Patent Grant
8071181
The present invention relates to a metal nanoparticle and use thereof for inducing chirality in liquid crystal phases.
Nematic liquid crystals (LCs) are one-dimensionally ordered fluids commonly formed by rod-shaped molecules. Dispersed colloidal particles disrupt the nematic order, and minimization of the elastic energy leads to the formation of anisotropic colloidal structures.1 Sufficiently large particles, depending on the strength and direction of the nematic anchoring on the particle surface, can form various types of topological defects such as Saturn rings, hyperbolic hedgehogs, and boojums in agreement with theoretical considerations.2-7 Past experimental studies focused on dispersions of water microdroplets,1,8,9 ferro-fluids,10 gold coated glass spheres,11 or silicon oil12-15 in nematic LCs (N-LCs) as well as latex particles in lyotropic LCs.9,16 For most particles, if the nematic LC molecules are strongly and perpendicularly anchored at the surface of a spherical particle, the particles act like a radial hedgehog carrying a topological charge. Placed in a uniformly aligned nematic solvent to satisfy the boundary conditions at infinity, the particle should nucleate a further defect in its nematic environment. As theoretically predicted,17,18 the dipole is the preferred configuration for large particles and sufficiently strong anchoring, although quadrupoles are also observed.11 The topological dipole formed by one quasi-spherical particle and an accompanying topological defect, known as a hyperbolic hedgehog, generate elastic forces that lead to the formation of chain-like particle aggregates.19 However, the interactions between colloidal particles and the nematic LC molecules strongly depend on the particular combination of the two materials, the molecular structure and elastic properties of the LC, as well as on the type and likely the size and shape of the colloidal particle used.
Recent theoretical studies on the structural properties of gold nanoclusters have shown that the most stable (lowest energy) isomers of bare Au28, Au55 as well as thiol-protected clusters (e.g., Au28(SCH3)16) correspond to chiral nanostructures.20 These findings provide support for the existence of chirality in noble metal clusters suggested by the intense optical activity measured in the metal-based electronic transitions of size-separated glutathione-protected gold particles in the size range of 20 to 40 atoms.21 Further theoretical work, based on quantifying chirality via the Hausdorff chirality measure (HCM),20,22,23 predicts that strong structural distortions in a gold cluster upon thiol protection could, for example, induce chirality in an achiral unprotected cluster.20
In addition to the work of Whetten et al. on glutathione capped gold nanoparticles,21 the groups of Fujihara and Yao reported, for example, on the syntheses of optically active nanoclusters protected with chiral (R)- and (S)-BINAP24 or penicillamines25 (D-Pen, L-Pen, and racemate). It is important to note that all three groups used enantiomeric species of the capping agent for the synthesis of their gold nanoparticles resulting in enantiopure particles with an optical activity that is easily identified by circular dichroism (CD) spectroscopy. However, it appears that none of the considerably complex CD spectra in the UV regions, the CD signals at wavelengths where the used protecting agent does not absorb as well as an inversion of the ellipticity, and θ (mirror image) from free capping agent to the capped nanocluster25 can not be explained by the chirality of the capping agent itself. Hence, the structured CD spectra are likely due to the quantized electronic transitions and their interactions in the cluster, which indicates, as theory predicts,20 that nanoparticles can indeed form well-defined stereostructures as ‘normal’ chiral molecules do.
Circular Dichroism is observed when optically active matter absorbs left and right handed circularly polarized light with a different absorption coefficient. Another sensitive probe for molecular chirality are liquid crystalline phases, in particular the nematic phase. Nematic liquid crystals are one-dimensionally ordered fluids commonly formed by rod-shaped molecules. It has been known for a long time that doping nematic phases with chiral, nonracemic compounds (chiral additives or dopants) transforms them into chiral nematic phases,26 characterized by a helical spatial arrangement of the director. In this chiral structure, the anisotropic molecules rotate in a helical manner to form lamellae of equally spaced planes with a common molecular orientation. Polarizing optical microscopy (POM) commonly provides direct evidence of the chirality induced by a chiral dopant in a non-chiral nematic liquid crystal. Characteristic textures and defect structures clearly reveal the difference between chiral and non-chiral nematic phases. Depending on the boundary conditions (planar, homeotropic), between crossed polarizers nematic liquid crystals such as Felix-2900-03 usually produce so-called Schlieren (
According to one aspect of the present invention, there is provided a metal nanoparticle comprising: a metal; and a chiral group bonded to the metal.
