Matrix liquid crystal display

Abstract

The invention relates to a matrix liquid crystal display containing integrated non-linear elements and a liquid crystal mixture which has a particularly high resistivity.

Description

The invention relates to a matrix liquid crystal display containing

two plane parallel support plates which together with a frame form a cell, integrated non-linear elements for switching individual picture elements on the support plates and a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity, the liquid crystal mixture being based on the following components: a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR1## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms, the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene, Z.sup.1 and Z.sup.2 are each, independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond, and m is 0, 1 or 2, and c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5, and the nematic liquid crystal mixture having a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of 30 mPa.s and a mean dielectricity constant .epsilon..ltoreq.8.

Matrix liquid crystal displays (MLC displays) according to the preamble are known. For example, active elements (i.e. transistors) can be used as non-linear elements for the individual switching of the individual picture elements. This is referred to as an "active matrix", in which two types can be distinguished:

1. MOS (metal oxide semiconductor) transistors on a silicon wafer as the substrate. 2. Thin film transistors (TFT) on a glass plate as the substrate.

In the case of type 1, dynamic scattering or the guest/host effect is usually used as the electrooptical effect. The use of single-crystal silicon as the substrate material limits the size of the display, since, even if different partial displays are put together in the form of modules, difficulties arise at the joints.

In the case of the more promising type 2, which is preferred, the TN effect is usually used as the electrooptical effect. Two technologies are distinguished: TFTs consisting of compound semiconductors, such as, for example, CdSe, or TFTs based on polycrystalline or amorphous silicon. The latter technology is the subject of intense development work worldwide.

The TFT matrix is disposed on the inside surface of one of the glass plates of the display, while the other glass plate carries the transparent counter electrode on its inside surface. Compared with the size of the picture element electrode, the TFT is very small and essentially does not interfere with the picture. This technology can also be extended to picture displays in fully satisfactory colours by arranging a mosaic of red, green and blue filters in such a manner that each filter element is opposite to a switchable picture element.

The TFT displays usually operate as TN cells which contain crossed polarizers in transmission and are illuminated from behind.

The term MLC displays in this context comprises each matrix display which has integrated non-linear elements, i.e. apart from the active matrix also displays which contain passive elements such as varistors or diodes (MIM=metal/insulator/metal).

MLC displays of this type are in particular suitable for TV applications (e.g. portable TVs) or for highly informative displays in automobile and aircraft construction. In addition to problems regarding the angle dependency of the contrast and the switching times, difficulties in MLC displays arise from the insufficient resistivity of the liquid crystal mixtures [TOGASHI, S., SEKIGUCHI, K., TANABE, H., YAMAMOTO, E., SORIMACHI, K., TAJIMA, E., WATANABE, H., SHIMIZU, H., Proc. Eurodisplay 84, Sept. 1984: A 210-288 Matrix LCD Controlled by Double Stage Diode Rings, p. 141 ff, Paris; STROMER, M., Proc. Eurodisplay 84, Sept. 1984: Design of Thin Film Transistors for Matrix Addressing of Television Liquid Crystal Displays, p. 145 ff, Paris]. With decreasing resistivity, the contrast of an MLC display deteriorates. Since the resistivity of the liquid crystal mixture usually decreases by interaction with the inside surfaces of the displays over the lifetime of an MLC display, a high (initial) resistance is very important for achieving acceptable service lives.

Therefore, there is still a high demand for MLC displays which have very high resistivity in combination with a large range of operating temperatures, short switching times and low threshold voltage.

The object of the invention is to provide MLC displays which do not or only to a small extent have the above disadvantages and, at the same time, have very high resistivities.

It has now been found that this object can be achieved by using nematic liquid crystal mixtures in these display elements, which mixtures are based on the abovementioned components A, B and C, B and C, or B.

Accordingly, the invention relates to an MLC display containing

two plane parallel support plates which together with a frame form a cell, integrated non-linear elements for switching individual picture elements on the support plates and a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity, the liquid crystal mixture being based on the following components: a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR2## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms, the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene, Z.sup.1 and Z.sup.2 are each, independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond, and m is 0, 1 or 2, and c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5, and the nematic liquid crystal mixture having a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of 30 mPa.s and a mean dielectricity constant .epsilon..ltoreq.8.

The invention also relates to the corresponding liquid crystal mixtures, in particular for use in MLC displays. However, the mixtures are also suitable for many other applications, such as, for example, TN, STN or OMI.

Nematic liquid crystal mixtures which instead of the compounds of the formula I contain analogous compounds in which one of the radicals R.sup.1 and R.sup.2 is n-alkyl and the other is n-alkoxy are known and commercially utilized in various designs. However, these liquid crystal mixtures are distinguished by values for the resistivity which are too low and are often between 5.times.10.sup.9 and 1.1.times.10.sup.11 .OMEGA.cm or less at 20.degree.. The corresponding MLC displays have values for the resistivity which are too low for some commercial applications.

The resistivity of liquid crystal mixtures is in general high, if the dielectric anisotropy is small, since the polar components which are present in mixtures which have a high .DELTA..epsilon. have a stabilizing effect on ions and thus lead to high conductivity or low resistance. Surprisingly, it has now been found that the resistivity is particularly high, if the mean dielectricity constant .epsilon. [=1/3(2.epsilon..sub..perp. +.epsilon..sub.11)] is small and, at the same time, the dielectrically neutral (.DELTA..epsilon. from -1.5 to +1.5) components of the liquid crystal mixture do not contain any functional groups such as, for example, aromatically bound alkoxy or ester functions. The dielectrically positive (.DELTA..epsilon..gtoreq.1.5) components usually carry terminal cyano groups. However, in the mixtures according to the invention, it is preferred to use, in addition to compounds which have a terminal cyano, also those which have a terminal --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub. 5.

However, component B can also substantially consist only of nitrile-containing compounds, of which those compounds of the formulae IIa to IIf where X is CN are preferred. In this case, the liquid crystal mixture essentially consists of components A, B and C, or A and B.

Particular preference is given to liquid crystal mixtures which contain nitrile-containing and nitrile-free, fluorinated compounds, the latter preferably conforming to the formulae IIa to IIf in which X is F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5.

The ratio of nitrile-free to nitrile-containing compounds in component B is preferably >1:1, in particular >2:1. Particularly preferred ranges are 2.5:1 to 6:1.

However, very particular preference is given to liquid crystal mixtures whose component B essentially consists of nitrile-free, fluorinated compounds. Preferably, the abovementioned preferred compounds of the formulae IIa to IIf are used.

`Essentially` is understood to mean that the amount of further compounds in the corresponding component is .ltoreq.20%, in particular .ltoreq.10%.

Preference is also given to liquid crystal mixtures whose component B contains compounds whose end groups are chlorinated. Compounds of this type are known to one skilled in the art and preferably conform to the formulae IIa to IIf where X is Cl. In a particularly preferred embodiment, the mixtures contain one or more compounds of the formula IIa to IIf in which A.sup.2 --X or A.sup.3 --X is ##STR3## where X is CF.sub.3, --OCF.sub.3, --OCHF.sub.2 or Cl. Furthermore, component B can also contain tetranuclear compounds, for example in accordance with formulae IIc to IIf in which one of the rings A.sup.1 to A.sup.3 is present twice.

In a particularly preferred embodiment, the mixtures contain compounds which have a terminal nitrile and are present in component B in an amount from 0 to 50% by weight. Particular preference is given to mixtures which do not contain any compounds which have a terminal nitrile. Surprisingly, it has been found that groups such as --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5 have a considerably less stabilizing effect in the displays than --OCH.sub.3 or --OC.sub.2 H.sub.5. The same is true for aliphatically bound alkoxy (compounds of the formulae III and IV).

The mixtures according to the invention preferably have a resistivity of .ltoreq.10.sup.12 .OMEGA..times.cm, particularly preferably >10.sup.13 .OMEGA..times.cm, at 20.degree.. The mean .epsilon. is preferably .ltoreq.7, in particular .ltoreq.5.

The values of dielectric anisotropy of the individual compounds of components A to C are determined at 20.degree. by extrapolation from a polar mixture (containing 24% of p-trans-4-propylcyclohexylbenzonitrile, 36% of p-trans-4-pentylcyclohexylbenzonitrile, 25% of p-trans-4-heptylcyclohexylbenzonitrile and 15% of 4-cyano-4'-(trans-4-pentylcyclohexyl)biphenyl), if the compound to be determined contains a dipole along the longitudinal axis of the molecule, or from a neutral mixture (containing 22% of trans-1-p-ethylphenyl-4-propylcyclohexane, 20% of trans-1-p-methoxyphenyl-1-propylcyclohexane, 15% of trans-1-p-ethoxyphenyl-4-propylcyclohexane, 19% of 4-ethyl-4-(trans-4-propylcyclohexyl)biphenyl, 14% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)biphenyl, 5% of 4,4'-bis(trans-4-propylcyclohexyl)biphenyl and 5% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)biphenyl) in the case of neutral compounds.

