This application relates to Russian Patent Application No. 2000129858 filed Nov. 30, 2000.
The present invention relates to the field of plasma engineering, particularly to electrodes for low temperature AC (alternating current and voltage) plasma generators, and more particularly the materials for fabricating such electrodes which have heat conduction, electric conductance, structural strength and electron emitting characteristics.
In the field of plasma engineering, substantial effort has been directed to manufacturing of electrodes for low temperature plasma generators providing emission of electrons and stable arc burning, i.e., AC plasma electrodes. Such electrodes have typically been made from copper and chromium carbide, although other materials and methods for production have been proposed.
In general, materials for electrodes (not AC plasma electrodes) containing barium and/or barium oxide as a component emitting electrons was proposed in U.S. Pat. No. 5,126,622 issued Jun. 30, 1992 to J. Jeong et al. Emitter of electrons is enclosed in porous metal material which has a lot of diffusion cavities. European Patent Application No. 0537495 published Apr. 21, 1993 proposes to mix dry metal powders with high melting point, high heat resistance and substances emitting electrons for manufacturing electrodes. The mixture is compacted in the sealed reaction vessel and is subjected to hot isostalic compacting to obtain a semifinished item which is processed on the machine-tool to receive the electrode of the designed shape. Barium aluminate is the substance emitting electrons.
U.S. Pat. No. 5,128,584 issued Jul. 7, 1992 to J. Choi proposes an impregnated dispersion electrode containing a porous metal matrix impregnated with the material, emitting electrons on the basis of scandium or scandium tungstate. By this means the availability of an emitting additive and metal matrix, providing current supply and fixating emitting addition, are common for all mentioned above patents. The present invention is based on the same principle but other combinations of components are used as a base and an emitter.
Material of the electrodes of low temperature plasma generators containing porous metal matrix impregnated with the material emitting electrons differs from those listed above in that it uses a mixture of copper and iron powders as a porous metal matrix and a Group IIIB metal-containing component (such as Y2O3) is used as a material emitting electrons at the following proportion of the components, mass %:
Copper provides high level of heat conduction and electric conductance, iron decreases intensity of copper evaporation in the process of plasma creation providing increased strength and lifetime, the Group IIIB metal-containing component such as Y2O3 provides decreasing of electronic work function and stability of arc burning. Previous electrodes used in AC plasma generators have contained only copper or chromium carbide. The composition of the electrode of the invention contributes to a substantial increase in the lifetime of the electrodes to at least 10 times that of chromium carbide electrodes and 20 times that of copper electrodes. (The lifetime of the AC plasma electrode is that time after which the electrode must be replaced in an AC generator due to sufficient corrosion to cause the essential cease of function of the electrode.)
In an exemplary embodiment, dry metal powders of (Cu+Fe) and Y2O3 are mixed in the manufacture of electrodes. The received mixture is compacted on air in the mold in such a manner that cross-section areas of the compacted item and finished item relate as 4:1-8:1. Then the mixture is baked in shielding-reducing medium (hydrogen, dissociated ammonia) in temperature range of 900-1050° C. during 20 min-4 hours. After that, it is subjected to forging in temperature range of 850-950° C. to obtain the rod which has allowance on diameter of 2-3 mm or extrusions. Then mechanical processing is carried out to obtain ultimate dimensions.
Uniformity of distribution of introduced charge components by member volume is of great importance for stable operation of the plasma generator electrodes. In this connection particular emphasis should have been placed to the process of mixing of the initial components having different density and properties.
The electrode of the invention includes the combination of Iron (Fe) and Copper (Cu) together with electron emitting materials selected from one or more components containing Group IIIB metals of the Periodic Table. Such Group IIIB metal-containing components can include Scandium (Sc), Lanthanum (La), Actinium (Ac), and preferably Yttrium (Y). Although several Group IIIB metal-containing components may be employed, effective components include boron, tungsten and/or oxygen in combination with one or more Group IIIB metals. A highly useful composition contains Yttrium oxide (Y2O3), which hereinafter is described in several exemplary embodiments of the invention.
So that to create the composition containing 30% of Fe and 0.1% of Y2O3, the mixing was carried out in three steps sequentially:
It was found experimentally in creation of the invention that optimum compaction pressure is 300-400 MPa (3-4 t/cm2). Pressure increases above 400 MPa (3-4 t/cm2) results in appearance of bulging and cracks on the surface of baking blanks because of the evaporation of adsorbed films inside the blanks.
