The present invention relates to a metal reactor cell useful for the treatment of gases, and the manufacturing method thereof.
Reactor cells having channels through which gas is passed are widely used in the treatment of gases, for instance in the purification of exhaust and flue gases. On the surfaces of the channels, there are active agents such as catalysts. Such reactor cells may be made from metal sheets. The sheets are coated with ceramic porous support in which the active metals or metal oxides are immobilized. Also fully ceramic reactor cells are being manufactured.
Mechanical requirements imposed on such a reactor cell are getting higher due to increasingly stricter regulations concerning the protection of the atmosphere. For instance to purify exhaust gases, the reactor cell is adjusted as close to the engine as possible to guarantee an adequate performance thereof. The reactor cell is thus subjected to very high temperature and pressure changes. In general, the temperatures in reactor cells close to the engine are high since the purpose is to burn the fuel at a high temperature with a minimal amount of air.
The pressure losses of a metal reactor cell are low, geometrical surface area for reactions is high, and thus the operation thereof will start more quickly in comparison with a ceramic cell. A ceramic reactor cell is mechanically relatively strong, but joining it for instance to a housing may cause problems. Normally, ceramic reactor cells are only made in form of so-called straight cells where the thermal and mass transfer properties of gases are not optimal for the gas treatment.
In metal reactor cells, corrugated sheets are often used, the sheets being either wound or bent to an S-form together with flat sheets. The reactor cell is combined with a housing in the gas line either with welding or soldering joints on the housing, or with strips or rods within the housing. A reactor cell having corrugated sheets overlapping flat sheets and they are joined together with weld joints at the edges of the sheets is currently in use. Further, a reactor cell having corrugated sheets connected to each other with very widely separated soldering or welding joints is known.
The resistance of the reactor cell is tested with accelerated tests wherein the reactor cell is exposed to very quick temperature and pressure changes. Commercially available reactor cells for the purification of exhaust gases withstand undamaged only few hours most demanding test conditions of this kind. In future, reactor cells should resist such test conditions for tens or even for hundreds of hours.
A reactor cell that is also particularly resistant to demanding conditions and useful for the treatment of gases has now been invented.
In this invention, a corrugated sheet means any sheet with a corrugation. A corrugation refers to any part of the sheet having a surface on a different level relative to the middle plane of the sheet. A corrugated sheet may comprise impressions or depressions as corrugations. The corrugated sheet may also be a profiled sheet made from a flat sheet by bending or pressing symmetrically or unsymmetrically relative to the middle plane of the sheet. The profiles may for instance be corrugations or the sheet may comprise profiles in V-form. As for the other sheet, it may be any different sheet that may be joined to the corrugated sheet. This another sheet may be a corrugated sheet or for instance a flat sheet, perforated sheet or a mesh sheet. This another sheet may also be a sheet made from the corrugated sheet by bending or winding.
The corrugations of the corrugated sheet may have different shapes and sizes at different points of an individual corrugated sheet. In separate corrugated sheets, the corrugations may also have different shapes and sizes. It is thus possible to assemble a reactor cell having at its center densely corrugated sheets that are very close to one another, and at its edges thinly corrugated sheets that are more widely spaced apart. With such a solution, the flows within the reactor cell may be controlled.
In this patent application, the direction of the corrugation refers to the direction in which the plane of the surface of the corrugation differs most from the plane of the surface of the sheet adjacent to the corrugation. In a profiled sheet, the direction of the corrugation is the direction of the corrugations or grooves of the profile. The directions of the corrugations determine the directions of the channels formed between the sheets. Thus, the corrugation substantially influences the flow of the gas being treated in the channels of the reactor cell.
The corrugation shapes, sizes and directions of the reactor cell sheets as well as the density of channels in the reactor cell cross section are selected according to the intended application.
The reactor cell may also have many different shapes, it may e.g. be a spiral, bent to S-, J- or V-form or stacked or bent reactor cell. The density of the channels may for instance be 1 to 300 channels per cm.sup.2, preferably 1-10 or 10-50 or 50-100 or 100-300 channels per cm.sup.2. Further, the thickness of the sheet may vary. In this manner, reactor cells with very different flow properties may be accomplished. The cross section of the housing may be varied freely according to the intended application. It may for instance be circular, oval or semiparallelogram. Sizes and shapes of the housings conventional in the art may be preferably used.
