1. Technical Field
The present invention relates to a part useful for casting that is obtained by converting base paper for paper tubing into a tube, a process of producing the part, and a casting production method using the part.
2. Background Art
Casting production generally involves forming a casting mold having a cavity (and, if necessary, a core) from casting sand, forming a pouring cup, a sprue, a channel and a gate to make a passage leading to the cavity through which molten metal is fed to the cavity (these parts will hereinafter be inclusively referred to as a gating system), and additionally forming a vent, a feeder, and a flow-off which lead to the outside. The gating system, vent, feeder, and flow-off are formed integrally with the mold, or the gating system is assembled from parts separately made of refractories such as earthenware and brick.
Where a mold and a gating system, etc. are integrally formed, it is difficult to design the gating system in a intricate configuration, and sand enters molten metal easily. Where, on the other hand, parts made of refractories are used to set up the gating system, etc., molten metal is liable to experience a temperature drop on contact with the gating system, etc. Moreover, assembly of the refractory parts into a gating system, etc. is troublesome, involving cutting refractories with a high-speed cutter, e.g., a diamond cutter, and joining the cut pieces by tape winding. In addition, after filling, the refractory gating system, etc. break due to thermal shock and the like to produce a large quantity of industrial waste, the disposal of which is labor intensive. In general, a gating system made of refractories is inconvenient to handle.
The technique disclosed in JP-A-U-1-60742 (Japanese utility model laid-open publication) is among known methods addressing these problems. According to this technique, a heat-insulating material obtained by molding a slurry comprising organic or inorganic fiber and an organic binder is used to make parts forming a gating system in place of refractories.
However, a gating system, etc. molded from a combination of organic fiber and an organic binder largely shrinks due to thermal decomposition on feeding molten metal, which can lead to leakage of the molten metal from the gating system, etc. Where inorganic fiber and an inorganic binder are combined, it is difficult to mold into a heat-insulating material having a three-dimensional shape (e.g., a hollow shape), resulting in a failure to make a gating system, etc. matching various cavity shapes.
It is also known to use a paper core for casting produced from a material having a reduced cellulose fiber content by mixing inorganic powder and/or inorganic fiber into cellulose fiber (see, e.g., JP-A-9-253792). The paper core can be produced with suppressed shrinkage on drying. By use of this core, generation of gas or tar-like polymers from cellulose fiber during casting can be suppressed. As a result, casting deflects are prevented, and casting workability is improved.
Notwithstanding these advantages, the paper core according to that technique contains no binder and is therefore not suited for use in a gating system, etc. applied to various cavity shapes.
Accordingly an object of the present invention is to provide a part for use in the production of castings which is less liable to thermal shrinkage due to thermal decomposition, easy to handle, and configured to constitute a gating system, etc. applicable to various cavity shapes, a process of producing the part, and a casting production method using the part.
The present invention accomplishes the above object by providing a part for casting obtained by converting base paper for paper tubing into a tube and containing an organic fiber, carbon fiber, and a binder.
The present invention also provides a method of producing a casting using a part for casting containing an organic fiber, carbon fiber, and a binder. The part is disposed in casting sand.
The present invention also provides a process of producing the part for casting according to the invention. The process includes the steps of making base paper for paper tubing by papermaking using a slurry containing at least the organic fiber and the carbon fiber, converting the base paper into a paper tube, and impregnating the paper tube with the binder.
The present invention will be described with reference to its preferred embodiments.
The part for casting according to the present invention is obtained by converting base paper for paper tubing into a tubular form and contains an organic fiber, carbon fiber, and a binder. The part for casting is preferably formed by winding base paper. The base paper can be wound with or without an overlap between adjacent turns. A plurality of base papers may be wound one on top of another. A long, cylindrical part for casting is preferably formed by spirally winding a strip of base paper. The part for casting of the invention may be formed otherwise than winding. For example, a rectangular base paper for paper tubing is curled into a cylinder, and the opposing two sides are joined. Taking the strength required of a part for casting into consideration, the thickness of the base paper for paper tubing is preferably 0.4 to 2 mm, more preferably 0.7 to 1.5 mm.
