This application claims priority to and the benefit of Korean Patent Application No. 10-2006-0083524 filed in the Korean Intellectual Property Office on Aug. 31, 2006, the entire content of which is incorporated herein by reference.
The present invention relates to a membrane-electrode assembly for a fuel cell, a method of preparing the same, and a fuel cell system including the same.
A fuel cell is a power generation system for producing electrical energy through an electrochemical redox reaction of an oxidant and a fuel such as hydrogen, or a hydrocarbon-based material such as methanol, ethanol, natural gas, and the like. Such a fuel cell is a clean energy source that can replace fossil fuels. It includes a stack composed of unit cells and produces various ranges of power output. Since it has four to ten times higher energy density than a small lithium battery, it has been highlighted as a small portable power source.
Representative exemplary fuel cells include a polymer electrolyte membrane fuel cell (PEMFC) and a direct oxidation fuel cell (DOFC). The direct oxidation fuel cell includes a direct methanol fuel cell that uses methanol as a fuel.
The polymer electrolyte fuel cell has an advantage of high energy density and high power, but it also has problems in the need to carefully handle hydrogen gas and the requirement of accessory facilities, such as a fuel reforming processor, for reforming hydrocarbon-based gases in order to produce hydrogen as the fuel gas.
On the contrary, a direct oxidation fuel cell has a lower energy density than that of the gas-type fuel cell but has the advantages of easy handling of the liquid-type fuel, a low operation temperature, and no need for additional fuel reforming processors. Therefore, it has been acknowledged as an appropriate system for a portable power source for small and common electrical equipment.
In the above-mentioned fuel cell system, the stack that generates electricity substantially includes several to many unit cells stacked adjacent to one another, and each unit cell is formed of a membrane-electrode assembly (MEA) and a separator (also referred to as a bipolar plate). The membrane-electrode assembly is composed of an anode (also referred to as a “fuel electrode” or an “oxidation electrode”) and a cathode (also referred to as an “air electrode” or a “reduction electrode”) that are separated by a polymer electrolyte membrane.
A fuel is supplied to an anode and adsorbed on catalysts of the anode, and the fuel is oxidized to produce protons and electrons. The electrons are transferred into a cathode via an external circuit, and the protons are transferred into the cathode through the polymer electrolyte membrane. In addition, an oxidant is supplied to the cathode, and then the oxidant, protons, and electrons are reacted on catalysts of the cathode to produce electricity along with water.
For the polymer electrolyte membrane, a perfluorosulfonic acid resin membrane (NAFION®) having good conductivity, mechanical properties, and chemical resistance has been commonly used. The perfluorosulfonic acid resin membrane has a thickness ranging from 130 to 180 μm to inhibit crossover of a hydrocarbon fuel. However, the thicker the perfluorosulfonic acid resin membrane is, the worse the proton conductivity grows and the higher the cost of the polymer electrolyte membrane becomes.
Particularly, a polymer electrolyte membrane that is thermally compressed with a platinum catalyst electrode undergoes a change of 15 to 30% in membrane thickness and volume depending on temperature and degree of hydration, and results in a volume change of over 200% maximum with 3 to 50 wt % methanol as a fuel. Such a thickness increase of an electrolyte membrane applies a stress to a gas diffusion layer as an electrode substrate, and thus a dimension change in a surface direction induces a physical deterioration at the interface between catalyst particles and an electrolyte membrane during long term operation.
One embodiment of the present invention provides a membrane-electrode assembly that has excellent adherence between a polymer electrolyte membrane and a catalyst layer, a good moisture retention property in a polymer electrolyte membrane, and that decreases fuel crossover due to an osmotic pressure decrease and thus improves cell performance.
Another embodiment of the present invention provides a method of preparing the membrane-electrode assembly for a fuel cell.
Yet another embodiment of the present invention provides a fuel cell system including the membrane-electrode assembly.
According to an embodiment of the present invention, a membrane-electrode assembly is provided, which includes an anode and a cathode facing each other, and a polymer electrolyte membrane disposed therebetween. The polymer electrolyte membrane has surface roughness, and a metal layer is randomly disposed on at least one side of the membrane.
According to yet another embodiment of the present invention, a method of fabricating a membrane-electrode assembly is provided, which includes the following processes. The membrane is surface-treated to have surface roughness, a metal layer is formed on the membrane having a surface roughness to fabricate a polymer electrolyte membrane, and the polymer electrolyte membrane is disposed between an anode and a cathode.
