Patent Application
20090087353
The present application claims priority under 35 U.S.C §119 to Japanese Patent Application Publication No. 2007-255889 filed Sep. 28, 2007, the entire contents of which are incorporated herein by reference.
1. Field of the Invention
The present invention relates to a mat member and an exhaust gas treatment apparatus and a muffling apparatus.
2. Discussion of Background
The number of vehicles has been dramatically increased from the beginning of this century, thereby steadily and rapidly increasing the amount of exhaust gas exhausted from the internal combustion engines of the vehicles. Particularly, various materials included in the exhaust gas exhausted from diesel engines are responsible for causing contamination, thereby seriously damaging the world-wide environment.
Under such circumstances, various exhaust gas treatment apparatuses have been proposed and put into practice. In a typical exhaust gas treatment apparatus there is a cylindrical member (casing) in the middle of an exhaust gas tube connected to an exhaust gas manifold of an engine. In the casing there is an exhaust gas treatment member having opening surfaces for the inlet and the outlet of exhaust gas, and an inner part with plural fine holes. As examples of the exhaust gas treatment member, there are a catalyst carrier and an exhaust gas filter such as a Diesel Particulate Filter (DPF). When such a DPF is used, due to the structure of the exhaust gas treatment member, fine particles in exhaust gas are trapped onto the circumferential walls of the holes and removed from the exhaust gas between when the exhaust gas is introduced though the inlet opening and when the exhaust gas is exhausted from the output opening of the exhaust gas treatment member.
Generally, a holding and sealing member is placed between such an exhaust gas treatment member and a casing. The holding and sealing member is used to prevent contact between the exhaust gas treatment member and the casing so as to avoid damage while the vehicle is being operated and also prevent leakage of exhaust gas through the gaps between the casing and the exhaust gas treatment member. Further, the holding and sealing member has a role to avoid the displacement of the exhaust gas treatment member due to the pressure of the exhaust gas. Still further, the holding and sealing member is required to be kept at high temperature to sustain reactivity, and to have thermal insulation efficiency. As a member that meets the above requirements, there is a mat member made of inorganic fibers such as alumina-based fibers.
The mat member is wound around at least one part on the outer surface except for an opening surface of the exhaust gas treatment member and is integrated with the exhaust treatment member by, for example, taping, so as to be used as a holding and sealing member. After the processes, the integrated parts are housed inside the casing to form the exhaust gas treatment apparatus.
There is disclosed a mat member with resin films disposed on the front and the back sides of the mat member (see Japanese Patent Application Publication No. H08-61054 and Japanese Patent Application Publication No. 2003-293756).
The contents of Japanese Patent Application Publication No. H08-61054 and Japanese Patent Application Publication No. 2003-293756 are incorporated herein by reference in their entirety.
According to an aspect of the present invention, a mat member includes a base member and a sheet member. The base member includes inorganic fibers and has first and second main surfaces. The sheet member is disposed on at least one of the first and the second main surfaces. The sheet member has an opening provided on at least a part of a surface of the sheet member.
In the mat member, the sheet member may have plural openings, and the plural openings may be substantially regularly arranged.
Further, the sheet member may have plural openings; and the shapes of the openings may be substantially equal to each other.
Still further, the sheet member may include the opening and a framework part surrounding the opening, and the framework part may include at least a first straight line part extending in substantially a first direction and a second straight line part extending in substantially a second direction.
Still further, the first line part may include plural straight lines extended in substantially the first direction and arranged at a substantially regular interval, and the second line part may include plural straight lines extended substantially in the second direction and arranged at a substantially regular interval.
Especially, it is preferable that a maximum length of the opening of the sheet member be equal to or less than an approximately 95% lower limit value of a fiber length distribution of the inorganic fibers.
Alternatively, it is also preferable that a maximum length of the opening of the sheet member be equal to or less than approximately 6 mm.
Alternatively, the sheet member may include organic material or any one of polyethylene, polypropylene, and polyethylene terephthalate.
