Mechanical shear based synthesis of alumoxane nanoparticles

Abstract

A method for forming carboxylate-alumoxane nanoparticles comprises subjecting a mixture comprising boehmite and carboxylic acid to mechanical shear. The method can be carried out at a temperature above ambient and preferably a temperature greater than 80° C., and can be carried out in the absence of a liquid phase.

Description

FIELD OF THE INVENTION

[0003] The present invention relates to a method for quickly and effectively making alumoxane nanoparticles, preferably alumina nanoparticles with surface functionalization based upon an organic carboxylic acid. The present technique makes possible the manufacture of carboxylate-alumoxane nanoparticles without requiring solvents, carrier liquids, extensive mixing times or elevated temperatures. In particular, the present invention combines a process for production of carboxylate-alumoxane nanoparticle production with the use those particles, thereby enabling many applications for which carboxylate-alumoxane nanoparticles were heretofore impossible or impractical. Such applications include coatings and related polymer compositions.

BACKGROUND OF THE INVENTION

[0004] Carboxylate alumoxanes, also known as carboxylato alumoxanes, are inorganic-organic hybrid materials that contain a boehmite-like ([AlO(OH)]n) aluminum oxygen core (FIG. 1), to whose surfaces are attached covalently bound carboxylate groups (i.e., RCO2−, where R=alkyl or aryl group) (FIG. 2). The carboxylate groups are tethered to the aluminum-oxygen surface through bidentate bonding of the carboxylate group to two aluminum atoms on the surface of the boehmite particle. The properties and processability of the carboxylate alumoxanes are strongly dependent on the nature and size of the attached organic groups.

[0005] Until recently, carboxylate alumoxanes were not ideal as processable precursors because they were relatively difficult to prepare. New synthetic routes, including aqueous based techniques, have been discovered which have reduced the high cost of preparing the carboxylate alumoxanes.

[0006] Although there can be significant advantages to the synthesis of carboxylate alumoxanes via the sol-gel route (such as preparation of small particles size and good homogeneity), however, a number of significant difficulties remain. For example, while the reaction of boehmite with a carboxylic acid can be carried out in either water or a variety of organic solvents (including, but not limited to toluene and xylene), it is preferable to use water as the solvent so as to minimize the production of environmentally problematic waste. In a typical reaction, the carboxylic acids are added to boehmite or pseudoboehmite particles, the mixture is heated to reflux at temperatures as high as 100° C. for a period of time, often greater than 24 hours. The water is removed and the resulting solids are collected. As can be appreciated, this process may generate excessive waste, is time consuming, and requires elevated reaction temperatures, and typically must be performed on a batch process.

[0007] It is desirable, therefore to identify materials and processes that can be continuously used to prepare carboxylate alumoxanes using lower reaction temperatures and shorter reaction times. The process would preferably lend itself to the fabrication of a wide range of carboxylate alumoxanes with fine control over composition and particle size. The present invention provides a method of making carboxylate alumoxanes that provides these benefits and avoids many of the problems of prior art processes.

SUMMARY OF THE INVENTION

[0008] The present invention relates to methods and apparatus that can be used to prepare carboxylate alumoxanes. In a preferred embodiment, solid carboxylic acid and solid boehmite particles are mixed and subjected to shear. Even in the absence of a carrier or solvent, a reaction occurs that results in the formation of carboxylate-alumoxanes. The shear forces may be on the order of one N·m and heat may optionally be applied to the reactants.

[0009] These and other embodiments of the present invention, as well as their features and advantages, will become apparent with reference to the following detailed description.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] A better understanding of the present invention can be obtained when the following detailed description of the preferred embodiment is considered in conjunction with the following drawings, in which:

[0011] FIG. 1 is a schematic diagram showing a postulated structure for an aluminum-oxygen core structure analogous to that found in the mineral boehmite, [Al(O)(OH)]n;

[0012] FIG. 2 is a schematic diagram showing how a carboxylate anion, RCO2−, is an isoelectronic and structural analog of the organic portion found in the siloxy-alumoxanes and is known to act as a bridging ligand across two aluminum centers;

[0013] FIG. 3 is several schematic diagrams showing a representative sample of carboxylic acids suitable for reaction with boehmite or pseudoboehmite

[0014] FIG. 4 is a schematic diagram showing a representation of the reaction of boehmite with carboxylic acids; and

[0015] FIG. 5 is an Exemplary plot of calculated torque vs. reaction time for a batch reaction carried out in accordance with the principles of the present invention.

