The present invention relates to metal-organic frameworks (MOFs) of the formula [M2(dcx)2L2] containing dicarboxylates (dcx) and hydrazones (L), method for their preparation and their application.
In recent years the design and fabrication of metal-organic frameworks (MOF) has become one of the most intensively developing areas of materials chemistry and nanotechnology. The wide range of their practical application mainly results from the large inner surface and high flexibility, as well as high mechanical strength and thermal resistance. These characteristics provide these materials with the ability to adsorb different “guest” molecules, which is reflected in multiple applications of MOF materials including the storage of hydrogen and other gases, molecular identification, separation of mixtures (by selective sorption), catalysis, synthesis and adsorption of drugs. Because of the enormous variety of organic ligands, allowing for the control of network geometry, it is possible to design a product with unique properties based on the available reactants. Such metal-organic systems are described for example in U.S. Pat. No. 7,119,219, concerning the preparation of metal-organic network from a metal salt and a bidentate organic ligand. Another example of the preparation of a metal-organic network is the reaction of metal ions with one or more organic ligands, as disclosed in description EP0790253. Metal-organic networks can be obtained electrochemically, as disclosed in description U.S. Pat. No. 8,163,949.
The article Cooperative Effect of Unsheltered Amide Groups on CO2 Adsorption Inside Open-Ended Channels of a Zinc(II)-Organic Framework published in Inorg. Chem. 2013, 52, 3962-3968 describes for example a network comprising a zinc metalloligand with terephthalate groups.
Metal-organic frameworks (MOFs) according to the present invention comprise a repeating unit of the general formula [M2(dcx)2L2], wherein M is a metal cation (M2+), dcx is an anion of a dicarboxylic acid, and L is a neutral molecule of hydrazone. Metal cation belongs to the group comprising: Zn2+, Cd2+, Cu2+, Mn2+, Co2+, Ni2+. The ligand dcx is an anion of carboxylic acid selected from 1,4-benzenedicarboxylic acid (formula 1), substituted 1,4-benzenedicarboxylic acid (formula 2), 1,4-cyclohexanedicarboxylic acid (formula 3), 2,6-naphthalenedicarboxylic acid (formula 4), biphenyl-4,4′-dicarboxylic acid (formula 5), thiophene-2,5-dicarboxylic acid (formula 6), and 2,5-dihydroxyterephthtalic acid (formula 7), where X is selected from NH2, Br, NO2, OH.
Hydrazone L is selected from compounds of the formulas 8, 9 or 10, wherein A, D, X, Z independently represent a nitrogen (N) atom, or a carbon atom with the amine substituent (C—NH2), or a carbon atom with a hydrogen atom (CH), and wherein R represents a hydrogen atom, a C1-C6 alkyl or aryl group.
A method for preparation of metal-organic frameworks (MOFs) of the formula [M2(dcx)2L2] according to the present invention consists of two steps. The first step comprises a synthesis of hydrazone, wherein a compound from the group of aldehydes or ketones, selected from the compounds of the formulas 11, 12 or 13,
wherein A and D independently represent a nitrogen (N) atom, a carbon atom with an amine substituent (C—NH2), or a carbon atom with a hydrogen atom (CH), and R represents a hydrogen atom, a C1-C6 alkyl or aryl group is condensed with a hydrazide of the formula 14, wherein X and Z independently represent a nitrogen (N) atom, a carbon atom with an amine substituent (C—NH2), or a carbon atom with a hydrogen atom (CH).
The condensation reaction is conducted at a 1:1 molar ratio of carbonyl to hydrazide group or with a stoichiometric excess of one of the reactants. The reaction is conducted by mechanochemical means (without or with a small participation of a solvent) or in a solvent selected from C1-C8 alcohols, aqueous alcoholic solutions, N,N′-dimethylformamide (DMF), or N,N′-diethylformamide (DEF), preferably in ethanol or in an aqueous alcoholic solution. The product of the first step is hydrazone L of the formula 8, 9 or 10, in its ketone or enol form, neutral or deprotonated.
