The corrosion resistance of a metal strip can be enhanced by coating the strip with molten metal, such as zinc. It has been known to anneal the metal strip, prepare the surface of the metal strip for coating in a protective atmosphere maintained in an enclosure, and then immerse the metal strip in a bath of molten metal to coat the metal strip with the molten metal.
Immersion baths may not guarantee consistent product quality of the metal strip.
For example, changes in the surface condition of pot rolls directing the metal strip through the bath can cause negative effects on the metal strip such as marks or scratches, as well as nonuniform coating thickness formation. Further, immersion bath methods often require a large molten metal reservoir that, with the pot rolls, is costly to manufacture and maintain.
Meniscus coating methods are known, as disclosed in U.S. Pat. No. 5,453,127, entitled “Apparatus for Meniscus Coating a Metal strip,” issued Sep. 26, 1995, and U.S. Pat. No. 5,399,376, entitled “Meniscus Coating Metal strip,” issued Mar. 21, 1995, which patents are incorporated by reference herein. The metal strip is treated (for example, the metal strip is heated in a furnace, or heated and cooled, to achieve a temperature near a melting point of a coating metal prior to the metal strip being coated with the coating metal). After such treatment, the metal strip passes through a protective, often non-oxidizing, atmosphere contained within an enclosure to arrive at a coating tray holding a pool of molten coating metal. The metal strip typically passes close to the pool of molten metal and surface tension bridges the gap between the molten metal surface and the metal strip, allowing the molten metal to coat the strip.
The present application describes a meniscus coating apparatus that provides for coating of the strip outside of the protective enclosure by minimizing the ingress of ambient air into the enclosure containing the protective atmosphere.
While the specification concludes with claims which particularly point out and distinctly claim the invention, it is believed the present invention will be better understood from the following description of certain examples taken in conjunction with the accompanying drawings, in which like reference numerals identify the same elements and in which:
The drawings are not intended to be limiting in any way, and it is contemplated that various embodiments of the invention may be carried out in a variety of other ways, including those not necessarily depicted in the drawings. The accompanying drawings incorporated in and forming a part of the specification illustrate several aspects of the present invention, and together with the description serve to explain the principles of the invention; it being understood, however, that this invention is not limited to the precise arrangements shown.
The following description of certain examples of the invention should not be used to limit the scope of the present invention. Other examples, features, aspects, embodiments, and advantages of the invention will become apparent to those skilled in the art from the following description. As will be realized, the invention is capable of other different and obvious aspects, all without departing from the invention. Accordingly, the drawings and descriptions should be regarded as illustrative in nature and not restrictive.
As disclosed in U.S. Pat. Nos. 5,453,127 and 5,399,376, which patents are incorporated by reference above, a metal strip is advanced through a meniscus coating apparatus to be coated with molten metal. Before coating, the metal strip must be clean and free of any oxides or other materials that may adversely affect coating adherence. Such surface preparation and treatment is well known in the art. With respect to temperature, the metal strip may be heated in a furnace, or heated in a furnace and then cooled, to achieve a desired temperature, as is also well-known in the art.
As the metal strip approaches coating, this prepared condition must be maintained. This can be done by enclosing the prepared strip in a roll enclosure with a specialized, protective atmosphere as is well known in the art, and is described in U.S. Pat. No. 5,435,127. The roll enclosure may be a substantially enclosed chamber that houses the coating trays in a protective environment along with shaping rolls, which help to maintain the shape of the strip prior to coating. The metal strip advances past the coating trays to be coated with molten metal within the enclosure.
According to an embodiment of the present disclosure, a coating tray of a meniscus coating apparatus is disposed outside of a roll enclosure. The present disclosure describes embodiments of a meniscus coating apparatus that maintains a protective atmosphere within a roll enclosure, while the coating tray is disposed outside of the roll enclosure. The meniscus coating apparatus of the present disclosure includes physical or pressurized gas barriers that allow the strip to exit the enclosure while minimizing the ingress of ambient air into the roll enclosure, as described below. Further, the described physical or pressurized gas barriers aid in maintaining a protective atmosphere, in particular they assist in maintaining an oxygen-free, or at least substantially oxygen-free, environment, around the strip after it exits the enclosure and until the molten metal coating is applied to it.
The coating tray includes a top lip that delivers a coating metal in a molten phase to a surface of a metal strip. Meniscus coating trays are well-known in the art, and suitable trays include those described in U.S. Pat. Nos. 5,453,127 and 5,399,376, among others. The strip may comprise carbon steel, stainless steel, or any other suitable metal strip. The coating metal may comprise zinc, aluminum, zinc magnesium, tin, terne (including lead and tin), or other suitable coating metals, as is known in the art.
