The present invention relates to a method for recording data in an optical recording medium and, particularly, to a method for recording data in a rewritable type optical recording medium whose recording layer contains a phase change material. The present invention also relates to an optical recording medium and, particularly, to a rewritable type optical recording medium whose recording layer contains a phase change material.
Optical recording media such as the CD, DVD and the like have been widely used as recording media for recording digital data and a data recording method for recording data by modulating data to be recorded into lengths of record marks along a track has been widely used. For example, in a DVD-RW, which is a kind of optical recording media in which data can be rewritten by a user, record marks whose lengths correspond to 3T to 11T and 14 T, where T is a clock period, are used for recording data.
When such record marks are to be formed, a laser beam is projected on the optical recording medium along its track, whereby an amorphous region of a predetermined length to be used as a record mark is formed in a recording layer formed of a phase change material in the optical recording medium. Regions other than the amorphous region are crystallized.
When a record mark is to be formed in the recording layer, a laser beam whose power has been set at a sufficiently high level, namely, a recording power Pw, is projected onto the recording layer to heat it to a temperature higher than the melting point thereof and the recording layer is then quickly cooled by changing the power of the laser beam to a sufficiently low level, namely, a ground power Pb. As a result, the phase of the phase change material is changed from a crystal phase to an amorphous phase, thereby forming a record mark. On the other hand, when a record mark is to be erased, a laser beam whose power has been set to a level equal to or lower than the recording power Pw and equal to or higher than the ground power Pb, namely, an erasing power Pe, is projected onto the recording layer to heat it up to a temperature equal to or higher than the crystallization temperature thereof and the recording layer is gradually cooled, whereby the phase of the phase change material is changed from an amorphous phase to a crystal phase and the record mark is erased. Therefore, it is possible not only to form a record mark in an unrecorded region of the recording layer but also to directly overwrite a record mark with a different record mark in a recorded region by modulating the power of the laser beam between a plurality of levels including the recording power Pw, the erasing power Pe and the ground power Pb.
The optimum level of the erasing power Pe mainly depends upon the composition of the phase change material contained in the recording layer as a primary component and, therefore, the optimum level of the erasing power Pe generally changes depending upon the composition of the phase change material contained in the recording layer. For this reason, when an optical recording medium is designed, ordinarily a mixed signal for forming a plurality of record marks is recorded onto the same track of a prototype optical recording medium a plurality of times and the erasing power Pe at which a reflection coefficient of a blank region between record marks neighboring in the direction of a track becomes saturated is determined to be the optimum level of the erasing power Pe.
However, the inventors of the present invention vigorously pursued a study and, as a result, made the discovery that in the case where the erasing power Pe determined by this method is used, jitter of overwritten data may not be good depending upon the linear velocity of data recording (recording linear velocity). Therefore, a good direct overwriting characteristic can be obtained at a certain recording linear velocity while a good direct overwriting characteristic cannot be obtained at another recording linear velocity.
It is therefore an object of the present invention to provide a method for recording data in an optical recording medium with a good direct overwriting characteristic and an optical recording medium in which data can be recorded with a good direct overwriting characteristic.
It is another object of the present invention to provide a method for recording data in an optical recording medium with a good direct overwriting characteristic irrespective of recording linear velocity and an optical recording medium in which data can be recorded with a good direct overwriting characteristic irrespective of recording linear velocity.
In a study carried out by the inventors of the present invention, it was found that even if the recording layers have the exactly the same composition, the relationship between the erasing power Pe and the reflection coefficient of a blank region between record marks neighboring in the direction of a track greatly changes depending upon the recording linear velocity.
The area indicated by the symbol {circle around (1)} in
The area indicated by the symbol {circle around (3)} in
In the case where the direct overwriting is conducted at the linear velocity (low linear velocity) at which the relationship between the erasing power Pe and the reflection coefficient of a region between the record marks neighboring in the direction of a track is as shown in
As can be seen from
Although the reason why jitter property can be most improved by setting the actual erasing power Pe within the area “{circle around (3)}-A” is not clear, it is reasonable to conclude that since the recording layer begins to be melted by a laser beam whose erasing power Pe is in the area “{circle around (3)}-A,” record marks not sufficiently erased by the solid-state erasure at a high linear velocity in the area {circle around (2)} can be desirably erased.