According to another aspect of the present invention, there is provided a colloidal suspension or dispersion comprising: a metal nanoparticle comprising a metal and a chiral group bonded to the metal; and a liquid crystal.
According to still another aspect of the present invention, there is provided a process for preparing a metal nanoparticle as described herein comprising: providing a solution comprising HAuCl4 and a thiol comprising a chiral group; and reducing HAuCl4 with a reducing agent.
According to yet another aspect of the present invention, there is provided a use of a metal nanoparticle comprising: a metal and a thiolate group bonded to the metal; as a chiral dopant in a liquid crystal.
According to a further aspect of the present invention, there is provided a colloidal suspension or dispersion comprising: a metal nanoparticle comprising a metal and a thiolate group bonded to the metal; and a liquid crystal.
According to still a further aspect of the present invention, there is provided a method for determining chirality or local chiral effects of a metal nanoparticle comprising: mixing a non-chiral nematic liquid crystal with a metal nanoparticle; and identifying a textural change in the non-chiral nematic liquid crystal to a nematic liquid crystal thin film showing birefringent stripe domains (colored when viewed with crossed polarizers as well as parallel polarizers), wherein the presence of the textural change indicates a sort of chirality transfer or local induction of chiral interfaces by the metal nanoparticle.
According to another aspect of the present invention, there is provided a method for transferring chirality to a liquid crystal comprising: providing a liquid crystal; and doping the liquid crystal with a metal nanoparticle comprising a metal and a chiral group bonded to the metal.
According to still another aspect of the present invention, there is provided a method for transferring chirality to a liquid crystal comprising: providing a liquid crystal; and doping the liquid crystal with a gold nanoparticle comprising gold and a thiolate group bonded to the gold.
In the accompanying drawings, which illustrate an exemplary embodiment of the present invention:
Metal Nanoparticles
The present invention relates to a metal nanoparticle comprising a metal and chiral group bonded to the metal.
The metal of the metal nanoparticle may be, for example, gold, silver, platinum, or palladium. In a preferred embodiment, the metal is gold. Chirality is imparted to the metal nanoparticles by a chiral group bonded to the metal.
The chiral group may be bonded to the metal through any one of a variety of linkages, for example, a thiol linkage, a bis-thiol linkage, a thiosulfate linkage, or phosphorous linkage. In a preferred embodiment, the linkage is a thiol linkage, such as alkylthiol.
Generally, alkylthiols provide a stable monolayer protection for functionalized gold nanoparticles. The nanoparticles were synthesized using a modified Brust-Schiffrin procedure28. For example, Au1 was synthesized using a Brust-Schiffrin two phase method with a phase transfer agent such as tetraoctylammonium bromide (TOAB). The one phase method does not require the use of phase transfer agents, and provides gold nanoparticles that are stable under ambient conditions and to elevated temperature up to at least 120° C.
Thiol-protected silver29 and platinum30 nanoparticles may be prepared in the same size regime as the gold nanoparticles. Since the local chiral effect produced by the straight alkylthiol protected gold nanoparticles leading to the formation of birefringence of the stripes is only a result of a local twist of the director (coinciding with the long molecular axis of the nematic LC), silver and platinum nanoparticles, in the same size regime, should produce the same effects if dispersed in a non-chiral nematic liquid crystal. In the same sense, chirally-modified silver and platinum nanoparticles (bearing chiral dopant structures) should also produce chiral phenomena in non-chiral nematic liquid crystals.
The linkage may also comprise a spacer group, for example, an aliphatic group such as C4-18 alkyl. The length of the spacer group depends on whether it is functionalized with a chiral or liquid crystal (pro-mesogenic) moiety since thiol functionalized metal nanoparticles undergo aggregation and so-called Ostwald ripening (aggregation and sintering to form a larger particle)31 at elevated temperatures depending on the length of the aliphatic chain. Therefore, metal nanoparticles with ‘simple’ straight alkylthiols may be used with a spacer group having a length in the range of C6-18, and metal nanoparticles protected with alkylthiols that are functionalized with pro-mesogenic, liquid crystal and/or chiral moieties may be used with a spacer group having a length in the range of C4-18.
