Claims
- 1. A metal article having at least one surface thereof coated with an adherent layer of a corrosion-inhibiting coating, said corrosion-inhibiting coating comprising:
- (a) from about 55% to about 78.5%, by weight, of an epoxy resin having a molecular weight of about 15,000 to about 80,000;
- (b) from about 20% to about 40%, by weight, of a phenolic resin; and
- (c) from about 1.5% to about 5%, by weight, of an organic corrosion inhibitor having the structural formula:
- TABLE I______________________________________60 Day Accelerated Corrosion(2% Acetic Acid Vapor at 100.degree. F.)Corrosion-InhibitingCoating Composition Overall Score______________________________________Example 3 -3.52Example 2 0.29Example 1 2.87Commercial Composition.sup.1) 3.58.sup.2)______________________________________ .sup.1) a composition including 70% epoxy resin and 30% phenolic resin, b weight of nonvolatile material; and .sup.2) the closures exhibited many perforations. ##STR8## wherein each R is selected independently, from the group consisting of hydrogen, alkyl, haloalkyl, alkoxy, alkylthio, alkylsulfonyl, cycloalkyl, phenyl, alkylphenyl, phenylalkyl, halo, cyano, nitro, carboxyl, carboxyalkyl, hydroxy, amino, and carbamoyl, and wherein R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are selected, independently, from the group consisting of hydrogen, alkyl, hydroxyalkyl, haloalkyl, alkoxyalkyl, carboxyalkyl, carboxyl, penyl, and phenylalkyl, and wherein at least one of the R.sub.1, R.sub.2, R.sub.3 and R.sub.4 groups are a carboxyl group.
- 2. The metal article of claim 1 wherein the corrosion-inhibiting coating further comprises:
- (d) from about 1% to about 4%, by weight, of a low molecular weight polyfunctional epoxy resin.
- 3. The metal article of claim 1 wherein the epoxy resin is branched at least at about 3% of secondary hydroxyl positions of the epoxy resin.
- 4. The metal article of claim 1 wherein the epoxy resin has a molecular weight of about 30,000 to about 80,000.
- 5. The metal article of claim 11 wherein the phenolic resin has a molecular weight of about 1,000 to about 8,000.
- 6. The metal article of claim 1 wherein the phenolic resin includes a phenol component selected from the group consisting of phenol, bisphenol A, cresylic acid, and combinations thereof.
- 7. The metal article of claim 1 wherein the phenolic resin includes a phenol component comprising bisphenol A and cresylic acid, wherein the bisphenol A and the cresylic acid are present in a weight ratio of bisphenol A to cresylic acid of about 0.25:1 to about 4:1.
- 8. The metal article of claim 1 wherein the organic corrosion inhibitor has the structural formula: ##STR9##
- 9. The metal article of claim 1 wherein the organic corrosion inhibitor has the structural formula: ##STR10##
- 10. The metal article of claim 1 wherein the corrosion-inhibiting coating comprises:
- (a) from about 60% to about 70%, by weight, of the epoxy resin, said epoxy resin having a molecular weight of about 40,000 to about 75,000, and said epoxy resin branched at least at about 4% of the secondary hydroxyl positions of the epoxy resin;
- (b) from about 25% to about 35%, by weight, of the phenolic resin, said phenolic resin having a molecular weight of about 3,000, and said phenolic resin having a phenol component comprising bisphenol A and cresylic acid, wherein the bisphenol A and cresylic acid are present in a weight ratio of about 0.6:1 to about 1.5:1; and
- (c) from about 2% to about 3%, by weight, of the organic corrosion inhibitor, said organic corrosion inhibitor having the structural formula: ##STR11##
- 11. The metal article of claim 10 wherein the corrosion-inhibiting coating further comprises:
- (d) from about 2% to about 3%, by weight, of a low molecular weight polyfunctional epoxy resin.
CROSS-REFERENCE TO RELATED APPLICATIONS
This is a divisional of U.S. application Ser. No. 753,930, filed Sep. 3, 1991.
US Referenced Citations (11)
Foreign Referenced Citations (1)
Number |
Date |
Country |
0259255 |
Aug 1986 |
EPX |
Non-Patent Literature Citations (1)
Entry |
R. A. Behrens, A. Braig, "A New Organic Collosion Inhibitor for Coatings", Water-Borne & Higher Solids Coatings Symposium, Feb. 3-5, 1988. |