According to yet another embodiment of the present invention, a fuel cell system is provided, which includes an electricity generating element, a fuel supplier that supplies the electricity generating element with a fuel, and an oxidant supplier that supplies the electricity generating element with an oxidant. The electricity generating element includes a membrane-electrode assembly and a separator positioned at each side of the membrane-electrode assembly, and generates electricity through electrochemical reactions of fuel and oxidants.
A membrane-electrode assembly of a fuel cell according to one embodiment of the present invention is composed of a polymer electrolyte membrane and an anode and a cathode disposed at both sides of the polymer electrolyte membrane. The membrane-electrode assembly generates electricity through oxidation of a fuel and reduction of an oxidant. The reactions of such a membrane-electrode assembly have been affected by adherence and contact areas at the interface between a polymer electrolyte membrane and an electrode. The higher the adherence and contact area is, the better the reactions occur.
In general, the polymer electrolyte membrane is a perfluorosulfonic acid resin membrane. A thicker perfluorosulfonic acid resin membrane provides better dimensional stability and mechanical properties, but increased membrane resistance. A thinner membrane provides lower membrane resistance, but diminished mechanical properties whereby unreacted fuel gas and liquid tend to pass through the polymer membrane resulting in lost, unreacted fuel during operation and lower performance of the cell. Moreover, since hydrocarbon-based fuel is transferred to the cathode through a polymer electrolyte membrane and oxidized in a cathode in a direct oxidation fuel cell using hydrocarbon-based fuel such as methanol, ethanol, and propanol, the reduction space of an oxidant is reduced in the cathode and this degrades the battery performance.
Therefore, it is desired to develop a technique for controlling an interface between the polymer electrolyte membrane and the electrode, and a technique for controlling the physical and chemical interface characteristics to prevent the durability of the membrane-electrode assembly from being deteriorated due to separation of the catalyst layer, and thus maximizing electrode catalyst efficiency.
According to one embodiment of the present invention, it is possible to increase the adherence between the polymer electrolyte membrane and the catalyst layer, increase the contact area, improve moisture retention properties of the polymer electrolyte membrane, and reduce fuel crossover caused by decreased osmotic pressure. This may be accomplished by forming a membrane having appropriate surface roughness and randomly forming a metal layer on the membrane in the membrane-electrode assembly.
Referring to
The membrane 20 performs an ion exchange function, that is, it transfers protons generated in the catalyst layer 70 of the anode 30 to the catalyst layer 70′ of the cathode 30′ in the polymer electrolyte membrane 20.
In one embodiment, the membrane 20 may have roughness on one side, or in another embodiment on both sides, to increase the contact area with the metal layer 60 and 60′ and the catalyst layer 70 or 70′ of the electrode for high power output. In an embodiment, the membrane 20 may have an average surface roughness Ra in the range of 200 nm to 2 μm, and in another embodiment 500 nm to 2 μm. When the average surface roughness of the membrane 20 is not more than 200 nm, the active specific surface area with the catalyst layer is small and the adherence to the catalyst layer may be diminished after a long time. When the average surface roughness of the membrane 20 exceeds 2 μm, the mechanical strength of the membrane 20 may be reduced, which is also not desirable.
One or both sides of the membrane 20 may be patterned. The pattern formed in the membrane 20 may be a regular pattern. When the pattern is irregular, there may be non-uniform current and a reduction in the fuel cell performance.
In one embodiment, the membrane 20 may have a thickness ranging from 50 to 150 μm, in another embodiment from 110 to 140 μm. When the membrane 20 is thinner than 50 μm, the mechanical strength is deteriorated. When it is thicker than 150 μm, membrane resistance is increased, which is not desirable.
The membrane may include a highly proton-conductive polymer. In one embodiment, the proton-conductive polymer may be a polymer resin having a cation exchange group selected from the group consisting of a sulfonic acid group, a carboxylic acid group, a phosphoric acid group, a phosphonic acid group, and derivatives thereof, at its side chain.
