Patent Grant
10285905
The present invention relates to a medical rubber stopper and a method for producing a medical rubber stopper.
The quality stability of drugs in vials has been improved by laminating the leg portion of a rubber stopper, which is to be in contact with drugs, with an inert film, such as of fluororesin, to improve the chemical resistance of the rubber stopper. Known lamination methods include two-step molding processes (see
Rubber stoppers produced by two-step molding processes are excellent in airtightness as the lower surface of their flange region and the base of their leg portion are provided as a rubber surface. The two-step molding processes, however, have a problem in that a molding step and a step of removing unnecessary parts both need to be performed twice, thereby resulting in poor productivity. Another problem is that oily preparations may reach the rubber surface to swell the rubber, thereby resulting in poor chemical resistance and airtightness.
On the other hand, one-step molding processes can produce rubber stoppers whose flange region has a lower surface entirely laminated with an inert film, and are also excellent in productivity as the number of steps is greatly smaller than that of the two-step molding processes. The airtightness of a vial can be achieved, for example, by bringing the inner wall and the upper surface of the vial into intimate pressure contact with the base of the leg portion and the lower surface of the flange region of a rubber stopper. However, disadvantageously, rubber stoppers produced by the one-step molding processes have poor airtightness because each of the above contact surfaces is hard glass or an inert film.
Patent Literature 1: JP 2004-216753 A
The present invention aims to provide a medical rubber stopper that is excellent in chemical resistance and airtightness while having good productivity.
The present invention relates to a medical rubber stopper, including: a disk-shaped head portion with a flange region; and a cylindrical leg portion protruding from a lower surface of the head portion and having a smaller diameter than the head portion, a lower surface of the flange region and the leg portion being laminated with an inert film, at least one of the lower surface of the flange region or an outer periphery of the leg portion being provided with an annular groove through which the base rubber is exposed.
Preferably, at least one edge of the groove is provided with a projection elevated above an adjacent surface of the inert film, and the projection has a height of 1 to 40 μm from the adjacent surface of the inert film.
The groove is preferably provided at least on the outer periphery of the leg portion.
The groove is preferably provided at least at a base of the leg portion.
The groove preferably has a width of 0.1 to 10 mm.
The inert film preferably has a thickness of 200 μm or less.
The present invention also relates to a method for producing a medical rubber stopper, the medical rubber stopper including: a disk-shaped head portion with a flange region; and a cylindrical leg portion protruding from a lower surface of the head portion and having a smaller diameter than the head portion, the method including: a molding step including forming by one step molding a rubber stopper in which a lower surface of the flange region and the leg portion are continuously laminated with an inert film; and a groove-forming step including forming an annular groove to expose the base rubber on at least one of the lower surface of the flange region or an outer periphery of the leg portion each laminated with the inert film.
The groove-forming step preferably includes forming the groove by laser processing.
The present invention relates to a medical rubber stopper in which the lower surface of the flange region and the leg portion are laminated with an inert film, and the lower surface of the flange region and/or the outer periphery of the leg portion is provided with an annular groove through which the base rubber is exposed. The present invention also relates to a method for producing a medical rubber stopper, which includes: a molding step including forming by one step molding a rubber stopper in which the lower surface of the flange region and the leg portion are continuously laminated with an inert film; and a groove-forming step including forming an annular groove to expose the base rubber on the lower surface of the flange region and/or the outer periphery of the leg portion each laminated with the inert film. Accordingly, the present invention can provide a medical rubber stopper that is excellent in chemical resistance and airtightness while having good productivity.
The present invention relates to a medical rubber stopper including: a disk-shaped head portion with a flange region; and a cylindrical leg portion protruding from the lower surface of the head portion and having a smaller diameter than the head portion. The lower surface of the flange region and the leg portion are laminated with an inert film, and the lower surface of the flange region and/or the outer periphery of the leg portion is provided with an annular groove through which the base rubber is exposed.
In the medical rubber stopper of the present invention, since the lower surface of the flange region and/or the outer periphery of the leg portion each laminated with an inert film is provided with an annular groove through which the base rubber is exposed, the groove portion where the base rubber is exposed can be brought into sufficiently intimate contact with the upper surface of the mouth and the inner wall of a vial upon capping of the vial, thereby resulting in good airtightness. This is presumably because upon capping of a vial with a rubber stopper designed to have a leg portion diameter larger than the mouth diameter of the vial, and upon sealing of the capped vial with an aluminum cap, the leg portion and the lower surface of the flange region are compressed to allow the base rubber defining the groove to be exposed to facilitate the contact with the upper surface of the mouth and the inner wall of the vial. In addition, the inert film ensures chemical resistance.
