Mercury vapor discharge lamp containing means for reducing mercury leaching

Abstract

A mercury vapor discharge lamp having an envelope of light-transmitting vitreous material containing an inert starting gas and a quantity of elemental mercury at least partially convertible to soluble mercury. Enclosed within the lamp is an amount of chemical agent suitable for electrochemically reducing a substantial portion of the soluble mercury to elemental mercury when the lamp is pulverized as a result of disposal. Preferably, the chemical agent is an element (i.e., copper or iron) which has an electrode potential for oxidation reactions higher than mercury. In a preferred embodiment, the chemical agent is sealed within an enclosure (e.g., glass) which is rupturable upon pulverization of the lamp. The sealed enclosure is disposed within the envelope or external to the envelope, such as within a cavity defined by a lamp base member. In another embodiment, the chemical agent is mixed with the basing cement used to secure the lamp bases to the envelope.

Description

CROSS-REFERENCE TO A RELATED APPLICATION

This application discloses, but does not claim, inventions which are claimed in U.S. Ser. No. 07/773,834 filed concurrently herewith and assigned to the Assignee of this application.

FIELD OF THE INVENTION

This invention relates in general to mercury vapor arc discharge lamps and pertains, more particularly, to a fluorescent lamp which contains a chemical agent for substantially reducing the amount of soluble mercury measurable after pulverization of the lamp.

BACKGROUND OF THE INVENTION

Fluorescent lamps are well known in the art and are characterized as low pressure arc discharge lamps which include a pair of electrodes sealed in an elongated envelope whose interior surface is coated with phosphor. The envelope contains a quantity of mercury and a rare gas at a reduced pressure, for example, in the order of 1-5 torr.

During lamp manufacture, about 10-40 milligrams of elemental mercury is sealed in each fluorescent lamp. It is known that most of this mercury adheres to the phosphor coating with only a very small portion of the mercury being in the form of mercury vapor. After the alkali earth metal oxides coating the lamp electrodes are volatized, the oxides decompose in the discharge space and the freed oxygen converts some of this elemental mercury to a salt or compound such as mercuric oxide (HgO) which is highly soluble.

There is a growing concern that a waste stream resulting from the disposal of fluorescent lamps may leach excessive amounts of this soluble form of mercury. One method of measuring the amount of soluble mercury which may leach from the waste stream resulting from the disposal of fluorescent lamps is described in the Toxicity Characteristic Leaching Procedure (TCLP) prescribed on pages 26987-26998 of volume 55, number 126 of the Jun. 29, 1990 issue of the Federal Register. According to the procedure, the lamp being tested is pulverized into granules having a surface area per gram of material equal to or greater than 3.1 cm.sup.2 or having a particle size smaller than 1 cm in its narrowest dimension. Following pulverization, the granules are subjected to a sodium acetate buffer solution having a pH of approximately 4.93 and having a weight twenty times the weight of the granules.

At the present time, the Environmental Protection Agency defines a maximum concentration level for mercury at 0.2 milligram leachable mercury per liter extract fluid when the TCLP is applied. According to present standards, a fluorescent lamp is considered non leachable when less than 0.2 milligram per liter of leachable mercury results from a TCLP extraction.

Various methods have been proposed which attempt to treat or process burned-out discharge lamps or scrap lamp exhaust tubing containing mercury in order to reclaim the mercury and thereby reduce the amount of mercury-contaminated scrap glass. For example, U.S. Pat. No. 4,268,306 (Bjorkman) discloses a treatment whereby the expanded or scrapped lamps are crushed into fragments which are then placed in a treatment vessel in which the mercury is recovered by distillation processes. This treatment is carried out batchwise in a sealed container into which nitrogen is introduced. The container is heated and placed under vacuum so as to vaporize the mercury. The vaporized mercury is then removed from the container through a bottom outlet and condensed in a cooling trap. It is apparent that following the process, the treated lamp fragments (i.e., glass and phosphor) may be dumped without concerns about mercury leaching.

U.S. Pat. No. 4,715,838 (Kulander) teaches a method and apparatus for recovering the luminescent material from mercury vapor electric discharge lamps whereby the amount of lamp waste requiring treatment in the distillation chamber can be reduced thereby increasing the capacity of the chamber with respect to the number of lamps. After the ends of the lamp bulb or tube are separated from the intermediate bulb, the luminescent material is loosened from the inner wall surface of the bulb part with the aid of a stripping device which is arranged to be inserted into the bulb part from one end thereof. The loosened material is collected with the aid of a suction device connected to the other end of the bulb part and thereafter may be introduced into the distillation chamber, thereby obviating the need to fill the chamber with the residual "clean" glass bulb.