The organic fiber functions mainly to form the skeleton of the part. On casting, part of the whole of the organic fiber decomposes by the heat of molten metal to leave voids in the part after casting production.
The organic fiber includes paper fiber and fibrillated synthetic fiber or regenerated fibers (e.g., rayon fiber) or etc. These fibers are used either individually or as a mixture of two or more thereof. Preferred of them is paper fiber for the following reasons. Paper fiber is easily and stably supplied and therefore contributory to reduction of production cost. Paper fiber provides sufficient strength after dewatering and drying.
The paper fiber includes not only wood pulp but non-wood pulp, such as cotton pulp, linter pulp, bamboo, and straw. Virgin pulp or used paper (recycled) pulp can be used either alone or in combination thereof. From the standpoint of ease and stability of supply, environmental conservation, reduction of production cost and etc., used paper pulp is preferred.
It is preferred for the organic fiber to have an average length of 0.8 to 2.0 mm, more preferably 0.9 to 1.8 mm, from the viewpoint of surface smoothness, impact strength, thickness uniformity and the like of the resulting part.
The content of the organic fiber in the part for casting of the present invention is preferably 10 to 70 parts by weight, more preferably 20 to 60 parts by weight, in view of ease of conversion into a desired part, for securing strength as part for casting, for reducing gas generation and etc. The unit “part(s) by weight” as used throughout the description is based on 100 parts by weight of the total amount of an organic fiber, carbon fiber, and a binder.
The carbon fiber serves mainly to form the skeleton of the part for casting similarly to the above-described organic fiber. On casting molten metal, it does not decompose nor burn even with the heat of the molten metal and continues serving to retain the original shape of the part.
When in using an organic binder as a binder, carbon fiber maintains high strength even in high temperatures, and is preferred for reducing thermal shrinkage accompanying carbonization of the organic binder.
The carbon fiber preferably has an average length of 0.2 to 10 mm, more preferably 0.5 to 8 mm, in order to secure good drainage in papermaking process, processability of the resulting base paper for paper tubing, and the like.
The content of the carbon fiber is preferably 1 to 80 parts by weight, more preferably 7 to 40 parts by weight, taking into consideration strength as a part for casting, processability of the resulting base paper for paper tubing, and the like.
The weight ratio of the carbon fiber to the organic fiber (i.e., carbon fiber content/organic fiber content) is preferably 1 to 60, more preferably 2 to 30, in the case of using carbon fiber for ease of conversion as a part for casting, securing strength and the like.
The binder includes organic ones and inorganic ones as hereinafter described. The organic and the inorganic binders can be used either individually or as a mixture thereof.
The organic binders include such kinds as those serving to bind the organic fiber and the carbon fiber of the part for casting and those which enhance the strength of the part and, on casting, carbonize by the heat of molten metal to maintain the strength of the part.
The organic binders include thermosetting resins, such as phenol resins, epoxy resins, and furan resins. Preferred of them are phenol resins in view of reduced generation of combustible gas, resistance to burning, a high carbon residue content after thermal decomposition (carbonization) and the like. Of the phenol resins more preferred are resol type ones that require no curing agent and can impregnate into a part for casting of the present invention.
The inorganic binders include those capable of binding the organic fiber and the carbon fiber of the part for casting, those which do not thermally decompose on casting thereby reducing generation of combustion gas or flame, those effective in inhibiting carburizing on casting and etc.
The inorganic binders include compounds mainly comprising SiO2, such as colloidal silica, obsidian, mullite, perlite, ethyl silicate, and water glass. Among them colloidal silica is preferred in view of its independent utility, ease of application and the like, and obsidian is preferred for prevention of carburizing. The inorganic binders can be used either individually or as a mixture of two or more thereof.
