of the starting materials and may also be able to regulate the cell structure of the polyurethane foams. Specific examples are siloxane-oxyalkylene copolymers and other organopolysiloxanes, oxyethylated alkylphenols, oxyethylated fatty alcohols, paraffin oils, castor oil, ricinoleic acid esters and turkey red oil; these are used in amounts of from 0.2 to 6 parts by weight per 100 parts by weight of polyisocyanate.
Flameproofing agents may be incorporated into the light-stable polyurethane foams manufactured according to the invention, in order to improve their flame-retardant characteristics. Examples are compounds containing phosphorus and/or halogen which can additionally reduce the brittleness of the foams and act as plasticizers, eg. tricresyl phosphate, tris-2-chloroethyl phosphate, tris-chloropropyl phosphate and tris-2,3-dibromopropyl phosphate, and inorganic flameproofing agents, eg. antimony trioxide, arsenic oxide, ammonium phosphate and the like. In general, it has proved advantageous to use from 1 to 10 parts by weight of the said flameproofing agents per 100 parts by weight of polyisocyanate.
Further data relating to the above additional conventional assistants and adjuvants are to be found in the relevant literature, for example the monograph by J. H. Saunders and K. C. Frisch "High Polymers", volume XVI, Polyurethanes, parts 1 and 2, Interscience Publishers 1962 and 1964.
The polyurethane integral skin foams are manufactured by conventional methods known for aromatic polyisocyanates, for example by the prepolymer process and preferably by the one-shot process.
If the polyurethane integral skin foams are manufactured by the one-shot process, the conventional procedure is to react a mixture of polyol, catalyst and blowing agent, with or without chain extender, crosslinking agent, assistants and adjuvants, with the aliphatic and/or cycloaliphatic polyisocyanate at from 15.degree. to 60.degree. C., preferably from 20.degree. to 50.degree. C., the amounts used being such that the ratio of hydroxyl groups of the polyol, together with any NCO-active hydrogen atoms of the chain extender and/or crosslinking agent, to NCO groups of the polyisocyanate is from 0.8:1 to 1.2:1, preferably about 1:1. If a mixing chamber with several feed nozzles is used, the liquid starting materials may be introduced individually or, where the components are solid, in the form of a solution or suspension, and be mixed thoroughly in the mixing chamber. However, it has proved particularly advantageous to employ the two-component process and use a mixture of polyol, catalyst and blowing agent, with or without chain extender and/or crosslinking agent, assistants and adjuvants, as component A, and the aliphatic and/or cycloaliphatic polyisocyanate as component B.
Regarding the manufacture of the integral skin foams, reference may also be made to the relevant technical literature, for example to A. Nicolay et al., Gummi, Asbest, Kantschuk 30, No. 4 (1977), 226-232 and H. Y. Fabris, Advances in Urethane Technology, 2 (1973), 203-220.
The polyurethane integral skin foams manufactured according to the invention have densities of from about 60 to 600 g/l and are particularly distinguished by their light stability.
The flexible products are particularly suitable for the manufacture of automotive components, eg. headrests, armrests, crash pads and fenders, shoe soles and sports mats.
The rigid products are used in sports goods and window frames and as a wood substitute.

In the Examples, parts are by weight.