The metal strip is advanced toward the coating tray through a cover of a roll enclosure. In particular, the metal strip is advanced through a strip receiving portion of an aperture in the cover of the roll enclosure, as described further below. The aperture in the cover of the roll enclosure includes at least one open portion that does not receive the metal strip. The aperture may extend completely or partially between edges of the cover.
An adjustable plate or baffle, further described below, is adapted to cover all or part of the open portion of the aperture in the cover. The baffle may be disposed within the roll enclosure or outside of the roll enclosure, such as on top of the cover. One or more seals may be disposed between the baffle and the coating tray, or between the coating tray and the cover of the roll enclosure. Isolation of an area between the coating lips of the coating trays and the cover by a baffle and/or seals may permit the development of a positive gas pressure in that area that allows the distance between the coating lips and the strip to be greater. For example, unsupported molten metal in the meniscus bows downward via a downward pull that is a balance between gravity and surface tension. For a given surface tension, there is a maximum lip to strip distance before the meniscus will fall, or escape from the bow formation and drop downwards following a gravitational pull, as the surface tension would no longer be high enough to retain the molten metal. An increase of pressure below the meniscus can counteract gravity to allow for a larger lip to strip distance. Regulating the pressure may allow the meniscus coating process to be started at a low pressure and ramp up the pressure as the lip to strip distances increases. Larger lip to strip distances may allow for an increased amount of strip shape variation possibilities, for example.
Referring to
While a pair of coating trays (10) is shown, an embodiment of the present disclosure may include a single coating tray (10). Each coating tray (10) includes top lip (12), bottom edge (14), and lip adjacent sidewall (16) that extends between top lip (12) and bottom edge (14). Top lip (12) and/or coating tray (10) comprises a ceramic, a plastic ceramic, metal, a non-wetting material, and/or other suitable material and combinations thereof. Coating tray (10) may be heated via gas burners and/or induction heating. Each top lip (12) is able to coat at least one surface (18) of metal strip (20) with a coating metal. When metal strip (20) passes next to coating tray (10), surface tension bridges a gap between the molten metal at top lip (12) and metal strip (20) to coat metal strip (20) with the coating metal. As will be understood by those of skill in the art, other coating tray configurations can also be used in the coating apparatus.
The coating metal comprises a molten metal, such as zinc, aluminum, tin, and/or terne metal (including lead and tin), or other molten metal usable to coat a metal strip. Suitable coating metals are well-known in the art. In the event that more than one coating tray is used, each coating tray may contain the same coating metal, or a different coating metal, such that different coating metals are applied on opposite sides of metal strip (20). A first surface (18) of the metal strip (20) may be coating with a first coating metal, and a second opposite surface (18) may be coated with a second coating metal. For example, one side of metal strip (20) may be coated with a tin coating and another side of metal strip (20) may be coated with a zinc or terne metal coating.
Referring to
Disposed within roll enclosure (22) may be at least one roll (26). A pair of rolls (26) is shown in the embodiment of
Cover (24) of roll enclosure (22) includes aperture (28). A portion of aperture (28) in cover portion (24) may be covered by baffles, as described below, to minimize ingress of air into roll enclosure (22) near steel strip (20) or to minimize contact of the steel strip with the ambient atmosphere prior to coating. Aperture (28) includes strip receiving portion (30), which is that portion of the aperture (28) occupied by the metal strip (20) during coating, and at least one open portion (32), which is any portion of the aperture (28) not occupied by the metal strip (20) during coating (
At least one adjustable plate or baffle (34) may be disposed to cover some or all of an open portion (32). Baffle (34) may be manually and/or automatically adjusted into a desired position via, for example, edge sensing systems such as those provided by EMG-Automation GmBH, D-57482 Wenden, Germany; Keyence Corporation, Itasca, Ill.; FMS Force Measuring Systems AG, Hoffman Estates, Ill.; and Microsonic GmbH, 44227 Dormund, Germany; and as will be apparent to one of ordinary skill in the art in view of the teachings herein.
Referring to
Additionally or alternatively, as shown in
Each coating tray (10) may include surface (44) such that a second seal (42) may be disposed between surface (44) and cover (24) of roll enclosure (22). For example, as shown in
In addition to the physical barriers described above, or alternatively, a gas barrier may be used to help to seal the enclosure. A gas delivery device may be disposed on the coating apparatus before the top lip of the coating tray generally proximate to the cover of the roll enclosure. The gas delivery device operates to deliver a gas, such as nitrogen, in the area of the coating apparatus prior to the coating of the metal strip. This delivery of a gas can build a positive pressure about the pre-coated metal strip. In this way, it can assist with providing or maintaining a protective atmosphere about the pre-coated metal strip and thereby minimize effects of ambient atmosphere on the pre-coated metal strip. The gas delivery device may additionally deliver other suitable gases, such as hydrogen, to improve heat transfer properties and/or to induce chemical reactions on the metal strip prior to the coating of the metal strip. For example, the gas delivery device may deliver nitrogen and low levels of hydrogen that are below an explosive limit and in a sufficient amount to allow for heat transfer improvements and to react with oxygen that is present before and upstream of the top lip of the coating tray. The composition and effects of various desirable gases is known to those of skill in the art of coating metal strip.
