MANUFACTURE OF METAL CORE BY USING RAPID PROTOTYPING METHOD AND METHOD FOR MANUFACTURING PRECISION PARTS THROUGH HOT ISOSTATIC PRESSING USING SAME, AND TURBINE BLISK FOR DRIVING LIQUID ROCKET TURBO PUMP USING SAME

Abstract

Disclosed is a method for manufacturing precision parts through hot isostatic pressing using a metal core manufactured through metal rapid prototyping to manufacture a turbine blisk for driving a turbo pump of a liquid rocket. The method includes: manufacturing a metal core that has an internal vacant space having the same shape as the precision parts, using rapid prototyping; putting the metal core in a housing; filling an inside of the housing with heat resistant steel powder and creating a vacuum state in the housing; treating the housing under high temperature and pressure to produce heat resistant steel; removing the housing and a portion of the heat resistant steel to expose a portion of the metal core; performing etching to remove the exposed metal core; and removing only a portion of the heat resistant steel through mechanical machining, wherein the remaining portion corresponds to the shape of the precision part.

Description

TECHNICAL FIELD

The present invention relates to manufacture of a metal core manufactured through metal rapid prototyping or rapid tooling, a method of manufacturing precision parts through hot iso static pressing using the metal core, and a turbine blisk manufactured using the method, the turbine blisk for driving a liquid rocket turbo pump. More specifically, the present invention relates to manufacture of a metal core using metal rapid prototyping or rapid tooling, a method of manufacturing precision parts through hot isostatic pressing using the metal core, and a turbine blisk manufactured using the method, the turbine blisk for driving a turbo pump of a liquid rocket, each of the manufacture, method and turbine blisk being applicable to metal casings having a complex internal structure, pump impellers, and the like as well as gas turbine disks.

BACKGROUND ART

Generally, a turbine blisk for driving a turbo pump of an engine of a liquid rocket includes a turbine disk, blades, and a shroud.

FIG. 1 is a picture illustrating a disk-blade assembly; FIG. 2 is a picture illustrating the shape of a conventional individual blade; FIG. 3 is a picture illustrating a processed disk integrated with blades; and FIG. 4 is a picture illustrating a state in which a shroud is disposed at the brim of a disk. A description will be made below with reference to FIGS. 1 and 4.

Conventionally, blades (including a shroud) and a disk are separately processed from each other and then the blades are later integrated with the disk.

This method allows that a disk and blades are made of different materials. However, this method poses problems such as vibration of individual blades, fatigue of the structure of inserted portions of blades, and high cost.

Alternatively, there is another conventional blisk manufacturing method. That is, blades are first manufactured through either electric-discharge processing or mechanical machining, a shroud is then manufactured, and the shroud is finally joined to the blades through welding or the like.

This method has an advantage in that an assembly of a disk, blades, and a shroud is considered a single integrated body that is structurally stable, but also has a disadvantage in that a joining process for joining the shroud to the blades is complicated and the integrated structure is not always free from joint failure.

There is a further conventional blisk manufacturing method. That is, a disk, blades, and a shroud are integrally processed at one time by subjecting a side surface of a disk to electric-discharge processing.

This method produces the most desirable structure because a disk, blades, and a shroud are genuinely integrated as a single piece. However, the structure and arrangement of electrodes and instruments for electric-discharging are complicated and expensive. Further, electrical discharge machining causes a recast layer to form on the machined surface of the workpiece, and the recast layer deteriorates fatigue lifetime of the machined structure.

Accordingly, the recast layer formed on the surface of a machined blade is likely to deteriorate the structural stability of a turbine.

DISCLOSURE

Technical Problem

Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and an object of the present invention is to provide a method of manufacturing precision parts through hot isostatic press processing (HIP) using a metal core manufactured through metal rapid prototyping or rapid tooling.

Another object of the present invention is to provide a turbine blisk for driving a turbo pump of a liquid rocket, the turbine blisk having a relatively complex structure and being manufactured using the method.

