This application is the National Stage entry under § 371 of International Application No. PCT/JP2020/039698, filed on Oct. 22, 2020, and which claims the benefit of priority to Japanese Application No. 2019-192372, filed on Oct. 22, 2019. The content of each of these applications is hereby incorporated by reference in its entirety.
The present invention relates to a mesh hook surface fastener, a production method therefor, and a production method for a surface fastener-attached molded body integrally including the mesh surface fastener.
Conventionally, as a means for attaching a target object to a surface of another object, there has been used a method of fixing a surface fastener having hook-shaped engagement elements (what is called a hook surface fastener) to a surface of one of the target object and the other object and fixing a surface fastener having loop-shaped engagement elements (what is called a loop surface fastener) to a surface of the other, and laying engagement element surfaces of these surface fasteners on each other to engage their engagement elements, thereby fixing the target object to the surface of the other object.
In recent years, for forming a seat structure of automobiles and airplanes, widely used is a method of injecting a foamable resin liquid of polyurethane or the like into a seat-shaped mold, molding the foamable resin liquid into the seat shape simultaneously with foaming, then fixing a hook surface fastener to a predetermined place of a front surface of a foamed resin molded body (cushioning member) molded into the seat shape, attaching a loop surface fastener to the rear surface of an outer layer member that is to cover the surface of the foamed resin molded body, and covering the surface of the foamed resin molded body with the outer layer member while laying the hook surface fastener and the loop surface fastener on each other to engage them, thereby fixing the outer layer member to the surface of the foamed resin molded body. It is also done to form a groove in the surface of the foamed molded body at a place where to fix the hook surface fastener and fix the hook surface fastener in the groove, thereby reducing a feeling of something foreign due to the hook surface fastener as much as possible.
As a method for fixing the hook surface fastener to the surface of the foamed resin molded body, there is widely used a method of fixing the hook surface fastener to the surface of the foamed resin molded body simultaneously with the molding of the foamed resin molded body instead of pasting the hook surface fastener to the surface of the foamed resin molded body after the molding, specifically, a method called a mold-in forming method of forming a protrusion for forming the aforesaid groove, at a predetermined place in a mold for molding the foamed resin molded body and also providing a recession along an end surface of the protrusion, placing the hook surface fastener in the recession with its engagement element surface facing the bottom surface of the recession (the inner surface of the mold), in this state, injecting the foamable resin liquid into the mold, and fixing the hook surface fastener to the surface of the foamed resin molded body simultaneously with the molding.
What are important in such a mold-in forming method are that the engagement element surfaces of the hook surface fastener are not covered with the foamed resin and that, even if the hook surface fastener is fixed to the surface of the obtained foamed resin molded body, the foamed resin molded body does not have a great difference in flexibility and stretchability between its part covered with the hook surface fastener and its other part not covered with the hook surface fastener.
If the engagement element surfaces of the hook surface fastener are covered with the foamed resin at the time of the molding, the surface fastener loses its engagement ability and the outer layer member cannot be fixed. Even if the foamed resin is tried to be dissolved and removed using a solvent, it is very difficult to remove the foamed resin filled between the engagement elements, and ordinarily, such a hook surface fastener-attached foamed resin molded body is often discarded.
If, in the obtained foamed resin molded body, its part covered with the hook surface fastener is greatly inferior in flexibility and stretchability to its other part not covered therewith, such a seat gives a seated person a feeling of something foreign and is not comfortable to sit.
By using a mold that can make the aforesaid groove in the surface of the foamed molded body for housing the surface fastener deeper so that the surface fastener is attached to the deep part of this deep groove, it may be possible to prevent the seat from giving a feeling of something foreign to a seated person, but attaching the surface fastener to the deep part of such a deep groove necessitates the engagement mate attached to the outer layer member to also reach the deep part of the deep groove, which complicates the structure and necessitates a special device for sufficiently engaging the engagement mate with the hook surface fastener present in the deep part of the deep groove. Therefore, preferably, the groove where to place the surface fastener to be attached to the surface of the foamed resin molded body need not be very deep, that is, the surface fastener has flexibility and stretchability close to those of the foamed resin molded body so that it does not give a feeling of something foreign to a seated person even if the groove is shallow.
Various means have conventionally been contrived to prevent the engagement element surfaces of the hook surface fastener from being covered with the foamed resin at the time of the mold-in forming.
For example, Patent Document 1 describes that, when a hook surface fastener having a region of hook-shaped engagement elements provided upright on the surface of a base is subjected to mold-in forming, the engagement element region is surrounded by a high wall member so that a foamable resin liquid is prevented from entering the engagement element region.
Further, Patent Document 2 describes that, in the case where a hook surface fastener is set in a recession formed along an end surface of a protrusion in a mold, a fitting element capable of sealing a gap between the recession and the hook surface fastener is formed on the rear surface of the hook surface fastener, thereby preventing a foamable resin liquid from entering engagement element surfaces on the front surface side at the time of the molding of the surface fastener.
Indeed, the use of the arts of these prior documents makes it possible to prevent the engagement element surfaces of the hook surface fastener from being covered with the foamed resin, but the high wall member surrounding the engagement element region or the fitting element provided on the base rear surface impairs the flexibility of the hook surface fastener to give a person seated in such a seat a feeling of something foreign, and the presence of the high wall member surrounding the engagement element region lowers the engagement ability of the hook surface fastener.
Patent Document 3, for example, discloses a mesh hook molded surface fastener that includes a first set of a plurality of thermoplastic strands and a second set of a plurality of strands integrally molded with the first set of strands, not present on the same plane as the first set of strands, and intersecting with the first set of strands, wherein at least one of the first set of strands and the second set of strands include hook-shaped engagement elements.
It is also described that such a mesh hook fastener is suitable as a disposable diaper stopper that prevents sweatiness owing to its high breathability.