In one embodiment, the proton-conductive polymer may include at least one selected from the group consisting of fluoro-based polymers, benzimidazole-based polymers, polyimide-based polymers, polyetherimide-based polymers, polyphenylenesulfide-based polymers, polysulfone-based polymers, polyethersulfone-based polymers, polyetherketone-based polymers, polyether-etherketone-based polymers, and polyphenylquinoxaline-based polymers. According to an embodiment, the polymer electrolyte membrane includes proton conductive polymers selected from the group consisting of poly(perfluorosulfonic acid) (NAFION®), poly(perfluorocarboxylic acid), a copolymer of tetrafluoroethylene and fluorovinylether having a sulfonic acid group, defluorinated polyetherketone sulfide, aryl ketone, poly(2,2′-(m-phenylene)-5,5′-bisbenzimidazole), and poly(2,5-benzimidazole).
H in an ion exchange group of the proton conductive polymer can be replaced with Na, K, Li, Cs, or tetrabutyl ammonium. When the H is substituted by Na in an ion exchange group at the terminal end of the proton conductive polymer, NaOH is used. When the H is replaced with tetrabutylammonium, tributylammonium hydroxide is used. K, Li, or Cs can also be replaced by using appropriate compounds. Since a method of substituting H is widely known in this related art, detailed description thereof will not be provided herein.
The membrane 20 includes the metal layers 60 and 60′ randomly disposed in at least one side. Randomly disposed means that the metal layers 60 and 60′ do not form a closed layer covering the membrane 20.
The metal layers 60 and 60′ disposed on one or both sides of the membrane 20 not only improve cooperative performance between the membrane 20 and the catalyst layers 70 and 70′, but also reduce crossover of fuel. Therefore, it is desirable to dispose the metal layers on both sides of the membrane 20, instead of forming a metal layer on any one side of the membrane 20. In an embodiment, when it is disposed on one side, it is desirable to dispose the metal layer on a side adjacent to the anode.
In one embodiment, the metal layers 60 and 60′ may be randomly disposed in the membrane 20 in the form of a nano nodule or a nano horn. In another embodiment, the metal layers 60 and 60′ are formed in the shape of a nano nodule. When a metal layer has the shape of a nano nodule, the metal layer is porous and this is advantageous because the morphology of the metal layer interface is increased three-dimensionally.
In one embodiment, the metal layers 60 and 60′ include at least one metal selected from Au, Pt, Ru, W, Pd, Fe, and alloys thereof. In another embodiment, the metal layers 60 and 60′ include Au.
As described above, the metal included in the metal layers 60 and 60′ functions as a catalyst, and since it has a nano particle size, it increases the moisture retention property of the polymer electrolyte membrane 20 to thereby maintain the humidity of the polymer electrolyte membrane 20 at a predetermined level at a high temperature.
Also, the metal in the metal layers 60 and 60′ directly increases the number of oxide species quantitatively through a bifunctional mechanism with respect to electro-oxidation. Thus, it is possible to improve an electrode activity for an oxidation reaction of fuel.
In one embodiment, the membrane 20 and the metal layers 60 and 60′ may have a thickness ratio of 25:1 to 1500:1, and in another embodiment 100:1 to 260:1. When the thickness ratio of the membrane to the metal layer is within the range, the co-catalytic effect of the metal element in the metal layer is maximized. Since the porous state is maintained, the specific surface area is increased, which is desirable. When the thickness ratio is out of the range, the density of the metal layer is increased. Since this allows less access of fuel, it is not desirable.
In one embodiment, the metal layers 60 and 60′ may have a thickness in the range of 100 nm to 2 μm, and in another embodiment from 500 nm to 1 μm. When the metal layer is thinner than 100 nm, the effect obtained from the formation of the metal layer is insignificant. When the metal layer is thicker than 2 μm, it provides narrow paths for fuel.
An anode 30 and a cathode 30′ are disposed on respective sides of the polymer electrolyte membrane.
At least one of the anode 30 and the cathode 30′ includes electrode substrates 50 and 50′ and catalyst layers 70 and 70′ disposed on the electrode substrates 50 and 50′.
The electrode substrates 50 and 50′ of the anode 30 and cathode 30′ support the anode and cathode, respectively, and provide a path for transferring fuel and oxidant to the catalyst layers 70 and 70′. Such electrode substrates 50 and 50′ may be conductive substrates. As for the electrode substrates 50 and 50′, a conductive substrate is used, for example carbon paper, carbon cloth, carbon felt, and metal cloth (a porous film including a metal cloth fiber or a metalized polymer fiber), but it is not limited thereto.
