Masterbatch, masterbatch group, production method for masterbatch, and synthetic resin molded article

Information

  • Patent Grant
  • 10385172
  • Patent Number
    10,385,172
  • Date Filed
    Monday, September 8, 2014
    10 years ago
  • Date Issued
    Tuesday, August 20, 2019
    5 years ago
Abstract
The present invention aims to provide a masterbatch containing a large amount of an aluminum component and having high pellet strength, wherein aluminum particles retain their inherent brightness and the amount of a component which may impair the strength or appearance of a synthetic resin molded article is small. The masterbatch of the present invention contains aluminum particles, a heat-resistant wetting agent, and a resin, wherein the proportion of the aluminum particles in the masterbatch is 50 to 80% by weight, the resin has a melt flow rate of 0.2 to 60 g/10 min, and the proportion of wax having a melt flow rate of more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s in the masterbatch is 10% by weight or less.
Description
TECHNICAL FIELD

The present invention relates to a masterbatch, a masterbatch group, a method for producing the masterbatch, and a synthetic resin molded article.


BACKGROUND ART

Mixing and kneading aluminum powder with a synthetic resin is a known method for coloring a synthetic resin to give a metallic finish. Aluminum particles having a plate-like shape or a spherical shape are commonly known, and plate-like particles can give high brightness with a glittering granular appearance because the flat and smooth surface of these particles uniformly reflect light.


Use of the aluminum powder by itself is associated with a risk of dust explosion. Thus, the aluminum powder is usually wetted by a solvent such as mineral turpentine before use.


In the case where such aluminum powder that has been wetted by a solvent is mixed and kneaded with a synthetic resin, it causes the solvent to remain in the synthetic resin. Thus, the residual solvent will be volatilized into a gas during formation of a synthetic resin molded article using such a synthetic resin. This may impair the strength or appearance of the synthetic resin molded article. The residual solvent in the synthetic resin can be removed by heating during production of the synthetic resin molded article; however, it has been difficult to completely remove the solvent by this method.


In addition, the aluminum particles have poor affinity for the resin. Thus, despite attempts to disperse the aluminum particles in the resin, the aluminium particles cannot be sufficiently dispersed, resulting in color unevenness or agglomerations of the aluminum particles.


In order to solve these problems, there has been proposed a method for coloring a synthetic resin using masterbatches substantially free of a solvent which are obtained by solidifying aluminum powder with wax.


As examples of such masterbatches, Patent Literature 1 discloses an aluminum powder-containing resin composition (masterbatch) obtained by mixing an olefin resin, aluminum powder, olefin wax, and quicklime, wherein the aluminum powder content is 40%.


Patent Literature 2 discloses a masterbatch for coloring a synthetic resin, the masterbatch containing an aluminum pigment, polyethylene wax, and a linear low density polyethylene resin, wherein the aluminum pigment is contained in an amount of 60 to 80% by mass, and the polyethylene wax and the linear low density polyethylene resin are contained at a mass ratio of 9:1 to 7:3.


CITATION LIST
Patent Literature

Patent Literature 1: JP-A H06-220257


Patent Literature 2: JP-A 2010-121092


SUMMARY OF INVENTION
Technical Problem

The masterbatch disclosed in Patent Literature 1 contains an aluminum component only in a small amount. Thus, a large amount of masterbatches must be added if it is desired to increase the amount of the aluminum component in a synthetic resin molded article. In this case, the synthetic resin molded article will end up containing, besides the aluminum component, a large amount of an essentially unnecessary masterbatch component. A large amount of such an unnecessary masterbatch component may impair the strength or appearance of the synthetic resin molded article produced using the masterbatches. Further, an increase in the amount of the aluminum component in each masterbatch reduces the pellet strength of each masterbatch, making the masterbatches difficult to handle.


The masterbatch disclosed in Patent Literature 2 contains a large amount of an aluminum component, but also contains a large amount of polyethylene wax which may impair the strength or appearance of a synthetic resin molded article produced using the masterbatches.


In addition, use of a large amount of polyethylene wax reduces the pellet strength of each masterbatch, so that fine powder is easily generated as a result of cracking of the masterbatch, and the pellet shape tends to be irregular. Resin particles to be colored tend to separate from the fine power of the masterbatches in the step of forming a synthetic resin molded article because of the difference in particle size. This has been a cause of color unevenness of a synthetic resin molded article.


In addition, Patent Literature 1 and Patent Literature 2 both disclose that the masterbatch production involves a heat-mixing step to remove a solvent used as a wetting agent for the aluminum particles; and a pellet molding step. Masterbatch components are heated and dispersed in each of these two steps. Thus, the masterbatch components are prone to thermal degradation, resulting in low strength or a poor appearance of a synthetic resin molded article. Further, the shape of the plate-like aluminum particles will be cracked, bent, or broken if the particles are subjected to excessive mechanical shear during masterbatch processing. Once the aluminum particles are broken as described above, the aluminum particles tend to reduce their inherent brightness.


The present invention was made in view of the above problems. The present invention aims to provide a masterbatch containing a large amount of an aluminum component and having high pellet strength, wherein aluminum particles retain their inherent brightness and the amount of a component which may impair the strength or appearance of a synthetic resin molded article is small. The present invention also aims to provide a masterbatch group including a plurality of the masterbatches, a method for producing the masterbatch, and a synthetic resin molded article produced using the masterbatch or the masterbatch group.


Solution to Problem

The present inventors carried out extensive studies to solve the above problems. As a result, they found that it is possible to obtain a masterbatch containing a large amount of an aluminum component and having high pellet strength, wherein aluminum particles retain their inherent brightness and the amount of a component which may impair the strength or appearance of a synthetic resin molded article is small, by the following method: wetting aluminum particles by a heat-resistant wetting agent; mixing the aluminum particles with a resin having a melt flow rate of 0.2 to 60 g/10 min; and adjusting the proportion of wax in the masterbatch to be in a certain range, the wax having a melt flow rate of more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s as measured by a Brookfield viscosity. The present invention was thus completed.


Specifically, a first embodiment of the present invention relates to a masterbatch containing aluminum particles, a heat-resistant wetting agent, and a resin, wherein the proportion of the aluminum particles in the masterbatch is 50 to 80% by weight, the resin has a melt flow rate of 0.2 to 60 g/10 min, and the proportion of wax having a melt flow rate of more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s in the masterbatch is 10% by weight or less.


Preferably, in the masterbatch of the present invention, the aluminum particles are surface-coated aluminum particles.


Preferably, the masterbatch of the present invention further contains a melt tension improver.


Preferably, in the masterbatch of the present invention, the resin contains a high melt tension resin having a melt tension at 190° C. of 30 to 200 mN.


Preferably, in the masterbatch of the present invention, the resin is a polymer alloy having a melt tension at 190° C. of 20 to 100 mN.


Preferably, the masterbatch of the present invention further contains a metal deactivator.


A second embodiment of the present invention relates to a masterbatch group including a plurality of the masterbatches, wherein each masterbatch has a pellet shape, the plurality of the masterbatches included in the masterbatch group has a relative standard deviation of the major axis of 5.00% or less, the plurality of the masterbatches included in the masterbatch group has a relative standard deviation of the minor axis of 5.00% or less, and the plurality of the masterbatches included in the masterbatch group has a relative standard deviation of the length of 5.00% or less.


Preferably, in the masterbatch group of the present invention, the average major axis of the plurality of the masterbatches included in the masterbatch group is 2.0 to 4.0 mm, the average minor axis of the plurality of the masterbatches included in the masterbatch group is 2.0 to 4.0 mm, and the average length of the plurality of the masterbatches included in the masterbatch group is 2.0 to 4.0 mm.


A third embodiment of the present invention relates to a method for producing the masterbatch, the method including a mixing step of mixing an aluminum paste obtained by wetting aluminum particles by a heat-resistant wetting agent with a resin having a melt flow rate of 0.2 to 60 g/10 min so as to produce an aluminum-resin mixture in which the proportion of the aluminum particles is 50 to 80% by weight and the proportion of wax having a melt flow rate of more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s is 10% by weight or less; an extruding step of extruding the aluminum-resin mixture; and a cutting step of cutting the extruded aluminum-resin mixture.


Preferably, in the method for producing the masterbatch of the present invention, the mixing step is carried out without using a stirring member.