The binder content (on a solid basis) preferably ranges 10 to 85 parts by weight, more preferably 20 to 80 parts by weight, for securing strength as a part for casting, ease of conversion, and the like.
In using a binder other than obsidian, the content of the binder in the part for casting is preferably 10 to 70 parts by weight, more preferably 20 to 50 parts by weight. In using obsidian as a binder, it is preferably used in an amount of at least 20 parts by weight based on the total binder content. The binder may consist solely of obsidian.
Two or more kinds of binders different in melting point can be used in combination. In order to retain the shape of the parts in an temperature range of from ambient temperature (before casting) to high temperature (during casting), to prevent carburizing during casting and the like, it is preferred to use a low-melting binder and a high-melting binder in combination. In this case, the low-melting binder includes clay, water glass, obsidian or etc., and the high-melting binder includes the above-recited compounds mainly comprising SiO2, mullite, wollastonite, Al2O3 and etc.
The part for casting according to the present invention can contain a paper strengthening agent. When a paper tube is impregnated with a binder, the paper strengthening agent added reduces a swell of the paper tube.
A preferred amount of the paper strengthening agent to be added is 1% to 20%, more preferably 2% to 10%, based on the weight of the organic fiber.
The paper strengthening agent includes polyvinyl alcohol, carboxymethyl cellulose (CMC), Kymene (polyamideamine-epichlorohydrin resin) and etc.
The part for casting according to the present invention can further contain other additives such as a flocculant and a colorant.
The thickness of the part for casting is subject to variation according to where it is applied. For example, the portion which comes into contact with molten metal preferably has a thickness of 0.2 to 2 mm, more preferably 0.4 to 1.5 mm, for securing strength required of a part for casting while securing air permeability, reducing the production cost, and the like.
To secure strength, the part for casting preferably has a compressive strength of 10 N or higher, more preferably 30 N or higher before use in casting.
It is preferred for the part before use in casting to have a water content of not more than 10% by weight, more preferably 8% by weight or less, in order to minimize gas generation accompanying thermal decomposition of the organic binder.
The density of the part for casting is preferably 0.5 g/cm3 or higher, more preferably 0.6 to 1.2 g/cm3, from the standpoint of strength, light weight, processability, and the like.
The process of producing the part for casting will then be described.
A slurry is prepared by dispersing the organic and the carbon fibers and the binder in a prescribed dispersing medium. It is possible to exclude the binder from the composition of the slurry, if desired, because the binder may be incorporated by impregnation into base paper for paper tubing obtained by papermaking, dewatering and drying or into a paper tube formed from the base paper.
The dispersing medium includes water, white water, solvents such as ethanol and methanol, and etc. Water is particularly preferred in view of stability in papermaking and dewatering, stability of quality of the resulting base paper, cost, ease of handling, and the like.
The slurry preferably contains the organic fiber in an amount of 0.1% to 3% by weight, more preferably 0.5% to 2% by weight, based on the dispersing medium in view of surface smoothness, thickness uniformity, etc. of the resulting base paper for paper tubing.
If desired, the slurry can contain additives including a flocculant, an antiseptic and etc.
The slurry is then converted into base paper for paper tubing by a papermaking process.
Papermaking can be carried out by any technique selected from, for example, continuous papermaking methods using a cylinder paper machine, a Fourdrinier paper machine, a short-wire paper machine or a twin-wire paper machine, and batchwise papermaking methods including manual papermaking.
In order for the base paper for paper tubing to keep the shape retention and mechanical strength after papermaking, the base paper for paper tubing is dewatered to reduce its water content (water content by weight, hereinafter the same) preferably to 70% or smaller, more preferably to 60% or smaller. Dewatering of the base paper after papermaking can be conducted by, for example, suction, blowing pressurized air or pressing with a pressure roll or a pressure plate.
The dewatered base paper for paper tubing is forwarded to a drying step. Any means for drying that has conventionally been used to dry paper can be used in the drying step.
