Patent Application
20160172127
The present invention relates to a membrane and a seat device.
A seating sensor for detecting whether or not a passenger is seated is provided on a seat of an automobile. If such seating sensor is configured by a membrane, such membrane sometimes includes a first film with a first wiring. Additionally, an inexpensive raw material such as a PET film and a PEN film is sometimes used for the first film.
Patent Literature 1: JP 2012-121364 A
The PET, the PEN, and the like are inexpensive, but have a relatively small heat capacity. Therefore, when a combustion test is performed on the membrane, the film, and the like at the periphery of the wiring are combusted when the first wiring reaches a high temperature by greater than or equal to a certain extent. Furthermore, when the film and the like at the periphery of the wiring are combusted, the wiring may sag by its own weight. In this case, the molten film flows along the sagged wiring, thus acting as a fuel and increasing the force of the fire at the periphery of the distal end of the sagged wiring, and the entire membrane may be burnt by a high temperature outer flame part of the fire of the relevant portion. In light of the foregoing problem, the object of the present invention is to provide a membrane excelling in flame retardancy, and a seat device using the same.
A membrane according to the present invention includes a first film having at least a first wiring. A layer of flame retardant material is formed on a surface not formed with the first wiring of the first film. The layer contains an organic substance and phosphorus, and that forms a layer of carbide for physically supporting the first wiring by combustion.
The membrane according to the present invention includes the layer of flame retardant material that forms a layer of carbide (char) for physically supporting the first wiring by combustion. Therefore, the wiring can be prevented from sagging. Additionally, the supply of oxygen to the combusting portion can be shielded by the char. Moreover, since the char has low thermal conductivity, the conduction of heat to the membrane can be significantly reduced. Therefore, the flame retardancy of the membrane can be enhanced. Note that in the membrane according to the present invention, the flame retardant material contains the organic substance and the phosphorus. Therefore, at the time of combustion of the membrane, a char having the organic substance as a material can be formed and the formation of such char can be promoted with the phosphorus.
According to one embodiment of the present invention, the organic substance may be a polyester resin. The polyester resin has high polymerization degree compared to the other resins, and thus has high durability, strong withstanding to pulling, and also flexibility so as to have strong withstanding to stress as well.
According to another embodiment of the present invention, the organic substance may contain carboxyl group (COOH). Thus, the adhesiveness of the flame retardant material and the first film can be enhanced, and the occurrence of stripping and cracks at the time of combustion can be suppressed.
According to further another embodiment of the present invention, the phosphorus may be bonded to a side chain of the organic substance. That is, if the organic substance and the phosphorus exist independently in the flame retardant material layer, the proportion of the concentration of the organic substance and the phosphorus may vary within the plane in the flame retardant material. In such a case, for example, the char is less likely to be formed at the portion were the amount of phosphorus is small in the membrane, and such portion tends to relatively easily burn. Additionally, at where the phosphorus exists in excess, the phosphorus may precipitate to the surface. On the contrary, in the present embodiment, the phosphorus is bonded to the side chain of the organic substance. Therefore, the variation within the plane of the proportion of the organic substance and the phosphorus can be prevented, and the char can be appropriately formed at the time of the combustion of the membrane.
According to further another embodiment of the present invention, the flame retardant material may contain ester phosphate. The flame retardant material containing the ester phosphate forms a composite film (char), which includes the polyphosphoric acid and a carbide layer on the combustion surface and thus can suitably form the char. The polyphosphoric acid is generated from a phosphorus compound. The carbide layer is generated from a dehydrated ester polymer.
Furthermore, according to another embodiment of the present invention, the film thickness of the layer of flame retardant material may be greater than or equal to one twentieth and smaller than or equal to one third of a film thickness of a film brought into contact with the layer of flame retardant material and physically supported by the layer of carbide. That is, in view of the mechanical rigidity of the char or the like, the film thickness of the layer of flame retardant material is desirably greater than or equal to one twentieth of the film thickness of the film to support the first wiring, the molten resin, and the like with the char. Additionally, upon using the membrane, the film thickness of the layer of flame retardant material is desirably smaller than or equal to one third of the film thickness of the film so that the properties originally possessed by the film such as flexibility are not affected.