Technical Solution

In order to accomplish the above objects, according to one aspect, there is provided a method of manufacturing a method of manufacturing precision parts through hot iso static press processing using a metal core manufactured through metal rapid prototyping or rapid tooling, the method including: a first step of manufacturing a metal core using a metal rapid prototyping method or a rapid tooling; a second step of putting the metal core in a housing, filling the inside of the housing with heat resistant steel powder and creating a vacuum state in the housing; a third step of treating the housing under high temperature and pressure in a hot isostatic press (HIP) furnace; a fourth step of removing the housing to expose a portion of the metal core; a fifth step of etching the metal core; and a sixth step of performing mechanical machining to produce the precision parts.

In addition, according to another aspect, there is provided a turbine blisk for driving a turbo pump of a liquid rocket, the turbine blisk manufacturing using the same method.

Advantageous Effects

According to the aspects, any metal can be used as long as it can be provided in the form of power. Heat resistant steel is typically hard to machine. However, the present invention can solve this problem. That is, according to the aspects of the present invention, there is a large choice of materials that can be used to manufacture a metal core and a turbine blisk by using heat resistant steel power and hot isostatic pressing (HIP).

The manufacture of a metal core using a metal rapid prototyping method or a rapid tooling method is based on the idea of stacking layers, but not based on the idea of conventional machining. Therefore, even parts with a very complicated shape can be manufactured to be a single piece according to the present invention. That is, there is no limit in the shape of parts to be manufactured when using the present invention.

Furthermore, an article manufactured using a metal rapid prototyping method typically suffers internal flaws attributable to micro-melting and stacking, residual stress distribution, deformation, and the like. Therefore, such an article is limitedly applied, by way of experiment, to the aerospace field which requires high reliability. However, according to the present invention, since a core manufactured using a metal rapid prototyping method is removed and only a mold produced through an HIP process, which is a mature and stable process, is left for use, those problems can be solved.

DESCRIPTION OF DRAWINGS

FIG. 1 is a picture illustrating a blade-disk assembly according to a conventional art;

FIG. 2 is a picture illustrating the shape of an individual blade according to a conventional art;

FIG. 3 is a picture illustrating a state in which a disk is machined to be equipped with blades;

FIG. 4 is a picture illustrating a state in which a shroud is joined to the outer circumference of a disk;

FIG. 5 is a flowchart illustrating a method of manufacturing a metal core using a metal rapid prototyping method and a method of manufacturing precision parts through a hot iso static press process using the metal core;

FIG. 6 is a schematic diagram illustrating a precision part (the shape of a turbine) to be manufactured according to one embodiment of the present invention;

FIG. 7 is a schematic diagram illustrating a metal core that has an internal vacant space therein having the same shape as a precision part to be manufactured according to one embodiment of the present invention;

FIG. 8 is a picture illustrating a process of manufacturing a metal core using a metal rapid prototyping method according to one embodiment of the present invention;

FIG. 9 is a schematic diagram illustrating a state in which a metal core is put in a housing, the inside of the housing is filled with heat resistant steel powder, and a vacuum state is created in the housing, according to one embodiment of the present invention;

FIG. 10 is a schematic diagram illustrating a state in which the housing of FIG. 8 is treated under high pressure and temperature in an HIP furnace according to one embodiment of the present invention;

FIG. 11 is a schematic diagram illustrating a state in which the housing is removed after the HIP process is finished;

FIG. 12 is a schematic diagram illustrating a state in which one side of the heat resistant steel is mechanically machined to be removed, exposing one surface of the metal core, according to one embodiment of the present invention;

FIG. 13 is a schematic diagram illustrating a state in which the metal core of FIG. 11 is dipped in an etching solution so that the metal core can be removed; and

FIG. 14 is a picture illustrating a precision part manufactured according to the method according to one embodiment of the present invention.

BEST MODE

Reference will now be made in detail to various embodiments of the present invention, specific examples of which are illustrated in the accompanying drawings and described below, since the embodiments of the present invention can be variously modified in many different forms.

