Material with spectrally selective reflection

Abstract

The invention relates to a material with spectrally selective reflection in the primary valences of red, green and blue. This material is applied preferably onto laser projection screens in order to make possible the projection even in daylight. In a first embodiment, a first layer of a material that is highly reflective over the entire range of visible light, e.g., aluminum is applied onto a substrate, e.g., glass or a synthetic material, which is followed by a second layer of a material that is essentially non-absorbing over the entire range of visible light, e.g., SiO2, on which, in turn, a third layer f a material that is partially transmissive over the entire range of visible light, e.g., of NiCr is disposed. The latter is in contact with air. An alternative embodiment comprises five layers, of which a first is comprised of a material with a high index of refraction, e.g., TiO2, a second of a material with a low index of refraction, e.g., SiO2, the third of a material with a high index of refraction, e.g., TiO2; a fourth of a material with a low index of refraction, e.g., SiO2, and a fifth layer of a material with a high index of refraction, e.g., TiO2. In this embodiment, the first layer is here connected with the substrate, while the fifth layer is in contact with air.

Description

FIELD OF THE INVENTION

[0001] The invention relates to a material with spectrally selective reflection, preferably in the valences of red, green and blue.

BACKGROUND AND SUMMARY OF THE INVENTION

[0002] Materials with specific optical properties are needed in numerous technical fields. For example specific layers are applied onto synthetic materials in order to generate mirror properties (DE 39 27 087 C2), or multilayer systems are applied onto window panes in order to provide thermal protection (DE 197 45 881 A1).

[0003] Multilayer filter systems, which have specific reflection and/or transmission properties (WO 95/17690), are also employed in the case of liquid crystal displays. These filter systems comprise for example in each pixel region filters for red, green and blue, with each filter having a common dielectric broadband mirror. The difference between the filters consists in the tuning thickness between the mirrors for each filter. Use of the common dielectric broadband mirror simplifies the process of production of mosaic arrays in the RGB filter.

[0004] Furthermore a color filter grouping for a surface image sensor is known, which comprises several color filters on the sensor, which selectively filter out different colors (U.S. Pat. No. 4,979,803). Each color filter comprises at the bottom a semitransparent and partially reflecting silver layer. On this silver layer is disposed a transparent and absorption-free dielectric layer having a thickness which is selected such that it corresponds to the wavelengths of the light to impinge onto the image sensor.

[0005] A further known optical filter is comprised of two mirror layers which form an optical resonance space with a dielectric layer being disposed between these mirror layers (U.S. Pat. No. 5,726,805).

[0006] Another filter with variable wavelengths of modifying etalon type comprises at least two reflecting surfaces whose spacing from each other is not constant but rather increases or decreases monotonically from the spacing in a selected direction in a light-sensitive plane of the etalon (EP 0 442 738 A2).

[0007] Interference filter groupings on the basis of a thin metal filter and comprising at least one dielectric layer between two metal layers are disclosed in U.S. Pat. No. 6,031,653. The two metal layers are of a thickness which is less than the penetration depth of the radiation.

[0008] Furthermore is known an optical filter in which several optical layers are disposed one on the other, which are alternately comprised of a high-refraction material, TiO2, and a low-refraction material, SiO2 (U.S. Pat. No. 5,731,898).

[0009] None of the filters listed above reflects spectrally selectively in the primary valences of red, green and blue, as a consequence of which the filters are not suitable for a laser projection screen.

[0010] Projection screens must have special optical properties in order to ensure brilliant image representation. This applies especially to laser projection, in which a deflectable laser beam, into which the primary colors red, green and blue are coupled, scans the screen (cf DE 196 40 404 A1). The projection screens must have reflection maxima in the red, green, blue wavelengths of approximately 629 nm, 532 nm and 447 nm, respectively. In addition, a broadband background light must be absorbed, for example in a subjacent black layer.

[0011] A further requirement made of the properties of laser projection screens comprises that the reflection must not involve a mirror-like reflection but rather a diffuse reflection in a preselectable solid angle range in order for the viewing of the projected images to be possible from different locations. Reflections in a spatial region in which no observer is present must be avoided in order to minimize intensity losses. The screen must thus not be a Lambert radiator in which the luminance is constant in all directions of a half space. According to DIN standard 19045, Bereich Betrachtungsbedingungen {Area: Viewing Conditions}, the reflection should be up to ±40° in the horizontal direction, measured from the projection axis, and ±10° in the vertical direction, measured from the visual axis of a central viewer. In addition, the shift which can be observed of the reflection characteristic with changed reflection angle—the so-called color flop—should also be largely suppressed.