Patent Document 3, however, does not describe at all that the mesh hook surface fastener is used in mold-in forming. From common general knowledge, it is easily inferred that, if a surface fastener having a mesh shape is used in mold-in forming, a foamable resin liquid passes through its meshes to enter an engagement element surface side with great force, and hook-shaped engagement elements are covered with a foamed resin to lose their engagement ability. A mesh surface fastener not only has breathability but also has characteristics of easily stretching owing to the elastic function by the deformation of the meshes, and thus being excellent in followability to the movement of an engagement target and not easily giving a feeling of something foreign. Therefore, if its use in the mold-in forming is feasible, the mesh hook fastener is applicable to a part that comes into contact with a person to easily move, such as a cushioning member of a seat structure, and its application range is expected to further widen.
Further, as the resin used for the mesh molded surface fastener, Patent Document 3 only cites non-elastomer thermoplastic resins such as a polyolefin-based resin, polyvinyl chloride, polystyrene, nylon, and polyethylene terephthalate. However, a surface fastener obtained using any of these resins cannot be expected to have required flexibility and stretchability when used for fixing, for example, a cushioning member of a seat structure and an outer layer member.
The present invention was made in consideration of the above and has an object to provide a mesh surface fastener that can be integrated with a foamed resin molded body such as a cushioning member of a seat structure by mold-in forming and can contribute to the widening of its application, a production method therefor, and a production method for a surface fastener-attached molded body.
To solve the aforesaid problem, a mesh hook surface fastener of the present invention includes:
Preferably, the shape holding ribs include two types which are a first shape holding rib the protrusion height of which is relatively small and a second shape holding rib the protrusion height of which is relatively large, and the first shape holding rib and the second shape holding rib are alternately arranged in an adjacent direction.
Preferably, the protrusion height of the first shape holding rib is 0.4 to 0.8 times the protrusion height of the second shape holding rib.
Preferably, a position of outer end surfaces located opposite to surfaces facing the base layer in the overhanging portions of the first shape holding ribs are closer to the base layer than a position of surfaces facing the base layer in the overhanging portions of the second shape holding ribs.
Preferably, the shortest distance of the overhanging portions of one of the adjacent first shape holding rib and second shape holding rib from the other is 0.2 to 0.6 times a distance between the vertical wall portions of the adjacent first shape holding rib and second shape holding rib along a plane orthogonal to a direction in which the vertical wall portions protrude.
Preferably, a ratio at which the vertical wall portions and the overhanging portions forming the shape holding ribs cover the other surface of the base layer is 60 to 100% of a plane area of the base layer.
Preferably, the mesh hook surface fastener is comprised of a thermoplastic elastomer resin.
More preferably, the thermoplastic elastomer resin is a polyester elastomer or a polyamide elastomer.
Preferably, the hook-shaped engagement elements are each at least one selected from:
Preferably, the rows of the second engagement elements as the hook-shaped engagement elements are close to side edges of the base layer which are length-direction end edges of the strands, and the row of the first engagement elements as the hook-shaped engagement elements is between the row of the second engagement elements close to one of the side edges and the row of the second engagement elements close to the other side edge.
Preferably, the rows of the hook-shaped engagement elements and the shape holding ribs are symmetrical across the base layer.
Preferably, on the one surface of the base layer, a row composed only of stems without having any engagement portion is present between the adjacent rows of the hook-shaped engagement elements.
Preferably, a water/oil repellent is applied on outer surfaces of the hook-shaped engagement elements and an outer surface of the one surface of the base layer between the adjacent hook-shaped engagement elements.
Preferably, the hook-shaped engagement elements are covered with a fiber sheet having loop-shaped engagement elements and not coated with a water/oil repellent.
A production method for a mesh hook fastener of the present invention includes:
A manufacturing method for a surface fastener-attached molded body of the present invention includes:
Preferably, the foamed resin molded body is employed as a cushioning member of a seat structure.
In the mesh hook surface fastener of the present invention, out of the shape holding ribs protruding opposite to the hook-shaped engagement elements across the base layer, the adjacent ones have different protrusion heights. Preferably, the first shape holding ribs having a relatively small protrusion height and the second shape holding ribs having a relatively large protrusion height are alternately arranged.
In the case where a foamable resin liquid is injected in the state in which a mesh hook surface fastener is set in a mold with its hook-shaped engagement elements facing the inner surface of the mold, in a conventional mesh hook surface fastener whose adjacent shape holding ribs have the same protrusion height, the foamable resin liquid having passed through gaps between the adjacent shape holding ribs directly reaches meshes of a base layer with great force without any barrier and further tries to pass through up to hook-shaped engagement elements side. In the present invention, on the other hand, since the protrusion heights of the adjacent shape holding ribs are different as described above, the foamable resin liquid, when reaching, for example, the overhanging portions of the first shape holding ribs whose protrusion height from the base layer is small, branches off to the left and right there, and the branching foamable resin liquid hits against the side surfaces of the vertical wall portions of the second shape holding ribs whose protrusion height from the base layer is large, and thus is prevented from straightly entering the hook-shaped engagement elements and reduces in its force. When its force weakens, its foaming and curing readily progress, resulting in a reduction in the amount of the foamable resin liquid passing through the meshes of the base layer to reach the hook-shaped engagement elements.
Therefore, the mesh hook surface fastener of the present invention can be integrated with the foamed resin molded body with almost no engagement ability lost even if the mold-in forming is employed. Therefore, it is suitable for being integrated with a molded body that comes into contact with a person to easily move, such as a cushioning member of a seat structure, which can contribute to the wider application of the mesh hook surface fastener.
In the mesh hook surface fastener of the present invention, by applying the water/oil repellent on the hook-shaped engagement elements side, it is possible to further reduce the adhesion of the foamed resin to the hook-shaped engagement elements side after the molding. Further, even if the foamed resin having passed through the meshes and cured between the hook-shaped engagement elements is present, by covering the mesh hook surface fastener with the fiber sheet having the loop-shaped engagement elements and peeling this fiber sheet after the molding, it is possible to easily remove the foamed resin in the state of adhering to the fiber sheet, enabling a further increase in the engagement ability.