Spacer groups may also be linked. For example, if a bis-thiol linkage such as thioctic acid is employed, the alkyl spacer groups may be linked via an ester linkage.
The chiral group may be any group having one or more chiral centers. For example, the chiral group may be a chiral ester such as 6-sulfanylhexyl (2S)-(6-methoxy-2-naphthyl)propanoate, 12-sulfanyldodecyl (2S)-(6-methoxy-2-naphthyl)propanoate, (2S)-methylbutyl 7-sulfanylheptanoate, or an enantiomer thereof.
Other chiral groups, particularly those commonly used as chiral dopants for inducing chiral nematic liquid crystalline phases should also produce local and overall chiral effect in non-chiral nematic liquid crystals or liquid crystal mixtures. Given that the chiral dopants can be well-dispersed in the nematic liquid crystal host, the chiral dopant should, if reported to induce a chiral nematic phase when not linked to a metal nanoparticle, also work when linked to a metal nanoparticle in the same size regime. Such other chiral groups could contain atropisomeric cores, cholesterol structures or generally rod-like rigid segments with chiral centers in the attached side chains similar to the (S)-Naproxen functionalized thiols.
The metal nanoparticle may also be a mixed monolayer protected nanoparticle such that groups bonded to the metal are not all identical and/or not all chiral. For example, a non-chiral group may also be bonded to the metal through any one of a variety of linkages, for example, a thiol linkage, a bis-thiol linkage, a thiosulfate linkage, or phosphorous linkage. In a preferred embodiment, the non-chiral group is a C4-18 alkyl thiolate such as hexanethiol or dodecanethiol. The mixed monolayer protected nanoparticle may, for example, comprise a chiral group formed from a chiral ester such as 6-sulfanylhexyl (2S)-(6-methoxy-2-naphthyl)propanoate, 12-sulfanyldodecyl (2S)-(6-methoxy-2-naphthyl)propanoate, (2S)-methylbutyl 7-sulfanylheptanoate, or an enantiomer thereof, and a non-chiral group such as hexanethiol or dodecanethiol. The ratio of chiral to non-chiral groups may be in the range of about 5:1 to about 1:5, about 4:1 to about 1:5, about 3:1 to about 1:5, about 2:1 to about 1:5, about 1:1 to about 1:5, about 1:2 to about 1:5, about 1:3 to about 1:5, about 1:4 to about 1:5, about 5:1 to about 1:4, about 5:1 to about 1:3, about 5:1 to about 1:2, about 5:1 to about 1:1, about 5:1 to about 2:1, about 5:1 to about 3:1, about 5:1 to about 4:1, about 4:1 to about 1:4, about 3:1 to about 1:3, about 2:1 to about 1:2, about 5:1, about 4:1, about 3:1, about 2:1, about 1:1, about 1:2, about 1:3, about 1:4 or about 1:5.
For mixed monolayer protected metal nanoparticles, the ratio depends on the ratio of the two thiols used during the modified Brust-Schiffrin procedure. For the mixed cluster Au4 described herein, a 1:1 ratio of starting thiols resulting in the formation of a metal nanoparticle protected with the two thiols in a ratio of 2:1. However, this ratio likely also depends on the type of thiols used in the synthesis as well as on the synthesis itself, i.e. if using the place exchange reaction32 for introducing the second thiol starting with a hexane thiolate-coated metal nanoparticle.
In a preferred embodiment, the metal nanoparticle comprising a metal and a chiral group bonded to the metal as described herein may be:
wherein n is greater than or equal to (1) one, and x and y are in a ratio of about 5:1 to about 1:5, more preferably about 1:1 or about 1:2.
The present invention also relates to a metal nanoparticle comprising a metal and thiolate group bonded to the metal.
The metal of the metal nanoparticle may be, for example, gold, silver, platinum, or palladium. In a preferred embodiment, the metal is gold.