[0012] Lastly, projection screens should meet the requirement that they also ensure good recognizability of the projected images in non-darkened rooms.

[0013] The invention therefore addresses the problem of providing a material for projecting screens which is suitable for laser projection. This problem is solved according to the present invention.

[0014] The invention consequently relates to a material with spectrally selective reflection in the primary valences of red, green and blue. This material is preferably applied onto laser projection screens in order to make projection possible even in daylight. In a first solution, onto a substrate, for example glass or synthetic material, a first layer of aluminum is applied, which is followed by a second layer of SiO2, on which, in turn, a layer of NiCr is disposed. The latter is in contact with air. A second solution comprises five layers, of which the first is comprised of TiO2, the second of SiO2, the third of TiO2 the fourth of SiO2 and the fifth of TiO2. The first layer is here connected with the substrate, while the fifth layer is in contact with air. The first solution is much simpler than the second solution.

[0015] The advantage attained with the invention comprises in particular that utilizing only three layers, one metallic layer and two dielectric layers, the above stated requirements are met in a laser image screen. It is here especially advantageous that the metallic layer can be produced cost-effectively, for example by vapor deposition in film coating installations. In comparison to sputter processes the metal layer can be applied at approximately the 10- to 100-fold rate. The dielectric layer can alternatively be applied with the cost-effective vapor deposition technology or the sputter technology. The requirements are alternatively also fulfilled with the aid of a five-layer system of dielectric materials with a high index of refraction. However, the production of the five-layer system is significantly more costly than the production of the three-layer system. Both layer systems can be readily produced as a large-area system by means of a DC or a medium frequency sputter process. Consequently the expensive production of the fully dielectric layer systems commonly used up to now becomes superfluous. The reproducibility of the layer thickness and the indices of refraction is better than 1%.

[0016] It is understood that projection operation under daylight conditions entails a certain desaturation of the colors. Daylight contains a component in the RGB range. If the laser is switched off and only daylight falls onto the coated screen, the screen appears white since the reflected daylight component in the RGB range yields the color white through an additive color mixture. This white is superimposed onto the laser colors such that the color saturation decreases slightly in comparison to pure spectral colors. The decrease of the color saturation, however, is less than is the case with conventional white screens, since a large component of the daylight spectrum, which is outside of the RGB maxima, is absorbed.

[0017] Embodiment examples of the invention are depicted in the drawings and will be described in further detail below.

BRIEF DESCRIPTION OF THE FIGURES

[0018] FIG. 1 the reflection curve of a material comprised of three layers,

[0019] FIG. 2 the reflection curve of a material comprised of five layers.

DETAILED DESCRIPTION

[0020] FIG. 1 depicts the reflection curve of a material comprised of three layers disposed one above the other, which is applied onto a substrate, for example onto glass or a synthetic material film. The first layer of this material, disposed directly on the substrate, is an aluminum layer having a thickness of approximately 100 nm, the second layer, disposed on the aluminum, is an SiO2 layer approximately 1030 nm thick, and the third layer, which is applied onto the SiO2 and which is in contact with air, is an NiCr layer approximately 30 nm thick. The first layer consequently is a layer highly reflecting over the entire range of visible light, while the second layer, which is disposed on the first layer, is a layer essentially non-absorbing over the entire range of visible light. Lastly the third layer is a layer, disposed on the second layer, which is partially transmissive over the entire range of visible light. This third layer is disposed above the other layers; the light to be reflected impinges directly onto this third layer.

[0021] As is evident in FIG. 1, the three-layer material has reflection maxima at approximately 445 nm, at 525 nm and at 629 nm. These wavelengths correspond rather precisely to the primary wavelengths for blue, green and red. In the case of the solution according to FIG. 1 the property of metallic layers is utilized, with which, in combination with a dielectric layer, reflection spectra can be generated which selectively reflect at different wavelengths.

