MEDICAL DEVICES AND INSTRUMENTS WITH NON-COATED SUPERHYDROPHOBIC OR SUPEROLEOPHOBIC SURFACES

Abstract

Device surfaces are rendered superhydrophobic and/or superoleophobic through microstructures and/or nanostructures that utilize the same base material(s) as the device itself without the need for coatings made from different materials or substances. A medical device includes a portion made from a base material having a surface adapted for contact with biological material, and wherein the surface is modified to become superhydrophobic, superoleophobic, or both, using only the base material, excluding non-material coatings. The surface may be modified using a subtractive process, an additive process, or a combination thereof. The product of the process may form part of an implantable device or a medical instrument, including a medical device or instrument associated with an intraocular procedure. The surface may be modified to include micrometer- or nanometer-sized pillars, posts, pits or cavitations; hierarchical structures having asperities; or posts/pillars with caps having dimensions greater than the diameters of the posts or pillars.

Description

FIELD OF THE INVENTION

This invention relates generally to devices that come in contact with liquids, fluids, oils, gels, and the like and, in particular, to methods and products of processes wherein at least a portion of such devices are rendered superhydrophobic and/or superoleophobic through microstructures and/or nanostructures that utilize the same base material(s) as the device itself.

BACKGROUND OF THE INVENTION

The term hydrophobic/philic is often used to describe the contact of a solid surface with any liquid. The term “oleophobic/philic” is used with regard to wetting by oil and organic liquids. The term “amphiphobic/philic” is used for surfaces that are both hydrophobic/philic and oleophobic/philic. Surfaces with high energy, formed by polar molecules, tend to be hydrophilic, whereas those with low energy and built of non-polar molecules tend to be hydrophobic.

The primary parameter that characterizes wetting is the static contact angle, which is defined as the angle that a liquid makes with a solid. The contact angle depends on several factors, such as surface energy, surface roughness, and its cleanliness. If a liquid wets the surface (referred to as wetting liquid or hydrophilic surface), the value of the static contact angle is 0≤θ≤90 degrees, whereas if the liquid does not wet the surface (referred to as a non-wetting liquid or hydrophobic surface), the value of the contact angle is 90 degrees<θ≤180 degrees.

Surfaces with a contact angle of less than 10 degrees are called superhydrophilic, while surfaces with a contact angle between 150 degrees and 180 degrees are considered superhydrophobic. It is known that surfaces exhibiting microscopic roughness tend to be hydrophobic. With such surfaces, air is trapped between the liquid and the substrate, causing the value of the contact angle to be greater than 90 degrees. In nature, water droplets on the surface of a lotus leaf readily sit on the apex of organic nanostructures because air bubbles fill in the valleys of the structure under the droplet. Therefore, these leaves exhibit considerable superhydrophobicity. The static contact angle of a lotus leaf is about 164 degrees.

One of the ways to increase the hydrophilic properties of a surface is to increase surface roughness. Studies showed that for micro-, nano- and hierarchical structures, the introduction of roughness increased the hydrophobicity of the surfaces. One such hierarchical structure, composed of a microstructure with a superimposed nanostructure of hydrophobic waxes, led to superhydrophobicity with static contact angles of 173 degrees. (See, for example: Bhushan, B., Jung, Y. C., and Koch, K., “Micro-, Nano- and Hierarchical Structures for Superhydrophobicity, Self-Cleaning and Low Adhesion,” Phil. Trans. R. Soc. A 367 (2009b) 1631-1672, the entire content of which is incorporated herein by reference.)

Micro-, nano- and hierarchical patterned structures have been fabricated using soft lithography, photolithography, and techniques which involve the replication of micropatterns, self assembly of hydrophobic alkanes and plant waxes, and a spray coating of carbon nanotubes. FIG. 1 is a schematic of a structure having an ideal hierarchical surface. Microasperities consist of the circular pillars with diameter D, height H, and pitch P. Nanoasperities consist of pyramidal nanoasperities of height h and diameter d with rounded tops. In essence, with such structures, the nanostructures prevent liquids from filling the gaps between the pillars.

There are numerous applications for hydrophobic surfaces, including self-cleaning, drag reduction, energy conservation and conversion. It has also been recognized that certain medical devices could benefit from hydrophobic surfaces. Published U.S. Application No. 2013/0110222, entitled MEDICAL DEVICES INCLUDING SUPERHYDROPHOBIC OR SUPEROLEOPHOBIC SURFACES, discusses the use of superhydrophobic/oleophopic surfaces for numerous medical applications, but it is clear from this reference that the disclosure is limited to superhydrophobic/oleophopic coatings as opposed to engineered microstructures or nanostructures that use the same base material as the device itself.