For the treatment of exhaust gases, the material of the reactor cell sheets may for instance be ferritic iron-chromium-aluminium alloy, e.g. W1.4767. The cells may also be made of so-called austenitic superalloy W2.4633 having high nickel and chromium contents, for example.
The reactor cell of the invention may be placed in a housing having a shape corresponding to that of the reactor cell. Thus, the number of so-called dead centers or bypass points in the housing are minimized. This solution also improves the performance of the reactor cell. The applicability of the invention thus becomes more versatile.
A corrugated sheet is mechanically more rigid and stronger than a flat one. The corrugations of the sheet may also reduce the resonances in the reactor cell due to e.g. the gas flow. The corrugations of the sheet increase the contact surface of the reactor cell thus making the operation thereof more efficient. Moreover, the profiled sheet has the inherent property to yield internally in case of e.g. thermal expansion. The joints are thus not broken as easily as the joints on surfaces of flat sheets.
Joining the sheets together may be carried out by welding such as by resistance welding or beam welding. Said welding techniques are particularly suitable for manufacturing reactor cells since they allow high numbers of sheets to be joined together quickly and locally. Sheets may also be joined together by soldering.
The cell of the invention is mechanically substantially stronger than any known metal reactor cell. The service life thereof in highly demanding engine tests is even 5 to 10 times longer than service lives of commercially available rivaling products. It may be placed directly adjacent to the engine since it withstands even extremely variable conditions for long periods of time without breaking.
The reactor cell of the invention may also be made from relatively thin sheets thus decreasing the thermal mass thereof. Accordingly, the reactor cell warms up and thus the operation thereof also starts more quickly. Accordingly, the performance thereof under extremely demanding conditions is very good. Pressure loss caused by the reactor cell of the invention made from thin sheets is also low. The thicknesses of the sheets may be for instance from 0.01 to 0.2 mm, such as from 0.02 to 0.05 mm. The heights of the corrugations may be e.g. between 0.2 and 5 mm, such as 0.1 to 2 mm.
An object of the present invention is a corrugated sheet of a reactor cell connected at least at one corrugation to another sheet with densely spaced joints in such a manner that channels are formed between the sheets. Joining the sheets together at corrugations makes the reactor cell substantially more rigid and mechanically particularly strong even under demanding conditions. The reactor cell becomes mechanically particularly strong if the joints of the corrugations are as close to each other as possible. This may be achieved for instance by joining the sheets together with 10-1000 joints per cm.sup.3, preferably with 10-50 or 50-200 or 200-500 or 500-1000 joints per cm.sup.3 of the reactor cell.
According to an object of the invention corrugated sheets are joined together at the corrugations of said overlapping sheets with joints that are located at least at some corrugations of each corrugated sheet and spaced apart by intervals of 0.5 to 10 mm, the number of said joints between each overlapping corrugated sheets being 10 to 1000 per cm3.
An object of the invention is the preoxidation of the sheets. Preoxidation of the sheets was surprisingly found to improve the joining the sheets together especially by resistance welding. This preoxidation of the sheets may be carried out for instance by preannealing or chemical oxidation.
Sheet may be preoxidized by annealing for e.g. 0.1-10 hours at the temperature of 500-1000.degree. C., preferably for 1-3 hours at 700-800.degree. C. An alumina layer is thus formed on the sheets containing aluminium. This thin alumina layer improves the efficiency of resistance welding. Oxide layer may also be formed from other elements or compounds than aluminium.
An object of the invention is a reactor cell having overlapping sheets, the overlapping corrugations of which lie at oblique angle relative to one another. The reactor cell is made resistant and effective by superimposing corrugated sheets and joining them together so as to contact the corrugations of the overlapping sheets with one another and to place said corrugations in different orientations relative to one another. In such a reactor cell, the contact area between the sheet surfaces and the exhaust gas to be purified is high and the performance is good.
Said overlapping corrugated sheets joined together and having corrugations in oblique angles relative to each other may be profiled sheets. The profiled sheets joined together contact one another only at the junctions of the corrugations. The reactor cell is made particularly strong by joining the profiled sheets together at oblique angles relative to the directions of the corrugations with e.g. welding or soldering joints spaced by intervals of 1 to 5 mm.
