Patent Grant
7399431
1. Technical Field
This invention relates to a material for neutron shielding and for maintaining sub-criticality, and a process for preparation of this material and applications of it.
The material according to the invention has the special feature that it is remarkably suitable for slowing and absorbing neutrons, while having a particularly low density.
Therefore, it can represent an ideal material for making neutron shields in packagings for transport, interim storage and/or ultimate storage of radioactive materials, and particularly new nuclear fuel assemblies, in other words assemblies that have not yet been irradiated, like those composed of plutonium-base oxides that emit neutrons rather than gamma radiation.
2. State of Prior Art
Materials designed to form neutron shields in packaging for transport, interim storage and/or ultimate storage of nuclear fuels must have a number of properties.
Firstly, they must be capable of slowing and very efficiently capturing neutrons, particularly to keep these packagings sub-critical, in other words to prevent neutrons formed in them from causing a nuclear chain reaction.
They must also have a good resistance to aging at relatively high temperatures since the presence of nuclear fuels in the packagings generates high temperatures (of the order of 150° C. during normal transport conditions).
They must also have a low thermal conductivity, but the conductivity must be high enough so that heat released by nuclear fuels within the packagings can be dissipated.
They must also have good fire resistance, which assumes that they are self-extinguishing, in other words they stop burning as soon as the flames have gone out.
Finally, it is desirable that these materials should have a relatively low density so that their presence in the packagings does not increase their weight any more than necessary.
The materials should have a high content of hydrogen and should contain an inorganic compound, for example based on boron that is efficient in capturing neutrons, in order to slow and capture neutrons.
Thus, for example:
These materials are not fully satisfactory. In particular, they do not have sufficient resistance to thermal aging due to the nature of the hydrogenated polymers contained in them, and their density is too high.
Thus for example, the material described in EP-A-0 628 968 has a density of at least 2.
Within the context of his research work, the Applicant has developed a material that combines excellent properties for neutron shielding and maintaining sub-criticality, with very satisfactory self-extinguishing and thermal properties, particularly in terms of resistance to thermal aging.
This material comprises a matrix based on a vinylester resin such as a novolac resin within which are dispersed firstly a hydrogenated inorganic compound capable of slowing neutrons such as alumina hydrate, and secondly an inorganic boron compound such as zinc borate, capable of capturing them.
Its remarkable properties are explained particularly by the fact that vinylester resins, apart from being rich in hydrogen and consequently capable of very efficiently slowing neutrons, have low thermal conductivity and excellent thermal stability.
However, its density is equal to at least 1.6 and it is usually between 1.65 and 1.9.
Therefore, the Inventors set themselves the objective of finding a material with properties similar to the properties of this material based on a vinylester resin, but with a lower density.
This purpose is achieved by the invention that proposes a material for neutron shielding and maintaining sub-criticality, in which the material comprises a matrix based on a vinylester resin, at least one polyamide and an inorganic filler capable of slowing and absorbing neutrons.
The Inventors observed that by incorporating a compound chosen from within the polyamides family (most members of this family have a relatively high content of hydrogen, low density (of the order of 1 to 1.2 depending on the polyamide) and a high melting temperature) into a vinylester resin-based matrix, together with an inorganic filler capable of slowing and absorbing neutrons, a material can be obtained with properties that are as just as attractive as the properties of the said material based on a vinylester resin, or even better in terms of neutron shielding and maintaining sub-criticality, but with a density of between 1.3 and 1.6.
According to this invention, the term “polyamide” refers equally well to a homopolyamide derived from the reaction between amino and acid groups belonging to the same molecule, or a copolyamide resulting from the reaction between amino and acid groups belonging to different molecules.
According to the invention, the polyamide may equally well be an aliphatic, semi-aromatic or aromatic polyamide.
However, it is preferred to use an aliphatic polyamide, since aliphatic polyamides are richer in hydrogen than semi-aromatic and aromatic polyamides, and consequently capable of making a greater contribution to slowing of neutrons by the material.
The polyamide is preferably chosen from among the group composed of 11 polyamides (C11H21ON), 12 polyamides (C12H23ON) and 6–12 polyamides (C12H22O2N2), which have densities equal to 1.04, 1.02 and 1.07 respectively and melting temperatures equal to 187, 178 and 212° C. respectively.
These polyamides are available in the form of powders with different size gradings, for example from ATOFINA company that markets them under the brands Rilsan® D (11 polyamide) and Orgasol® (6, 12, 6–12 polyamides).
Also according to the invention, the choice of the polyamide is guided firstly by its chemical composition (which controls its hydrogen content), its density and melting temperature, and also by its size grading as a function of conditions for use of the material, and particularly the viscosity required from this material before the vinylester resin is polymerized.