NOTATION AND NOMENCLATURE

[0016] In the following discussion and in the claims, the terms “including” and “comprising” are used in an open-ended fashion, and thus should be interpreted to mean “including, but not limited to . . . ” In addition, the term “nanoparticle” is intended to encompass particles having an average diameter of less than 200 nm, and more preferably less than 20 nm. The terms “nanosol” or “nanosolution” may be used interchangeably and describe a uniformly dispersed solution containing boehmite particles. Also, the size distribution of a quantity of particles is given in terms of standard deviation or particle size range. As used herein, a “narrow size distribution” is one in which the particle size range is ±20% of the average size.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0017] The present invention comprises a method and apparatus in which boehmite and a carboxylic acid are reacted in a high shear mixing environment to produce carboxylate alumoxanes.

[0018] In a preferred embodiment, a mixture of boehmite or pseudoboehmite and a desired carboxylic acid is formed in a shear flow apparatus. The mixture can be a mixture of solid particles that is substantially free of liquid, can contain some amount of liquid, or can be a slurry comprising solid particles in a liquid. If liquid-containing slurry is used, the liquid can be simply a carrier liquid or can be any liquid in which the carboxylic acid is soluble, including but not limited to water, toluene, and aromatic solvents such as polyethers or glycol solvents.

[0019] The carboxylic acid can be any monocarboxylic acid. The carboxylic acid can be aromatic or aliphatic, and can contain hetero-atom functional atoms such as nitrogen, oxygen, sulfur, etc., or hetero-atom functional groups such as amines, hydroxyls, acrylics, etc. A representative sample of suitable carboxylic acids is shown in FIG. 3.

[0020] The solubility of the carboxylate alumoxanes in a given solvent is dependent primarily on the identity of the carboxylic acid residue, which is almost unrestricted according to the present invention, providing it contains a reactive substituent that reacts with the desired co-reactants. The solubilities of the carboxylate-alumoxanes are therefore readily controllable, so as to make them compatible with any desired co-reactants.

[0021] The boehmite (or pseudoboehmite) source can be a commercial boehmite product such as Catapal (A, B, C, D, or FI, Condea-Vista Chemical Company), boehmite prepared by the precipitation of aluminum nitrate with ammonium hydroxide and then hydrothermally treated at 200° C. for 24 hours, or boehmite prepared by the hydrolysis of aluminum trialkoxides followed by hydrothermal treatment at 200° C. Preferred methods for the preparation of the pseudoboehmite or boehmite particles are those that produce particle sizes of the carboxylate alumoxanes below 1,000 nm and more preferably below 100 nm.

[0022] According to the present invention, the mixture of boehmite and carboxylic acid particles is subjected to high shear stresses and, preferably, elevated temperature that cause the boehmite to react with the carboxylic acid to enhance the formation of carboxylated alumoxane particles, as shown in FIG. 4. In FIG. 4, the shaded triangles represent a side view of boehmite and the carboxylate groups are represented by a semicircle and bar. The reaction shown in FIG. 4 may be a condensation reaction, wherein, for example, the carboxylic acids react with the boehmite structure, producing water as a bi-product. One embodiment of the invention entails blending the boehmite and carboxylic acid particles in a high-shear mixer. High shear mixers are known in the art and are commercially available. Such mixers are available as batch mixers or as in-line mixers and can be configured to process either mixtures of solid particles or liquid-based slurries, or both.

[0023] In embodiments in which liquid slurry is used, another apparatus that has been found to be effective for achieving the desired reactions comprises a small diameter tube, preferably having a predetermined length. The diameter of tube is preferably small enough and the viscosity and rate of flow of the slurry are such that particles in the slurry undergo high shear as they pass through the tube.

[0024] In some embodiments, the shearing apparatus may include a rotor/stator device or other mechanical shearing means including the addition of conventional materials that help with the exfoliation of the boehmite by increasing the viscosity of the slurry. For example, a ceramic medium in the range of 5 to 1,000 microns can be used. Examples include ceramic microspheres, micaceous iron oxide, mica, and so forth.