Further, the mesh hook surface fastener of the present invention is preferably formed of a thermoplastic elastomer. Because the thermoplastic elastomer has very excellent flexibility and stretchability, the foamed resin molded body to which such a mesh hook surface fastener is attached does not have a great difference in flexibility and stretchability between its part where the surface fastener is attached and its other part where the surface fastener is not attached, and gives less feeling of something foreign ascribable to the surface fastener.
An embodiment of a mesh hook surface fastener of the present invention will be hereinafter described in detail based on the drawings. As illustrated in
As is seen from
The hook-shaped engagement elements in this embodiment include first engagement elements (B1) and second engagement elements (B2). The first engagement elements (B1) each have a stem (S1) extending from a root (the one surface (A1a) of the base layer (A1) (more correctly, the one surface of the strand (a1)) and an engagement portion (M1) composed of a pair of protruding pieces (M1a, M1b) extending from the middle or top of the stem (S1) in both directions along the length direction of the strand (a1). As illustrated in the right side edge in
Though the protruding pieces (M1a, M1b) forming the engagement portion (M1) of the first engagement element (B1) may protrude from the stem (S1) to both sides as in this embodiment, the engagement portion (M1) may have a protruding piece protruding only to one side, and further the protruding pieces (M1a, M1b) may protrude in multiple upper and lower tiers. The second engagement elements (B2) may also have the engagement portions (M2) in multiple upper and lower tiers. Further, the hook-shaped engagement elements may include both the first engagement elements (B1) and the second engagement elements (B2) as illustrated in
However the second engagement elements (B2) are each preferably shaped such that the pair of stems (S2, S2) rise back-to-back from bulging portions present on the one surface (A1a) of the base layer (A1), the stems (S2, S2) bend in the opposite directions along the strand (a1) from the middle, and the extreme tips of the engagement portions (M2, M2) approach the one surface (A1a) of the base layer (A1). This shape enables the engagement of the loop-shaped engagement elements from whichever direction they approach and makes it difficult for the engagement portions (M2, M2) to be torn off by the engagement.
Preferably, multiple (typically, three to ten) rows of the first engagement elements (B1) are present near the middle of the mesh hook surface fastener (1) in terms of a direction (width direction: the X direction in
The plurality of shape holding ribs (a21, a22) protrude from the other surface (A1b) of the base layer (A1), are arranged in parallel at intervals, and intersect with the strands (a1). The strands (a1) and the shape holding ribs (a21, a22) are integrated at their intersection points, and many meshes (A3) are formed in the base layer (A1), each formed by the two adjacent strands (a1) and the two adjacent shape holding ribs (a21, a22).
The shape holding ribs (a21, a22) each have a vertical wall portion (P) extending along their length direction (the Y direction in
Further, as illustrated in
Since the shape holding ribs (a21, a22) have the overhanging portions (Q) protruding outward in the width direction of the vertical wall portions (P), a foamable resin liquid first hits against the overhanging portions (Q) to be prevented from directly entering the base layer (A1) with great force at the time of mold-in forming. Preferably, the first shape holding ribs (a21) having a relatively small protrusion height (h) and the second shape holding ribs (a22) having a relatively large protrusion height (h) are alternately arranged in the adjacent direction (X direction). Since the protrusion heights (h) of the adjacent shape holding ribs (a21, a22) are different, that is, the adjacent ones have a level difference, the flow of the foamable resin liquid is hindered at some portion of either of these. For example, the foamable resin liquid is blocked by the overhanging portions (Q) located at the small protrusion height, and the flow of the foamable resin liquid branching off to the left and right hits against the side surfaces of the adjacent vertical wall portions (P) having a large protrusion height. Consequently, the force of the flow of the foamable resin liquid weakens.
As the force of the flow of the foamable resin liquid weakens, the foaming and curing of the foamable resin liquid progress, and accordingly the amount of the foamed resin capable of reaching the base layer (A1) and further passing through the meshes (A3) of the base layer (A1) to reach the vicinity of the hook-shaped engagement elements (B1, B2) is small. Nevertheless, before the molding of the foamed resin, the outer surfaces of the hook-shaped engagement elements (B1, B2) and the one-surface (A1a) side outer surface of the base layer (A1) (strands (a1)) are preferably covered with a water/oil repellent. This makes it more difficult for the foamed resin to adhere to the hook-shaped engagement elements (B1, B2), and even if adheres, it can be easily removed. Further, if the hook-shaped engagement elements (B1, B2) are covered with a fiber sheet (not illustrated) having loop-shaped engagement elements before the mesh hook surface fastener (1) is set in a mold in the above-described manner, and the foamable resin liquid is injected, by peeling the fiber sheet after foam molding, it is possible to easily remove the foamed resin adhering to the hook-shaped engagement elements (B1, B2) at a time simultaneously with the peeling of the fiber sheet.
The protrusion height (h) of the first shape holding ribs (a21) is preferably 0.4 to 0.8 times the protrusion height (h) of the second shape holding ribs (a22). Further, the position of outer end surfaces (Q2) located opposite to surfaces (Q1) facing the base layer (A1) in the overhanging portions (Q) of the first shape holding ribs (a21) having a small protrusion height (h) is preferably closer to the base layer (A1) than the position of a surface (Q1) facing the base layer (A1) in the overhanging portions (Q) of the second shape holding ribs (a22) having a large protrusion height (h). Further, the shortest distance (D1) of the overhanging portion (Q) of one of the adjacent first shape holding rib (a21) and second shape holding rib (a22) from the other is preferably 0.2 to 0.6 times a distance (D2) between their vertical wall portions (P) along a plane perpendicular to a direction in which the vertical wall portions (P) protrude. Note that the shortest distance (D1) refers to a distance of a section with the shortest interval from any portion of the overhanging portions (Q) of one of the adjacent first shape holding rib (a21) and second shape holding rib (a22) up to any portion of the vertical wall portion (P) and the overhanging portion (Q) of the other as illustrated in
Setting the relation between the adjacent first shape holding rib (a21) and second shape holding rib (a22) in this way makes it possible to effectively hinder the aforesaid entrance of the foamable resin liquid toward the hook-shaped engagement elements (B1, B2).