The resulting base paper for paper tubing is slit into strips of prescribed width, which are wound in a helix pattern to produce a spiral-wound paper tube having a multilayer structure.
When necessary, a part or the whole of the resulting paper tube is impregnated with a binder. Binders to be infiltrated into the paper tube include resol type phenol resins, colloidal silica, ethyl silicate, water glass and etc.
Where the paper tube is impregnated with a binder, it is possible to omit addition of a binder to the slurry.
Finally, the paper tube is dried by heating at a predetermined temperature to complete production of a paper tube. It is possible that conversion of base paper into a paper tube is preceded by impregnation of the base paper with a binder.
The part for casting according to the present invention is useful as a sprue as in the embodiment shown in
The casting production method of the present invention will be described based on an embodiment in which the above-mentioned sprue is used.
As shown in
The assembled parts for casting are buried in casting sand (not shown). Molten metal having a prescribed composition is fed to the cavity of the mold 9 through the gating system. Where the part for casting contains an organic binder, the binder and the organic fiber thermally decompose and carbonize by the heat of the molten metal, but the strength required as a part for casting is maintained. Because the inorganic fiber suppresses thermal shrinkage of the part due to the thermal decomposition, the part is prevented from cracking or flowing away together with the molten metal so that incorporation of casting sand and the like into the molten metal does not occur. After the casing mold is broken to take out the casting product, it is easy to remove the part from the mold because the organic fiber has decomposed thermally.
Casting sands conventionally employed for casting can be used without particular restriction.
After completion of mold filling, the mold is cooled to a prescribed temperature. The casting sand is removed, and the casting is subjected to blasting. Unnecessary parts such as the gating system parts are also removed. If needed, the casing is finished by trimming and the like to complete casting production.
As described, the part for casting of the aforementioned embodiment and a casting production method using the part offer the following advantages. The organic fiber decomposes by the heat of molten metal to leave voids inside of the part for casting, while the carbon fiber and the binder maintain strength required of a part for casting. After destruction of the casting mold, the part can easily be separated and removed. In other words, the use of the organic fiber, carbon fiber, and binder provides a part for casting that retains strength required of a part for casting during the casting mold formation and casting and reduces its strength in destroying the mold. Accordingly, the method of casting production of the present invention simplifies disposal of used parts for casting and greatly reduces the waste itself as compared with the conventional casting method using the parts made of refractories.
Since the part for casting according to the present invention contains an organic fiber, carbon fiber, and a binder, it produces a smaller amount of flame on filling than a part for casting made solely of an organic fiber. The part for casting of the present invention is prevented from reducing its strength due to combustion of the organic fiber, cracking due to thermal shrinkage accompanying thermal decomposition (carbonization) of the organic binder and the like. As a result, the defect of products due to contamination of casting sand into the molten metal can be avoided.
Having air permeability, the part of the present invention allows gas generated on pouring to escape toward the casting sand side. Production of defective castings attributed to so-called blow holes (or pin holes) and the like is thus prevented.
The part for casting according to the present invention is lightweight and easy to cut with a simple tool and is therefore excellent in handling properties.
The present invention is not limited to the above-described embodiments, and various changes and modifications can be made therein without departing from the spirit and scope thereof.
The part for casting according to the present invention can be used as not only the sprue 1 as in the above-described embodiment but the pouring cup, the runner, the gate, the vent, the feeders, and the flow-off (numerals 2 to 8) which are shown in
The method for casting production according to the present invention is applicable to not only cast iron but casting of nonferrous metals, such as aluminum and its alloys, copper and its alloys, nickel, and lead.
The present invention will now be illustrated in greater detail with reference to Example.
A slurry shown below was converted into paper, dewatered, and dried to obtain base paper for paper tubing having a thickness of 1 mm and a basis weight of 440 g/m2. The base paper was converted into a paper tube in the manner described below to obtain a sprue (a part for casting) weighing about 30 g and having the physical properties shown below.