Furthermore, according to another embodiment of the present invention, the film thickness of the layer of flame retardant material may be greater than or equal to 20 μm and smaller than or equal to 100 μm. That is, in view of the mechanical rigidity of the char or the like, the film thickness of the layer of flame retardant material is desirably greater than or equal to 20 μm to support the first wiring, the molten resin, and the like with the char. Additionally, upon using the membrane, the film thickness of the layer of flame retardant material is desirably smaller than or equal to 100 μm so that the properties originally possessed by the film are not affected.
The membrane may further include cushion material provided via the layer of flame retardant material. For example, if the membrane includes a switch that is turned to an ON state by a load, by providing the cushion material, when the load is applied, the cushion material is moved so as to enter an opening of the membrane so that the load can be easily propagated to the switch. In such a case, the ignition to the membrane can be suitably prevented even if the cushion material is ignited, for example, and furthermore, even the flame retardancy in the cushion material can be enhanced by shielding the thermal conduction.
A seat device according to the present invention includes: a cushion pad on which a passenger of an automobile sits; and any one of the membranes to be attached to the cushion pad, the layer of flame retardant material being formed on a surface not facing the cushion pad of the first film.
According to the present invention, a membrane excelling in flame retardancy and a seat device using the same can be provided.
[1. Seat Device and Membrane According to First Embodiment]
Now, a membrane and a seat device according to a first embodiment of the present invention will be described with reference to the drawings
The membrane 3 is provided at a portion on a rear side of an opening 22 of an installing surface 21 of the seat pan 2, and as shown in
A switch 321 and a switch 331 are provided at the front end portions of the sensor side parts 32 and 33, respectively. A switch 322 and a switch 332 are provided at the back end portions of the sensor side parts 32 and 33, respectively. The switches 321, 322, 331, and 332 can, for example, be formed from a pair of electrodes formed on the surfaces facing each other through a space formed by a spacer, in which case, the electrode can be brought into contact by pushing to obtain conduction. The switches 321, 322, 331, and 332 can adopt a configuration capable of detecting the pressure and obtaining electrical conduction.
The first film 35, the spacer 36, and the second film 37 can be generated from a resin having flexibility such as polyethylene terephthalate (PET), polyethylene naphthalate (PEN). The first wiring 351 and the second wiring 371 can be formed by printing a metal such as silver, carbon paste, and the like on such resin.
[2. Flame Retardant Material Layer 38]
[2-1. Outline]
The flame retardant material layer 38 will now be described.
The seat pan 2 is often formed from a material that does not have flexibility, and hence an appropriate load may not be propagated to the membrane 3 from the seat pan 2, and the load may not be appropriately detected. In the comparative example, therefore, the cushion material 39 is interposed between the seat pan 2 and the first film 35. Thus, when the load is applied, the cushion material 39 is moved to enter the opening 22 of the membrane 3, so that the load can be appropriately propagated to the membrane 3. However, since the cushion material 39 generally has a small heat capacity compared to the seat pan 2, the cushion material 39 has a possibility of being ignited before the membrane 3 when an excessive heat is applied.
When the cushion material 39 is ignited, the film, and the like at the periphery of the wiring are sometimes combusted when the first wiring 351 or the second wiring 371 reaches a high temperature by greater than or equal to a certain extent. Furthermore, when the film, and the like at the periphery of the wiring are combusted, the wiring may sag by its own weight. In this case, the molten film flows along the sagged wiring, thus acting as a fuel and increasing the force of the fire at the periphery of the distal end of the sagged wiring. The entire membrane 3′ may be burnt by a high temperature outer flame part of the fire of the relevant portion.