The thiolate group may be chiral or non-chiral.
In the case where the thiolate group is chiral, it may comprise any group with one or more chiral centers. For example, the thiolate group may comprise a chiral ester.
In a preferred embodiment, the thiolate group may be a chiral ester such as 6-sulfanylhexyl (2S)-(6-methoxy-2-naphthyl)propanoate, 12-sulfanyldodecyl (2S)-(6-methoxy-2-naphthyl)propanoate, (2S)-methylbutyl 7-sulfanylheptanoate, or an enantiomer thereof.
In the case where the thiolate group is non-chiral, it may be a C4-18 alkyl thiolate optionally substituted with one or more substituents. Such substituents may include, for example, halogen, hydroxyl, carbonyl (such as carboxyl, ketones (including alkylcarbonyl and arylcarbonyl groups), and esters (including alkyloxycarbonyl and aryloxycarbonyl groups)), thiocarbonyl, acyloxy, alkoxyl, phosphoryl, phosphonate, phosphinate, amino, acylamino, amido, amidine, imino, cyano, nitro, azido, sulfhydryl, alkylthio, sulfate, sulfonate, sulfamoyl, sulfonamido, heterocyclyl, aralkyl, or an aromatic or heteroaromatic moiety.
In a preferred embodiment, the thiolate group may be, for example, hexanethiol or dodecanethiol.
The metal nanoparticle comprising a metal and a thiolate group bonded to the metal as described herein may also be a mixed monolayer protected nanoparticle such that thiolate groups bonded to the metal are not all identical, more specifically the chemical nature and the chirality of the thiolate groups need not be identical.
In a preferred embodiment, the mixed monolayer protected nanoparticle may, for example, comprise a thiolate group formed from a combination of thiols such as 6-sulfanylhexyl (2S)-(6-methoxy-2-naphthyl)propanoate, 12-sulfanyldodecyl (2S)-(6-methoxy-2-naphthyl)propanoate, (2S)-methylbutyl 7-sulfanylheptanoate, hexanethiol or dodecanethiol.
In a preferred embodiment, the metal nanoparticle comprising a metal and a thiolate group bonded to the metal may be:
wherein n is greater than or equal to (1) one, and x and y are in a ratio of about 5:1 to about 1:5, more preferably about 1:1 or about 1:2.
The metal nanoparticles described herein may further comprise a luminescent atom or group. Examples of such atoms or groups are lanthanide atoms doped into the metal core or organic dyes on the surface of the metal via the spacer groups.
Luminescent functionalities may be introduced and should not interfere with the domain formation and the chirality transfer. The reason for introducing luminescent groups is twofold: (i) application and self-illumination for device applications, and (ii) to study the assembly process by techniques such as fluorescence microscopy. Two possible ways to introduce luminescence (electro- or photo-luminescence) into these materials are: (i) using fluorescently labeled thiols during the particle synthesis using common fluorescent dyes (with rod-like shape), and (ii) using doped metal nanoparticles (some of which are commercially available). In principle, both ways of introducing luminescence will neither interfere with the assembly process nor with the chiral effects due to chirality transfer or to local twist of the director configuration.
The average size of the metal nanoparticles described herein may be, for example, from about 1 nm to about 100 nm, from about 1 nm to about 90 nm, from about 1 nm to about 80 nm, from about 1 nm to about 70 nm, from about 1 nm to about 60 nm, from about 1 nm to about 50 nm, from about 1 nm to about 40 nm, from about 1 nm to about 30 nm, from about 1 nm to about 20 nm, from about 1 nm to about 10 nm, from about 10 nm to about 100 nm, from about 20 nm to about 100 nm, from about 30 nm to about 100 nm, from about 40 nm to about 100 nm, from about 50 nm to about 100 nm, from about 60 nm to about 100 nm, from about 70 nm to about 100 nm, from about 80 nm to about 100 nm, from about 90 nm to about 100 nm, from about 20 nm to about 90 nm, from about 30 nm to about 80 nm, from about 40 nm to about 70 nm, from about 50 nm to about 60 nm, from about 1 nm to about 10 nm, from about 1 nm to about 9 nm, from about 1 nm to about 8 nm, from about 1 nm to about 7 nm, from about 1 nm to about 6 nm, from about 1 nm to about 5 nm, from about 1 nm to about 4 nm, from about 1 nm to about 3 nm, from about 1 nm to about 2 nm, from about 2 nm to about 10 nm, from about 3 nm to about 10 nm, from about 4 nm to about 10 nm, from about 5 nm to about 10 nm, from about 6 nm to about 10 nm, from about 7 nm to about 10 nm, from about 8 nm to about 10 nm, from about 9 nm to about 10 nm, from about 2 nm to about 9 nm, from about 3 nm to about 8 nm, from about 4 nm to about 7 nm, from about 5 nm to about 6 nm, from about 2 nm to about 5 nm, about 1 nm, about 2 nm, about 3 nm, about 4 nm, about 5 nm, about 6 nm, about 7 nm, about 8 nm, about 9 nm, about 10 nm, about 20 nm, about 30 nm, about 40 nm, about 50 nm, about 60 nm, about 70 nm, about 80 nm, about 90 nm, or about 100 nm.