Japanese Patent Application No. 58-184558 (Kitsugi et. al.) teaches a method for solidifying discarded fluorescent lamps and insolubilizing the mercury contained therein. The method involves adding sulfur to crushed fluorescent lamp waste in the proportion of 0.1-5 parts by weight per 100 parts by weight of the discard. The result is placed into a ball mill and pulverized an amount of time sufficient to produce granules with sizes 5 millimeters or less. Cement and water were added and the result is kneaded. The kneaded material prepared in this way is put into molds so as to form a stabilized solidified material having a mercury concentration of less than 0.005 milligram per liter water.

U.S. Pat. No. 4,435,284 (Heytmeijer) teaches a process for removing residual mercury from scrap fluorescent lamp exhaust tubulation or similar scrap glass. A very small predetermined amount of finely divided silica or alumina powder is added to the mercury contaminated scrap glass and the mixture is agitated for a very short predetermined time during which the mercury is stripped from the tubulation. The separated mercury, powder and glass mixture is then decanted through a screen of suitable mesh to remove the separated mercury and powder from the glass and the mercury is then rinsed with a suitable solvent to remove the oxide powder from the mercury.

While these processes may be effective in separating mercury from lamp fragments or scrap glass or for insolubilizing the mercury contained in discarded fluorescent lamps, each process requires treatment equipment which may be relatively expensive.

SUMMARY OF THE INVENTION

It is, therefore, an object of the present invention to obviate the disadvantages of the prior art.

It is still another object of the invention to provide a mercury vapor discharge lamp which can be considered non leaching upon disposal.

It is another object of the invention to provide a mercury vapor discharge lamp which can be disposed of without prior expensive treatment to reclaim mercury.

These objects are accomplished in one aspect of the invention by the provision of a mercury vapor discharge lamp having an envelope of light-transmitting vitreous material containing an inert starting gas and a quantity of elemental mercury at least partially convertible to soluble mercury. First and second electrodes are located within the envelope for establishing an arc discharge therebetween. An effective amount of a chemical agent suitable for electrochemically reducing a substantial portion of the soluble mercury to elemental mercury when the lamp is pulverized to granules and subjected to a suitable aqueous acid solution is located within the lamp and effectively remote from the arc discharge.

In accordance with further teachings of the present invention, the chemical agent is an element having an electrode potential for oxidation reactions higher than mercury but not sufficiently active to displace hydrogen from the aqueous acid solution. Preferably, the chemical agent is selected from the group consisting of iron, copper, tin, indium, nickel, cobalt and titanium. In one embodiment, the chemical agent comprises approximately 0.5 to 5 grams of copper powder or copper dust. In another embodiment, the chemical agent comprises approximately 0.25 gram to 5 grams of iron powder.

In accordance with further aspects of the present invention, the lamp further includes a sealed enclosure (e.g., glass) for containing the chemical agent. The sealed enclosure is disposed within the envelope or external to the envelope, such as with a cavity defined by a lamp base member. The sealed enclosure is rupturable upon pulverization of the lamp.

In accordance with still further aspects of the present invention, the chemical agent is mixed with the basing cement used to secure one or more of the lamp bases to the lamp envelope.

Additional objects, advantages and novel features of the invention will be set forth in the description which follows, and in part will become apparent to those skilled in the art upon examination of the following or may be learned by practice of the invention. The aforementioned objects and advantages of the invention may be realized and attained by means of the instrumentalities and combination particularly pointed out in the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will become more readily apparent from the following exemplary description in connection with the accompanying drawings, wherein:

FIG. 1 represents a front elevational view, partially broken away, of a mercury vapor discharge lamp according to the present invention;

FIG. 2 is a perspective view of a portion of a mercury vapor discharge lamp according to one embodiment of the invention; and

FIG. 3 is a perspective view of a portion of a mercury vapor discharge lamp according to another embodiment of the invention.

BEST MODE FOR CARRYING OUT THE INVENTION

For a better understanding of the present invention, together with other and further objects, advantages and capabilities thereof, reference is made to the following disclosure and appended claims in connection with the above-described drawings.