Preferably, in the method for producing the masterbatch of the present invention, the mixing step is carried out at 80° C. or lower, and the extruding step is carried out at 150 to 250° C.


Preferably, in the method for producing the masterbatch of the present invention, the mixing step is carried out using surface-coated aluminum particles as the aluminum particles.


A fourth embodiment of the present invention relates to a synthetic resin molded article produced using the masterbatch or the masterbatch group.


Advantageous Effects of Invention

The masterbatch of the present invention contains a heat-resistant wetting agent and a resin having a melt flow rate of 0.2 to 60 g/10 min. Thus, although the masterbatch does not contain a component such as wax which may impair the strength or appearance of a synthetic resin molded article, the proportion of the aluminum particles in the masterbatch is 50 to 80% by weight while maintaining a high pellet strength. Namely, the masterbatch can have a high aluminum particle concentration while maintaining a high pellet strength. If the pellet strength of each masterbatch is high, the amount of fine powder to be generated from broken masterbatches due to vibration, contact, or the like will be small. Thus, each masterbatch has a uniform pellet shape, and these masterbatches are less likely to be non-uniformly dispersed during synthetic resin molded article processing. As a result, it is possible to suppress color unevenness attributable to non-uniform dispersion of the masterbatches during synthetic resin molded article processing.


In the masterbatch of the present invention, the proportion of the aluminum particles in the masterbatch is 50 to 80% by weight. Thus, it is possible to reduce the amount of a masterbatch component other than the aluminum component in a synthetic resin molded article. Thus, the masterbatch is less likely to result in low strength or a poor appearance of the synthetic resin molded article.


Further, the proportion of the wax having a melt flow rate of more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s in the masterbatch of the present invention is 10% by weight or less. Thus, the masterbatch is less likely to result in low strength or a poor appearance of a synthetic resin molded article.





BRIEF DESCRIPTION OF DRAWINGS


FIG. 1 is a schematic perspective view of a masterbatch of the present invention which is formed to have a pellet shape.



FIG. 2 is an image of a masterbatch group according to Example 1.



FIG. 3 is an image of a masterbatch group according to Comparative Example 2.



FIG. 4(a) is a 1000 times magnified microscopic image of the shape of aluminum particles in a synthetic resin molded article formed using the masterbatches according to Example 1. FIG. 4(b) is a 3000 times magnified image.



FIG. 5(a) is a 1000 times magnified microscopic image of the shape of aluminum particles in a synthetic resin molded article formed using the masterbatches according to Comparative Example 2. FIG. 5(b) is a 3000 times magnified image.



FIG. 6(a) is a 1000 times magnified microscopic image of the shape of aluminum particles in an aluminum paste.



FIG. 6(b) is a 3000 times magnified image.





DESCRIPTION OF EMBODIMENTS

The proportion of the aluminum particles in the masterbatch of the present invention is 50 to 80% by weight. The proportion of the aluminum particles is more preferably 60 to 80% by weight, still more preferably 65 to 80% by weight.


If the proportion of the aluminum particles in the masterbatch is more than 80% by weight, each masterbatch will have lower pellet strength and will be susceptible to cracking, chipping, or the like. Thus, the masterbatches will be difficult to handle. Further, fine fragments or powder may result from cracking, chipping, or the like. Such fine fragments or powder tends to cause color unevenness in a synthetic resin molded article. In addition, such fragments or powder of the masterbatches may remain in a container when moving the masterbatches from the container. In other words, the fragments or powder of the masterbatches may not be used for production of a synthetic resin molded article. Thus, generation of fragments or powder of the masterbatches is economically disadvantageous.


If the proportion of the aluminum particles in each masterbatch is less than 50% by weight, a masterbatch component other than the aluminum component is necessarily added in a large amount to produce a synthetic resin molded article. Such a masterbatch component may impair the strength or appearance of the synthetic resin molded article produced using such masterbatches.


It is preferred that the aluminum particles contained in the masterbatch of the present invention have a uniform shape and a smooth surface without being broken or bent and that the aluminum particles are not agglomerated by overlapping.


Breaking or bending of the aluminum particles creates bumps on the surface of the aluminum particles, thus diffusing light. The diffused light is absorbed at the interface of another aluminum particle, thus decreasing the brightness. In addition, the aluminum particles that are broken or bent into small pieces cannot provide a glittering and clear grainy appearance.


The aluminum particles that are not broken or bent can sufficiently increase the brightness of the masterbatch. Thus, a synthetic resin molded article produced using the masterbatches of the present invention can be provided with a clear metallic luster.


The average particle size of the aluminum particles is not limited, but it is preferably 5 to 100 μm, more preferably 5 to 50 μm.


The shape of the aluminum particles is not limited, but plate-like particles having a flake shape or a coin shape are preferred. The term “plate-like particles” refers to the particles having a shape in which the ratio of the average particle size to the average thickness (average particle size:average thickness) is 5:1 to 1000:1. If the aluminum particles has a plate-like shape, the ratio of the average particle size to the average thickness (average particle size:average thickness) is preferably 5:1 to 1000:1.


A synthetic resin molded article produced using masterbatches containing such aluminum particles has a highly bright and glittering granular appearance which is similar to the appearance of a molded article coated with aluminum.


The term “average particle size of the aluminum particles” as used herein refers to a value calculated based on the particle size distribution as measured by a conventional particle size distribution measurement method such as laser diffractometry.


The aluminum particles may be untreated aluminum particles which are not surface-treated, or surface-coated aluminum particles which are surface-treated.


The term “surface-coated aluminum particles” refers to the aluminum particles obtained by coating the surface of untreated aluminum particles with a substance such as resin, inorganic compound, organosilicon compound, coupling agent, or any other organic compound.


If the aluminum particles are surface-coated aluminum particles, the aluminum particles will exhibit higher affinity for the resin, which results in good melt tension, making strands less likely to break off. The resulting masterbatch is provided with sufficient strength and higher brightness.


It is also possible to prevent the aluminum-catalyzed oxidation of the resin and the wax in the masterbatch. Thus, a synthetic resin molded article produced using the masterbatches of the present invention can be prevented from having fisheyes and gel particles that are generated from oxidization of the resin and the wax in the masterbatch.


The surface-coated aluminum particles are not limited, but resin-coated aluminum particles are preferred. More preferably, the resin is acrylic resin, melamine resin, epoxy resin, urethane resin, or polyester resin.


In the case where the surface-coated aluminum particles are aluminum particles coated with an inorganic compound, the inorganic compound is preferably, for example, an oxide, a hydrated oxide, or a hydroxide of aluminum or silicon.


In the case where the surface-coated aluminum particles are aluminum particles coated with an organosilicon compound, the organosilicon compound is preferably, for example, an alkoxysilane compound, a chlorosilane compound, a silazane compound, a reactive silicone, or a modified silicone.


In the case where the surface-coated aluminum particles are aluminum particles coated with a coupling agent, the coupling agent is preferably, for example, a silane-based, titanate-based, aluminate-based, or zirconium-based coupling agent.


In the case where the surface-coated aluminum particles are aluminum particles coated with a different organic compound other than the organic compounds described above, the different organic compound is preferably a saturated fatty acid or an unsaturated fatty acid.


The surface-coated aluminum particles described above may be commercially available products. Examples of the surface-coated aluminum particles having a surface coated with acrylic resin include astroflake available from Hori Metal Leaf & Powder Co., Ltd.; FZ series, BP series and PCF series available from Toyo Aluminum K.K.; and TR series and HR series available from Asahi Kasei Metals Co., Ltd.


In the case where the aluminum particles are resin-coated aluminum particles, the resin for coating the aluminum may be mixed with another resin such as polyolefin resin that is mixed during masterbatch production. In such a case, the resin in the masterbatch is a mixture of the resin for coating the aluminum and the resin such as polyolefin resin. Thus, the melt flow rate of the resin in the masterbatch may be considered as the melt flow rate of the mixture. In reality; however, the resin for coating the aluminum has hardly any effect on the melt flow rate of the mixture, so that the result is substantially the same even if only taking into account the melt flow rate of the resin such as polyolefin resin that is mixed during masterbatch production. Therefore, as long as a resin having a melt flow rate of 0.2 to 60 g/10 min is used as a resin to be mixed during masterbatch production, the resin contained in the masterbatch of the present invention is considered to have a melt flow rate in the range of 0.2 to 60 g/10 min.