While the present invention will be described in conjunction with exemplary embodiments thereof, it is to be understood that the present description is not intended to limit the present invention to those exemplary embodiments. On the contrary, the present invention is intended to cover not only the exemplary embodiments, but also various alternatives, modifications, equivalents and other embodiments that may be included within the spirit and scope of the present invention as defined by the appended claims. Throughout the drawings, the same reference numerals will refer to the same or like parts.

It will be understood that, although the terms “first”, “second”, etc. may be used herein to describe various elements, these elements should not be limited by these terms.

These terms are only used to distinguish one element from another element. For instance, a first element discussed below could be termed a second element without departing from the teachings of the present invention. Similarly, the second element could also be termed the first element. The term “and/or” specifies the presence of any one of stated elements or combinations of them.

It will be understood that when an element is referred to as being “coupled” or “connected” to another element, it can be directly coupled or connected to the other element or intervening elements may be present therebetween. In contrast, it should be understood that when an element is referred to as being “directly coupled” or “directly connected” to another element, there are no intervening elements present. Other expressions that explain the relationship between elements, such as “between”, “directly between”, “adjacent to”, or “directly adjacent to” should be construed in the same way.

The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. As used herein, the singular forms “a”, “an”, and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprise”, “include”, “have”, etc. when used in this specification, specify the presence of stated features, integers, steps, operations, elements, components, and/or combinations of them but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or combinations thereof.

Unless otherwise defined, all terms including technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the present disclosure, and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.

Hereinbelow, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

FIG. 5 is a flowchart illustrating a method of manufacturing a metal core using a metal rapid prototyping method or a rapid tooling method and a method of manufacturing precision parts through hot isostatic pressing using the metal core, according to one embodiment of the present invention. The methods will be described below with reference to FIG. 5.

The method of manufacturing a metal core using a metal rapid prototyping method or a rapid tooling method and the method of manufacturing precision parts through hot isostatic pressing using the metal core, according to one embodiment of the present invention, includes: a first step S100 of preparing a metal core 200 having an internal vacant space that is the same as the shape of a precision part 100 to be manufactured, using a metal rapid prototyping method or a rapid tooling method; a second step S200 of putting the metal core 200 in a housing 300, filling the internal vacant space of the metal core 200 and the inside of the housing 300 with heat resistant steel powder, and creating a vacuum state in the housing 300; a third step S300 of manufacturing a heat resistant steel 600 by treating the housing 300 under high temperature and pressure in a hot isostatic press (HIP) furnace 500; a fourth step S400 of removing the housing 300 and partially removing the heat resistant steel 600 to expose one surface of the metal core 200; a fifth step S500 of etching the metal core 200 to remove the metal core 200; and a sixth step S600 of partially removing the heat resistant steel 600, from which the metal core 200 is removed, through mechanical machining to leave only a portion of the heat resistant steel 60, which corresponds to the shape of the precision part 100.

1) First Step S100

FIG. 6 is a schematic diagram illustrating the precision part (turbine blisk) 100 to be manufactured using the present invention, FIG. 7 is a schematic diagram illustrating the metal core 200 having an internal vacant space having the same shape as the precision part 100, and FIG. 8 is a schematic diagram illustrating the flow of processes in the method of manufacturing the metal core 200 using a metal rapid prototyping method or a rapid tooling method according to the present invention.

The manufacturing method will be described below with reference to FIGS. 6 to 8.

FIG. 6 illustrates a schematic diagram illustrating the shape of a turbine blisk to be manufactured according to the present invention. The metal core 200 made of low carbon steel is first prepared as illustrated in FIG. 7.

Since it is difficult with an existing mechanical machining technology to machine low carbon steel to produce the metal core 200, the metal core 200 is prepared using a metal rapid prototyping method or a rapid tooling method.

As illustrated in FIG. 8, the metal rapid prototyping (rapid tooling) includes: a step of creating a cross-section data file for each unit height by slicing a three-dimension model of an object to be prepared; and a step of melting metal (low carbon steel) with a laser and dripping the molten metal according to the shape of each cross-section for each unit height; or a step of stacking metal powder, layer by layer, to produce the metal core 200.