To overcome the disadvantages mentioned above with respect to the prior art, the present invention provides a method of rendering the mercury in a mercury vapor discharge lamp non leachable upon disposal without necessitating the need for relatively expensive treatment equipment as discussed above. More specifically, the invention prevents leaching of mercury as measured by TCLP by the incorporation of a substance (i.e., materials or agents) in the lamp construction which renders the mercury non leachable upon disposal. In accordance with the teachings of the present invention, these substances comprise chemical agents (i.e., elements, compounds or combinations thereof) which electrochemically have the potential to reduce soluble mercury produced during lamp operation to elemental mercury. Elemental (metallic) mercury is not leachable as measured by the TCLP.

In one embodiment, the chemical agent is located "effectively remote" from the arc discharge so as not to interfere with the discharge or the operation of the lamp. One suitable method for disposing the chemical agent "effectively remote" from the discharge is to contain the chemical agent within a sealed enclosure within the lamp envelope. Alternatively, the chemical agent may be disposed remote from the arc discharge by disposing the chemical agent within one or more of the lamp bases. In the latter instance, the chemical agent may be located within a cavity formed by the lamp base or may be mixed with the basing cement used to secure the lamp base(s) to the envelope. If the chemical agent is placed within the base cavity, the chemical agent may be further contained within a sealed enclosure secured to an inner surface of the base.

Referring to the drawings with greater particularity, there is illustrated in FIG. 1 a mercury vapor discharge lamp 10, such as a fluorescent lamp, comprising an elongated sealed envelope 12 of light-transmitting vitreous material. Envelope 12 is filled with an inert gas such as argon at a low pressure, for example two torr, and a quantity of mercury 40, at least enough to provide a low vapor pressure of about six mm. of Ag during operation. An electrode 14 and 16 is disposed at each end of envelope 12 supported by lead-in wires 18, 20, and 22, 24, respectively. Electrodes 14 and 16 are coated with electron-emitting materials such as BaO--SrO--CaO containing MgZrO.sub.3. The lead-in wires extend through stem presses 26, 28 in mount stems 30, 32 to the contacts in base members 34, 36 secured to the ends of envelope 12.

A phosphor coating 38 is disposed on the interior surface of envelope 12. Phosphor coating 38, which may be a halophosphate phosphor such as Cool White, is responsive to the ultraviolet radiation generated by the arc discharge established between electrodes 14, 16 to provide a desired emission spectrum.

During lamp manufacture, about 10-40 milligrams of elemental mercury is sealed in each fluorescent lamp. During lamp life, most of this mercury adheres to the phosphor coating with only a very small portion of the mercury being in the form of mercury vapor. After the alkali earth metal oxides coating the lamp electrodes are volatized, the oxides decompose in the discharge space and the freed oxygen converts some of this elemental mercury to a salt or compound such as mercuric oxide (HgO) which is highly soluble.

In accordance with the teaching of the present invention, located within the lamp is an effective . amount of a chemical agent 42 suitable for electrochemically reducing a substantial portion of the soluble mercury available within the lamp to elemental mercury measurable when the lamp is pulverized to granules and subjected to a suitable aqueous acid solution. Evidence of a substantial portion of the soluble mercury having been reduced is apparent when the amount of soluble mercury is less than 0.2 milligram per liter of the aqueous acid solution.

Soluble mercury is produced during lamp operation and during TCLP as the result of the action of elemental mercury with other metals found in the lamp (e.g., lead wires and metal bases). The chemical agent is generally an element, compound or combinations thereof which is described as "more active" or "higher" than mercury in a listing of the standard electrode potentials for oxidation reactions in the Electrochemical (or Electromotive) Series of Oxidation Potentials. Typically, the chemical agent should be more active than mercury in order to displace mercury ions but not sufficiently active to displace hydrogen from water or a mild acid. Preferably, the chemical agent is selected from the group consisting of iron, copper, tin, indium, nickel, cobalt and titanium.

The chemical agent may be used in various forms. For example, the chemical agent may be in the form of a powder, dust, wire mesh or metallic foil. The amount or size of the chemical agent is directly related to the surface area and surface condition. A metallic powder or dust is preferred over a solid mass because of their large effective surface areas. Because of their availability and inexpensive cost, iron and copper, in the form of a powder or dust, are preferred. Typical amounts of iron and copper which are effective in reducing the amount of leachable mercury are from about 0.1 gram to 10 grams.