Examples of the surface-coated aluminum particles having a surface coated with silica include Chromashine available from Toyo Aluminum K.K.


Examples of the surface-coated aluminum particles having a surface coated with a coupling agent include LX series available from Toyo Aluminum K.K.


The masterbatch of the present invention contains a heat-resistant wetting agent.


In the production of the synthetic resin molded article, the masterbatches and the resin are heated and melt-kneaded. At this point, usually, the kneaded mixture is heated at 150° C. to 250° C.


If the masterbatch contains a conventional wetting agent such as mineral turpentine, the wetting agent may be volatilized into a gas by heating. The gas generated from volatilization may impair the appearance and strength of a synthetic resin molded article.


In contrast, the masterbatch of the present invention contains a heat-resistant wetting agent, so that the heat-resistant wetting agent is hardly volatilized into a gas even when heated during melt-kneading and is thus less likely to result in a poor appearance and low strength of a synthetic resin molded article.


The heat-resistant wetting agent contained in the masterbatch of the present invention is defined as follows.


In the case of wetting agents having a boiling point, the heat-resistant wetting agent is one having a boiling point of 250° C. or higher.


In the case of wetting agents that are volatilized into a gas by pyrolysis before boiling, the heat-resistant wetting agent is one having an intermediate pyrolysis temperature of 250° C. or higher in a nitrogen atmosphere.


The intermediate pyrolysis temperature is a value determined according to JIS K 7120 using a thermogravimetric balance.


The heat-resistant wetting agent is not limited. Examples include polyethylene glycols; phosphoric esters such as and triphenyl phosphate; phthalate esters such as bis(2-ethylhexyl)phthalate and dibutyl phthalate; and aliphatic esters such as bis(2-ethylhexyl) adipate, dibutyl adipate, bis(2-ethylhexyl) sebacate, and dibutyl sebacate. Polyethylene glycols are preferred among these.


The masterbatch of the present invention may contain one or a combination of two or more of the heat-resistant wetting agents.


The aluminum particles wetted by the heat-resistant wetting agent may be commercially available products. Examples include Silveeds series (aluminum particles wetted by polyethylene glycol) available from Asahi Kasei Chemicals Corporation; and No. 300 80PA (aluminum particles wetted by bis(2-ethylhexyl)phthalate) and No. 300 DOA (aluminum particles wetted by bis(2-ethylhexyl) adipate) available from Yamato Metal Powder Co., Ltd.


In addition, the intermediate pyrolysis temperature of the heat-resistant wetting agent in the wetted aluminum particles in a nitrogen atmosphere can be measured according to JIS K 7120 as is the case with the intermediate pyrolysis temperature of the heat-resistant wetting agent described above, and is substantially the same as the intermediate pyrolysis temperature measured for the wetting agent itself.


If the heat-resistant wetting agent is a polyethylene glycol, a polyethylene glycol having an intermediate pyrolysis temperature of 250° C. or higher and a freezing point of −20° C. or higher is preferred.


The term “freezing point” of the polyethylene glycol refers to the freezing point of a chemical product as measured according to JIS K 0065 specified in the Japanese Industrial Standards.


The weight ratio of the heat-resistant wetting agent to the aluminum particles (wetting agent:aluminum particles) is preferably 5:95 to 30:70, more preferably 5:95 to 15:85.


If the proportion of the heat-resistant wetting agent exceeds the above range, the proportion of the aluminum particles will be low, so that the masterbatch produced will fail to have a sufficiently high aluminum particle concentration, and the proportion of a resin in the masterbatch will be low. The masterbatch having a lower resin proportion tends to have low pellet strength. An excess proportion of the heat-resistant wetting agent also results in a decrease in measurability and in stable supply of the aluminum paste during masterbatch production.


If the proportion of the heat-resistant wetting agent is below the above range, the dust of the aluminum particles will easily spread in the air during masterbatch production, which may cause a dust explosion.


The masterbatch of the present invention contains a resin having a melt flow rate of 0.2 to 60 g/10 min. The melt flow rate of the resin is preferably 0.2 to 40 g/10 min, more preferably 0.2 to 30 g/10 min.


Such a resin can improve the pellet strength of each masterbatch.


If the melt flow rate of the resin is more than 60 g/10 min, the pellet strength of each masterbatch will be reduced, making the masterbatch susceptible to cracking, chipping, or the like. Thus, the masterbatches will be difficult to handle. Further, fine fragments or powder will be easily generated, which is economically disadvantageous.


If the melt flow rate of the resin is less than 0.2 g/10 min, the pellet strength of each masterbatch will be too high. Thus, these masterbatches are likely to be insufficiently kneaded during production of a synthetic resin molded article. This may cause color unevenness in a synthetic resin molded article.


The term “melt flow rate” as used herein refers to the fluidity as measured according to JIS K 7210: 1999 (ISO 1333: 1997) specified in the Japanese Industrial Standards.


The proportion of the resin having a melt flow rate of 0.2 to 60 g/10 min in the masterbatch is preferably 8 to 45% by weight, more preferably 10 to 35% by weight.


A masterbatch containing the resin having a melt flow rate of 0.2 to 60 g/10 min in a proportion of less than 8% by weight tends to have low pellet strength and exhibits markedly poor processability during its production.


A masterbatch containing the resin having a melt flow rate of 0.2 to 60 g/10 min in a proportion of more than 45% by weight fails to have a sufficiently high aluminum particle concentration. Thus, a masterbatch component other than the aluminum component is necessarily added in a large amount to produce a synthetic resin molded article. This may impair the strength or appearance of the synthetic resin molded article produced using such masterbatches.


Examples of the resin include polyolefin resins such as polyethylene resin and polypropylene resin, polyacetal resin, polystyrene resin, acrylonitrile resin, ABS resin, PMMA resin, polycarbonate resin, PBT resin, and PET resin.


Among these, polyolefin resins such as polyethylene resin and polypropylene resin are preferred.


The melt flow rate of the resin can be measured by the method specified in JIS K 7210: 1999. For example, polyethylene resin can be measured at a test temperature of 190° C. and a nominal load of 2.16 kg; polypropylene resin at a test temperature of 230° C. and a nominal load of 2.16 kg; polyacetal resin at a test temperature of 190° C. and a nominal load of 2.16 kg; polystyrene resin at a test temperature of 200° C. and a nominal load of 5 kg; acrylonitrile resin at a test temperature of 220° C. and a nominal load of 10 kg; ABS resin at a test temperature of 220° C. and a nominal load of 10 kg; PMMA resin at a test temperature of 230° C. and a nominal load of 3.8 kg; polycarbonate resin at a test temperature of 300° C. and a nominal load of 1.2 kg; PBT resin at a test temperature of 260° C. and a nominal load of 2.16 kg; and PET resin at a test temperature of 280° C. and a nominal load of 5 kg.


The proportion of the wax having a melt flow rate of more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s in the masterbatch of the present invention is 10% by weight or less.


That the proportion of the wax in the masterbatch is 10% by weight or less means that the masterbatch does not contain any wax or that the wax content (if any) is 10% by weight or less.


The masterbatch of the present invention may contain wax. The presence of wax makes the aluminum particles compatible with the resin during masterbatch processing, allowing the aluminum particles to be uniformly dispersed.


However, if the proportion of the wax is more than 10% by weight, the pellet strength of each masterbatch will be reduced, and such wax content may impair the strength of a synthetic resin molded article produced using the masterbatches.


In addition, the wax is easily oxidized. The oxidized wax has a partially modified molecular chain, and thus has poor compatibility with the resin and poor diffusibility. Thus, the masterbatches will not be uniformly dispersed during synthetic resin molded article formation, which may cause the generation of fisheyes and gel particles on the surface of the synthetic resin molded article.


The proportion of the wax in the masterbatch is not limited as long as it is 10% by weight or less; however, it is preferably 0.00001 to 5.0% by weight, more preferably 0.1 to 3.0% by weight.


The term “wax” as used herein refers to a low-density, low-crystalline resin having a melt-starting temperature of 40° C. or higher, a melt flow rate of more than 60 g/10 min as measured under conditions of a temperature of 190° C. and a load of 2.16 kg, and a melt viscosity at 140° C. of 15 to 8000 mPa·s.


The melt-starting temperature can be measured by differential scanning calorimetry (DSC) according to JIS K 7121.


The melt viscosity can be measured with a Brookfield viscometer.


