Patent Application
20060228571
The present invention relates to a member of a plasma processing apparatus, a member of a processing apparatus, a plasma processing apparatus, a processing apparatus and a method of plasma processing.
For a member, for example, a chamber, used in an apparatus performing plasma processing, an aluminum alloy is used in consideration of its weight reduction, and in order to prevent an inner wall of the chamber from being corroded by active species such as ions and by corrosive gas when various kinds of gases are dissociated by plasma, the inner wall of the chamber is subjected to oxidation processing in advance so that a corrosion-resistant coating film of Al2O3 is formed on its surface.
The aforesaid oxidation processing has been conventionally applied by a method called anodic oxidation processing (for example, Japanese Patent Application Laid-open No. Hei 7-216589).
The coating film of Al2O3 formed by the anodic oxidation processing is basically a porous film and its surface has irregularities. Therefore, post processing such as the filling of pores is applied to the coating film in a manner such that, for example, the coating film is exposed to high-temperature vapor so that molecules of the film absorb moisture to expand.
However, even with such post processing, if the anodically oxidized aluminum alloy is used for the chamber of a process vessel of the plasma apparatus that generally performs the processing under a high degree of reduced pressure, it takes a very long time to reach a predetermined degree of the reduced pressure. This is a phenomenon prominently seen at the start-up time of the apparatus.
This is because the oxide coating film formed on the surface of the anodically oxidized aluminum alloy is inherently porous and thus has a problem of outgas and includes pores formed and remaining therein, so that it takes an excessively long time for vacuuming to the predetermined degree of reduced pressure.
The present invention was made in consideration of these respects, and its object is to realize the formation of a coating film that is denser and has a more improved corrosion resistance than a conventional coating film, on various kinds of members used in a plasma processing apparatus and a processing apparatus, such as chambers of these processing apparatuses, and further on the apparatuses themselves. It is another object to provide a method of plasma processing suitable for forming such a coating film.
In order to achieve the objects stated above, a member of a plasma processing apparatus of the present invention is a member which is used in a plasma processing apparatus applying plasma processing and at least part of which is exposed to plasma, the member being made of aluminum or an aluminum alloy and including an oxide coating film on a surface of the part exposed to the plasma, and the oxide coating film being formed through oxidation by plasma processing.
A possible example of the oxide coating film formed through the oxidation by the plasma processing is an oxide coating film formed through oxidation by, for example, an oxygen radical generated by plasma.
According to findings by the inventors, an oxide coating film formed on a surface of aluminum or an aluminum alloy by plasma processing, for example, by an oxygen radical generated by plasma, has properties of being extremely dense and having a flat surface, and few pore exists in the film. Further, it has been found out that the abovementioned oxide coating film is strong and has improved corrosion resistance. Therefore, a member having such a coating film is very much suitable as a member exposed to the plasma. When the member having undergone such processing is used as a constituent member of a chamber of various kinds of pressure-reduced apparatuses, such as a process vessel of a plasma processing apparatus, it is possible to shorten the time required for vacuuming to a predetermined degree of reduced pressure, compared with the time conventionally required. The oxidation by the oxygen radical, which will be described later, is realized by, for example, turning oxygen-containing gas into plasma to thereby apply the plasma processing to the surface of the aluminum or aluminum alloy.
Examples of the member as the object of the present invention are, besides the aforesaid chamber, a mounting table to place a substrate thereon, an electrode, a gate valve, and an exhaust pipe used for exhausting the inside of the chamber.
A member of a plasma processing apparatus of the present invention may be a member made of aluminum or an aluminum alloy and including an oxide coating film of aluminum or an aluminum alloy on a surface of a part exposed to plasma, the oxide coating film containing a minute amount of a rare gas component. When the rare gas is contained, a film stress is alleviated and adhesiveness and reliability are improved. As the rare gas, krypton (Kr) gas is especially preferable.
According to another aspect, a member of a plasma processing apparatus of the present invention may be a member made of an aluminum alloy containing, besides aluminum, at least one of magnesium, strontium, and barium, and including an oxide coating film on a part exposed to plasma, wherein the oxide coating film includes an aluminum oxide and at least one of a magnesium oxide, a strontium oxide, and a barium oxide. The member of the plasma processing apparatus described above has a further improved corrosion resistance.