Alternatively, the inorganic fibers included in the base member may include alumina and silica.
Further, the base member may further include any one of inorganic binder and organic binder or both.
Alternatively, an organic component amount included in the mat member may be equal to or less than approximately 4.5 wt %.
According to another aspect of the present invention, there is provided an exhaust gas treatment apparatus including an exhaust gas treatment member having two opening surfaces for passing exhaust gas, a holding and sealing member wound around at least a part of a circumferential surface of the exhaust gas treatment member, the circumferential surface excluding the opening surfaces, and a cylindrical member housing the exhaust gas treatment member with the holding and sealing member wound around the exhaust gas treatment member, wherein the holding and sealing member includes the mat member as described above.
According to still another aspect of the present invention, there is provided an exhaust gas treatment apparatus including an inlet tube and an outlet tube for exhaust gas, and an exhaust gas treatment member disposed between the inlet tube and the outlet tube, wherein a heat insulating member is disposed on at least a part of the inlet tube, and the heat insulating member includes the mat member as described above.
Here, the exhaust gas treatment member may be a catalyst carrier or an exhaust gas filter.
According to still another aspect of the present invention, there is provided a muffling apparatus including an inner pipe, an outer shell covering the outside of the inner pipe, and a sound absorber disposed between the inner pipe and the outer shell, wherein the sound absorber includes the mat member described above.
According to an embodiment of the present invention, there is provided a mat member from which inorganic fibers are difficult to be scattered and, when the mat member is actually used in an exhaust gas treatment apparatus or a muffling apparatus, a lesser amount of organic components are exhausted from the apparatus. Further, in the exhaust gas treatment apparatus using such a mat member as the holding and sealing member and/or the heat insulating member and in the muffling apparatus using such a mat member as the sound absorber, it is possible to significantly better control the amount of organic components exhausted from the apparatus when being used.
A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:
Next, exemplary embodiments of the present invention are described with reference to the accompanying drawings.
As shown in
As shown in
As shown in
Referring back to
In such a sheet member, the opening ratio contributes to the reduction of the total weight of the sheet member. Therefore, even when the sheet members 310 and 360 are made of organic material such as polymer resin, the amount of organic components generated by thermal decomposition of the mat member used as the holding and sealing member of the exhaust gas treatment apparatus can be significantly reduced compared to a conventional mat member having a resin film on the surface of the mat member.
Further, as is obvious, the sheet members 310 and 360 include parts other than openings (hereinafter referred to as “framework part”). Therefore, the framework part presses down and contains the inorganic fibers of the base member 340. As a result, when a mat member having such a sheet member is handled, the scattering amount of the inorganic fibers can be significantly reduced compared to a mat member having no such a sheet member. It should be noted that the term “framework part” in this description refers to the part other than the openings of the sheet member.
Here, in a mat member according to an embodiment of the present invention, the number of the openings formed on the sheet member is not necessarily limited to a specific number. Further, the opening ratio is not necessarily limited to a specific number either. For example, a sheet member according to an embodiment of the present invention may have plural openings, and the plural openings (and the framework part as well) may be substantially regularly formed. Further, the shape of the openings may have substantially the same shape or may be different shapes. For example the shape of the openings may be substantially circular, ellipsoidal, triangular, rectangular, square, rhombic, or polygonal.
Such a sheet member may be made of, for example, organic polymer-based material. The organic polymer-based material is not limited to, but may include, polyethylene, polypropylene, and polyethylene terephthalate. Especially, it is preferable that the sheet member include heat sealable material such as polyethylene (for example, “WARIFU” (registered trademark), manufactured by Nisseki Plasto, and “CONWED”). In this case, the sheet member can be adhered to the main surface of the base member when heated without using any adhesive. Therefore, the operatability is improved and the output amount of organic components can be further controlled. Further, in this case, the inorganic fibers disposed on the main surface of the base member are heat-sealed with the sheet member, so that the scattering of the inorganic fibers from the base member can be further controlled.
