The invention relates to medical devices, such as endoprostheses, and methods of making the devices.
The body includes various passageways such as arteries, other blood vessels, and other body lumens. These passageways sometimes become occluded or weakened. For example, the passageways can be occluded by a tumor, restricted by plaque, or weakened by an aneurysm. When this occurs, the passageway can be reopened or reinforced, or even replaced, with a medical endoprosthesis. An endoprosthesis is typically a tubular member that is placed in a lumen in the body. Endoprostheses can be delivered inside the body by a catheter that supports the endoprosthesis in a compacted or reduced-size form as the endoprosthesis is transported to a desired site. Upon reaching the site, the endoprosthesis is expanded, for example, so that it can contact the walls of the lumen.
The expansion mechanism may include forcing the endoprosthesis to expand radially. For example, the expansion mechanism can include the catheter carrying a balloon, which carries a balloon-expandable endoprosthesis. The balloon can be inflated to deform and to fix the expanded endoprosthesis at a predetermined position in contact with the lumen wall. The balloon can then be deflated, and the catheter withdrawn.
In another delivery technique, the endoprosthesis is formed of an elastic material that can be reversibly compacted and expanded, e.g., elastically or through a material phase transition. During introduction into the body, the endoprosthesis is restrained in a radially compacted condition. Upon reaching the desired implantation site, the restraint is removed, for example, by retracting a restraining device such as an outer sheath, enabling the endoprosthesis to self-expand by its own internal elastic restoring force.
The invention relates to medical devices, such as endoprostheses, and methods of making the devices. Exemplary endoprostheses include stents, covered stents, and stent-grafts.
In some embodiments, an endoprosthesis for deployment within a body passage includes a tubular framework and a metallic film having a thickness of about 50 μm or less and disposed internally of the tubular framework. The endoprosthesis may be self-expanding.
The tubular framework may have an internal surface. The metallic film, which may be generally tubular in shape, may have an outer surface that contacts the internal surface of the tubular framework.
The film may be a deposited metallic film including, e.g., deposited nickel and titanium. The deposited film may have a thickness of about 50 μm or less, 50 μm or less, e.g., about 35 μm or less. The deposited film may have a thickness of 4 μm or greater. The film may exhibit super-elastic properties. In embodiments, the film is not shape set.
The endoprosthesis, when in a deployed state within a body passage, may exert an outward radial force against the body passage, with essentially all of the outward radial force resulting from the tubular framework.
The endoprosthesis may have an internal surface that is substantially defined by an internal surface of the metallic film.
In embodiments, the endoprosthesis includes only one framework.
In some embodiments, the endoprosthesis includes at least a second tubular framework. At least a portion or all of the metallic film is sandwiched between the tubular framework and the second tubular framework. The endoprosthesis may be self expanding. In embodiments, neither the tubular framework nor the second tubular framework, by itself, exerts a radial force sufficient to secure the endoprosthesis within a body passage but together, the tubular framework and second tubular framework exert force sufficient to secure the endoprosthesis. In a deployed state, the tubular framework and the second tubular framework may each exert a radial force. The radial force of the second tubular framework may greater than the radial force of the tubular framework.
A total radial thickness of the tubular framework and the second tubular framework may be about 75 microns or less. The tubular framework and the second tubular framework may have at least some relative freedom of movement along at least one of the radial, circumferential, and longitudinal dimensions.
Substantially all or all of the metallic film may be a single layer.
In some embodiments, a self-expanding endoprosthesis for deployment within a body passage includes a first tubular framework, a tubular member disposed around the first tubular framework, and a second tubular framework disposed around the tubular member.
In embodiments, neither of the first and second tubular frameworks alone exerts sufficient outward radial force to self-expand the endoprosthesis within a body passage but the first and second tubular frameworks together exert sufficient outward radial force to self-expand the endoprosthesis.
The film may be a deposited metallic film including, e.g., deposited nickel and titanium. The deposited film may have a thickness of about 50 μm or less, 50 μm or less, e.g., about 35 μm or less. The deposited film may have a thickness of 4 μm or greater. The film may exhibit super-elastic properties. In embodiments, the film is not shape set.
