Metal gasket and method of producing the same

Abstract
A method of producing a metal gasket includes steps of alkaline cleaning a metal plate, coating a non-rinse chemical for chromate conversion of surfaces of the metal plate and drying to form chromate films, coating an adhesive on the chromate films and drying or baking the adhesive to form adhesive layers, and coating rubber compound of a sheet-like or an amorphous mixed compound to a predetermined thickness on the adhesive layers and heating and vulcanizing the rubber compound to form rubber coated metal plate. A metal gasket manufactured in this manner has a high bonding power of the rubber layers to the metal plate to obtain an improved durability for long use.
Description

BACKGROUND OF THE INVENTION
This invention relates to a metal gasket for use in automobile engines, screw engines, freezing equipment, air conditioning units and the like and a method of producing the metal gasket.
As gaskets for automobile engines, so-called asbestos type gaskets have been widely used which are made of single, jointed or beat sheets of asbestos as sole or composite materials. Recently, however, various kinds of new type gaskets have been progressively practically used which are made of metals, graphites, fibers and the like as sole or composite materials in place of the asbestos causing a problem of public nuisance. Particularly, metal gaskets provided on their surfaces with rubber layers are superior in performance and cost to other new gaskets in substitution for the asbestos gaskets and expected to be widely used in future.
Sealing faculty and durability are important among various faculties required as gaskets for automobiles. It has been proposed to deposit a rubber coating layer directly on surfaces of a metal plate as a substrate in order to improve the sealing faculty. In case of metal gaskets, however, the sealing faculty and durability depend mainly upon bonding power between the metal plate and the rubber coating layer. It is therefore important in manufacturing the rubber coated metal gaskets to improve the bonding power therebetween and to prevent the bonding power from lowering in used conditions.
Therefore, attempt has been made to improve the bonding power between the metal plate and the bonding layer or the rubber layer and to maintain the improved bonding power for a long period of time with the aid of an activation treatment or galvanizing which is applied to the surfaces of the metal plate.
Recently, however, high performance automobile engines have been developed and widely used so that metal gaskets are also used under severer conditions, with the result that the durability of the gaskets becomes more important. Under such circumstances, even the above gaskets of metals coated with rubber coating layers encounter a problem of insufficient durability.
SUMMARY OF THE INVENTION
It is an object of the invention to provide a metal gasket and a method of producing the same which eliminate all the disadvantages of the prior art and provide an improved metal gasket which has high bonding power of rubber layers to a metal substrate to improve the durability of the metal gasket for long use.
In order to achieve the object, a metal gasket according to the invention comprises a metal plate, a chromate film on at least one surface of the metal plate formed by coating a non-rinse chemical for chromate conversion thereon, an adhesive coating on the chromate film and a rubber compound layer provided thereon.
A method of producing a metal gasket according to the invention comprises steps of coating a non-rinse chemical for chromate conversion on at least one surface of a metal plate and drying it in a first process, coating an adhesive thereon in a second process, and providing a rubber compound layer thereon and vulcanizing it in a third process.
According to the invention, by coating the non-rinse chemical for chromate conversion on a metal plate before providing a rubber type coating layer on the metal plate, the bonding power of the rubber layers to the metal plate is further improved to obtain the superior durability for long use.
Moreover, the chromate treatment with the non-rinse chemical for chromate conversion used in the invention is easy in operation in comparison with the chemical reaction conversion and the electrolytic treatment. Furthermore, the chromate treatment has an advantage enabling thicknesses of the chromate films to adjust easily.





The invention will be more fully understood by referring to the following detailed specification and claims taken in connection with the appended drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a plan view of one embodiment of a metal gasket according to the invention;
FIG. 2 is an enlarged sectional view of the gasket shown in FIG. 1;
FIG. 3 is a partial enlarged view of FIG. 2;
FIG. 4 is a block diagram illustrating processes for carrying out the method according to the invention; and
FIGS. 5a and 5b are views for explaining the boiling water and antifreeze coolant durability tests for metal gaskets.