The gas delivery device may also help to solidify any excess coating metal and minimize the negative effects of any drips of molten metal from the coating lips. For example, when the gas delivery device is disposed below the top lip of the coating tray, the stream of gas from the gas delivery device can freeze any drips of coating metal that may escape from the metal strip and drop downwards toward the roll enclosure. Without the gas delivery device, molten metal may drip onto the shaping rolls (26) and freeze onto these rolls, ultimately causing them to stop operation. If the gas delivery devices freeze the molten metal, this can help to prevent, or at least minimize, this plating of the coating metal onto the rolls.
At least one gas delivery device (44), as shown in
Gas delivery device (44) may comprise a pipe and nozzle assembly (46), as shown in
In operation, metal strip (20) is treated, as described above, to achieve the desired condition, such as an oxide free, clean state. Metal strip (20) is then advanced into roll enclosure (22) and may be shaped by a pair (or more) of rolls (26). When in roll enclosure (22), the condition of metal strip (20) is maintained as roll enclosure (22) includes a protective atmosphere about metal strip (20). Metal strip (20) advances through aperture (28) toward top lip (12) of coating tray (10) to allow one or both surface(s) (18) of metal strip (20) coated with coating metal as described above. Physical and/or air pressure barriers, such as baffle (34) and/or gas delivery device (44), are positioned between top lip (12) and the rolls (26) to assist with maintaining a substantially oxygen-free environment about pre-coated metal strip (20) both within roll enclosure (22) and before coating, preventing ambient air from leaking in through aperture (28) into roll enclosure (22), and minimizing the effect of ambient atmosphere on pre-coated metal strip (20) after metal strip (20) advances from aperture (28) of roll enclosure (22) toward top lip (12) of coating tray (10).
For example, flat portions (36) of baffles (34) are disposed over open portions (32) of aperture (28). Baffles (34) may additionally include sidewall portions (38) that seal against lip adjacent sidewall (16) of coating tray (10). Baffles (34) seal some or all of open portions (32) of aperture (28) to prevent ambient air/oxygen from leaking into the protected environment within roll enclosure (22). As metal strip (20) advances through aperture (28) and past baffles (34) toward top lip (12) of coating tray (10), sidewall portions (38) seal against side edge portions of advances metal strip (20).
Additionally or alternatively, as described above, gas delivery devices (44) such as pipe and nozzle assemblies (46) or plenums (48) are disposed proximate to cover (24) of roll enclosure (24) and between top lip (12) and rolls (26). As metal strip (20) advances past the rolls (26) and before it is coated via top lip (12), gas delivery devices (44) deliver a gas such as nitrogen to metal strip (20), assisting to maintain the clean, oxide-free state of metal strip (20). Additionally, if upper portions of metal strip (20) have already been coated with coating metal and portions of that coating metal escape and drip down toward roll enclosure (22) in a molten state, for example, gas delivery devices (44) may assist to solidify the molten coating metal and prevent molten metal from passing into roll enclosure (22) to potentially affect the operation of the rolls (26).
Metal strip (20) advances to top lip (12), which contains a sufficient amount of coating metal to, via surface tension, adhere to and coat surface (18) of metal strip (20). The thickness of molten metal coating on metal strip (20) may be further adjusted by, for example, jet nozzles as described in U.S. Pat. No. 5,453,127, incorporated by reference above.
Having shown and described various embodiments of the present invention, further adaptations of the methods and systems described herein may be accomplished by appropriate modifications by one of ordinary skill in the art without departing from the scope of the present invention. Several of such potential modifications have been mentioned, and others will be apparent to those skilled in the art. For instance, the examples, embodiments, geometries, materials, dimensions, ratios, steps, and the like discussed above are illustrative. Accordingly, the scope of the present invention should be considered in terms of the following claims and is understood not to be limited to the details of structure and operation shown and described in the specification and drawings.
This application claims priority to U.S. Provisional Patent Application Ser. No. 61/490,862, filed May 27, 2011, entitled “BAFFLE SYSTEM FOR MENISCUS COATING APPARATUS,” the disclosure of which is incorporated by reference herein.
Number | Date | Country | |
---|---|---|---|
61490862 | May 2011 | US |