Next, more details of the reduction of the organic component amount and the scattering amount of the inorganic fibers, the characteristic features of the mat member according to an embodiment of the present invention, are further described below.
In the vehicle industry, it is recommended that the total organic component amount be approximately 4.5 wt % or less so as to reduce the output amount of organic components from an exhaust gas treatment apparatus.
Generally, the organic component amount “M1” included in a sheet member using organic material is given by the following formula:
M1=S×t×ρ×(1−α) (1)
Where
In a general case, a prescribed amount of organic binder (for example, approximately 1 wt %) is added in the forming process to facilitate the handling of the mat member. Therefore, when “M2” represents the organic component amount included in the base member, the following relational formula to control the output amount of the organic components from the mat member to be less than approximately 45% is obtained.
{(M1+M2)/(M1+W+M2)}×100≦approximately 4.5(wt %) (2)
where the symbol “W” represents the weight (g) of the base member excluding the weight of the organic binder (therefore, the weight of the base member is given as “W+M2”).
Here, to tentatively calculate the total organic amount included in a mat member according to an embodiment of the present invention, the following values are selected and used.
Basis weight of the base member: approximately 1,160 g/m2
Area: approximately 100 cm2
Amount of organic binder included in the base member: approximately 1 wt % of the total weight of the base member (the weight of the base member+the amount of organic binder)
Material of the sheet member: polypropylene having the density of approximately 0.91 g/cm3
Thickness of the sheet member: approximately 0.15 mm
Opening ratio of the sheet member: approximately 93%
Then, values, M1=approximately 0.096 g, M2=approximately 0.117 g, and W=approximately 11.6 g, are obtained. As a result, the total organic component amount included in the mat member according to an embodiment of the present invention is approximately 1.8 wt % when one sheet member is used (namely, the sheet member is disposed on one main surface only), and approximately 2.6 wt % when two sheet members are used (namely, the sheet members are disposed one on each main surface). Therefore, both values adequately meet the requirement of formula (2).
On the other hand, when a conventional sheet member (having the opening ratio: a 0) is used, values, M1=approximately 1.365 g, M2=approximately 0.117 g, and W=approximately 11.6 g, are obtained. As a result, the total organic component amount included in the mat member is approximately 11.3 wt % and approximately 19.7 wt % when one and two sheet members are used, respectively. Therefore, even when the sheet member is disposed only on one main surface of the mat member, the value does not meet the requirement of formula (2). Conversely, in order to meet the requirement of formula (2) in a conventional mat member, it is necessary to reduce the thickness “t” of the sheet member down to less than approximately 0.047 mm when one sheet member is used and less than approximately 0.024 mm when two sheet members are used. However, a sheet member having such a thickness is too thin to be handled.
As described above, in a mat member according to an embodiment of the present invention, the organic component amount can be significantly better controlled compared to a conventional mat member. Further, the organic component amount of the mat member according to an embodiment of the present invention can easily attain the required range (approximately 4.5 wt % or less). It should be noted that the above tentative calculation is provided as an example for explanation purposes. In a practical case, it should be kept in mind that an output amount of the organic component due to thermal decomposition from the mat member varies depending on, for example, the unevenness of the in-plane distribution of the organic binder included in the base member.
The sheet member 310 in
Obviously, some parts of the main surface of the base member 340 are exposed though the openings 315. However, in a mat member according to an embodiment of the present invention, the scattering and dropping off of the inorganic fibers 342 included in the base member 340 though the openings 315 may be controlled due to the reason(s) described below.