In embodiments, a delivery device for deploying an endoprosthesis within a body passage includes an elongate inner member, a self-expanding endoprosthesis disposed about a distal portion of the inner member, the endoprosthesis comprising a tubular framework disposed about a deposited metallic film and an outer sheath surrounding the elongate inner member and the self-expanding endoprosthesis, wherein the tubular framework prevents substantial frictional contact between the tubular member and the outer sheath.
In one aspect, the invention features an endoprosthesis including a metallic film, e.g., a vapor deposited film, including nickel, titanium, and chromium. A ratio of a weight of chromium of the metallic film to a combined weight of nickel, titanium, and chromium of the metallic film is at least 0.001 and can be less than 0.0075.
Other aspects, features, and advantages of the invention will be apparent from the description of the preferred embodiments thereof and from the claims.
a is a side view of a distal portion of a deployment device prior to radial expansion of the endoprosthesis.
b is a side view of the distal portion of the deployment device subsequent to radial expansion of the endoprosthesis adjacent the aneurysm.
Referring to
In some embodiments, endoprosthesis 100 modifies an amount or velocity of blood passing between vessel 26 and aneurysm 25. For example, prosthesis 100 can be deployed to reduce or block blood flow between vessel 26 and aneurysm 25, e.g., to occlude the aneurysm 25. If so deployed, prosthesis 100 may sufficiently reduce blood flow to allow clotting or other healing processes to take place within aneurysm 25 and/or opening 29 thereof. Tubular member 54 can provide a greater attenuation of the blood flow into the aneurysm 25 than stent body 52 alone. Endoprosthesis 100, however, can allow some flow to pass between vessel 26 and aneurysm 25 even while providing some reduction in the rate and/or volume of flow. Prosthesis 100 can also (or alternatively) allow blood to pass between vessel 26 containing the prosthesis and adjacent vessels, e.g., feeder vessel 27, while still providing reduced flow with respect to the aneurysm.
Referring to
With reference to
Upon expansion, endoprosthesis 100 assumes a shape and radial extent generally coextensive with an inner surface of the vessel 26, e.g., a tubular shape centered about a longitudinal axis a1 of the prosthesis (
In some embodiments the tubular member 54 of endprosthesis 100 includes a metallic film deposited by a vapor deposition process. Vapor deposited materials are formed by depositing film constituents from a vapor or a vacuum onto a surface. In embodiments, the constituents are vaporized by bombarding, heating or sputtering a bulk target. The vaporized constituents deposit on a substrate to form the film. Deposited films can exhibit highly uniform thickness and microstructure in very thin films, e.g. about 50 microns or less, e.g. 4-35 microns. Suitable vapor deposition processes are described in Busch et al. U.S. Pat. No. 5,061,914, Bose et al. U.S. Pat. No. 6,605,111, Johnston U.S. Pat. No. 6,533,905, and Gupta et al. U.S. 2004/0014253, the entire contents of all of which are hereby incorporated by reference.
In some embodiments, the deposited film can include an alloy of nickel and titanium present in amounts sufficient to provide the deposited film with desirable mechanical or shape memory properties. For example, the film may include an alloy, e.g., a superelastic or pseudo-elastic metal alloy, as described, for example, in Schetsky, L. McDonald, “Shape Memory Alloys,” Encyclopedia of Chemical Technology (3rd ed.), John Wiley & Sons, 1982, vol. 20. pp. 726-736; and commonly assigned U.S. Ser. No. 10/346,487, filed Jan. 17, 2003. The alloy may be nitinol. The alloy may include a third compound, e.g., chromium, which modifies a mechanical property, e.g., a hardness or elasticity, of the film. Tubular member 54 may include a deposited metal film including nickel, titanium, and, optionally, chromium. Exemplary films and deposition of such films is described in U.S. application Ser. No. ______, filed concurrently herewith, titled MEDICAL DEVICES INCLUDING METALLIC FILMS AND METHODS FOR MAKING SAME, attorney docket no. 10527-570001, which application is incorporated herein by reference.