The liquid crystal mixtures according to the invention make it possible to achieve a high value for the resistivity in combination with low viscosities, which allows to produce excellent MLC displays. The MLC displays according to the invention preferably operate in the first transmission minimum according to Gooch and Tarry [C. H. Gooch and H. A. Tarry, Electron. Lett. 10, 2-4, 1974; C. H. Gooch and H. A. Tarry, Appl. Phys., Vol. 8, 1575-1584, 1975], in which case in addition to particularly favourable electrooptical properties such as, for example, high steepness of the characteristic curve and low angle dependence of the contrast (German Patent Specification 3,022,818) in combination with the same threshold voltage as in an analogous display, a smaller dielectric anisotropy is sufficient in the second minimum. This makes it possible to achieve significantly higher resistivities in the first minimum, when the mixtures according to the invention are used.

The viscosity at 20.degree. C. is preferably .ltoreq.25 mPa.s. The nematic phase range is preferably at least 70.degree., in particular at least 80.degree.. Preferably, this range extends at least from -20.degree. to +70.degree..

The individual compounds of the formulae I to IV and their subformulae which can be used in the MLC displays according to the invention are either known or can be prepared analogously to known compounds.

Preferred liquid crystal mixtures to be used according to the invention contain a total of, preferably, 10% to 90%, in particular 20% to 90%, of compounds of the formula I. If component B is not composed predominantly of strongly dielectrically positive nitrile components but predominantly only of weakly dielectrically positive compounds such as, for example, the fluorinated compounds mentioned below, component A can under certain circumstances be omitted entirely, and the mixtures according to the invention can in this special embodiment be solely based on component B and, if desired, component C. Particular preference is given to liquid crystal mixtures whose component B contains one or more compounds selected from the group consisting of compounds of the formulae IIa to IIf ##STR4## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is cyano, --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2 , --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and the rings A.sup.1, A.sup. 2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene.

Preferably, component B contains compounds of the formulae IIa to IIf in which X is cyano and compounds of the formulae IIa to IIf in which X is --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and the amount of cyano compounds in component B is 0 to 50% by weight.

In a particularly preferred embodiment, component B does not contain any compounds of the formulae IIa to IIf in which X is cyano.

In the compounds of the partial formulae IIa to IIf, X is preferably F, Cl, CF.sub.3, --OCF.sub.3, --OCHF.sub.2 or --CHF.sub.2.

The rings A.sup.1, A.sup.2 and A.sup.3 are each preferably, independently of one another, trans-1,4-cyclohexylene or 1,4-phenylene. In a preferred embodiment, one of the rings A.sup.1, A.sup.2 and A.sup.3 is 2- or 3-fluoro-1,4-phenylene or 2,3-difluoro-1,4-phenylene. The ring bound to X (i.e. A.sup.2 in IIa and IIb and A.sup.3 in IIc to IIf) is preferably 1,4-phenylene which is unsubstituted or even mono- or di-substituted by fluorine. A.sub.2 --X and A.sup.3 --X are preferably a group selected from the formulae (a) to (h): ##STR5## of which (a) , (b), (d), (f), (g) and (h) are particularly preferred.

Particularly preferred smaller groups of compounds are listed below: ##STR6##

In the partial formulae IIa1 to IIf3, R is in each case n-alkyl or n-alkenyl of up to 9 carbon atoms. Y and Z are each, independently of one another, H or F although one or two of the radicals Y and Z is preferably fluorine. However, X is preferably F, Cl, --CF.sub.3 --, --OCF.sub.3 or --OCHF.sub.2.

Component B preferably represents 10% to 100%, in particular 20% to 80%, of the mixtures according to the invention.

Component A preferably contains one or more compounds selected from the group consisting of II1 to II7: ##STR7## in which R.sup.1 and R.sup.2 have the meaning given in claim 1.

Preferably, component A additionally contains one or more compounds selected from the group consisting of II8 to II20: ##STR8## in which R.sup.1 and R.sup.2 have the meaning given in claim 1 and the 1,4-phenylene groups in II8 to II17 can each, independently of one another, also be mono- or polysubstituted by fluorine.

Furthermore, component A preferably additionally contains one or more compounds selected from the group consisting of II21 to II25: ##STR9## in which R.sup.1 and R.sup.2 have the meaning given in claim 1 and the 1,4-phenylene groups in II21 to II25 can each, independently of one another, also be mono- or polysubstituted by fluorine.

Finally, those mixtures are preferred whose component A contains one or more compounds selected from the group consisting of II26 and II27: ##STR10## in which C.sub.r H.sub.2r+1 is a straight-chain alkyl group of up to 7 carbon atoms.

In some cases, the addition of compounds of the formula ##STR11## in which R.sup.1 and R.sup.2 have the meaning given in claim 1

and Z.sup.0 is a single bond, --CH.sub.2 CH.sub.2 --, ##STR12## or proves to be advantageous for suppressing smectic phases, although the resistivity is thereby lowered. Whether and in which amount these compounds should be added for achieving optimum parameter combinations for practical application can easily be determined by one skilled in the art. Usually, less than 15%, in particular 5-10%, are used.

Further preference is given to liquid crystal mixtures which, in addition to components A, B and C, additionally contain one or more compounds selected from the group consisting of III and IV: ##STR13## in which R.sup.1 and R.sup.2 have the abovementioned meaning and/or one or more compounds selected from the group consisting of V and VI ##STR14## in which R.sup.1 and R.sup.2 have the abovementioned meaning and/or one or more compounds selected from the group consisting of VII to XI ##STR15## in which R.sup.1 and R.sup.2 have the abovementioned meaning and s is 0 or 1.

The amounts of the compounds of the formulae III to XI in the mixtures according to the invention (preferred ranges) can be seen from the table below:

Sum of compounds III and IV: 0% to 40%, preferably 10% to 30% Sum of compounds V and VI: 0% to 40%, preferably 5% to 20% Sum of compounds VII to XI: 0% to 20%, preferably 5% to 15%

It goes without saying that the mixtures according to the invention, which preferably consist essentially of the compounds mentioned as preferred for components A to C, may additionally also contain further compounds not mentioned here explicitly. However, this leads in many cases to more unfavourable properties. One skilled in the art can easily determine whether and in which amounts further compounds can be used.

The design of the MLC display according to the invention which consists of polarizers, electrode base plates and electrodes which have been subjected to surface treatment is that which is customary for this type of display. The definition of customary design is in this case very broad and also comprises all modifications and alterations of the MLC display, in particular also matrix display elements based on poly-Si TFT or MIM.

However, a significant difference between the displays according to the invention and those which have been customary so far and are based on the twisted nematic cell is the selection of the liquid crystal parameters of the liquid crystal layer.

The preparation of the liquid crystal mixtures to be used according to the invention is carried out in the usual manner. As a rule, the desired amount of the components used in a minor amount is dissolved in the components which constitute the major component, advantageously at elevated temperature. It is also possible to mix solutions of the components in an organic solvent, for example in acetone, chloroform or methanol, and remove the solvent again after the mixing, for example by distillation.

The dielectrics can also contain further additives known to one skilled in the art and described in the literature. For example, 0-15% pleochroic colorants or chiral doping substances can be added.

The examples which follow are intended to illustrate the invention without limiting it. Hereinbefore and hereinafter all temperatures are given in .degree.C. The percentages are by weight.

EXAMPLE 1

A matrix liquid crystal display of the TFT type containing a nematic liquid crystal mixture consisting of

17% of p-trans-4-propylcyclohexylbenzonitrile, 13% of p-trans-4-butylcyclohexylbenzonitrile, 22% of trans-1-p-propylphenyl-4-pentylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 9% of E-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a resistivity of 3.times.10.sup.12 .OMEGA.cm. The nematic mixture has a clear point of 91.degree., a viscosity of 18 mPa.s at 20.degree., a mean DC of 5.0 and an optical anisotropy of 0.118.

EXAMPLE 2

A nematic mixture consisting of

7% of p-trans-4-propylcyclohexylbenzonitrile, 13% of p-trans-4-butylcyclohexylbenzonitrile, 13% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 13% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 7% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 7% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 93.degree., a viscosity of 19 mPa.s, a mean DC of 5.4, a .DELTA.n of 0,107 and a resistivity of 2.5.times.10.sup.12 .OMEGA.cm.

EXAMPLE 3

A nematic mixture consisting of

10% of p-trans-4-pentylcyclohexyl-fluorobenzene, 17% of trans-1-p-propylphenyl-4-pentylcyclohexane, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, 10% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(3,4-difluorophenyl)-ethane, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(3,4-difluorophenyl)-ethane, 20% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, 20% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, and 3% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 88.degree., a viscosity of 15.2 mPa.s, a mean DC of 4.3, a .DELTA.n of 0.078 and a resistivity of 8.6.times.10.sup.13 .OMEGA.cm. This mixture is particularly suitable for operation in the first minimum according to Gooch and Tarry at a threshold voltage of 2.7 V.