Process for Preparing a Metal Nanoparticle
The present invention also relates to a process for preparing a metal nanoparticle as described herein when the metal is gold. The process comprises providing a solution comprising HAuCl4 and a compound having a chiral or non-chiral thiolate group; and reducing the HAuCl4 with a reducing agent.
For example, the compound having a chiral and/or non-chiral thiolate group may be 6-sulfanylhexyl (2S)-(6-methoxy-2-naphthyl)propanoate, 12-sulfanyldodecyl (2S)-(6-methoxy-2-naphthyl)propanoate, (2S)-methylbutyl 7-sulfanylheptanoate, hexanethiol or dodecanethiol.
The reducing agent may be for example a complex hydride such as NaBH4 or LiAlH4.
The solvent used for the solution comprising HAuCl4 and a compound having a chiral group may be tetrahydrofuran, toluene, hexane or a mixture thereof. The solution may also be biphasic requiring the use of a phase transfer agent.
Use of Metal Nanoparticles with a Liquid Crystal
The present invention also relates to a metal nanoparticle as described herein for use as a chiral dopant in a non-chiral liquid crystal phase. Examples of liquid crystal phases are nematic phases, such as uniaxial, biaxial, or discotic; smectic phases, such as smectic A, smectic C, or hexatic; and banana phases produced by bent-core liquid crystals or discotic liquid crystals. In a preferred embodiment, the liquid crystal may be Felix-2900-03
or a cyanobiphenyl derivative such as 4′-n-pentyl-4-cyanobiphenyl (5CB), 4′-n-octyl-4-cyanobiphenyl (8CB) or 4′-n-octyloxy-4-cyanobiphenyl (8OCB), or other nematic LCs or LC mixtures.
Liquid crystal modified thiols may be used. The use of cyanobiphenyls (common nematic liquid crystals) results in a higher compatibility between metal nanoparticles and the liquid crystal host due to the liquid crystal functionalization of the metal nanoparticle surface maximizing interactions between the two components. Also a combination of chiral units such as (S)-Naproxen and alkylthiol functionalized cyanobiphenyls may be used.
Characterization of the nanoparticle doped nematic phase of Felix-2900-03 by polarized optical microscopy revealed the formation of textures similar to textures commonly formed by chiral nematic liquid crystalline phases, namely the formation of so-called cholesteric finger-like textures (striped textures) due to the formation of topological defects coupled with either induced chirality (chirally modified metal nanoparticles), or local chiral twist (non-chiral metal nanoclusters).
The present invention also relates to a colloidal suspension or dispersion comprising a metal nanoparticle as described herein and a liquid crystal.