The medical rubber stopper of the present invention is therefore applicable to vials to be filled with drugs in any form, including powder, solid, liquid (solution, oil), and lyophilizate forms, and can provide them with excellent chemical resistance and airtightness.
Exemplary preferred embodiments of the present invention will be described below with reference to drawings.
The exemplary medical rubber stopper 1 of the present invention shown in
The head portion 11 includes a flange region 11a, and the leg portion 12 is provided to extend continuously from the inner edge 11c of the (donut-shaped) lower surface 11b of the flange region. The leg portion 12 is provided to protrude in the shape of a cylinder with a smaller diameter than the outer diameter of the head portion 11 from the lower surface of the head portion 11, specifically from the inner edge 11c of the lower surface of the flange region.
In the medical rubber stopper 1, since the lower surface 11b of the flange region and the surface of the leg portion 12 are laminated with an inert film 13, chemical resistance can be ensured for the medical rubber stopper. The thickness of the inert film 13 may be appropriately adjusted according to the shape or size of the medical rubber stopper, and is preferably 20 to 200 μm, more preferably 50 to 100 μm.
The medical rubber stopper 1 is provided with an annular groove 14 which is not laminated with the inert film 13 so that the base rubber is exposed. The groove 14 is provided on the outer periphery 12a of the base 12b of the leg portion 12 in a location which is continuous with the inner edge 11c of the lower surface of the flange region. The presence of the groove 14 provided at the base facilitates the contact with the inner wall of a bottle, leading to improved airtightness. Especially in the case of vials having a protrusion on the inner side of their mouth as illustrated in
The “annular” shape of the groove 14 means a substantially annular shape centered on the central axis of the disk-shaped head portion. The cross-sectional shape of the groove is not particularly limited, and is preferably a simple recess or a rounded recess from the standpoint of productivity. Although
The width 14w of the groove 14 is preferably 0.1 to 10 mm, more preferably 0.5 to 8.0 mm, still more preferably 2.0 to 8.0 mm, from the standpoint of the balance between airtightness and chemical resistance. The depth 14d of the groove 14 from the adjacent interface 16 between the base rubber and the inert film 13 is preferably 0 to 100 μm, more preferably 0 to 50 μm, from the standpoint of airtightness.
As illustrated in the partially enlarged view (e) of the groove 14, the medical rubber stopper 1 is provided with a projection 15 at the edge 14a on the leg portion 12 side of the groove 14. The projection 15 is configured to be elevated above (protrude from) the adjacent surface 13s of the inert film 13. The presence of the projection 15 further enhances the airtightness.
The width 15w of the projection 15 is preferably 1 to 100 μm, more preferably 30 to 60 μm, from the standpoint of airtightness. The height 15h of the projection 15 from the adjacent surface 13s of the inert film 13 is preferably 1 to 40 μm, more preferably 10 to 25 μm, from the standpoint of airtightness. With the projection within the ranges indicated above, the airtightness can be further improved. The shape (cross-sectional shape) of the projection 15 is not particularly limited, and is preferably a simple projection or a rounded projection from the standpoint of productivity. The projection 15 may be provided at either one or both edges of the groove 14.
The exemplary medical rubber stopper 2 of the present invention shown in
The head portion 21 and leg portion 22 are provided in the same manner as illustrated in
The medical rubber stopper 2 is provided with an annular groove 24 which is not laminated with the inert film 23 so that the base rubber is exposed. The groove 24 is provided in the substantial center of the lower surface 21b of the flange region. The presence of the groove 24 provided on the lower surface 21b of the flange region facilitates the contact with the mouth surface of a bottle, leading to improved airtightness. Especially in the case of vials having a protrusion on the upper surface of their mouth as illustrated in
The annular shape, number, and width 24w of the groove 24, and the depth 24d of the groove 24 from the adjacent interface 26 between the base rubber and the inert film 23 may be the same as those described above.