Examples of the wax include polyethylene wax, polypropylene wax, paraffin wax, microcrystalline wax, Fischer-Tropsch wax, carnauba wax, and products obtained by modifying these waxes with acid such as maleic acid or carboxylic acid.


The melt flow rate of these waxes can be measured by the method specified in JIS K 7210: 1999. For example, polyethylene wax can be measured at a test temperature of 190° C. and a nominal load of 2.16 kg; polypropylene wax at test temperature of 190° C. and a nominal load of 2.16 kg; paraffin wax at a test temperature of 190° C. and a nominal load of 2.16 kg; microcrystalline wax at a test temperature of 190° C. and a nominal load of 2.16 kg; Fischer-Tropsch wax at a test temperature of 190° C. and a nominal load of 2.16 kg; and carnauba wax at a test temperature of 190° C. and a nominal load of 2.16 kg.


In the case of using another wax, the melt flow rate can be measured at a test temperature of 190° C. and a nominal load of 2.16 kg.


The masterbatch of the present invention containing the above described elements has high pellet strength.


If the pellet strength is high, the amount of fine powder to be generated from broken masterbatches due to vibration, contact, or the like will be small. Thus, the pellets will have a uniform shape, and the masterbatches are less likely to be non-uniformly dispersed during synthetic resin molded article processing. As a result, it is possible to suppress color unevenness attributable to non-uniform dispersion of the masterbatches during synthetic resin molded article processing.


Preferably, the masterbatch of the present invention contains a melt tension improver. Owing to the presence of the melt tension improver, the masterbatches having a uniform pellet shape can be easily obtained.


Examples of the melt tension improver include a fluorine-based melt tension improver and an acrylic melt tension improver, with the fluorine-based melt tension improver being preferred.


Examples of the fluorine-based melt tension improver include polytetrafluoroethylene (product name “Fluon PTFE CD145E” available from AGC, and product name “Polyflon FA-500H” available from Daikin Industries, Ltd.), and composites formed from polytetrafluoroethylene and an alkyl methacrylate-alkyl acrylate copolymer (product names “Metablen A3000” and “Metablen A3800” available from Mitsubishi Rayon Co., Ltd.). Examples of the acrylic melt tension improver include alkyl methacrylate copolymers (product names “Metablen P530” and “Metablen P570” available from Mitsubishi Rayon Co., Ltd.).


The proportion of the melt tension improver in the masterbatch is preferably 0.1 to 5.0% by weight, more preferably 0.3 to 3.0% by weight.


Preferably, in the masterbatch of the present invention, the resin contains a high melt tension resin having a melt tension at 190° C. of 30 to 200 mN. If the resin contains a high melt tension resin, the masterbatches having a uniform pellet shape can be easily obtained. Masterbatches having a uniform pellet shape are less likely to be non-uniformly dispersed during production of a synthetic resin molded article using these masterbatches, making it possible to prevent color unevenness. In addition, such masterbatches are easy to handle during production of a synthetic resin molded article.


The term “high melt tension resin” as used herein refers to a resin having a melt tension at 190° C. of 30 to 200 mN.


The melt tension at 190° C. of the high melt tension resin is preferably 30 to 200 mN, more preferably 50 to 200 mN.


Examples of the high melt tension resin include a resin having a melt flow rate of 0.4 g/10 min and a melt tension of 88 mN (product name “HI-ZEX 6200BPU” available from Prime Polymer Co., Ltd.).


The melt tension of the resin can be measured with a capilograph.


The resin is measured under the following conditions.


Measuring device: capilograph (Toyo Seiki Co., Ltd.)


Capillary inner diameter: 2.095 mm


Capillary length: 8.0 mm


Measurement temperature: 190° C.


Extrusion rate: 10 mm/min


Haul-off speed: 5 m/min


Preferably, in the masterbatch of the present invention, the resin is a polymer alloy having a melt tension at 190° C. of 20 to 100 mN. If the resin is such a polymer alloy, the balance between melt flow rate and melt tension can be easily adjusted, and the masterbatches having a uniform pellet shape can be easily obtained. In addition, various characteristics can be imparted to the masterbatch by the selection of resin.


The polymer alloy is not limited, but preferably, it includes any combination of resins selected from high melt tension polyethylene, polyethylene resin, polypropylene resin, ethylene-vinyl acetate copolymer, and ethylene-acrylic acid copolymer. Among these, a combination of high melt tension polyethylene, polyethylene resin, and polypropylene resin is preferred. If the polymer alloy is a combination of high melt tension polyethylene, polyethylene resin, and polypropylene resin, the weight ratio of these components (high melt tension polyethylene:polyethylene resin:polypropylene resin) is preferably 10-50:10-50:10-50.


Preferably, the masterbatch of the present invention further contains a metal deactivator. The presence of the aluminum in the masterbatch makes the resin and the wax susceptible to aluminum-catalyzed oxidation. The oxidized resin and the oxidized wax may cause the generation of fisheyes and gel particles on the surface of a synthetic resin molded article.


The presence of a metal deactivator in the masterbatch can prevent the aluminum-catalyzed oxidation of the resin and the wax.


The metal deactivator is not limited. Examples include triazine-based compounds (1,3,5-triazine-2,4,6-triamine (product name “Adekastab ZS-27” available from ADEKA)), a phenolic compounds (2-hydroxy-N-1H-1,2,4-triazol-3-ylbenzamide (product name “Adekastab CDA-1” available from ADEKA)), and N,N′-bis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionyl]hydrazine (product name “Irganox MD1024” available from BASF)).


The shape of the masterbatch of the present invention is not limited. Examples include a pellet shape, a rod shape, and a spherical shape. Among these, a pellet shape is preferred. The masterbatch of the present invention having a pellet shape is described below with reference to a drawing.



FIG. 1 is a schematic perspective view of the masterbatch of the present invention which is formed to have a pellet shape.


As shown in FIG. 1, a masterbatch 10 having a pellet shape is formed in a generally elliptical cylindrical shape and has a generally elliptical bottom 11 and a generally elliptical top 12. The bottom 11 is generally congruent with the top 12. The term “generally elliptical” as used herein includes a generally circular shape, and thus the masterbatch 10 having a pellet shape may be formed in a columnar shape.


The term “length” of the masterbatch as used herein refers to the distance (L) between the bottom 11 and the top 12. The term “major axis” of the masterbatch as used herein refers to the major axis (D1) of the bottom 11 or the top 12. The term “minor axis” of the masterbatch as used herein refers to the minor axis (D2) of the bottom 11 or the top 12. In the case where the bottom 11 and the top 12 are circle, the major axis D1 and the minor axis D2 are equal to each other.


Masterbatches having a pellet shape are less likely to vary in shape, so that the masterbatches are less likely to be non-uniformly dispersed during production of a synthetic resin molded article using these masterbatches, making it possible to prevent color unevenness.


The masterbatch of the present invention may contain any conventional additive as long as the effects of the present invention are not impaired. Examples of such additives include fillers such as talc and silica; organic pigments such as azo-based pigment, anthraquinone-based pigment, quinacridone-based pigment, phthalocyanine-based pigment, perylene-based pigment, perinone-based pigment, dioxazine-based pigment, and quinophthalone-based pigment; inorganic pigments such as titanium oxide, red oxide, ultramarine, Prussian blue, yellow iron oxide, chrome yellow, chrome bar million, and composite oxide-based pigment; pigments such as carbon black; and dispersants.


The present invention also relates to a masterbatch group including a plurality of the masterbatches of the present invention, wherein each masterbatch has a pellet shape, the plurality of the masterbatches included in the masterbatch group has a relative standard deviation of the major axis of 5.00% or less, the plurality of the masterbatches included in the masterbatch group has a relative standard deviation of the minor axis of 5.00% or less, and the plurality of the masterbatches included in the masterbatch group has a relative standard deviation of the length of 5.00% or less.


Such a masterbatch group consists of the masterbatches having a substantially uniform shape, so that color unevenness is less likely to occur in a synthetic resin molded article produced using such masterbatches.


The relative standard deviation of the major axis, the relative standard deviation of the minor axis, and the relative standard deviation of the length of the plurality of the masterbatches are not limited as long as they are in the above ranges. However, preferably, the relative standard deviation of the major axis is 3.00% or less, the relative standard deviation of the minor axis is 3.00% or less, and the relative standard deviation of the length is 3.00% or less.