Namely, the framework part 312 (312X1 and 312Y1) of the sheet member 310 holds down and contains the organic fibers disposed on the main surface side of the base member 340 close to the sheet member 310. Generally, the length of the inorganic fibers 342 included in the base member 340 is in a range between approximately 10 mm and approximately 100 mm. Therefore, as long as at least a part of each inorganic fiber is pressed down by the framework part 312, neither significant scattering nor drop off of the inorganic fibers 342 from the openings 315 are likely to occur. Especially, when the “maximum length” of the opening 315 is selected and formed according to the procedure described below, the scattering and drop off of the inorganic fibers through the openings can be extremely effectively controlled. It should be noted that the terms “maximum length” refers to the longest distance between any ends of an opening in a two-dimensional plane. For example, when an opening has a shape as in
Especially, it is preferable that the maximum length of the opening 315 be equal to or less than the “approximately 95% lower limit value” (“M95%”)
Here, the “approximately 95% lower limit value” (“M95%”) of the fiber length of the inorganic fibers can be determined from the fiber length distribution of the inorganic fibers 342 included in the base member 340 as follows:
First, one hundred inorganic fibers included in the base member 340 are randomly selected, and each length, “Li” (i=1 through 100) of the selected inorganic fibers is measured. Next, each natural logarithm value “ln(Li)” of the corresponding “Li” value is obtained. Then an average value “A” and a standard deviation “σ” of the “In(Li)” are obtained. Further, a value “K” is obtained from the following formula:
K=A−2×α (3)
This “K” value corresponds to the “approximately 95% lower limit value”. Namely, the fiber length data of the inorganic fibers is in a range equal to or more than the value of “K” with 95% probability. Last, a conversion to restore the “K” to the original dimension is made by an exponential function “ek” to obtain the “approximately 95% lower limit value” (“M95%”) of the fiber length of the inorganic fibers.
When it is assumed that the maximum length of the opening 315 is equal to or less than the approximately 95% lower limit value M95% of the inorganic fibers 342 included in the base member 340, most of the inorganic fibers 342 included in the base member 340 are contained by the framework part 312 of the sheet member 310. Therefore, in this case, the amount of inorganic fibers scattered or dropped through the openings 315 can be significantly controlled.
As described above, a mat member according to an embodiment of the present invention can control the organic component amount in the mat member more than a conventional sheet member having sheet members disposed one on each of the front side and the back side, and can provide a scattering reduction effect comparable to a conventional mat member.
In the example in
For example, the sheet member 310 may be a sheet-type member having a net shape. The net-shaped sheet type member may be like a net with a knot at each cross-point (like a so-called knot net), a net without knots like a raschel net and a knotless net, or a so-called woven net where two straight line parts extending in two directions are mutually woven to constitute its framework part.
Still further, the framework part does not always necessarily include an array of straight lines, and may have an array of curved lines. Otherwise, the sheet member may have one or more openings formed regularly and randomly by a punching process. Ultimately, what is important point for the sheet member used in a mat member according to an embodiment of the present invention is that the sheet member does have an opening. As long as the sheet member has the opening, the sheet member and the framework part and the openings of the sheet member may have any shape.
The mat member according to an embodiment of the present invention may be used as a holding and sealing member and/or a heat insulating member of an exhaust gas treatment member 10.
The exhaust gas treatment apparatus 10 includes an exhaust gas treatment member 20, a holding and sealing member 24 wound around the exhaust gas treatment member 20, a casing 12 housing the exhaust gas treatment member 20, and an inlet tube 2 and an outlet tube 4 for the inlet and the outlet of exhaust gas connected to the input side and the outlet side of the casing 12, respectively. Both the inlet tube 2 and the outlet tube 4 have a tapered shape so that the diameters of the inlet tube 2 and the outlet tube 4 are increased where connected to the casing 12. Further, a heat insulating member 26 is disposed on the tapered section of the inlet tube 2. The heat insulating member 26 controls the heat transfer from the inside of the exhaust gas treatment member 10 to the outside through the inlet tube 2. In this example in
In this configuration, a mat member 30 according to an embodiment of the present invention is used as the holding and sealing member 24 and the heat insulating member 26. In the exhaust gas treatment apparatus having such a configuration, when the mat member 30 is handled, more specifically, for example, when the mat member 30 is wound around the exhaust gas treatment member 20 as the holding and sealing member 24, or when the mat member 30 is disposed on the exhaust gas treatment member 20 as the heat insulating member 26, the scattering of the inorganic fibers can be significantly controlled. Further, when the exhaust gas treatment apparatus 10 is being used (especially used in an initial operation), the amount of organic components decomposed and emitted due to the heat of exhaust gas can be significantly better controlled.