In the second step the condensation product, hydrazone L, is reacted with a compound selected from M(NO3)2, M(ClO4)2, M(SO4)2, or M(CH3COO)2, MCl2 using a dicarboxylic acid selected from the acids of the formulas 1-7. The reaction is conducted at a 1:1:1 molar ratio of metal to dicarboxylic acid and hydrazone L or with a stoichiometric excess or deficiency of one of the reactants.
Both steps of the synthesis are conducted within a temperature range from −20° C. to 150° C., preferably from 60 do 130° C. and under autogenous pressure, in a closed vessel.
The application of coordination polymers of MOF type according to the present invention comprise the detection, capturing, separation or storage of molecules such as hydrogen, carbon dioxide, carbon monoxide, alcohols, water, hydrocarbons, fabrication of ionic conductors, including those containing H+, Li+, Na+, K+, NH4+, construction of batteries and fuel cells, as well as drug carriers.
The advantage of a metal-organic framework (MOF) of the formula [M2(dcx)2L2] is a combination of two types of ligands (dcx and L), which allowed for the compensation of the charge of metal ions (M2+) with anions of dicarboxylic acids and the introduction of two different functional groups (C═O and N—H) in the form of a neutral hydrazone linker into the framework. These moieties may play a respective role of an acceptor or a donor of hydrogen bond, thereby creating the possibility of a selective interaction with potential molecules-guests and a dynamic behavior of the framework in case of interpenetration and interaction of interpenetrating frameworks using hydrogen bonds. Furthermore, hydrazide-hydrazones L introduced into the network can be subject to both keto-enol tautomerism and deprotonation, which can be used in case of further postsynthetic modifications of the network with ions introduced e.g. mechanochemically.
The invention has been described using the following embodiment.
Synthesis of [M2(dcx)2L2].G (product 1),
wherein M2+=Zn2+; dcx=anion of 1,4-benzenedicarboxylic acid; L=hydrazone of the formula 8, wherein A=N; D=CH; X=N; Z=CH; R=H; G=1DMF.1H2O
Step 1: Synthesis of hydrazone L:
Isonicotinic acid hydrazide (686 mg; 5.00 mmol) was dissolved in 20 cm3 of ethanol. 4-picolinic aldehyde (0.471 cm3; 5.00 mmol) was added and the mixture was heated to reflux for 20 min. Subsequently the solution was left to cool and crystallize the product. After the crystallization the precipitate was filtered, and the filtrate was concentrated and left in ice bath until the crystallization of a further product fraction. The second crystallized fraction was filtered. The fractions were combined and air-dried. Yield: 1.02 g (90%). The synthesis and the X-ray structure of this hydrazone were described in the literature (W.-X. Ni, M. Li, X.-P. Zhou, Z. Li, X.-C. Huang, D. Li Chem. Commun. 2007, 3479).
The compound was identified spectrally based on the selected bands:
FT-IR (ATR, cm−1): ν(C═O)L 1683, ν(NH) 3190.
Step 2: Hydrazone L (453 mg; 2.00 mmol), 1,4-benzenedicarboxylic acid (332 mg; 2.00 mmol) and Zn(NO3)2 were dissolved in 162 cm3 of N,N′-dimethylformamide (DMF) and 18 cm3 of water. The sealed vessel was heated at 70° C. for 48 hours to yield a fine-crystalline yellow product (420 mg). The product was washed with DMF and dried in a vacuum oven (30 min, 60° C., 500 mbar). Yield: 42%.
The product was identified using elemental, spectral, crystallographic, diffractometric and thermogravimetric analysis:
Elemental analysis: Measured: N, 12.58; C, 49.80; H, 3.91. Calculated for C43H37N9O12Zn2: N, 12.57; C, 51.51; H, 3.72%.
FT-IR (ATR, cm−1): ν(COO)as 1580, ν(COO)s 1392, ν(C═O)DMF 1661, ν(C═O)L 1680, ν(NH) 3222.