The aluminum alloy may contain at least zirconium, or contain at least hafnium. When either of them is contained, mechanical strength is improved.
Furthermore, a content ratio of each of Fe, Mn, Cr, and Zn in the aluminum alloy is preferably 0.01 weight % or less. This is because containing a large amount of any of these metals leads to deterioration in the corrosion resistance.
Because of the above-described properties of the oxide coating film, it is also possible to propose a member which is used in a processing apparatus applying processing to a processing target in a process vessel by using a highly reactive gas or chemical solution and at least part of which is exposed to the gas or chemical solution.
Specifically, a member of a processing apparatus of the present invention is a member which is used in a processing apparatus applying processing to a processing target in a process vessel by using a highly reactive gas or chemical solution and at least part of which is exposed to the gas or chemical solution, the member being made of aluminum or an aluminum alloy and including an oxide coating film on a surface of the part exposed to the gas or chemical solution, and the oxide coating film being formed through oxidation by plasma processing.
A possible example of the oxide coating film formed through the oxidation by the plasma processing is an oxide coating film formed through oxidation by, for example, an oxygen radical generated by plasma.
Possible examples of the highly reactive gas or chemical solution are Chlorine gas, Fluorine gas, HCl, H2SO4, and HF. Further, besides the aforementioned chamber, mounting table, and gate valve, possible examples of the member exposed to the gas or chemical solution are a chemical solution tank, various pipes such as a supply pipe and an exhaust pipe, a member (for example, a blade) of a pump for exhaust, and a valve.
Examples of the processing apparatus are those used in manufacturing electronics devices such as a semiconductor device and a liquid crystal display device, and include: processing apparatuses such as an etching apparatus, a deposition apparatus, other electronic device manufacturing apparatuses in general, a cleaning apparatus using a chemical solution for cleaning, and various kinds of heating apparatuses; and a plasma processing apparatus applying plasma processing by generating plasma.
Further, a member of a processing apparatus of the present invention may be a member made of aluminum or an aluminum alloy and including an oxide coating film of aluminum or an aluminum alloy on a surface of a part exposed to plasma, the oxide coating film containing a minute amount of a rare gas component.
As previously described, when the rare gas is contained, a film stress is alleviated and adhesiveness and reliability are improved. Krypton (Kr) gas is preferable as the rare gas.
Furthermore, a member of a processing apparatus of the present invention may be a member made of an aluminum alloy containing, besides aluminum, at least one of magnesium, strontium, and barium, and including an oxide coating film on a surface of a part exposed to plasma, wherein the oxide coating film includes an aluminum oxide and at least one of a magnesium oxide, a strontium oxide, and a barium oxide. Such composition achieves further improvement in the corrosion resistance.
The aluminum alloy may contain at least zirconium, or contain at least hafnium. When either of them is contained, mechanical strength is improved.
Furthermore, a content ratio of each of Fe, Mn, Cr, and Zn in the aluminum alloy is preferably 0.01 weight % or less. This is because containing a large amount of any of these metals leads to deterioration in the corrosion resistance.
A plasma processing apparatus of the present invention is a plasma processing apparatus applying plasma processing to a substrate in a process vessel, the apparatus including a member which is exposed to plasma and at least part of which is made of aluminum or an aluminum alloy and includes an oxide coating film on a surface of the aluminum or aluminum alloy, the oxide coating film being formed through oxidation by plasma processing.
A possible example of the oxide coating film formed through the oxidation by the plasma processing is an oxide coating film formed through oxidation by, for example, an oxygen radical generated by plasma.
According to another aspect, the present invention is a plasma processing apparatus applying plasma processing to a substrate in a process vessel, the apparatus including a member which is exposed to plasma and at least part of which is made of aluminum or an aluminum alloy and comprises an oxide coating film of aluminum or an aluminum alloy on a surface of the aluminum or aluminum alloy, the oxide coating film containing a minute amount of a rare gas component. As the rare gas, krypton (Kr) gas is preferable.
According to another aspect, the present invention is a plasma processing apparatus applying plasma processing to a substrate in a process vessel, the apparatus including a member which is exposed to plasma and at least part of which is made of an aluminum alloy containing, besides aluminum, at least one of magnesium, strontium, and barium, and includes an oxide coating film on a surface of the aluminum alloy, wherein the oxide coating film includes an aluminum oxide and at least one of a magnesium oxide, a strontium oxide, and a barium oxide.