Next, another application of a mat member according to an embodiment of the present invention is described.
Here, the mat member 30 according to an embodiment of the present invention can be used as the sound absorber 74. By using a mat member according to an embodiment of the present invention as the sound absorber 74, the scattering of the inorganic fibers when the sound absorber 74 is disposed in the muffling apparatus 70 can be significantly controlled.
In the following, an example of the forming method of the mat member 30 according to an embodiment of the present invention is described.
First, the base member mostly made of inorganic fibers is formed. It should be noted that in the following descriptions, though the mixture of alumina and silica is used as the inorganic fibers, the inorganic fibers are not limited to this mixture and may be made of alumina only or silica only. Silica sol is added to a basic aluminum chloride aqueous solution with aluminum content approximately 70 g/l and Al/Cl=approximately 1.8 (atom ratio) such that the composing ratio of alumina and silica is approximately 60-80: approximately 40-20 to prepare the precursor of inorganic fibers. More preferably, the composing ratio of alumina and silica is approximately 70-74: approximately 30-26. This is because when the composing ratio of alumina is equal to or less than approximately 60%, since the composing ratio of mullite prepared from alumina and silica is lowered, the heat conductivity of each formed layer is apt to be increased.
Next, an organic polymer such as polyvinyl alcohol is added to the precursor of the alumina-based fibers. Then the liquid is condensed to prepare a spinning solution. Next, fibers are formed by a blowing process using the obtained spinning solution.
The blowing method refers to a method of forming fibers using a air flow blown from an air nozzle and a spinning solution flow pushed out through a spinning solution supply nozzle. The gas flow speed per slit from the air nozzle is typically in a range between approximately 40 to approximately 200 m/s. The diameter of the spinning nozzle is typically in a range between approximately 0.1 to approximately 0.5 mm, and the fluid volume per spinning solution supplying nozzle is typically in a range between approximately 1 to approximately 120 ml/h, preferably between approximately 3 to approximately 50 ml/h. Under such conditions, the spinning solution pushed out through the spinning solution supply nozzle can be sufficiently extended without being turned into a spray (a fine liquid mist). In this case, since the formed fibers are hard to be adhered to each other, it is possible to form a uniform alumina fiber precursor having a narrower fiber diameter distribution by optimizing spinning conditions.
Next, the base member is formed by laminating the precursors in which the fibers have been formed. Further, a needling process is performed on the base member. In this case, the needling process refers to a process in which needles are thrust into and pulled out of the base member to reduce the thickness of the base member. In the needling process, a dedicated needling device is usually used.
Generally, the needling device includes a needle board reciprocally movable in the thrusting direction (typically in the up-and-down direction) and a pair of supporting boards provided on both sides facing the front face and the rear face of the base member. On the needle board there are plenty of needles arranged in a density of, for example, approximately 25 to approximately 5,000 needles per 100 cm2 to thrust into the base member. In each supporting board, there are plenty of through holes for passing the needles. Therefore, while the base member is held down on both sides by a pair of the supporting boards, by bringing the needle board close to the base member and separating the needle board away from the base member, the needles are thrust into and pulled out of the base member to form a base member having plenty of interlaced points where the fibers are confounded.
As another configuration, the needling device may include a pair of needle boards as a set. Each needle board has the corresponding supporting board. Two needle boards are provided on both first and second sides of the base member, and the base member is held down on both sides by the supporting boards. The needles on the needle boards are arranged so that the positions of the needles on one needle board are not overlapped with the positions of the needles on the other needle board. Further, there are so many through holes provided in each of the supporting boards in consideration of the positions of needles on both needle boards so that no needle should contact the supporting boards when the needling process is performed on both surfaces of the base member. With such a device, the base member may be held down from both surfaces by using the two supporting boards and the needling process may be performed on the base member from both surfaces by using a pair of needle boards. By using such a method for needling process, the processing time can be shortened.