The preferred embodiments of the Published '222 application prescribe the use of a slippery liquid-infused porous surface (SLIPS) comprising, for example, 1-butyl-3-methylimidazolium hexafluorophosphate. The Application states that “[s]tructured surfaces can also provide coatings, materials, or surfaces that are superhydrophobic, superoleophobic, or both. Suitable structure surfaces include those described in L. Mischchenko et al. ACS Nano 4 (12), 7699-7707 (2010), the disclosure of which is incorporated herein by reference. Suitable silicon nanostructures can be fabricated according to the Bosch process (citations from Published Application omitted). These nanostructures are then treated with a hydrophobic silane (e.g., tridecafluoro-1,1,2,2-tetrahydrooctyl)-trichlorosilane) by vapor exposure in a desiccator under vacuum overnight.” (222 Application; [0035]) “These structured surfaces can have geometrical features in the form of staggered bricks (e.g., subway brick pattern), posts, wide posts, blades, or honeycomb. Suitable geometrical features can be described by pitch, height, and wall/post thickness ratio . . . ” (222 Application; [0036]).

SUMMARY OF THE INVENTION

This invention relates generally to devices that come in contact with liquids, fluids, oils, gels, and the like and, in particular, to methods and products of processes wherein at least a portion of such devices are rendered superhydrophobic and/or superoleophobic through microstructures and/or nanostructures that utilize the same base material(s) as the device itself.

A medical device according to the invention includes a portion made from a base material having a surface adapted for contact with biological material, and wherein the surface is modified to become superhydrophobic, superoleophobic, or both, using only the base material, excluding non-material coatings. The surface may be modified using a subtractive process, an additive process, or a combination thereof. The product of the process may form part of an implantable device or a medical instrument, including a medical device or instrument adapted for use with an intraocular procedure.

In accordance with the invention, the surface adapted for contact with biological material is modified to include micrometer- or nanometer-sized structures or patterns made from the base material. For example, the surface may be modified to include micrometer- or nanometer-sized pillars, posts, pits or cavitations; hierarchical structures having asperities; or posts/pillars with caps having dimensions greater than the diameters of the posts or pillars.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic of a preferred structure having a hierarchical surface including asperities;

FIG. 2 is a diagram that shows potential fabrication techniques used to fabricate micron- and nano-scale structures;

FIG. 3A shows an array of pointed conical shapes applicable to the invention;

FIG. 3B shows an array of tapered pillars with caps applicable to the invention;

FIG. 3C shows an array of wider tapered pillars with caps applicable to the invention;

FIG. 3D shows an array of shorter, tapered pillars applicable to the invention;

FIG. 3E shows an array of short, coin-like structures;

FIG. 3F shows an array of narrower, tapered pillars with caps applicable to the invention;

FIG. 4A illustrates a woven superomniphobic surface;

FIG. 4B illustrates a random superomniphobic surface;

FIG. 5A shows a post or pillar having an inverse trapezoidal cross-section;

FIG. 5B shows a post or pillar having a non-inverted trapezoidal cross-section;

FIG. 5C depicts a preferred array of the structures of FIG. 5A;

FIG. 6 is an illustration that depicts intraocular scissors;

FIG. 7 is an illustration that shows a vitrectomy probe; and

FIG. 8 is an illustration that depicts intraocular forceps.

DETAILED DESCRIPTION OF THE INVENTION

This invention improves upon existing designs by providing medical devices with hydrophobic/oleophobic surfaces using the same material(s) that such devices are constructed from; that is, without resorting to coatings. This is significant in that the substances used for such coatings may become detached during use and/or implantation, leading to contamination, infection, and other undesirable side-effects.

FIG. 2 is a diagram that shows potential fabrication techniques used to fabricate micron- and nano-scale structures. In the preferred embodiments, reduction processes (i.e., lithographic and/or etching) are preferred to additive steps such as deposition since the goal is to avoid material coatings. In the most preferred embodiments, e-beam lithographic and/or laser etching steps are used to create an array of pillars on the surface being modified. The invention does not preclude additive processes, however, so long as the same base material of the device is used to produce the additive microstructure. That is, if the base material is metal (i.e., stainless steel, chrome-cobalt, etc.), a metallic microstructure or nanostructure is additively formed to achieve a continuity in material type as opposed to dissimilar materials having a greater tendency to separate and flake off. Thus, processes requiring silicon (including the Bosch process), would not be recommended if a silicon coating is first required.