The aluminum alloy may contain at least zirconium, or contain at least hafnium. When either of them is contained, mechanical strength is improved.
A content ratio of each of Fe, Mn, Cr, and Zn in the aluminum alloy is preferably 0.01 weight % or less. This is because containing a large amount of any of these metals leads to deterioration in the corrosion resistance.
According to yet another aspect, the present invention is a processing apparatus applying processing to a processing target in a process vessel by using highly reactive gas or chemical solution, the apparatus including a member which is exposed to the gas or chemical solution and at least part of which is made of aluminum or an aluminum alloy and includes an oxide coating film on a surface of the aluminum or aluminum alloy, the oxide coating film being formed through oxidation by plasma processing.
A possible example of the oxide coating film formed through the oxidation by the plasma processing is an oxide coating film formed through oxidation by, for example, an oxygen radical generated by plasma.
At least part of the member which is exposed to the gas or chemical solution may be made of aluminum or an aluminum alloy and may include an oxide coating film of aluminum or an aluminum alloy on a surface of the aluminum or aluminum alloy, the oxide coating film containing a minute amount of a rare gas component. As the rare gas, krypton (Kr) gas is preferable.
Furthermore, at least part of the member which is exposed to the gas or chemical solution may be made of an aluminum alloy containing at least one of magnesium, strontium, and barium, and may include an oxide coating film on a surface of the aluminum alloy, wherein the oxide coating film includes an aluminum oxide and at least one of a magnesium oxide, a strontium oxide, and a barium oxide.
The aluminum alloy may contain at least zirconium, or contain at least hafnium. When either of them is contained, mechanical strength is improved.
A content ratio of each of Fe, Mn, Cr, and Zn in the aluminum alloy is 0.01 weight % or less. This is because containing a large amount of any of these metals leads to deterioration in the corrosion resistance.
A method of plasma processing of the present invention is a method for applying plasma processing to a processing target in a process vessel, the method comprising the step of, while keeping a temperature of the processing target made of aluminum or an aluminum alloy in the process vessel at 450° C. or lower, applying oxidation processing to a surface of the processing target in the process vessel by an oxygen radical generated by plasma.
According to findings by the inventors, when plasma was generated by using, for example, krypton-containing oxygen gas, it was possible to apply suitable oxidation processing to a processing target made of aluminum or an aluminum alloy, by an oxygen radical generated by the plasma even when the processing target was kept at room temperature (for example, 23° C.), and as a result, it was possible to form, on a surface of the processing target, a coating film of Al2O3 which was extremely dense without any pore and whose surface was flat.
This is because the reformation of the surface of the aluminum or aluminum alloy was promoted by the oxygen radical as shown by the expression below.
2Al+3O*→Al2O3
According to another aspect of the present invention, a method of plasma processing of the present invention includes the steps of: heating the processing target made of aluminum or an aluminum alloy in the process vessel to a temperature of 150° C. to 250° C.; and applying oxidation processing to a surface of the processing target in the process vessel by an oxygen radical generated by plasma.
According to findings by the inventors, when a processing target made of aluminum or an aluminum alloy was heated to the temperature of 150° C. to 250° C. and oxidation processing was applied to the processing target in a process vessel, by an oxygen radical generated by plasma, it was also possible to form a coating film of Al2O3 which was extremely dense without any pore and whose surface was flat, when oxygen gas containing rare gas other than krypton was turned into plasma.
When an aluminum alloy containing magnesium (Mg) is used as the aforesaid aluminum alloy, an oxide coating film containing a large amount of MgO produced by an oxygen radical can be formed on a surface of the aluminum alloy. Therefore, it is possible to provide a material with improved corrosion resistance and strength. An appropriate content ratio of the magnesium is 0.5 weight % to solubility limit (the inventors think that it is about 6.0 weight %).
Incidentally, when krypton-containing oxygen gas is turned into plasma to generate an oxygen radical, it is possible to obtain MgO by oxidizing magnesium, even if the content ratio of the magnesium is extremely low such as 0.5 weight % or 1.0 weight %.