EXAMPLE 4

A nematic mixture consisting of

4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 10% of p-trans-4-pentylcyclohexyl-fluorobenzene, 12% of trans-1-p-propylphenyl-4-pentylcyclohexane, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, 10% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(3,4-difluorophenyl)-ethane, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(3,4-difluorophenyl-ethane, 20% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, 20% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, and 4% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 91.degree., a .DELTA.n of 0.076, a mean DC of 4.2 and a resistivity of 7.3.times.10.sup.13 .OMEGA.cm.

EXAMPLE 5

A nematic mixture consisting of

13% of p-trans-4-propylcyclohexylbenzonitrile, 8% of p-trans-4-butylcyclohexylbenzonitrile, 15% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 17% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 8% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 96.degree., a .DELTA.n of 0.103, a mean DC of 4.9 and a resistivity of 1.0.times.10.sup.13 .OMEGA.cm. This mixture is particularly suitable for operation in the first minimum according to Gooch and Tarry at a threshold voltage of 2.3 V.

EXAMPLE 6

A nematic mixture consisting of

13% of p-trans-4-propylcyclohexylbenzonitrile, 13% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 15% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 12% of trans,trans-4-pentyl-4'-(2-fluoroethyl)-cyclohexylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 8% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 99.degree., a .DELTA.n of 0,097, a mean DC of 4.1 and a resistivity of 7.8.times.10.sup.13 .OMEGA.cm. This mixture is particularly suitable for operation in the first minimum according to Gooch and Tarry at a threshold voltage of 2.9 V.

EXAMPLE 7

A nematic mixture consisting of

16% of p-trans-4-propylcyclohexylbenzonitrile, 13% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 13% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 11% of trans,trans-4-pentyl-4'-(2-fluoroethyl)-cyclohexylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 8% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 99.5.degree., a .DELTA.n of 0.100, a mean DC of 4.2 and a resistivity of 7.5.times.10.sup.13 .OMEGA.cm. This mixture is particularly suitable for operation in the first minimum according to Gooch and Tarry at a threshold voltage of 2.7 V.

EXAMPLE 8

A nematic mixture consisting of

17% of p-trans-4-propylcyclohexylbenzonitrile, 13% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 13% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 9% of trans-1-p-propylphenyl -4-pentylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 9% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of-4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 93.4.degree., a .DELTA.n of 0.108, a mean DC of 4.4 and a resistivity of 1.3.times.10.sup.13 .OMEGA.cm. The viscosity at 20.degree. is 18.4 mPa.s.

EXAMPLE 9

A nematic mixture consisting of

17% of p-trans-4-propylcyclohexylbenzonitrile, 13% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 13% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 11% of trans-1-p-propylphenyl-4-pentylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 8% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 8% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 89.8.degree., a .DELTA.n of 0.102, a mean DC of 4.4, a resistivity of 1.5.times.10.sup.13 .OMEGA.cm and a viscosity of 18.1 mPa.s.

EXAMPLE 10

A nematic mixture consisting of

8% of p-trans-4-propylcyclohexyl-fluorobenzene, 7% of p-trans-4-pentylcyclohexyl-fluorobenzene, 8% of p-trans-4-hexylcyclohexyl-fluorobenzene, 7% of p-trans-4-heptylcyclohexyl-fluorobenzene, 5% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(2,3',4'-trifluorobiphenyl-4-yl)-ethane, 5% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(2,3',4'-trifluorobiphenyl-4-yl)-ethane, 8% of trans,trans-1-(p-ethylphenyl)-4-propyl-cyclohexylcyclohexane, 7% of trans,trans-1-(p-propylphenyl)-4-pentyl-cyclohexylcyclohexane, 8% of trans,trans-1-(p-fluorophenyl)-4-propyl-cyclohexylcyclohexane, 7% of trans,trans-1-(p-fluorophenyl)-4-pentyl-cyclohexylcyclohexane, 6% of trans,trans-1-(p-trifluoromethoxyphenyl)-4-propyl-cyclohexylcyclohexane, 4% of trans,trans-1-(p-trifluoromethoxyphenyl)-4-pentyl-cyclohexylcyclohexane, 6% of trans,trans-1-[p-(1,1,2,2-tetrafluoroethoxy)phenyl]-4-propyl -cyclohexylcyclohexane, 4% of trans,trans-1-[p-(1,1,2,2-tetrafluoroethoxy)phenyl]-4-pentyl -cyclohexylcyclohexane, 3% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 3% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl and 4% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 92.degree., a .DELTA.n of 0.099, a mean DC of 4.1, a resistivity of 5.4.times.10.sup.13 .OMEGA.cm and a viscosity of only 14 mPa.s.

EXAMPLE 11

A nematic mixture consisting of

10% of p-trans-4-propylcyclohexylbenzonitrile, 22% of trans-1-p-propylphenyl-4-pentylcyclohexane, 5% of 4,4'-bis-propylbiphenyl, 5% of trans,trans-4-propyl-4'-methyl-cyclohexylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 5% of 1,4-bis-(trans-4-propylcyclohexyl)-benzene, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 9% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 5% of 1-(trans-4-propylcyclohexyl)-2-(4'-ethyl-2'-fluorobiphenyl-4-yl)-ethane, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 95.degree., a viscosity of 16 mPa.s, a .DELTA.n of 0.113, a mean DC of 3.8 and a resistivity of 7.times.10.sup.13 .OMEGA.cm.

EXAMPLE 12

A nematic mixture consisting of

17% of p-trans-4-propylcyclohexylbenzonitrile, 11% of trans-1-p-propylphenyl-4-pentylcyclohexane, 13% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 13% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 8% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 8% of E [sic]-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 90.degree., a viscosity of 18 mPa.s and a .DELTA.n of 0.102.

EXAMPLE 13

A nematic mixture consisting of

14% of p-trans-4-propylcyclohexylbenzonitrile, 14% of trans-1-p-fluorophenyl-4-pentylcyclohexane, 14% of trans-1-p-fluorophenyl-4-heptylcyclohexane, 10% of trans-1-p-propylphenyl-4-pentylcyclohexane, 6% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-fluorophenyl)-ethane, 6% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-fluorophenyl)-ethane, 5% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, 5% of 4,4'-bis-(trans-4-propylcyclohexyl)-biphenyl, 5% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 5% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, 5% of 4,4'-bis-(trans-4-pentylcyclohexyl)-biphenyl, 5% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-biphenyl and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 95.degree., a viscosity of 17 mPa.s and a .DELTA.n of 0.105.

The following mixtures are very suitable for MLC displays:

EXAMPLE 14

A nematic mixture is prepared which consists of:

10% of 1-(trans-4-pentylcyclohexyl)-2-(4'-fluorobiphenyl-4-yl)-ethane, 17% of trans-1-p-propylphenyl -4-pentylcyclohexane, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, 10% of 1-(trans-4-pentylcyclohexyl)-2-[trans-4-(3,4-difluorophenyl)-cyclohexyl]-ethane, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(3,4-difluorophenyl)-ethane, 20% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, 20% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, and 3% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl.

EXAMPLE 15

A nematic mixture is prepared which consists of:

4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 10% of p-trans-4-pentylcyclohexyl-fluorobenzene, 12% of trans,trans-4-propyl-4'-methoxymethyl-cyclohexylcyclohexane, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, 10% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(3,4-difluorophenyl)-ethane, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(3,4-difluorophenyl)-ethane, 20% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, 20% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, and 4% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl.

EXAMPLE 16

A nematic mixture is prepared which consists of:

13% of 1-(trans-4-propylcyclohexyl)-2-(p-cyanophenyl)-ethane, 8% of p-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-benzonitrile, 18% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 17% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 4% of 1-(trans-4-propylcyclohexyl)-2-(trans-4-pentylcyclohexyl)-ethane, 4% of 1-[P-(trans-4-propylcyclohexyl-phenyl]-2-(trans-4-pentylcyclohexyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 8% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl.

EXAMPLE 17

A nematic mixture is prepared which consists of:

13% of p-trans-4-propylcyclohexylbenzonitrile, 13% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 15% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 12% of 1-(trans-4-pentylcyclohexyl)-4-propylcyclohex-1-ene, 4% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-4-propylcyclohex-1-ene, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 8% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl.

EXAMPLE 18

A nematic mixture is prepared which consists of:

16% of p-trans-4-propylcyclohexylbenzonitrile, 13% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 13% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 11% of trans,trans-4-pentyl-4'-(2-fluoroethyl)-cyclohexylcyclohexane, 4% of 1-(trans-4-propylcyclohexyl)-2-(4-pentylbiphenyl-4'-yl)-ethane, 4% of 1-[p-(trans-4-pentylcyclohexyl)-phenyl]-2-(p-propylphenyl)-ethane, 4% of 1-(trans-4-pentylcyclohexyl)-2-[trans-4-(p-propylphenyl)-cyclohexyl]-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 8% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl.

EXAMPLE 19

A nematic mixture is prepared which consists of:

17% of p-trans-4-propylcyclohexylbenzonitrile, 13% of trans,trans-4-pentyl-4'-ethoxy-cyclohexylcyclohexane, 13% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 9% of trans-1-p-propylphenyl -4-pentylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 9% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl.