Preferably, in the masterbatch group of the present invention, the average major axis of the plurality of the masterbatches included in the masterbatch group is 2.0 to 4.0 mm, an average minor axis of the plurality of the masterbatches included in the masterbatch group is 2.0 to 4.0 mm, and an average length of the plurality of the masterbatches included in the masterbatch group is 2.0 to 4.0 mm, though not limited as long as they are in the above relative standard deviation ranges. More preferably, the plurality of the masterbatches has an average major axis of 2.5 to 3.6 mm, an average minor axis of 2.5 to 3.6 mm, and an average length of 2.5 to 3.6 mm.


Such masterbatches having the above size are easy to handle during production of a synthetic resin molded article.


An example of the method for producing the masterbatch of the present invention is described below.


(a) Aluminum Paste Preparing Step


First, an aluminum paste is prepared by wetting aluminum particles by a heat-resistant wetting agent.


Aluminum particles in powder form (hereinafter also referred to as “aluminum powder”) are very easily oxidized, and the spread of dust caused by scattering of the aluminum powder in the air may cause a dust explosion. Thus, a wetting agent such as mineral turpentine is usually applied to suppress scattering of the aluminum powder before use. However, if a low-boiling wetting agent such as mineral turpentine is used as the wetting agent for the aluminum powder, a gas will be easily generated by volatilization from masterbatch. A synthetic resin molded article produced using the masterbatches may have poor appearance and low strength.


Thus, the wetting agent is preferably a heat-resistant wetting agent.


The aluminum particles may be untreated aluminum particles that are not surface-treated, or may be surface-coated aluminum particles that are surface-treated.


If the aluminum particles are surface-coated aluminum particles, wearing of the aluminum metal portions of the aluminum particles can be prevented in the later-described mixing step (b), which otherwise occurs due to the aluminum particles come to contact with each other. Wearing of the aluminum metal portions of the aluminum particles reduces the brightness of the aluminum particles, thus reducing the brightness of the masterbatch as well. However, if the aluminum particles are surface-coated aluminum particles, wearing of the aluminum metal portions of the aluminum particles can be prevented, so that a reduction in the brightness of the masterbatch produced through the subsequent steps can be prevented.


The surface-coated aluminum particles are not limited, but they are preferably resin-coated aluminum particles. If the surface-coated aluminum particles are resin-coated aluminum particles, the aluminum particles will exhibit higher affinity for the resin in the later-described mixing step. As a result, the masterbatch containing the resin-coated aluminum particles is provided with sufficient strength, and strands thereof are less likely to break off and have good melt tension.


The resin-coated aluminum particles have been described so that the description thereof is omitted here.


The method for wetting aluminum particles by a heat-resistant wetting agent is not limited. For example, any known mixer such as a ball mill, Proshare mixer, Nauta mixer, tumbler mixer, or Henschel mixer can be used.


The weight ratio of the aluminum particles to the heat-resistant wetting agent (heat-resistant wetting agent:aluminum particles) in the aluminum paste is preferably 5:95 to 30:70, more preferably 5:95 to 15:85.


If the proportion of the heat-resistant wetting agent exceeds the above range, the proportion of the aluminum particles will be low, so that the masterbatch produced will fail to have a sufficiently high aluminum particle concentration, and the proportion of a resin in the masterbatch will be low. The masterbatch having a lower resin proportion tends to have low pellet strength. An excess proportion of the heat-resistant wetting agent also results in a decrease in measurability and in stable supply of the aluminum paste during masterbatch production.


If the proportion of the heat-resistant wetting agent is below the above range, the dust of the aluminum particles will easily spread in the air during masterbatch production, which may cause a dust explosion.


(b) Mixing Step


Subsequently, the aluminum paste obtained by wetting the aluminum particles by the heat-resistant wetting agent is mixed with a resin having a melt flow rate of 0.2 to 60 g/10 min, to prepare an aluminum-resin mixture in which the proportion of aluminum particles is 50 to 80% by weight, and the proportion of wax having a melt flow rate or more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s is 10% by weight or less.


In the mixing step, additives such as a melt tension improver and a metal deactivator may be mixed together. Preferred examples of the melt tension improver and the metal deactivator include those described above for the masterbatch of the present invention.


The resin to be used in the mixing step may be a single resin or a polymer alloy containing a mixture of two or more resins. The resin to be used in the mixing step may also be a high melt tension resin having a melt tension at 190° C. of 30 to 200 mN.


If the resin is a polymer alloy containing two or more resins, the melt tension at 190° C. is preferably 20 to 100 mN. A preferred resin combination of the polymer alloy may be one described above for the case where the resin in the masterbatch of the present invention is a polymer alloy.


Preferably, in the method for producing the masterbatch of the present invention, the mixing step is carried out without using a stirring member.


The stirring member refers to a member such as a stirring blade or a stirring bar that comes to physical contact with the aluminum paste and the resin for kneading. Use of such a stirring member causes wearing of the aluminum particles in the aluminum paste due to contact with the stirring member. Wearing of the aluminum particles reduces the brightness of the aluminum particles. This leads to a reduction in the brightness of the masterbatch produced through the subsequent steps.


The method for mixing the aluminum paste and the resin without using a stirring member is not limited. Examples include mixing by rotating a container and mixing by oscillating a container. Use of these methods allows the aluminum paste and the resin to be mixed together without wearing of the aluminum particles in the aluminum paste.


The mixing temperature is not limited. However, the mixing step in the method for producing the masterbatch of the present invention is preferably carried out at 80° C. or lower, more preferably at 60° C. or lower.


With the mixing temperature in the above range, heat-induced oxidation of the resin and the wax can be prevented. As a result, it is possible to prevent the generation of fisheyes and gel particles on the surface of a synthetic resin molded article produced using the masterbatches produced through the subsequent steps.


It is also possible to prevent the aluminum particles from being broken by shear strength applied thereto during melting of the resin and the wax. This makes it possible to process the masterbatch while retaining the inherent brightness of the aluminum particles.


Preferably, the aluminum-resin mixture has a melt tension at 230° C. of 30 to 150 mN. Such an aluminum-resin mixture can be suitably extruded in the later-descried extruding step (c).


The method for adjusting the melt tension is not limited. Examples include a method in which a melt tension improver is added, a method in which a high melt tension resin having a melt tension at 190° C. of 30 to 200 mN is added, and a method in which two or more resins are mixed together to obtain a polymer alloy.


(c) Extruding Step


Subsequently, the aluminum-resin mixture obtained in the above step is extruded.


Extrusion is a process where the aluminum-resin mixture is pushed out from a die using a pushing member such as a screw so as to mold the aluminum-resin mixture into a specific shape.


The extruding temperature is not limited. However, the extruding step in the method for producing the masterbatch of the present invention is preferably carried out at 150° C. to 250° C., more preferably at 160° C. to 230° C. Extrusion at a temperature in the above range causes the resin in the aluminum-resin mixture to quickly melt. Once the resin is melted, wearing of the aluminum particles due to contact with a screw or the like can be prevented. Thus, it is possible to improve the brightness of the masterbatch produced through the subsequent steps.


(d) Cutting Step


Subsequently, the aluminum-resin mixture extruded in the above step is cut.


The cutting method is not limited, but preferably, the aluminum-resin mixture is cut into a pellet shape. Examples of such a cutting method include a strand cutting method.


The masterbatch of the present invention can be produced through the above steps.


(Synthetic Resin Molded Article)


The masterbatch or the masterbatch group of the present invention is kneaded into a synthetic resin in an appropriate manner, whereby a synthetic resin molded article can be suitably produced. In other words, the synthetic resin molded article of the present invention is produced using the masterbatch or the masterbatch group of the present invention.


The synthetic resin is not limited. Examples include olefin resins such as polyethylene resin and polypropylene resin and thermoplastic resins such as polystyrene resin, ABS resin, polyamide resin, polyethylene terephthalate, and polybutylene terephthalate.


The amount of the masterbatches in the synthetic resin is preferably 0.1 to 10.0% by weight, more preferably 0.3 to 5.0% by weight. If the amount of the masterbatches is in the range of 0.1 to 10.0% by weight, the amount of a masterbatch component other than the aluminum component in a synthetic resin molded article will be sufficiently small. Thus, the synthetic resin molded article is prevented from having low strength or a poor appearance.