Preferably, the amount of chemical agent present is sufficient to electrochemically reduce the amount of soluble mercury within the lamp which is leached at the time of disposal to less than 0.2 milligram per liter of an aqueous acid solution such as a sodium acetate buffer solution as prescribed by TCLP. An effective amount of iron powder is at least about 0.25 gram.

Referring next to FIGS. 2 and 3, there are shown two preferred embodiments of the present invention, wherein several of the same constituent members as those in FIG. 1 are denoted by the same reference numerals In the first embodiment as illustrated in FIG. 2, chemical agent 42 is contained in a sealed enclosure or vial 44 disposed within lamp envelope 12. The sealed enclosure is formed from a material which is easily rupturable when the lamp is crushed for disposal in a landfill or to meet the size reduction required by TCLP. Rupture of the sealed enclosure facilitates dispersion of the chemical agent with the lamp granules. Glass is a suitable material for sealed enclosure 44.

In order to prevent movement of the sealed enclosure within the lamp envelope, sealed enclosure 44 containing chemical agent 42 may be secured to mount stem 30 by a suitable means. In FIG. 2, a securing wire or strap 46 is wrapped around mount stem 30 and sealed enclosure 44.

In the second embodiment as illustrated in FIG. 3, sealed enclosure 44 containing chemical agent 42 is disposed external to envelope 12 and within a cavity 48 formed by base member 34. To prevent movement within the base member, the sealed enclosure may be secured to an inner surface of the base member by a suitable means such as an epoxy or cement (not shown).

Sealing the chemical agent within the enclosure 44 facilitates handling of the material during manufacturing and insures that the active material remains contained during normal lamp life. Moreover, in the embodiment illustrated in FIG. 2, the sealed enclosure prevents the active material from adversely affecting the arc discharge or the phosphor coating during lamp operation.

Indium has been used in mercury discharge lamps in the past as an amalgam-forming material for regulating the mercury vapor pressure and thus permitting the lamp to be operated at high power loadings and under high ambient temperature conditions. Typically, the amount of indium in such an application may be in the order of 150 milligrams. Since in the present invention it is desirable that the chemical agent not affect the mercury vapor pressure, the indium (or any other chemical agent which may otherwise affect the operation of the lamp) is preferably disposed external to the lamp envelope (e.g., in the lamp base) or, if disposed within the lamp envelope, should remain contained within a sealed enclosure during lamp operation.

It is within the scope of the invention to dispose the chemical agent in locations other than those shown in the drawings. For example, it is possible to locate the sealed enclosure containing the chemical agent at a location 50 (FIG. 3) within mount stem 30. Alternatively, the chemical agent may include an alloy from which the base member is made of a coating of the chemical agent on a surface of at least one of the lamp base members 34, 36. The chemical agent may also be incorporated with the adhesive or basing cement 52 (FIG. 3) used to secure one or more of the base members 34, 36 to lamp envelope 12. Finally, the chemical agent may be disposed at more than one location within the lamp.

EXAMPLE I--COPPER

In a typical but non-limitative example of a mercury vapor discharge lamp in accordance with the teachings of the present invention, both "new" and "used" 40-watt Cool White fluorescent lamps in the presence of 5 grams of either copper metal powder or or copper metal dust are subjected to the Federal TCLP for leachable mercury. The "used" lamps utilized in the test were lamps expected to be near the end of life.

In one test, copper metal powder available from Fisher Scientific and designated #C434 is first subjected to a dilute HCl wash prior to use. This material has a surface area of 0.34 meter.sup.2 /gram. In the other test, copper metal dust also available from Fisher Scientific and designated #431 is utilized without prewashing. This latter material has a surface area of 0.35 meter.sup.2 /gram. According to the TCLP measuring procedure, each lamp is pulverized into granules having a surface area per gram of material equal to or greater than 3.1 cm.sup.2 or having a particle size smaller than 1 cm in its narrowest dimension. Following pulverization, the granules are subjected to a sodium acetate buffer solution having a pH of approximately 4.93 and having a weight twenty times the weight of the granules. Mercury in the TCLP extract is determined by cold vapor atomic absorption spectrometry as prescribed by the TCLP procedure. The results of these tests are shown in the following TABLE I:

TABLE I______________________________________ ACTIVE AMOUNT OF MERCURYLAMP SUBSTANCE LEACHED BY TCLP______________________________________F40/CW 5 GRAMS 0.06 MG/L(NEW) COPPER POWDERF40/CW 5 GRAMS 0.14 MG/L(USED) COPPER POWDERF40/CW 5 GRAMS 0.12 MG/L(NEW) COPPER DUSTF40/CW 5 GRAMS 0.18 MG/L(USED) COPPER DUST______________________________________

Typical TCLP results obtained on similar lamps but not containing an effective amount of a chemical agent as described by the present invention range from 0.3 mg/L Hg to 2.3 mg/L Hg. According to TABLE I, it is evident that the addition of 5 grams of copper powder or copper dust substantially reduces the amount of soluble mercury.

EXAMPLE II--COPPER

In a second example of a mercury vapor discharge lamp in accordance with the teachings of the present invention, 20-watt Cool White fluorescent lamps in the presence of approximately 5 grams of either copper metal dust, a mesh of copper, or a sheet of copper are subjected to the Federal TCLP for leachable mercury. The copper metal dust is similar to that used in the previous test. The copper mesh is constructed from strands having a 0.15 millimeter diameter. The copper sheet consists of 35 pieces of copper each measuring 5.5 millimeters by 50 millimeters.

According to the TCLP measuring procedure, each lamp is pulverized into granules having a surface area per gram of material equal to or greater than 3.1 cm.sup.2 or having a particle size smaller than 1 cm in its narrowest dimension. Following pulverization, the granules are subjected to a sodium acetate buffer solution having a pH of approximately 4.93 and having a weight twenty times the weight of the granules. Mercury in the TCLP extract is determined by cold vapor atomic absorption spectrometry as prescribed by the TCLP procedure. The results of these tests are shown in the following TABLE II:

TABLE II______________________________________ SURFACEACTIVE AREA AMOUNT OF MERCURYSUBSTANCE OF COPPER LEACHED BY TCLP______________________________________NO COPPER -- 0.63 MG/LADDITIONCOPPER DUST 1.8 SQ. 0.05 MG/L(5 GRAMS) METERCOPPER MESH 0.03 SQ. 0.11 MG/L(4.9 GRAMS) METERCOPPER SHEET 0.01 SQ. 0.19 MG/L(5 GRAMS) METER______________________________________

TABLE II above shows the effect of various forms of copper and their resulting surface areas on the amount of mercury leached by TCLP. It is apparent therefrom that in order to limit the amount of soluble mercury to less than 0.2 milligram per liter of the aqueous acetate solution used in the test procedure, the total surface area of the active substance should be greater than or equal to approximately 0.01 meter.sup.2.

EXAMPLE III--IRON

In another example of a mercury vapor discharge lamp in accordance with the teachings of the present invention, 40-watt Cool White fluorescent lamps in the presence of 0.5 to 5 grams of iron powder are subjected to the Federal TCLP for leachable mercury. Suitable iron powder is available from Fisher Scientific and designated I60. The surface area of the powdered iron is 0.15 meter.sup.2 /gram. According to the TCLP measuring procedure, each lamp is pulverized into granules having a surface area per gram of material equal to or greater than 3.1 cm.sup.2 or having a particle size smaller than 1 cm in its narrowest dimension. Following pulverization, the granules are subjected to a sodium acetate buffer solution having a pH of approximately 4.93 and having a weight twenty times the weight of the granules. Mercury in the TCLP extract is determined by cold vapor atomic absorption spectrometry as prescribed by the TCLP procedure. The results of these tests are shown in the following TABLE III:

TABLE III______________________________________ SURFACEACTIVE AREA AMOUNT OF MERCURYSUBSTANCE OF IRON LEACHED BY TCLP______________________________________NO IRON -- 0.63 MG/LADDITIONIRON POWDER 0.075 SQ. 0.11 MG/L(0.5 GRAM) METERIRON POWDER 0.15 SQ. 0.05 MG/L(1 GRAM) METERIRON POWDER 0.75 SQ. 0.05 MG/L(5 GRAMS) METER______________________________________

Table III would suggest that the quantity of iron powder necessary to limit the amount of soluble mercury to less than 0.2 milligram per liter of the aqueous acetate solution used in the test procedure, can be even less than 0.5 gram which translates into a surface area being less than 0.075 meter.sup.2.