The membrane 3 according to the present embodiment includes the flame retardant material layer 38, which contains an organic substance or phosphorus, between the first film 35 and the cushion material 39. The membrane 3 according to the present embodiment includes the cushion material 39, and hence the load can be appropriately propagated to the membrane 3, similar to the comparative example. Additionally, for example, as shown in
[2-2. Suitable Flame Retardant Material]
In the present embodiment, the flame retardant material layer 34 is generated by applying the flame retardant material, in a paste form, containing the organic substance and the phosphorus on the first film 35. The organic substance contained in the flame retardant material may be, for example, polyester resin, epoxy resin, and the like. In particular, the polyester resin has a high polymerization degree compared to the other resins, and thus has high durability, strong withstanding to pulling, and also flexibility so as to have strong withstanding to stress as well. Therefore, the polyester resin is suitable for the organic substance in the flame retardant material.
The organic substance may contain carboxyl group (COOH). Thereby, the adhesiveness of the flame retardant material and the first film can be enhanced, and the occurrence of stripping and cracks at the time of combustion can be suppressed. Note that when referring to “containing carboxyl group (COOH)”, this means that, for example, the carboxyl group (COOH) is contained as a side chain of polymerized polyester.
Furthermore, the phosphorus contained in the flame retardant material may be bonded to the side chain of the organic substance. That is, if the organic substance and the phosphorus exist independently in the flame retardant material layer, the proportion of the concentration of the organic substance and the phosphorus may vary within the plane in the flame retardant material. In such a case, for example, the char is less likely to be formed at the portion where the amount of phosphorus is small in the membrane, and such portion tends to relatively easily burn. Additionally, at where the phosphorus exists in excess, the phosphorus may precipitate to the surface. On the contrary, in the present embodiment, the phosphorus is bonded to the side chain of the organic substance. Therefore, the variation within the plane of the proportion of the organic substance and the phosphorus can be prevented, and the char can be appropriately formed at the time of the combination of the membrane.
The flame retardancy can be more suitably enhanced by using the flame retardant material containing ester phosphate as the flame retardant material containing the organic substance and the phosphorus. The flame retardant material containing the ester phosphate forms a composite film (char), which includes the polyphosphoric acid and a carbide layer on the combustion surface and thus can suitably form the char. The polyphosphoric acid is generated from a phosphorus compound. The carbide layer is generated from a dehydrated ester polymer.
As the flame retardant material containing the ester phosphate, for example, application of a material of aromatic ester phosphate series (triphenylphosphate, etc.), a material of aromatic condensed ester phosphate series (1,3-phenylene bis (diphenylphosphate), etc.) a material of halogen containing ester phosphate series (tris (dichloropropyl) phosphate, etc.), a material of halogen containing condensed ester phosphate series (polyoxy alkylene bis dichloro alkyl phosphate etc.) can be considered. Additionally, a flame retardant material other than the flame retardant material containing the ester phosphate can be used, and for example, a material of red phosphorus series (e.g., red phosphorus) can be applied for such flame retardant material.
[2-3. Application of Flame Retardant Material]
Next, a mode of when applying the flame retardant material containing the organic substance and the phosphorus on, for example, the first film 35 will be described. Upon performing the application, the flame retardant material is applied on the first film 35 as a paste containing a solvent. Thereafter, the applied paste is dried to form the flame retardant material layer 38. For the solvent contained in the paste, for example, application of that of diethylene glycol monoethyl ether acetate (CH3COOC2H4OC2H4OC2H5) having a viscosity of 150 to 250 dPa·s is considered.
[2-4. Film Thickness of Flame Retardant Material Layer 38]
As described above, the membrane 3 according to the present embodiment forms the char 38′ at the time of the combustion firstly, to physically support the wirings 351, 371, secondly, to shield the supply of oxygen, and thirdly, to shield the thermal conduction. Therefore, the range of the film thickness of the flame retardant material layer 38 needs to be determined in view Of the mechanical rigidity of the formed char, the shielding property of the oxygen, the thermal conductivity, and the like. The film thickness of the flame retardant material layer 38 will now be reviewed.