2) Second Step S200

FIG. 9 is a schematic diagram illustrating a state in which the metal core 200 is put in the housing 300 according to one embodiment of the present invention, the inside of the housing 300 is filled with heat resistant steel powder 400, and a vacuum state is created in the housing 300. This process will be described in more detail below.

The housing 300 is made of a thin metal plate and takes the form of a can. Next, the metal core 200 manufactured using a metal rapid prototyping method is put into the housing 300. The inside of the metal core 200, including a portion corresponding to the shape 110 of the precision part, as well as the inside of the housing 300 is filled with heat resistant steel powder 400 and air in the housing 300 is purged to create a vacuum state in the housing 300. Next, the inside of the housing 300 is sealed.

When a turbine blisk is manufactured with the heat resistant steel powder 400, it is preferable to use a nickel-based alloy such as Inconel 718.

3) Third Step S300

FIG. 10 is a schematic diagram illustrating a state in which the housing 300 of FIG. 8 is treated under high temperature and pressure in a hot isostatic press (HIP) furnace 500 according to the present invention. FIG. 11 is a schematic diagram illustrating a state in which the housing 300 is removed after the HIP process is finished. This step will be more specifically described below with reference to FIGS. 10 and 11.

As illustrated in FIG. 10, the heat resistant steel powder 400 is pressed in the housing 300 through hot isostatic pressing (HIP), air in the housing 300 is drawn to create a vacuum state in the housing 300, and the inside of the housing 300 is sealed. Next, the housing 300 is treated for several hours under high pressure (about 1000 bars or higher) and high temperature close to the melting point (typically 1000° C. or higher) of the heat resistant steel powder 400 to produce a solid object with a density of 100%.

Hot iso static pressing (HIP) has an advantage of being able to produce a solid object without being limited by properties of a raw material. Therefore, a solid object substantially similar to the final target shape is first manufactured through HIP, thereby minimizing the amount of mechanical machining.

To form an empty space between blades, the metal core 200 is preliminarily inserted into the heat resistant steel powder 400 and then an HIP process is performed.

As illustrated in FIG. 11, after the HIP process is finished, the housing 300 is removed. Since the heat resistant steel powder 400 is sintered to have a density of 100%, its volume is reduced and the heat resistant steel 600 is thus produced. On the other hand, since the metal core 200 is originally solid, its volume is not reduced so that the metal core 200 is disposed inside the heat resistant steel 600 as it is.

Since the HIP process is a known technology, a detailed description thereabout will not be given herein below.

4) Fourth Step S400

FIG. 12 is a schematic diagram illustrating a state in which one side of the heat resistant steel 600 according to the present invention is removed through mechanical machining to expose one surface of the metal core 200. This process will be more specifically described below.

An outer shell of the housing 300 is typically made of stainless steel. Therefore, it is removed through mechanical machining so that the surface of the metal core 200 made of low carbon steel is exposed. To this end, as illustrated in FIG. 12, one side of the heat resistant steel 600 is removed through mechanical machining.

There are various methods for mechanical machining, which are known very well. Accordingly, a detailed description thereabout will not be given herein.

5) Fifth Step S500

FIG. 13 is a schematic diagram illustrating a state in which the metal core 200 of FIG. 11 is dipped in an etching solution to be removed. This process will be more specifically described below.

The metal core 200 made of low carbon steel, whose one surface is exposed, is dipped in an etching solution 700. The etching solution 700 may be a nitric acid-based solution.

The heat resistant steel 600 (heat resistant alloy or super alloy) used as a material for a turbine is mostly a nickel alloy. Accordingly, the heat resistant steel 700 is highly anti-corrosive, but low carbon steel that is used as a material for the metal core 200 is corrosive. By using this corrosiveness difference, it is possible to selectively etch only the metal core 200 made of low carbon steel.

It is possible to easily remove the metal core 200 made of low carbon steel with use of the nitric acid-based etching solution 700.

6) Sixth Step S600

FIG. 14 is a diagram illustrating a precision part 100 manufactured according to the manufacturing method according to the present invention. A description thereabout will be described below with reference to FIG. 14.