When an aluminum alloy containing strontium (Sr) is used as the aforesaid aluminum alloy, an oxide coating film containing a large amount of SrO produced through the oxidation by an oxygen radical can be formed on a surface of the aluminum alloy, so that it is possible to provide a material with improved corrosion resistance and strength.
When an aluminum alloy containing barium (Ba) is used as the aforesaid aluminum alloy, an oxide coating film containing a large amount of BaO produced through the oxidation by an oxygen radical can be formed on a surface of the aluminum alloy, so that it is possible to provide a material with improved corrosion resistance and strength.
When an aluminum alloy containing zirconium (Zr) is used as the aforesaid aluminum alloy, grain growth of the alloy can be suppressed, so that it is possible to provide a material with improved corrosion resistance and strength. A content ratio of about 0.1 to 0.15 weight % is thought to be sufficient.
When an aluminum alloy containing hafnium (Hf) is used as the aforesaid aluminum alloy, grain growth of the alloy can be suppressed, so that it is possible to provide a material with improved corrosion resistance and strength. A content ratio of about 0.1 to 0.15 weight % is thought to be sufficient.
Furthermore, a content ratio of each of Fe, Mn, Cr, and Zn in the aluminum alloy is preferably 0.01 weight % or less. This is because containing a large amount of any of these metals leads to deterioration in the corrosion resistance.
From this viewpoint, Fe, Mn, Cr, and Zn can be removed from the processing target if the processing target of the aluminum alloy undergoes pre-processing while being set at 450° C. or lower in a hydrogen reducing atmosphere before the oxidation processing is applied thereto.
In generating the oxygen radical by the plasma, gas in which krypton (Kr) gas is mixed in oxygen-containing gas may be used to generate the plasma. Mixing the krypton gas makes it possible to easily generate two oxygen radicals since krypton excited to a high energy state collides with an oxygen molecule (O2), and as a result, a large amount of the oxygen radical can be generated in a short time, which enables improvement in the oxidation rate.
Moreover, the processing target can be suitably oxidized even when the temperature thereof is room temperature.
In generating the oxygen radical, gas in which argon (Ar) gas is mixed in oxygen-containing gas may be used to generate plasma. Since the argon gas is easy to handle and is inexpensive, these merits can be enjoyed when they are in practical use.
Further, when the oxidation processing is applied by generating plasma using rare gas such as krypton or argon, for example, when the oxidation processing by an oxygen radical is applied, a produced oxide contains a minute amount of a component of this rare gas. Accordingly, a film stress of the coating film is suppressed and adhesiveness and reliability thereof are improved.
Though a plasma source used for generating the oxygen radical is not limited to a specific one, plasma generated by a microwave having a frequency of 2.45 GHz is an example suitable for the present invention. The microwave plasma is, so to speak, moderate plasma, being high in density and relatively low in Vdc, and therefore, it is possible to suitably apply radical oxidation processing to the surface of the processing target to form the oxide coating film, without giving any damage to the surface of the aluminum or aluminum alloy.
The oxidation processing, according to the present invention, by the oxygen radical to the processing target having the aluminum or aluminum alloy surface may be performed until the oxide coating film with a desired thickness is formed, but it can be proposed that, for example, the oxidation processing be performed up to a so-called saturation state in which the oxygen radical no longer reacts with the surface of the processing target, resulting in no growth of the coating film. When the processing target processed up to this state is used as, for example, a chamber wall of a plasma processing apparatus, and then oxidation processing, film deposition processing, or the like is applied to a semiconductor wafer or the like by the plasma processing apparatus, it is possible to prevent the oxygen radical necessary for the processing from reacting with the inner wall of the chamber. As a result, feed efficiency of the oxygen radical into the semiconductor wafer or the like is improved, enabling high-rate processing.
Hereinafter, embodiments of the present invention will be described.
In the bottom portion of the process vessel 2, provided is an exhaust pipe 12 through which an atmosphere in the process vessel 2 is exhausted by an exhaust device 11 such as a turbo molecular pump. The process vessel 2 further has, in a sidewall thereof, a supply pipe 14 through which process gas from a process gas supply source 13 is supplied. In this embodiment, supply sources 15, 16 of oxygen gas (O2) and argon (Ar) gas being inert gas are connected to the process gas supply source 13.