Profiled sheets having corrugations that are joined at an oblique angle relative to each other may be produced e.g. from a profiled sheet strip having profiles at an oblique angle relative to the edges of the strip. From this sheet strip, sheets having the shape of the reactor cell are cut and stacked one upon the other transversely relative to the profiles by turning every second sheet before stacking it. From this sheet strip, profiled sheets may be made by folding the strip on itself alternately in different directions. The profiles of the strip may typically lie at angles between 8 and 45 degrees relative to the edges of the strip, the profiles lying preferably at angles between 5 and 30 degrees. Accordingly, the directional angle between the corrugations of the profiled sheets joined together is preferably 10 to 60 degrees.
The gas being treated in a reactor cell made from overlapping profiled sheets joined together at an oblique angle also flows in the lateral direction of the sheets. Due to this fact, the gas is mixed and the flow distribution in the cell is equalized.
In a reactor cell made from profiled sheets, the directional angle between the corrugations thereof may be e.g. 5 to 90 degrees. The higher this angle is, the more the contact areas between the corrugated sheets are point-like. The reaction surface of the sheets is thus maximal. On the other hand, a wide profile angle may cause pressure losses in the flow of the substance or compound being treated due to excessive turbulences. The directional angle of the corrugations of the overlapping profiled sheets is preferably 20 to 60 degrees in the direction of the flow of the gas being treated, if for instance exhaust gases of combustion engine are treated.
A uniform flow distribution equalizes the temperatures in the reactor cell, and accordingly, internal temperature stresses are lower. A uniform flow distribution improves the operation of the reactor cell in general. This is favourable to the successful performance. By using in series several reactor cells having sheets at different orientations, the flows of gases may be equalized very well. Several such cells may also be connected in series. Such successive reactor cells having sheets at least partially transversely oriented relative to each other may have a spiral structure, a structure bent to an S-form, or they may comprise stacked corrugated sheets.
An object of the present invention is to connect the sheets and the reactor cell to a housing. The surface of the housing may be provided in the region of the reactor cell with connecting grooves that connect the sheets of the reactor cell to the inner surface of the housing. When providing the housing having a reactor cell therein with connecting grooves, the edges of the sheets will be oriented parallel to the housing. This stabilizes the connection between the housing and the reactor cell. In this case it is not necessary to join the sheets of the reactor cell to each other. Bypassing gas flows parallel to the inner wall of the housing are also prevented by the connecting grooves.
The number of the connecting grooves may for instance be 2 to 8. Said connecting grooves are preferably situated close to each other to minimize the thermal expansion between the reactor cell and the housing. Typically, the distance between the connecting grooves is 10 to 30 mm, the depth and width thereof being 0.5 to 2.0 mm. The connecting grooves are preferably situated substantially in the middle section of the reactor housing or at the inlet end of the housing relative to the flow direction of the gas being treated.
According to an object of the invention when making a connecting groove said connecting groove has orientated a sheet of the reactor cell parallel to the inside of the housing, and said sheet is also connected to the housing with one or several weld joints made on the bottom of the connecting groove through the housing.
The reactor cell may also be connected to the housing with welded joints, for instance by welding the reactor cell to the housing from outside. A particularly stable connection between the sheets and the reactor cell, and the housing is provided by carrying out the welding on the bottom of the connecting groove through the housing. Laser welding may preferably be used, TIG and MIG welding techniques being also useful.
According to an object of the invention the reaction cell in connected to the housing or to part of it by weld joints made by resistance welding. The resistance welding can preferably be made simultaneously when joining sheets together by resistance welding. The resistance welding can be made so that the reaction cell is installed inside the housing and the whole reaction cell and the whole housing are welded together. The resistance welding can also be made preferably so that a half of the reaction cell is installed inside a half of the housing and these are welded together. After that, the reaction cell and the housing can be connected by welding two connected splits together.