EXAMPLE IV--IRON

In a fourth example of a mercury vapor discharge lamp in accordance with the teachings of the present invention, 20-watt Cool White fluorescent lamps in the presence of iron metal dust, iron wire, or iron foil are subjected to the Federal TCLP for leachable mercury. The iron powder is similar to that used in the previous test. The iron wire has a length of 1500 millimeters and a diameter of 0.23 millimeter and is of reagent grade. The iron foil consists of three 0.127 millimeter thick pieces having the following dimensions: 1.2 mm by 25 mm, 6.2 mm by 25 mm, and 9.6 mm by 25 mm. The iron foil is available from Strem Chemical and is designated #93-2661. According to the TCLP measuring procedure, each lamp is pulverized into granules having a surface area per gram of material equal to or greater than 3.1 cm.sup.2 or having a particle size smaller than 1 cm in its narrowest dimension. Following pulverization, the granules are subjected to a sodium acetate buffer solution having a pH of approximately 4.93 and having a weight twenty times the weight of the granules. Mercury in the TCLP extract is determined by cold vapor atomic absorption spectrometry as prescribed by the TCLP procedure. The results of these tests are shown in the following TABLE IV:

TABLE IV______________________________________ SURFACEACTIVE AREA AMOUNT OF MERCURYSUBSTANCE OF IRON LEACHED BY TCLP______________________________________NO IRON -- 0.93 MG/LADDITIONIRON POWDER 0.015 SQ. 0.83 MG/L(0.1 GRAM) METERIRON POWDER 0.038 SQ. 0.19 MG/L(0.25 GRAM) METERIRON POWDER 0.15 SQ. LESS THAN(1.0 GRAM) METER 0.05 MG/LIRON WIRE 0.001 SQ. 0.35 MG/L(0.5 GRAM) METERIRON FOIL 0.0004 SQ. 0.65 MG/L(0.5 GRAM) METER______________________________________

TABLE IV above shows the effect of surface area active material on the amount of mercury leached by TCLP. It is apparent therefrom that in order to limit the amount of soluble mercury to less than 0.2 milligram per liter of the aqueous acid solution used in the test procedure, the weight of the iron powder should be greater than or equal to 0.25 gram which translates into a total surface area greater than or equal to approximately 0.038 meter.sup.2. While the iron wire and iron foil reduced the amount of soluble mercury leached by TCLP to 0.35 and 0.65 milligram per liter, respectively, it is believed that increasing the surface area of the wire or foil is necessary in order to limit the amount of soluble mercury to less than 0.2 milligram per liter.

EXAMPLE V--IRON IN BASING CEMENT

In a fifth example of a mercury vapor discharge lamp in accordance with the teachings of the present invention, each lamp base member was secured to respective ends of a group of new 40-watt Cool White fluorescent lamps by means of basing cement containing 0.5 gram of powdered iron. Suitable iron powder is available from Fisher Scientific and designated I60. The surface area of the powdered iron is 0.15 meter.sup.2 per gram. The basing cement into which the iron powder was mixed is manufactured by GTE Product Corporation in Towanda, PA. According to the TCLP measuring procedure, each lamp is pulverized into granules having a surface area per gram of material equal to or greater than 3.1 cm.sup.2 or having a particle size smaller than 1 cm in its narrowest dimension. Following pulverization, the granules are subjected to a sodium acetate buffer solution having a pH of approximately 4.93 and having a weight twenty times the weight of the granules. Mercury in the TCLP extract is determined by cold vapor atomic absorption spectrometry as prescribed by the TCLP procedure. The results of this test is shown in the following TABLE V:

TABLE V______________________________________ SURFACE AMOUNT OFACTIVE AREA OF MERCURY LEACHEDSUBSTANCE IRON POWDER BY TCLP______________________________________NO IRON -- 0.56 MG/LADDITIONIRON POWDER 0.075 SQ. 0.09 MG/LIN BASING METERCEMENT(0.5 .times. 2 GRAM)______________________________________

TABLE V above shows that iron powder mixed in the basing cement of new 40-watt fluorescent lamps electrochemically reduces a substantial portion of soluble mercury to elemental mercury when subjected to TCLP. Since the amount of soluble mercury within a lamp increases as the lamp ages, it is believed that in order to insure that a substantial portion of the soluble mercury in an aged lamp is reduced to elemental mercury, approximately 1.0 gram of iron powder should be mixed with the basing cement of each base.