Referring to
During introduction via a delivery device along a body passageway, e.g., within a blood vessel, stent body 152 is positioned between the surrounding delivery device, e.g., the outer sheath 31 of device 30, and the tubular member 154. Upon deployment, as the outer sheath is retracted over the endoprosthesis, the substantially all or all of any friction between the sheath and endoprosthesis is experienced by the stent body 152 not the tubular member 154. For example, at least about 75% or at least 90% of the frictional contact between the sheath and the endoprosthesis during radial expansion may be between an inner surface of the outer sheath and the tubular framework. Such a configuration can protect the tubular member from damage, e.g., tears, when the endoprosthesis is loaded into the delivery device and during deployment.
As the endoprosthesis 150 radially expands against a body passageway, stent body 152 can limit or prevent contact between the internal surface of the body passageway and the tubular member. For example, locating the tubular member internal of the stent body prevents the stent body from forcing the tubular member against the body passageway during radial expansion. Hence, fenestrations of the tubular member, if present, will not slide with significant force against the body passageway internal surface so as to minimize mechanical damage from the fenestrations to the body passageway.
In embodiments, the endoprosthesis is a re-sheathable endoprosthesis, such as a closed cell stent body with internal tubular member.
Once deployed, tubular member 154 shields blood flowing longitudinally through the endoprosthesis from stent body 152, e.g., from circumferential bands 157 and longitudinal members 158. Hence, a tendency for the blood flow to be disrupted or perturbed by stent body 152 is reduced or eliminated. A tendency for blood to clot within the interior 162 is also reduced or eliminated because the generally smoother topography presented by tubular member 154 offers fewer projections than if stent body 152 were internal of tubular member 152.
Because stent body 152 is disposed of connected circumferential bands rather than a more contiguous surface, stent body 152 presents less surface area to the wall of the passageway than would tubular member 154. Consequently, when radially expanded against the wall of a body passageway, e.g., vessel 26, endoprosthesis 150 produces less metal to tissue contact than if the stent body 152 were not positioned between the passageway wall and the tubular member 154. Additionally, interstices created by stent body 152 between the passageway wall and tubular member 154 can enhance endothelial growth and recovery.
Endoprosthesis 150 can be assembled by overexpanding stent body 152 to a greater diameter than it assumes in a body passageway and then sliding or drawing the tubular member into the interior of the stent body. Subsequently, stent body 152 is allowed to contract against the tubular member. In embodiments, when expanded within a body passageway, the tubular member is about as long as the stent body and may be shorter.
The tubular member and stent body can be secured, e.g., mechanically, with adhesive, or combination thereof. As shown, filaments 101 pass around portions of stent body 152 and through fenestrations 165 of tubular member 154. Filaments 101 can be formed of a polymer, a suture, a ductile metal wire, such as nitinol or gold wire, or other suitable material. In some embodiments, the tubular member differs from a fabric at least in that the tubular member is a metallic film that lacks fibers that can be pushed apart to receive a filament as by sewing a fabric. Accordingly, the fenestrations can be formed prior to the process of passing the filament through the tubular member. Fenestrations that receive the filaments can be formed by, e.g., etching, laser cutting, or a photolithographic process. Other mechanical securing structures include fasteners, such as grommets and rivets. Securing techniques are described in U.S. Ser. No. ______, {Attorney Docket No. 10527-566001}, filed contemporaneously herewith and incorporated herein by reference.
In embodiments, substantially all of the radial outward force exerted by endoprosthesis 150 is due to stent body 152. In some embodiments, tubular member 154 is a deposited metallic film of a memory alloy that is shape set to a larger diameter than the radially expanded diameter of the stent body 152 within a body passageway. The resulting outward radial force exerted by the tubular member 154 against the stent body helps secure the tubular member and stent body. The tubular member outward force may supplement the outward force exerted by the stent body.
