Means for applying conducting members to arc tubes

Information

  • Patent Grant
  • 6538377
  • Patent Number
    6,538,377
  • Date Filed
    Friday, November 3, 2000
    24 years ago
  • Date Issued
    Tuesday, March 25, 2003
    21 years ago
Abstract
An arc discharge lamp comprising an arc tube including a starting aid is described. The starting aid comprises at least one metal cermet coating applied to the surface of the arc tube, or a metal layer including refractory glass disposed over said cermet coating or said metal layer.
Description




BACKGROUND OF THE INVENTION




Field of the Invention




The present invention relates generally to lighting, and more specifically to an arc discharge lamp, such as a ceramic metal halide lamp. This invention relates particularly to a means for applying conducting members to high pressure arc discharge lamps, e.g. sodium (HPS) arc tubes.




Discharge lamps produce light by ionizing a fill such as a mixture of metal halides and mercury with an electric arc passing between two electrodes. The electrodes and the fill are sealed within a translucent or transparent discharge chamber which maintains the pressure of the energized fill material and allows the emitted light to pass through it. The fill, also known as a “dose” emits a desired spectral energy distribution in response to being excited by the electric arc. However, arc discharge lamps, particularly those of a high pressure variety are often difficult to start.




Presently known metallic starting aids for discharge lamps which are composed of tungsten metal reduce the required electrical breakdown voltage for starting. Unfortunately, they may not survive an air firing step used for cleaning ceramic arc tubes. Moreover, the tungsten oxidizes and becomes useless as a starting aid. A similar oxidation problem prevents application of metallic starting aids on arc tubes intended for open air operation, such as ceramic or quartz mercury arc tubes for light projectors. Another problem with existing metallic starting aids is that tungsten is relatively expensive. Lower cost metals have higher vapor pressure, which, in the vacuum established within the outer envelope of HPS lamps, would evaporate to produce bulb darkening and lumen depreciation.




Previous HPS starting aids have been designed in the form of a wire or coiled ignition filament. The starting aid is positioned in contact with the outer surface of the arc tube and is connected to one electrical power lead of the lamp. When an arc is formed and the lamp begins to warm up, the electrical connection is either removed from the starting aid, or the starting aid is moved away from the arc tube, so as to prevent electric field accelerated sodium diffusion through the arc tube wall. Such sodium diffusion would adversely affect the lamp life. One drawback to this method for applying an external conducting member to HPS arc tubes is the cost and complexity of designing lamps with movable starting aids. Furthermore, in the absence of direct attachment to the lamp, the starting aid may sag away from the arc tube due to the high temperature of operation. If the starting aid is not in direct contact with the arc tube, anywhere along its length, the starting voltage increases. Additionally, these switches are typically attached to the lamp frame, resulting in heating by radiation, rather than by conduction. This results in variation of lamp performance depending on the wattage of different lamps.




It would therefore be desirable to find a means for applying an external conducting member to arc tubes which would overcome the above mentioned problems.




SUMMARY OF THE INVENTION




The present invention provides an arc discharge lamp comprising an arc tube including a starting aid. The starting aid comprises at least one metal cermet coating applied to the surface of the arc tube, or a metal layer applied to the surface of the arc tube with refractory glass disposed over the metal cermet or metal layer.




In another embodiment of the present invention, a method for forming an arc discharge lamp is provided. This method comprises binding a metal starting aid to an arc tube with refractory glass.




In a further embodiment of the present invention, the starting aid comprises a mixture of two or more metals.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

illustrates a light source including a ceramic discharge chamber with a starting aid according to an exemplary embodiment of the invention.





FIG. 2

illustrates a cross section of the discharge body


22


shown in FIG.


1


.











DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS




Referring now to

FIG. 1

, a discharge lamp


10


, such as a high pressure sodium lamp, according to an exemplary embodiment of the invention is depicted. The discharge lamp


10


includes a discharge chamber


12


which houses two electrodes


14


,


16


and a fill (not shown). The electrodes


14


,


16


are connected to conductors


18


,


20


which apply a potential difference across the electrodes. In operation, the electrodes


14


,


16


produce an arc which ionizes the fill in discharge chamber


12


. The emission characteristics of the light produced by the plasma depend primarily on the constituents of the fill material, the current through the electrodes, the temperature distribution of the chamber, the pressure in the chamber, and the geometry of the chamber. For a ceramic metal halide lamp, the fill material typically comprises a mixture of mercury, a rare gas such as argon or xenon and a metal halide such as NaI, ThI


3


, or DyI


3


. Of course, other examples of fills are well known in the art.




As shown in

FIG. 1

, the discharge chamber


12


comprises a central body portion


22


with an attached starting aid


24


. The ends of the electrodes


14


,


16


are typically located near the opposite ends of the body portion


22


. The electrodes are connected to a power supply by the conductors


18


,


20


, which are disposed through each seal


28


,


30


. The electrodes typically comprise tungsten. The conductors typically comprise molybdenum and niobium, the latter having a thermal expansion coefficient close to that of the ceramic (usually alumina) used to construct the discharge chamber to reduce thermally induced stresses on the seals


28


,


30


.