Crystallographic data (SCXRD): orthorhombic system, space group Iabc, a=15.1123(3), b=9.9069(3), c=31.2591(6) Å, V=9404.0(3) Å3, T=293(2) K, Z=8, Dc=1.403 Mg m−3, μ=1.082 mm−1, 61329 measured reflections, 5813 independent reflections, 4390 observed reflections [I>2σ(I)]. R1=0.0724; wR2=0.1918 [for 4390 observed reflections].
Spatial structure of the obtained product 1 was illustrated in figures:
Synthesis of [M2(dcx)2L2].G (product 2),
wherein M2+=Zn2+; dcx=anion of 1,3-benzenedicarboxylic acid (formula XX below, X1=H);
L=hydrazone of the formula 8, wherein A=N; D=CH; X=N; Z=CH; R=H; G=2DMF
Step 1: Synthesis of hydrazone L:
Isonicotinic acid hydrazide (686 mg; 5.00 mmol) was dissolved in 20 cm3 of ethanol. 4-picolinic aldehyde (0.471 cm3; 5.00 mmol) was added and the mixture was heated to reflux for 20 min. Subsequently the solution was left to cool and crystallize the product. After the crystallization the precipitate was filtered, and the filtrate was concentrated and left in ice bath until the crystallization of a further product fraction. The second crystallized fraction was filtered. The fractions were combined and air-dried. Yield: 1.02 g (90%). The synthesis and the X-ray structure of this hydrazone were described in the literature (W.-X. Ni, M. Li, X.-P. Zhou, Z. Li, X.-C. Huang, D. Li Chem. Commun. 2007, 3479).
The compound was identified spectrally based on the selected bands:
FT-IR (ATR, cm−1): ν(C═O)L 1683, ν(NH) 3190.
Step 2: Hydrazone L (36 mg; 0.16 mmol), 1,3-benzenedicarboxylic acid (27 mg; 0.16 mmol) and Zn(NO3)2 (62 mg; 0.16 mmol) were dissolved in 16.2 cm3 of N,N′-dimethylformamide (DMF) and 1.8 cm3 of water. The sealed vessel was heated at 60° C. for 70 hours to yield a fine-crystalline yellow product (20 mg). The product was washed with DMF and dried in a vacuum oven (30 min, 60° C., 500 mbar). Yield: 12%.
The product was identified using elemental, spectral, crystallographic, diffractometric and thermogravimetric analysis:
Elemental analysis: Measured: N, 13.21; C, 52.06; H, 4.19. Calculated for C46H44N10O12Zn2: N, 13.22; C, 52.14; H, 4.19%.
FT-IR (ATR, cm−1): ν(CO)as 1557, ν(COO)s 1394, ν(C═O)DMF 1685, ν(C═O)L 1675, ν(NH) 3208.
| Number | Date | Country | Kind |
|---|---|---|---|
| 408565 | Jun 2014 | PL | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2015/054558 | 6/16/2015 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2015/193820 | 12/23/2015 | WO | A |
| Entry |
|---|
| Hu et al., Cryst. Eng. Comm., 15(45), 2013, 9553-9561. (Year: 2013). |
| Lu et al., Polyhedron, 83, 2014, 108-115 (Year: 2014). |
| International Search Report and Written Opinion issued in corresponding International Patent Application No. PCT/IB2015/054558 dated Oct. 2, 2015 (9 pages). |
| Lu et al., “A series of two-dimensional coordination polymer crystal materials based on two flexible bis-pyridyl-bis-amide ligands with fluorescent sensing activities and photocatalytic properties,” Polyhedron, vol. 83, 2014, pp. 108-115. |
| Hu et al., “Structure diversities of ten entangled coordination polymers assembled from reactions of Co(II) or Ni(II) salts with 5-(pyridin-4-yl)isophthalic acid in the absence or presence of auxiliary N-donor ligands,” CrystEngComm, vol. 15, No. 45, 2013, pp. 9553-9561. |
| Number | Date | Country | |
|---|---|---|---|
| 20180161755 A1 | Jun 2018 | US |