The overhanging portions (Q) of the first shape holding ribs (a21) and the second shape holding ribs (a22) may be present at the tip portions of the vertical wall portions (P) in one tier as in this embodiment but may be present in two tiers or more in the up-down direction of the vertical wall portions (P).
The transverse sectional shape of the overhanging portions (Q) forming the shape holding ribs (a21, a22) is not limited to that illustrated in
As for specific dimensions of the mesh hook surface fastener (1) suitable to be integrated with a cushioning member of a seat structure, the protrusion height (h) of the second shape holding ribs (a22) is preferably 0.70 to 1.50 mm, and the protrusion height (h) of the first shape holding ribs (a21) is preferably 0.30 to 0.60 mm. To prevent the entrance of the foamable resin liquid toward the hook-shaped engagement elements (B1, B2), the protrusion height (h) of the second shape holding ribs (a22) is preferably larger than the protrusion height (h) of the first shape holding ribs (a21) by 0.15 to 0.40 mm, and the width-direction outward extension length of the overhanging portions (Q) is preferably 0.40 to 1.00 mm for the same reason.
The sectional area of each of the first shape holding ribs (a21) and the second shape holding ribs (a22) in the plane perpendicular to the length direction is preferably 0.20 to 0.26 mm2, and the sectional area of the overhanging portions (Q) is preferably 20 to 50% of the total sectional area of each of the shape holding ribs (a21, a22). Such a shape is preferable for obtaining an anchoring effect to the foam-molded body and for preventing the entrance of the foamable resin liquid toward the hook-shaped engagement elements (B1, B2).
Further, to maintain the strength, the number of the shape holding ribs (a21,a22) arranged in the direction (the X direction in
The shape holding ribs (a21, a22) are preferably provided such that a ratio at which the vertical wall portions (P) and the overhanging portions (Q) cover the other surface (rear surface) (A1b) of the base layer (A1) (rear surface coverage) is 60 to 100% of the plane area of the other surface (rear surface) (A1b) of the base layer (A1).
In the case where the overhanging portions (P) protrude to the width-direction both sides from the tip portions of the vertical wall portions (P) as illustrated in
As described above, in the mesh hook surface fastener (1), the strands (a1) forming the base layer (A1) and the shape holding ribs (a21, a22) extend in different directions, and the strands (a1) are arranged in parallel at intervals and the shape holding ribs (a21, a22) are also arranged in parallel at intervals. The strands (a1) are on the upper side in the drawings and the shape holding ribs (a21, a22) are on the lower side in the drawings. Therefore, they are not on the same plane but intersect with and are laid on each other to be integrated, so that the base layer (A1) has a mesh shape having the meshes (A3).
The mesh hook surface fastener (1) has very excellent flexibility and stretchability because it has the mesh shape with the strands (a1) and the shape holding ribs (a21, a22) not present on the same plane. Therefore, a foamed resin molded body to which the mesh hook surface fastener (1) of this embodiment is attached is excellent inflexibility and stretchability at its part where the mesh hook surface fastener (1) is attached and gives almost no feeling of the presence of the mesh hook surface fastener (1). This eliminates a need for adopting the structure of forming a deep groove in the foamed resin molded body and fixing the surface fastener to the deep part of the groove, to alleviate a feeling of something foreign as is conventionally adopted, and allows the groove to be shallow. This facilitates the work of attaching an outer layer member that is to be fixed to the surface fastener.
The rows of the hook-shaped engagement elements (B1, B2) on the one surface (A1a) of the base layer (A1) and the shape holding ribs (a21, a22) on the other surface (A1b) of the base layer (A1) may be present back-to-back symmetrically with the base layer (A1) therebetween, or may be positionally deviated from each other. However, they are preferably present back-to-back from a viewpoint of preventing the hook-shaped engagement elements (B1, B2) from being broken by some factor such as the action of external force pulling them. The back-to-back presence enables to effectively prevent the breakage when the pulling force is applied to the hook-shaped engagement elements (B1, B2) because the roots of the hook-shaped engagement elements (B1, B2) are reinforced in the length direction by the shape holding ribs (a21, a22) which have been molecular-oriented by the drawing.
Further, the rows of the hook-shaped engagement elements (B1, B2) need not be present on the back-to-back facing surfaces of all the shape holding ribs (a21, a22), and depending on the size and the number of the engagement elements, a row composed only of stems not having engagement ability (in this embodiment, corresponding to low plateau-shaped bulging portions (N)) may be present as illustrated in
The mesh hook surface fastener (1) of this embodiment is preferably formed of a thermoplastic elastomer resin. The use of the thermoplastic elastomer resin in combination with the aforesaid mesh shape can make flexibility and stretchability more excellent.
Specific examples of the thermoplastic elastomer resin used include a polyurethane-based resin, a styrene-based elastomer resin, a polyamide elastomer resin, a polyolefin-based elastomer resin, a soft vinyl chloride resin, and a polyester elastomer. Among all, a polyester elastomer and a polyamide elastomer are preferable because the use of either of these more prevents the protruding portions of the engagement elements from being tom off from the stems by being pulled when the engagement is released, than the use of other elastomer resins.
Moreover, a polyester elastomer and a polyamide elastomer are resins having sufficient properties of an elastomer irrespective of having a high modulus of elasticity as compared with other elastomer resins and impart excellent followability to the surface fastener even if its relative movement is caused from various directions, to prevent the easy disengagement from an engagement mate.