The present invention is directed to solving the above described problems based on this finding. A method for recording data in an optical recording medium according to one aspect of the present invention is adapted for recording data in an optical recording medium including a recording layer containing a phase change material by projecting a laser beam thereonto and comprises the steps of projecting the laser beam onto the recording layer so that the portion of the recording layer onto which the laser beam impinges is continuously moved and modulating the power of the laser beam between a plurality of power levels including at least an erasing power, thereby recording a plurality of record marks in the recording layer, the level of the erasing power being set to a level within an area where a reflection coefficient of a region between record marks neighboring in the direction of a track approaches a reflection coefficient of the record mark as the erasing power increases.
According to this aspect of the present invention, a good overwriting characteristic can be obtained when data are recorded at a high linear velocity, thereby improving jitter property of the thus formed record mark.
In a preferred aspect of the present invention, the plurality of power levels includes a recording power whose level is higher than that of the erasing power and a ground power whose level is lower than that of the erasing power.
In a preferred aspect of the present invention, the optical recording medium is constituted as a “high-to-low” type and the level of the erasing power is set to a level within which the reflection coefficient of a region between record marks neighboring in the direction of a track decreases as the erasing power increases.
A method for recording data in an optical recording medium according to another aspect of the present invention is adapted for recording data in an optical recording medium including a recording layer containing a phase change material by projecting a laser beam thereonto and comprises the steps of projecting the laser beam onto the recording layer so that the portion of the recording layer onto which the laser beam impinges is continuously moved and modulating the power of the laser beam between a plurality of power levels including at least an erasing power, thereby recording a plurality of record marks in the recording layer, the level of the erasing power being set to higher than a level within an area where the reflection coefficient of the region between the record marks neighboring in the direction of a track is not substantially changed even if the erasing power increases and lower than a level within an area where the reflection coefficient of the region between the record marks neighboring in the direction of a track moves away from that of the record mark as the erasing power increases.
A method for recording data in an optical recording medium according to a further aspect of the present invention is adapted for recording data in an optical recording medium by modulating the power of a laser beam between a plurality of power levels including at least erasing power and recording record marks in a recording layer containing a phase change material wherein the erasing power is set to a first level when data are to be recorded at a first linear velocity and the erasing power is set to a second level different from the first level when data are to be recorded at a second linear velocity higher than the first linear velocity. According to this aspect of the present invention, multi-velocity recording of data can be accomplished for an optical recording medium.
In a preferred aspect of the present invention, the first linear velocity is set so that the reflection coefficient of the region between recording marks neighboring in the direction of a track becomes substantially saturated when the erasing power is set to be equal to or higher than a predetermined level and the second linear velocity is set so that the reflection coefficient of the region between the record marks neighboring in the direction of a track approaches the reflection coefficient of the record mark as the erasing power increases when data are recorded at the second linear velocity.
In a further preferred aspect of the present invention, the first level is set so that the reflection coefficient of the region between the record marks neighboring in the direction of a track becomes equal to a first value and the second level is set so that the reflection coefficient of the region between the record marks neighboring in the direction of a track becomes equal to a second value closer to the reflection coefficient of the record mark than the first value is.
An optical recording medium according to one aspect of the present invention is provided with a recording layer which contains a phase change material and in which record marks are to be formed by irradiation with a laser beam and with predetermined information necessary for setting an erasing power of the laser beam to a level within an area where a reflection coefficient of a region between record marks neighboring in the direction of a track approaches the reflection coefficient of the record mark as the erasing power increases.
An optical recording medium according to another aspect of the present invention is provided with a recording layer which contains a phase change material and in which record marks are to be formed by irradiation with a laser beam, and with first predetermined information necessary for setting a level of an erasing power corresponding to a first recording linear velocity and second predetermined information necessary for setting a level of the erasing power corresponding to a second recording linear velocity higher than the first recording linear velocity.
In a preferred aspect of the present invention, when data are recorded at the first recording linear velocity, the reflection coefficient of the region between the record marks neighboring in the direction of a track becomes equal to a first value and when data are recorded at the second recording linear velocity, the reflection coefficient of the region between record marks neighboring in the direction of a track becomes equal to a second value that is closer to the reflection coefficient of the record mark than the first value is.
The above and other objects and features of the present invention will become apparent from the following description made with reference to the accompanying drawings.
Hereinafter, a preferred embodiment of the present invention will be described in detail with reference to accompanying drawings.
As shown in
The translucent substrate 11 constitutes an incident surface of the laser beam and has a thickness of about 0.6 mm. The surface of the translucent substrate 11 on the opposite side from the incident surface is formed with pregrooves (not shown). The material for forming the translucent substrate 11 is not particularly limited and polycarbonate can be used for forming the translucent substrate 11.