Thus for example, Rilsan® D80 polyamides that are in the form of fine powders (Ø=75−85 μm) are used to obtain mixes with a lower viscosity than mixes obtained using Orgasol®, which are ultrafine powders (Ø=5−60 μm) and are therefore easier to pour into a mould.
Different types of vinylester resin may be used in the composition of the material.
Preferably, a vinylester resin will be used derived from the reaction caused by the addition of a carboxylic acid with an epoxy resin.
In particular, this carboxylic acid may be acrylic acid or methacrylic acid, methacrylic acid being preferred since it has a higher hydrogen content, while the macromolecular pattern of the epoxy resin may be of the bisphenol A or novolac type.
Thus, the vinylester resin is preferably chosen from the group composed of bisphenol A-type epoxyacrylate and epoxymethacrylate resins, novolac-type epoxyacrylate and methacrylate resins, and epoxyacrylate and epoxymethacrylate resins based on halogenated bisphenol A.
The bisphenol A-type epoxyacrylate and epoxy-methacrylate resins respond to the following formula
in which R represents a hydrogen atom or a methyl group.
The novolac-type epoxyacrylate or epoxymethacrylate resins are defined by the following formula (II):
in which R represents a hydrogen atom or a methyl group.
Halogenated epoxyacrylate or epoxymethacrylate resins based on bisphenol A are defined by the following formula (III):
in which R represents a hydrogen atom or a methyl group.
As a variant, a non-epoxy vinylester resin obtained from an isophthalic polyester and an urethane can also be used in a material according to the invention, for example responding to the following formula (IV):
where R represents a hydrogen atom or a methyl group, while U represents an urethane group.
Preferably, the vinylester resin is an epoxyacrylate or epoxymethacrylate resin of the novolac type.
According to the invention, the material also comprises an inorganic filler capable of slowing and absorbing neutrons.
This inorganic filler preferably comprises at least one hydrogenated inorganic compound and at least one inorganic boron compound.
Advantageously, the hydrogenated inorganic compound is chosen from the group composed of alumina hydrates and magnesium hydroxide (Mg(OH)2), while the inorganic boron compound is chosen from the group composed of boric acid (H3BO3), colemanite (Ca2O14B6H10), zinc borates (Zn2O14,5H7B6, Zn4O8B2H2, Zn2O11B6), boron carbide (B4C), boron nitride (BN) and boron oxide (B2O3).
Preferably, the hydrogenated inorganic compound is alumina hydrate with formula Al2O3, while the inorganic boron compound is zinc borate with formula Zn2O14.5H7B6 or boron carbide.
The material according to the invention may also comprise an anti-shrinkage agent such as a poly(vinyl acetate) capable of preventing it from shrinking during polymerization of the vinylester resin.
It may also comprise a hydrogenated organic filler such as melamine, to improve its self-extinguishing properties.
According to the invention, the quantity of hydrogenated inorganic compound is chosen such that, considering the hydrogen quantities also provided by the vinylester resin and the polyamide, the atomic concentration of hydrogen in the material will preferably be between about 4.5×1022 and 6.5×1022 at/cm3.
Similarly, the quantity of the inorganic boron compound is chosen such that the material preferably has an atomic concentration of boron between about 8×1020 and 3×1021 at/cm3.
Very satisfactory materials have been obtained from mixes in which the vinylester resin and the polyamide account for between 30 and 45% and between 10 to 30% respectively of the total mass of this resin, this polyamide and inorganic filler being capable of slowing and absorbing neutrons.
The material according to the invention may be preferred by setting of a mix containing its different constituents, this setting resulting from polymerization of the vinylester resin.
Another purpose of the invention is a process for preparation of this material including the following steps:
Commercially available vinylester resins are in the form of solutions in which the solvent is a vinyl solvent, and the quantity of solvent present in these resins is usually sufficient so that the various constituents of the material are easy to mix and the resulting consistency is suitable.
However, a vinyl solvent could be added while mixing the said constituents if necessary.
Examples of vinyl solvents that could be used include styrene, vinyltoluene, divinylbenzene, methylstyrene, methyl acrylate, methyl methacrylate or an allylic derivative such as diallyl phthalate.
Preferably, the solvent used will be the same solvent as for vinylester resin, and particularly styrene, since this is the most frequently used solvent for the preparation of vinylester resins.
Accelerators and polymerization catalysts are chosen from along the compounds normally used to obtain polymerization of vinylester resins.
In particular, accelerators may consist of divalent cobalt salts such as cobalt naphthenate or octoate, and aromatic tertiary aminos such as dimethylaniline, dimethylparatoluidine and diethylaniline.
In particular, catalysts may for example be organic peroxides, for example:
One or several additives can also be added to the mix, such as a resin polymerization inhibitor, a surfactant or an anti-shrinkage agent.
Acetylacetone and tertiobutylcathecol are other examples of polymerization inhibitors that can be used.
The process according to the invention may be used as follows.