The discharge chamber


12


is sealed at the ends of the body portion with seal members


28


,


30


. Seal members


28


,


30


typically comprise a disposium-alumina silica glass and can be formed as a glass frit in the shape of a ring around one of the conductors, e.g.


18


, and aligned vertically with the discharge chamber


12


, and melted to flow down over the conductor


18


and form a seal between the conductor


18


and the body portion


22


. The discharge chamber is then turned upside down to seal the other end of the body portion


22


after being filled with the dose.




The starting aid of the present invention is in the form of a metal layer


24


bound to the body of the discharge tube


22


by refractory glass


25


. The metal layer


24


serves as a starting aid and extends substantially between the main electrodes


14


,


16


.




With reference to

FIG. 2

, a cross section of the body of the discharge chamber


22


is shown. An electrode


16


is located near the end of the body


22


, and the seal


28


is shown behind and around the electrode. The starting aid


24


is shown as a metal strip


24


covered with refractory glass layer


25


on the surface of the body


22


.




The body of the discharge chamber


22


can be constructed by forming a mixture of ceramic powder and a binder into a hollow cylinder. Typically, the mixture comprises about 95-98 weight % ceramic powder and about 2-5 weight % organic binder. The ceramic powder may comprise alumina, Al


2


O


3


(having a purity of at least 99.98%) in a surface area of about 2-10 meters


2


per gram. The alumina powder may be doped with magnesia to inhibit grain growth, for example, an amount equal to 0.03% to 0.2%, preferably 0.05% by weight of the alumina. Other ceramic materials which may be used include nonreactive refractory oxides and oxynitrides such as yttrium oxide, hafnium oxide and solid solutions and components with alumina such as yttrium aluminum garnet, aluminum oxynitride, and aluminum nitride. Binders which may be used individually or in combination of inorganic polymers such as polyols, polyvinyl alcohol, vinylacetates, acrylates, cellulosics, and polyethers. Subsequent to die pressing, the binder is removed from the green part typically by a thermal-treatment, to form a bisque fired part. Thermal treatment may be conducted, for example, by heating the green part in air from room temperature to a maximum temperature from about 980-1100° C. over 4 to 8 hours, then holding the maximum temperature for 1 to 5 hours, and then cooling the part. After thermal treatment, the porosity of the bisque fired part is typically about 40-50%.




While the invention has been described with reference to ceramic arc tubes, it should be noted that the present invention would be equally applicable to discharge lamps with quartz arc tubes.




The metal starting aid strip may be bound to the surface of the arc tube after the ceramic arc tube has been sintered. The metal used for the starting aid may be selected from tungsten, molybdenum, and mixtures thereof. The metal may be in various forms. The metals are preferably in the form of a wire or small particles. In deposited form, the metal starting aid will extend at least the distance between electrode tips and will have a width between about 0.1 and 1 mm and a height between about 0.1 and 1 mm, depending upon the overall dimension of the tube.




The metal starting aid strip is bound to the presintered arc tube by a refractory glass matrix. The glass matrix is selected from alumina, silica, magnesia, calcia, boria, and mixtures thereof. Of course, it is preferable that the refractory glass be translucent or transparent to allow the light emitted by the lamp to pass through.




In the embodiment described, the glass layer should be of sufficient thickness to protect the metal starting aid from oxidation. Preferably, the glass layer will be between about 0.1 and 1000 μm thick, more preferably between about 0.1 and 100 μm thick, and most preferably between about 0.1 and 10 μm thick. The glass must also exhibit a melting point in excess of about 1000° C., preferably greater than about 1100° C., and most preferably greater than about 1200° C. The refractory glass of the present invention will also preferably have a thermal expansion coefficient which matches that of the arc tube body. This will prevent flaking of the covering and metal which would lower the lifetime of the lamp.




In an alternative embodiment, the conductive metal strip may comprise a single layer of combined refractory glass and metal, i.e. a cermet, applied to the ceramic body before final sintering. Moreover, the refractory glass may have metal particles dispersed throughout the matrix to serve as the starting aid strip for the lamp. Moreover, the cermet comprises a refractory glass matrix having conductive metal disposed therein. Exemplary refractory materials include alumina, zirconia, magnesia, silica, and mixtures thereof. Exemplary metals include Mo, W, and mixtures thereof. Preferably the cermet will comprise between about 30 and 80% metal and between about 20 and 70% refractory material. The embodiment wherein the starting aid


24


comprises electrically conducting cermet also benefits from a refractory layer


25


for oxidation protection.




According to either embodiment, the lamps of the present invention contain conductive starting aids which are capable of surviving an air firing step for arc tube cleaning, such as temperatures exceeding 750° C. for several minutes to remove organic surface contaminants. Preferably, the starting aids can survive thousands of hours of operation in air. Furthermore, they will permit the use of metals, such as molybdenum, in a vacuum environment. Furthermore, the binding/protection function of the refractory glass may facilitate the use of higher vapor pressure, and less expensive, metals.