The electrode substrates 50 and 50′ may be treated with a fluorine-based resin to be water-repellent to prevent deterioration of diffusion efficiency due to water generated during operation of a fuel cell. In one embodiment, the fluorine-based resin may be one selected from the group consisting of polytetrafluoroethylene, polyvinylidene fluoride, polyhexafluoro propylene, polyperfluoroalkylvinylether, polyperfluoro sulfonylfluoride alkoxyvinyl ether, fluorinated ethylene propylene, polychlorotrifluoro ethylene, and copolymers thereof, but it is not limited thereto.
A microporous layer (MPL, not shown) can be added between the aforementioned electrode substrates 50 and 50′ and catalyst layer to increase reactant diffusion effects. The microporous layer generally includes conductive powders with a particular particle diameter. In one embodiment, the conductive material may include, but is not limited to, carbon powder, carbon black, acetylene black, activated carbon, carbon fiber, fullerene, nano-carbon, or combinations thereof. The nano-carbon may include a material such as carbon nanotubes, carbon nanofiber, carbon nanowire, carbon nanohorns, carbon nanorings, or combinations thereof.
The microporous layer is formed by coating a composition comprising a conductive powder, a binder resin, and a solvent on the conductive substrate. In one embodiment, the binder resin may include, but is not limited to, polytetrafluoro ethylene, polyvinylidene fluoride, polyhexafluoro propylene, polyperfluoroalkylvinyl ether, polyperfluoro sulfonylfluoride alkoxy vinyl ether, polyvinyl alcohol, cellulose acetate, or copolymers thereof. In one embodiment, the solvent may include, but is not limited to, an alcohol such as ethanol, isopropyl alcohol, n-propyl alcohol, butanol and so on, water, dimethyl acetamide, dimethyl sulfoxide, N-methylpyrrolidone, and tetrahydrofuran. In one embodiment, the coating method may include, but is not limited to, screen printing, spray coating, doctor blade methods, gravure coating, dip coating, silk screening, painting, and so on, depending on the viscosity of the composition.
The catalyst layers 70 and 70′ are disposed on the electrode substrates 50 and 50′.
The catalyst layers 70 and 70′ include catalysts to promote related reactions, such as fuel oxidation and oxidant reduction.
The catalysts may be any catalyst that can promote a fuel cell reaction. For example, platinum-based catalysts are generally used. In one embodiment, examples of the platinum-based catalysts include platinum, ruthenium, osmium, platinum-ruthenium alloys, platinum-osmium alloys, platinum-palladium alloys, platinum-M alloys, and combinations thereof, where M is a transition element selected from the group consisting of Ga, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Sn, Mo, W, Rh, and combinations thereof. According to an embodiment, platinum-based catalysts may include Pt, Pt/Ru, Pt/W, Pt/Ni, Pt/Sn, Pt/Mo, Pt/Pd, Pt/Fe, Pt/Cr, Pt/Co, Pt/Ru/W, Pt/Ru/Mo, Pt/Ru/V, Pt/Fe/Co, Pt/Ru/Rh/Ni, Pt/Ru/Sn/W, and combinations thereof.
The metal catalyst may be supported on a carrier, or it may be a black type of catalyst that is not supported on a carrier. In one embodiment, the carrier may include carbon-based materials such as graphite, denka black, ketjen black, acetylene black, carbon nanotubes, carbon nanofiber, carbon nanowire, carbon nanoballs, and activated carbon. In one embodiment, for a carrier, an inorganic particulate such as alumina, silica, zirconia, and titania may also be used. A carbon-based material is generally used as a carrier.
The catalyst layers 70 and 70′ may further include a binder resin to improve adherence of catalyst layers and proton conductivity.
In one embodiment, the binder resin may be a proton-conductive polymer resin having a cation exchange group selected from the group consisting of a sulfonic acid group, a carboxylic acid group, a phosphoric acid group, a phosphonic acid group, and derivatives thereof, at its side chain. In an embodiment, the proton-conductive polymer may include at least one selected from the group consisting of fluoro-based polymers, benzimidazole-based polymers, polyimide-based polymers, polyetherimide-based polymers, polyphenylenesulfide-based polymers polysulfone-based polymers, polyethersulfone-based polymers, polyetherketone-based polymers, polyether-etherketone-based polymers, and polyphenylquinoxaline-based polymers. In another embodiment, the polymer electrolyte membrane includes proton conductive polymers selected from the group consisting of poly(perfluorosulfonic acid) (NAFION®), poly(perfluorocarboxylic acid), a copolymer of tetrafluoroethylene and fluorovinylether having a sulfonic acid group, defluorinated polyetherketone sulfide, aryl ketone, poly(2,2′-(m-phenylene)-5,5′-bisbenzimidazole), or poly(2,5-benzimidazole).