As illustrated in the partially enlarged view (e) of the groove 24, the medical rubber stopper 2 is provided with a projection 25 at the edge 24a on the center side of the groove 24. The projection 25 is configured to be elevated above (protrude from) the adjacent surface 23s of the inert film 23. The presence of the projection 25 further enhances the airtightness.
The width 25w and shape of the projection 25, and the height 25h of the projection 25 from the adjacent surface 23s of the inert film 23 may be the same as those described above. The projection 25 may be provided at either one or both edges of the groove 24.
The medical rubber stopper of the present invention including a disk-shaped head portion with a flange region, and a cylindrical leg portion protruding from the lower surface of the head portion and having a smaller diameter than the head portion can be produced by, for example, a method that includes: a molding step including forming by one step molding a rubber stopper in which the lower surface of the flange region and the leg portion are continuously laminated with an inert film; and a groove-forming step including forming an annular groove to expose the base rubber on the lower surface of the flange region and/or the outer periphery of the leg portion each laminated with the inert film. With this method, medical rubber stoppers having excellent chemical resistance and airtightness can be produced in good productivity.
In the molding step, the upper and lower molds are preheated before the molding of a rubber stopper. The preheating temperature is preferably about 155 to 200° C.
An inert film superposed on a kneadate sheet (unvulcanized rubber sheet) formed from materials of a rubber stopper body is set on the upper surface of the lower mold. Here, the upper and lower molds may be disposed below and above, respectively, and an unvulcanized rubber sheet on which a lamination film is superposed may be placed on the upper mold.
The inert film is not particularly limited, and preferred examples include films of fluorinated resins such as tetrafluoroethylene polymers (PTFE), tetrafluoroethylene-ethylene copolymers (ETFE), modified tetrafluoroethylene polymers, modified tetrafluoroethylene-ethylene copolymers, and chlorofluoroethylene polymers (PCTFE), and films of olefinic resins. For good chemical resistance, the inert film is more preferably of a fluorinated resin, still more preferably ETFE or modified ETFE. The inert film is preferably subjected to a treatment for enhancing adhesion to rubber or the like (e.g. chemical treatment or surface roughening treatment).
The kneadate sheet for forming a rubber stopper body is formed of an elastic material. The elastic material of the rubber stopper body is not particularly limited, and examples include rubber materials such as natural rubber, butyl rubber, polyisoprene rubber, polybutadiene rubber, styrene-butadiene rubber, silicone rubber, epichlorohydrin rubber, ethylenepropylene rubber, and nitrile rubber; and thermoplastic elastomers such as polyurethane-based, polyester-based, polyamide-based, olefin-based, and styrene-based thermoplastic elastomers. Preferred among these are materials that become elastic by vulcanization. In the case of vulcanizable materials, compounding agents known in the rubber industry, such as vulcanizing agents (e.g. sulfur) and vulcanization accelerators, may be appropriately added.
The kneadate sheet can be prepared as follows. Compounding materials are mixed at a predetermined ratio using, for example, an internal mixer or open roll mill to give a kneadate, which is then prepared into an unvulcanized rubber sheet using a calendering machine or sheeting machine. Subsequently, an inert film is superposed on the unvulcanized rubber sheet of predetermined weight and size and placed on a mold, followed by vacuum-press molding to obtain a molded sheet including a set of laminated rubber stoppers.
The molding conditions are not particularly limited, and may be selected as appropriate. The molding temperature is preferably 155° C. to 200° C., more preferably 165° C. to 190° C. The molding time is preferably 3 to 15 minutes, more preferably 5 to 10 minutes.
If needed, unnecessary parts may be cut and removed from the molded rubber stopper, and the upper surface of the flange region or the surface laminated with the inert film of the rubber stopper may be coated with a non-reactive or reactive silicone.
Next, the rubber stopper prepared in the molding step is subjected to a groove-forming step that includes forming an annular groove to expose the base rubber on the lower surface of the flange region and/or the outer periphery of the leg portion each laminated with the inert film.
The groove may be formed by methods that can expose the base rubber of the laminate of the inert film and the rubber stopper body material, such as grinding. For the grinding, cutting tools, laser irradiation (laser processing) or other means may be used. Among these, grinding by laser irradiation is suitable because with this method, fine groove structures can be easily formed and also because then there is a smaller influence such as stress around the formation site.