The organic fiber and the carbon fiber described below were dispersed in water to prepare an about 1% slurry (a total weight of the organic and the carbon fibers was 1% by weight with respect to water). The binder and the flocculant shown below were added to the slurry to prepare a stock. The mixing weight ratio of the organic fiber, carbon fiber and binder was as shown below.
The slurry was converted into a wet paper sheet on a tilted short-wire paper machine at a line speed of 1.5 m/min.
The paper sheet was held in between two felt pads and dewatered by suction and then passed between heating rolls of 120° C. at a line speed of 1.5 m/min to reduce the water content to 5% by weight or less.
The resulting base paper was slit to obtain strips of five widths: 54.4 mm, 54.8 mm, 55.2 mm, 55.6 mm, and 56.0 mm. The strip of the smallest width was spirally wound into a tube. The other strips of four widths were spirally wound around the tube in succession in ascending order of width to obtain a paper tube having an inner diameter of about 30 mm and a density of 1.0 g/cm3. The strips were adhered to each other with an adhesive.
The paper tube was dried in a drying oven at 200° C. for about 60 minutes to obtain a sprue.
A gating system as shown in
Neither blowback in the pouring cup nor vigorous flaming from the flow-off was observed. After casting, the mold was broken to find the sprue covering the solidified metal neatly. The sprue was easily removed by blasting.
As described, it was confirmed that the sprue (part for casting) obtained in Example 1 was prevented from thermal shrinkage accompanying thermal decomposition and was excellent in handling properties.
The present invention provides a part for casting that is prevented from thermal shrinkage accompanying thermal decomposition and is excellent in handling properties; a process of producing the part; and a method for casting production using the part.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2002-329787 | Nov 2002 | JP | national |
| 2003-379397 | Nov 2003 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP03/14314 | 11/11/2003 | WO | 00 | 10/13/2005 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2004/043627 | 5/27/2004 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 1925584 | Fisher | Sep 1933 | A |
| 2006392 | Greider et al. | Jul 1935 | A |
| 2269455 | Hagemeyer | Jan 1942 | A |
| 2971877 | Arledter | Feb 1961 | A |
| 3006805 | Waggoner | Oct 1961 | A |
| 3236719 | Waggoner | Feb 1966 | A |
| 3418203 | Asunmaa | Dec 1968 | A |
| 3773513 | MacClaren | Nov 1973 | A |
| 3844337 | Bessett et al. | Oct 1974 | A |
| 4069859 | Nagai et al. | Jan 1978 | A |
| 4081168 | Atterbury et al. | Mar 1978 | A |
| 4251320 | Cederqvist et al. | Feb 1981 | A |
| 4256801 | Chuluda | Mar 1981 | A |
| 4291781 | Niguchi et al. | Sep 1981 | A |
| 4356994 | Thornton | Nov 1982 | A |
| 4789430 | Fredenucci | Dec 1988 | A |
| 4923665 | Andersen et al. | May 1990 | A |
| 4981166 | Brown et al. | Jan 1991 | A |
| 5205340 | Brown et al. | Apr 1993 | A |