The colloidal suspension or dispersion described herein may comprise, for example, from about 1 to about 20%, from about 2 to about 20%, from about 3 to about 20%, from about 4 to about 20%, from about 5 to about 20%, from about 6 to about 20%, from about 7 to about 20%, from about 8 to about 20%, from about 9 to about 20%, from about 10 to about 20%, from about 11 to about 20%, from about 12 to about 20%, from about 13 to about 20%, from about 14 to about 20%, from about 15 to about 20%, from about 16 to about 20%, from about 17 to about 20%, from about 18 to about 20%, from about 19 to about 20%, from about 1 to about 19%, from about 1 to about 18%, from about 1 to about 17%, from about 1 to about 16%, from about 1 to about 15%, from about 1 to about 14%, from about 1 to about 13%, from about 1 to about 12%, from about 1 to about 11%, from about 1 to about 10%, from about 1 to about 9%, from about 1 to about 8%, from about 1 to about 7%, from about 1 to about 6%, from about 1 to about 5%, from about 1 to about 4%, from about 1 to about 3%, from about 1 to about 2%, from about 2 to about 19%, from about 3 to about 18%, from about 4 to about 17%, from about 5 to about 16%, from about 6 to about 15%, from about 7 to about 14%, from about 8 to about 13%, from about 9 to about 12%, from about 10 to about 11%, about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 11%, about 12%, about 13%, about 14%, about 14%, about 15%, about 16%, about 18%, about 19%, or about 20% by weight of the metal nanoparticle in the colloidal suspension or dispersion.
The colloidal suspension or dispersion may also comprise bent-core liquid crystals. These are non-chiral compounds that can form chiral liquid crystalline phases due to their bent molecular structure and a molecular tilt within the layers of the layer structure resulting in a macroscopic polarization that can be switched between different orientations by applying an electric field.
The metal nanoparticles described herein which further comprise a luminescent atom or group may be used in self-illuminating displays.
The colloidal suspensions or dispersions described herein may be used in, for example, an optical device, an electro-optical device, a liquid crystal display, a liquid crystal thermometer, a coating, a sensor, an optical memory, a non-linear optical device, or a light shutter or valve.
The following examples are provided to illustrate the invention. It will be understood, however, that the specific details given in each example have been selected for the purpose of illustration and are not to be construed as limiting in scope of the invention.
General Considerations
HAuCl4.3H2O (99.999%), (S)-Naproxen, p-toluenesulfonic acid, NaBH4, hexamethyldisilathiane (Me3Si)2S, hexan-1-thiol, dodecane-1-thiol, tetraoctylammonium bromide, 12-bromododencan-1-ol, and tetrabutylammonium fluoride TBAF (1.0M in THF) were purchased from Aldrich and used as received.
X-ray diffraction (XRD) patterns were obtained on an MPD X'Pert system (PANalytical) using CuKα radiation (40 kv, 200 mA). Au3 and Au6 were measured in reflection geometry using a zero-background flat sample holder, Au7 using a 0.3 mm glass capillary in transmission geometry. UV-Vis spectra were obtained using an Agilent 8453 spectrophotometer. Transmission electron microscopy (TEM) images were obtained on a JEOL FX 2000 TEM instrument operating at an accelerating voltage of 160 kV. A 3 μL drop of the isolated gold colloid solutions was dropcasted on carbon coated cooper grids (400 mesh) and dried for 2 hours. Circular dichroism (CD) spectra were recorded on a J-810 spectropolarimeter (Jasco Inc.) using a bandwidth of 2 nm (accumulation of three spectra, circular quartz cuvettes with 1 cm path length). Polarizing optical microscopy (POM) was performed using an Olympus BX51-P polarizing microscope in conjunction with a Linkam LS350 heating/cooling stage.