[0022] The position of the curve in the spectrum can be varied readily by varying the layer thickness of the dielectric central layer. The central layer acts like a spacer in a Fabry-Perot filter, with the layer thickness being selected such that the higher orders generate the additional peaks. This means that for example the principal reflection is in the infrared range, i.e. at the fundamental frequency, but the reflection of the primary valences is in the secondary reflections, the so-called higher orders. A vacuum spacer without absorption could also be employed. The colors red, green and blue are reflected if as the higher order of the spacer layer is selected that at which the reflection peaks or maxima are at the wavelengths of the colors red, green and blue.

[0023] The first layer on the substrate ideally has as high a reflection as is possible in the visible range. Suitable materials are aluminum and silver. If, for example, NiCr were to be selected as the first layer, the height of the reflection peak would decrease drastically to 30 to 40%. The partial transmissivity of the third layer, which is provided above, lies at approximately 50% transmission and approximately 25% reflection. If the thickness of the NiCr layer is decreased from 30 nm to 20 nm, the reflection is increased at the maxima but also at the minima. If the thickness of the NiCr layer is increased from 30 nm to 50 nm, the reflection at the maxima is strongly decreased but less so at the minima.

[0024] There also is an optimum of the layer thickness in the upper layer, at which simultaneously high reflection at the maxima and as low as possible a reflection at the minima is attained.

[0025] The optimum layer thickness is a function of the material. With different metals different layer thicknesses result in the upper layer.

[0026] FIG. 2 depicts a further reflection curve, which has its maxima at the desired RGB locus of the spectrum. This reflection curve relates the optical properties of a material which is comprised of five layers. The first layer directly connected with the substrate—for example glass or synthetic material—is comprised of an approximately 468 nm thick TiO2 layer. On this TiO2 layer is disposed an approximately 127 nm thick SiO2 layer, on which, in turn, a 468 nm thick TiO2 layer is disposed. The last cited TiO2 layer is followed by a 72 nm thick SiO2 layer on which, in turn, a 483 nm thick TiO2 layer is disposed. This last TiO2 layer is in contact with air.

[0027] TiO2 has a high index of refraction of approximately 2.35; Bi2O3, Ta2O5 or TiOxNy or diamond C or silver bromide or silver iodide or cadmium sulfide have similarly high indices of refraction. SiO2 has a low index of refraction of approximately 1.45. Similarly low are the indices of refraction of fluorspar or opal. The refractive index is a function of the wavelength and is often measured at 589 nm, which corresponds to the wavelength of yellow sodium light. Titanium dioxide is present in the modifications anatase (index of refraction 2.49-2.56) and rutile (index of refraction 2.61-2.90).

[0028] Application of these layers onto the substrate is accomplished by means of a sputter process carried out for example with a 6-cathode sputter installation. Preferred is the high-rate medium frequency magnetron sputter process.

[0029] With such an installation, synthetic material films up to a thickness of 100 μm can be coated.

[0030] The adhesion of the layers on one another and that of the lowest layer on the substrate is very good such that no special adhesion layers are required.

[0031] As the substrate material, preferably rigid synthetic material substrates and firm composite materials are employed. Glass is a preferred substrate.

Claims

1. Material with spectrally selective reflection in the primary valences of red, green and blue, characterized by the following layers: 1.1 a first layer highly reflecting over the entire range of visible light; 1.2 a second layer, essentially non-absorbing over the entire range of visible light, which is disposed on the first layer and whose optical thickness is between approximately 600 nm and 900 nm, with the optical thickness being defined as 4·n·d where n is the index of refraction and d the geometric thickness; 1.3 a third layer, partially transmissive over the entire range of visible light, which is disposed on the second layer, with the third layer having a geometric thickness of approximately 20 to 80 nm.

2. Material as claimed in claim 1, characterized in that the first layer is comprised of aluminum, the second layer of SiO2 and the third layer of NiCr.