A dielectric window 22 made of, for example, quartz glass is provided on an opening of the upper portion of the process vessel 2 via a sealing member 21 such as an O-ring for ensuring airtightness. A process space S is formed in the process vessel 2 by this dielectric window 22.
On an upper side of the dielectric window 22, an antenna member 31 is provided. In this embodiment, the antenna member 31 is constituted of, for example, a radial slot antenna 32 positioned on a lowest surface, a retardation plate 33 positioned on an upper side thereof, and an antenna cover 34 covering the retardation plate 33 to protect it and cooling the retardation plate 33.
The radial slot antenna 32 is made of a thin disc of a conductive material, for example, copper, and pairs of slits are formed in the disc to be arranged coaxially, the slits in each pair making an acute angle approximate to a right angle.
The retardation plate 33 has at a center thereof a bump 35 constituting part of a conical shape and made of a conductive material, for example, metal. The bump 35 is electrically connected to an inner conductor 36a of a coaxial waveguide 36 which is constituted of the inner conductor 36a and an outer pipe 36b. The coaxial waveguide 36 guides a microwave of, for example, 2.45 GHz generated in a microwave supply device 37 so that the microwave propagates to the antenna member 31 through a load matching device 38 and the coaxial waveguide 36.
The plasma processing apparatus 1 has the above-described configuration, and next, a method of plasma processing according to an embodiment of the present invention will be described.
Each of processing targets T used in this embodiment is made of a thin-plate aluminum alloy in a rectangular shape and they are arranged in a radial direction and pasted on a surface of the wafer W placed on the susceptor 3. This aluminum alloy contains 2.5 weight % magnesium.
The heater 5 when in operation is capable of heating the processing target T pasted on the wafer W on the susceptor 3 to temperatures in a range from room temperature to about 300° C. and maintaining the raised temperature. By this operation, the temperature of the processing target T was maintained at a predetermined temperature. Then, the inside of the process vessel 2 was exhausted through the exhaust pipe 12 while predetermined mixed gas of oxygen and argon was being supplied thereto from the supply pipe 14 so that the inside of the process space S came to have a predetermined pressure, and then the microwave was generated by the microwave supply device 37 to be propagated to the antenna member 31 by the coaxial waveguide 36, so that plasma was generated in the process space S, and by an oxygen radical generated in the process vessel 2 by the plasma, oxidation processing was applied to a surface of the processing target T.
The plasma conditions for the oxidation processing are as follows.
gas: 1% O2/Ar
pressure: 133 Pa (1 Torr)
microwave output: 2 kW
plasma irradiation time: 10 min.
the temperature of the processing target: room temperature to 200° C.
Results of the oxidation processing will be described based on
(1) First, a depth profile of Al2O3—Al of the processing target T before undergoing the oxidation processing is as shown in
(2) A depth profile of Al2O3—Al when the oxidation processing by the oxygen radical is applied to the processing target T that is not heated but kept at room temperature (about 23° C.) is shown in
(3) A depth profile of Al2O3—Al when the oxidation processing by the oxygen radical is applied to the processing target T heated to 200° C. is shown in
As is apparent from the experiment results shown in the drawings, Al2O3 is initially formed through natural oxidation up to a depth of about 15 nm on the surface of the processing target T before the oxidation processing, but Al being a base material still remains at a further deeper portion.
Next, as shown in
On the other hand, when the processing target T heated to 200° C. is subjected to the oxidation processing, Al2O3 is formed entirely up to an examined 40 nm depth, and no Al being the base material is observed, as shown in
Therefore, it is possible to form a considerably thick coating film of Al2O3 when the processing target T is heated to 200° C. and is subjected to the oxygen radical processing. Moreover, the formed coating film itself can be a denser coating film without any pore and with a flatter surface, compared with that formed by anodic oxidation processing as is conventionally practiced.