[0025] As an example of a liquid/solid phase reaction, it has been found that a premixed slurry, or nanosol, of boehmite particles having an average size in the range of microns and carried in a liquid comprising 70-97 wt. % of water and 3-30 wt. % of a carboxylic acid, when fed through the small diameter tube at a rate in the range of one tube volume per minute, is converted into carboxylate alumoxane nanoparticles after making a single pass in the pipe. In a preferred embodiment, high shear is realized at velocities above about 1,000 ft/min, more preferably above about 5,000 ft/min, and more preferably in the range of 7,000-9,000 ft/min. A preferred flow rate has been found to be between 5,000 and 9,000 ft/min.

[0026] In some embodiments, the processing system may further include a heat source. The heat source may comprise any external heat mechanism including, but not limited to an electric heater. Alternatively, at least a portion of the heat source can result from the mechanical energy that is applied via the mechanical shearing means.

[0027] In a preferred embodiment, the apparatus comprises a rheometer or rheomixer, such as are commercially available from various companies, including Thermo Haake, Thermo Electron (Karlsruhe) GmbH, Dieselstrasse 4, Karlsruhe, BW 76227, Germany. As can be appreciated, rheometers or rheomixers have internal mixing chambers in which high shear stresses are created, thereby exposing the agglomerates in a mixture to shear forces that will tend to break up the agglomerates. The mixing is generally achieved via blades. Heaters may be present to keep the mixture at a predetermined viscosity/rheology. The “Examples” section below details samples prepared using a Haake Rheomixer 600 instrument having roller-style blades or rotors.

[0028] Carboxylate alumoxane nanoparticles formed using the present method have an average diameter of less than 200 nm, and more preferably less than 20 nm. Furthermore, the nanoparticles exhibit a narrow particle size distribution, wherein any individual particle size typically is ±20% of the average nanoparticle size.

[0029] The present inventors have discovered that the application of shear, and in some instances the combination of high shear and a high viscosity nanosol mixture, greatly accelerates the formation of carboxylate alumoxane nanoparticles and results in a composition in which the boehmite is quickly exfoliated to yield a composition having a narrow particle size distribution. Without wishing to be bound by any particular theory, it is believed that the cleavage of the boehmite is accomplished by shear forces applied to the particles as they pass through the shear mixer, or by a combination of shear forces and heat. As described above, at least a portion of the heat may result from the mechanical energy that is applied during shearing. The heat may drive the reaction between the boehmite and the carboxylate groups. The shear may promote the physical interaction between the boehmite and the carboxylate groups, effectively exposing reaction sites of the two reactants.

[0030] The present technique can achieve in minutes a particle size reduction that requires more than 24 hours using the conventional technique. Because the formation of carboxylate alumoxane nanoparticles can now be achieved very quickly, the process can readily be carried out in a continuous mode.

EXAMPLES

[0031] A Haake Rheomixer 600 instrument was used for all experiments. The miniaturized internal mixer (MIM) was developed for formulating multi-component polymer systems and studying flow behavior, thermal sensitivity, and shear sensitivity. Since torque is proportional to shear stress and rpm to shear rate, shear sensitivity, viscosity and the energy required to process a material can be obtained. The Rheomixer consists of three independent sections, each heated and controlled by its own heater and temperature controller. The mixing chamber is shaped like a figure eight, with a rotor in each chamber. The mixing rotors revolve in opposite directions and at different controlled speeds, to achieve shear action. MIMs have two characteristic geometric features; they have a narrow a gap between the rotor wings and the mixer wall and a larger space between the rotors. The rotors rotate typically at a relative speed of 3:2; the left rotor rotates clockwise while the right one counter clockwise in order to affect a shearing action on the mixture. The mixture is sheared repeatedly through the narrow gap and recycled to the core of the mixture between the rotors. The rotors themselves have helical projections that perform additional axial mixing by moving the mixture around the rotor and towards the center. Extensive mixing takes place exclusively in the core of the mixture while dispersion occurs in the vicinity of the narrow gap under the rotor wing, in which high shear stresses are created exposing the agglomerates to hydrodynamic forces that will tend to break up the agglomerates. It will be understood that the foregoing equipment is exemplary only and that other mix or shearing equipment could be used.

[0032] The Haake Rheomixer 600 instrument was preset with the following settings prior to mixing carboxylic acid and boehmite: (1) the heaters were allowed to reach the desired temperature; and (2) after the heaters were set, the roller-style rotors were brought to the desired speed or rate per minute (rpm).