In this embodiment, a polyester elastomer that is the most preferable as the thermoplastic elastomer is one in which polyoxytetramethylene glycol is copolymerized with a resin whose main repeating unit is a butylene terephthalate unit and is a resin that has more sufficient properties of an elastic polymer irrespective of having a high modulus of elasticity than other typical elastomer resins, for example, polyurethane, a styrene-based elastomer, an olefin-based elastomer, and so on as described above. Preferably, a ratio of [poly(oxytetramethylene)]terephthalate groups in the polyester elastomer is within a range of 40 to 70 wt %, and more preferably 50 to 60%.
A polyamide elastomer preferable next to the polyester elastomer is an elastomer whose hard segment component is a polyamide block such as a nylon 6 block, a nylon 11 block, or a nylon 12 block and whose soft segment component is polyether such as polyethylene glycol or polytetramethylene glycol, or aliphatic polyether, and that has sufficient properties of an elastic polymer irrespective of having a higher modulus of elasticity than other typical elastomer resins similarly to a polyester elastomer. Preferably, a ratio of the soft segment is 30 to 80 wt %.
The mesh hook surface fastener (1) of this embodiment is most preferably formed of only a polyester elastomer or only a polyamide elastomer, but in the case where a polyester elastomer, a polyamide elastomer, or a mixture of these is used, an elastomer resin other than these, for example, a polyolefin-based elastomer, a styrene-based elastomer, a polyurethane-based elastomer, or the like may be blended, and a small amount of a resin other than the elastomer, for example, a polyolefin-based resin, a polyester-based resin, a polyamide-based resin, a vinyl chloride-based resin, or an ethylene-vinyl alcohol copolymer may be blended.
Besides these, a plasticizer, various stabilizers, a weather-resistant agent, a cross-linking agent, an antibacterial agent, a filler, a flame retardant, an antistatic agent, a reinforcer, a conductive agent, a coloring agent, and so on may be added.
Here, as for the heights of the hook-shaped engagement elements (B1, B2), the first engagement elements (B1) and the second engagement elements (B2) both preferably have a height of 0.80 to 2.00 mm. The density of the hook-shaped engagement elements (B1, B2) is preferably within a range of 30 to 60 pieces/cm2. Further, from a viewpoint of engagement force and the strength of the surface fastener, the number of the rows of such hook-shaped engagement elements (B1, B2) present in the direction perpendicular to the drawing direction of the mesh hook surface fastener (1) is preferably five to fifteen per cm. In the case of the second engagement elements (B2) each having the pair of stems (S2, S2) rising back-to-back and the engagement portions (M2, M2) at the extreme tips of the steins (S2, S2), in counting the density and the number of the rows of the hook-shaped engagement elements (B1, B2) mentioned here, the pair of the back-to-back stems (S2, S2) is counted as one. Further, in
As illustrated in
Since the stems (S1, S2) and the engagement portions (M1, M2) are coplanar with the strands (a1), their widths are typically equal and are preferably within a range of 0.20 to 0.50 mm from a viewpoint of engagement force and the strength of the surface fastener, and more preferably within a range 0.30 to 0.40 mm.
From a viewpoint of the engagement force and the strength, preferably, the sectional area of each of the stems (S1, S2) of the hook-shaped engagement elements (B1, B2) taken along a plane parallel to the strands (a1) at its middle portion in terms of the height direction is 0.05 to 0.20 mm2, the protrusion length of the engagement portions (M1, M2) from the stems (S1, S2) is 0.30 to 1.00 mm, and an average thickness of the engagement portions (M1, M2) is 0.15 to 0.50 mm.
Further, from a viewpoint of strength and stretchability, preferably, the thickness of the strands (a1) is within a range of 0.10 to 0.40 mm and the adjacent strands (a1) are arranged such that a space having an about 0.20 to 1.00 mm width is formed therebetween.
The mesh hook surface fastener (1) of this embodiment is produced through the sequential execution of the following steps (i) to (iii):
(i) a first step of charging a molding material into an extruder including an extrusion nozzle, and extruding a tape-shaped object from the extrusion nozzle, the extrusion nozzle having a laterally long slit having a predetermined width in a direction orthogonal to an extrusion direction, upward protruding space portions extending upward from the laterally long slit and arranged at predetermined intervals in the width direction of the laterally long slit, and downward protruding space portions extending downward from the laterally long slit and arranged at intervals in the width direction of the laterally long slit, with the adjacent ones being different in an amount of the downward protrusion from the laterally long slit;
(ii) a second step of making incisions at predetermined intervals in the extrusion direction, the incisions each extending along a direction intersecting with the extrusion direction and being made from the tops of portions extruded from the upward protruding space portions up to the other surface of a portion extruded from the laterally long slit; and
(iii) a third step of thereafter drawing the tape-shaped object in the extrusion direction.
In more detail, first, in the first step, a melt of a thermoplastic elastomer resin is extruded from a mold including an extrusion nozzle (2) illustrated in
As illustrated in
In the second step, the incisions (E) extending in the direction (C direction in
The thickness of the sheet portion (R) for base layer is preferably within a range of 0.10 to 0.40 mm, and especially preferably within a range of 0.20 to 0.30 mm. This thickness scarcely changes even after the drawing is performed. Therefore, this thickness is the thickness of the strands (a1) because the sheet portion (R) for base layer becomes the strands (a1) forming the base layer (A1).
The width of the sheet portion (R) for base layer before the drawing is preferably 10 to 200 mm, and especially preferably 25 to 150 mm. Too wide a width makes it difficult to make the incisions with a uniform depth in the ribs (K1, K2) for hook-shaped engagement elements and the sheet portion (R) for base layer at a high speed.
The incisions (E) made in the ribs (K1, K2) for hook-shaped engagement elements and the sheet portion (R) for base layer are formed in parallel at uniform intervals of, preferably 0.20 to 0.50 mm, and especially preferably 0.30 to 0.40 mm. This interval is the width of the strands (a1) (in
In view of engagement force and so on, the incisions (E) preferably have an angle of 90 to 35 degrees from the length direction (extrusion direction) of the tape-shaped object (3). Particularly preferably, the angle is set such that the strands (a1) and the shape holding ribs (a21, a22) intersect at angles of 45 to 85 degrees not at right angles after the drawings, from a viewpoint of imparting stretchability in the width direction of the mesh hook surface fastener (1) (the X direction in
The formation from the thermoplastic elastomer as in this embodiment leads to excellent followability, facilitates making the base layer flat, and facilitates the sure forming of the incisions up to the roots of the shape holding ribs.