After the etching process is finished, unnecessary portions other than a portion corresponding to the precision part 100 such as a turbine blisk are removed through mechanical machining and then a finishing process is performed. Through this process, as illustrated in FIG. 14, a turbine blisk can be formed using HIP and the heat resistant steel powder 400.

Not only the manufacture of a turbine blisk for driving a turbo pump of a liquid rocket but also metal casings and pump impellers that have a complex structure can be easily manufactured using the method described above.

When the metal core 200 has a simple shape, it can be manufactured through mechanical machining. However, when a metal core has a complex structure like the metal core 200 used to prepare a turbine blisk, the metal core is desirably manufactured using a direct metal rapid prototyping method as in the present invention.

Among rapid prototyping methods (or rapid tooling methods) that are being currently widely spread, by using a direct metal rapid prototyping method using metal powder, it is possible to easily manufacture the metal core 200 having a complex structure.

There is a large choice of metal powder and any metal power can be freely selected according to a rapid prototyping method and equipment that is used. In addition, materials for a turbine blisk and a metal core 200 are not limited but can be selected according to usages. In this case, a composition of a chemical solution that can selectively etch two materials used for a turbine blisk and a metal core should be determined.

Conventionally, there is a method of using a ceramic core in which an internal vacant space having the same shape as a target object is formed in an HIP process. However, since a ceramic core and a metal core largely differ in thermal expansion coefficient, residual stress occurs in a metal at the time of cooling the metal after the HIP process is finished, which is highly likely to cause cracks in metal.

In addition, some documents present a conventional method of using a metal core instead of a ceramic core but the conventional method relates only to formation of a blade that can be easily formed through mechanical machining.

The technical gist of the present invention is to prepare the metal core 200 used to manufacture a turbine blisk having a complex structure, using a metal rapid prototyping method.

<Description of the Reference Numerals in the Drawings>
100: precision part   110: shape of precision part
200: metal core       300: housing
400: heat resistant steel powder
500: HIP furnace      600: heat resistant steel
700: etching solution S100: first step
S200: second step     S300: third step
S400: fourth step     S500: fifth step
S600: sixth step

Claims

1. A method of manufacturing a precision part through hot isostatic pressing using a metal core manufactured through metal rapid prototyping or rapid tooling, the method comprising: a first step of manufacturing the metal core in which an internal vacant space having the same shape as the precision part is formed, using a metal rapid prototyping method or a rapid tooling method;a second step of putting the metal core in a housing, filling the internal vacant space of the metal core and an inside of the housing with heat resistant steel powder, and creating a vacuum state in the housing;a third step of treating the housing under high temperature and pressure in a hot isostatic press (HIP) furnace to produce heat resistant steel;a fourth step of removing the housing and removing a portion of the heat resistant steel to expose one surface of the metal core;a fifth step of etching the metal core whose one surface is exposed, to remove the metal core; anda sixth step of removing a portion of the heat resistant steel from which the metal core is removed, through mechanical machining, in which the remaining portion of the heat resistant steel corresponds to the shape of the precision part.

2. The method of manufacturing a precision part through hot isostatic pressing using a metal core manufactured through metal rapid prototyping or rapid tooling, according to claim 1, wherein the housing is treated at a temperature of 1000° C. or higher and at 1000 bars or higher.

3. The method of manufacturing a precision part through hot isostatic pressing using a metal core manufactured through metal rapid prototyping or rapid tooling, according to claim 1, wherein the heat resistant metal is a nickel alloy.

4. The method of manufacturing a precision part through hot isostatic pressing using a metal core manufactured through metal rapid prototyping or rapid tooling, according to claim 1, wherein an etching solution in the fifth step is a nitric acid-based solution.

5. A turbo blisk for driving a turbo pump of a liquid rocket, the turbo blisk manufactured through the method according to claim 1.

6. A turbo blisk for driving a turbo pump of a liquid rocket, the turbo blisk manufactured through the method according to claim 2.

7. A turbo blisk for driving a turbo pump of a liquid rocket, the turbo blisk manufactured through the method according to claim 3.

8. A turbo blisk for driving a turbo pump of a liquid rocket, the turbo blisk manufactured through the method according to claim 4.