At the interlaced points generated in the needling process, the fibers complexly confounded are arranged in the laminating direction, thereby reinforcing the base member in the laminating direction.
After being subject to the needling process, the base member is heated from room temperature and calcinated at a maximum temperature approximately 1,250° C. to obtain the base member having a prescribed basis weight (weight per unit area).
Next, organic binder like resin may be impregnated into the base member to facilitate the handling of the base member. It is preferable to reduce the amount of the organic binder as much as possible down to, for example, approximately 1.0 wt %.
As the organic binder, for example, epoxy resin, acrylic resin, rubber-based resin, and styrene-based resin may be used. For example, it is preferable to use, for example, acrylic-based (ACM), acrylonitrile-butadiene rubber (NBR), or styrene-butadiene rubber (SBR) resin.
Next, a sheet member with at least an opening is disposed on first and/or second main surfaces of the sheet member. As described above, when thermally adhesive material (for example, polyethylene) is used in the sheet member, the sheet member can be easily adhered to the main surface of the base member without using binder, which significantly facilitates operations. Further, when the mat member formed as described above is integrated into and used in the exhaust gas treatment apparatus, the output amount of organic elements can be further reduced. When the sheet member including thermally adhesive material is disposed on each of the main surfaces of the base member, first, a sheet member is disposed on the first main surface of the base member and is heated at a temperature between approximately 140° C. and approximately 270° C. for one minute under a pressure between approximately 10 kPa and approximately 100 kPa so as to be adhered to the first main surface of the base member. Next, the sheet member including the above-mentioned or another thermally adhesive material is disposed on the second main surface of the base member and is heated at a temperature between approximately 140° C. and approximately 270° C. for one minute under a pressure between approximately 10 kPa and approximately 100 kPa. By doing this, the sheet members can be adhered to both of the main surfaces of the base member. However, it should be noted that sheet members may be adhered to both main surfaces of the base member at the same time as well.
Through the processes described above, the mat member with the sheet member having openings on the first and/or the second main surfaces can be formed.
It should be noted that the thus obtained mat member is finally cut into a prescribed shape (for example, a shape shown in
In the following, effects according to the embodiment of the present invention are described with reference to the examples below.
First, silica sol is added to basic aluminum chloride aqueous solution with aluminum content of 70 g/l and Al/Cl=1.8 (atom ratio) such that the relative proportion of Al2O3:SiO2 in alumina-based fibers is 72:28 to prepare the precursor of alumina-based fibers. Next, polyvinyl alcohol is added to the precursor of alumina-based fibers. Further, this liquid is condensed to prepare a spinning solution. From the spinning solution, fibers are formed by the blowing spinning process. The flow rate of the carrier gas (air) is 52 m/s and the supplying rate of the spinning solution is 5.3 ml/h.
Then, the precursor of the alumina-based fibers is folded and laminated to form a base member of alumina-based fibers.
Next, the needling process is performed to the obtained base member. In the needling process, a needling board having needles at a density of 80 needles per 100 cm2 is provided on one side of the base member and the needling is performed from the one side of the base member.
Then, the obtained base member is heated from room temperature to 1,250° C. and the temperature is maintained for one hour for continuous calcination. Next, organic binder is impregnated into the base member through a first main surface of the base member. As the organic binder, acrylate-based Latex Emulsion is used and the impregnation amount is 1 wt % of the total weight of the base member (including the organic binder). The basis weight of the obtained base member is 1,160 g/m2.
Next, each fiber length of the 100 inorganic fibers included in the base member is measured. Then, the “95% lower limit value” “(M95%)” of the inorganic fibers is calculated base on the above-mentioned method. The obtained value of the “(M95%)” is 6.08 mm.
