Material for retainers of tapered roller bearings

Abstract

A retainer for a tapered roller bearing comprising a polyamide resin, 10 to 20% by weight of an elastomer and 15 to 30% by weight of a reinforcing fiber.

Description

BACKGROUND OF THE INVENTION

The present invention relates to the retainers of tapered roller bearings, and it more particularly relates to a particularly effective synthetic resin composition to be used for the retainers of tapered roller bearings.

Synthetic resin materials are widely used for the retainers or cages of antifriction bearings such as ball bearings. However, conventional synthetic resin materials still have problems when used for the retainers of tapered roller bearings, and thus need to be improved in performance. For example, polyamide resins, such as nylon 66, undergo marked dimensional variations due to hygroscopicity, rendering the inner ring assembly subject to separation. When reinforced with glass fiber or carbon fiber, nylon 66, and similar polyamide resins, exhibit reduced dimensional variations but have poorer elongation, with result that the rib portion of the retainer is prone to damage when the retainer is assembled into a bearing or during handling.

SUMMARY OF THE INVENTION

The main object of the present invention is to provide a retainer for tapered roller bearings made of a material which is less susceptible to dimensional variations and to damage.

The material to be used for the retainer of a tapered roller bearing according to this invention is characterized in that it comprises a polyamide resin, 10 to 20% by weight of an elastomer and 15 to 30% by weight of a reinforcing fiber.

Examples of suitable polyamide resins include nylon 66 and the like. Examples of useful elastomers include polybutadiene rubber and the like. Examples of useful reinforcing fibers are glass fiber, carbon fiber, etc. Preferably, a mixture of polyamide resin and elastomer is reinforced with such fiber to obtain a composite material. The nylon 66, polybutadiene, glass and carbon fibers, and other comparable components of the instant invented retainer are all commercially available commodities purchasable from several sources.

The polymer mixture to be used for retainer material of the present invention has incorporated therein the reinforcing fiber and is therefore diminished in dimensional variations due to hygroscopicity. Moreover, the presence of the elastomer imparts enhanced impact strength and increased elongation to the material, rendering the retainer less susceptible to damage during assembling or handling. The retainer of this invention being based on a synthetic resin material, is light-weight and has a longer life, giving products which require lower maintenance.

Thus, the present invention provides a retainer material which is diminished in dimensional changes, resistant to damage, lightweight and serviceable over a prolonged period of time, all of which are highly improved properties.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph showing the results obtained by testing the retainers of comparative examples and examples of the invention for thermal hysteresis contraction and expansion due to absorption of water;

FIG. 2 is a graph showing the relation between the water absorption ratio and the dimensional variation as established by testing a comparative retainer and a retainer of the invention; and

FIG. 3 is a graph showing the results of grease immersion tests conducted on the same retainers as shown in FIG. 2.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

To substantiate the advantages of the invention described above, examples of the invention are given below.

First, retainers were prepared from six materials listed in Table 1 as Comparative Examples 1 to 4 and Examples 1 and 2.

TABLE 1______________________________________ Glass fiber RubberEx- content contentample Component (wt. %) (wt. %)______________________________________Comp. Nylon 66 only 0 0Ex. 1Comp. Nylon 66 reinforced with 8.3 0Ex. 2 glass fiberComp. Same as above 25 0Ex. 3Comp. Mixture of nylon 66 and 0 10Ex. 4 polybutadiene rubberEx. 1 Mixture of nylon 66 and 15 10 polybutadiene rubber, rein- forced with glass fiberEx. 2 Same as above 30 20______________________________________ *In each example, the remainder of the product in addition to the percentages set forth, was nylon 66.

The retainers of the comparative examples and the examples were annealed, under conditions of 120.degree. C. for 2 hours, 150.degree. C. for 3 hours or 180.degree. C. for 4 hours, to check them for contraction due to annealing. The retainers were also immersed in tap water at room temperature (25.degree. C.) and checked for expansion due to the absorption of water by measuring their dimensions from time to time. The retainers were thereafter immersed in water for 1 month to determine the saturation water absorption ratio and the resulting dimensional variation.

FIG. 1 shows the amount of thermal hysteresis contraction resulting, for example, from annealing the molded retainer rings at 180.degree. C. for 4 hours, and the amount of expansion due to the absorption of water to saturation, in terms of variations in the radial clearance. The hatched portion of the expansion diagram represents the amount of expansion due to 5% water absorption.

The illustrated results reveal the following. The examples of the invention are not greater than the comparative examples in the amount of thermal hysteresis contraction and are substantially smaller than Comparative Example 4 in the amount of expansion due to water absorption. The invention examples having about the same glass fiber content as Comparative Examples 2 and 3 are smaller than the latter in the amount of expansion.