EXAMPLES

The present invention is described in further detail below with reference to examples, but the present invention is not limited to these examples.


Example 1

A masterbatch according to Example 1 was produced by the following procedure.


(a) Aluminum Paste Preparing Step


An aluminum paste (product name “Silveeds M100-BP” available from Asahi Kasei Chemicals Corporation) containing aluminum particles (average particle size: 10 μm, average thickness: 0.2 μm, shape: coin shape) and a polyethylene glycol at a weight ratio (aluminum particles:polyethylene glycol) of 90:10 was provided.


The intermediate pyrolysis temperature of the aluminum paste in a nitrogen atmosphere was 270° C. or higher.


(b) Mixing Step


To a container rotary-type mixer (model name “Tumbler ST-50E” available from Kawata MFG Co., Ltd.) were added 77.8% by weight of the aluminum paste, 19.9% by weight of polyethylene resin (melt flow rate of 22 g/10 min (test temperature: 190° C., nominal load: 2.16 kg), product name “Novatec LJ803” available from Japan Polyethylene Corporation), 1.0% by weight of maleic acid-modified wax (melt flow rate of 9680 g/10 min (test temperature: 190° C., nominal load: 2.16 kg), melt viscosity at 140° C. of 150 mPa·s, product name “Mitsui Hiwax 1105A” available from Mitsui Chemicals, Inc.), 1.0% by weight of a fluorine-based melt tension improver (an additive obtained by acrylic modification of polytetrafluoroethylene, product name “Metablen A3800” available from Mitsubishi Rayon Co., Ltd.), 0.2% by weight of an acrylic melt tension improver A (a high-molecular-weight acrylic polymer, product name “Metablen P570” available from Mitsubishi Rayon Co., Ltd.), and 0.1% by weight of a metal deactivator (N,N′-bis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionyl]hydrazine, product name “Irganox MD1024” available from BASF). These components were mixed at room temperature for 10 minutes. Thus, an aluminum-resin mixture was prepared.


(c) Extruding Step


The aluminum-resin mixture prepared in the above step was fed into an extruder (model name “TEM-37SS” available from Toshiba Machine Co., Ltd.). Subsequently, the aluminum-resin mixture was extruded at an extrusion temperature of 170° C. and a screw rotation speed of 150 rpm. The extruded aluminum-resin mixture was a noodle-like molded product having a major axis of 2.9 mm and a minor axis of 2.7 mm.


(d) Cutting Step


The extruded aluminum-resin mixture obtained in the above step was cut into 2.7 mm-long pieces by strand-cut method.


The obtained pellet-shaped product is a masterbatch according to Example 1, and a group of a plurality of the masterbatches is a masterbatch group according to Example 1. FIG. 2 shows the appearance of the masterbatch group according to Example 1. FIG. 2 is an image of the masterbatch group according to Example 1.


Example 2 to Example 7

Masterbatches according to Example 2 to Example 7 were produced in the same manner as in Example 1 except that the masterbatch composition was changed as shown in Table 1.


The numbers in the composition shown in Table 1 represent the percentage by weight.


In Table 1, the acrylic melt tension improver B is a high-molecular-weight acrylic polymer (product name “Metablen P530” available from Mitsubishi Rayon Co., Ltd.); the polypropylene resin is polypropylene (product name “H-700” available from Prime Polymer Co., Ltd) having a melt flow rate of 8.0 g/10 min (test temperature: 230° C., nominal load: 2.16 kg) and a melt tension at 190° C. of 18.6 mN; and the high melt tension polyethylene is polyethylene (product name “HI-ZEX 6200BPU” available from Prime Polymer Co., Ltd) having a melt flow rate of 0.4 g/10 min (test temperature: 190° C., nominal load: 2.16 kg) and melt tension at 190° C. of 88 mN.


Example 8

A masterbatch according to Example 8 was produced by changing the aluminum paste to be prepared in the aluminum paste preparing step (a) in Example 1 as follows.


An aluminum paste containing acrylic resin-coated surface-coated aluminum particles (product name “PCF7640” available from Toyo Aluminum K.K., average particle size: 18 μm, average thickness: 0.4 μm) and a polyethylene glycol at a weight ratio (aluminum particles:polyethylene glycol) of 90:10 was prepared.


Comparative Example 1

A masterbatch according to Comparative Example 1 was produced in the same manner as in Example 1 except that the masterbatch composition was changed as shown in Table 1.


In Table 1, the polyethylene wax is polyethylene (product name “Hiwax NL900” available from Mitsui Chemicals, Inc.) having a melt flow rate of 4840 g/10 min (test temperature: 190° C., nominal load: 2.16 kg) and a melt viscosity at 140° C. of 7400 mPa·s.


Comparative Example 2

A masterbatch according to Comparative Example 2 was produced by changing the process including mixing step (b) to the cutting step (d) in the Example 1 to the process described below. The masterbatch composition according to Comparative Example 2 is the same as that according to Comparative Example 1.


First, the raw materials in proportions shown in Table 1 were kneaded using a universal stirrer at a heating temperature of 160° C. to produce an aluminum-resin mixture.


Subsequently, the obtained aluminum-resin mixture was pre-crushed using a crusher, and a cylindrical pellet-shaped product having a diameter of 2.0 mm and a length of 7.8 mm, i.e., a masterbatch, was produced using a disk pelletizer (model name “Disk Pelleter F60” available from Dalton Co., Ltd.).


The obtained cylindrical pellet-shaped product is the masterbatch according to Comparative Example 2, and a group of a plurality of the masterbatches is a masterbatch group according to Comparative Example 2. FIG. 3 shows the appearance of the masterbatch group according to Comparative Example 2. FIG. 3 is an image of the masterbatch group according to Comparative Example 2.


(Processability Evaluation)


The masterbatches according to Examples 1 to 8 and Comparative Example 1 were evaluated for the processability. The evaluation was based on the following criteria.


1. Extrusion Evaluation


Good: Extrusion can be carried out without any trouble. The discharge state is stable.


Fair: Extrusion can be carried out with some trouble.


Poor: Extrusion is difficult to carry out and the melt cannot be discharged from the die.


2. Strand State Evaluation


Good: Strands are strong and do not break off.


Fair: Strands are slightly weak and break off occasionally.


Poor: The mixture cannot be extruded into strands.


3. Cutting Evaluation


Good: Cutting hardly produces any chips, and the pellet shape is uniform.


Fair: Cutting produces a small amount of chips, but the pellet shape is uniform.


Poor: Cutting produces a large amount of chips, and the pellet shape is not uniform.


4. Comprehensive Evaluation


Very good: All the items of the extrusion evaluation, strand state evaluation, and cutting evaluation are rated “Good”.


Good: Two items out of the extrusion evaluation, strand state evaluation, and cutting evaluation are rated “Good”, and none of these items are rated “Poor”.


Fair: One item out of the extrusion evaluation, strand state evaluation, and cutting evaluation is rated “Good”, and none of these items are rated “Poor”.


Poor: None of the items of the extrusion evaluation, strand state evaluation, and cutting evaluation are rated “Good”, or one or more items are rated “Poor”.


The masterbatches according to Examples 1 to 3 and 8 exhibited particularly excellent processability. The masterbatches according to Example 4 to 7 exhibited excellent processability.


In contrast, the masterbatches according to Comparative Example 1 exhibited poor processability. The reason is presumably that each masterbatch failed to have sufficient pellet strength due to a high proportion of the wax having a melt flow rate of more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s, and thus the specific shape could not be maintained in the extruding step or the cutting step.


(Melt Tension)


The masterbatches according to Examples 1 to 8 and Comparative Example 2 were evaluated for the melt tension. Evaluation was carried out as follows. Table 1 shows the results.


Measuring device: capilograph (Toyo Seiki Co., Ltd.)


Capillary inner diameter: 2.095 mm


Capillary length: 8.0 mm


Measurement temperature: 230° C.


Extrusion rate: 100 mm/min


Haul-off speed: 3.3 m/min


The melt tension of the masterbatches according to Examples 1 to 8 was 30 to 110 mN.


The value of the melt tension of the masterbatch indicates that the molten masterbatch has sufficient strength and is suitable for masterbatch production by extrusion.


In contrast, in the case of the masterbatch according to Comparative Example 2, the molten strands were broken so that the melt tension could not be measured.


Breakage of the molten strands indicates that the molten masterbatch is weak and is not suitable for masterbatch production by extrusion.