Different micro-/nanostructures are applicable to the invention depending upon the hydrophobic and/or oleophobic properties to be achieved in view of a given application. FIGS. 3A-3F show arrays of shapes, certain of which may be more effective than other including pointed conical shapes and tapered pillars with and without caps. FIG. 4A illustrates a woven superomniphobic surface, and FIG. 4B illustrates a random superomniphobic surface.

Pillars formed in accordance with the invention may have straight sides or may have tapered sides. Pillars with any cross-sectional shape may be used, including circular or polygonal with 3, 4, 5, 6 or more sides. The pillars may have pointed or semi-pointed upper ends, as shown in FIGS. 3A-3F. Preferably, the pillars have a diameter (D) in the range of 10 microns or less, with a height (H) at least as tall as the pillars are wide. In more preferred embodiments, pillar height is 2-4 times the cross sectional height. Pillar spacing is preferably in the order of one to three times D.

The structures of FIGS. 5A-5C are considered to be particularly effective. FIG. 5A shows a post or pillar having an inverse trapezoidal cross-section; FIG. 5B shows a post or pillar having a non-inverted trapezoidal cross-section, and FIG. 5C depicts a preferred array of the structures of FIG. 5A.

In certain preferred embodiments, the structure is hierarchical (FIG. 1) in the sense that one or more of the tops, sides, or spaces between the pillars includes asperities of height h in the range of 1 micron or less, depending upon the size of the pillars themselves. Preferably, the asperities are from 0.5 to 0.01 times the nominal thickness of the pillars, more preferably 0.1 times the nominal thickness. Such asperities may be produced via chemical etching following pillar formation.

The above, coating-free hydrophobic/oleophobic surface modifications may be used on any implantable on non-implantable medical device or instrument. Substrates of metal, ceramics—even plastics—may be modified through appropriate engineering modification to the energetic beams/etching modalities. The invention finds particular utility in providing surgical instruments having hydrophobic/oleophobic surfaces, and more particular those used in intraocular procedures. Such instruments include, without limitation, intraocular scissors (FIG. 6); vitrectomy probes (FIG. 7); and intraocular forceps (FIG. 8). In the event the instrument has one or more sharpened edges, such sharpening may be performed before or after the above surface modification, though sharpening following surface modification is preferred to produce the sharpest edge(s), while ensuring that any loose pillars are sloughed off prior to use.

Claims

1. A method of modifying a medical device, comprising the steps of: providing a medical device including a distal end constructed from a base material;wherein the distal end of the device includes a surface adapted for contact with biological material;modifying the surface to become superhydrophobic, superoleophobic, or both, using only the base material; andinserting at least the distal end of the device into a body cavity including biological material such that the biological material is repelled by the modified surface.

2. The method of claim 1, wherein the distal end of the device is adapted for intraocular insertion.

3. The method of claim 2, wherein the medical device is intraocular scissors.

4. The method of claim 2, wherein the medical device is a vitrectomy probe.

5. The method of claim 2, wherein the medical device is intraocular forceps

6. The method of claim 1, wherein the base material is a metal.

7. The method of claim 6, wherein the base material is chrome-cobalt.

8. The method of claim 6, wherein the base material is stainless steel.

9. The method of claim 1, wherein the base material is a ceramic.

10. The method of claim 1, wherein the base material is a plastic.

11. The method of claim 1, wherein step of the modifying the surface to become superhydrophobic, superoleophobic, or both, include the use of e-beam lithography.

12. The method of claim 1, wherein step of the modifying the surface to become superhydrophobic, superoleophobic, or both, include the use of laser etching.

13. The method of claim 1, wherein the distal end of the device includes one or more sharpened edges; and the one or more edges are sharpened after modifying the surface to become superhydrophobic, superoleophobic, or both.

14. The method of claim 1, including the step of modifying the surface to include micrometer- or nanometer-sized structures or patterns made from the base material.

15. The method of claim 1, including the step of modifying the surface to include micrometer- or nanometer-sized pillars, posts, pits or cavitations using only the base material.

16. The method of claim 11, including the step of modifying the surface to include micrometer- or nanometer-sized hierarchical structures having asperities.

17. The method of claim 1, including the steps of: modifying the surface to include micrometer- or nanometer-sized posts or pillars having diameters; andforming upper caps on the posts or pillars with dimensions greater than the diameters of the posts or pillars.

18. The method of claim 1, including the step of using a subtractive process to modify the surface to become superhydrophobic, superoleophobic, or both.

19. The method of claim 1, including the step of using a subtractive process to modify the surface to become superhydrophobic, superoleophobic, or both.

20. The method of claim 1, including the step of using a combination of additive and subtractive processes to modify the surface to become superhydrophobic, superoleophobic, or both.