EXAMPLE 20

A nematic mixture is prepared which consists of:

17% of p-trans-4-propylcyclohexylbenzonitrile, 13% of trans,trans-4-pentyl-4'-methoxy-cyclohexylcyclohexane, 13% of trans,trans-4-propyl-4'-propoxy-cyclohexylcyclohexane, 11% of trans-1-p-propylphenyl-4-pentylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 8% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 8% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl.

EXAMPLE 21

A nematic liquid crystal mixture is prepared which consists of:

17% of p-trans-4-propylcyclohexylbenzonitrile, 13% of p-trans-4-butylcyclohexylbenzonitrile, 22% of trans-1-p-propylphenyl-4-pentylcyclohexane, 4% of 1-(trans-4-propylcyclohexyl)-2-(4-ethyl-2,3-difluorobiphenyl-4'-yl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 9% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 9% of 4-ethyl -4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl.

EXAMPLE 22

A nematic mixture is prepared which consists of:

15% of p-trans-4-propylcyclohexylbenzonitrile, 11% of p-trans-4-butylcyclohexylbenzonitrile, 11% of trans,trans-4-pentyl-4'-fluoromethyl-cyclohexylcyclohexane, 11% of trans,trans-4-propyl-4'-fluoromethyl-cyclohexylcyclohexane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-methylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-ethylphenyl)-ethane 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 4% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-pentylphenyl)-ethane, 4% of 2-p-fluorophenyl-5-hexylpyrimidine, 4% of 2-p-fluorophenyl-5-pentylpyridine, 7% of 4-ethyl-4'-(trans-4-propylcyclohexyl)-biphenyl, 7% of 4-ethyl-4'-(trans-4-pentylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, and 6% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl.

EXAMPLE 23

A nematic mixture consisting of:

14% of p-trans-4-propylcyclohexylbenzonitrile, 10% of p-trans-4-pentylcyclohexyl-fluorobenzene, 10% of p-trans-4-heptylcyclohexyl-fluorobenzene, 20% of p-trans-4-pentylcyclohexyl-difluoromethoxybenzene, 6% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-fluorophenyl)-ethane, 6% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-fluorophenyl)-ethane, 5% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-propylphenyl)-ethane, 5% of 4,4'-bis-(trans-4-propylcyclohexyl)-biphenyl, 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-biphenyl, 5% of 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl, 5% of 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl, 5% 5% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-biphenyl, and 5% of 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-2-fluorobiphenyl has a clear point of 93.degree., a viscosity of 17 mPa.s, a .DELTA.n of 0.105 and a high resistivity.

EXAMPLE 24

A nematic mixture consisting of

10% of p-trans-4-pentylcyclohexyl-fluorobenzene, 10% of p-trans-4-hexylcyclohexyl-fluorobenzene, 10% of p-trans-4-heptylcyclohexyl-fluorobenzene, 20% of p-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-trifluoromethoxybenzene, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, 20% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, and 10% of 4-trifluoromethoxy-4'-(trans-4-pentylcyclohexyl)-biphenyl has a clear point of 80.degree., a .DELTA.n of 0.079, a threshold voltage V.sub.(10/0/20) of 2.27 volt and a very low viscosity.

EXAMPLE 25

A nematic mixture consisting of

25% of p-trans-4-propylcyclohexyl-trifluoromethoxybenzene, 20% of 4-trifluoromethoxy-4'-(trans-4-pentylcyclohexyl)-biphenyl, 15% of p-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-trifluoromethoxybenzene, 20% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, and 20% of 1-[trans-4-(trans-4-pentylcyclohexyl-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane has a clear point of 54.degree., a .DELTA.n of 0.088, a threshold voltage V.sub.(10/0/20) of 2.18 volt and a very low viscosity.

EXAMPLE 26

A nematic mixture consisting of

10% of p-trans-4-pentylcyclohexyl-fluorobenzene, 10% of p-trans-4-hexylcyclohexyl-fluorobenzene, 12% of p-trans-4-hexylcyclohexyl-difluoromethoxybenzene, 10% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-fluorophenyl)-ethane, 11% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-fluorophenyl)-ethane, 11% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, 11% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p- trifluoromethoxyphenyl)-ethane, 11% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, 10% of p-[trans-4-(trans-4-propylcyclohexyl]-trifluoromethoxybenzene and 4% of 4,4'-bis-(trans-4-pentylcyclohexyl)-biphenyl has a clear point of 87.degree., a .DELTA.n of 0.0798; a dielectric anisotropy of +6.5, a threshold voltage of V.sub.(10/0/20) of 2.25 volt and a very low viscosity.

EXAMPLE 27

A nematic mixture consisting of

10% of p-trans-4-propylcyclohexyl-trifluoromethoxybenzene, 10% of p-trans-4-propylcyclohexyl-difluoromethoxybenzene, 10% of 1-[trans-4-(trans-4-pentylcylcohexyl)[sic]-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, 10% of 1-[trans-4-(trans-4-propylcylcohexyl)[sic]-cyclohexyl]-2-(p-fluorophenyl)-ethane, 10% of 1-[trans-4-(trans-4-pentylcylcohexyl)[sic]-cyclohexyl]-2-(p-fluorophenyl)-ethane, 10% of 1-[trans-4-(trans-4-propylcylcohexyl)[sic]-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, 15% of 1-[trans-4-(trans-4-pentylcylcohexyl)[sic]-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, 10% of 1-[trans-4-(trans-4-propylcylcohexyl)[sic]-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, 10% of p-[trans-4-(trans-4-pentylcylcohexyl)[sic]-cyclohexyl]-trifluoromethoxybenzene and 5% of 4-trifluoromethoxy-4'-(trans-4-pentylcyclohexyl)-biphenyl has a clear point of 81.degree., a .DELTA.n of 0.0795, a threshold voltage V.sub.(10/0/20) of 2.47 volt and a very low viscosity.

EXAMPLE 28

A nematic mixture consisting of

10% of p-trans-4-propylcyclohexyl-trifluoromethoxybenzene, 25% of p-trans-4-pentylcyclohexyl-difluoromethoxybenzene, 15% of p-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-trifluoromethoxybenzene, 15% of-1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, 15% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane, and 20% of 4-trifluoromethoxy-4'-trans-4-pentylcyclohexylbiphenyl has a clear point of 71.degree., a .DELTA.n of 0.0878, a .DELTA..epsilon. of +6.1, a threshold voltage V.sub.(10/0/20) of 2.09 volt and a viscosity of 12 mPa.s at 20 .degree. C.

EXAMPLE 29

A nematic mixture consisting of

10% of p-trans-4-pentylcyclohexyl-fluorobenzene, 15% of p-trans-4-hexylcyclohexyl-fluorobenzene, 15% of p-trans-4-heptylcylcohexyl[sic]-fluorobenzene, 20% of p-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-trifluoromethoxybenzene, 20% of 1-[trans-4-(trans-4-propylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, and 20% of 1-[trans-4-(trans-4-pentylcyclohexyl)-cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane, has a clear point of 65.degree., a viscosity of 11 mPa.s at 20.degree., a .DELTA.n of 0.074, a .DELTA..epsilon. of +5.6 and a threshold voltage V.sub.(10/0/20) of 2.06 volt.

The composition of the mixtures of Examples 30 to 58 is given below, the individual compounds being coded as follows:

PCH-301: trans-1-p-methoxyphenyl-4-propylcyclohexane CCH-301: trans,trans-4-methoxy-4'-propylcyclohexylcyclohexane CBC-33F: 4,4'-bis-(trans-4-propylcyclohexyl)-2-fluorobiphenyl CBE-55F: 4,4'-bis-(trans-4-pentylcyclohexyl)-2-fluorobiphenyl CBC-53F: 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclcohexyl)[sic]-2-fluorobiphenyl CBC-33: 4,4'-bis-(trans-4-propylcyclohexyl)-biphenyl CBC-55: 4,4'-bis-(trans-4-pentylcyclohexyl)-biphenyl CBC-53: 4-(trans-4-pentylcyclohexyl)-4'-(trans-4-propylcyclohexyl)-biphenyl ECCP-33: 1-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-2-(p-propylphenyl)-ethane CCH-51F: trans,trans-4-fluoromethyl-4'-pentylcyclohexylcyclohexane CCH-31F: trans,trans-4-fluoromethyl-4'-propylcyclohexylcyclohexane PTP -102: 4-methyl-4'-ethoxy-tolan PTP -201: 4-methoxy-4'-ethyl-tolan CPTP-301: 4-(trans-4-propylcyclohexyl)-4'-methoxy-tolan CPTP-302: 4-(trans-4-propylcyclohexyl)-4'-ethoxy-tolan CPTP-303: 4-(trans-4-propylcyclohexyl)-4'-propoxy-tolan PCH-5F: trans-1-p-fluorophenyl-4-pentylcyclohexane PCH-6F: trans-1-p-fluorophenyl-4-hexylcyclohexane PCH-7F: trans-1-p-fluorophenyl-4-heptylcyclohexane EPCH-20CF.sub.2 : 1-(trans-4-ethylcyclohexyl)-2-(p-trifluoromethoxyphenyl)-ethane EPCH-30CF.sub.2 : 1-(trans-4-propylcyclohexyl)-2-(p-trifluoromethoxyphenyl)-ethane EPCH-50CF.sub.3 : 1-(trans-4-pentylcyclohexyl)-2-(p-trifluoromethoxyphenyl)-ethane EPCH-70CF.sub.3 : 1-(trans-4-heptylcyclohexyl)-2-(p-trifluoromethoxyphenyl)-ethane PCH-30CF.sub.3 : trans-1-p-trifluoromethoxyphenyl-4-propylcyclohexane PCH-50CF.sub.3 : trans-1-p-trifluoromethoxyphenyl-4-pentylcyclohexane ECCP-30CF.sub.3 : 1-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane ECCP-50CF.sub.3 : 1-[trans-4-(trans-4-pentylcyclohexyl)cyclohexyl]-2-(p-trifluoromethoxyphenyl)-ethane CCP-20CF.sub.3 : p-[trans-4-(trans-4-ethylcyclohexyl)cyclohexyl]-trifluoromethoxybenzene CCP-30CF.sub.3 : p-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-trifluoromethoxybenzene CCP-40CF.sub.3 : p-[trans-4-(trans-4-butylcyclohexyl)cyclohexyl]-trifluoromethoxybenzene CCP-50CF.sub.3 : p-[trans-4-(trans-4-pentylcyclohexyl)cyclohexyl]-trifluoromethoxybenzene BCH-30CF.sub.3 : 4-trifluoromethoxy-4'-(trans-4-propylcyclohexyl)-biphenyl ECCP-3F.F: 1-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-2-(3,4-difluorophenyl)-ethane ECCP-5F.F: 1-[trans-4-(trans-4-pentylcyclohexyl)cyclohexyl]-2-(3,4-difluorophenyl)-ethane CCP-3F.F: 4-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-1,2-difluorobenzene CCP-5F.F: 4-[trans-4-(trans-4-pentylcyclohexyl)cyclohexyl]-1,2-difluorobenzene CCP-3F: 4-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl)-fluorobenzene ECCP-3F: 1-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-2-(p-fluorophenyl)-ethane ECCP-5F: 1-[trans-4-(trans-4-pentylcyclohexyl)cyclohexyl]-2-(p-fluorophenyl)-ethane CP-3F: p-fluorophenyl trans-4-(trans-4-propylcyclohexyl)-cyclohexanecarboxylate CP-5F: p-fluorophenyl trans-4-(trans-4-propylcyclohexyl)-cyclohexanecarboxylate PYP-5F: 2-p-fluorophenyl-5-pentylpyrimidine PYP-6F: 2-p-fluorophenyl-5-hexylpyrimidine PYP-7F: 2-p-fluorophenyl-5-heptylpyrimidine PYP-30CF.sub.3 : 2-p-trifluoromethoxyphenyl-5-propylpyrimidine PYP-50CF.sub.3 : 2-p-trifluoromethoxyphenyl-5-pentylpyrimidine PYP-70CF.sub.3 : 2-p-trifluoromethoxyphenyl-5-heptylpyrimidine PCH-3: p-trans-4-propylcyclohexyl-benzonitrile PCH-4: p-trans-4-butylcyclohexyl-benzonitrile PCH-5: p-trans-4-pentylcyclohexyl-benzonitrile ECCP-3: 1-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-2-(p-cyanophenyl)-ethane ECCP-3CF.sub.3 : 1-[trans-4-(trans-4-propylcyclohexyl)cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane ECCP-5CF.sub.3 : 1-[trans-4-(trans-4-pentylcyclohexyl)cyclohexyl]-2-(p-trifluoromethylphenyl)-ethane PYP-5N.F: 2-(3-fluoro-4-cyanophenyl)-5-pentylpyrimidine PYP-7N.F: 2-(3-fluoro-4-cyanophenyl)-5-heptylpyrimidine PCH-30CF.sub.2 : trans-1-p-difluoromethoxyphenyl-4-propylcyclohexane PCH-50CF.sub.2 : trans-1-p-difluoromethoxyphenyl-4-pentylcyclohexane PCH-30CF.sub.2 : trans-1-p-difluoromethoxyphenyl-4-propylcyclohexane PCH-53: trans-1-p-propylphenyl-4-pentylcyclohexane ______________________________________Example 30 Example 31PCH-301 10.00 PCH-3OCF.sub.2 9.00PCH-7F 4.00 PCH-4OCF.sub.2 8.00EPCH-3OCF.sub.3 9.00 PCH-5OCF.sub.2 9.00EPCH-7OCF.sub.3 5.00 CCH-301 7.00CCP-3OCF.sub.3 13.00 CCP-3OCF.sub.3 13.00CCP-5OCF.sub.3 12.00 CCP-5OCF.sub.3 12.00ECCP-30CF.sub.3 12.00 ECCP-3OCF.sub.3 8.00ECCP-5OCF.sub.3 8.00 ECCP-5OCF.sub.3 6.00ECCP-3F.F 12.00 ECCP-3F.F 9.00ECCP-3F 8.00 ECCP-3F 6.00CBC-33F 2.00 CBC-33F 5.00CBC-53F 3.00 CBC-53F 4.00CBC-55F 2.00 CBC-55F 4.00Example 32 Example 33CCH-301 7.00 PCH-5F 13.0PCH-5F 12.00 PCH-7F 10.0PCH-7F 9.00 CCP-3OCF.sub.3 13.0CCP-3OCF.sub.3 13.00 CCP-4OCF.sub.3 11.0CCP-5OCF.sub.3 12.00 CCP-5OCF.sub.3 12.0ECCP-3OCF.sub.3 11.00 ECCP-3OCF.sub.3 11.0ECCP-5OCF.sub.3 8.00 ECCP-5OCF.sub.3 8.0ECCP-3F.F 12.00 ECCP-3F.F 9.0ECCP-3F 7.00 ECCP-5F.F 6.0CBC-33F 3.00 CBC-33F 3.0CBC-53F 3.00 CBC-53F 2.0CBC-55F 3.00 CBC-55F 2.0Example 34 Example 35PCH-5F 11.0 PCH-5F 13.0PCH-6F 4.0 PCH-7F 10.0PCH-7F 10.0 CCP-2OCF.sub.3 10.0CCP-2OCF.sub.3 9.0 CCP-3OCF.sub.3 13.0CCP-3OCF.sub.3 13.0 CCP-4OCF.sub.3 7.0CCP-4OCF.sub.3 7.0 CCP-5OCF.sub.3 11.0CCP-5OCF.sub.3 11.0 ECCP-3OCF.sub.3 11.0ECCP-3OCF.sub.3 10.0 ECCP-3F.F 10.0ECCP-5OCF.sub.3 8.0 ECCP-3F 8.0ECCP-3F.F 8.0 CBC-33F 3.0CBC-33F 3.0 CBC-53F 2.0CBC-53F 3.0 CBC-SSF 2.0CBC-55F 3.0Example 36 Example 37PCH-5F 13.0 PCH-5F 13.0PCH-7F 10.0 PCH-7F 10.0CCP-2OCF.sub.3 10.0 CCP-2OCF.sub.3 10.0CCP-3OCF.sub.3 13.0 CCP-3OCF.sub.3 13.0CCP-4OCF.sub.3 7.0 CCP-4OCF.sub.3 7.0CCP-5OCF.sub.3 11.0 CCP-5OCF.sub.3 11.0ECCP-3OCF.sub.3 11.0 ECCP-3F.F 10.0ECCP-3F.F 10.0 ECCP-5F.F 8.0ECCP-5F.F 7.0 ECCP-3F 11.0CBC-33F 3.0 CBC-33F 3.0CBC-53F 3.0 CBC-53F 2.0CBC-55F 2.0 CBC-55F 2.0Example 38 Example 39PCH-5F 12.0 PCH-5F 12.0PCH-7F 10.0 PCH-6F 9.0CCP-2OCF.sub.3 11.0 PCH-7F 10.0CCP-3OCF.sub.3 13.0 CCP-2OCF.sub.3 11.0CCP-4OCF.sub.3 7.0 CCP-3OCF.sub.3 13.0CCP-5OCF.sub.3 12.0 CCP-4OCF.sub.3 5.0ECCP-3OCF.sub.3 9.0 CCP-5OCF.sub.3 12.0ECCP-3F.F 9.0 ECCP-3F.F 9.0ECCP-5F.F 5.0 ECCP-5F.F 5.0ECCP-3F 6.0 ECCP-3F 5.0CBC-33F 3.0 CBC-33F 3.0CBC-53F 2.0 CBC-53F 3.0 CBC-55F 3.0Example 40 Example 41PCH-5F 12.0 PCH-5F 10.0PCH-6F 8.0 PCH-6F 5.0PCH-7F 10.0 PCH-7F 7.0CCP-2OCF.sub.3 11.0 CCP-2OCF.sub.3 11.0CCP-3OCF.sub.3 13.0 CCP-3OCF.sub.3 13.0CCP-4OCF.sub.3 5.0 CCP-4OCF.sub.3 6.0CCP-5OCF.sub.3 12.0 CCP-5OCF.sub.3 11.0ECCP-3F.F 11.0 ECCP-3OCF.sub.3 7.0ECCP-5F.F 8.0 ECCP-5OCF.sub.3 3.0CBC-33F 4.0 ECCP-3F.F 9.0CBC-53F 3.0 ECCP-5F.F 4.0CBC-55F 3.0 ECCP-3F 7.0 CBC-33F 3.0 CBC-53F 2.0 CBC-55F 2.0Example 42 Example 43PCH-3 19.0 PCH-3 20.00PCH-7F 7.0 PCH-4 8.00CCP-2OCF.sub.3 11.0 PCH-5F 8.00CCP-3OCF.sub.3 13.0 PCH-6F 8.00CCP-4OCF.sub.3 6.0 PCH-7F 7.00CCP-5OCF.sub.3 12.0 ECCP-3F 7.00ECCP-3OCF.sub.3 7.0 ECCP-5F 7.00ECCP-3F.F 10.0 CP-3F 12.00ECCP-5F.F 8.0 CP-5F 12.00ECCP-3F 7.0 ECCP-3 11.00Example 44 Example 45PCH-3 20.00 PCH-3 14.00PCH-5F 9.00 PCH-5F 14.00PCH-6F 9.00 PCH-7F 14.00PCH-7F 9.00 PCH-53 10.00ECCP-3F 8.00 ECCP-3F 6.00ECCP-5F 8.00 ECCP-5F 6.00CP-3F 12.00 ECCP-3CF.sub.3 5.00CP-5F 12.00 CBC-33 5.00ECCP-3 13.00 CBC-53 5.00 CBC-55 5.00 CBC-33F 5.00 CBC-53F 6.00 CBC-55F 5.00 Example 46 Example 47PCH-5F 20.00 PCH-3 24.00PCH-6F 15.00 PCH-SF 9.00PCH-7F 15.00 PCH-7F 8.00ECCP-3F 10.00 ECCP-3F 8.00ECCP-5F 10.00 ECCP-SF 8.00CBC-33 5.00 ECCP-3OCF.sub.3 11.00CBC-53 5.00 ECCP-5OCF.sub.3 11.00CBC-55 5.00 ECCP-3CF.sub.3 11.00CBC-33F 5.00 ECCP-3 10.00CBC-53F 5.00CBC-55F 5.00Example 48 Example 49PCH-3 24.00 PCH-3 24.00PCH-5F 7.00 CCH-31F 7.00PCH-7F 6.00 CCH-51F 7.00CCH-31F 6.00 ECCP-3F 8.00ECCP-3F 5.00 ECCP-5F 8.00ECCP-5F 5.00 ECCP-3OCF.sub.3 11.00ECCP-3OCF.sub.3 11.00 ECCP-5OCF.sub.3 11.00ECCP-5OCF.sub.3 11.00 ECCP-3CF.sub.3 11.00ECCP-3CF.sub.3 11.00 ECCP-3 13.00ECCP-3 4.00CP-3F 5.00CP-5F 5.00Example 50 Example 51PYP-SN.F 5.00 PCH-5F 10.00PYP-7N.F 5.00 PCH-6F 12.00PCH-3 14.00 PCH-7F 12.00PCH-SF 5.00 ECCP-3F 14.00CCH-31F 7.00 ECCP-5F 14.00CCH-51F 7.00 CP-3F 15.00ECCP-3F 5.00 CP-5F 15.00ECCP-SF 5.00 ECCP-3 8.00ECCP-3OCF.sub.3 11.00ECCP-5OCF.sub.3 11.00ECCP-3CF.sub.3 11.00ECCP-3 4.00CP-3F 5.00CP-5F 5.00Example 52 Example 53PCE-5F 10.00 PCH-3 16.00PCH-6F 10.00 PCH-301 8.00PCH-7F 10.00 CCP-3OCF.sub.3 9.00ECCP-3F 13.00 CCP-5OCF.sub.3 8.00ECCP-5F 14.00 ECCP-3OCF.sub.3 8.00ECCP-3CF.sub.3 13.00 ECCP-5OCF.sub.3 7.00CP-3F 15.00 ECCP-3F.F 7.00CP-5F 15.00 ECCP-3F 6.00 ECCP-3CF.sub.3 7.00 BCH-3OCF.sub.3 7.00 PTP-102 4.00 PTP-201 4.00 CPTP-301 2.00 CPTP-302 2.00 CPTP-303 3.00Example 54 Example 55PCH-3 18.00 PCH-3 20.00PCH-301 8.00 PCH-301 10.00PYP-3F 5.00 PCH-3OCF.sub.2 5.60PYP-5OCF.sub.3 5.00 PCH-4OCF 5.60PYP-7OCF.sub.3 5.00 PCH-5OCF.sub.2 5.60CCP-3OCF.sub.3 9.00 CCP-3OCF.sub.3 7.00CCP-5OCF.sub.3 8.00 CCP-5OCF.sub.3 6.30ECCP-3OCF.sub.3 8.00 ECCP-3OCF.sub.3 6.30ECCP-SOCF.sub.3 7.00 ECCP-SOCF.sub.3 5.60ECCP-3F.F 5.00 ECCP-3F.F 5.60ECCP-3F 5.00 ECCP-3CF.sub.3 5.60BCH-3OCF.sub.3 7.00 BCH-3OCF.sub.3 7.00CPTP-301 3.00 CPTP-301 3.50CPTP-302 3.00 CPTP-302 2.80CPTP-303 4.00 CPTP-303 3.50Example 56 Example 57PCH-3 20.00 PCH-3 18.00PCH-301 10.00 PCH-5F 12.00PYP-3F 5.60 PCH-6F 12.00Pyp-5F 5.60 PCH-7F 10.00PYP-5OCF.sub.3 5.60 ECCP-3F 7.00PYP-7OCF.sub.3 5.60 ECCP-5F 7.00CCP-3OCF.sub.3 7.00 ECCP-33 5.00CCP-5OCF.sub.3 6.30 CBC-33 5.00ECCP-3OCF.sub.3 6.30 CBC-53 5.00ECCP-SOCF.sub.3 5.60 CBC-55 4.00ECCP-3F.F 5.60 CBC-33F 5.00ECCP-3CF.sub.3 5.60 CBC-53F 5.00CPTP-301 3.50 CBC-55F 5.00CPTP-302 3.50CPTP-303 4.20Example 58PCH-3 10.00PCH-5F 18.00PCH-6F 14.00PCH-7F 10.00ECCP-3F 9.00ECCP-5F 7.00CBC-33 5.00CBC-53 6.00CBC-55 5.00CBC-33F 5.00CBC-53F 6.00CBC-55F 5.00______________________________________