In the third step, the tape-shaped object (3) having the incisions (E) is drawn in the extrusion direction (the Y direction in
On the other hand, since the incisions are not made in the shape holding ribs (a21, a22) present on the rear surface of the sheet portion (R) for base layer, the shape holding ribs (a21, a22) keep the continuous rib shape even after the drawing and function as parts for fixing the strands (a1) and holding the sheet shape of the mesh hook surface fastener (1).
Preferably, the intervals of the incisions (E) become 0.20 to 1.00 mm after the drawing from a viewpoint of the flexibility, followability, and so on of the surface fastener. The shape holding ribs (a21, a22) are not changed in the sectional shape even by the drawing, but because of the drawing in the length direction, their sectional area reduces while their shape after the drawing is similar to the shape before the drawing.
As a result of the third step, the shape holding ribs (a21, a22) are drawn and molecular-oriented in their length direction while kept continuous. On the other hand, the strands (a1) have almost the same shape as that before the drawing and are not molecular-oriented in the length direction because they are not drawn.
Next, a method for producing a cushioning member used in a seat structure of an automobile, an airplane, or the like, using the mesh hook surface fastener (1) of this embodiment will be described.
First, in the mesh hook surface fastener (1) of the present invention, a water/oil repellent is applied on the outer surfaces of the hook-shaped engagement elements (B1, B2) and the outer surfaces of the strands (a1) on the side where the hook-shaped engagement elements (B1, B2) are present. This can prevent the foamed resin from firmly adhering to the outer surfaces of the hook-shaped engagement elements (B1, B2) even if the foamable resin liquid enters from the rear surface side.
As the water/oil repellent, a generally used one is usable, and its typical examples include a silicon compound-based one, a carbon compound-based one, and a fluorine compound-based one, and among all, a fluorine-based compound is preferable. Examples of the fluorine-based compound include a fluorine-based urethane resin and a fluorine-based acrylic resin.
Next, in the mesh hook surface fastener (1), the hook-shaped engagement elements (B1, B2)-side surface coated with the water/oil repellent (the one surface (A1a) of the base layer (A1)) is covered with a fiber sheet that has loop-shaped engagement elements, which are to engage with the hook-shaped engagement elements (B1, B2), and that is not coated with a water/oil repellent. Consequently, when the fiber sheet is removed after the foamed resin molding, the foamed resin having passed through the meshes (A3) of the base layer (A1) from the rear surface side, entered the gaps between the hook-shaped engagement elements (B1, B2), and cured can be very easily removed in the state of adhering to the fiber sheet.
Examples of the fiber sheet include fiber-made sheets, such as a woven fabric, a knitted fabric, and a nonwoven fabric, having, on their surfaces, fibers that are to be loop-shaped engagement elements engageable with the hook-shaped engagement elements (B1, B2). One example thereof is a fabric in which a surface of a tricot knitted fabric which is a ribbed warp knitted fabric having stretchability and thickness is raised with a card clothing or the like, and fibers are pulled out in a loop shape to the surface from the knitted fabric. Another example besides this is a fabric or a nonwoven fabric on whose surface a fiber having loops or crimps engageable with the hook-shaped engagement elements (B1, B2) is present. The fiber sheet is not limited. Such a fiber sheet used is preferably not coated with the water/oil repellent.
Next, the mesh hook surface fastener (1) whose hook-shaped engagement elements (B1, B2) are engaged with the fiber sheet is subjected to the mold-in forming
Specifically, as illustrated in
However, in this embodiment, since the hook-shaped engagement sides (B1, B2) are covered with the fiber sheet during the molding as described above, the fiber sheet is removed after the foamed resin molded body is taken out from the forming mold. As a result, the foamed resin that has entered the gaps between the hook-shaped engagement elements (B1, B2) is almost completely removed, making it possible to obtain the foamed resin molded body with which the mesh hook surface fastener (1) capable of exhibiting higher engagement ability of the hook-shaped engagement elements (B1, B2) is integrally molded.
An outer layer member made of fabric or leather is attached to thus obtained foamed resin molded body to cover its surface. A loop surface fastener is attached to the outer layer member at a position corresponding to the attachment position of the mesh hook surface fastener (1) and is put on the mesh hook surface fastener (1), thereby engaging the mesh hook surface fastener (1) and the loop surface fastener. Consequently, a seat for an automobile or an airplane, a reception chair, or an office chair to which the outer layer member is firmly fixed is obtained.
Since the mesh hook surface fastener (19) has high flexibility and stretchability, the foamed resin molded body to which the mesh hook surface fastener (1) is attached at a predetermined position does not have a great difference in flexibility and stretchability between its part where the surface fastener is attached and its part where the surface fastener is not attached, and thus gives almost no feeling of something foreign caused by the presence of the surface fastener. Moreover, even though the surface fastener has a mesh shape having the meshes (A3), its engagement ability is not poor because almost no foamed resin enters the gaps between the hook-shaped engagement elements (B1, B2).
The mesh hook surface fastener of the present invention is usable as a mold-in surface fastener when the foamed resin is molded as described above, and besides, is usable in typical mold-in forming using an unfoamable resin. Further, similarly to an ordinary hook surface fastener, it can be of course usable for bonding members in clothing, shoes, hats, rain gear, industrial materials, miscellaneous daily goods, toys, fastening bands, supporters, belts, and so on using its flexibility and stretchability.