The binder resins may be used singularly or in combination. They may be used along with non-conductive polymers to improve adherence with a polymer electrolyte membrane. The binder resins may be used in a controlled amount adapted to their purposes.
Non-limiting examples of the non-conductive polymers include polytetrafluoroethylene (PTFE), tetrafluoroethylene-hexafluoropropylene copolymers (FEP), tetrafluoroethylene-perfluoro alkyl vinylether copolymers (PFA), ethylene/tetrafluoroethylene (ETFE), chlorotrifluoroethylene-ethylene copolymers (ECTFE), polyvinylidene fluoride, polyvinylidenefluoride-hexafluoropropylene copolymers (PVdF-HFP), dodecylbenzene sulfonic acid, sorbitol, or combinations thereof.
Referring to
First, a polymer electrolyte membrane is prepared. A method for forming the membrane is not limited to a specific method, and the membrane can be fabricated in the form of a thin film by using a conventional fabrication method and proton-conductive cation exchange resin. The proton-conductive cation exchange resin may be the same as described above.
Subsequently, roughness is formed on the surface of the membrane through surface treatment at step S1. As for the surface treatment, a conventional patterning method may be used. In one embodiment, the surface treatment may be one selected from the group consisting of sandpapering, sandblasting, corona treatment, rubbing, compressing, a plasma method, electron beam irradiation, and combinations thereof. In another embodiment, the surface treatment may be sandpapering.
The patterning of the membrane may be performed on one or both sides of the membrane, and in an embodiment, the patterning is performed on both sides of the membrane.
Subsequently, a metal layer is disposed on the membrane having the roughness to thereby prepare a polymer electrolyte membrane at step S2.
In an embodiment, the metal layer is formed on the membrane by using a method selected from the group consisting of sputtering, Physical Vapor Deposition (PVD), Chemical Vapor Deposition (CVD), Plasma Enhanced Chemical Vapor Deposition (PECVD), Thermal Chemical Vapor Deposition (TCVD), electron beam evaporation, vacuum thermal evaporation, laser ablation, thermal evaporation, e-beam evaporation, and combinations thereof. In another embodiment, the metal layer is disposed by using the sputtering method.
When the metal layer is disposed by the sputtering method, in one embodiment, it is desirable to apply a current in the range of 3 to 9 mA, and in another embodiment from 5 to 7 mA. When the current is lower than 3 mA, the density of the metal layer is increased and thus the metal layer provides narrower paths for fuel. When the current is higher than 7 mA, the porosity of the metal layer is increased and thus the mechanical strength of the metal layer may be deteriorated.
In one embodiment, the sputtering may be performed for 50 to 300 seconds, and in another embodiment for 50 to 250 seconds. When the sputtering is performed for less than 50 seconds, the porosity of the metal layer is excessively increased and the mechanical strength is deteriorated. When the sputtering is performed for longer than 300 seconds, the density of the metal layer is increased too much to provide appropriate paths for fuel.
As described above, the metal layer may be formed to have a thickness ratio in the range of 25:1 to 1500:1.
Subsequently, the preparation of the membrane-electrode assembly is completed by forming an anode and a cathode in the polymer electrolyte membrane at step S3.
The anode and the cathode of the membrane-electrode assembly may be made by forming a catalyst layer on the polymer electrolyte membrane and bonding it with an electrolyte substrate, or by bonding the polymer electrolyte membrane with an electrode substrate having a catalyst layer disposed thereon.
Particularly, according to an embodiment of the present invention, the catalyst layer is formed on the prepared polymer electrolyte membrane by coating the polymer electrolyte with a composition for forming the catalyst layer, or coating a releasing film with the composition for forming the catalyst layer and drying the film to thereby form a first catalyst layer, transferring the first catalyst layer to the polymer electrolyte membrane through thermal pressing to thereby form a catalyst layer, and bonding the catalyst layer with the electrode substrate.