The properties of the mixtures from Examples 30 to 58 are listed in the table below:

__________________________________________________________________________ ExampleProperty 30 31 32 33 34 35 36 37 38__________________________________________________________________________Clear point [.degree.C.] 100 101 100 103 100 101 101 100 101Vicosity at 20.degree. 15 15 15 15 15(mPa.s).DELTA..epsilon. +4.0 +6.6 +5.9 +4.0 +4.6.epsilon..sub.11 7.0 6.8 7.5.DELTA.n 0.090 0.090 0.084 0.076 0.087 0.084 0.085 0.081 0.081V.sub.(10,0,20) [Volt] 2.44 2.40 2.57 2.52 2.27 2.29 2.20 2.26 2.27__________________________________________________________________________ ExampleProperty 39 40 41 42 43 44 45 46 47__________________________________________________________________________Clear point [.degree.C.] 88 90 102 98 82 84 95 89 87Vicosity at 20.degree. 14 14 15 17 18 18 17 15 16(mPa.s).DELTA..epsilon. +4.0 +4.0 +3.9 +8.0 +7.3 +4.6 +2.7 +8.7.epsilon..sub.11 6./ 7.0 6.6 11.9 11.0 7.6 12.1.DELTA.n 0.081 0.079 0.081 0.090 0.094 0.090 0.105 0.093 0.094V.sub.(10,0,20) [Volt] 2.13 2.20 2.33 1.90 1.71 1.75 2.15 2.98 1.82__________________________________________________________________________ ExampleProperty 48 49 50 51 52 53 54 55 56 57 58__________________________________________________________________________Clear point [.degree.C.] 84 101 85 94 94 106 91 81 73 95 94Vicosity at 20.degree. 16 20 19 17 17 17(mPa.s).DELTA..epsilon. +7.9 +8.3 +10.2 +6.9 +8.1 +6.5 +8.7 +5.2.epsilon..sub.11 11.5 11.8 14.2 10.4 11.8 10.8 12.8 8.4.DELTA.n 0.089 0.094 0.096 0.074 0.072 0.132 0.125 0.113 0.125 0.105 0.101V.sub.(10,0,20) [Volt] 1.86 1.98 1.56 2.42 2.58 2.51 2.12 2.15 1.85 2.03 2.223__________________________________________________________________________

Further mixtures according to the invention are listed below:

______________________________________Example 59 Example 60CCH-301 7.00 PCH-5F 13.0PCH-5F 12.00 PCH-7F 10.0PCH-7F 9.00 CCP-3OCF.sub.3 13.0CCP-3F.F 13.00 CCP-4OCF.sub.3 11.0CCP-5F.F 12.00 CCP-5OCF.sub.3 12.0ECCP-3OCF.sub.3 11.00 ECCP-3OCF.sub.3 11.0ECCP-5OCF.sub.3 8.00 ECCP-5OCF.sub.3 8.0ECCP-3F.F 12.00 CCP-3F.F 9.0ECCP-3F 7.00 CCP-SF.F 6.0CBC-33F 3.00 CBC-33F 3.0CBC-53F 3.00 CBC-53F 2.0CBC-55F 3.00 CBC-55F 2.0Example 61 Example 62PCH-5F 11.0 PCH-3 20.0PCH-6F 4.0 PCE-4 8.0PCH-7F 10.0 PCH-5 8.0CCP-2OCF.sub.3 9.0 PCH-6F 8.0CCP-3OCF.sub.3 13.0 PCH-7F 7.0CCP-4OCF.sub.3 7.0 CCP-3F.F 7.0CCP-5OCF.sub.3 11.0 CCP-5F.F 7.0CCP-3F.F 10.0 CP-3F 12.0CCP-5F.F 8.0 CCP-3F 12.0CCP-3F 8.0 ECCP-3 11.00CBC-33F 3.0CBC-53F 3.0CBC-55F 3.0Example 63 Example 64PCH-3 14.00 PCH-5F 20.00PCH-5F 14.00 PCH-6F 15.00PCH-7F 14.00 PCH-7F 15.00PCH-53 10.00 CCP-3F.F 10.00CCP-3F 6.00 CCP-5F.F 10.00CCP-5F 6.00 CBC-33 5.00CCP-3F.F 5.00 CBC-53 5.00CBC-33 5.00 CBC-55 5.00CBC-53 5.00 CBC-33F 5.00CBC-55 5.00 CBC-53F 5.00CBC-33F 5.00 CBC-S5F 5.00CBC-53F 6.00CBC-55F 5.00Example 65 Example 66PCH-3 16.00 PCH-3 18.00PCH-301 8.00 PCH-SF 12.00CCP-3OCF.sub.3 9.00 PCH-6F 12.00CCP-5OCF.sub.3 8.00 PCH-7F 10.00CCP-3F.F 8.00 CCP-3F.F 7.00CCP-5F.F 7.00 CCP-SF.F 7.00ECCP-3F.F 7.00 ECCP-33 5.00CCP-3F 6.00 CBC-33 5.00ECCP-3CF.sub.3 7.00 CBC-S3 5.00BCH-3OCF.sub.3 7.00 CBC-55 4.00PTP-102 4.00 CBC-33F 5.00PTP-201 4.00 CBC-53F 5.00CPTP-301 2.00 CBC-55F 5.00CPTP-302 2.00CPTP-303 3.00Example 67PCH-3 10.00PCH-5F 18.00PCH-6F 14.00PCH-7F 10.00CCP-3F.F 9.00CCP-5F.F 7.00CBC-33 5.00CBC-53 6.00CBC-55 5.00CBC-33F 5.00CBC-53F 6.00CBC-55F 5.00______________________________________Example 68______________________________________Composition:PCH-3 10.0 %PCH-SF 18.0 %PCH-6F 14.0 %PCH-7F 10.0 %ECCP-3F 9.0 %ECCP-5F 7.0 %CBC-33 5.0 %CBC-53 6.0 %CBC-55 5.0 %CBC-33F 5.0 %CBC-53F 6.0 %CBC-55F 5.0 %S .fwdarw. N <-20 .degree.C.Clearing point +94 .degree.C.Viscosity .nu. +20.degree. C. 16 mm.sup.2 s.sup. -1Dielectric anisotropy .DELTA..epsilon. 1 kHz, 20.degree. C. +4.1 .epsilon..sub..parallel. 1 kHz, 20.degree. C. 7.1 .epsilon..sub..perp. 1 kHz, 20.degree. C. 3.0Optical anisotropy .DELTA.n +0.1006(p0.degree. C., 589 nm) n.sub.e 1.5932 n.sub.o 1.4926______________________________________Example 69______________________________________Composition:PCH-3 18.0 %PCH-5F 12.0 %PCH-6F 12.0 %PCH-7F 10.0 %ECCP-3F 7.0 %ECCP-5F 7.0 %ECCP-33 5.0 %CBC-33 5.0 %CBC-53 5.0 %CBC-55 4.0 %CBC-33F 5.0 %CBC-53F 5.0 %CBC-55F 5.0 %S .fwdarw. N <-40 .degree.C.Clearing point +95 .degree.C.Viscosity .nu. +20.degree. C. 17 mm.sup.2 s.sup.-1Dielectric anisotropy .DELTA..epsilon. 1 kHz, 20.degree. C. +5.2 .epsilon..sub..parallel. 1 kHz, 20.degree. C. 8.4 .epsilon..sub..perp. 1 kHz, 20.degree. C. 3.2Optical anisotropy .DELTA.n +0.1050(.degree. C., 589 nm) n.sub.e 1.5981 n.sub.o 1.4931______________________________________Example 70______________________________________Composition:PCH-3 7.0 %PCH-5F 12.0 %PCH-6F 12.0 %PCH-7F 10.0 %ECCP-3F 7.0 %ECCP-5F 7.0 %PCH-53 8.0 %ECCP-33 5.0 %CBC-33 5.0 %CBC-53 6.0 %CBC-55 9.0 %CBC-33F 5.0 %CBC-53F 6.0 %CBC-55F 5.0 %S .fwdarw. N <-20 .degree.C.Clearing point +98 .degree.C.Viscosity .nu. +20.degree. C. 16 mm.sup.2 s.sup.-1Dielectric anisotropy .DELTA..epsilon. 1 kHz, 20.degree. C. +3.2 .epsilon..parallel. 1 kHz, 20.degree. C. 6.0 .epsilon..sub..perp. 1 kHz, 20.degree. C. 2.8Optical anisotropy .DELTA.n +0.1008(20.degree. C., 589 nm) n.sub.e 1.5942 n.sub.o 1.4934______________________________________Exemples 71 72______________________________________S .fwdarw. N [.degree.C.] <0 <0Clearing point +100 +101[.degree.C.]Viscosity 16 16[mm.sup.2 s.sup. -1 ] 20.degree. C..DELTA.n +0.086 +0.086(20.degree. C., 589 nm)n.sub.e 1.558 1.556(20.degree. C., 589 nm)V.sub.(10,0,20) 2.33 2.38V.sub.(50,0,20) 2.86 2.92V.sub.(20,0,20) 3.52 3.62Composition EPCH- 13.0 EPCH- 13.0[%]: 3OCF3 3OCF3 PCH-7F 10.0 EPCH- 10.0 6OCF3 CCP-2OCF3 10.0 CCP-2OCF3 10.0 CCP-3OCF3 13.0 CCP-30CF3 13.0 CCP-4OCF3 7.0 CCP-4OCF3 7.0 CCP-6OCF3 11.0 CCP-6OCF3 11.0 ECCP-3F.F 10.0 ECCP-3F.F 10.0 ECCP-3F.F 6.0 ECCP-3F.F 6.0 ECCP-3F 11.0 ECCP-3F 11.0 CBC-33F 3.0 CVC-33F 3.0 CBC-63F 2.0 CBC-63F 2.0 CBC-66F 2.0 CBC-66F 2.0______________________________________

The liquid crystal mixtures according to the invention can contain, in addition to component B and, where present, A and C, still further additives such as, for example, chiral doping substances, isotropic additives for modifying various parameters, pleochroic dyes and the like. Components A, B and C preferably comprise predominantly the compounds mentioned (that is, more than 50%, in particular more than 60%, of them). However, in a preferred manner, components A, B and C comprise the compounds mentioned (that is, more than 80%, in particular 100% of them).

Claims

1. Matrix liquid crystal display containing

two plane parallel support plates which together with a frame form a cell,

integrated non-linear elements for switching individual picture elements on the support plates and

a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity,

characterized in that the liquid crystal mixture is based on the following components:

(a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, ##STR16## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2-or 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR17## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms,

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

Z.sup.1 and Z.sup.2 are each, independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond,

and

m is 0, 1 or 2, and

c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5 selected from the compounds of the formulae VII to XI, ##STR18## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1,

and the nematic liquid crystal mixture has a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of 30 mPA.s and a mean dielectricity constant of .epsilon..ltoreq.8.

2. Display according to claim 1, characterized in that component A contains one or more compounds selected from the group consisting of II1 to II7: ##STR19## in which R.sup.1 and R.sup.2 have the meaning given in claim 1.

3. Display according to claim 2, characterized in that component A additionally contains one or more compounds selected from the group consisting of II8 to II20: ##STR20## in which R.sup.1 and R.sup.2 have the meaning given in claim 1 and the 1,4-phenylene groups in I8 to II17 can each, independently of one another, also be mono- or polysubstituted by fluorine.