The present invention will be hereinafter specifically described based on Examples. In Examples, at the time of the measurement of engagement force, surface fasteners are removed from foamed resin molded bodies with care taken not to change the state of engagement element surfaces. As an engagement mate, a loop surface fastener HAT-1548-9 produced by Hatta Tateami Co., Ltd. was used, and as for the engagement force, an initial value of the engagement force was measured as tensile strength (the measurement was conducted according to the method in JIS 13416: 2000 except that an effective width was set to 15 mm). Ten samples were used at the time of the measurement, and an average value in the ten samples was defined as the value of the target surface fastener.
Further, a degree of a feeling of something foreign that the foamed resin molded body to which the surface fastener was attached by mold-in forming gave because of the attachment of the surface fastener to its surface was examined by sensory evaluation, that is, by the touching or pressing of the foamed molded body with a hand.
As a resin used for molding, a thermoplastic polyester elastomer (Hytrel, product No. 6377 produced by DU PONT-TORAY CO., LTD.) was used, and this resin was extruded from an extrusion nozzle (2) and immediately put into water to be cooled, to produce a tape-shaped object (3) with a 25 mm width (width along the X direction in
The extrusion nozzle (2) of a mold used in this example is illustrated in
In the tape-shaped object (3), the total number of the ribs (K1, K2) for hook-shaped engagement elements on the front surface was 10/25 mm in the tape width direction (the direction indicated by reference sign W in
Next, as illustrated in
The obtained mesh surface fastener (1) had a total width of 25 mm (width in the direction indicated by reference sign W in
As the shape holding ribs (a21, a22), first shape holding ribs (a21) with a 0.58 mm protrusion height and second shape holding ribs (a22) with a 0.85 mm protrusion height were alternately arranged, and they protruded from the other surface (rear surface (A1b) of the base layer (A1)). The shape holding ribs (a21, a22) intersect with the strands (a1) forming the base layer (A1) at 80 degree-angles, and at their intersection points, the base layer (A1) and the shape holding ribs (a21, a22) were integrated. Further the hook-shaped engagement elements (B1, B2) with a 1.1 mm height protruded from the front surfaces of the strands (a1) (one surface (A1a) of the base layer (A1)) at a density of 51 pieces/cm2.
Therefore, the protrusion height of the first shape holding ribs (a22) was about 0.7 times the protrusion height of the second shape holding ribs (a22), and the position of outer end surfaces (Q2) of the overhanging portions (Q) of the first shape holding ribs (a21) was closer to the other surface (rear surface) (A1b) of the base layer (A1) by 0.25 mm than the position of surfaces (Q1), of the second holding ribs (a22), facing the base layer (A1). Further, the shortest distance (D1) of the overhanging portions (Q) of either the first shape holding ribs (a21) or the second shape holding ribs (a22) from the other was 0.36 mm on average, and the overhanging portions (Q) both spread from the vertical wall portions (P) to both sides by 0.68 mm. Further, the rear surface coverage of the shape holding ribs (a21, a22) occupying the area of the rear surface of the mesh hook surface fastener (1) was 77%, and the aforesaid shortest distance (D1) was 0.35 times the distance (D2) between the vertical wall portions (P) along a plane orthogonal to the protrusion direction.
In each of the first engagement elements (B1) having a T-shaped cross section, its sectional area in a plane parallel to the strand (a1) at a height middle portion was 0.37 mm2, the protrusion length of protruding pieces (M1a, M1b) forming an engagement portion (M1) from a stem (S1) was 0.26 mm, an average thickness of (M1) was 0.13 mm and the width of the stem (S1) was 0.19 mm. Further, in each of the second engagement elements (B2), its sectional area in a plane parallel to the strand (a1) at a height middle portion of stems (S1, S2) was 0.99 mm2 per stem, the protrusion length of engagement portions (M2, M2) from the stems (S2, S2) was 0.38 mm, an average thickness of the engagement portions (M2, M2) was 0.15 mm, and the width of the stems (S2, S2) was 0.24 mm.
In each of the shape holding ribs (a21, a22), the width of the overhanging portions (Q) along a plane perpendicular to the length direction was 3.4 times that of the vertical wall portions (P). The sectional shape of the overhanging portions (Q) was an oblong circle as illustrated in
Next, a fluorine-based water/oil repellent was applied on the outer surfaces of the hook-shaped engagement elements (B1, B2) and the outer surface of the one surface (A1a) of the base layer (A1) of the obtained mesh hook surface fastener (1), a loop surface of a fiber sheet having loops on the front surface was laid on the hook-shaped engagement elements (B1, B2) so that the hook-shaped engagement elements (B1, B2) were covered with the fiber sheet as illustrated in
Next, as illustrated in
The fiber sheet covering the hook-shaped engagement elements (B1, B2) was removed from the obtained molded body, and the hook-shaped engagement elements (B1, B2) exposed to the molded body surface and the removed fiber sheet were observed. The result showed that there was almost no place where the foamed resin filled the gaps between the hook-shaped engagement elements (B1, B2) due to the flow of the foamable resin liquid toward the hook-shaped engagement elements (B1, B2), the foamed resin entering through meshes (A3) of the base layer (A1) almost entirely adhered to the removed fiber sheet and thus had been removed from the gaps between the hook-shaped engagement elements (B1, B2).
Fifteen engineers engaging in foam molding were requested to participate and evaluate whether or not they had a feeling of something foreign given by the mesh hook surface fastener (1) present on the surface of the obtained surface fastener-attached molded body, by touching or pressing the surface of the molded body with their hands. As a result, owing to the excellent flexibility and stretchability of the surface fastener, they all felt that the presence of the surface fastener did not give a feeling of something foreign, and the obtained surface fastener-attached molded body was a very excellent one that had a completely different touch from that of a conventional foam-molded body to whose surface a surface fastener was fixed.
Then, the engagement force of the mesh hook surface fastener (1) present on the surface of the hook surface fastener-attached foamed resin molded body was measured. The result showed that its tensile shear strength was 45.4 N, leading to the confirmation that its engagement force was also excellent.