According to another embodiment, the membrane-electrode assembly may be fabricated by coating an electrode substrate with a composition for forming the catalyst layer to thereby form the catalyst layer and bonding the electrode substrate having the catalyst layer formed thereon with the above-prepared polymer electrolyte membrane.
In one embodiment, when both sides of the polymer electrolyte membrane are directly coated with the composition for forming a catalyst layer, the coating may be performed in a method selected from the group consisting of screen printing, spray coating, doctor blade coating, gravure coating, dip coating, silk screening, painting, slot dying, and combinations thereof according to the viscosity of the composition, but the coating method is not limited thereto. In another embodiment, the coating may be performed by screen printing.
Also, when the catalyst layer is formed by coating the composition for forming a catalyst layer on only one side of a releasing film and drying the film coated with the composition and then the catalyst layer is transferred to the polymer electrolyte membrane, in one embodiment, the releasing film used therein may be a fluorinated resin film having a thickness of approximately 200 μm such as polytetrafluoroethylene (PTFE), a tetrafluoroethylene-hexafluoropropylene copolymer (FEP), a tetrafluoroethylene-perfluoro alkylvinylether copolymer (PFA), and ethylene/tetrafluoroethylene (ETFE), or the releasing film may be non-fluorinated resin film such as polyimide (KAPTON® produced by the DuPont Company) and polyester (MYAR® produced by the DuPont Company). The releasing film is coated with the composition for forming a catalyst layer in the method described above.
The transferring process may be performed by disposing the catalyst layer formed in the releasing film onto the polymer electrolyte membrane and then compressing them while applying heat thereto.
In one embodiment, the thermal pressing may be performed at a temperature in the range of from 100 to 250° C., and in another embodiment from 100 to 200° C. Also, in an embodiment, the thermal pressing may be performed by applying pressure in the range of 300 to 2000 psi, and in another embodiment from 300 to 1500 psi.
The transferring of the catalyst layer is smoothly performed within the temperature and pressure ranges. Out of the ranges, the transferring of the catalyst layer may not be performed perfectly or the catalyst layer becomes too dense to transfer reactant therethrough.
Since the electrode substrate and the catalyst layer are as described above and an exemplary method for bonding the electrode substrate with the polymer electrolyte membrane is widely known to those skilled in the art of the present invention, a detailed description thereof will not be provided herein.
The above-prepared membrane-electrode assembly includes the membrane having appropriate roughness on the surface through a surface treatment, and a metal layer formed on the membrane. Therefore, the contact area and the adherence between the polymer electrolyte membrane and the catalyst layer are increased, and the moisture retention property of the polymer electrolyte membrane is improved. Also, the crossover of fuel caused by decreased osmotic pressure can be reduced and this brings about excellent fuel cell characteristics.
Another embodiment of the present invention provides a fuel cell system including the above membrane-electrode assembly.
In one embodiment, a fuel cell system of the present invention includes at least one of an electricity generating element, a fuel supplier, and an oxidant supplier.
The electricity generating element includes a membrane-electrode assembly that includes a polymer electrolyte membrane and a cathode and an anode positioned at both sides of the polymer electrolyte membrane, and separators positioned at both sides of the membrane-electrode assembly. The electricity generating element generates electricity through oxidation of a fuel and reduction of an oxidant.
The fuel supplier supplies the electricity generating element with a fuel including hydrogen, and the oxidant supplier supplies the electricity generating element with an oxidant. The oxidant includes oxygen or air.
In one embodiment, the fuel includes liquid or gaseous hydrogen, or a hydrocarbon-based fuel such as methanol, ethanol, propanol, butanol, or natural gas.
The fuel cell system 100 includes at least one electricity generating element 115 that generates electrical energy through an electrochemical reaction of a fuel and an oxidant, a fuel supplier 120 for supplying a fuel to the electricity generating element 115, and an oxidant supplier 130 for supplying an oxidant to the electricity generating element 115.
In addition, the fuel supplier 120 is equipped with a tank 122 that stores fuel, and a fuel pump 124, which is connected to the fuel tank 122. The fuel pump 124 supplies fuel stored in the tank 122 to a fuel cell stack 110.
The oxidant supplier 130, which supplies the electricity generating element 115 with an oxidant, is equipped with at least one pump 132 for supplying an oxidant to the stack 110.