First, 12-bromododecyl (2S)-2-(6-methoxy-2-naphthyl) propanoate was synthesized according to a procedure33 using Naproxen (7.8 mmol, 1.8 g), 12-bromo-dodecan-1-ol (7.8 mmol, 2.0 g) and p-toluenesulfonic acid (9.8 mmol, 1.7 g) in toluene (50 ml). The mixture was refluxed for about 10 h under N2 in a round bottom flask using a Dean-Stark trap. The reaction progress was monitored by TLC (hexane:ethyl acetate=8:2). After the reaction was complete, the reaction mixture was cooled to room temperature, and then washed with water (3×). The organic layer was separated, dried (Na2SO4), and the solvent evaporated under reduced pressure. The crude residue was purified by column chromatography (hexane:ethyl acetate=8:2) to afford 3.6 g (97%). 1H NMR (300 MHz, CDCl3) δ (ppm): 1.22 (m, br, 16H, CH2), 1.44 (m, H, CH2CH2O), 1.62 (d, 3H, J=7.2 Hz, CH3CH), 1.88 (m, 2H, CH2CH2Br), 3.43 (t, 2H, J=6.8 Hz, CH2Br), 3.83 (m, 1H, CHCH3), 3.93 (s, 3H, CH3O), 4.10 (t, 2H, J=6.6 Hz, OCH2CH2), 7.18 (m, 2H, Ar—H), 7.46 (d, 1H, J=8.5 Hz, Ar—H), 7.70 (d, 2H, J=3.6 Hz, Ar—H), 7.74 (s, 1H, Ar—H). 13C NMR (75 MHz, CDCl3): 129.66, 128.63, 127.46, 126.31, 125.70, 119.32, 105.98, 65.28, 55.69, 45.95, 34.43, 33.25, 29.89, 29.17, 28.58, 26.19, 18.91. MS m/z (rel. int., %): 478 (7.1) [M]+, 396 (9.3), 185 (100), 170 (5.9), 141 (7.5).
The compound 12-sulfanyldodecyl (2S)-2-(6-methoxy-2-naphthyl) propanoate was then synthesized according to a procedure reported by Hu and co-workers.34 Briefly, 12-bromododecyl (2S)-2-(6-methoxy-2-naphthyl) propanoate (2.5 mmol, 1.2 g) was dissolved with freshly distilled dry THF (5 ml) and then cooled to −10° C. using an acetone/ice bath. To the resulting solution, hexamethyldisilathiane (3.0 mmol, 0.63 ml) and TBAF (1M in THF, 2.76 mmol, 2.76 ml) were added under an inert gas atmosphere. After the reaction was complete (TLC, hexane:ethyl acetate=8:2), the mixture was allowed to warm to room temperature. Thereafter, the solution was partitioned between diethyl ether (100 ml) and saturated aqueous ammonium chloride (100 ml), the layers were separated, and the organic phase washed with water (50 ml). After evaporation of the solvent under reduced pressure, the crude residue was purified by column chromatography (hexane:ethyl acetate=8:2) to yield 1.95 g of 12-sulfanyldodecyl (2S)-2-(6-methoxy-2-naphthyl) propanoate (60%). 1H NMR (300 MHz, CDCl3) δ (ppm): 1.21-1.37 (m, br, 20H, CH2, and overlapped 1H, SH), 1.58 (d, 3H, J=7.2 Hz, CH3CH), 2.53 (q, 2H, J=7.5 Hz, CH2SH), 3.88 (q, 1H, J=6.2 Hz, CHCH3), 3.93 (s, 3H, CH3O), 4.08 (t, 2H, J=6.8 Hz, CH2O), 7.18 (m, 2H, Ar—H), 7.46 (d, 1H, J=1.8 Hz, Ar—H), 7.70 (d, 2H, J=4.4 Hz, Ar—H), 7.73 (s, 1H, Ar—H). 13C NMR (75 MHz, CDCl3): 129.65, 127.45, 126.68, 126.30, 119.30, 105.97, 65.28, 55.68, 45.94, 34.45, 29.92, 29.47, 28.77, 26.31, 26.19, 25.05, 18.91. MS m/z (rel. int., %): 432 (3.4) [M]+, 230 (3.2), 212 (5.3), 185 (100), 171 (2.7), 155 (2.0), 141 (8.8).
All glassware used for the preparation and storage of colloidal gold was treated with aqua regia, cleaned with piranha solution, and rinsed with deionized water (Millipore, resistivity 18.2 MΩ) and dried overnight at 100° C.
The gold nanoparticle Au3 was prepared according to the Brust procedure.28 12-sulfanyldodecyl (2S)-2-(6-methoxy-2-naphthyl) propanoate (1.16 mmol, 0.5 g) and HAuCl4.3H2O (0.58 mmol, 0.2 g) were dissolved in freshly distilled dry THF (20 ml). The resulting solution was stirred 10 min, after which a freshly prepared solution of NaBH4 (0.22 g) in deionized water (10 ml) was added at once. The mixture was stirred for additional 2 h. The solvent was evaporated under reduced pressure, and the black precipitate was collected and exhaustively washed with deionized water and hexane.