The film thickness of the flame retardant material layer 38 that does not cause mechanical breakage of the char 38′ changes according to the film thickness of the film physically supported by the char 38′ such as the first film 35. The film thickness of the flame retardant material layer 38 may become uneven in the process of applying the flame retardant material on the first film 35. As a result of reviewing the results of the above described experiment and the above embodiments, the inventors assumed that the film thickness of the flame retardant material layer that does not cause mechanical breakage of the char 38′ is t2≧t1/20, where t1 is the film thickness of the film physically supported by the char 38′ such as the first film 35 or the second film 37, and t2 is the film thickness of the flame retardant material layer 38.
If the film to be supported is, for example, the first film 35 and the second film, the film thickness t1 of the film physically supported by the char 38′ is, for example, the sum of the film thicknesses of the first and second films. If the membrane 3 further includes films to be supported at the time of the combustion, the film thickness becomes a size including the film thickness of the relevant films. Moreover, if only one layer exists for the film to be physically supported by the char 38′, as shown in a third embodiment to be described later, the film thickness of the film physically supported by the char 38′ becomes equal to the film thickness of such film. Furthermore, if another layer is configured from a different material, the weight, and the like of the relevant layer also need to be considered. If the first film 35, and the like, and the type of flame retardant material differ from the present embodiment, such embodiment also needs to be taken into consideration.
In view of the shielding property of the oxygen, the thermal conductivity, and the like of the char 38′, the film thickness of the flame retardant material layer 38 is assumed to be greater than or equal to 20 μm. Note that the flame retardant material is desirably applied over the entire surface of the first film 35, but even if the flame retardant material is applied to only one part, the mechanical strength can be ensured and the heat insulating effect can be exhibited.
If the flame retardant material layer 38 is too thick, the properties originally possessed by the film such as flexibility, and the like may be affected in the usage of the membrane. The membrane 3 according to the present embodiment includes the switches 321, 322, 331, and 332, which are turned to the ON state by pushing. Therefore, if the flame retardant material layer 38 is too thick, the film is less likely to bend, and an ON load for turning the switches to the ON state becomes high. In view of such aspect, the film thickness of the flame retardant material layer 38 is desirably smaller than or equal to 100 μm. Thus, the ON load can be adjusted to an appropriate range.
The appropriate film thickness of the flame retardant material layer 38 of when the ON load is taken into consideration varies according to the film thickness of the film. In view of such aspect, the film thickness t2 of the flame retardant material layer 38 is desirably t2≦t1/3, where t1 is the film thickness of the film physically supported by the char 38′ such as the first film 35 or the second film 37, and t2 is the film thickness of the flame retardant material layer 38. Thus, the ON load can be adjusted to an appropriate range. Additionally, the film thickness t2 of the flame retardant material layer 38 is more desirably t2≦<t1/5.
[3. Seat Device According to Second Embodiment]
Next, a membrane 3-2 and a seat device according to a second embodiment of the present invention will be described with reference to the drawings.
[4. Seat Device According to Third Embodiment]
Next, a membrane and a seat device according to a third embodiment of the present invention will now be described. In the first and second embodiments, the membrane switch having a three-layer structure is adopted for the membrane. On the contrary, in the present embodiment, a capacitance sensor having a one-layer structure is adopted for the membrane. Note that the membrane and the seat device according to the present embodiment are similar to the first and second embodiments with regards to the other aspects. In such a case as well, the membrane excelling flame retardancy and the seat device using the same can be supplied by providing the flame retardant material layer 38. Note that in the present embodiment, the membrane has a one-layer structure. Therefore, if other layers are not formed in the membrane, the film physically supported by a char 38′ is only one layer.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-141966 | Jul 2013 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2014/067991 | 7/4/2014 | WO | 00 |