FIG. 2 shows the relation between the water absorption ratio and the radial clearance determined for Example 1 and Comparative Example 1. The graph indicates that the dimensional variation of Example 1 is smaller than that of Comparative Example 1.

Next, the retainers of Example 1 and Comparative Example 1 were immersed in grease at 120.degree. C. or 150.degree. C. and tested for resistance to grease. The grease used was Li-mineral oil grease, #2 in consistency, which is a multipurpose grease generally used for passenger motor vehicle wheels.

FIG. 3 shows the test results, which reveal the following. Comparative Example 1 exhibits decreasing tensile strength with time, especially a marked reduction at the higher temperature (150.degree. C.), whereas in the case of Example 1, the tensile strength remains almost unchanged despite prolonged immersion time.

The foregoing test results show that the retainers made of the material of this invention have: low saturation water absorption ratios and dimensional variations due to the absorption of water and have high dimensional stability and greatly improved resistance to grease.

Next, two bearing sets were prepared, each of which comprised two tapered roller bearings fabricated using retainers of Example 1, and combined together back-to-back. The retainers were tested for durability by rotating the inner ring and subjecting the outer ring to a load under the following conditions.

______________________________________Radial load: 400 kg fThrust load: 160 kg fSpeed of rotation of inner ring: 910 r.p.m.Nut clamping force: 23 .+-. 2 kg f (center)Test period: 1200 hoursGrease: Li-mineral oil grease (same as above)Temperature: Allowed to rise spontaneously (60-70.degree. C.)______________________________________

The results were listed in Table 2, in which the two bearings of each of the sets (sets 1 and 2) are designated by A and B.

TABLE 2______________________________________ Dimensional change StrengthIron in retainer (%) ofin Small end Large end retainergrease inside inside (new one,(wt. %) diameter diameter 12.6 kg f)______________________________________Set 1Bearing A 0.02 -0.09 -0.13 11.9 (-5.6%)Bearing B 0.03 -0.12 -0.15 12.7 (+0.8%)Set 2Bearing A 0.07 -0.07 -0.08 12.3 (-2.4%)Bearing B 0.05 -0.10 -0.06 12.8 (+1.6%)______________________________________

The durability test revealed the following. The iron content of the grease was lower than 0.1%, indicating that the grease remained substantially free of contamination. The resulting dimensional variations (changes) were less than 0.15% and exceedingly smaller than in conventional products (which are usually less than about 1%). Variations in the strength of retainers were also small, hence the invented retainers showed high strength.

Retainers of Example 1 were tested for heat resistance in the same manner as in the above durability test under the following conditions. For heating, a band heater was provided around the bearing assembly.

______________________________________Radial load: 300 kg fThrust load: 120 kg fSpeed of rotation of inner ring: 910 r.p.m.Test period: 500 hoursGrease: Li-mineral oil grease (same as above)Temperature: 135 .+-. 5.degree. C.______________________________________ TABLE 3______________________________________ Dimensional change StrengthIron in retainer (%) ofin Small end Large end retainergrease inside inside (new one,(wt. %) diameter diameter 12.6 kg f)______________________________________Set 1Bearing A * -0.14 -0.09 14.4 (+14.3%)Bearing B * -0.07 -0.06 13.1 (+4.0%)Set 2Bearing A * -0.06 -0.07 12.9 (+2.4%)Bearing B * -0.10 -0.12 13.7 (+8.7%)______________________________________ *Not measurable due to carbonization.

The heat resistance test reveals the following. Although the grease was completely carbonized, no abnormalities were found in the appearance of the retainers. Despite the exposure to a high temperature, the resulting dimensional variations were less than 0.014%, hence the products exhibited very high heat resistance. The strength of the retainers was improved by 2 to 14% and therefore entailed no problem. Even after the 1200-hour durability test and the heat resistance test at a high temperature of 135.+-.5.degree. C., the retainers of the invention retained a good appearance, exhibited only small variations in dimensions and in strength and were found satisfactory in properties. These test results indicate that the retainer material of the invention is outstanding in durability and heat resistance.

Claims

1. A retainer for a tapered roller bearing comprising a mixture of 15 to 30% by weight reinforcing glass fiber, 10 to 20% by weight of a polybutadiene elastomer and the remainder a nylon 66 resin.

2. A retainer as claimed in claim 1 wherein said retainer consists essentially of about 15% glass fiber, about 10% polybutadiene and about 75% nylon 66.

3. A retainer as claimed in claim 1 wherein said retainer consists essentially of about 30% glass fiber, about 20% polybutadiene and about 50% nylon 66.