The gold nanoparticles Au1, Au2, Au4, Au5 and Au7 were also prepared according to the Brust procedure, while the gold nanoparticle Au6 was prepared according to the method by Shon and coworkers.35
The purity of each nanoparticle sample (removal of unreacted thiol) was checked by 1H NMR spectroscopy. Further, each nanoparticle sample was characterized by TEM (see representative examples in
To obtain information on the optical activity of the gold nanoparticles, the CD spectrum of each nanoparticle sample was measured in solution over a range extending from 240 to 600 nm (see representative example in
The CD spectra of hexane thiolate and dodecane thiolate protected gold nanoparticles exhibited weak CD signals with features centered at 285 and 475 nm that are attributed to scattering artifacts. The scattering observed for the ellipticity of the alkane thiolate clusters (Au6 and Au7) is also likely due to the size distribution of the present nanoparticles as observed by TEM (
A representative example of a size distribution analysis of a gold nanoparticle is shown in
To probe the propensity of metal nanoparticles to induce chiral nematic phases upon dispersion in non-chiral nematic liquid crystal hosts, the gold nanoparticles Au1-Au7 were mixed with the nematic/monotropic smectic-C (SmC) liquid crystal Felix-2900-03.
All glass vials and Teflon-coated spatulas were rinsed with aqua regia prior to all mixtures preparations. Mixtures of Felix-2900-03 doped with Au1-Au7 were then prepared by mixing ready prepared solutions of both components in a common pure, dry solvent (e.g., ethyl acetate). The resulting solutions were sonicated for approximately 3 minutes, and the solvent was evaporated by a steady stream of dry N2 over the open glass vials. Thereafter, all mixtures were dried in vacuum for 24 hours. Prior to the preparation of the thin films sandwiched between microscope glass slides, all mixtures were heated just below the isotropic-nematic phase transition (TNI) and continuously mixed (stirred or sonicated).
Recent studies on the stability of thiolate-protected gold nanoparticles suggest that thiols with a carbon chain longer than C6 begin to desorb from the gold nanoparticle surface above a threshold of 160° C.36 Therefore, it was assumed that during all mixing experiments no changes in the nanoparticle composition (surface) via desorption of thiolate takes place.
Rather striking is the effect of the thiolate-protected gold nanoparticles on the liquid crystal texture of the nematic phase of Felix-2900-03 as observed by Polarizing Optical Microscopy. On cooling from just below the nematic to isotropic phase transition (TNI), Felix-2900-03 doped with 5 wt % of Au1-Au7 (see representative examples in
Similar chiral nematic textures were also observed for mixtures of Felix-2900-03 either doped with 5 wt % of the 12-sulfanyldodecyl (2S)-2-(6-methoxy-2-naphthyl) propanoate (
A comparison of a nematic liquid crystal before and after doping with Au7 is shown in
Although various embodiments of the invention are disclosed herein, many adaptations and modifications may be made within the scope of the invention in accordance with the common general knowledge of those skilled in this art. Such modifications include the substitution of known equivalents for any aspect of the invention in order to achieve the same result in substantially the same way. Numeric ranges are inclusive of the numbers defining the range. In the claims, the word “comprising” is used as an open-ended term, substantially equivalent to the phrase “including, but not limited to”.
This application is the §371 U.S. National Stage of International Application No. PCT/CA2007/000046, filed 12 Jan. 2007, which claims the benefit of U.S. Provisional Application Ser. No. 60/758,201, filed 12 Jan. 2006, all of which are incorporated herein by reference in their entirety.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/CA2007/000046 | 1/12/2007 | WO | 00 | 9/11/2008 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2007/079585 | 7/19/2007 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6287649 | Fukushima et al. | Sep 2001 | B1 |
| 6482988 | Fukushima et al. | Nov 2002 | B2 |
| 20040250750 | Reda et al. | Dec 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| 2334238 | Dec 1999 | CA |
| 2 537 199 | Mar 2005 | CA |
| 20080134866 | Nov 2008 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20090027611 A1 | Jan 2009 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60758201 | Jan 2006 | US |