The electricity generating element 115 includes a membrane-electrode assembly 112, which oxidizes hydrogen or a fuel and reduces an oxidant, and separators 114 and 114′ that are respectively positioned at opposite sides of the membrane-electrode assembly and supply hydrogen or a fuel, and an oxidant, respectively. At least one electricity generating element 115 constitutes the stack 110.
The following examples illustrate the present invention in more detail. However, it is understood that the present invention is not limited by these examples.
For a membrane, a commercial product NAFION 115 membrane having a thickness of 125 μm was rinsed with distilled water several times and treated with 1 liter of 2% hydrogen peroxide for 2 hours. Subsequently, the hydrogen peroxide was removed by rinsing with distilled water three times, and then the NAFION 115 membrane was treated with 1 liter of 1M sulfuric acid solution for 2 hours. The NAFION 115 membrane was rinsed with distilled water again, such that an H-type NAFION 115 membrane was prepared.
Both sides of the NAFION 115 membrane were sandblasted to form a pattern. One side of the patterned NAFION 115 membrane toward the anode was sputtered with Au at 20° C. for 100 seconds to thereby form an Au metal layer having a thickness of 500 nm and prepare a polymer electrolyte membrane.
10 wt % solid content of a composition for forming a catalyst layer was prepared by mixing 10 g of Pt black (HISPEC® 1000 produced by the Johnson Matthey Company), 10 g of Pt/Ru black (HISPEC® 6000 produced by the Johnson Matthey Company), 10 g of water, 12 wt % of a 5 wt % concentration of NAFION solution, and 62 g of isopropyl alcohol. The composition for forming a catalyst layer was sprayed onto the Au sputtered polymer electrolyte membrane. Herein, the catalyst layer area was 3.2×3.2 cm2 and the catalyst loading quantity was 4 mg/cm2. The catalyst layer prepared as above became an anode catalyst layer. A cathode catalyst layer was formed by performing the same process onto the other side of the polymer electrolyte membrane.
Subsequently, an electrode substrate (uncatalyzed gas diffusion electrode, SGL Carbon 10DA) was prepared to have a microporous layer with a Vulcan black loading quantity of 1.4 mg/cm2 by using a composition for forming a microporous layer including Vulcan black (VULCAN SDN 2). The electrode substrate was bonded with the polymer electrolyte membrane having the cathode catalyst layer by pressing the electrode substrate with a compression molder at 300 psi and 135° C. for 3 minutes. Also, an electrode substrate (uncatalyzed gas diffusion electrode, SGL Carbon 31BC) without a microporous layer was physically bonded with the polymer electrolyte membrane having the anode catalyst layer to thereby prepare a membrane-electrode assembly. The membrane-electrode assembly was interposed between two gaskets, interposed again between two separators having a predetermined gas flow channel and a cooling channel, and then compressed between Cu end plates to thereby prepare a single cell.
It can be seen from
In
Also, it can be seen from
It can be seen from
A single cell was prepared according to Example 1, except that an Au metal layer was formed by performing Au sputtering onto a polymer electrolyte membrane on the side of the cathode instead of the anode side.
A single cell was prepared according to Example 1, except that an Au metal layer was formed in the polymer electrolyte membrane on the side of the cathode as well, by performing Au sputtering onto the polymer electrolyte membrane on the side of the cathode.
As for a membrane, a commercial product NAFION 115 membrane having a thickness of 125 μm was rinsed with distilled water several times and treated with 1 liter of 2% hydrogen peroxide for 2 hours. The hydrogen peroxide was removed and the NAFION 115 membrane was rinsed with distilled water three times and treated again with 1 liter of 1M sulfuric acid solution for 2 hours. The NAFION 115 membrane was rinsed again with distilled water and an H-type NAFION 115 membrane was thus prepared.
10 wt % solid content of a composition for forming a catalyst layer was prepared by mixing 10 g of Pt black (HISPEC® 1000 produced by the Johnson Matthey Company), 10 g of Pt/Ru black (HISPEC® 6000 produced by the Johnson Matthey Company), 10 g of water, 12 wt % of a 5 wt % concentration of NAFION solution, and 62g of isopropyl alcohol. The composition for forming a catalyst layer was sprayed onto one side of the polymer electrolyte membrane for coating. Herein, a catalyst layer area was 3.2×3.2 cm2 and a catalyst loading quantity was 4 mg/cm2. The catalyst layer prepared as above became an anode catalyst layer. A cathode catalyst layer was formed on the other side of the polymer electrolyte membrane in the same method.