Baking in reducing medium (hydrogen, dissociated ammonia) protects porous material from internal oxidation. It was experimentally found that temperature range of baking is 900-1050° C., baking time is from 20 minutes till 4 hours. For typical cases, baking temperature is 1000° C., baking time is 2 hours.
After compaction and baking, the blanks with dimensions indicated by arrows a and b of, for example, 60×90 mm were produced, as seen in
Due to two following circumstances, it is difficult to forge copper: Presence of <<brittleness zone>> of copper base in temperature range of 300-600° C.; presence of significant amount of brittle addition—yttrium oxide.
In the case being considered, the temperature range of forging was chosen in temperature range of 900-950° C. with time of exposure of 60 minutes at forging temperature. Forging was conducted in swages after 5 mm in a pass to the diameter with intermediate heating after each pass according to the scheme:
Ø60→Ø55→Ø45→Ø40→Ø35→Ø29 mm as shown by arrow d in
Samples for determination of mechanical properties were made along with the blanks for electrodes. The main mechanical properties are represented in Table 1.
From represented data, it transpires that insertion of iron tends to increase the strength. Insertion of Y2O3 decreases the strength. Presence of 1% mass Y2O3 and more essentially hampers plastic deformation and further processing of the blanks.
The range of component content is chosen from the following considerations. Increase of Y2O3 content above than 1% decreases material plasticity and it is impossible to obtain the members of required shape and dimensions. Decrease of the Group IIIB metal component (such as Y2O3) content below about 0.1%, and in some cases below about 0.05%, is detrimental to arc stability, and decrease of Fe below 3%, greatly reduces strength. Increase of Fe content above 30% impermissibly decreases heat conduction and electric conduction.
Mechanical processing and bending of blanks were carried out to obtain finished member, see
The finished electrode, indicated at 10, of
It has thus been shown that the present invention provides a material for electrodes of low temperature AC plasma generators. This material for low temperature AC plasma generators contains a porous metal matrix impregnated with the material emitting electrons and uses a baked mixture of copper and iron powders as a porous metal matrix and Group IIIB metal component (yttrium oxide Y2O3) inserted in the process of mixing of matrix powders as a material emitting electrons at the following proportion of the components, mass %:
In another example, three AC plasma electrodes containing (1) copper, (2) chromium carbide and (3) the above 30% Cu, 0.1% Y2O3, remainder Fe composition of the invention, were manufactured and operated in two types of AC plasma generators, a single phase 10 kW generator and a 50 kW three phase plasma generator. The results of testing are indicated below:
The data in Table 2 indicates that Group IIIB metal components in combination with iron and copper, provide enhanced lifetimes to AC plasma electrode compositions employed in an AC plasma generator.
While a particular embodiment, including specific materials and parameters has been described and illustrated to exemplify and teach the principles of the invention, such is not intended to be limiting. Modifications and changes may become apparent to those skilled in the art, and it is intended that the invention be limited only by the scope of the appended claims.
The United States Government has rights in this invention pursuant to Contract No. W-7405-ENG-48 between the United States Department of Energy and the University of California for the operation of Lawrence Livermore National Laboratory.
Number | Name | Date | Kind |
---|---|---|---|
3138453 | Foster et al. | Jun 1964 | A |
3918957 | Suzuki et al. | Nov 1975 | A |
3953705 | Painter | Apr 1976 | A |
4168565 | Ishii et al. | Sep 1979 | A |
4229873 | Bykhovsky et al. | Oct 1980 | A |
4420346 | Belkin et al. | Dec 1983 | A |
5075589 | Derks et al. | Dec 1991 | A |
5126622 | Jeong et al. | Jun 1992 | A |
5128584 | Choi | Jul 1992 | A |
5200594 | Okada et al. | Apr 1993 | A |
5318468 | Lotthammer et al. | Jun 1994 | A |
5507675 | Frost | Apr 1996 | A |
5609777 | Apunevich et al. | Mar 1997 | A |
5800618 | Niori et al. | Sep 1998 | A |
5904828 | Sekhar et al. | May 1999 | A |
20020057043 | Miyamoto | May 2002 | A1 |
Number | Date | Country |
---|---|---|
0537495 | Apr 1993 | EP |
06081057 | Mar 1994 | JP |
Number | Date | Country | |
---|---|---|---|
20100007262 A1 | Jan 2010 | US |