3. Material as claimed in claim 1, characterized in that the first layer is disposed on a substrate.

4. Material as claimed in claim 1, characterized in that the third layer is in contact with air.

5. Material as claimed in claim 2, characterized in that the first layer of aluminum is approximately 100 nm thick.

6. Material as claimed in claim 2, characterized in that the second layer of SiO2 is approximately 1030 nm thick.

7. Material as claimed in claim 1, characterized in that the third layer of NiCr is approximately 30 nm thick.

8. Material with spectrally selective reflection in the primary valences red, green and blue, characterized by the following layers: 8.1 a first layer of a material with a high index of refraction, for example TiO2, Ta2O5, TiOxNy or Bi2O3, which is approximately 400 to 600 nm thick; 8.2 a second layer of a material with a low index of refraction, for example SiO2, which is approximately 127 nm thick and which is disposed on the first layer of TiO2, Ta2O5, TiOxNy or Bi2O3; 8.3 a third layer of a material with a high index of refraction, for example TiO2, Ta2O5, TiOxNy or Bi2O3, which is approximately 400 to 600 nm thick and which is disposed on the second layer of SiO2; 8.4 a fourth layer of a material with a low index of refraction, for example SiO2, which is approximately 72 nm thick and which is disposed on the third layer of TiO2, Ta2O5, TiOxNy or Bi2O3; 8.5 a fifth layer of a material with a high index of refraction, for example TiO2, Ta2O5, TiOxNy or Bi2O3, which is approximately 400 to 600 nm thick and which is disposed on the fourth layer of SiO2.

9. Material as claimed in claim 8, characterized in that the first layer is disposed on a substrate.

10. Material as claimed in claim 3 or claim 9, characterized in that the substrate is glass.

11. Material as claimed in claim 3 or claim 9, characterized in that the substrate is a synthetic material.

12. Material as claimed in claim 8, characterized in that the fifth layer is in contact with air.

13. Material as claimed in claim 8, characterized in that when employing TiO2, the thickness of the first layer is 468 nm.

14. Material as claimed in claim 8, characterized in that when employing TiO2, the thickness of the third layer is 468 nm.

15. Material as claimed in claim 8, characterized in that when employing TiO2, the thickness of the fifth layer is 483 nm.

16. A material with spectrally selective reflection in the primary valences of red, green and blue, comprising: a first layer highly reflecting over the entire range of visible light; a second layer, essentially non-absorbing over the entire range of visible light, which is disposed on said first layer and whose optical thickness is between approximately 600 nm and 900 nm, with the optical thickness being defined as 4*n*d where n is the index of refraction and d the geometric thickness; a third layer, partially transmissive over the entire range of visible light, which is disposed on the second layer, wherein the third layer has a geometric thickness of approximately 20 to 80 nm.

17. The material as claimed in claim 16, wherein said first layer comprises aluminum, said second layer comprises SiO2 and said third layer comprises NiCr.

18. The material as claimed in claim 16, wherein said first layer is disposed on a substrate.

19. The Material as claimed in claim 16, wherein said third layer is in contact with air.

20. The material as claimed in claim 17, wherein said first layer has a thickness of approximately 100 nm.

21. The material as claimed in claim 17, wherein said second layer has a thickness of approximately 1030 nm.

22. The material as claimed in claim 17, wherein said third layer has a thickness approximately 30 nm thick.

23. A material with spectrally selective reflection in the primary valences red, green and blue, comprising: a first layer of a material with a high index of refraction which is approximately 400 to 600 nm thick; a second layer of a material with a low index of refraction which is approximately 127 nm thick and which is disposed on said first layer; a third layer of a material with a high index of refraction which is approximately 400 to 600 nm thick and which is disposed on said second layer; a fourth layer of a material with a low index of refraction which is approximately 72 nm thick and which is disposed on said third layer; a fifth layer of a material with a high index of refraction which is approximately 400 to 600 nm thick and which is disposed on said fourth layer; wherein said material with a high index of refraction in at least one of said first layer, said third layer and said fifth layer is selected from the group consisting of TiO2, Ta2O5, TiOxNy and Bi2O3 and said material with a low index of refraction in said second layer and said fourth layer are each SiO2.

24. The material as claimed in claim 23, wherein said first layer is disposed on a substrate.

25. The material as claimed in claim 18, wherein said substrate is glass.

26. The material as claimed in claim 24, wherein said substrate is glass.

27. The material as claimed in claim 18, wherein said substrate is a synthetic material.

28. The material as claimed in claim 24, wherein said substrate is a synthetic material.

29. The material as claimed in claim 23, wherein said fifth layer is in contact with air.

30. The material as claimed in claim 23, wherein said first layer is TiO2 and has a thickness of 468 nm.

31. The material as claimed in claim 23, wherein said third layer is TiO2 and has a thickness of 468 nm.

32. The material as claimed in claim 23, wherein said fifth layer is TiO2 and has a thickness of 483 nm.