The first dielectric layer 12 mainly serves as a protective layer for the recording layer 13 formed thereabove and preferably has a thickness of 40 to 250 nm. The material for forming the first dielectric layer 12 is not particularly limited and the first dielectric layer 12 can be formed of an oxide, nitride, sulfide or carbide of silicon (Si), aluminum (Al), tantalum (Ta), zinc (Zn) or the like, such as SiO2, Si3O4, Al2O3, AlN, TaO, ZnS.
The recording layer 13 is formed of a phase change material and data are recorded in the recording layer 13 utilizing difference in reflection coefficients between crystalline structure and amorphous structure. A region of the recording layer 13 can be changed from a crystalline state to an amorphous state by modulating the power of the laser beam projected from the side of the translucent substrate 11 in accordance with a pulse wave having an amplitude between a recording power Pw and a ground power Pb, heating the region of the recording layer 13 to a temperature equal to or higher than the melting point thereof and quickly cooling the region. As a result, the region of the recording layer 13 melted by the laser beam having the recording power Pw is changed to an amorphous state, thereby forming a record mark. On the other hand, a region of the recording layer 13 can be changed from an amorphous state to a crystalline state by projecting the laser beam having an erasing power Pe from the side of the translucent substrate 11 and heating the region of the recording layer 13 to a temperature equal to or higher than the crystallization temperature thereof. The region heated to a temperature equal to or higher than the crystallization temperature by the laser 4 beam having the erasing power Pe is gradually cooled and the region is changed to a crystalline state.
The recording power Pw, the erasing power Pe and the ground power Pb are set so that the erasing power Pe is lower than the recording power Pw and equal to or higher than the ground power Pb.
Therefore, it is possible not only to form a record mark at an unrecorded region of the recording layer 13 but also to directly overwrite a record mark with a different record mark in a recorded region by modulating the power of the laser beam between a plurality of levels including the recording power Pw, the erasing power Pe and the ground power Pb.
The material for forming the recording layer 13 is not particularly limited but an SbTe system material is preferably used for forming the recording layer 13. As the SbTe system material, SbTe may be used alone or InSbTeGe, AgInSbTe, AgInSbTeGe containing indium (In), tellurium (Te), germanium (Ge) or the like as an additive may be used. The recording layer 13 preferably has a thickness of 10 to 30 nm.
Similarly to the first dielectric layer 12, the second dielectric layer 14 mainly serves as a protective layer for the recording layer 13 and the thickness of the second dielectric layer 14 is preferably 5 to 200 nm, more preferably 10 to 30 nm. The material for forming the second dielectric layer 14 is not particularly limited and the second dielectric layer 12 can be formed of an oxide, nitride, sulfide or carbide of silicon (Si), aluminum (Al), tantalum (Ta), zinc (Zn) or the like, such as SiO2, Si3O4, Al2O3, AlN, TaO, ZnS.
The reflective layer 15 serves to reflect the laser beam projected from the side of the translucent substrate 11 and to emit it through the translucent substrate 11, and preferably has a thickness of 20 to 400 nm. The material for forming the reflective layer 15 is not particularly limited but the reflective layer 15 may be preferably formed of alloy containing silver (Ag) or aluminum (Al) and be formed of gold (Au), platinum (Pt) or the like.
The first dielectric layer 12, the recording layer 13, the second dielectric layer 14 and the reflective layer 15 can be formed by sputtering on the surface of the translucent substrate 11 on which the pregrooves (not shown) are formed.
The protective layer 16 serves to physically and chemically protect the reflective layer 15 and preferably has a thickness of 5 to 50 μm. The material for forming the protective layer 16 is not particularly limited but acrylic resin is preferably used for forming the protective layer 16.
The dummy substrate 17 serves to ensure the mechanical strength required by the optical recording medium 10 and helps to ensure the thickness (about 1.2 mm) required by the optical recording medium 10. It has a thickness of about 0.6 mm. The material for forming the protective layer 17 is not particularly limited but polycarbonate can be used for forming the dummy substrate 17. The dummy substrate 17 is adhered onto the translucent substrate 11 formed with the first dielectric layer 12, the recording layer 13, the second dielectric layer 14, the reflective layer 15 and the protective layer 16 thereon via an adhesive layer (not shown), thereby forming the optical recording medium 10. If the reflective layer 15 can be protected by the adhesive layer, the protective layer 16 can be omitted. The adhesive agent used for forming the adhesive layer is not particularly limited but acrylic resin curable by radical polymerization or cation polymerization in accordance with the object of the adhesive layer and/or the method of fabricating the optical recording medium 10 may be used for forming the adhesive layer.