Further, in the case of the masterbatch in which the molten strands are likely to break, the pellet shape tends to be non-uniform and the pellet strength tends to be low. In the case where such masterbatches are used to produce a synthetic resin molded article, color unevenness easily occurs in the synthetic resin molded article because the masterbatches tend to be non-uniformly dispersed.


(Brightness Evaluation)


The masterbatches according to Examples 1 to 8 and Comparative Example 2 were evaluated for the brightness.


The brightness was evaluated as follows.


First, these masterbatch groups were separately kneaded into polyethylene resin in such a manner that the amount of the aluminum component would be 1 part by weight relative to 100 parts by weight of polyethylene resin, and a 0.5 mm-thick sheet-like synthetic resin molded article was formed.


Subsequently, a spectrophotometer (model name “CM3600d” produced by Konica Minolta, Inc.) was used to measure the lightness L* of the synthetic resin molded article. Measurement was carried out under conditions specified in JIS Z 8722 and JIS Z 8729. Table 1 shows the results.


The synthetic resin molded article using the masterbatches according to Examples 1 to 8 had higher brightness than the synthetic resin molded article using the masterbatch according to Comparative Example 2. The reason is presumably that the aluminum particles in the masterbatch according to Comparative Example 2 were broken or bent during masterbatch production.


(Fisheye and Gel Particle Generation Evaluation)


The masterbatches according to Examples 1 to 8 and Comparative Example 2 were evaluated for the generation of fisheyes and gel particles. For evaluation, an injection (INJ) plate was produced with an injection molding device, and fisheyes and gel particles were observed.


The INJ plate was produced by the following method.


First, these masterbatch groups were separately fed together with polypropylene resin into an injection molding device in such a manner that the amount of the aluminum component would be 1 part by weight relative to 100 parts by weight of polypropylene resin. The polypropylene resin and each masterbatch group were heated at 210° C. into a melt-kneaded mixture in an injection unit of the injection molding device. Subsequently, the melt-kneaded mixture was injected from the injection unit into a die (size: 50.0×90.0×3.0 mm) of the injection molding device. The die was set at 30° C. and the injected melt-kneaded mixture was cooled and solidified. The thus-obtained molded product is an INJ plate.


The number of fisheyes and gel particles formed on the surface of 10 INJ plates obtained by the above method was visually checked to evaluate the generation of fisheyes and gel particles.


The fisheyes and gel particles are semitransparent or white spots each having a diameter of 0.1 mm or more formed on the surface of each INJ plate. Table 1 shows the results.


The molded articles produced using the masterbatch groups according to Examples 1 to 8 had fewer fisheyes and gel particles than the molded article produced using the masterbatch group according to Comparative Example 2. In particular, the molded article of Example 8 which had two fisheyes and gel particles exhibited the best result among all of the examples.


The masterbatch according to Comparative Example 2 contains a large amount of wax. The wax is easily oxidized. The oxidized wax has a partially modified molecular chain, and thus has poor compatibility with the resin and poor diffusibility. Thus, the masterbatches will not be uniformly dispersed during synthetic resin molded article formation, which may cause the generation of fisheyes and gel particles on the surface of the synthetic resin molded article.


In addition, the masterbatch production according to Comparative Example 2 involves a heat-mixing step with a universal stirrer and a pellet molding step with a disk pelletizer. A heating treatment and a dispersion process are carried out in each of these two steps. These two steps also facilitate oxidation of the wax and the like, which may cause the generation of fisheyes and gel particles on the surface of the synthetic resin molded article.


The INJ plate produced using the masterbatch group according to Comparative Example 2 had many fisheyes and gel particles. The reason is presumably that the wax and the like in the masterbatch were oxidized during masterbatch production and during synthetic resin molded article formation due to the phenomena described above.


(Evaluation of the Shape of Aluminum Particles)


The shape of the aluminum particles in the masterbatches according to Example 1 and Comparative Example 2 were evaluated.


The shape of the aluminum particles was evaluated by microscopically observing the surface of the INJ plates produced for the fisheye and gel particle generation evaluation.



FIG. 4 and FIG. 5 show the results. FIG. 6 shows the shape of the aluminum particles in the aluminum paste for comparison.



FIG. 4(a) is a 1000 times magnified microscopic image of the shape of the aluminum particles in a synthetic resin molded article produced using the masterbatches according to Example 1. FIG. 4(b) is a 3000 times magnified image.



FIG. 5(a) is a 1000 times magnified microscopic image of the shape of the aluminum particles in a synthetic resin molded article formed using the masterbatches according to Comparative Example 2. FIG. 5(b) is a 3000 times magnified image.



FIG. 6(a) is a 1000 times magnified microscopic image of the shape of the aluminum particles in the aluminum paste. FIG. 6(b) is a 3000 times magnified image.


As is clear from FIG. 4(a) and FIG. 4(b), in the case of the synthetic resin molded article produced using the masterbatches according to Example 1, the aluminum particles had a uniform shape and were not agglomerated. In contrast, as is clear from FIG. 5(a) and FIG. 5(b), in the case of the synthetic resin molded article produced using the masterbatches according to Comparative Example 2, the aluminum particles were broken, had a non-uniform shape, and were agglomerated by overlapping.


(Strength Evaluation)


The masterbatch groups according to Examples 1 to 8 and Comparative Example 2 were evaluated for the strength.


The strength was evaluated by the following method.


First, each masterbatch group (33.3 g) was placed on a sieve having an opening of 1000 μm and an inner diameter of 75 mm. Subsequently, the sieve was shaken by a horizontal rotary sieve shaker “MVS-1” available from AS ONE Corporation at a frequency of 1500 rpm for 10 minutes.


Subsequently, the mass was measured for each masterbatch group after shaking to determine the mass decrease rate of the masterbatches. Table 1 shows the results.


If cracking or chipping occurs in the masterbatches during the shaking and fragments of the masterbatches pass through the sieve, the mass of the masterbatch group will decrease. In other words, if the masterbatches have low pellet strength and are susceptible to cracking or chipping, the mass decrease rate of the masterbatches will be high.


As shown in Table 1, the masterbatch group of Comparative Example 2 exhibited a higher mass decrease rate than the masterbatch groups according to Examples 1 to 8. In other words, according to the results, the masterbatches included in the masterbatch group of Comparative Example 2 had low pellet strength. The reason is presumably that each masterbatch failed to have sufficient pellet strength due to a high proportion of the wax having a melt flow rate of more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s.


(Pellet Shape Variation Evaluation)


The average values and the relative standard deviation and relative standard deviation of the major axis, minor axis, and length of the pellets of the masterbatch groups according to Examples 1 to 8 and Comparative Example 2 were calculated. Table 1 shows the results.


The masterbatch groups according to Examples 1 to 8 exhibited low variation with low relative standard deviations of the major axis, minor axis, and length of the pellets.


The masterbatch group according to Comparative Example 2 exhibited high variation with a high relative standard deviation of the length of the pellets while the relative standard deviations of the major axis and the minor axis of the pellets were low.

















TABLE 1










Example 1
Example 2
Example 3
Example 4
Example 5
Example 6





Aluminum paste
Aluminum particles
Not surface-coated
70.0
70.0
70.0
70.0
70.0
72.0




Surface-coated





















Polyethylene glycol
7.8
7.8
7.8
7.8
7.8
8.0


Resin
Polyethylene resin
19.9
20.2
19.3

7.0
17.9



Polypropylene resin




6.8




High melt tension polyethylene



21.1
6.8



Wax
Maleic acid-modified polyethylene wax
1.0
1.0
1.0
1.0
1.0
1.0



Polyethylene wax








Melt tension improver
Fluorine-based melt tension improver
1.0
0.7
1.5


1.0



Acrylic melt tension improver A
0.2
0.2
0.3






Acrylic melt tension improver B




0.5














Metal deactivator
0.1
0.1
0.1
0.1
0.1
0.1














Processability
Extrusion evaluation
Good
Good
Good
Good
Good
Good


evaluation
Strand state evaluation
Good
Good
Good
Good
Good
Good



Cutting evaluation
Good
Good
Good
Fair
Fair
Fair



Comprehensive evaluation
Very good
Very good
Very good
Good
Good
Good


Melt tension
(mN)
85
78
103
38
40
87


Brightness evaluation
(L*)
77.5
77.2
77.3
77.2
77.5
77.2


Fisheye and
(pieces)
4
4
4
3
4
5


Gel Particle


generation evaluation


Strength evaluation
Mass decrease rate after shaking
0.0132
0.0211
0.0122
0.0275
0.0285
0.0362



the sieve (%)