[0033] A sample of a carboxylic acid (L-lysine (14 g)) and boehmite (6.0 g) was then added to the rheomixer. In each case, the experiment was allowed to run for 120 minutes. In many instances, however, it appeared that the reaction had reached completion well before the end of the 120 minute period. Completion of the reaction was indicated by a significant drop in both torque and temperature. Because torque is proportional to shear stress and rpm is proportional to shear rate, shear sensitivity, viscosity and the energy required to process the material could be calculated. Accordingly, the “time to complete” was determined from the calculated torque versus reaction time plot. FIG. 5 is an exemplary plot and corresponds to Example C.

[0034] After 120 minutes, the sample was extracted into water and any unreacted boehmite was separated. The solution was then pumped dry or the product precipitated with ethanol. The resulting white solid was air-dried. This sample preparation was repeated a number of times to yield the data in Table 1, with each of the samples having essentially the same initial reactants. Referring to Table 1, particle size measurements were obtained on a Coulter N4 Plus Particle Size Analyzer at an angle of 90° and a concentration of 1.0 g.L−1. The water used for dispersing the alumoxanes was distilled and filtered (using a 0.2 μm filter) prior to use.

TABLE 1
	Temp		Average Size	Time to Complete
Run	(° C.)	Rpm	(nm)	(min)
A	60	60	1684	>120
B	70	60	200	>120
C	80	60	3.2	43
D	90	60	1.92	0.7
F	110	60	2.02	38
H	130	60	1.54	12
I	110	70	1.13	11
J	110	80	1.48	40

[0035] Referring to Table 1, it is believed that the combination of increasing temperature and increasing shear rate generally leads to smaller particle size. For example, at temperatures of 80° C. and above, the average particle size decreases dramatically. Also, as shown in Examples I and J, the increase in shear rate (rpm) may aid in the production of smaller particles. In accordance with the spirit of the present invention, temperature and shear conditions which produce particles having an average size of less than 100, more preferably less than 20, more preferably less than 50 nm and still more preferably less than 2 nm are preferred. Furthermore, in some embodiments, while any particle shape may be produced, particles having a generally round or oval shape are preferred.

[0036] From the foregoing experiments, it was determined that, in order to achieve the desired rapid reaction, the torque applied by the mixer is preferably at least 1 N·m, more preferably at least 2 N·m, and still more preferably at least 3 N·m. Nonetheless, shear rates as low as 0.2 or 0.5 N·m may be sufficient, particularly if additives are used to enhance the reaction. If the shear rates greater than 1 N·m are combined with elevated temperatures of at least 60° C., more preferably at least 70° C., more preferably at least 80° C., more preferably at least 90° C., and still more preferably at least 100° C., the reaction time can be reduced to mere minutes. In accordance with the spirit of the present invention, temperature and shear conditions which produce desirable particles having a reaction time (time of completion) of less than 2 hours, more preferably less than 1 hour, more preferably less than 30 minutes and still more preferably less than 10 minutes are preferred.

[0037] Uses

[0038] One traditional approach to the use of nanoparticles in industrial applications is to manufacture and sell the nanoparticles as a “drop-in” additive. Because nanoparticles are not created on-site, there is little flexibility in the conventional approach. The prior art processes are disadvantageous for commercial use because, as mentioned above, such a process poses a logistical problem, which in turn increases costs.

[0039] The present method allows carboxylate-alumoxane nanoparticles to be generated in situ, using mixing equipment that is readily available in most coating manufacturing facilities. In many instances, unlike the prior art technique, the present technique avoids need to recover and wash the carboxylate-alumoxane nanoparticles. In addition, because the present method allows processing to take place in minutes or hours instead of days it is much better suited to use in conjunction with a commercial coating manufacturing facility or other commercial/industrial application, such as packaging film production units or adhesive manufacturing plants.

[0040] It is expected that the present invention will have a broad and significant impact on the industrial coatings market; which includes interior linings, chemical resistant coatings, and rail car linings. One example of a potential use for carboxylate-alumoxane nanoparticles is a highly flexible and impermeable polyurea nanoparticle composite coating that is suitable for many applications; for example, on the many bridges that are protected with red-lead coatings. Overcoating with this polyurea-nanocomposite could extend service life without the prohibitively expensive removal of the old coating.