The optical recording medium 10 shown in
For example, the present invention can be applied to a DVD type optical recording medium fabricated by bonding two translucent substrates 11, each being formed thereon with the first dielectric layer 12, the recording layer 13, the second dielectric layer 14, the reflective layer 15 and the protective layer 16. Further, the present invention can be also applied to a CD type optical recording medium having a translucent substrate having a thickness of about 1.1 mm and no dummy substrate. Moreover, the present invention can be applied to a next-generation type optical recording medium fabricated by employing a dummy substrate having a thickness of about 1.1 mm and formed with pregrooves thereon and providing a very thin light transmission layer having a thickness of 10 to 300 nm instead of the translucent substrate 11.
An overview of a method for recording data in the thus constituted optical recording medium 10 will now be set out.
Although the method is not particularly limited, an 8, 16 modulation method can be used for recording data in the optical recording medium 10 according to this embodiment. In the 8, 16 modulation method, data to be recorded are modulated to record marks having lengths corresponding to 3T to 11T and 14T, where T is one clock period. The modulation method is not limited to the 8, 16 modulation method and data can also be recorded by other modulation methods such as the (1, 7) RLL modulation method.
Next, one example of a pulse pattern of a laser beam used in the 8, 16 modulation method will be described.
As shown in
In the period of Tpulse, high energy is imparted to the recording layer 13 of the optical recording medium 10 and the temperature of the recording layer 13 exceeds the melting point thereof, and in the period Tcl, the recording layer 13 of the optical recording medium 10 is quickly cooled. As a result, a record mark whose length corresponds to 3T is formed in the recording layer 13 of the optical recording medium 10.
In the case of forming record marks having different lengths, similarly to the case of forming a record mark whose length corresponds to 3T, the power of the laser beam for recording data is modulated to Pw, Pe or Pb and a record mark having a desired length is formed by (n−2) number of pulses, where n is a multiple of T and can assume one of 3 to 11 and 14.
Next, the method of setting the erasing power Pe in this embodiment will be described.
As described above, the erasing power Pe is generally set so that, irrespective of the recording linear velocity, the level of the erasing power Pe at which a reflection coefficient of a region (blank region) between record marks neighboring in the direction of a track becomes saturated is optimum. However, in the case of overwriting data using a pulse pattern of the laser beam designed using the erasing power Pe set in this manner, jitter of overwritten data may become worse depending upon the recording linear velocity. Therefore, in this embodiment, the erasing power Pe is set by a different method from that in which the erasing power Pe is set based on the saturation of the reflection coefficient so that jitter of overwritten data is smallest and the erasing power Pe is set in the following manner.
The erasing power Pe is first set at a predetermined level and a mixed signal for forming a plurality of record marks is recorded on the same track a plurality of times. It is preferable to set the number of overwirtings in accordance with Part 1 (PHYSICAL SPECIFICATIONS) of DVD Specifications for Re-recordable Disk and record the mixed signal on the same track ten times.
The reflection coefficients of the track are then measured and the highest reflection coefficient among the thus measured reflection coefficients is defined as the reflection coefficient corresponding to the erasing power Pe. In this case, since the record marks are in the amorphous state and have low reflection coefficients, the highest reflection coefficient must be obtained from a region (blank region) between record marks neighboring in the direction of a track.
This operation is conducted at a fixed recording linear velocity by varying the erasing power Pe and it is judged whether the relationship between the erasing power Pe and the highest reflection coefficient coincides with that shown in
Therefore, when the result of measuring the relationship between the erasing power Pe and the highest reflection coefficient at various recording linear velocities is that the relationship between the erasing power Pe and the highest reflection coefficient coincides with that shown in
It is preferable to store the thus set level of the erasing power Pe together with the corresponding recording linear velocity in the optical recording medium 10 as “predetermined information for setting recording conditions”. If such predetermined information for setting recording conditions is stored in the optical recording medium 10, the predetermined information for setting recording conditions can be read out by a drive when a user actually records data and, therefore, it is possible to adjust the erasing power Pe based on the thus read predetermined information for setting recording conditions. For example, as shown in
It is preferable for the predetermined information for setting recording conditions to include, in addition to the level of the erasing power Pe and the corresponding recording linear velocity, information necessary for identifying various conditions such as the pulse pattern required for recording data in the optical recording medium 10. The predetermined information for setting recording conditions may be recorded as wobbles or prepits and may be recorded in the recording layer 13. The predetermined information for setting recording conditions is not limited to information directly indicating respective conditions necessary for recording data but may be information which can indirectly identify recording conditions by specifying one of the conditions stored in the drive in advance based thereon.