Variation evaluation
Average of pellet major axis (mm)
2.89
2.92
2.85
2.90
2.93
2.92



Standard deviation of pellet
0.0433
0.0538
0.0311
0.0537
0.0525
0.0388



major axis (mm)



Relative standard deviation of
1.4982
1.8424
1.0912
1.8517
1.7918
1.3288



pellet major axis (%)



Average of pellet minor axis (mm)
2.68
2.70
2.72
2.68
2.71
2.70



Standard deviation of pellet
0.0404
0.0502
0.0366
0.0501
0.0490
0.0499



minor axis (mm)



Relative standard deviation of
1.5075
1.8593
1.3456
1.8694
1.8081
1.8481



pellet minor axis (%)



Average of pellet length (mm)
2.66
2.88
2.80
2.62
2.61
2.61



Standard deviation of pellet length (mm)
0.0490
0.0505
0.0390
0.0510
0.0450
0.0422



Relative standard deviation of
1.8421
1.7535
1.3929
1.9466
1.7241
1.6169



pellet length (%)























Comparative
Comparative






Example 7
Example 8
Example 1
Example 2







Aluminum paste
Aluminum particles
Not surface-coated
74.0

70.0
70.0





Surface-coated

70.0

















Polyethylene glycol
8.2
7.8
7.8
7.8



Resin
Polyethylene resin
15.7
19.9
4.2
4.2




Polypropylene resin








High melt tension polyethylene







Wax
Maleic acid-modified polyethylene wax
1.0
1.0
1.0
1.0




Polyethylene wax


16.9
16.9



Melt tension improver
Fluorine-based melt tension improver
1.0
1.0






Acrylic melt tension improver A

0.2






Acrylic melt tension improver B

















Metal deactivator
0.1
0.1
0.1
0.1














Processability evaluation
Extrusion evaluation
Good
Good
Fair





Strand state evaluation
Good
Good
Poor





Cutting evaluation
Fair
Good
Poor





Comprehensive evaluation
Good
Very good
Poor




Melt tension
(mN)
90
105


Unmeasurable




Brightness evaluation
(L*)
77.3
77.0

75.2



Fisheye and Gel Particle
(pieces)
5
2

45



generation evaluation



Strength evaluation
Mass decrease rate after shaking
0.0422
0.0101

1.225




the sieve (%)



Variation evaluation
Average of pellet major axis (mm)
2.92
2.91

2.01




Standard deviation of pellet
0.0452
0.0378

0.0511




major axis (mm)




Relative standard deviation of
1.5479
1.2990

2.5422




pellet major axis (%)




Average of pellet minor axis (mm)
2.70
2.70

2.01




Standard deviation of pellet
0.0489
0.0369

0.0512




minor axis (mm)




Relative standard deviation of
1.8111
1.3667

2.5473




pellet minor axis (%)




Average of pellet length (mm)
2.60
2.70

7.76




Standard deviation of pellet length (mm)
0.0478
0.0345

2.7922




Relative standard deviation
1.8385
1.2778

35.9820




of pellet length (%)








Unmeasurable due to rupture of the molten strand







REFERENCE SIGNS LIST




  • 10 Masterbatch


  • 11 Bottom


  • 12 Top


Claims
  • 1. A masterbatch comprising: aluminum particles;a heat-resistant wetting agent; anda resin,wherein a ratio of the aluminum particles in the masterbatch is in a range from 50 to 80% by weight,the resin is a polymer alloy having a melt tension at 190° C. in a range from 20 to 100 mN,the resin has a melt flow rate in a range from 0.2 to 60 g/10 min,a ratio of wax having a melt flow rate in a range of more than 60 g/10 min and a melt viscosity at 140° C. in a range from 15 to 8000 mPa·s in the masterbatch is in a range of 10% by weight or less, andthe heat-resistant wetting agent is one or more polyethylene glycols.
  • 2. The masterbatch according to claim 1, wherein the aluminum particles are surface-coated aluminum particles.
  • 3. The masterbatch according to claim 1 further comprising a melt tension improver.
  • 4. The masterbatch according to claim 1, wherein the resin comprises a high melt tension resin having a melt tension at 190° C. in a range from 30 to 200 mN.
  • 5. The masterbatch according to claim 1 further comprising a metal deactivator.
  • 6. A masterbatch group comprising a plurality of the masterbatches according to claim 1, wherein each masterbatch has a pellet shape,the plurality of the masterbatches included in the masterbatch group has a relative standard deviation of a major axis in a range of 5.00% or less,the plurality of the masterbatches included in the masterbatch group has a relative standard deviation of a minor axis in a range of 5.00% or less, andthe plurality of the masterbatches included in the masterbatch group has a relative standard deviation of a length in a range of 5.00% or less.
  • 7. The masterbatch group according to claim 6, wherein an average major axis of the plurality of the masterbatches included in the masterbatch group is in a range from 2.0 to 4.0 mm,an average minor axis of the plurality of the masterbatches included in the masterbatch group is in a range from 2.0 to 4.0 mm, andan average length of the plurality of the masterbatches included in the masterbatch group is in a range from 2.0 to 4.0 mm.
  • 8. A method for producing the masterbatch according to claim 1, the method comprising: mixing an aluminum paste, which is obtained by wetting the aluminum particles with the heat-resistant wetting agent, with the resin having a melt flow rate in a range from 0.2 to 60 g/10 min so as to produce an aluminum-resin mixture, wherein the aluminum-resin mixture has a ratio of the aluminum particles in a range from 50 to 80% by weight and a ratio of the wax having a melt flow rate in a range of more than 60 g/10 min and a melt viscosity at 140° C. of 15 to 8000 mPa·s in a range of 10% by weight or less;extruding the aluminum-resin mixture; andcutting the extruded aluminum-resin mixture.
  • 9. The method for producing the masterbatch according to claim 8, wherein the mixing is carried out without using a stirring member.
  • 10. The method for producing the masterbatch according to claim 8, wherein the mixing is carried out at a temperature in a range of 80° C. or lower, andthe extruding is carried out at a temperature in a range from 150° C. to 250° C.
  • 11. The method for producing the masterbatch according to claim 8, wherein the mixing is carried out using surface-coated aluminum particles as the aluminum particles.
  • 12. A synthetic resin molded article, wherein the synthetic resin molded article is produced using the masterbatch according to claim 1.
Priority Claims (1)
Number Date Country Kind
2013-212902 Oct 2013 JP national
PCT Information
Filing Document Filing Date Country Kind
PCT/JP2014/073716 9/8/2014 WO 00
Publishing Document Publishing Date Country Kind
WO2015/053025 4/16/2015 WO A
US Referenced Citations (7)
Number Name Date Kind
5460768 Akao Oct 1995 A
5814697 Akao Sep 1998 A
5932325 Ebihara et al. Aug 1999 A
20010016627 Koshirai et al. Aug 2001 A1
20080249211 Smink et al. Oct 2008 A1
20090250103 Katoh et al. Oct 2009 A1
20110230611 Asano et al. Sep 2011 A1
Foreign Referenced Citations (16)
Number Date Country
101425545 May 2009 CN
101805457 Aug 2010 CN
102216374 Oct 2011 CN
2 351 784 Aug 2011 EP
6-220257 Aug 1994 JP
9-241390 Sep 1997 JP
9-255816 Sep 1997 JP
10-168240 Jun 1998 JP
11-124478 May 1999 JP
3022027 Mar 2000 JP
2000-248072 Sep 2000 JP
2000-327850 Nov 2000 JP
2002-283350 Oct 2002 JP
2002-238635 Nov 2002 JP
2010-095681 Apr 2010 JP
2010-121092 Jun 2010 JP
Non-Patent Literature Citations (2)
Entry
DiMaio, V.V., et al; The Effect of Chain Structure on Melt Strength of Polypropylene and Polyethylene, 1997, p. 1512-1516.
IARC Monographs on the Evolution of Carcinogenic Risks to Humans, 2000, vol. 77, p. 149-150 (Year: 2000).
Related Publications (1)
Number Date Country
20160237223 A1 Aug 2016 US