An object of the present invention is the insertion of the reactor cell in a conical housing. To manufacture the reactor cell, the reactor may also be assembled in this conical housing by using sheets cut or bent into the form of the conical housing. The walls of the conical housing improve the rigidity of the structure of the reactor cell since the reactor cell becomes wedged conforming to the walls of the housing in the conical area. The reactor cells are well anchored to the housing by the conical walls even without any grooves on the surface of the housing or welded joints. The conical housing may have the shape of a truncated cone, truncated angular cone or cylinder. The shape thereof may be symmetrical or unsymmetrical.
In a conical housing, in the direction of the gas flow, since the cross section of the upstream end of the housing is smaller than that of the middle part thereof, turbulence at the inlet end of the housing is low. This improves the efficiency of the operation of the reactor cell and brings about relatively low flow resistances. The cone angle of a conical housing is typically 3 to 30 degrees.
A second conical housing may be joined to a first conical housing abutting on it, or two conical reactor cells abutting against each other may be inserted into a housing tapering conically at both ends. Such reactor cells are made particularly effective by using in the reactor cells such corrugated sheets that are joined together at an oblique directional angle relative to the corrugations and by joining the reactor cells together in such a way that the sheets are at least partially transversely orientated.
The pressure loss at the upstream end of the reactor cell is particularly significant. In a cylindrical reactor cell, the pressure loss at the upstream end may even be half of the total pressure loss in the reactor cell. The pressure loss at the upstream end of the cone crucially depends on the ratio of the cross section of the feed line to that of the inlet end of the reactor cell. This ratio is favorable in a reactor cell tapering towards the inlet end. In this case, the turbulence of the flow will decrease, the pressure loss being significantly lower.
Reactor cells or housings having other shapes may be combined with conical housings. It is for instance contemplated to use a housing conically tapering towards both ends and having a straight middle section.
The corrugated sheets of the conical reactor cell preferably have corrugations that are higher at one end than at the other. Such sheets may for instance have at one end U-shaped grooves with low profiles that continuously change their shapes to form higher V-shaped grooves towards the other end of the sheet. By selecting a suitable height difference of the corrugations, the reactor cell may be assembled of intact sheets welded together, thus obtaining a reactor cell with a high mechanical strength that may be manufactured in a simple way. Now some embodiments of the present invention will be described in more detail with reference to the appended drawings.
In
In
In
In
In
An embodiment of the reactor cell of the invention (Kemira) and some commercially available reactor cells were subjected to a comparative mechanical resistance test (Cycle 2010). The reactor cell 41 comprised corrugated sheets 2, 3 with oblique corrugations joined together by resistance welding at an angle of 40 degrees relative to the corrugations 31, 32, 33, the joint density being 200 joints/cm.sup.3. The reactor cell was inserted into a round housing 47 and connected thereto by means of three connecting grooves 43, 44, 45. Further, a weld joint 46 was formed on the bottom of one of the connecting grooves using laser welding.
The reactor cells being tested were connected to an exhaust manifold of an engine (Saab 2.0 L 16-V) on a motor test bench. Following the installations, the engine was started and allowed to warm up with partial load until the thermostat of the engine levelled off. In the test, full load and idle running cycles of 50 seconds, respectively, were repeated. In the full load cycle, the initial number of revolutions of 5500 rpm was lowered to 4700 rpm before the idle running cycle. During the full load, pressurized air was fed upstream of the reactor cell in an amount sufficient to raise the temperature therein to about 1020.degree. C. In the idle running cycle, the pressurized air feed was higher to lower the temperature below 400.degree. C. quickly.
High mechanical stress of the cycle is due to high temperature, high gas flow, strong gas impulses, rapid temperature changes, and vibrations of the engine transferred via the exhaust manifold. The cycle was interrupted every 5 hours and the reactor cells being tested were checked. In some cases the test was stopped earlier if the reactor cell was already mechanically damaged. The results of these comparative tests are as follows:
According to the test results, the Kemira embodiment of the reactor cell of the invention withstood the test conditions undamaged at least 5 to 10 times longer than the control reactor cells.
| Number | Date | Country | Kind |
|---|---|---|---|
| FI-20010257 | Feb 2001 | FI | national |
| FI-20010258 | Feb 2001 | FI | national |
| FI-20010259 | Feb 2001 | FI | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10072906 | Feb 2002 | US |
| Child | 11944743 | US |