Index of abbreviations used in the Table of the Examples:
______________________________________ Mole- Func- OH- Ethy- Propy- cular tion- num- lene leneA-component: weight ality ber Starter oxide oxide______________________________________Polyols A 6,500 3 26 TMP + + B 4,000 2 28 EG + + C 4,900 3 35 GLY + + D 465 4 480 EDA - + E 2,000 2 58 GLY + + F 3,100 3 550 GLY - + G 2,000 2 56 PG - + H 2,000 2 56Polyester-ols I 2,000 2 56______________________________________Chain B 1,4 1,4-Butanediolextenders: EG Ethylene glycol PG Propylene glycolCrosslinking GLY Glycerolagents: TMP Trimethylolpropane .RTM.Ortegol 615 (from Goldschmidt AG) EDA Ethylenediamine Lu 3420 An adduct of ethylene- diamine and propylene oxide, OH-number 480Catalysts: 1. Polyurethane catalysts: DBTDL Dibutyl-tin dilaurate Sn Oct Tin dioctoate Zn Oct Zinc dioctoate Fe acetylacetonate DBTDA Dibutyl-tin diacetate DBTV Dibutyl-tin versatate2. Polyisocyanurate catalysts: KOH = 33% strength by weight potassium hydroxide solution in EG K But = 33% strength by weight potassium tert.-butylate solution in EG K Phen = 33% strength by weight potassium phenolate solution in EG K Oct = 50% strength by weight potassium octoate solution in propylene glycol K Ac = 33% strength by weight potassium acetate solution in EG KF = 33% strength by weight potassium formate solution in EG HHT = Tris-(N,N-dimethylaminopropyl)-s- hexahydrotriazineFoam stabilizers: .RTM.Tegostab B 3471 (Goldschmidt) .RTM.Tegostab B 4113 (Goldschmidt) .RTM.Tegostab B 2888 (Goldschmidt)Emulsifiers: SM (from Bayer) OS 710 (from Bayer) TDAO Tridecylammonium oleateBlowing F 11 Monofluorotrichloromethaneagents: F 12 Difluorodichloromethane F 113 TrifluorotrichloromethaneB-component:Isocyanates: HMDI Hexamethylene diisocyanate TMHMDI Trimethylhexamethylene diisocyanate H.sub.12 MDI Dicyclohexylmethylene diisocyanate IPDI Isophorone diisocyanate XDI Xylylene diisocyanateIsocyanate prepolymers:HMDI biuret Biuretized hexamethylene diisocyanate from 3 moles of HMDIHMDI HPN Reaction product of 1 mole of neopentylglycol mono-hydroxypivalate and 2 moles of HMDIHMDI DPG Reaction product of 1 mole of dipropylene glycol and 2 moles of HMDI______________________________________Notes on the Table showing the Examples:The entries in the first column to all sub-sequent columns unless a fresh entry is shown. Thetest data of the foams have been obtained in accordance withthe following DIN and ASTM Standard Specifications:Tensile strength and elongation DIN 53,571Tear propagation test DIN 53,515Shore A hardness DIN 53,505E-modulus (flexural test), flexural strength DIN 53,423Compressive strain at 10% compression DIN 53,421Shore D hardness DIN 53,505.DELTA.Y (yellowness index difference) ASTM D 1925
__________________________________________________________________________Polyurethane soft integral skin foamExample No. 1 2 3 4Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols A 21 A 21 A 21 A 21 B 68 B 68 B 68 B 68Chain extenders B 1,4 8 B 1,4 8 B 1,4 8 B 1,4 8Crosslinking agents EG 0.5 EG 0.5 EG 0.5 EG 0.5A Catalysts DBTDL 3 DBTDL 3 Sn Oct 3 DBTDL 3 KOH 0.75 HHT 3 KOH 0.75 KOH 0.75Foam stabilizers SM 1Blowing agents F 11 6 F 11 6 F 11 6 F 11 15 Water 0.5 Water 0.5 Water 0.5 --__________________________________________________________________________B Isocyanates HMDI HMDI HMDI HMDI biuret 50 biuret 100 biuret 50 biuret 50 HMDI DPG 50 -- HMDI DPG 50 HMDI HPN 50__________________________________________________________________________Ratio B/100 A 70 51 80 80Free density .kg/m.sup.3 180 180 180 100Pot life sec 30 50 70 25Rise time sec 60 75 120 50Molded density kg/m.sup.3 400 600 400 350Tensile strength N/mm.sup.2 0.8 1.4 0.8 1.0Elongation % 120 100 110 120Tear propagationresistance N/mm 2.0 2.5 3.0 2.0Shore A hardness 45 50 40 40.DELTA.