As shown in
Referring to
Either of stent bodies 252, 253 may exert a greater outward radial force than the other. In embodiments, internal stent body 252 exerts a greater radial outward force, which helps secure internal stent body 252 and tubular member 254 with respect to external stent body 253. In embodiments, a radial thickness of each stent body 252, 253 is about 60 μm or less, about 50 μm or less, about 30 μm or less, e.g., about 25 μm or less. The total radial thickness of stent bodies 252, 253 may be about 120 μm or less, about 100 μm or less, about 60 μm or less, e.g., about 50 μm or less. One of the stent bodies 252, 253 may make up at least about 50%, at least about 75%, e.g., at least about 85% of the total radial thickness.
In some embodiments, stent bodies 252, 253 and tubular member 254 are secured with respect to one another by filaments 101, which pass through fenestrations 265 of the tubular member and pass around and/or are secured to either or both of stent bodies 252, 253. In embodiments, a given filament secures the tubular member with respect to one but not both stent bodies 252, 253.
Endoprosthesis 200 can be configured so that stent bodies 252, 253 have relative freedom of movement with respect to one another and/or with respect to tubular member 254. The freedom of movement may be provided along a given dimension, e.g., a radial, a circumferential, a longitudinal dimension, or combination thereof. For example, filaments 101 may have a length sufficient to provide some freedom of movement. Filaments that pass around longitudinal members 258 can allow longitudinal movement whereas filaments that pass around portions of circumferential bands 257 can allow circumferential movement. In some embodiments, stent bodies 252, 253 have essentially no freedom of movement along one or more dimensions, e.g., along one or all of the radial, circumferential, and longitudinal dimensions. Securing techniques alternative to or supplemental to filaments can be used.
Referring to
An end 357 of each projection 353 can be flattened or otherwise broadened to prevent the projection from retracting through the aperture 355. Depending upon the relative shape and size of the apertures and projections, the apertures and projections can be configured to provide the stent bodies with radial, longitudinal and/or circumferential freedom of movement.
Other examples of endoprostheses including a thin film as well as related systems and methods are described in U.S. provisional patent application No. 60/549,287, filed Mar. 2, 2004, which application is incorporated herein by reference.
Methods and structures for securing a framework and one or more deposited thin film covers are described in U.S. patent application Ser. No. ______, attorney docket no. 10527-566001, titled MEDICAL DEVICES INCLUDING METALLIC FILMS AND METHODS FOR MAKING SAME, and filed concurrently herewith, which application is incorporated herein by reference.
An endoprosthesis may include a cover disposed externally to a framework as shown and/or internally of a framework. Endoprostheses having a cover including, e.g., a deposited thin film, disposed internally of a framework are described in U.S. patent application Ser. No. ______, attorney docket no. 10527-567001, titled MEDICAL DEVICES INCLUDING METALLIC FILMS AND METHODS FOR MAKING SAME, and filed concurrently herewith, which application is incorporated herein by reference.
An endoprosthesis may include features to enhance a flexibility of the endoprosthesis as described in U.S. patent application Ser. No. ______ attorney docket no. 10527-568001, titled MEDICAL DEVICES INCLUDING METALLIC FILMS AND METHODS FOR MAKING SAME, and filed concurrently herewith, which application is incorporated herein by reference.
An endoprosthesis may include a deposited thin film and a polymer as described in U.S. patent application Ser. No. ______, attorney docket no. 10527-596001, titled MEDICAL DEVICES INCLUDING METALLIC FILMS AND METHODS FOR MAKING SAME, and filed concurrently herewith, which application is incorporated herein by reference.
An endoprosthesis may include one or more filaments, e.g., wires, adapted to enhance mechanical properties of a deposited thin film as described in U.S. patent application Ser. No. ______, attorney docket no. 10527-621001, titled MEDICAL DEVICES INCLUDING METALLIC FILMS AND METHODS FOR MAKING SAME, and filed concurrently herewith, which application is incorporated herein by reference.
Methods for loading an endoprosthesis into a delivery device and systems for delivering an endoprosthesis to a treatment site are described in U.S. patent application Ser. No. ______, attorney docket no. 10527-569001, titled MEDICAL DEVICES INCLUDING METALLIC FILMS AND METHODS FOR LOADING AND DEPLOYING SAME, which application is incorporated herein by reference.
All publications, references, applications, and patents referred to herein are incorporated by reference in their entirety.
Other embodiments are within the claims.