DESCRIPTION OF THE PREFERRED EMBODIMENTS
FIG. 1 illustrates one embodiment of the metal gasket according to the invention. The metal gasket comprises a metal plate 1 as a substrate and coating layers C coated on both surfaces of the metal plate 1 (FIGS. 2 and 3). The gasket is formed with a cylinder opening 2, cooling water openings 3 and bolt apertures 4. The gasket is further formed with beads 5 about the cylinder opening 2 and the cooling water openings 3.
As shown in FIG. 3 illustrating a section of the gasket on an enlarged scale, the metal gasket is made in the following processes. First, a metal plate 1 is pickled or cleaned and water-rinsed. Surfaces of the metal plate 1 are then coated with a non-rinse chemical for chromate conversion shown at 6 in FIG. 3. After the coated metal plate 1 has been dried, the coated surfaces are further coated with a rubber adhesive 7 and baked. Moreover, the surfaces coated with the rubber adhesive are coated with a rubber compound 8. Thereafter, the rubber compound on the metal surfaces is vulcanized to complete the coating layers C on the surfaces of the metal plate 1.
The metal plate as substrate may be a stainless steel sheet or a carbon steel sheet. As an alternative, it may be zinc-plated stainless plate or a zinc-plated carbon steel plate.
The method of producing the metal gasket according to the invention will be explained in detail hereinafter.
Processes of the method is shown in a process flow diagram in FIG. 4. As shown in FIG. 4, the chromate film 6 on the metal plate 1 is produced in a first process and the rubber adhesive 7 is provided in a second process. The rubber compound 8 is provided in a third process. The chromate film 6 is produced by a tarnishing reaction of the chromate conversion in the first process. A stainless steel plate coil having a predetermined thickness is used as a blank material which is pickled and water-rinsed in the first process.
In the first process, a chemical for chromate conversion for steel materials consisting mainly of an aqueous chrome composition and functional chemicals is coated on the metal surface and dried to form the chromate film 6 which is closely bonded to the metal plate 1 and has a chromium of the order of 20-30 mg/m.sup.2 as shown in FIG. 3.
In the second process, the rubber adhesive as a primer is coated on the chromate film 6 and baked to form the rubber adhesive layer 7. The adhesive layer 7 is closely bonded onto the chromate film 6 and has a thickness of the order of 5-30 .mu.m.
In the third process, moreover, the heat-resistant rubber compound is coated on the adhesive layer 7 to a predetermined thickness and vulcanized to form the rubber layer 8 closely bonded to the adhesive layer 7. In this manner, a rubber coated metal as a substrate for the metal gasket is obtained.
In stead of coating the rubber compound in the third process, a rubber compound in the form of a sheet or kneaded amorphous rubber compound having a predetermined thickness may be attached to the adhesive layer. In the third process, after the rubber compound is coated on the adhesive layer, the rubber compound layer may be heated and vulcanized, while surface pressure is being applied to a surface of the rubber compound layer.
The chromate film 6 formed in the first process of the method according to the invention has great effects to improve the practical use of the metal gasket. In more detail, the chromate film 6 servers to increase the bonding force and improve the scratch-resistance, water-resistance, antifreeze coolant-resistance and the like.
By providing the chromate film 6, the resistance to physical or mechanical scratching is increased so that occurrence of scores in the adhesive layer and the rubber layer is prevented. The scratch-resistance is estimated by a coin scratch test wherein surfaces in question are scratched by a jig in the form of a coin having serrations at its edge.
There are various testing methods for estimating the performance of rubber coated metals, such as Erichsen test, water-resistance test, antifreeze coolant-resistance test, brine-resistance test, oil-resistance test and the like. The sealing faculty and durability are important as useful properties for metal gaskets and depend mainly upon the bonding power for a long period of time between the metal plate and the rubber layer. Therefore, in order to ascertain the bonding power of the rubber layer for long time, rubber coated metals as substrates of metal gaskets are often tested by boiling water durability test and antifreeze coolant durability test as durability tests for metal gaskets for automobiles. With these tests, it can be judged that the longer the time until rubber layers separate, the higher is the bonding power for long time.
In order to compare the rubber coated metals of the embodiment of the invention with those of the prior art (Comparative Example), a comparative test was effected. At the same time, performances of the rubber coated metals according to the invention were tested by changing ingredients of the adhesive and the rubber compound used in the second and third processes and changing amounts of chromium of the chromate film formed in the first process.
TABLE I______________________________________Comparative Test Comparative Embodiment 1 example______________________________________Blank material SUS * SUSAmount of chromium by 30 mg/m.sup.2 nonechromate treatmentAdhesive NBR type NBR type (standard (standard ingredient) ingredient)Rubber compound NBR type NBR type (standard (standard ingredient) ingredient)Boiling water durability >2,000 h 72 htest (100.degree. C.)Antifreeze coolant 168 h 24 hdurability test (130.degree. C.)______________________________________ * Stainless steel (Japanese Industrial Standard)
TABLE II______________________________________Amounts of chromium affectingperformances of metal gaskets Embodiment Embodiment Embodiment 1 2 3______________________________________Blank material SUS SUS SUSAmount of chro- 30 mg/m.sup.2 60 mg/m.sup.2 100 mg/m.sup.2mium by chromatetreatmentAdhesive NBR type NBR type NBR type (standard (standard (standard ingredient) ingredient) ingredient)Rubber compound NBR type NBR type NBR type (standard (standard (standard ingredient) ingredient) ingredient)Boiling water dura- >2,000 h >4,000 h >5,000 hbility test (100.degree. C.)Antifreeze coolant 168 h 240 h 336 hdurability test(130.degree. C.)______________________________________