Next, a polypropylene sheet member (thickness: 0.15 mm) having openings is disposed only on one main surface (a first main surface) of the base member. After being disposed on the first main surface of the base member, the sheet member is heated at a temperature of 200° C. for one minute under the pressure of approximately 15 kPa to adhere to the base member. The framework part of the sheet member has a structure where two groups of straight lines extending in two directions cross each other at substantially right angles as shown in
In the same manner as above, mat members “Examples 2 through 4” each having a sheet member and openings on the first main surface of the mat member are formed. However, in “Example 2”, the pitch of the straight lines constituting the framework part of the sheet member in both X1 and Y1 directions (distance between the centers of adjoining straight lines) is 4 mm; the maximum length of the openings of the sheet member is 5.7 mm; and the opening ratio is 93%. In “Example 3”, the pitch of the straight lines in both X1 and Y1 directions (distance between centers of adjoining straight lines) is 6 mm; the maximum length of the openings of the sheet member is 8.5 mm; and the opening ratio is 95%. In “Example 4”, the pitches of the straight lines (distances between the centers of adjoining straight lines) in X1 and Y1 directions are 8 mm and 9 mm, respectively; the maximum length of the openings of the sheet member is 12.0 mm; and the opening ratio is 96%.
In the same manner as in “Example 2”, a mat member (“Example 5”) is formed. However, in “Example 5” after a sheet member having openings is disposed on the first main surface of the base member, the base member is reversed so that another sheet member having openings is disposed on the entire second main surface of the base member in the same manner described above. The specifications of the sheet members disposed on both main surfaces are the same as those of the sheet member used in “Example 2”. Namely, the pitch of the straight lines constituting the framework part of the sheet member in both X1 and Y1 directions (distance between the centers of adjoining straight lines) is 4 mm; the maximum length of the openings of the sheet member is 5.7 mm; and the opening ratio is 93%.
In the same manner as in “Example 5”, a mat member (“Example 6”) is formed. However, in “Example 6”, the same sheet member is disposed around the entire circumference surface including the first and the second main surfaces of the base member in the same manner.
In the same manner as in “Example 1”, a mat member with a sheet member disposed on the first main surface of the mat member is formed. However, in “Comparative example 1”, a polypropylene film having no openings is used as the sheet member. The thickness of the film is 0.05 mm.
A mat member having only the base member formed in the same manner as in “Example 1” is formed. The mat member thus obtained is called “Comparative example 2”.
Each organic component amount included in the above-mentioned mat member is measured. The method of measuring the organic component amount is as follows:
First, a sample of a mat member (100 mm×100 mm) is dried at a temperature of 110° C. for one hour, and the weight of the sample (weight before calcination) is measured. Next, the sample is calcinated at a temperature of 600° C. for one hour and is cooled to room temperature, and the weight of the sample (weight after calcination) is measured. Based on the measured values, the organic component amount of the mat member is calculated in the following formula:
Organic component amount(%)={(“Weight before calcination”−“Weight after calcination”)/(“weight before calcination”)}×100 (4)
Table 1 shows the measurement result of the organic component amount of each mat member. Further,
According to Table 1 and
An inorganic fiber air erosion test is performed on each mat member described above.
The air erosion test is performed as follows: first, each test sample 160 (100 mm×100 mm) of mat members described above is prepared. As shown in
Scattering rate of inorganic fibers(wt %)=(“weight of mat member sample before test”−“weight of mat member sample after test”)/(“weight of mat member sample before test”)×100 (5)
Table 1 shows the air erosion test results of each mat member. Further,
According to Table 1 and
A mat member and an exhaust gas treatment apparatus according to embodiments of the present invention may be used in, for example, an exhaust gas treatment apparatus for a vehicle.
The present invention is not limited to the above-mentioned embodiments, and variations and modifications may be made without departing from the scope of the present invention.
Obviously, numerous modifications and variations of the present invention are possible in light of the above teaching. It is therefore to be understood that within the scope of the appended claims, the inventions may be practiced otherwise than as specifically described herein.