[0041] Polyurea polymers offer many excellent protective coating properties, such as flexibility over a wide temperature range, adherence to most substrates, low stress to an “undercoat”, allowing for its use as a restorative overcoat. In addition, they can bridge cracks, which is an important consideration in protecting concrete structures. Over the past decade polyureas have grown in popularity and are becoming one of the more promising of the modern coatings and sealants, but their permeability to oxygen and water vapor compromises their corrosion inhibition.

[0042] The preferred function ligands have primary acid sites. In such cases, the carboxylate-alumoxane nanoparticles react with polyurea precursor molecules, i.e. the isocyanate species, to yield a polymer having enhanced resistance to oxygen and water diffusion and increased tensile strength. Suitable polyurea precursors for use in this embodiment include isophorone di-isocyanate (IPDL), methylene bis phenyl di-isocyanate (MDI), and toluene di-isocyanate (TDI).

[0043] In one embodiment, the carboxylate-alumoxane nanoparticles are formed in a high-shear device that is upstream of a mixing device. In the mixing device, the newly-formed carboxylate-alumoxane nanoparticles are mixed with a desired second material. The second material can be a coating, such as a paint or polymeric coating, a moldable composition, such as a polyurea, or an epoxy polymer. The ability to make carboxylate-alumoxane nanoparticles in a high shear mixing environment at their site of use will greatly simplify their use and application by unskilled operators. In addition, the ability to make carboxylate-alumoxane nanoparticles at point of use will simplify shipping and cut out one potential step of manufacturing, and thus cost of production of coatings or other articles prepared using the alumoxanes.

[0044] The present apparatus for mixing the boehmite and the carboxylic acid can be either suitable for a chemical plant and have the potential for large scale continuous processing or as a hand held/back-pack style reactor for use by an individual.

[0045] While the present invention has been disclosed and described in terms of the formation of carboxylated alumoxane particles in a solid phase or slurry reaction, it will be understood that the principles disclosed herein may be altered or modified with deviating from the scope of the invention. For example, shear could be applied via any suitable means. Accordingly, the scope of protection is not limited by the description set out above, but is limited only by the claims that follow, that scope including all equivalents of the subject matter of the claims. Each and every claim is incorporated into the specification as an embodiment of the present invention. Thus the claims are a further description and are an addition to the preferred embodiments of the present invention. Use of the term “optionally” with respect to any element of a claim is intended to mean that the subject element may or may not be present. Both alternatives are intended to be within the scope of the claim.

[0046] Finally, the discussion of a reference in the Background is not an admission that it is prior art to the present invention, especially any reference that may have a publication date after the priority date of this application.

Claims

1. A method for forming carboxylate-alumoxane nanoparticles, comprising: subjecting a mixture comprising boehmite and carboxylic acid to mechanical shear.

2. The method according to claim 1 wherein the method is carried out at a temperature above ambient.

3. The method according to claim 1 wherein the method is carried out at a temperature greater than 80° C.

4. The method according to claim 1 wherein the method is carried out substantially in the absence of a liquid phase.

5. The method according to claim 1 wherein the carboxylate-alumoxane particles are formed within two hours of initiation of shear application.

6. The method according to claim 1 wherein the carboxylate-alumoxane particles are formed within one hour of initiation of shear application.

7. The method according to claim 1 wherein the mixture is heated by the application of heat from an external source.

8. The method according to claim 1 wherein the mixture is heated by the application of heat from an external source and by the application of mechanical shear.

9. The method according to claim 1 wherein the carboxylic acid is selected from the group consisting of an aliphatic carboxylic acid, an aromatic carboxylic acid, and a carboxylic acid containing an additional chemically reactive functional group.

10. The method according to claim 1 wherein the mixture is subjected to mechanical shear by passing it through a tube at a linear velocity of at least about 1,000 ft/min.

11. The method according to claim 1 wherein the mixture is subjected to mechanical shear by passing it through a device comprising a rotor and a stator.

12. The method according to claim 1 wherein the carboxylate-alumoxane nanoparticles have an average size of less than 200 nm.

13. The method according to claim 1 wherein the carboxylate-alumoxane nanoparticles have a size distribution such that the particle size range is ±20% of the average size.

14. Carboxylate-alumoxane particles produced by the method according to claim 1.