| 5272006 | Maine | Dec 1993 | A |
| 5569320 | Sasaki et al. | Oct 1996 | A |
| 5611848 | Sasaki et al. | Mar 1997 | A |
| 5830548 | Andersen et al. | Nov 1998 | A |
| 5906712 | Asami et al. | May 1999 | A |
| 5983268 | Freivald et al. | Nov 1999 | A |
| 5989390 | Lee | Nov 1999 | A |
| 5997785 | Skjelmose | Dec 1999 | A |
| 6264045 | Wilson et al. | Jul 2001 | B1 |
| 6278448 | Brown et al. | Aug 2001 | B1 |
| 6331358 | Kitahara et al. | Dec 2001 | B1 |
| 6335387 | Twardowska et al. | Jan 2002 | B1 |
| 6488811 | Dong | Dec 2002 | B1 |
| 6521085 | Kumamoto et al. | Feb 2003 | B2 |
| 6533897 | Wang et al. | Mar 2003 | B2 |
| 6540874 | Ling-Chen | Apr 2003 | B1 |
| 6616802 | Kinsley et al. | Sep 2003 | B1 |
| 6616804 | Foster et al. | Sep 2003 | B2 |
| 6733628 | Dinwoodie et al. | May 2004 | B2 |
| 6841041 | Kumamoto et al. | Jan 2005 | B2 |
| 6918997 | Goto et al. | Jul 2005 | B2 |
| 7067041 | Tsuura et al. | Jun 2006 | B2 |
| 7077933 | Otani et al. | Jul 2006 | B2 |
| 7297232 | Tsuura et al. | Nov 2007 | B2 |
| 20010040016 | Kumanoto et al. | Nov 2001 | A1 |
| 20020174963 | Wang et al. | Nov 2002 | A1 |
| 20020189776 | Kumamoto et al. | Dec 2002 | A1 |
| 20030029591 | Otani et al. | Feb 2003 | A1 |
| 20030121635 | Kumamoto et al. | Jul 2003 | A1 |
| 20030145968 | Kumamoto et al. | Aug 2003 | A1 |
| 20030150582 | Tsuura et al. | Aug 2003 | A1 |
| 20030150583 | Goto et al. | Aug 2003 | A1 |
| 20030209337 | Nonomura | Nov 2003 | A1 |
| 20040011489 | Kimbara et al. | Jan 2004 | A1 |
| 20040041305 | Tsuura et al. | Mar 2004 | A1 |
| 20040045690 | Eto et al. | Mar 2004 | A1 |
| 20040069429 | Tsuura et al. | Apr 2004 | A1 |
| 20060005937 | Sakaguchi et al. | Jan 2006 | A1 |
| 20060130987 | Tsuura et al. | Jun 2006 | A1 |
| Number | Date | Country |
|---|---|---|
| 713368 | Aug 1968 | BE |
| 1041715 | May 1990 | CN |
| 1167020 | Dec 1997 | CN |
| 2632880 | Feb 1977 | DE |
| 3039935 | May 1982 | DE |
| 0 062 193 | Oct 1982 | EP |
| 1 488 871 | Dec 2004 | EP |
| 1577034 | Sep 2005 | EP |
| 2085544 | Dec 1971 | FR |
| 2 246 516 | May 1975 | FR |
| 2475970 | Aug 1981 | FR |
| 2 047 766 | Dec 1980 | GB |
| 2047766 | Dec 1980 | GB |
| 43-13441 | Jun 1968 | JP |
| 49-125222 | Nov 1974 | JP |
| 50-77415 | Jun 1975 | JP |
| 50-20545 | Jul 1975 | JP |
| 51-1286 | Jan 1976 | JP |
| 53-48026 | May 1978 | JP |
| 57-177846 | Jan 1982 | JP |
| 57-190747 | Nov 1982 | JP |
| 59-165743 | Nov 1984 | JP |
| 62-89758 | Apr 1987 | JP |
| 63-295037 | Dec 1988 | JP |
| 1-60742 | Apr 1989 | JP |
| 1-262041 | Oct 1989 | JP |
| 1-278935 | Nov 1989 | JP |
| 1-1278935 | Nov 1989 | JP |
| 5-31128 | Feb 1993 | JP |
| 6-327704 | Nov 1994 | JP |
| 08-267222 | Oct 1996 | JP |
| 9-253792 | Sep 1997 | JP |
| 11-254091 | Sep 1999 | JP |
| 11-254091 | Sep 1999 | JP |
| 2004-195547 | Jul 2004 | JP |
| 0128008 | Apr 1998 | KR |
| 5-31128 | Feb 1993 | WO |
| 0058556 | Oct 2000 | WO |
| 0164527 | Sep 2001 | WO |
| 3076104 | Sep 2003 | WO |
| 2004-043627 | May 2004 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20060130987 A1 | Jun 2006 | US |