Next, depth profiles of MgO—Mg of the processing target T will be described based on
(1) The depth profile of MgO—Mg of the processing target T before undergoing the oxidation processing is as shown in
(2) The depth profile of MgO—Mg when the oxidation processing by the oxygen radical is applied to the processing target T that is not heated but kept at room temperature (about 23° C.) is as shown in
(3) The depth profile of MgO—Mg when the oxidation processing by the oxygen radical is applied to the processing target T heated to 200° C. is as shown in
As is apparent from the above results, first as shown in
Next, as shown in
On the other hand, when the processing target heated to 200° C. is subjected to the oxidation processing by the oxygen radical, MgO is formed entirely up to an examined 40 nm depth and no pure Mg is observed, as shown in
Therefore, it is possible to form a large amount of MgO in the aforesaid Al2O3 coating film if the processing target T is heated to 200° C. and is subjected to the oxidation processing by the oxygen radical.
The existence of a large amount of MgO in the Al2O3 coating film verifies that the coating film is accordingly a strong and a highly corrosion-resistant coating film.
In the aforesaid example, the processing target was heated to the temperature of 200° C., but the inventors think that the same effect can be obtained when the temperature range is 200° C.±50° C., namely, the range of 150° C. to 250° C. If the processing target is aluminum or an aluminum alloy, the same effect is also obtained when the processing is applied at a temperature lower than a temperature at which these metals soften (450° C.).
Incidentally, as previously described, the use of krypton-containing gas in generating the oxygen radical makes it possible to form a suitable oxide coating film by oxidizing the surface of the processing target even when the temperature thereof is room temperature.
Note that the plasma conditions for the oxidation processing are as follows.
gas: 1% O2/Kr
pressure: 133 Pa (1 Torr)
microwave output: 2 kW
plasma irradiation time: 10 min.
the temperature of the processing target: 25° C.
As is apparent from the result, even when the temperature of the processing target T was room temperature, namely, 25° C., it was possible to condense magnesium up to 30 at % and to oxidize this on the surface. Further, as for the film thickness, it was possible to form Al2O3 up to an 80 nm depth and moreover, to have the coating film contain a large amount of MgO.
In this example, the processing target T containing 4.5 weight % magnesium was processed, but as for processing targets containing magnesium whose content ratios are 1.0 weight % and 2.5 weight %, the use of krypton-containing gas in generating the oxygen radical makes it possible to form a suitable oxidation coating film by oxidizing the surface of each of the processing targets even when the temperature of each of the processing targets is room temperature.
Further, in the aforesaid embodiment using the argon-containing gas, the processing target T made of the aluminum alloy whose magnesium content ratio was 2.5 weight % was used, but according to findings by the inventors, a significantly prominent effect was not obtained when this content ratio was 1.0 weight %. Therefore, it is thought that desired MgO cannot be produced unless a certain amount of magnesium is contained, and it is also thought that the larger this amount is, the larger amount of MgO can be produced in the coating film.
When processing targets each of which was made of an aluminum alloy and whose magnesium content ratios were, for example, 2.5 weight % and 4.5 weight % respectively were subjected to oxidation processing by using argon-containing gas, XPS depth profiles as shown in
gas: 1% O2/Ar
pressure: 133 Pa (1 Torr)
microwave output: 2 kW
plasma irradiation time: 10 min.
the temperature of the processing targets: 200° C.
It is seen from the results that a larger amount of MgO is produced in a coating film of the processing target whose magnesium content ratio is 4.5 weight % than in a coating film of the processing target whose magnesium content ratio is 2.5 weight %.
However, when krypton-containing gas was used to generate an oxygen radical and oxidation processing was applied by this, it was possible to produce MgO even if the magnesium content ratio was 1.0 weight %.
gas: 1% O2/Kr
pressure: 133 Pa (1 Torr)
microwave output: 2 kW
plasma irradiation time: 10 min.
the temperature of the processing target: 200° C.
As is seen from the result, even for the processing target whose magnesium content ratio was 1.0 weight %, it was possible to condense magnesium up to about 30 at % and oxidize this even on the surface of the processing target when the krypton-containing gas was used to generate an oxygen radical and the oxidation processing was applied. Therefore, it can be confirmed that highly corrosion-resistant MgO is formed on the surface.
Naturally, when the krypton-containing gas is used to generate the oxygen radical for the oxidation processing, the higher the magnesium content ratio of the processing target of the aluminum alloy is, the larger amount of MgO can be generated and in addition, up to the deeper position in the coating film this MgO can exist.
As is seen from the results, the higher the magnesium content ratio is, the larger amount of MgO can be produced and up to the deeper position in the coating film MgO can exist. In the both cases, it was possible to condense the magnesium on the surface up to 30 at %.