(xenon test, 500 h) 0.5 1 3 5__________________________________________________________________________Polyurethane soft integral skin foamExample No. 5 6 7 8Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols C 41 C 41 C 41 C 41 B 25 B 25 B 25 B 25Chain extenders B 1,4 11 B 1,4 11 B 1,4 11 B 1,4 11A Crosslinking agents Lu 3420 1 Lu 3420 1 Lu 3420 1 Lu 3420 1Catalysts HHT 3 HHT 3 KOH 0.75 KOH 1.5 DBTDL 3 DBTDL 3 Zn Oct 3 DBTL 1.5Foam stabilizers Tegostab 0.3 Tegostab 0.3 -- B 3471 B 3471 SM 0.5 SM 0.5 SM 0.5 SM 0.25Blowing agents F 11 20 -- F 11 20 F 11 15 Water 0.8 -- --__________________________________________________________________________B Isocyanates HMDI 50 HMDI 50 HMDI 50 HMDI 50 biuret HMDI DPG 50 HMDI DPG 50 HMDI DPG 50 HMDI DPG 50__________________________________________________________________________Ratio B/100 A 80 80 70 70Free density .kg/m.sup.3 90 140 90 90Pot life sec 35 35 23 33Rise time sec 60 75 45 70Molded density kg/m.sup.3 350 300 400 250Tensile strength N/mm.sup.2 1.1 1.0 1.1 0.7Elongation % 130 130 100 140Tear propagationresistance N/mm 3.0 2.0 4 2Shore A hardness 35 50 60 24.DELTA.Y (xenon test 500 h) 2 0 5 3__________________________________________________________________________Polyurethane soft integral skin foamExample No. 9 10 11 12Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols C 41 C 41 C 41 C 41 B 25 B 25 B 25 B 25Chain extenders B 1,4 11 B 1,4 11 B 1,4 11 B 1,4 11A Crosslinking agentsCatalysts HHT 3 HHT 3 HHT 3 HHT 3 DBTDL 3 DBTDL 3 DBTDL 3 DBTDL 3Foam stabilizers Tegostab 0.3 Tegostab 0.3 Tegostab 0.3 Tegostab 0.3 B 3471 SM 0.5 SM 0.5 SM 0.5 SM 0.5Blowing agent F 11 20 F 11 20 F 11 20 F 11 20__________________________________________________________________________B Isocyanates HMDI 100 TMHMDI 100 H.sub.12 MDI 100 IPDI 100__________________________________________________________________________Ratio B/100 A 27 35 45 35Free density .kg/m.sup.3 50 50 60 70Pot life sec 15" 25" 35 90"Rise time sec 20" 35" 80 200"Molded density kg/m.sup.3 200 200 250 300Tensile strength N/mm.sup.2 1.0 1.1 0.8 0.9Elongation % 50 50 70 100Tear propagationresistance N/mm 2 2.2 1.5 2.0Shore A hardness 30 35 25 35.DELTA.Y (xenon test 500 h) 2 -1 2 5__________________________________________________________________________Polyurethane soft integral skin foamExample No. 13 14 15 16Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols A 21 A 21 A 21 A 21 B 68 B 68 B 68 B 68Chain extenders B 1,4 8 B 1,4 8 B 1,4 8 B 1,4 8A Crosslinking agents EG 0.5 EG 0.5 EG 0.5 EG 0.5Catalysts DBTDL 3.0 DBTDL 3.0 DBTDL 3.0 Sn Oct 3.0 KBut 0.75 K phenolate 1.5 K octoate 3.0 K acetate 3.0Foam stabilizers Tegostab B 3471 0.3 B 3471 0.3 B 3471 0.3 B 3471 0.3 SM 0.5 SM 0.5 SM 0.5 SM 0.5Blowing agents F 11 6 F 11 6 F 11 6 F 11 6 F 113 6.0 F 113 6.0__________________________________________________________________________B Isocyanates HMDI biuret 50 biuret 50 biuret 50 biuret 50 HMDI DPG 50 HMDI DPG 50 HMDI DPG 50 HMDI DPG 50__________________________________________________________________________Ratio B/100 A 70 70 70 70Free density .kg/m.sup.3 150 200 150 150Pot life sec 35 40 35 55Rise time sec 75 100 70 150Molded density kg/m.sup.3 600 600 350 400Tensile strength N/mm.sup.2 2.0 2.0 1.5 1.3Elongation % 120 150 170 160Tear propagationresistance N/mm 3.5 2.5 2 2Shore A hardness 50 40 35 40.DELTA.Y (xenon test 500 h) 0.7 6 3 5__________________________________________________________________________Polyurethane