Claims
- 1. A method for producing a vacuum-tight butt brazing joint between a metallized ceramic part and a stainless steel part, said method comprising the steps of
- (a) shaping the end portion of the stainless steel part to be joined with the metallized ceramic part such that it has a height of from about 4 mm to about 12 mm and a maximum thickness along this height of 0.8 mm,
- (b) annealing at least said shaped end portion of said stainless steel part, and
- (c) brazing said annealed and shaped end portion of said stainless steel part directly to said metallized ceramic part.
- 2. The method as defined in claim 1 wherein said stainless steel part is composed of austenitic stainless steel, and wherein the annealing in step (b) is conducted in an evacuated, oil-free environment and at a temperature of 1050.degree. C.
- 3. The method as defined in claim 2 wherein the time period during which the annealing in step (b) is conducted based on the thickness of the end portion of said stainless steel part in a ratio of about 1 hour per 1 mm of thickness.
- 4. The method as defined in claim 1 wherein the brazing in step (c) is conducted at a temperature of about 800.degree. C.
- 5. The method as defined in claim 1 wherein the ratio between the thickness of the end portion of said stainless steel part and its height is between about 1 and 10.
- 6. The method as defined in claim 1 wherein the ceramic material includes at least 95% of Al.sub.2 O.sub.3.
- 7. A method of producing a vacuum switch including a metallized ceramic housing and two stainless steel caps, said two stainless steel caps being joined to said metallized ceramic housing by separate vacuum-tight butt brazing joints, said method being produced by the steps of
- (a) providing a metallized tubular ceramic housing which has opposite annular end surfaces,
- (b) providing two stainless steel caps, each including a head part and a tubular part extending away from the head part, the tubular part defining a free annular end surface opposite the head part,
- (c) shaping the tubular part of each of said two stainless steel caps such that the portion thereof which extends from the associated free annular end surface to a location therealong about 4 mm to about 12 mm towards the associated head part has a thickness of 0.8 mm,
- (d) annealing at least said portion of each of said two stainless steel caps, and
- (e) brazing the respective free annular end surfaces of said two stainless steel caps directly to the respective opposite annular end surfaces of said metallized tubular ceramic housing.
Priority Claims (1)
Number |
Date |
Country |
Kind |
7901740 |
Mar 1979 |
NLX |
|
Parent Case Info
This application is a continuation application of application Ser. No. 126,286, filed Mar. 3, 1980, now abandoned.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
3371406 |
Bronnes |
Mar 1968 |
|
4148973 |
Sexton |
Apr 1979 |
|
Non-Patent Literature Citations (1)
Entry |
Connell et al., Method of Soldering Refractory Metals, IBM Tech. Disc. Bull., vol. 3, No. 11, 4/61. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
126286 |
Mar 1980 |
|