The laser processing allows for suitable formation of an annular groove having a width and depth as described earlier on the outer periphery of the base of the leg portion or on the lower surface of the flange region. In addition, the surface of the inert film is evaporated or decomposed by laser light, and this material is then partially re-accumulated at the edge of the groove to form a projection. Thus, a projection having a width and height as described earlier and elevated above the adjacent surface of the inert film can be suitably formed at at least one edge of the groove. The direction of laser irradiation may be varied to form a projection only at one edge of the groove.
The type, output, and other conditions of laser light may be selected as appropriate. For example, laser processing using infrared light is industrially easy to carry out. The irradiation time may also be selected as appropriate. In order to reduce the influence of heat on the surroundings of the cutting site, short-pulse irradiation is particularly preferred.
The medical rubber stopper of the present invention that may be produced as described above or by other methods is used to seal vials filled with drugs. For example, a vial filled with a drug is capped with the medical rubber stopper and then sealed with an aluminum or resin cap before use.
The present invention is specifically described with reference to, but not limited to, examples.
An inert film with one adhesive-treated surface superposed on an unvulcanized rubber sheet, which are described below, was placed on a forming mold and vulcanization-bonded using a vacuum press at 175° C. for 10 minutes for one step molding to prepare a rubber stopper having the shape described below. Both surfaces were silicone-coated, and burrs were removed. Then, an annular groove having the width and depth listed in Table 1 and a projection having the width and height listed in Table 1 (at the edge of the groove) were formed at the base of the leg portion using a laser device as described below. Then, cleaning, sterilization, and drying were performed to obtain a desired rubber stopper as illustrated in
(Materials and Devices)
Unvulcanized rubber sheet: 100 parts by mass of chlorinated butyl rubber added to 50 parts by mass of a silica-based filler (JIS-A hardness: 45).
Inert film: modified ETFE “AFLEX” (thickness: 75 μm, surface roughness Ra (μm): 0.02 to 0.03 (cut-off value: 0.08, evaluation length: 0.25)) available from Asahi Glass Co., LTD.
Laser device: ML-Z9550T available from Keyence Corporation
(Basic Shape of Rubber Stopper)
Flange region diameter: 19.0 mm (outer diameter), maximum diameter of leg portion: 13.0 mm, flange region thickness: 3.0 mm, thickness of needle penetration site: 2.0 mm
A desired rubber stopper as illustrated in
A desired rubber stopper was prepared in the same manner as in Examples 1 to 3, except that no inert film was used and no groove and no projection located at its edge were formed.
A desired rubber stopper was prepared by conventional two step molding.
(Method for Testing Airtightness)
Among glass vials in various shapes such as those illustrated in
A silica gel desiccant tablet (Yamani chemicals, 0.62 g per tablet) was accurately weighed and placed in a dry and clean 10 ml vial. An aluminum cap was seamed to the vial under normal pressure. The vial was stored in a thermostat at a temperature of 40° C. and a humidity of 75% for a month or three months. Then, the silica gel desiccant was taken out and accurately weighed to determine the weight increase (change in the weight of moisture absorbed by the silica gel desiccant). Table 1 shows the results.
Table 1 shows that the rubber stoppers of the examples as illustrated in
Moreover, the rubber stoppers of the examples exhibited excellent chemical resistance in a test using a liquid drug, and therefore achieved a good balance of excellent airtightness and chemical resistance. Additionally, these rubber stoppers can be produced by one-step molding processes in good productivity.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2016-095486 | May 2016 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3527215 | Witt | Sep 1970 | A |
| 3584770 | Taylor | Jun 1971 | A |
| 4265364 | Baba | May 1981 | A |
| 4386929 | Peery | Jun 1983 | A |
| RE36410 | Meshberg | Nov 1999 | E |
| 8357137 | Yandell | Jan 2013 | B2 |
| 8827977 | Fangrow | Sep 2014 | B2 |
| 9351905 | Fangrow | May 2016 | B2 |
| 20080071243 | Yandell | Mar 2008 | A1 |
| 20100298806 | Yandell | Nov 2010 | A1 |
| 20120248057 | Bogle | Oct 2012 | A1 |
| Number | Date | Country |
|---|---|---|
| 2106084 | Aug 1982 | GB |
| 2004-216753 | Aug 2004 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20170326031 A1 | Nov 2017 | US |