As described above, an appropriate magnesium content ratio in the aluminum alloy adoptable in the present invention is thought to be, for example, 0.5 weight % to the solubility limit, more preferably, 1.0 weight % to the solubility limit.
As described above, when the oxidation processing by the oxygen radical is applied to the processing target made of the aluminum alloy by the method of plasma processing according to the present invention, it is possible to form on the surface thereof a highly corrosion-resistant oxide coating film with a considerably large thickness. Therefore, in view of these respects, when a member whose surface has been subjected to the oxidation processing of the oxygen radical by the aforesaid plasma processing is used as a member exposed to plasma in the aforesaid plasma processing apparatus 1, for example, an inner wall and the susceptor of the process vessel 2, the exhaust pipe 12 and the supply pipe 14, and further, a not-shown gate valve through which the wafer is carried in/out, it is possible to provide a plasma apparatus that is extremely durable and in which the time for vacuuming up to a predetermined degree of reduced pressure is shortened.
Of course, if the member whose surface has been subjected to the oxidation processing of the oxygen radical by the aforesaid plasma processing is used not only as such members around the process vessel 2 but also as members in contact with corrosive gas generated in the process vessel, it is possible to improve durability of these members.
Further, from a different viewpoint, in the case where the member subjected to the oxidation processing of the oxygen radical by the plasma processing according to the present invention is used as such members around the process vessel, the use of the member to which the oxidation processing is applied to a saturation state (a state where no film growth is observed) can prevent the oxygen radical, which is to be fed into a portion of a wafer or a semiconductor element, from oxidizing the chamber or the gate valve of the process vessel and thus being consumed in, for example, executing semiconductor manufacturing processes such as etching processing and film deposition processing, if this processing uses the oxygen radical. That is, it is possible to prevent a state in which the number of oxygen radicals decreases to lower the processing rate being a primarily important factor.
Therefore, the use of the member subjected to the plasma processing of the present invention as a constituent material of, typically, a process vessel of a processing apparatus makes it possible not only to improve durability but also to improve the processing rate itself being a primarily important factor.
Incidentally, even when a member not subjected to the oxidation processing up to such a saturation state (for example, a chamber wall and a susceptor) is used, if the apparatus is operated at a temperature equal to or lower than a temperature for the oxidation processing (for example, 150° C. to 450° C., preferably 150° C. to 250° C.), the oxygen radical generated for the processing in the semiconductor processes does not react with surfaces of these members and thus is not uselessly consumed.
Incidentally, in the examples described above, the wavelength of the microwave is 2.45 GHz, but this is not of course restrictive, and the present invention is applicable to microwaves with various frequencies. Further, the plasma source itself is not limited to the microwave, but various plasma sources using a high frequency of, for example, 13.56 MHz are usable.
Further, the oxide coating film according to the present invention is effectively used for portions other than the portion exposed to the plasma. That is, the application of the present invention is not limited to the plasma processing apparatus, but it is applicable not only to the plasma processing apparatus but also to members of portions exposed to highly reactive and corrosive gas (for example, Chlorine gas, Fluorine gas, or the like) or a highly reactive and corrosive chemical solution (HCl, H2SO4, HF, or the like) in processing apparatuses used in manufacturing electronic devices such as a semiconductor device and a liquid crystal device, for example, in an etching apparatus, a deposition apparatus, other electronic device manufacturing apparatuses in general, a cleaning apparatus using a chemical solution for cleaning, and various kinds of heating apparatuses. The use of the member of aluminum or its alloy in these electronic device manufacturing devices and so on is preferable in view of reducing the weight of the apparatuses, and by coating the surface of the member with the coating film according to the present invention, it is possible to flatten the surface of the member and to improve its corrosion resistance and durability.
According to the present invention, a denser coating film having a flatter surface is formed and the corrosion resistance is made higher than when the conventional anodic oxidation processing is applied.
The present invention is extremely effective for improving the corrosion resistance of various kinds of members such as a chamber using aluminum or an aluminum alloy in various kinds of processing apparatuses such as a plasma processing apparatus.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-006213 | Jan 2003 | JP | national |
| 2003-028476 | Feb 2003 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP04/00179 | 1/14/2004 | WO | 4/6/2006 |