Although the invention has been described with reference to exemplary embodiments, various changes and modifications can be made without departing from the scope and spirit of the invention as defined by the appended claims.



Claims
  • 1. An arc discharge lamp comprising an arc tube including a starting aid, said starting aid comprising a metal layer applied to the surface of the arc tube, including a refractory glass disposed over and in contact with said metal layer.
  • 2. The lamp of claim 1 wherein said metal is selected from tungsten and molybdenum.
  • 3. The lamp of claim 1 wherein said starting aid is stable to temperatures greater than about 800° C.
  • 4. The lamp of claim 1 wherein said refractory glass serves as a binding agent to the arc tube.
  • 5. The lamp of claim 1 wherein said arc tube is comprised of ceramic or quartz.
  • 6. The lamp of claim 1 wherein said metal layer is in the form of a wire.
  • 7. The lamp of claim 1 wherein said arc discharge lamp is a high pressure sodium lamp.
  • 8. The lamp of claim 1 wherein said refractory glass is selected from the group consisting of alumina, magnesia, silica, calcia, boria, zirconia, and mixtures thereof.
  • 9. The lamp of claim 1 wherein said metal layer is applied after the lamp arc tube has been formed and densified.
  • 10. A method for forming an arc discharge lamp comprising binding a metal starting aid to an arc tube with refractory glass.
  • 11. The method of claim 10 wherein said starting aid is selected from one of the groups consisting of tungsten, molybdenum, and mixtures thereof.
  • 12. The method of claim 10 wherein said starting aid is in the form of particles dispersed in a glass matrix, a fine refractory metal wire that uses the glass as a binding agent, or metal covered with a glass matrix.
  • 13. The method of claim 10 wherein said starting aid is stable at temperatures between about 700 and 1100° C.
  • 14. The method of claim 10 wherein said arc tube is comprised of a ceramic arc tube.
  • 15. The method of claim 10 wherein said arc tube is comprised of a quartz arc tube.
  • 16. The method of claim 10 wherein said arc discharge lamp comprises a high pressure sodium lamp.
  • 17. An arc discharge lamp comprising an arc tube including a starting aid, said starting aid comprising a cermet coating applied to the surface of the arc tube, including a refractory glass disposed over said cermet coating.
  • 18. The lamp of claim 17, wherein said cermet comprises metal particles disposed in a refractory material matrix.
  • 19. The lamp of claim 18, wherein said metal comprises at least about 30% of said cermet.
  • 20. The lamp of claim 17, wherein said cermet comprises tungsten or molybdenum and alumina.
US Referenced Citations (17)
Number Name Date Kind
3424935 Gungle et al. Jan 1969 A
3828214 Keeffe et al. Aug 1974 A
4048539 Walker et al. Sep 1977 A
4053809 Fridrich et al. Oct 1977 A
4568859 Houkes et al. Feb 1986 A
4633135 Akins Dec 1986 A
4727294 Houkes et al. Feb 1988 A
4788475 Jacobs Nov 1988 A
4940923 Kroontje et al. Jul 1990 A
5047693 Roberts et al. Sep 1991 A
5059868 El-Hamamsy et al. Oct 1991 A
5079479 Weske et al. Jan 1992 A
5355053 Zhu Oct 1994 A
5541480 Renardus et al. Jul 1996 A
5757137 Zhu May 1998 A
5994823 Okamura et al. Nov 1999 A
6380679 Leers et al. Apr 2002 B1
Non-Patent Literature Citations (9)
Entry
Waymouth and Kusko, Monographs in Modern Electrical Technology (1971), Electric Discharge Lamps.
Nortup, Krasko and Lou, Journal of the Illuminating Engineering Society (Summer 1996), Pulse Start of Metal Halide Lamps for Improved Lumen Maintenance.
Byszewski and Budinger, Journal of the Illuminating Engineering Society (Summer 1990), Enhanced Starting of HID Lamps.
Wyner, Journal of the IES (Apr., 1979), Electrolysis of Sodium Through Alumina Arc Tubes.
Gregor, Li, Budinger and Byszewski, Journal of the Illuminating Engineering Society (Summer, 1996), Arc Tube Transparency Loss Due to Starting of HID Lamps.
Waymouth, Koury, Gungle and Peterson, Illuminating Engineering (Apr., 1967), Sodium Loss Processes in Metal Iodide Arc Lamps.
Cohen, Gungle, Gutta, Olson and Richardson, Journal of IES (Jul., 1974), Heat Starting a High-Pressure Sodium Lamp.
Collins and McVey, Lighting Design & Application (Sep., 1975), HPS Lamps for Use on HPM Ballasts.
Illuminating Engineering Society of North America Lighting Handbook, Eighth Edition, High-Intensity Discharge Lamps, p. 219.