There has thus been shown and described a mercury vapor discharge lamp containing a chemical agent for substantially reducing the amount of soluble mercury measurable after pulverization of the lamp. The invention provides a discharge lamp which can be disposed of in a landfill without prior expensive treatment to reclaim mercury.

While there have been shown and described what are at present considered to be the preferred embodiments of the invention, it will be apparent to those skilled in the art that various changes and modifications can be made herein without departing from the scope of the invention. Therefore, the aim in the appended claims is to cover all such changes and modifications as fall within the true spirit and scope of the invention. The actual scope of the invention is intended to be defined in the following claims when viewed in their proper perspective based on the prior art.

Claims

1. In a mercury vapor discharge lamp having an envelope of light-transmitting vitreous material containing an inert starting gas and a quantity of elemental mercury at least partially convertible to soluble mercury, first and second electrodes located within said envelope for establishing an arc discharge therebetween, the improvement comprising: an effective amount of a chemical agent located within said lamp so as not to interfere with the arc discharge or the operation of the lamp, said chemical agent electrochemically reducing portion of said soluble mercury to elemental mercury when said lamp is pulverized to granules and subjected to a suitable aqueous acid solution, said chemical agent being in an amount such that the remaining portion of soluble mercury leachable after said portion of soluble mercury is electrochemically reduced to elemental mercury is less than 0.2 milligram per liter of said aqueous acid solution.

2. The mercury vapor discharge lamp of claim 1 wherein said chemical agent is an element having an electrode potential for oxidation reactions higher than mercury but not sufficiently active to displace hydrogen from said aqueous acid solution.

3. The mercury vapor discharge lamp of claim 2 wherein said chemical agent is selected from the group consisting of iron, copper, tin, indium, nickel, cobalt and titanium.

4. The mercury vapor discharge lamp of claim 3 wherein said chemical agent comprises approximately 0.5 to 5 grams of copper powder or copper dust.

5. The mercury vapor discharge lamp of claim 3 wherein said chemical agent comprises approximately 0.25 gram to 5 grams of iron powder.

6. The mercury vapor discharge lamp of claim 1 wherein said chemical agent is contained within a sealed enclosure, said sealed enclosure being rupturable upon pulverization of said lamp.

7. The mercury vapor discharge lamp of claim 6 wherein said sealed enclosure is disposed within said envelope.

8. The mercury vapor discharge lamp of claim 6 further comprising at least one base member secured to said envelope and defining a cavity, said sealed enclosure containing said chemical agent being disposed within said cavity of said base member.

9. The mercury vapor discharge lamp of claim 6 wherein said sealed enclosure containing said chemical agent is glass.

10. The mercury vapor discharge lamp of claim 1 wherein said lamp comprises at least one base member secured to said envelope with basing cement means, said chemical agent being mixed with said basing cement means.

11. In a mercury vapor discharge lamp having an envelope of light-transmitting vitreous material containing an inert starting gas and a quantity of elemental mercury at least partially convertible to soluble mercury, first and second electrodes located within said envelope for establishing an arc discharge therebetween, the improvement comprising: an effective amount of a chemical agent selected from the group consisting of iron, copper, tin, nickel, cobalt and titanium located within said lamp, said chemical agent electrochemically reducing a portion of said soluble mercury to elemental mercury when said lamp is pulverized to granules and subjected to a suitable aqueous acid solution, said chemical agent being in an amount such that the remaining portion of soluble mercury leachable after said portion of soluble mercury is electrochemically reduced to elemental mercury is less than 0.2 milligram per liter of said aqueous acid solution.

12. The mercury vapor discharge lamp of claim 11 wherein said chemical agent is disposed within said envelope.

13. The mercury vapor discharge lamp of claim 11 further comprising at least one base member secured to said envelope and defining a cavity, said chemical agent being disposed within said said cavity.

14. The mercury vapor discharge lamp of claim 11 wherein said lamp comprises at least one base member secured to said envelope with basing cement means, said chemical agent being mixed with said basing cement means.

15. The mercury vapor discharge lamp of claim 11 wherein said lamp is a fluorescent lamp.