As described above, according to this embodiment, in the case of recording data at a linear velocity at which an area where the reflection coefficient of a region between record marks neighboring in the direction of a track appears between the region where the record mark is erased by the solid state erasure and the area where the record mark is erased by the melt-quench erasure, since the erasing power Pe is set to a level within an area where the reflection coefficient of a region between record marks neighboring in the direction of a track decreases as the erasing power Pe increases and the pulse pattern of the laser beam is designed based on the thus set erasing power Pe, a good direct overwriting characteristic can be obtained.
The present invention has thus been shown and described with reference to specific embodiments. However, it should be noted that the present invention is in no way limited to the details of the described arrangements but changes and modifications may be made without departing from the scope of the appended claims.
For example, in the above described embodiment, although explanation was made as to the case where the present invention is applied to a so-called “high-to-low” type optical recording medium whose reflection coefficient is lowered by the formation of a record mark (amorphous record mark), the present invention can be applied to a so-called low-to-high type optical recording medium in which the reflection coefficient of a recording layer is increased by the formation of a record mark. In this case, as shown in
As described above, according to the present invention, a good direct overwriting characteristic can be obtained.
A good overwrite shelf characteristic, namely, a good rewritable characteristic of a data recorded portion after long-term storage, is required in a rewritable phase change type optical recording medium. According to the present invention, a good overwrite shelf characteristic can be ensured even in the case of conducting direct overwriting at a high linear velocity since the erasing power is raised to higher than usual by setting it to a level within an area where the reflection coefficient of a region between record marks neighboring in the direction of a track approaches the reflection coefficient of a record mark as the erasing power increases.
An optical recording medium sample having the structure shown in
A mixed signal for forming a plurality of record marks was recorded in a predetermined track of the thus fabricated optical recording medium sample by fixing the erasing power Pe of the laser beam at a predetermined level in accordance with the conditions shown in Table 1. As shown in Table 1, the recording linear velocity was 3.5 m/sec (DVD uniform velocity).
Then, the mixed signal for forming a plurality of record marks was recorded on the same track nine times in accordance with the conditions shown in Table 1 and thereafter, clock jitter of the recorded mixed signal was measured. The fluctuation σ of a reproduced signal was measured using a time interval analyzer and the clock jitter was calculated as σ/Tw, where Tw was one clock period.
The recording of the mixed signal and the measurement of jitter were repeated using various pulse patterns of the laser beam and the pulse pattern at which jitter was lowest was identified.
Reflection coefficients of the track in which the mixed signal had been recorded by the pulse pattern at which jitter was lowest were measured and the highest reflection coefficient was defined as a reflection coefficient corresponding to the erasing power Pe. The highest reflection coefficient was measured in a region (blank region) between neighboring record marks.
This operation was repeated at the recording linear velocity of 3.5 m/sec using various erasing powers Pe and the highest reflection coefficient corresponding to each of the erasing powers Pe was measured.
Thus, it was confirmed that when data were recorded (overwritten) in the optical recording medium at the recording linear velocity of 3.5 m/sec, a good direct overwriting characteristic was obtained by setting the erasing power Pe slightly higher than the level at which the highest reflection coefficient saturated.
The highest reflection coefficient was measured using the optical recording medium sample used in Working Example 1 in the manner of Working Example 1, except that the recording conditions shown in Table 2 were employed. As shown in Table 2, the recording linear velocity was 7.0 m/sec (DVD double velocity).
It can be seen from
Thus, it was confirmed that when data were recorded (overwritten) in the optical recording medium at the recording linear velocity of 7.0 m/sec, a good direct overwriting characteristic was obtained by setting the erasing power Pe to a level within the area where the highest reflection coefficient decreased as the erasing power Pe increased.
Number | Date | Country | Kind |
---|---|---|---|
2002-025618 | Feb 2002 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
5276670 | Nogami et al. | Jan 1994 | A |
5848043 | Takada et al. | Dec 1998 | A |
6096400 | Inoue et al. | Aug 2000 | A |
6154437 | Utsunomiya et al. | Nov 2000 | A |
6459666 | Yokoi | Oct 2002 | B1 |
6770346 | Harigaya et al. | Aug 2004 | B1 |
6886177 | Katoh et al. | Apr 2005 | B1 |
20020105875 | Ushiyama et al. | Aug 2002 | A1 |
20030086345 | Ueki | May 2003 | A1 |
20060044968 | Narumi et al. | Mar 2006 | A1 |
Number | Date | Country |
---|---|---|
2002-245663 | Aug 2002 | JP |
Number | Date | Country | |
---|---|---|---|
20040053076 A1 | Mar 2004 | US |