4. Display according to claim 2, characterized in that component A additionally contains one or more compounds selected from the group consisting of II21 to II25: ##STR21## in which R.sup.1 and R.sup.2 have the meaning given in claim 1 and the 1,4-phenylene groups in II21 to II25 can each, independently of one another, also be mono- or polysubstituted by fluorine.

5. Display according to claim 1, characterized in that the liquid crystal mixture additionally contains, in addition to components A, B and C, one or more compounds selected from the group consisting of III and IV: ##STR22## in which R.sup.1 and R.sup.2 have the meanings given in claim 1.

6. Display according to claim 1, characterized in that the liquid crystal mixture additionally contains, in addition to components A, B and C, one or more compounds of the formula ##STR23## in which R.sup.1 and R.sup.2 have the meaning given in claim 1

and

Z.sup.0 is a single bond, --CH.sub.2 CH.sub.2 --, ##STR24##

7. Matrix liquid crystal display containing

two plane parallel support plates which together with a frame form a cell,

integrated non-linear elements for switching individual picture elements on the support plates and

a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity,

characterized in that the liquid crystal mixture is based on the following components:

(a) at least 10% by weight Of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, ##STR25## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is cyano, --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR26## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms,

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

Z.sup.1 and Z.sup.2 are each, independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond,

and

m is 0, 1 or 2, and

c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5, selected from the compounds of the formulae VII to XI, ##STR27## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1,

and the nematic liquid crystal mixture has a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of 30 mPA.s and a mean dielectricity constant of .epsilon..ltoreq.8, characterized in that component B consists essentially of nitrile-free, fluorinated compounds.

8. Matrix liquid crystal display containing

two plane parallel support plates which together with a frame form a cell,

integrated non-linear elements for switching individual picture elements on the support plates and

a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity,

characterized in that the liquid crystal mixture is based on the following components:

(a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, ##STR28## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is cyano, --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2-or 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR29## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms,

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

Z.sup.1 and Z.sup.2 are each, independently of one another, --CH.sub.2 CH.sub.2 --or a single bond,

and

m is 0, 1 or 2, and

c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5, selected from the compounds of the formulae VII to XI, ##STR30## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1,

and the nematic liquid crystal mixture has a nematic phase range of at least 60.degree. C., a maximum viscosity of 20.degree. C. of 30 mPA.s and a mean dielectricity constant of .epsilon..ltoreq.8, characterized in that component B contains compounds of the formulae IIa to IIf in which X is cyano and compounds of the formulae IIa to IIf in which X is --NCS, F, Cl, --CF.sub.3, --CHF.sub.3, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5 and the amount of cyano compounds in component B is 0 to 50% by weight.

9. Display according to claim 8, characterized in that component B does not contain any compounds of the formulae IIa to IIf in which X is cyano.

10. Matrix liquid crystal display containing

two plane parallel support platers which together with a frame form a cell,

integrated non-linear elements for switching individual picture elements on the support plates and

a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity,

characterized in that the liquid crystal mixture is based on the following components:

(a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, ##STR31## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is cyano, --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2-or 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR32## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms,

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

Z.sup.1 and Z.sup.2 are each, independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond,

and

m is 0, 1 or 2, and

c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5, selected from the compounds of the formulae VII to XI, ##STR33## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1,

and the nematic liquid crystal mixture has a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of 30 mPA.s and a mean dielectricity constant of .epsilon..ltoreq.8, characterized in that X is F, Cl, CF.sub.3, --OCF.sub.3, --OCHF.sub.2 or --CHF.sub.2.

11. Matrix liquid crystal display containing

two plane parallel support plates which together with a frame form a cell,

integrated non-linear elements for switching individual picture elements on the support plates and

a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity,

characterized in that the liquid crystal mixture is based on the following components:

(a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, ##STR34## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is cyano, --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and

the rings A.sup.1, A.sup.2 and A.sup.3 are each independently of one another, 1,4-phenylene, 2-or 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR35## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms,

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

Z.sup.1 and Z.sup.2 are each, independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond,

and

m is 0, 1 or 2, and

c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5, selected from the compounds of the formulae VII to XI, ##STR36## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1,

and the nematic liquid crystal mixture has a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of 30 mPA.s and a mean dielectricity constant of .epsilon..ltoreq.8, characterized in that component A contains one or more compounds selected from the group consisting of II26 and II27: ##STR37## in which C.sub.r H.sub.2r+1 is a straight-chain alkyl group of up to 7 carbon atoms.

12. Matrix liquid crystal display containing

two plane parallel support plates which together with a frame form a cell,

integrated non-linear elements for switching individual picture elements on the support plates and

a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity,

characterized in that the liquid crystal mixture is based on the following components:

(a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, ##STR38## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is cyano, --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and

the rings A.sup.1, A.sup.2 and A.sup.3 are each independently of one another, 1,4-phenylene, 2-or 3-fluoro, 1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR39## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms,

the rings A.sup.1, A.sup.2 and A.sup.3 are each independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

Z.sup.1 and Z.sup.2 are each independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond,

and

m is 0, 1 or 2, and

c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5, selected from the compounds of the formulae VII to XI, ##STR40## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1,

and the nematic liquid crystal mixture has a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of 30 mPA.s and a mean dielectricity constant of .epsilon..ltoreq.8, characterized in that the liquid crystal mixture additionally contains, in addition to compounds A, B and C, one or more compounds selected from the group consisting of V and VI: ##STR41## in which R.sup.1 and R.sup.2 have the meaning given above.

13. Matrix liquid crystal display containing

two plane parallel support plates which together with a frame form a cell,

integrated non-linear elements for switching individual picture elements on the support plates and

a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity,

characterized in that the liquid crystal mixture is based on the following components:

(a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, ##STR42## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is cyano, --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2-or 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR43## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms,

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

Z.sup.1 and Z.sup.2 are each, independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond,

and

m is 0, 1 or 2, and

c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5, selected from the compounds of the formulae VII to XI, ##STR44## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1,

and the nematic liquid crystal mixture has a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of 30 mPA.s and a mean dielectricity constant of .epsilon..ltoreq.8, characterized in that the liquid crystal mixture additionally contains, in addition to components A, B and C, one or more compounds selected from the group consisting of VII to XI: ##STR45## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1.

14. Matrix liquid crystal display containing

two plane parallel support plates which together with a frame form a cell,

integrated non-linear elements for switching individual picture elements on the support plates and

a nematic liquid crystal mixture which is present in the cell and has a positive dielectric anisotropy and high resistivity,

characterized in that the liquid crystal mixture is based on the following components:

(a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, ##STR46## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is cyano, --NCS, F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR47## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms,

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

Z.sup.1 and Z.sup.2 are each independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond,

and

m is 0, 1 or 2, and

c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5, selected from the compounds of the formulae VII to XI, ##STR48## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1,

and the nematic liquid crystal mixture has a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of 30 mPA.s and a mean dielectricity constant of .epsilon..ltoreq.8, which contains .ltoreq.20% of components of formulae IIa-IIf wherein X denotes nitrile and contains compounds which conforms to formulae IIa to IIf where X is --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5.

15. A nematic liquid crystal mixture which has a positive dielectric anisotropy and high resistivity,

characterized in that the liquid crystal mixture consists essentially of the following components:

(a) at least 10% by weight of a liquid-crystalline component B comprising one or more compounds having a dielectric anisotropy of more than +1.5, ##STR49## in which R is n-alkyl or n-alkenyl of up to 9 carbon atoms,

X is F, Cl, --CF.sub.3, --CHF.sub.2, --OCF.sub.3, --OCHF.sub.2, --OCF.sub.2 CF.sub.2 H or --OC.sub.2 F.sub.5, and

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2-or 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

b) up to 90% by weight of a liquid-crystalline component A comprising one or more compounds having a dielectric anisotropy of -1.5 to +1.5 of the general formula I ##STR50## in which R.sup.1 and R.sup.2 are each, independently of one another, n-alkyl, .omega.-fluoroalkyl or n-alkenyl having up to 9 carbon atoms,

the rings A.sup.1, A.sup.2 and A.sup.3 are each, independently of one another, 1,4-phenylene, 2- or 3-fluoro-1,4-phenylene, trans-1,4-cyclohexylene or 1,4-cyclohexenylene,

Z.sup.1 and Z.sup.2 are each, independently of one another, --CH.sub.2 CH.sub.2 -- or a single bond,

and

m is 0, 1 or 2, and

c) 0 to 20% by weight of a liquid-crystalline component C comprising one or more compounds having a dielectric anisotropy of less than -1.5 selected from the compounds of the formulae VII to XI, ##STR51## in which R.sup.1 and R.sup.2 have the meaning given above

and

s is 0 or 1,

and the nematic liquid crystal mixture has a nematic phase range of at least 60.degree. C., a maximum viscosity at 20.degree. C. of mPA.s and a mean dielectricity constant of .epsilon..ltoreq.8.