The vinylester resin, polyamide, the inorganic filler capable of slowing and absorbing neutrons (for example inorganic hydrogenated and boron compounds) and the polymerization accelerator are mixed at ambient temperature until a perfectly uniform mix is obtained.
The polymerization catalyst is added and after homogenization, the resulting mix is degassed under a vacuum (less than 0.01 MPa).
Ideally, the viscosity of this mix must not exceed 300 Poises, so that it can easily be poured into a mould.
After degassing, the mix is poured into the required mould where it sets, due to polymerization of the vinylester resin, and is transformed into an insoluble material. This is a radical type polymerization and it is highly exothermal. The setting time may vary depending on pour conditions (temperature, catalyst, accelerator content, etc.). Thus, the gel time may be varied by varying the percentages of catalyst and accelerator. The gel time varies from 20 minutes to 2 hours.
According to the invention, the mould used for setting the mix may be composed of a compartment of a packaging for transport, interim storage and/or ultimate storage of radioactive products. This packaging may in particular comprise several peripheral components into which the mix is poured.
Another purpose of the invention is packaging for transport, interim storage and/or ultimate storage of radioactive materials that comprises at least one shield formed from a material like that described above.
Preferably, this packaging is designed to transport a new nuclear material such as a fuel composed of a plutonium-based oxide.
Other special features and advantages of the invention will become clearer after reading the following description related to an example production of a material according to the invention-and an example demonstration of its properties, and that is given for illustrative purposes and is in no way limitative, with reference to the attached drawing.
The mix is prepared:
A polymerization catalyst (Butanox® M50-AKZO) is added to this mix, at a content of 1% by mass of this mix.
The mix is then degassed for three minutes under a vacuum, and this mix is then poured into a mould composed of a compartment of the packaging used for transport of nuclear fuels.
The gel time is 25 minutes at 20° C.
The following are measured:
The results of these measurements are shown in Table 1.
Table 1 also shows the density, hydrogen and boron contents, the vitreous transition temperature (Tg), the coefficient of thermal expansion (α), the specific heat (Cp) and the thermal conductivity (λ) of a material hereinafter referred to as the “reference material” formed after setting of a mix of the following constituents (25 minutes at 20 C.), for comparison purposes:
Table 1 shows that the density of the material according to the invention is significantly lower than the density of the reference material that does not contain any polyamide (1.43 compared with 1.79).
It also has significantly higher hydrogen and boron contents than the reference material.
Thus, although it is lighter, its performances in terms of neutron shielding and maintenance of sub-criticality, are better.
Thermal aging tests of the material according to the invention are also carried out, by keeping samples of this material measuring 35×25×95 mm3 in two chambers heated to 160° C. and 170° C. respectively for 5 months, and monitoring the loss of mass of these samples with time.
The results of these tests are given in
Fire behavior tests are also carried out by placing blocks of material according to the invention with a diameter of 240 mm and a thickness of 60 mm, either directly in contact with the flame of a torch at a temperature of 800° C., or in contact with a 1 mm thick steel plate in contact with the torch flame, for half an hour.
In both cases, the material according to the invention obviously self-extinguishes as soon as the torch is removed.
| Number | Date | Country | Kind |
|---|---|---|---|
| 02 13369 | Oct 2002 | FR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2796411 | Zirkle et al. | Jun 1957 | A |
| 2961415 | Axelrad | Nov 1960 | A |
| 3133887 | Alliegro et al. | May 1964 | A |
| 3261800 | Collins | Jul 1966 | A |
| 3361684 | Chvatal | Jan 1968 | A |
| 3609372 | Vogel | Sep 1971 | A |
| 3829532 | Meloy | Aug 1974 | A |
| 3879318 | Forsyth | Apr 1975 | A |
| 4134937 | Cass | Jan 1979 | A |
| 6548570 | Lange | Apr 2003 | B1 |
| 6605817 | Nihei | Aug 2003 | B1 |
| 6797972 | Kamoshida et al. | Sep 2004 | B2 |
| 20050001205 | Malalel et al. | Jan 2005 | A1 |
| 20050012054 | Valiere | Jan 2005 | A1 |
| Number | Date | Country |
|---|---|---|
| 199 55 192 | May 2001 | DE |
| 0 108 622 | May 1984 | EP |
| 0 119 781 | Sep 1984 | EP |
| 0 372 758 | Jun 1990 | EP |
| 0 628 968 | Dec 1994 | EP |
| 2092848 | Jan 1972 | FR |
| 2505080 | Nov 1982 | FR |
| 2 546 331 | Nov 1984 | FR |
| 859696 | Jan 1961 | GB |
| 1 049 890 | Nov 1966 | GB |
| 55-119099 | Sep 1980 | JP |
| 59 126296 | Jul 1984 | JP |
| 60 065032 | Apr 1985 | JP |
| WO9528440 | Oct 1995 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20040127599 A1 | Jul 2004 | US |