Subsequently, an electrode substrate (uncatalyzed gas diffusion electrode, SGL Carbon 10DA) was prepared to have a microporous layer with a Vulcan black loading quantity of 1.4 mg/cm2 by using a composition for forming a microporous layer including Vulcan black (VULCAN SDN 2). The electrode substrate was bonded with the polymer electrolyte membrane having the cathode catalyst layer by pressing the electrode substrate with a compression molder at 300 psi at 135° C. for 3 minutes. Also, an electrode substrate (uncatalyzed gas diffusion electrode, SGL Carbon 31BC) without a microporous layer was physically bonded with the polymer electrolyte membrane having the anode catalyst layer to thereby prepare a membrane-electrode assembly. The membrane-electrode assembly was interposed between two gaskets, interposed again between two separators having a gas flow channel and a cooling channel of a predetermined shape, and then compressed between Cu end plates to thereby prepare a single cell.
As for a membrane, a commercial product NAFION 115 membrane having a thickness of 125 μm was rinsed with distilled water several times and treated with 1 liter of 2% hydrogen peroxide for 2 hours. The hydrogen peroxide was removed and the NAFION 115 membrane was rinsed with distilled water three times and treated again with 1 liter of 1M sulfuric acid solution for 2 hours.
The NAFION 115 membrane was rinsed again with distilled water and an H-type NAFION 115 membrane was thus prepared. A single cell was prepared according to Comparative Example 1, except that a pattern was formed on both sides of the NAFION 115 membrane through sandpapering, and the patterned NAFION 115 membrane was used as the polymer electrolyte membrane.
Moisture retention properties of the polymer electrolyte membranes of Example 3 and Comparative Examples 1 and 2 were measured by using a differential scanning calorimeter (DSC).
The moisture retention properties were measured after drying the polymer electrolyte membranes in a vacuum oven at 60° C. for one hour, impregnating the polymer electrolyte membranes in distilled water at 60° C. for one hour, and removing water from the polymer electrolyte membranes. The results are presented in
As shown in
Methanol crossover currents of the polymer electrolyte membranes prepared in accordance with Example 3 and Comparative Examples 1 and 2 were measured at 50° C. and 60° C. by flowing in 4 ml of 1M methanol and nitrogen 200 sccm (Standard Cubic Centimeter per Minute, cm3/min). The methanol permeability was calculated from the methanol crossover currents and the results are shown in the following Table 1.
As shown in Table 1, the polymer electrolyte membrane of Example 1 showed considerably low methanol permeability at 50° C. and 60° C., compared to the polymer electrolyte membranes of Comparative Examples 1 and 2.
CO stripping voltammetries of the membrane-electrode assemblies prepared in accordance with Example 3 and Comparative Example 1 were measured at 50° C. and 70° C. The measurement results are shown in
As shown in
Power density of the unit cells prepared in accordance with Examples 1 to 3 and Comparative Examples 1 and 2 were measured at 60° C. and 70° C. respectively by providing 1M methanol and ambient air with anode and cathode of the unit cells. The measurement results are shown in the following Table 2.
As illustrated in Table 2, the fuel cells of Examples 1 to 3 having a metal layer and a polymer electrolyte membrane with rough morphology showed excellent methanol permeability and high power density, compared to the fuel cell of Comparative Example 1 using a pure NAFION membrane as a polymer electrolyte membrane and the fuel cell of Comparative Example 2 including a polymer electrolyte membrane having only surface roughness. In addition, Table 2 shows that the fuel cell of Example 1 having the metal layer only in the side of the anode had superior power density to the fuel cell of Example 2.
One embodiment of the present invention provides a high-performance membrane-electrode assembly for a fuel cell that can improve interaction between the polymer electrolyte membrane and the catalyst by improving a contact area between the polymer electrolyte membrane and the catalyst and adherence between them, improve a moisture retention property of the polymer electrolyte membrane, and reduce crossover of fuel caused by deteriorated osmotic pressure.
While this invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims and their equivalents.
Number | Date | Country | Kind |
---|---|---|---|
10-2006-0083524 | Aug 2006 | KR | national |