TABLE III______________________________________Ingredients of rubber affectingperformances of metal gaskets Embodiment Embodiment Embodiment 1 4 5______________________________________Blank material SUS SUS SUSAmount of chro- 30 mg/m.sup.2 30 mg/m.sup.2 30 mg/m.sup.2mium by chromatetreatmentAdhesive NBR type NBR type NBR type (standard (ingredient (ingredient ingredient) to enhance to heat- antifreeze resistance) coolant resistance)Rubber compound NBR type NBR type NBR type (standard (ingredient (ingredient ingredient) to enhance to heat- antifreeze resistance) coolant resistance)Boiling water dura- >2,000 h >2,000 h >3,000 hbility test (100.degree. C.)Antifreeze coolant 168 h 216 h 312 hdurability test(130.degree. C.)______________________________________
The ingredient of the rubber compound in the above tests was an NBR (acrylonitrile butadiene rubber) polymer, a curing agent, a reinforcer, a plasticizer, an accelerator, an antioxidant and a filler. In the embodiments 4 and 5 in Table III, different kinds of the polymer and different amounts thereof from those of the standard ingredient were used.
The boiling water durability test and the antifreeze coolant durability test were carried out in the following manner. As shown in FIG. 5a, specimens of the rubber coated metals were rectangular plates 11 of a size 50 mm .times. 100 mm. Each specimen was formed on upper and lower halves with marking-off lines 12 in a checkerboard pattern whose distances between the lines were about 1 mm as shown in FIG. 5a.
The lower half of the specimen 11 was immersed in a liquid 14 in a vessel 13 as shown in FIG. 5b. The liquid 14 was maintained at 100.degree. C. in the boiling water durability test and at 130.degree. C. in the antifreeze coolant durability test. Hours until the marking-off lines 12 disappeared were measured. The longer the time, the better was the durability. The upper portion of the specimen was exposed to vapour 15 of the liquid 14 in the test.
As can be seen from Table I, the metal gasket according to the invention is considerably improved in the boiling water durability and the antifreeze coolant durability.
As shown in Table II, the boiling water durability and antifreeze coolant durability are significantly improved by increasing the amount of chromium in the chromate treatment.
Moreover, the boiling water durability and antifreeze coolant durability are also remarkably improved by changing the ingredients of the rubber compound to enhance the heat-resistance and the antifreeze coolant resistance as shown in Table III.
It is clear that the metal gasket according to the invention is superior in keeping high bonding power of the coating in long use.
As can be seen from the above description, according to the invention by coating the non-rinse chemical for chromate conversion on a metal plate before providing a rubber type coating layer on the metal plate, the bonding power of the rubber layers to the metal plate is further improved to obtain the superior durability for long use.
Moreover, the chromate treatment with the non-rinse chemical for chromate conversion used in the invention is easy in operation in comparison with the chemical reaction conversion and the electrolytic treatment. Furthermore, the chromate treatment has an advantage enabling thicknesses of the chromate films to adjust easily.
According to the invention as above described, by introducing the process of coating and drying the non-rinse chemical for chromate conversion, the bonding power of the rubber layer is increased to improve the sealing faculty and the durability of the metal gasket for automobiles without making difficult the operation in the production line.
Moreover, the invention is applicable to metal gaskets not only for automobiles but also screw engines, freezing equipment, air conditioning units and various industrial apparatuses.
While the invention has been particularly shown and described with reference to preferred embodiments thereof, it will be understood by those skilled in the art that the foregoing and other changes in form and details can be made therein without departing from the spirit and scope of the invention.
Claims
  • 1. A method of producing a metal gasket comprising steps of coating a non-rinse chemical for chromate conversion on at least one surface of a metal plate and drying it in a first process, coating an adhesive thereon in a second process, and providing a rubber compound layer thereon and vulcanizing it in a third process, wherein said metal plate is a steel plate selected from a stainless steel sheet and a carbon steel sheet.
  • 2. A method of producing a metal gasket as set forth in claim 1, wherein before coating the non-rinse chemical, the surface of the metal plate is cleaned by alkaline cleaning in the first process.
  • 3. A method of producing a metal gasket as set forth in claim 1, wherein said coated adhesive is then baked in the second process.
  • 4. A method of producing a metal gasket as set forth in claim 1, wherein said coated adhesive is then dried in the second process.
  • 5. A method of producing a metal gasket as set forth in claim 1, wherein said rubber compound layer is provided by coating a rubber cement to a predetermined thickness and drying it, and heating it before vulcanizing in the third process.
  • 6. A method of producing a metal gasket as set forth in claim 1, wherein said rubber compound is provided by attaching a rubber compound having a predetermined thickness selected from rubber compounds which are in the form of a sheet and kneaded amorphous, and heating it before vulcanizing in the third process.
  • 7. A method of producing a metal gasket as set forth in claim 1, wherein said rubber compound layer is heated and vulcanized, while surface pressure is being applied to a surface of the rubber compound layer.
Priority Claims (2)
Number Date Country Kind
63-186786 Jul 1988 JPX
63-128750 Oct 1988 JPX
Parent Case Info

This application is a division of application Ser. No. 386,219, filed Jul. 28, 1989.

US Referenced Citations (3)
Number Name Date Kind
2957784 Schiefelbein Oct 1960
4088621 Miller May 1978
5004650 Ashizawa et al. Apr 1991
Foreign Referenced Citations (2)
Number Date Country
63-128750 Oct 1988 JPX
63-186786 Jul 1989 JPX
Divisions (1)
Number Date Country
Parent 386219 Jul 1989