soft integral skin foamExample No. 17 18 19 20Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols C 80 C 80 C 80 C 80 G 10 G 10 G 10 G 10Chain extenders B 1,4 10 B 1,4 10 B 1,4 10 B 1,4 10A Crosslinking agents Ortegol 615 4.5 615 4.5 615 4.5 615 4.5Catalysts HHT 3 KOH 0.75 KF 0.75 KF 0.75 DBTDL 3 DBTDL 3 DBTDL 3 DBTDL 3Foam stabilizers Tegostab B 9113 0.5 B 9113 0.5 B 9113 0.5 B 9113 0.5Blowing agents F 11 5 F 11 5 F 11 5 F 11 5 Water 0.5 Water 0.5 Water 0.5 Water 0.5__________________________________________________________________________B Isocyanates HMDI biuret 100 HMDI biuret 50 HMDI 100 HMDI biuret 50 HMDI DPG 50 -- HMDI HPN 50__________________________________________________________________________Ratio B/100 A 60 65 26 65Free density .kg/m.sup.3 180 100 90 110Pot life sec 42 25 12 30Rise time sec 70 50 35 80Molded density kg/m.sup.3 250 300 150 250Tensile strength N/mm.sup.2 1.0 1.2 0.5 1.5Elongation % 110 150 120 130Tear propagationresistance N/mm 2.5 2.0 1.0 2.0Shore A hardness 45 35 40 30.DELTA.Y (xenon test 500 h) 0.5 3 3 5__________________________________________________________________________Polyurethane soft integral skin foamExample No. 21 22 23 24Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols I 75 I 75 I 75 I 75Chain extenders EG 10 EG 10 EG 10 EG 10A Crosslinking agentsCalalysts HHT 3 HHT 3 KOH 0.75 KBut 1.0 DBTDL 3 Sn Oct 3 DBTDL 3 DBTDL 3.0Foam stabilizers Tegostab B 2888 0.3 B 2888 0.3 B 2888 0.3 B 2888 0.3 SM 0.3 SM 0.3 SM 0.3 SM 0.3Blowing agent F 11 13 F 11 13 F 11 13 F 11 13__________________________________________________________________________B Isocyanates HMDI biuret 50 biuret 50 biuret 50 biuret 50 HMDI DPG 50 HMDI DPG 50 HMDI DPG 50 HMDI DPG 50__________________________________________________________________________ 5Ratio B/100 A 100 100 100 100Free dentity .kg/m.sup.3 150 150 150 160Pot life sec 25 28 20 15Rise time sec 60 75 50 30Molded density kg/m.sup.3 450 350 450 600Tensile strength N/mm.sup.2 1.0 0.8 1.1 2Elongation % 120 150 140 130Tear propagationresistance N/mm 8.0 7.0 8.0 9Shore A hardness 60 55 70 80.DELTA.Y (xenon test 500 h) 1 2 1.5 3__________________________________________________________________________Polyurethane soft integral skin foamExample No. 25 26 27 28Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols H 86 H 86 H 86 H 86Chain extenders B 1,4 11 B 1,4 11 B 1,4 11 B 1,4 11A Crosslinking agents Gly 0.5 Gly 0.5 Gly 0.5 Gly 0.5Catalysts HHT 3 HHT 3 HHT 3 HHT 3 DBTDL 3 DBTDL 3 DBTDL 3 DBTDL 3Foam stabilizers Tegostab 2888 0.2 2888 0.2 2888 0.2 2888 0.2 SM 1 --Blowing agents F 11 10 F 11 10 F 11 10 F 11 10 Water 0.5 Water 0.5 -- --__________________________________________________________________________B Isocyanates HMDI biuret 50 HMDI DPG 100 HMDI biuret 50 HMDI biuret 100 HMDI DPG 50 -- HMDI HPN 50 --__________________________________________________________________________Ratio B/100 A 80 90 90 85Free density .kg/m.sup.3 150 150 160 160Pot life sec 40 40 38 35Rise time sec 75 75 70 60Molded density kg/m.sup.3 300 350 450 400Tensile strength N/mm.sup.2 0.8 0.9 1.5 1.5Elongation % 150 140 150 120Tear propagationresistance N/mm 2.5 3.0 3.5 3Shore A hardness 30 45 45 50.DELTA.Y (xenon text 500 h) 0.7 1 2.5 0__________________________________________________________________________Polyurethane rigid integral skin foamExample No. 29 30 31 32Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols D 30 D 30 D 30 D 30 E 48 E 48 E 48 E 48Chain extenders EG 4.5 EG 4.5 EG 4.5 EG 4.5A Crosslinking agents TMP 12 TMP 12 TMP 12 TMP 12Catalysts HHT 1.5 HHT 3 