A mesh surface fastener was produced that had, as the shape holding ribs in Example 1 described above, those having the same height as that of the second shape holding ribs (a22) having a large protrusion height of Example 1 instead of the two kinds of shape holding ribs (a21, a22) with different protrusion heights which were alternately arranged as in Example 1. The shape holding ribs were present with the same density as that in Example 1, and their overhanging portions (Q) spread to both sides by 0.36 mm. The other structure is the same as that of Example 1. Then, a water oil repellent was applied on the outer surface on a hook-shaped engagement elements side as in Example 1, and the hook-shaped engagement elements were further covered with the same fiber sheet as that used in Example 1, and mold-in forming was executed similarly to Example 1 to produce a surface fastener-attached foamed resin molded body (Comparative Example 1).
Similarly, a mesh surface fastener was produced that had, as the shape holding ribs in Example 1 described above, those having the same height as that of the first shape holding ribs (a21) having a small protrusion height of Example 1. The shape holding ribs were present with the same density as that in Example 1, and their overhanging portions (Q) spread to both sides by 0.36 mm. The other structure is the same as that of Example 1. Then, a water/oil repellent was applied on the outer surface on a hook-shaped engagement elements side as in Example 1, and the hook-shaped engagement elements were covered with the same fiber sheet as that used in Example 1, and mold-in forming was executed similarly to Example 1 to produce a surface fastener-attached foamed resin molded body (Comparative Example 2).
The fiber sheets covering the hook-shaped engagement elements of the foamed resin molded bodies obtained in Comparative Examples 1 and 2 were removed, and the surfaces of the hook-shaped engagement elements of the mesh hook surface fasteners exposed from the molded bodies and the removed fiber sheets were observed. The observation result showed that both in Comparative Example 1 and Comparative Example 2, because of the violent flow of a foamed resin toward the hook-shaped engagement elements of the surface fasteners, gaps between the engagement elements were almost entirely filled with the foamed resin, and though the foamed resin entering from meshes partly adhered to the removed fiber sheets, the foamed resin had not been removed almost at all. The measurement results of the engagement force of the hook surface fasteners present on the surfaces of these hook surface fastener-attached foamed resin molded bodies showed that tensile shear strength in Comparative Example 1 was 25.4 N and tensile shear strength in Comparative Example 2 was 14.5, and thus the engagement forces of both were far inferior to that in Example 1. The reason for this might be that loop-shaped engagement elements of the engagement mate could not enter the inside of the hooks of the hook-shaped engagement elements because the teamed resin was filled between the hook-shaped engagement elements.
A mesh hook surface fastener (1) having completely the same size and structure as those of Example 1 was produced. Thereafter, a water/oil repellent was applied on a surface, of the fiber sheet, facing the hook-shaped engagement elements (B1, B2) instead of the outer surfaces of the hook-shaped engagement elements (B1, B2) and the outer surface of the one surface (A1a) of the base layer (A1), this fiber sheet was bonded to the hook-shaped engagement elements (B1, B2), and mold-in forming was executed similarly to Example 1 to produce a surface fastener-attached foamed resin molded body.
The fiber sheet covering the hook-shaped engagement elements (B1, B2) of the obtained foamed resin molded body was removed, and the hook-shaped engagement elements (B1, B2) of the mesh hook surface fastener (1) exposed from the surface of the molded body and the removed fiber sheet were observed. The result showed that there was almost no place where gaps between the hook-shaped engagement elements (B1, B2) were filled with a foamed resin due to the flow of a foamable resin liquid, and the foamed resin almost entirely had been removed from the surface of the surface fastener in the state of adhering to the removed fiber sheet as in Example 1.
The measurement result of the engagement force of the mesh hook surface fastener (1) present on the surface of this hook surface fastener-attached foamed resin molded body showed that tensile shear strength was 35.0 N, and thus the mesh hook surface fastener of Example 2 was also excellent as a surface fastener.
However, as a result of conducting tests on whether or not fifteen engineers engaging in foam molding had a feeling of something foreign from the surface of the molded body because of the presence of the hook surface fastener as in Example 1, a small number of (two) engineers answered that they had a feeling of something foreign from the foamed resin molded body because of the presence of the surface fastener. In view of this, Example 2 was slightly inferior to Example 1.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019-192372 | Oct 2019 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2020/039698 | 10/22/2020 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2021/079928 | 4/29/2021 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4454183 | Wollman | Jun 1984 | A |
| 5688576 | Ohno et al. | Nov 1997 | A |
| 5945193 | Pollard et al. | Aug 1999 | A |
| 5972465 | Ohno et al. | Oct 1999 | A |
| 11730239 | Takakuwa | Aug 2023 | B2 |
| 11986063 | Parellada Armela | May 2024 | B2 |
| 20040170801 | Seth et al. | Sep 2004 | A1 |
| 20040170802 | Seth et al. | Sep 2004 | A1 |
| 20050160534 | Akeno | Jul 2005 | A1 |
| 20100181695 | Murasaki | Jul 2010 | A1 |
| 20110030176 | Itoh | Feb 2011 | A1 |
| 20140130311 | Okuda et al. | May 2014 | A1 |
| 20160052433 | Ono | Feb 2016 | A1 |
| 20210100323 | Takakuwa | Apr 2021 | A1 |
| 20220378156 | Tanokura | Dec 2022 | A1 |
| Number | Date | Country |
|---|---|---|
| H07-148007 | Jun 1995 | JP |
| 2000516482 | Dec 2000 | JP |
| 2006520661 | Sep 2006 | JP |
| 2012011985 | Jan 2012 | JP |
| 4991285 | Aug 2012 | JP |
| 2015192793 | Nov 2015 | JP |
| 9720480 | Jun 1997 | WO |
| 2004077980 | Sep 2004 | WO |
| 2013005297 | Jan 2013 | WO |
| 2019107444 | Jun 2019 | WO |
| Entry |
|---|
| International Search Report dated Jan. 12, 2021 In PCT/P2020/039698, with English translation, 5 pages. |
| Written Opinion dated Jan. 12, 2021 in PCT/P2020/039698, with English translation, 7 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20220378156 A1 | Dec 2022 | US |