KOH 0.75 Kbut 1.0 DBTDL 1.5 DBTDL 3 DBTDL 1.5 DBTDL 1.5Emulsifiers OS 710 0.8 OS 710 0.8 OS 710 0.8 OS 710 0.8 TDAO 3 TDAO 3 TDAO 3 TDAO 3Blowing agents F 11 10 F 11 10 F 11 10 F 11 10 F 12 3.0 --__________________________________________________________________________B Isocyanates HMDI biuret 100 HMDI biuret 50 HMDI 100 H.sub.12 MDI 100 HMDI DPG 50 -- --__________________________________________________________________________Ratio B/100 A 170 180 75 105Free density .kg/m.sup.3 260 250 180 200Pot life sec 80 42 12 65Rise time sec 120 80 50 140Molded density kg/m.sup.3 600 500 700 600E-modulus(flexural test) N/mm.sup.2 1,400 1,200 1,400 1,300Flexural strength N/mm.sup.2 35 30 25 30Compressive strainat 10% compression N/mm.sup.2 5 4 5 3Shore D hardness 70 60 65 55.DELTA.Y (xenon test 500 h) 0.5 1 0.5 3__________________________________________________________________________Polyurethane rigid integral skin foamExample No. 33 34 35 36Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols F 53 F 53 F 53 F 53 C 10 C 10 C 10 C 10Chain extendersA Crosslinking agents TMP 18 TMP 18 TMP 18 TMP 18Catalysts HHT 1.5 KOH 0.75 KF 1.0 HHT 3 DBTDL 1.5 DBTDL 3 DBTDL 3 DBTDL 3Emulsifiers OS 710 2 OS 710 2 OS 710 2 DS 710 2 SM 0.6 SM 0.6 SM 0.6 SM 0.6Blowing agent F 11 10 F 11 10 F 11 10 F 11 10__________________________________________________________________________B Isocyanates HMDI biuret 50 HMDI biuret 50 -- HMDI biuret 50 HMDI HPN 50 HMDI HPN 50 HMDI HPN 100 HMDI 50__________________________________________________________________________Ratio B/100 A 220 100 110 80Free density .kg/m.sup.3 125 200 200 200Pot life sec 80 20 25 25Rise time sec 135 60 75 65Molded density kg/m.sup.3 700 600 750 600E-modulus(flexural test) N/mm.sup.2 1,200 1,400 1,200 1,300Flexural strength N/mm.sup.2 25 30 35 40Compressive strainat 10% compression N/mm.sup.2 4 3 5 6Shore D hardness 65 60 55 70.DELTA.Y (xenon test 500 h) 3 2 0.5 5__________________________________________________________________________Polyurethane soft integral skin formExample No. 37 38 39 40Starting materials Parts Parts Parts Parts__________________________________________________________________________Polyols A 21 A 21 A 21 A 21 B 68 B 68 B 68 B 68Chain extenders B 1,4 8 B 1,4 8 B 1,4 8 B 1,4 8A Crosslinking agents EG 0.5 EG 0.5 EG 0.5 EG 0.5Catalysts Fe acetyl- acetonate 1 Zn Oct 3 DBTDA 3 DBTV 3 KOH 0.75 KOH 0.75 KOH 0.75 KOH 0.75Foam stabilizers SM 0.25 SM 0.25 SM 0.25 SM 0.25Blowing agent F 11 15 F 11 15 F 11 15 F 11 15__________________________________________________________________________B Isocyanates HMDI biuret 100 HMDI biuret 100 HMDI biuret 100 XDI 100__________________________________________________________________________Ratio B/100 A 80 80 80 80Free density .kg/m.sup.3 150 120 180 160Pot life sec 30 35 25 30Rise time sec 55 60 45 75Molded density kg/m.sup.3 350 400 450 500Tensile strength N/mm.sup.2 1.5 1.0 1.2 1.1Elongation % 150 120 130 110Tear propagationresistance N/mm 2.0 2.1 2.5 2.5Shore A hardness 30 40 35 45.DELTA.Y (xenon test 500 h) 0.5 1 2 3__________________________________________________________________________

Number	Name	Date
3476933	Mendelsohn	Nov 1969
3726952	Boden et al.	Apr 1973
3793268	Dietrich et al.	Feb 1974
3799898	Lamplugh et al.	Mar 1974
3824199	Nadeau et al.	Jul 1974
3899454	Wagner et al.	Aug 1975
4025466	Jourquin et al.	May 1977
4058492	von Bonin et al.	Nov 1977
4065410	Schaefer et al.	Dec 1977
4150206	Jourquin et al.	Apr 1979

Manufacture of light-stable polyurethane integral foams

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (10)

Foreign Referenced Citations (1)